CN116285535A - Environment-friendly quick-setting building waterproof coating - Google Patents
Environment-friendly quick-setting building waterproof coating Download PDFInfo
- Publication number
- CN116285535A CN116285535A CN202310443351.9A CN202310443351A CN116285535A CN 116285535 A CN116285535 A CN 116285535A CN 202310443351 A CN202310443351 A CN 202310443351A CN 116285535 A CN116285535 A CN 116285535A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- building waterproof
- setting building
- quick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an environment-friendly quick-setting building waterproof coating, and relates to the technical field of building coatings. The invention relates to an environment-friendly quick-setting building waterproof coating, which comprises, by weight, 15-25 parts of quartz powder, 6-12 parts of calcium carbonate, 20-30 parts of acrylic emulsion, 12-18 parts of composite filler particles, 10-15 parts of accelerator, 3-5 parts of mildew-proof bactericide, 2-4 parts of pH regulator, 1-4 parts of emulsifier, 1-3 parts of silicone oil defoamer, 1-2 parts of thickener and 25-30 parts of deionized water. The environment-friendly quick-setting building waterproof paint can be quickly dried after being brushed, is not easy to peel off and separate, has strong durability in use, is environment-friendly in raw material component use, high in processing efficiency, simple in preparation process and high in popularization value.
Description
Technical Field
The invention relates to the technical field of building coatings, in particular to an environment-friendly quick-setting building waterproof coating.
Background
The building waterproofing is a measure taken on building materials and structures for preventing water from penetrating into certain parts of the building, the waterproofing is mainly used on roofs, underground buildings, underground parts of the building, inner chambers, water storage structures and the like which need to be waterproofed, and the building waterproofing is divided into two main categories of material waterproofing and construction waterproofing according to the difference of measures and measures taken by the building materials, wherein the material waterproofing is used for blocking a water passage by the building materials so as to achieve the aim of waterproofing or increasing the seepage resistance, such as coiled material waterproofing, coating film waterproofing, concrete and cement mortar rigid waterproofing, clay, gray soil waterproofing and the like, and the building waterproofing also comprises coating waterproofing;
the building waterproof paint is a viscous liquid polymer synthetic material which is in a non-fixed shape at normal temperature, and after being coated, the building waterproof paint can form a tough waterproof coating film on the surface of a base layer through volatilization of a solvent or evaporation or reaction solidification of moisture, and the current building waterproof paint is limited by components and properties, is difficult to form quick solidification after being brushed, affects the processing efficiency, is easy to fade or peel after being used for a long time, has a limited service life and has a certain limitation; therefore, we propose an environment-friendly quick-setting building waterproof coating.
Disclosure of Invention
The invention aims to provide an environment-friendly quick-setting building waterproof coating, which solves the problems in the background.
In order to solve the technical problems, the invention is realized by the following technical scheme:
the invention relates to an environment-friendly quick-setting building waterproof coating, which comprises, by weight, 15-25 parts of quartz powder, 6-12 parts of calcium carbonate, 20-30 parts of acrylic emulsion, 12-18 parts of composite filler particles, 10-15 parts of accelerator, 3-5 parts of mildew-proof bactericide, 2-4 parts of pH regulator, 1-4 parts of emulsifier, 1-3 parts of silicone oil defoamer, 1-2 parts of thickener and 25-30 parts of deionized water;
preferably, the composite filler comprises, by weight, 18-22 parts of quartz powder, 8-10 parts of calcium carbonate, 23-27 parts of acrylic emulsion, 14-16 parts of composite filler particles, 12-13 parts of accelerator, 3.5-4.5 parts of mildew-proof bactericide, 2.5-3.5 parts of pH regulator, 2-3 parts of emulsifier, 1.5-2.5 parts of silicone oil defoamer, 1.4-1.6 parts of thickener and 27-28 parts of deionized water.
The composite filler particles are a mixture of kaolin and wollastonite, and the use ratio of the kaolin to the wollastonite is 1:0.6.
