CN116178988A - 高牢度分散染料组合物、高牢度分散染料制品及其用途 - Google Patents
高牢度分散染料组合物、高牢度分散染料制品及其用途 Download PDFInfo
- Publication number
- CN116178988A CN116178988A CN202310119556.1A CN202310119556A CN116178988A CN 116178988 A CN116178988 A CN 116178988A CN 202310119556 A CN202310119556 A CN 202310119556A CN 116178988 A CN116178988 A CN 116178988A
- Authority
- CN
- China
- Prior art keywords
- disperse dye
- component
- fastness
- general formula
- fastness disperse
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本申请提供一种高牢度分散染料组合物、高牢度分散染料制品及其用途，涉及分散染料领域。高牢度分散染料组合物，以质量百分比计算，包括组分A40％‑80％、组分B10％‑30％、组分C1％‑15％和组分D1％‑15％。高牢度分散染料制品，包括所述的高牢度分散染料组合物和助剂。高牢度分散染料制品的用途，用于涤氨面料的染色和印花。本申请提供的高牢度分散染料组合物和染料制品，提升力好，染色品具有落色浅、水泡牢度好以及优异的水洗牢度和撞白牢度，尤其在涤氨面料染色和印花的应用上较为突出。
Description
技术领域
本申请涉及分散染料领域，尤其涉及一种高牢度分散染料组合物、高牢度分散染料制品及其用途。
背景技术
随着纺织工业的发展，越来越多的功能性新材料和新设计被应用于纺织服装和面料的生产中，如功能性涤纶面料的开发、涤氨弹力织物和新型聚酯纤维面料的应用及服装和面料的撞色搭配设计，而这些服装和面料对分散染料的水洗牢度有较高的要求。目前，常用的单偶氮和蒽醌分散染料已不能满足市场对面料高水洗牢度的要求。为提高涤氨弹力织物、细旦涤纶织物及涤沦撞色服装的水洗色牢度，需开发高水洗牢度的分散染料，这也成为印染行业的研究热点。
在牢度方面，水泡牢度、水洗牢度和撞白牢度是较为重要的三个指标。目前市面上缺少在水泡牢度、水洗牢度和撞白牢度三方面都有突出优势且提升力好的染料，尤其是针对涤氨面料更为缺乏，因氨纶纤维表面对分散染料的具有较大的吸附作用，染色结束后经水洗容易脱落进而沾染到其他纤维上，从而导致水洗、泡水等牢度变差，所以对分散染料的选择显得尤为重要。近年来开发一种提升力好、水泡牢度、水洗牢度和撞白牢度突出，适宜广泛用于涤氨面料的染料组合物及其制品，逐渐成为研究的重点之一。
发明内容
本申请的目的在于提供一种高牢度分散染料组合物、高牢度分散染料制品及其用途，以解决上述问题，该组合物分散染料在涤纶尤其涤氨弹性纤维混纺上拥有极佳的水洗、泡水和拼白牢度。
为实现以上目的，本申请采用以下技术方案：
一种高牢度分散染料组合物，以质量百分比计算，包括组分A40％-80％、组分B10％-30％、组分C1％-15％和组分D1％-15％；
所述组分A包括结构通式I所示化合物中的一种或多种，所述结构通式I为：
所述组分B包括结构通式II和结构通式III所示化合物中的一种或多种，所述结构通式II为：
所述结构通式III为：
