CN115741909A - Anti-corrosion and moisture-proof bamboo-wood composite shaving board and preparation method and application thereof - Google Patents
Anti-corrosion and moisture-proof bamboo-wood composite shaving board and preparation method and application thereof Download PDFInfo
- Publication number
- CN115741909A CN115741909A CN202211486779.3A CN202211486779A CN115741909A CN 115741909 A CN115741909 A CN 115741909A CN 202211486779 A CN202211486779 A CN 202211486779A CN 115741909 A CN115741909 A CN 115741909A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- wood composite
- layer
- wood
- shaving board
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anticorrosive and moistureproof bamboo-wood composite shaving board and a preparation method and application thereof, and relates to the technical field of composite boards and manufacturing methods thereof. This it is anticorrosive, dampproofing bamboo wood composite shaving board and preparation method and application, the package rubbing board comprises a core, bamboo wood composite shaving board layer on the top fixedly connected with of core, bamboo wood composite shaving board layer under the bottom fixedly connected with of core, go up the top fixedly connected with upper epidermis on bamboo wood composite shaving board layer, top layer under the bottom fixedly connected with of lower bamboo wood composite shaving board layer, the core, go up bamboo wood composite shaving board layer, lower bamboo wood composite shaving board layer, the waterproof corrosion resistant layer of outside fixedly connected with on upper epidermis and lower top layer, one kind is anticorrosive, dampproofing bamboo wood composite shaving board's preparation method, this application can effectual reduction in production cost through the setting up of last bamboo wood composite shaving board layer and lower bamboo wood composite shaving board layer, and can also prolong anticorrosive, the dampproofing composite shaving board's of bamboo wood life, greatly increased is anticorrosive, dampproofing bamboo wood composite shaving board's practicality.
Description
Technical Field
The invention relates to the technical field of composite boards and manufacturing methods thereof, in particular to an anti-corrosion and anti-moisture bamboo-wood composite shaving board and a manufacturing method and application thereof.
Background
Particle boards, bagasse boards, artificial boards made from wood or other lignocellulosic materials, glued under heat and pressure after the application of an adhesive, also known as particle boards, are used mainly in furniture manufacture and in the construction industry.
Bamboo is used as a characteristic resource and an advantageous resource in China, has the characteristics of high strength, good toughness and the like, is always considered as an ideal structural material, and has been widely applied to bamboo plywood used for a carriage bottom plate, building templates and the like. However, due to the lack of special automatic machining equipment, most of the processes (such as thin bamboo strips, woven mats and the like) still remain in the manual manufacturing stage for a long time, and large-scale continuous production cannot be formed. The development of the recombined bamboo wood product not only improves the utilization rate of raw materials, but also realizes the industrial production and application of the bamboo structural material.
The bamboo-wood composite structural board is one of common board products in the field of wood industry at present, and is mainly prepared by compounding a rotary-cut veneer and a bamboo curtain bamboo mat, the board has better mechanical property due to the complementary advantages of the wood and the bamboo performance, the application is very wide at present, when a common shaving board is put into use, the common shaving board can be corroded in a humid and severe environment to cause the phenomena of mildew and the like, and the service life of the shaving board is shortened, so that the anticorrosion and moistureproof bamboo-wood composite shaving board, the preparation method and the application thereof are provided to solve the problems
Disclosure of Invention
Aiming at the defects of the prior art, the invention provides an anti-corrosion and anti-moisture bamboo-wood composite shaving board and a preparation method and application thereof, and solves the problems in the background art. In order to achieve the purpose, the invention is realized by the following technical scheme: the utility model provides an anticorrosive, dampproofing bamboo wood composite shaving board and preparation method and application thereof, includes the core, bamboo wood composite board layer on the top fixedly connected with of core, bamboo wood composite board layer under the bottom fixedly connected with of core, go up the top fixedly connected with upper epidermis on bamboo wood composite board layer, the top layer under the bottom fixedly connected with of bamboo wood composite board layer down, the waterproof corrosion resistant layer of outside fixedly connected with on core, last bamboo wood composite board layer, lower bamboo wood composite board layer, upper epidermis and lower top layer.
