CN115651444A - 一种免打磨的腻子膏 - Google Patents
一种免打磨的腻子膏 Download PDFInfo
- Publication number
- CN115651444A CN115651444A CN202211278724.3A CN202211278724A CN115651444A CN 115651444 A CN115651444 A CN 115651444A CN 202211278724 A CN202211278724 A CN 202211278724A CN 115651444 A CN115651444 A CN 115651444A
- Authority
- CN
- China
- Prior art keywords
- parts
- bentonite
- sanding
- putty paste
- free
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种免打磨的腻子膏，涉及建筑材料装饰领域，由以下重量份的组份组成：填料25‑65份，水性丙烯酸乳液18‑45份，钛白粉2‑8份，羧甲基纤维素7‑15份，膨润土2‑5份，木质纤维2‑25份，消泡剂0.5‑3份，增稠剂1‑23份，成膜助剂0.2‑5份，负离子粉3‑23份，电气石1‑17份，中空玻璃微珠3‑8份，去离子水18‑40份。
Description
技术领域
本发明涉及建筑材料装饰领域，尤其涉及到一种免打磨腻子膏。
背景技术
传统腻子粉在运输、施工时产生的粉尘会污染大气，危害人类的健康；逸散在大气中的粉尘往往含有许多有毒成分，如铬，锰，镉，铅，汞，砷等；当人体吸入粉尘后，小于5um的微粒，极易深入肺部，引起中毒性肺炎或矽肺，有时还会引起肺癌；沉积在肺部的污染物一旦被溶解，就会直接侵入血液，引起血液中毒，未被溶解的污染物，也可能被细胞所吸收，导致细胞结构的破坏。此外，粉尘还会沾污建筑物，使有价值的古代建筑遭受腐蚀。降落在植物叶面的粉尘会阻碍光合作用，抑制其生长；在施工过程中打磨时产生的粉尘浓度平均低于1毫克/立方米时，对人体无害，浓度在1～3毫克/立方米范围内，有一定危害，高于3毫克/立方米时，有较大危害，最高允许值为10 毫克/立方米，目前实际上大多数施工过程中产生的粉尘都高于标准；粉尘不会直接伤人，但对呼吸道和眼睛等器官会造成很大危害；粒径大于10微米的粉尘在空气中停留时间较短，在呼吸作用中可被有效地保留在呼吸道上，不进入肺泡，但由于木粉尘中含有木焦油，这种物质由各种酚类和烃类组成，并含有致癌性较强的物质，长此以往，工人会部分的患有支气管炎、哮喘和肺气肿等，甚至致癌。粒径小于 10微米以下的木粉，会直接进入人的肺部组织，沉淀于肺泡中，有可能引起肺组织的慢性纤维化，甚至导致肺心病、心血管病等一系列病变。而且这些可吸入物质还会将多种污染物或病菌卷携入肺部，对人体危害很大。粉尘如果弹入或飞入人的眼睛，会造成伤害，影响正常操作。施工者在施工过程中身体会受到很大的伤害。
装修中产生的甲醛与危害:室内各种人造板材(刨花板、密度板、纤维板、胶合板等)中由于使用了脲醛树脂粘合剂，因而可含有甲醛；新式家具的制作，墙面、地面的装饰铺设，都要使用粘合剂；凡是大量使用粘合剂的地方，总会有甲醛释放；此外，某些化纤地毯、油漆涂料也含有一定量的甲醛。优质的腻子粉属天然无机矿物，附着力好，并无毒害。低端腻子粉需在调配时加胶，分解时释放大量有害物质，危及施工人员及住户健康。
家装中使用腻子粉的主要目的是填充施工面的孔隙及矫正施工面的曲线偏差，为获得均匀、光滑的基底打好基础，腻子粉是链接水泥基底层和乳胶漆的中间层，目前墙面出现的脱落、粉变、湿斑等几乎都是腻子粉质量引起的，因此腻子粉的质量关系到整个墙体装饰的成败。现有的所有需要做基层找平(包含墙布墙纸基层、水泥砂浆、石膏板、防潮板、木板等)，找平材料都是由水泥基或者石膏基找平腻子来进行找平或修补填充，其方式都一直存在非常冲突的矛盾问题，都存在一个共性就是硬度低，易返潮、易空鼓、易开裂、易发霉及甲醛超标等弊病一直困扰着所有用户，更限制着整个装饰行业的发展！因为涂装的下一流程的施工对基底的平整度及附着力有一定要求，若基材太硬就无法进行打磨，如果不打磨刮痕就无法消失，针对乳胶漆饰面、艺术涂料饰面、墙纸墙布饰面都无法实施，故而只有将基层硬度降低，退而求其次，即形成行业现状！因此要提升腻子粉在涂装领域的高效利用，必须改变腻子基层的性能。