所述组分C包括结构通式IV所示化合物中的一种或多种，所述结构通式IV为：
所述组分D包括结构通式V和结构通式VI所示化合物中的一种或多种，所述结构通式V为：
所述结构通式VI为：
其中，R1、R2为各自独立的氢、硝基、卤族元素、氰基；
R3为氢、甲氧基或乙氧基；
R4为-COCH3或-CO(CH2)aCH3，a为1或2或3；
R5、R6为各自独立的C1-C4的烷基、烯丙基、-(CH2)bCOOR7或-(CH2)c-X，b为1或2或3，R7为甲基、乙基或丙基，c为1或2或3，X为苯基、甲氧基、乙氧基或氰基；
R8、R9为各自独立的氢、硝基、氰基、甲氧基或乙氧基；
R10为苄基、甲基、乙基或丙基异丙氧基；
R11为C1-C4的烷基及其异构体或苄基；
R12、R13为各自独立的卤素或氰基；
R14是氢、甲基或乙酰氨基；
R15、R16为各自独立的苄基、-(CH2)dCOOR17、-CH2CH2OCH3或-CH2CH3，d为1或2或3，R17为甲基、乙基、丙基或-CH2COCH3；
R18、R19为各自独立的卤素、硝基、氰基、氢、-SO2CH3或-SCN；
R20、R21为各自独立的苄基、C1-C4的烷基及其异构体、-(CH2)eOOC-R23、-CH2CH2CN或-(CH2)f-Ph，e取1或2或3，R23为苯或甲基，f取2或3，Ph为苯基；
R22为氢、甲氧基、甲基或乙酰氨基；
R24为卤素、硝基、氰基、氢、-SO2CH3或-SCN；
R25、R26为各自独立的苄基、-CH2CH2CN、C1-C4的烷基及其异构体或-(CH2)gCOO-R27，g取1或2或3，R27为甲基或-CH2COCH3。
可选的，高牢度分散染料组合物中，组分A的用量可以为40％、45％、50％、55％、60％、65％、70％、75％、80％或者40％-80％之间的任一值；组分B的用量可以为10％、15％、20％、25％、30％或者10％-30％之间的任一值；组分C的用量可以为1％、2％、3％、4％、5％、6％、7％、8％、9％、10％、11％、12％、13％、14％、15％或者1％-15％之间的任一值；组分D的用量可以为1％、2％、3％、4％、5％、6％、7％、8％、9％、10％、11％、12％、13％、14％、15％或者1％-15％之间的任一值。
优选地，所述组分A包括以下化合物中的一种或多种：
优选地，所述组分B包括以下化合物中的一种或多种：
优选地，所述组分C包括以下化合物中的一种或多种：
优选地，所述组分D包括以下化合物中的一种或多种：
本申请还提供一种高牢度分散染料制品，包括所述的高牢度分散染料组合物和助剂。
优选地，所述助剂包括木质素磺酸盐、萘磺酸甲醛缩合物、扩散剂NNO、脂肪醇聚氧乙烯醚、蓖麻油聚氧乙烯醚磺酸盐、木质素85A、平平加O、聚羧酸盐高分子分散剂、马来酸丙烯酸共聚物、元明粉、异构醇聚氧乙烯醚及其盐类、烷基酚聚氧乙烯醚、亚甲基二萘磺酸钠、脂肪酸聚氧乙烯醚及其盐类、扩散剂CNF和分散剂MF中的一种或多种。
优选地，所述助剂与所述高牢度分散染料组合物的质量比为(0.1-4)：1。
可选的，所述助剂与所述高牢度分散染料组合物的质量比可以为0.1：1、0.5：1、1：1、2：1、3：1、4：1或者(0.1-4)：1之间的任一值。
优选地，所述高牢度分散染料制品的形态为固态或液态；
优选地，液态高牢度分散染料制品的固含量为15％-60％。
可选的，液态高牢度分散染料制品的固含量可以为15％、20％、25％、30％、35％、40％、45％、50％、55％、60％或者15％-60％之间的任一值。
本申请还提供一种所述的高牢度分散染料制品的用途，用于涤氨混纺面料的染色和印花。