A preparation method of an anticorrosive and moistureproof bamboo-wood composite shaving board comprises the following steps:
the method comprises the following steps: the base material comprises wood shavings and a bamboo-wood composite board, the thickness of the wood shavings is 0.3-1.2 mm, the length of the bamboo-wood composite board is 0.5-5 cm, and the moisture content of the wood shavings and the bamboo-wood composite board is 5-13%.
Step two: the preparation method of the wood shavings comprises the steps of preparing wood into block materials with the area of 1-10 square centimeters, and then slicing the block materials to obtain the wood shavings.
Step three: mixing base materials: mixing the wood shavings and the bamboo-wood composite plates to obtain an upper layer mixed material, a lower layer mixed material and a core body mixed material, wherein the mass ratio of the wood shavings to the bamboo-wood composite plates in the upper layer mixed material to the lower layer mixed material is (1-4); the wood shavings and the bamboo-wood composite board of the core body mixed material can be mixed in any proportion, and can only contain the wood shavings or the bamboo-wood composite board.
Step four: sizing: mixing the upper-layer mixed material, the lower-layer mixed material and the core mixed material with an adhesive respectively to obtain a mixed material after sizing, wherein the adhesive used for the upper-layer mixed material and the lower-layer mixed material is a lignin-based formaldehyde-free adhesive, and the glue application amount is 120-140 kg/cubic meter; the adhesives used for mixing the core body are 90% of lignin-based formaldehyde-free adhesives and 10% of MDI (diphenylmethane diisocyanate) or 80% of lignin-based formaldehyde-free adhesives and 20% of MDI.
Step five: and paving, hot-pressing and post-treating the mixed material after glue application to obtain the anti-corrosion and moisture-proof bamboo-wood composite shaving board.
Preferably, the core is formed by wood shavings and the mixed bonding of bamboo wood composite board, just the core is in the central point of anticorrosive, dampproofing bamboo wood composite shaving board.
Preferably, the upper surface layer and the lower surface layer are formed by mixing wood shavings and bamboo-wood composite boards.
Preferably, go up bamboo-wood composite board layer and bamboo-wood composite board layer down and constitute by bamboo-wood composite board, just it is the same with the size to go up bamboo-wood composite board layer and bamboo-wood composite board layer's shape down.
Preferably, the waterproof corrosion-resistant layer is made of waterproof and corrosion-resistant materials, and the waterproof corrosion-resistant layer is in a hollow rectangular shape.
Preferably, the atomization temperature of the lignin-based formaldehyde-free adhesive is 30-40 ℃, and the atomization temperature of the MDI is 50-60 ℃.
Preferably, the adhesives used by the upper layer mixing material and the lower layer mixing material are lignin-based aldehyde-free adhesives, and the glue application amount of the lignin-based aldehyde-free adhesives is 120-140 kg/cubic meter.
Preferably, the adhesives used for the core mixing material are 90% of lignin-based formaldehyde-free adhesives and 10% of MDI or 80% of lignin-based formaldehyde-free adhesives and 20% of MDI, and the mass ratio of the wood shavings to the bamboo-wood mixed board in the upper layer mixing material to the lower layer mixing material is 1-4.
The invention provides an anticorrosive and moistureproof bamboo-wood composite shaving board and a preparation method and application thereof. The method has the following beneficial effects:
(1) This application can effectual reduction in production cost through the setting of last bamboo wood composite sheet layer and lower bamboo wood composite sheet layer, and can also prolong the life of anticorrosive, dampproofing bamboo wood composite shaving board, greatly increased anticorrosive, dampproofing bamboo wood composite shaving board's practicality.
(2) This application can effectually be in the humidity through the setting on waterproof corrosion-resistant layer, and waterproof under the abominable condition, and can also be fine anticorrosion, prevent that anticorrosive, dampproofing bamboo wood composite shaving board from being corroded, going mildy under humid environment, lead to anticorrosive, dampproofing bamboo wood composite shaving board to be unable.
Drawings
FIG. 1 is a schematic front view of the inventive structure in cross-section.
In the figure: 1. a core body; 2. putting a bamboo-wood composite board layer; 3. a bamboo-wood composite board layer is arranged; 4. an upper surface layer; 5. a lower surface layer; 6. a waterproof corrosion-resistant layer.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the drawings in the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments.