The accelerator is a liquid alkali-free accelerator, and the mildew-proof bactericide is a nano silver bactericide.
The PH regulator is disodium hydrogen phosphate, and the thickener is sodium polyacrylate.
The preparation method of the environment-friendly quick-setting building waterproof coating comprises the following steps:
step one: preparing and weighing the raw materials according to the corresponding components, and drying the calcium carbonate and the composite filler particles;
step two: ball milling is carried out on quartz powder, calcium carbonate and composite filler particles for 10-15min to obtain powder;
step three: based on the steps, taking powder as a substrate, sequentially adding acrylic emulsion, an accelerator, a pH regulator, a thickener and deionized water, uniformly mixing, wherein the mixing speed is 1200-1400r/min, and the mixing time is 5-8min to obtain a mixture;
step four: continuously adding the rest raw materials including mildew-proof bactericide, emulsifier and silicone oil defoamer into the mixture, continuously mixing, heating in the mixing process for 15-20min, and standing for 2h to obtain the coating;
step five: and (5) inspecting the coating, and sub-packaging after the coating is qualified to obtain the required environment-friendly quick-setting building waterproof coating.
And in the first step, the calcium carbonate and the composite filler particles are dried to ensure that the surface water content is not higher than 0.8 percent.
The temperature rise temperature in the mixing process in the step four is 55-65 ℃.
The invention has the following beneficial effects:
according to the environment-friendly quick-setting building waterproof coating, the quartz powder is matched with the composite filler with similar properties to carry out solid filling, so that the properties of the coating are more stable when the coating is used in different environments, meanwhile, the waterproof performance of the coating is improved through adding acrylic emulsion, thickening, emulsifying and other operations, the coating can be quickly dried after being brushed, and the coating is not easy to peel off and separate, and has strong use durability.
The environment-friendly quick-setting building waterproof paint disclosed by the invention has the advantages of environment-friendly raw material components, quick setting after brushing, high processing efficiency, controllable production cost, simple and convenient preparation flow and high popularization value.
Of course, it is not necessary for any one product to practice the invention to achieve all of the advantages set forth above at the same time.
Detailed Description
The following description of the technical solutions in the embodiments of the present invention will be clear and complete, and it is obvious that the described embodiments are only some embodiments of the present invention, but not all embodiments. All other embodiments, which can be made by those skilled in the art based on the embodiments of the invention without making any inventive effort, are intended to be within the scope of the invention.
Example 1
The invention relates to an environment-friendly quick-setting building waterproof coating which comprises, by weight, 18 parts of quartz powder, 8 parts of calcium carbonate, 27 parts of acrylic emulsion, 16 parts of composite filler particles, 13 parts of accelerator, 3.5 parts of mildew-proof bactericide, 3.5 parts of pH regulator, 3 parts of emulsifier, 1.5 parts of silicone oil defoamer, 1.4 parts of thickener and 28 parts of deionized water.
The composite filler particles are a mixture of kaolin and wollastonite, and the use ratio of the kaolin to the wollastonite is 1:0.6; the accelerator is a liquid alkali-free accelerator, and the mildew-proof bactericide is a nano silver bactericide; the PH regulator is disodium hydrogen phosphate, and the thickener is sodium polyacrylate.
The preparation method of the environment-friendly quick-setting building waterproof coating comprises the following steps:
step one: preparing and weighing the raw materials according to the corresponding components, and drying the calcium carbonate and the composite filler particles to ensure that the surface water content is not higher than 0.8%;
step two: ball milling is carried out on quartz powder, calcium carbonate and composite filler particles for 10-15min to obtain powder;
step three: based on the steps, taking powder as a substrate, sequentially adding acrylic emulsion, an accelerator, a pH regulator, a thickener and deionized water, uniformly mixing, wherein the mixing speed is 1200-1400r/min, and the mixing time is 5-8min to obtain a mixture;
step four: continuously adding the rest raw materials including mildew-proof bactericide, emulsifier and silicone oil defoamer into the mixture, continuously mixing, heating to 55-65 ℃ in the mixing process, mixing for 15-20min, and standing for 2h to obtain the coating;
step five: and (5) inspecting the coating, and sub-packaging after the coating is qualified to obtain the required environment-friendly quick-setting building waterproof coating.