与现有技术相比，本申请的有益效果包括：
本申请提供的高牢度分散染料组合物和制品，包括有邻苯二甲酰亚胺或酯类结构的分散染料、苯并二呋喃酮类结构的分散染料、吡啶酮类分散染料、噻吩类分散染料、噻唑类分散染料、羧酸酯分散染料，上述结构的分散染料在遇碱时，在高温条件下容易发生水解反应，从而使未固着的或吸附在纤维表面的分散染料发生水解进而溶于水中达到去除的目的，最终提升染色织物的各项牢度。通过以上结构组分的分散染料进行复配，将既能提高染料的耐热迁移性，又能提高碱水溶解性的邻苯二甲酰亚胺类分散染料引入分散染料的偶合组分中，可提高染料的相对分子质量，增大染料与聚酯纤维的亲和力，使得组合物染料具有提升力好，染色品具有落色浅、水泡牢度好以及优异的水洗牢度和撞白牢度，尤其在涤氨面料染色和印花的应用上较为突出。
本申请提供的高牢度分散染料制品，可广泛应用于涤氨面料染色和印花。
附图说明
为了更清楚地说明本申请实施例的技术方案，下面将对实施例中所需要使用的附图作简单地介绍，应当理解，以下附图仅示出了本申请的某些实施例，因此不应被看作是对本申请范围的限定。
图1为实施例1和对比例1的水洗六纤沾色牢度粘片；
图2为实施例1和实施例1和对比例1的拼白牢度及拼白残液图；
图3为实施例1和实施例1和对比例1的泡水残液图。
具体实施方式
如本文所用之术语：
“由……制备”与“包含”同义。本文中所用的术语“包含”、“包括”、“具有”、“含有”或其任何其它变形，意在覆盖非排它性的包括。例如，包含所列要素的组合物、步骤、方法、制品或装置不必仅限于那些要素，而是可以包括未明确列出的其它要素或此种组合物、步骤、方法、制品或装置所固有的要素。
连接词“由……组成”排除任何未指出的要素、步骤或组分。如果用于权利要求中，此短语将使权利要求为封闭式，使其不包含除那些描述的材料以外的材料，但与其相关的常规杂质除外。当短语“由……组成”出现在权利要求主体的子句中而不是紧接在主题之后时，其仅限定在该子句中描述的要素；其它要素并不被排除在作为整体的所述权利要求之外。
当量、浓度、或者其它值或参数以范围、优选范围、或一系列上限优选值和下限优选值限定的范围表示时，这应当被理解为具体公开了由任何范围上限或优选值与任何范围下限或优选值的任一配对所形成的所有范围，而不论该范围是否单独公开了。例如，当公开了范围“1～5”时，所描述的范围应被解释为包括范围“1～4”、“1～3”、“1～2”、“1～2和4～5”、“1～3和5”等。当数值范围在本文中被描述时，除非另外说明，否则该范围意图包括其端值和在该范围内的所有整数和分数。
在这些实施例中，除非另有指明，所述的份和百分比均按质量计。
“质量份”指表示多个组分的质量比例关系的基本计量单位，1份可表示任意的单位质量，如可以表示为1g，也可表示2.689g等。假如我们说A组分的质量份为a份，B组分的质量份为b份，则表示A组分的质量和B组分的质量之比a：b。或者，表示A组分的质量为aK，B组分的质量为bK(K为任意数，表示倍数因子)。不可误解的是，与质量份数不同的是，所有组分的质量份之和并不受限于100份之限制。
“和/或”用于表示所说明的情况的一者或两者均可能发生，例如，A和/或B包括(A和B)和(A或B)。
下面将结合具体实施例对本申请的实施方案进行详细描述，但是本领域技术人员将会理解，下列实施例仅用于说明本申请，而不应视为限制本申请的范围。实施例中未注明具体条件者，按照常规条件或制造商建议的条件进行。所用试剂或仪器未注明生产厂商者，均为可以通过市售购买获得的常规产品。
首先对实施例使用的染料的来源进行说明，具体如下：
