CN116333350A - 一种高吸水性树脂粉体表面处理液、制备方法及其应用 - Google Patents
一种高吸水性树脂粉体表面处理液、制备方法及其应用 Download PDFInfo
- Publication number
- CN116333350A CN116333350A CN202211338868.3A CN202211338868A CN116333350A CN 116333350 A CN116333350 A CN 116333350A CN 202211338868 A CN202211338868 A CN 202211338868A CN 116333350 A CN116333350 A CN 116333350A
- Authority
- CN
- China
- Prior art keywords
- resin powder
- super absorbent
- absorbent resin
- treatment liquid
- surface treatment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种高吸水性树脂粉体表面处理液、制备方法及其应用，属于粉体表面处理技术领域，包括以下重量份的组分：去离子水：2～10，硫酸铝：1～3，多元醇2～10，十二烷基苯磺酸钠：0.1～1，二氧化硅分散液：1～5，多元醇为甘油、乙二醇或丁二醇中的一种或多种，本发明通过在高吸水性树脂粉体表面处理液中添加二氧化硅分散液和十二烷基苯磺酸钠，前人无使用，且使用这些物质可以大大提高吸水速度。
Description
技术领域
本发明属于粉体表面处理技术领域，具体涉及一种高吸水性树脂粉体表面处理液、制备方法及其应用。
背景技术
由丙烯酸和丙烯酸钠共聚合得到的高吸水性树脂粉体如不进行表面交联，则影响高吸水性树脂的吸水速度，吸水后粘在一起成为块状，使第二次吸水速度大大降低
发明内容
针对现有技术的不足，本发明的目的在于提供一种高吸水性树脂粉体表面处理液、制备方法及其应用。
本发明的目的可以通过以下技术方案实现：
一种高吸水性树脂粉体表面处理液，包括以下重量份的组分：
去离子水：2～10；
硫酸铝：1～3；
多元醇2～10；
十二烷基苯磺酸钠：0.1～1；
二氧化硅分散液：1～5。
进一步的，所述多元醇为甘油、乙二醇或丁二醇中的一种或多种。
一种高吸水性树脂粉体表面处理液的制备方法，先称取去离子水，然后称取硫酸铝、多元醇、十二烷基苯磺酸钠、二氧化硅分散液，在常温下溶于去离子水中，搅拌后得到表面交联处理的处理液。
一种高吸水性树脂粉体表面处理液在高吸水性树脂粉体上的应用。
进一步的，包括高吸水性树脂粉，所述高吸水性树脂粉表面吸收有表面交联处理的处理液。
一种高吸水性树脂粉体表面交联处理方法，将高吸水性树脂粉加入分散机中，然后常温下将上述制备的高吸水性树脂粉体表面处理液喷于其表面，再将其进行交联反应，反应结束后过筛。
进一步的：所述交联反应的温度为120～180度，时间为1.5～2小时。
进一步的：所述过筛的筛网为40～120目。
本发明的有益效果：
本发明通过在高吸水性树脂粉体表面处理液中添加二氧化硅分散液和十二烷基苯磺酸钠，前人无使用，且使用这些物质可以大大提高吸水速度。
具体实施方式
下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其它实施例，都属于本发明保护的范围。
一种高吸水性树脂粉体表面处理液、制备方法及其应用，表面处理液包括以下配方重量份
去离子水：2～10份
硫酸铝：1～3份
多元醇：2～10份
十二烷基苯磺酸钠：0.1～1份
二氧化硅分散液：1～5份
上述多元醇为甘油、乙二醇或丁二醇中的一种或多种
硫酸铝是一个被广泛运用的工业试剂，外观为白色晶体；十二烷基苯磺酸钠为阴离子表面活性剂，是化学基本原料，制取洗衣粉的常用原料；二氧化硅分散液为半透明液体，具有耐水、耐火、耐污性能，二氧化硅分散到液体之后，依据不同的分散体系，其外观从白色乳状到无色透明。