Referring to fig. 1-1, the present invention provides a technical solution: an anticorrosion and dampproof bamboo-wood composite shaving board and a preparation method and application thereof, comprising a core body 1, wherein the stability and fixity of the core body 1 are stronger. The adhesives used for mixing the core body are 90% of lignin-based formaldehyde-free adhesives and 10% of MDI (diphenyl-methane-diisocyanate) or 80% of lignin-based formaldehyde-free adhesives and 20% of MDI.90% of lignin-based formaldehyde-free adhesive and 10% of MDI or 80% of lignin-based formaldehyde-free adhesive and 20% of MDI can effectively and fully bond wood shavings and bamboo-wood composite boards. The core 1 is formed by mixing and bonding wood shavings and bamboo-wood composite boards, and the core 1 is located at the center of the anti-corrosion and moisture-proof bamboo-wood composite shaving board. Bamboo wood composite board layer 2 on the top fixedly connected with of core 1, go up bamboo wood composite board layer 2 and down bamboo wood composite board layer 2 and can promote the stability of anticorrosive, dampproofing bamboo wood composite shaving board greatly 9. Go up bamboo-wood composite sheet layer 2 and bamboo-wood composite sheet layer 3 down and constitute by bamboo-wood composite board, and go up bamboo-wood composite sheet layer 2 and bamboo-wood composite sheet layer 3 down's shape and size the same. Bamboo wood composite board layer 3 under the bottom fixedly connected with of core 1, this application can effectual reduction in production cost through last bamboo wood composite board layer 3 and lower bamboo wood composite board layer 4's setting, and can also prolong the life of anticorrosive, dampproofing bamboo wood composite shaving board, greatly increased anticorrosive, dampproofing bamboo wood composite shaving board's practicality. Go up bamboo wood composite board layer 2's top fixedly connected with upper epidermis 4, upper epidermis 4 and lower surface 5's setting can effectual whole anticorrosive, the dampproofing bamboo wood composite board's of enhancement life. The mass ratio of wood shavings to bamboo wood mixed plates in the upper surface layer mixed material and the lower surface layer mixed material is 1. The adhesives used for the upper layer mixing material and the lower layer mixing material are lignin-based formaldehyde-free adhesives, and the adhesive application amount of the lignin-based formaldehyde-free adhesives is 120-140 kg/cubic meter. The upper surface layer 4 and the lower surface layer 5 are formed by mixing wood shavings and bamboo-wood composite boards. The bottom fixedly connected with of lower bamboo-wood composite sheet layer 3 is top layer 5 down, and core 1, go up bamboo-wood composite sheet layer 2, lower bamboo-wood composite sheet layer 3, upper surface layer 4 and the outside fixedly connected with waterproof corrosion-resistant layer 6 of bottom layer 5, the setting of waterproof corrosion-resistant layer 6 can be effectual waterproof, corrosion-resistant, has prolonged the life of whole anticorrosive, dampproofing bamboo-wood composite shaving board. This application can be effectual in the humidity through the setting of waterproof corrosion resistant layer 6, waterproof under the abominable condition, and can also be fine anticorrosion, prevent that anticorrosive, dampproofing bamboo wood composite shaving board from being corroded, mildewing under humid environment, lead to anticorrosive, dampproofing bamboo wood composite shaving board to use. The waterproof corrosion-resistant layer 6 is made of waterproof and corrosion-resistant materials, and the waterproof corrosion-resistant layer 6 is in a hollow rectangular shape. The atomization temperature of the lignin-based formaldehyde-free adhesive is 30-40 ℃, and the atomization temperature of MDI is 50-60 ℃.
A preparation method of an anticorrosive and moistureproof bamboo-wood composite shaving board comprises the following steps:
the method comprises the following steps: the base material comprises wood shavings and a bamboo-wood composite board, the thickness of the wood shavings is 0.3-1.2 mm, the length of the bamboo-wood composite board is 0.5-5 cm, and the water content of the wood shavings and the bamboo-wood composite board is 5-13%.
Step two: the preparation method of the wood shavings comprises the steps of preparing wood into block materials with the area of 1-10 square centimeters, and then slicing the block materials to obtain the wood shavings.