专利文件《一种免打磨腻子膏》(专利申请号：201911160822.5)，其公开了一种免打磨腻子膏，其在有益效果部分声称其无需打磨工艺，施工者省时省工，可避免传统腻子粉存在的产生的粉尘污染破坏空气，危害施工者身体健康。但是，该技术方案并没有公开具体的技术手段来实现免打磨的技术效果。
发明内容
针对现有技术中存在的缺陷，本发明的目的在于提供一种免打磨的基面找平腻子膏，主要通过采用复合化技术对产品的本身结构进行改革创新，使之在常态及高温分解时均无毒性，化学安定性高，且圆形且无棱角的砂粒状的填料具有硬度和乳液的弹性进行物理反应，使产品的柔韧性大幅度提高，腻子膏中使用的带质感的砂粒目数可以调节批刮找平厚度与平整度，乳液可以提升批刮顺畅度，保湿剂可以延长干燥时间，批刮时可以重复收光、压平腻子的表面层，腻子膏还具有收缩性，干燥后细微刮痕可自然修复，且在外力作用下发生弹性式塑性变形而使表面抗基层龟裂，光滑的腻子表面无接头痕迹即无需进行砂纸打磨，同时起到抗霉、抗裂、防潮、防起皮、防空鼓、无甲醛成品后平整度极高的基层找平材料。另外，还通过对产品结构的改革创新，进而简化了施工步骤，让施工工艺更简单便捷，大大的降低了施工成本，由原来的8～10遍工艺步骤(例如石膏板基面：钉孔防锈处理—石膏填缝—涂刷白乳胶—粘贴牛皮纸或者网格带—刮涂找平腻子2～3遍—打磨砂纸—涂刷抗碱底漆)，本发明只需要三遍工艺即可：钉孔及接缝处理—刮涂2遍本发明的腻子膏，简化了大量繁琐的施工工艺。
为达到以上目的，本发明采取的技术方案是：一种免打磨的腻子膏，由以下重量份的组份组成：填料25-65份，水性丙烯酸乳液18-45 份，钛白粉2-8份，羧甲基纤维素7-15份，膨润土2-5份，木质纤维2-25份，消泡剂0.5-3份，增稠剂1-23份，润湿剂1-3份，成膜助剂0.2-5份，负离子粉3-23份，电气石1-17份中空玻璃微珠3-8份，去离子水18-40份。
在上述技术方案的基础上，由以下重量份的组份组成：矿物填料 30-60份，水性丙烯酸乳液20-40份，钛白粉3-8份，羧甲基纤维素 8-15份，膨润土3-5份，木质纤维3-8份，消泡剂1-3份，增稠剂12-23 份，润湿剂1-3份，成膜助剂1-3份，负离子粉3-5份，电气石1-3份，中空玻璃微珠3-8份，去离子水20-30份。
在上述技术方案的基础上，所述矿物填料为目数180目且打磨去棱角后的圆形砂粒，白度不小于60。
在上述技术方案的基础上，由以下重量份的组份组成：石英砂 25-50份，水性丙烯酸弹性乳液18-35份，钛白粉5-7份，羧甲基纤维素7-12份，膨润土3-5份，木质纤维15-25份，消泡剂0.5-1.5份，增稠剂5-8份，润湿剂1-3份，成膜助剂0.2-2份，负离子粉8-12份，电气石5-8份，中空玻璃微珠3-8份，去离子水18-28份。
在上述技术方案的基础上，所述石英砂为目数100目且打磨去棱角后的圆形砂粒，白度不小于60。
在上述技术方案的基础上，由以下重量份的组份组成：重质碳酸钙40-65份，水性丙烯酸乳液30-45份，钛白粉2-3份，羧甲基纤维素5-10份，膨润土2-4份，木质纤维2-5份，消泡剂0.5-2份，增稠剂1-3份，润湿剂1-3份，成膜助剂2-5份，负离子粉15-23份，电气石12-17份，中空玻璃微珠3-8份，去离子水30-40份。
在上述技术方案的基础上，所述重质碳酸钙为目数60目且打磨去棱角后的圆形砂粒，白度不小于60。
在上述技术方案的基础上，所述重质碳酸钙为白云石。
本发明的有益效果在于：