式(I-1)为红光蓝B，购自福莱恩特；式(I-2)为氯型红光蓝B，购自福莱恩特；式(I-3)为氰化红光蓝B，购自福莱恩特；式(I-4)为绿光蓝G-2，购自闰土；式(I-5)为苄基蓝G-4，购自闰土；式(I-6)为氰化苄基蓝G-3，购自闰土；式(I-7)为CI分散蓝165，可由多渠道购得；式(I-8)为CI分散蓝173，可由多渠道购得；式(I-9)为CI分散蓝201，可由多渠道购得；式(I-10)为CI分散蓝207，可由多渠道购得；式(I-11)为CI分散蓝301，可由多渠道购得；
式(II-1)为苄基金黄3G，购自亚邦；式(II-2)为苄基黄3G，购自亚邦；式(II-3)为氰化苄基黄3G，购自亚邦；式(II-4)为乙氧基苄基黄3G，购自亚邦；式(II-5)为异丙氧基丙基金黄G，购自福莱恩特；式(II-6)为乙基金黄G-1，购自福莱恩特；式(II-7)为甲基金黄G-2，购自福莱恩特；式(III-1)为CI分散黄114，可由多渠道购得；式(III-2)为异丁基嫩黄6G，购自吉华化工；式(III-3)为异丙基嫩黄6G，购自吉华化工；式(III-4)为苄基嫩黄6G，购自吉华化工；
式(IV-1)为CI分散棕19，可由多渠道购得；式(IV-2)为氯型分散棕RL，购自闰土；式(IV-3)为苄基黄棕，购自吉华；式(IV-4)为环保溴型CI分散棕19，可由多渠道购得；式(IV-5)为环保溴型分散棕RL，购自闰土；式(IV-6)为CI分散蓝257，可由多渠道购得；式(IV-7)为CI分散蓝366；式(IV-8)为分散红GF，购自福莱恩特或山东北澳化工；
式(V-1)为分散红玉GGF，购自亚邦；式(V-2)为分散红玉GGF-2，购自亚邦；式(V-3)为氰化分散红玉GGF，购自亚邦；式(V-4)为CI分散红359，可由多渠道购得；式(V-5)为CI分散红145，可由多渠道购得；式(V-6)为CI分散红131，可由多渠道购得；式(VI-1)为苄基分散红RL，购自福莱恩特；式(VI-2)为双苄基分散红FRL，购自福莱恩特；式(VI-3)为苄基分散红FRL，购自福莱恩特；式(VI-4)为CI分散红106，可由多渠道购得。
实施例1
本实施例提供一种高牢度分散染料组合物，具体包括如下结构的化合物：
其中，式(I-1)、式(I-5)、式(II-1)、式(III-1)、式(IV-4)、式(V-1)的质量比为26：8：6：5：1：3。
本实施例还提供一种高牢度分散染料制品，包括上述分散染料组合物以及助剂，其中，助剂为分散剂MF，分散染料组合物与助剂的质量比为49：51。
其制备方法如下：
将分散染料组合物中的各组分和分散剂MF与适量的水投入分散釜内进行打浆研磨，待粒径符合要求后进行喷雾干燥得到粉体分散染料制品。
实施例2
本实施例提供一种高牢度分散染料组合物，具体包括如下结构的化合物：
其中，式(I-3)、式(I-6)、式(II-2)、式(III-2)、式(IV-1)、式(VI-1)的质量比为20：4：4：4：1：2。
本实施例还提供一种高牢度分散染料制品，包括上述分散染料组合物以及助剂和水，其中，助剂包括分散剂MF5份、马来酸丙烯酸共聚物3份、脂肪醇聚氧乙烯醚2份，分散染料组合物与助剂和水的质量比为35：10：55。
其制备方法如下：
将分散染料组合物中的各组分、助剂与水投入分散釜内进行打浆研磨，然后将物料泵入纳米研磨系统进行细磨，最后检测合格后通过过滤得到液体分散染料制品。
实施例3-10
实施例3-10的配方如表1所示：
表1实施例3-10配方表
制备方法同实施例1或2。
对比例1
本对比例提供一种染料组合物，其组分如下：