Example 2
The invention relates to an environment-friendly quick-setting building waterproof coating which comprises, by weight, 20 parts of quartz powder, 9 parts of calcium carbonate, 27 parts of acrylic emulsion, 15 parts of composite filler particles, 12.5 parts of accelerator, 4 parts of mildew-proof bactericide, 3 parts of pH regulator, 3 parts of emulsifier, 1.5 parts of silicone oil defoamer, 1.6 parts of thickener and 28 parts of deionized water.
The composite filler particles are a mixture of kaolin and wollastonite, and the use ratio of the kaolin to the wollastonite is 1:0.6; the accelerator is a liquid alkali-free accelerator, and the mildew-proof bactericide is a nano silver bactericide; the PH regulator is disodium hydrogen phosphate, and the thickener is sodium polyacrylate.
The preparation method is the same as in example 1.
Example 3
The invention relates to an environment-friendly quick-setting building waterproof coating which comprises, by weight, 20 parts of quartz powder, 10 parts of calcium carbonate, 25 parts of acrylic emulsion, 15 parts of composite filler particles, 12.5 parts of accelerator, 4 parts of mildew-proof bactericide, 3 parts of pH regulator, 2.5 parts of emulsifier, 2 parts of silicone oil defoamer, 1.5 parts of thickener and 27.5 parts of deionized water.
The composite filler particles are a mixture of kaolin and wollastonite, and the use ratio of the kaolin to the wollastonite is 1:0.6; the accelerator is a liquid alkali-free accelerator, and the mildew-proof bactericide is a nano silver bactericide; the PH regulator is disodium hydrogen phosphate, and the thickener is sodium polyacrylate.
The preparation method is the same as in example 1.
Example 4
The invention relates to an environment-friendly quick-setting building waterproof coating which comprises, by weight, 21 parts of quartz powder, 8 parts of calcium carbonate, 24 parts of acrylic emulsion, 14.5 parts of composite filler particles, 13 parts of accelerator, 4.5 parts of mildew-proof bactericide, 3.5 parts of pH regulator, 2 parts of emulsifier, 1.5 parts of silicone oil defoamer, 1.5 parts of thickener and 27 parts of deionized water.
The composite filler particles are a mixture of kaolin and wollastonite, and the use ratio of the kaolin to the wollastonite is 1:0.6; the accelerator is a liquid alkali-free accelerator, and the mildew-proof bactericide is a nano silver bactericide; the PH regulator is disodium hydrogen phosphate, and the thickener is sodium polyacrylate.
The preparation method is the same as in example 1.
Example 5
The invention relates to an environment-friendly quick-setting building waterproof coating which comprises, by weight, 19 parts of quartz powder, 8.5 parts of calcium carbonate, 26 parts of acrylic emulsion, 16 parts of composite filler particles, 13 parts of accelerator, 4.5 parts of mildew-proof bactericide, 2.8 parts of pH regulator, 2.5 parts of emulsifier, 2.5 parts of silicone oil defoamer, 1.4 parts of thickener and 27.5 parts of deionized water.
The composite filler particles are a mixture of kaolin and wollastonite, and the use ratio of the kaolin to the wollastonite is 1:0.6; the accelerator is a liquid alkali-free accelerator, and the mildew-proof bactericide is a nano silver bactericide; the PH regulator is disodium hydrogen phosphate, and the thickener is sodium polyacrylate.
The preparation method is the same as in example 1.
In the scheme, the quartz powder is matched with the mixture of the kaolin and the wollastonite to be filled in a solid state, so that the property of the coating is more stable when the coating is used in different environments, and the embodiment shows that the building waterproof coating has good water absorption performance and stable structure, and the coating has water resistance by using the operations such as thickening, emulsifying and the like of the acrylic emulsion.