本发明从行业现状来说，其改革性的创新解决了装饰领域中生产者、施工者和用户一直无法避免的粉尘污染和打磨及清洁等通病问题，提升了装饰性能和实用性价值；从环保节能角度来说，该产品从生产到运输及施工均可达到无粉尘操作流程，其特性是刮涂顺畅、易施工、平整度高、施工成品后无刮涂痕迹，无需打磨、无粉尘、为节能减排，保护环境的促进做出巨大贡献。从经济价值来讲，产品的创新附带着施工工艺改革，至少节省4～6遍工艺创新，为广大用户带来巨大的经济价值，从健康角度来看讲，让所有相关从业人员，从传统腻子粉的生产—搬运—施工—打磨—卫生清理等过程中产生的灰尘粉尘对人体的伤害，在本发明中完全杜绝。
附图说明
图1为传统腻子与本发明免打磨的腻子膏的平整度及抗裂对比图。
具体实施方式
下面结合说明书的附图，通过对本发明的具体实施方式作进一步的描述，使本发明的技术方案及其有益效果更加清楚、明确。下面通过参考附图描述实施例是示例性的，旨在解释本发明，而不能理解为对本发明的限制。
本发明提供了一种免打磨的腻子膏，由以下重量份的组份组成：填料25-65份，水性丙烯酸乳液18-45份，钛白粉2-8份，羧甲基纤维素7-15份，膨润土2-5份，木质纤维2-25份，消泡剂0.5-3份，增稠剂1-23份，成膜助剂0.2-5份，负离子粉3-23份，电气石1-17份，去离子水18-40份。具体的，成膜助剂为Texanol，杀菌剂为CMIT/MIT，增稠剂为HEUR。
下面通过三个实施例对本发明作进一步说明。
实施例一
一种免打磨的腻子膏，由以下重量份的组份组成：矿物填料30-60 份，水性丙烯酸乳液20-40份，钛白粉3-8份，羧甲基纤维素8-15份，膨润土3-5份，木质纤维3-8份，消泡剂1-3份，增稠剂12-23份，成膜助剂1-3份，负离子粉3-5份，电气石1-3份，中空玻璃微珠3-8 份，去离子水20-30份。
本实施例中，矿物砂填料需具有一定的透气性，采用的矿物填料目数为180目，且需打磨去棱角后的圆形砂粒，白度达到60即可，其他指标均无要求，选材简单，只需将其加工后的圆形无棱角特征，制备方法简便，先将以上配和比的比例在反应釜中，以600-800转速混合，将混合料与矿物填料混合，静置60分钟形成该找平腻子膏，其优点在于易刮涂、光面找平、细找平、施工无刮涂痕迹，成品后具有超强的抗裂、抗霉、防潮防水效果和超细找平效果。
实施例二
一种免打磨的腻子膏，由以下重量份的组份组成：石英砂25-50 份，水性丙烯酸弹性乳液18-35份，钛白粉5-7份，羧甲基纤维素7-12 份，膨润土3-5份，木质纤维15-25份，消泡剂0.5-1.5份，增稠剂 5-8份，成膜助剂0.2-2份，负离子粉8-12份，电气石5-8份，中空玻璃微珠3-8份，去离子水18-28份。
成份中采用的石英砂，目数为100目，且需打磨去棱角后的圆形砂粒，白度达到60即可，其他指标均无要求，选材简单，只需将其加工后的圆形无棱角特征，制备方法简便，先将以上配和比的比例在反应釜中，以600-800转速混合，将混合料与石英砂混合，静置60 分钟形成该找平腻子膏，其优点在于易刮涂、家装基层找平、常规基层找平、施工无刮涂痕迹、成品后具有超强的抗裂、抗霉、防潮性、柔韧效果和找平效果。
实施例三
一种免打磨的腻子膏，由以下重量份的组份组成：重质碳酸钙 40-65份，水性丙烯酸乳液30-45份，钛白粉2-3份，羧甲基纤维素 5-10份，膨润土2-4份，木质纤维2-5份，消泡剂0.5-2份，增稠剂 1-3份，成膜助剂2-5份，负离子粉15-23份，电气石12-17份，中空玻璃微珠3-8份，去离子水30-40份。
成份中采用白云石，目数为60目，且需打磨去棱角后的圆形砂粒，白度达到60即可，其他指标均无要求，选材简单，只需将其加工后的圆形无棱角特征，制备方法简便，先将以上配和比的比例在反应釜中，以600-800转速混合，将混合料与白云石混合，静置60分钟形成该找平腻子膏，其优点在于易刮涂、粗找平、基础找平、水泥砂浆基面找平、施工无刮涂痕迹、成品后具有超强的抗裂、抗霉、防潮防水效果和找平效果，还可以释放负离子和空气中的氧气结合形成负氧离子，起到净化空气的作用。
参见图1所示，传统腻子与本发明免打磨的腻子膏的平整度及抗裂对比。