上述配方的具体制备方法为。
实施例1
步骤一：用量筒量取2份离子水倒入烧杯中，再用量筒量取2份多元醇和1份二氧化硅分散液倒入烧杯中，用电子天平称取1份硫酸铝、0.1份十二烷基苯磺酸钠依次加入烧杯中。
步骤二：用玻璃棒适当搅拌直至溶液中无固体颗粒，即可得到表面交联处理的处理液
实施例2
步骤一：用量筒量取10份离子水倒入烧杯中，再用量筒量取10份多元醇和5份二氧化硅分散液倒入烧杯中，用电子天平称取3份硫酸铝、1份十二烷基苯磺酸钠依次加入烧杯中。
步骤二：用玻璃棒适当搅拌直至溶液中无固体颗粒，即可得到表面交联处理的处理液
一种高吸水性树脂粉体表面处理液的应用：以实施1中制备的处理液为例，称取50克到100克高吸水性树脂粉加入分散机中，高吸水性树脂粉分散后在常温下将上述制备的表面处理液喷于其表面，喷洒过程中保持搅拌，待高吸水性树脂均匀吸收处理液，且其表面稍湿不黏手后，再于120～180度下交联反应1.5～2小时，过筛取40～120目为高吸水性树脂成品粉。
吸水性测试：称取一份10克加入上述处理液的高吸水性树脂成品粉，另一份10克未加上述处理液的高吸水性树脂粉，分别倒入烧杯中，向两个烧杯中同时加入20ml纯水，共加4次。
每次以加水开始计时，树脂表面无自由水为止的时间为判断高吸水性树脂的吸水速度，以秒计，时间越短则吸水速度越快。实验情况见下表：时间以秒表测试
表1
| 加水次数 | 1 | 2 | 3 | 4 |
| 未处理 | 13 | 18 | 28 | 41 |
| 表面处理 | 5.0 | 5.6 | 6.4 | 7.4 |
实验表明，加入上述处理液的高吸水性树脂粉吸水时间明显比未加处理液的高吸水性树脂粉的吸水时间短，第一次加入水时，加入处理液的树脂粉比未加处理液的树脂粉吸水速率快2倍多，第二次、第三次、第四次加水时，加入处理液的树脂粉比未加处理液的树脂粉依次快3倍多、4倍多、5倍多，加入处理液的树脂粉吸水效率明显高于未加树脂粉的吸水效率。
在本说明书的描述中，参考术语“一个实施例”、“示例”、“具体示例”等的描述意指结合该实施例或示例描述的具体特征、结构、材料或者特点包含于本发明的至少一个实施例或示例中。在本说明书中，对上述术语的示意性表述不一定指的是相同的实施例或示例。而且，描述的具体特征、结构、材料或者特点可以在任何的一个或多个实施例或示例中以合适的方式结合。
以上显示和描述了本发明的基本原理、主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。
Claims (8)
1.一种高吸水性树脂粉体表面处理液，其特征在于，包括以下重量份的组分：
去离子水：2～10；
硫酸铝：1～3；
多元醇：2～10；
十二烷基苯磺酸钠：0.1～1；
二氧化硅分散液：1～5。
2.根据权利要求1所述的一种高吸水性树脂粉体表面处理液，其特征在于，所述多元醇为甘油、乙二醇或丁二醇中的一种或多种。
3.权利要求1所述的一种高吸水性树脂粉体表面处理液的制备方法，其特征在于，先称取去离子水，然后称取硫酸铝、多元醇、十二烷基苯磺酸钠、二氧化硅分散液，在常温下溶于去离子水中，搅拌后得到表面交联处理的处理液。
4.权利1～2任一所述的一种高吸水性树脂粉体表面处理液在高吸水性树脂粉体上的应用。
5.根据权利要求4所述的一种高吸水性树脂粉体表面处理液在高吸水性树脂粉体上的应用，其特征在于，包括高吸水性树脂粉，所述高吸水性树脂粉表面吸收有表面处理液。
6.权利要求4所述的一种高吸水性树脂粉体表面交联处理方法，其特征在于，将高吸水性树脂粉加入分散机中，然后常温下将上述制备的高吸水性树脂粉体表面处理液喷于其表面，再将其进行交联反应，反应结束后过筛。
7.根据权利要求5所述的一种高吸水性树脂粉体表面交联处理方法，其特征在于，所述交联反应的温度为120～180度，时间为1.5～2小时。
8.根据权利要求5所述的一种高吸水性树脂粉体表面交联处理方法，其特征在于，所述过筛的筛网为40～120目。