其中，式(I-1)、式(A)、式(B)、式(II-7)、式(III-1)的质量比为26：8：6：5：3。
本对比例还提供一种分散染料制品，包括上述分散染料组合物以及分散剂MF，分散染料组合物和分散剂MF的质量比为48：52。
制备方法同实施例1。
对比例2
本对比例提供一种染料组合物，其组分如下：
其中，式(I-1)、式(I-5)、式(C)、式(III-1)、式(II-7)的质量比为20：4：4：4：3。
本对比例还提供一种分散染料制品，包括上述分散染料组合物以及助剂和水，助剂包括分散剂MF、蓖麻油聚氧乙烯醚磺酸盐和异构醇聚氧乙烯醚，三者质量比为5：3：2。分散染料组合物、助剂和水的质量比为35：10：55。
制备方法同实施例2。
对比例3
本对比例提供一种染料组合物，其组分如下：
其中，式(I-1)、式(I-5)、CI分散黄橙288、式(IV-4)、式(V-1)的质量比为27：6：5：4：2。本对比例还提供一种分散染料制品，包括上述分散染料组合物以及分散剂MF，分散染料组合物和分散剂MF的质量比为44：56。
制备方法同实施例1。
对比例4
本对比例提供一种染料组合物，其组分如下：
其中，式(I-1)、式(I-5)、式(II-1)、式(III-1)、CI分散红376的质量比为24：5：6：4：3。
本实施例还提供一种高牢度分散染料制品，包括上述分散染料组合物以及助剂，其中，助剂为分散剂MF，分散染料组合物与助剂的质量比为42：58。
制备方法同实施例1。
效果评价如下：
分别称取2克实施例1～15制得的分散染料制品、对比例1～4的分散染料制品，采用常规高温高压染色法处理涤氨针织物(90/10)，处理过程中，控制染色深度4.0％owf，浴比1:20，调染浴pH值4.0±0.2，室温入染，以1℃/min升温至130℃，保温45min，按常法水洗、还原清洗、中和、定型(180℃×30s)，得到染织物。再进行水洗牢度和拼白牢度以及泡水牢度的测试，其中水洗牢度参考AATCC61 2A标准进行测试。拼白牢度以及泡水牢度测试方法如下：
拼白牢度：
将涤氨针织物1g与同规格白布1g缝合后放入60℃水溶液(汰渍洗衣粉4g/L)中浸泡30min，浴比1:50，判断拼白残液颜色轻重、白布沾色评级。
泡水牢度：
将涤氨针织物1g放入100℃水溶液(汰渍洗衣粉5g/L)中浸泡5min，浴比1:100，判断泡水残液颜色轻重。
结果如表2所示：
表2牢度测试结果
由表2中测试结果的数据，结合实施例1和对比例1中染料组分的结构特点，可以看出，在对比例1中式(A)的组分为绿光分散蓝，由于其结构的不同，导致其碱水溶性较差，进而浮色去除率稍差。因此，本发明提供的分散染料组合物，在涤氨织物上进行染色时，有着更优越的各项牢度性能。
最后应说明的是：以上各实施例仅用以说明本申请的技术方案，而非对其限制；尽管参照前述各实施例对本申请进行了详细的说明，本领域的普通技术人员应当理解：其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分或者全部技术特征进行等同替换；而这些修改或者替换，并不使相应技术方案的本质脱离本申请各实施例技术方案的范围。
此外，本领域的技术人员能够理解，尽管在此的一些实施例包括其它实施例中所包括的某些特征而不是其它特征，但是不同实施例的特征的组合意味着处于本申请的范围之内并且形成不同的实施例。例如，在上面的权利要求书中，所要求保护的实施例的任意之一都可以以任意的组合方式来使用。公开于该背景技术部分的信息仅仅旨在加深对本申请的总体背景技术的理解，而不应当被视为承认或以任何形式暗示该信息构成已为本领域技术人员所公知的现有技术。