Step three: mixing base materials: mixing the wood shavings and the bamboo-wood composite boards to obtain an upper layer mixed material, a lower layer mixed material and a core body mixed material, wherein the mass ratio of the wood shavings to the bamboo-wood composite boards in the upper layer mixed material to the lower layer mixed material is 1-4; the wood shavings and the bamboo-wood composite board mixed by the core body can be mixed in any proportion, and also can only contain the wood shavings or the bamboo-wood composite board.
Step four: sizing: mixing the upper-layer mixed material, the lower-layer mixed material and the core mixed material with an adhesive respectively to obtain a mixed material after sizing, wherein the adhesive used for the upper-layer mixed material and the lower-layer mixed material is a lignin-based formaldehyde-free adhesive, and the glue application amount is 120-140 kg/cubic meter; the adhesive used for mixing the core body is 90% of lignin-based formaldehyde-free adhesive and 10% of MDI or 80% of lignin-based formaldehyde-free adhesive and 20% of MDI.
Step five: and paving, hot-pressing and post-treating the mixed material after glue application to obtain the anti-corrosion and moisture-proof bamboo-wood composite shaving board.
During the use, carry out anticorrosive, dampproofing preparation of bamboo wood composite shaving board through anticorrosive, dampproofing bamboo wood composite shaving board's preparation method step earlier:
the method comprises the following steps: the base material comprises wood shavings and a bamboo-wood composite board, the thickness of the wood shavings is 0.3-1.2 mm, the length of the bamboo-wood composite board is 0.5-5 cm, and the moisture content of the wood shavings and the bamboo-wood composite board is 5-13%.
Step two: the preparation method of the wood shavings comprises the steps of preparing wood into block materials with the area of 1-10 square centimeters, and then slicing the block materials to obtain the wood shavings.
Step three: mixing base materials: mixing the wood shavings and the bamboo-wood composite boards to obtain an upper-layer mixed material, a lower-layer mixed material and a core mixed material, wherein the mass ratio of the wood shavings to the bamboo-wood composite boards in the upper-layer mixed material to the lower-layer mixed material is 1-4; the wood shavings and the bamboo-wood composite board of the core body mixed material can be mixed in any proportion, and can only contain the wood shavings or the bamboo-wood composite board.
Step four: sizing: mixing the upper-layer mixed material, the lower-layer mixed material and the core body mixed material with an adhesive respectively to obtain the mixed materials after sizing, wherein the adhesive used for the upper-layer mixed material and the lower-layer mixed material is a lignin-based formaldehyde-free adhesive, and the adhesive application amount is 120-140 kg/cubic meter; the adhesives used for mixing the core body are 90% of lignin-based formaldehyde-free adhesives and 10% of MDI (diphenylmethane diisocyanate) or 80% of lignin-based formaldehyde-free adhesives and 20% of MDI.
Step five: and paving, hot-pressing and post-treating the mixed material after glue application to obtain the anti-corrosion and moisture-proof bamboo-wood composite shaving board.
Can install the use with it under the environment of difference after the preparation is accomplished, can effectual anticorrosion and go mildy, prolonged anticorrosive, dampproofing bamboo wood composite shaving board life and its practicality greatly.
The above description is only for the preferred embodiment of the present invention, but the scope of the present invention is not limited thereto, and any person skilled in the art should be considered to be within the technical scope of the present invention, and the technical solutions and the inventive concepts thereof according to the present invention should be equivalent or changed within the scope of the present invention.
Claims (9)
1. An anticorrosive, dampproofing bamboo wood composite shaving board and preparation method and application thereof, includes core (1), its characterized in that: bamboo-wood composite sheet layer (2) on the top fixedly connected with of core (1), bamboo-wood composite sheet layer (3) under the bottom fixedly connected with of core (1), go up top fixedly connected with upper epidermis (4) of bamboo-wood composite sheet layer (2), top layer (5) under the bottom fixedly connected with of lower bamboo-wood composite sheet layer (3), core (1), go up bamboo-wood composite sheet layer (2), lower bamboo-wood composite sheet layer (3), upper epidermis (4) and the waterproof corrosion resistant layer (6) of outside fixedly connected with of lower surface layer (5).