In the description of the present specification, the descriptions of the terms "one embodiment," "example," "specific example," and the like, mean that a particular feature, structure, material, or characteristic described in connection with the embodiment or example is included in at least one embodiment or example of the present invention. In this specification, schematic representations of the above terms do not necessarily refer to the same embodiments or examples. Furthermore, the particular features, structures, materials, or characteristics described may be combined in any suitable manner in any one or more embodiments or examples.
The preferred embodiments of the invention disclosed above are intended only to assist in the explanation of the invention. The preferred embodiments are not exhaustive or to limit the invention to the precise form disclosed. Obviously, many modifications and variations are possible in light of the above teaching. The embodiments were chosen and described in order to best explain the principles of the invention and the practical application, to thereby enable others skilled in the art to best understand and utilize the invention. The invention is limited only by the claims and the full scope and equivalents thereof.
Claims (8)
1. The environment-friendly quick-setting building waterproof coating is characterized by comprising, by weight, 15-25 parts of quartz powder, 6-12 parts of calcium carbonate, 20-30 parts of acrylic emulsion, 12-18 parts of composite filler particles, 10-15 parts of accelerator, 3-5 parts of mildew-proof bactericide, 2-4 parts of pH regulator, 1-4 parts of emulsifier, 1-3 parts of silicone oil defoamer, 1-2 parts of thickener and 25-30 parts of deionized water.
2. The environment-friendly quick-setting building waterproof coating according to claim 1 is characterized by comprising, by weight, 18-22 parts of quartz powder, 8-10 parts of calcium carbonate, 23-27 parts of acrylic emulsion, 14-16 parts of composite filler particles, 12-13 parts of accelerator, 3.5-4.5 parts of mildew-proof bactericide, 2.5-3.5 parts of pH regulator, 2-3 parts of emulsifier, 1.5-2.5 parts of silicone oil defoamer, 1.4-1.6 parts of thickener and 27-28 parts of deionized water.
3. The environment-friendly quick-setting building waterproof coating according to claim 1, wherein the composite filler particles are a mixture of kaolin and wollastonite, and the use ratio of the kaolin to the wollastonite is 1:0.6.
4. The environment-friendly quick-setting building waterproof paint according to claim 1, wherein the quick-setting agent is a liquid alkali-free quick-setting agent, and the mildew-proof bactericide is a nano silver bactericide.
5. The environment-friendly quick-setting building waterproof paint according to claim 1, wherein the PH regulator is disodium hydrogen phosphate, and the thickener is sodium polyacrylate.
6. The method for preparing the environment-friendly quick-setting building waterproof paint as claimed in claim 1, which is characterized by comprising the following steps:
step one: preparing and weighing the raw materials according to the corresponding components, and drying the calcium carbonate and the composite filler particles;
step two: ball milling is carried out on quartz powder, calcium carbonate and composite filler particles for 10-15min to obtain powder;
step three: based on the steps, taking powder as a substrate, sequentially adding acrylic emulsion, an accelerator, a pH regulator, a thickener and deionized water, uniformly mixing, wherein the mixing speed is 1200-1400r/min, and the mixing time is 5-8min to obtain a mixture;
step four: continuously adding the rest raw materials including mildew-proof bactericide, emulsifier and silicone oil defoamer into the mixture, continuously mixing, heating in the mixing process for 15-20min, and standing for 2h to obtain the coating;
step five: and (5) inspecting the coating, and sub-packaging after the coating is qualified to obtain the required environment-friendly quick-setting building waterproof coating.
7. The environmental-friendly quick-setting building waterproof paint according to claim 6, wherein in the first step, calcium carbonate and composite filler particles are dried to make the surface water content not higher than 0.8%.
8. The environmental-friendly quick-setting building waterproof paint according to claim 7, wherein the temperature rise temperature in the mixing process is 55-65 ℃.