Claims (10)
1.一种高牢度分散染料组合物，其特征在于，以质量百分比计算，包括组分A40％-80％、组分B10％-30％、组分C1％-15％和组分D1％-15％；
所述组分A包括结构通式I所示化合物中的一种或多种，所述结构通式I为：
所述组分B包括结构通式II和结构通式III所示化合物中的一种或多种，所述结构通式II为：
所述结构通式III为：
所述组分C包括结构通式IV所示化合物中的一种或多种，所述结构通式IV为：
所述组分D包括结构通式V和结构通式VI所示化合物中的一种或多种，所述结构通式V为：
所述结构通式VI为：
其中，R1、R2为各自独立的氢、硝基、卤族元素、氰基；
R3为氢、甲氧基或乙氧基；
R4为-COCH3或-CO(CH2)aCH3，a为1或2或3；
R5、R6为各自独立的C1-C4的烷基、烯丙基、-(CH2)bCOOR7或-(CH2)c-X，b为1或2或3，R7为甲基、乙基或丙基，c为1或2或3，X为苯基、甲氧基、乙氧基或氰基；
R8、R9为各自独立的氢、硝基、氰基、甲氧基或乙氧基；
R10为苄基、甲基、乙基或丙基异丙氧基；
R11为C1-C4的烷基及其异构体或苄基；
R12、R13为各自独立的卤素或氰基；
R14是氢、甲基或乙酰氨基；
R15、R16为各自独立的苄基、-(CH2)dCOOR17、-CH2CH2OCH3或-CH2CH3，d为1或2或3，R17为甲基、乙基、丙基或-CH2COCH3；
R18、R19为各自独立的卤素、硝基、氰基、氢、-SO2CH3或-SCN；
R20、R21为各自独立的苄基、C1-C4的烷基及其异构体、-(CH2)eOOC-R23、-CH2CH2CN或-(CH2)f-Ph，e取1或2或3，R23为苯或甲基，f取2或3，Ph为苯基；
R22为氢、甲氧基、甲基或乙酰氨基；
R24为卤素、硝基、氰基、氢、-SO2CH3或-SCN；
R25、R26为各自独立的苄基、-CH2CH2CN、C1-C4的烷基及其异构体或-(CH2)gCOO-R27，g取1或2或3，R27为甲基或-CH2COCH3。
2.根据权利要求1所述的高牢度分散染料组合物，其特征在于，所述组分A包括以下化合物中的一种或多种：
3.根据权利要求1所述的高牢度分散染料组合物，其特征在于，所述组分B包括以下化合物中的一种或多种：
4.根据权利要求1所述的高牢度分散染料组合物，其特征在于，所述组分C包括以下化合物中的一种或多种：
5.根据权利要求1-4任一项所述的高牢度分散染料组合物，其特征在于，所述组分D包括以下化合物中的一种或多种：
6.一种高牢度分散染料制品，其特征在于，包括权利要求1-5任一项所述的高牢度分散染料组合物和助剂。
7.根据权利要求6所述的高牢度分散染料制品，其特征在于，所述助剂包括木质素磺酸盐、萘磺酸甲醛缩合物、扩散剂NNO、脂肪醇聚氧乙烯醚、蓖麻油聚氧乙烯醚磺酸盐、木质素85A、平平加O、聚羧酸盐高分子分散剂、马来酸丙烯酸共聚物、元明粉、异构醇聚氧乙烯醚及其盐类、烷基酚聚氧乙烯醚、亚甲基二萘磺酸钠、脂肪酸聚氧乙烯醚及其盐类、扩散剂CNF和分散剂MF中的一种或多种。
8.根据权利要求7所述的高牢度分散染料制品，其特征在于，所述助剂与所述高牢度分散染料组合物的质量比为(0.1-4)：1。
9.根据权利要求6-8任一项所述的高牢度分散染料制品，其特征在于，其形态为固态或液态；
优选地，液态高牢度分散染料制品的固含量为15％-60％。
10.一种权利要求6-9任一项所述的高牢度分散染料制品的用途，其特征在于，用于涤氨混纺面料的染色和印花。