2. A preparation method of an anticorrosive and moistureproof bamboo-wood composite shaving board comprises the following steps:
the method comprises the following steps: the base material comprises wood shavings and a bamboo-wood composite board, the thickness of the wood shavings is 0.3-1.2 mm, the length of the bamboo-wood composite board is 0.5-5 cm, and the moisture content of the wood shavings and the bamboo-wood composite board is 5-13%.
Step two: the preparation method of the wood shavings comprises the steps of preparing wood into block materials with the area of 1-10 square centimeters, and then slicing the block materials to obtain the wood shavings.
Step three: mixing base materials: mixing the wood shavings and the bamboo-wood composite boards to obtain an upper-layer mixed material, a lower-layer mixed material and a core mixed material, wherein the mass ratio of the wood shavings to the bamboo-wood composite boards in the upper-layer mixed material to the lower-layer mixed material is 1-4; the wood shavings and the bamboo-wood composite board of core compounding can be the mixture of arbitrary proportion, also can only contain wood shavings or bamboo-wood composite board.
Step four: sizing: mixing the upper-layer mixed material, the lower-layer mixed material and the core body mixed material with an adhesive respectively to obtain the mixed materials after sizing, wherein the adhesive used for the upper-layer mixed material and the lower-layer mixed material is a lignin-based formaldehyde-free adhesive, and the adhesive application amount is 120-140 kg/cubic meter; the adhesive used for mixing the core body is 90% of lignin-based formaldehyde-free adhesive and 10% of MDI (diphenylmethane diisocyanate) or 80% of lignin-based formaldehyde-free adhesive and 20% of MDI.
Step five: and paving, hot-pressing and post-treating the mixed material after glue application to obtain the anti-corrosion and moisture-proof bamboo-wood composite shaving board.
3. The anticorrosion and dampproof bamboo-wood composite shaving board as claimed in claim 1, and its preparation method and application, characterized in that: core (1) is formed by wood shavings and the mixed bonding of bamboo wood composite board, just core (1) is in the central point of anticorrosive, dampproofing bamboo wood composite shaving board and puts.
4. The anti-corrosion and moisture-proof bamboo-wood composite shaving board as well as the preparation method and the application thereof according to claim 1, and is characterized in that: the upper surface layer (4) and the lower surface layer (5) are formed by mixing wood shavings and bamboo-wood composite boards.
5. The anticorrosion and dampproof bamboo-wood composite shaving board as claimed in claim 1, and its preparation method and application, characterized in that: go up bamboo-wood composite sheet layer (2) and down bamboo-wood composite sheet layer (3) and constitute by bamboo-wood composite board, just it is the same with the size to go up bamboo-wood composite sheet layer (2) and the shape of lower bamboo-wood composite sheet layer (3).
6. The anti-corrosion and moisture-proof bamboo-wood composite shaving board as well as the preparation method and the application thereof according to claim 1, and is characterized in that: the waterproof corrosion-resistant layer (6) is made of waterproof and corrosion-resistant materials, and the waterproof corrosion-resistant layer (6) is in a hollow rectangular shape.
7. The anti-corrosion and moisture-proof bamboo-wood composite shaving board as well as the preparation method and the application thereof according to claim 1, and is characterized in that: the atomization temperature of the lignin-based formaldehyde-free adhesive is 30-40 ℃, and the atomization temperature of the MDI is 50-60 ℃.
8. The anti-corrosion and moisture-proof bamboo-wood composite shaving board as well as the preparation method and the application thereof according to claim 1, and is characterized in that: the adhesive used by the upper layer mixing material and the lower layer mixing material is a lignin-based formaldehyde-free adhesive, and the glue application amount of the lignin-based formaldehyde-free adhesive is 120-140 kg/cubic meter.
9. The anticorrosion and dampproof bamboo-wood composite shaving board as claimed in claim 1, and its preparation method and application, characterized in that: the adhesive used for the core mixing material is 90% of lignin-based formaldehyde-free adhesive and 10% of MDI or 80% of lignin-based formaldehyde-free adhesive and 20% of MDI, and the mass ratio of wood shavings to bamboo-wood mixed boards in the upper surface mixing material to the lower surface mixing material is 1-4.