图中传统腻子为目前市面上现有的腻子粉配方，按质量比例如下：水泥或者氢氧化钙1-3份、白云石粉7-9粉、氢丙基纤维素0.02-0.05 份、可分散乳胶粉0.06-0.12份，其制备方法直接将各成分混合均匀后，装成20-40kg袋装，使用时以7:3加水搅拌成糊状再进行刮涂。图中新产品为本发明免打磨的腻子膏20-30kg桶装、膏状，开通后直接使用。
性能测试实验
测试方法：按照实施例1-3的配比制得腻子膏的性能进行测试，按照GB18582-2020和JG/T298-2020(耐水型N)的标准，对有害物质和物理性进行检测，结果见表1。
表1有害物质含量检测结果
从以上表可以看出，实施例1-3的实际有害物质指标含量均远低于GB18582-2020的要求标准，因此采用本发明的组分比例既能提升使用年限，为用户创造价值，还能起到保护环境的作用，其释放负离子还具有净化空气的效应，是更适合现代人理想生活环境中刚需产品。
本发明3个实施例施工性及其他性能检测：
表2物理性能检测结果
由表2检测结果可见，利用上述腻子膏，使用性简便，可减少从生产、运输、到现场混合及打磨过程中产生的大量粉尘，既减少能源浪费，还减少对环境的污染，才是真正的节能减排产品；其施工性、抗裂性、耐水性、耐碱性、平整度对标和JG/T298-2020(耐水型N) 的标准，上述产品都得到了更高质量标准的提升。
本发明施工工艺与现市面上腻子粉施工工艺对比：
表3施工工艺步骤对比结果
从上表3可以得出结论：使用目前市面上的传统腻子粉施工工艺步骤至少8-10遍，工艺繁琐，粘贴接缝带时采用的白乳胶甲醛含量高、打磨时粉尘大涂刷底漆对腻子硬度要求高等难题；故而采用本发明腻子膏，直接省去打磨环节，减少在打磨过程中粉尘对施工人员身体不可避免的伤害，为维护从业人员的健康在行业中做出巨大贡献，本发明办法在整个基层找平工艺中，只需要3遍工艺，直接节省下5 遍以上施工工艺，平整度及最终效果还得到提升，产品的创新带来工艺创新，节省了大量繁琐无用工艺，将为所有用户及社会带来巨大的经济价值。
本发明优点在于：
1、本发明腻子膏施工时不需要再行添加水及胶水调配，及其它辅助设备进行混合，开桶即可直接使用，降低了施工成本，杜绝了胶水分解时释放的有害物质，常温及高温分解时均无毒性。
2、生产工艺为集中调配搅拌制备，可杜绝拌料过程常常出现的因搅拌不均匀或是太稀太稠等造成的施工后产品的品质稳定性受到影响等一系列问题。
3、无需打磨工艺，施工者省时省工，打开包装直接施工可避免传统腻子粉存在的在拌料过程中或产生粉尘，破坏空气，危害施工者身体健康；
4、施工后成镜面状态时，附着力高，无需打磨直接进行喷漆工序；
5、纯天然物质，打开包装无异味、存诸期可达6个月:6、膏体细腻润滑，刮痕收刀1-2刀，优越的批刮性能，施工者可节省体力提高效率；
6、施工过程中途终止，再接头无需要打案后施工，喷少量水后施工无衔接痕迹；
7、具有环保功能，吸甲醛，防静电、除雾露等功能，利于居住者身体健康；
8、具有防潮功能，南风天回潮墙面不出水。
9、胶结材料使用弹性建筑乳液，具备真实意义上的弹性性状，抗基层龟裂，大大节约了整体墙面的保养成本。
在说明书的描述中，参考术语“一个实施例”、“优选地”、“示例”、“具体示例”或“一些示例”等的描述意指结合该实施例或示例描述的具体特征、结构、材料或者特点，包含于本发明的至少一个实施例或示例中，在本说明书中对于上述术语的示意性表述不一定指的是相同的实施例或示例。而且，描述的具体特征、结构、材料或者特点可以在任何的一个或多个实施例或者示例中以合适方式结合。
本发明不局限于上述实施方式，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也视为本发明的保护范围之内。本说明书中未作详细描述的内容属于本领域专业技术人员公知的现有技术。
Claims (8)
1.一种免打磨的腻子膏，其特征在于，由以下重量份的组份组成：
填料25-65份，
水性丙烯酸乳液18-45份，
钛白粉2-8份，
羧甲基纤维素7-15份，
膨润土2-5份，
木质纤维2-25份，
消泡剂0.5-3份，
增稠剂1-23份，
成膜助剂0.2-5份，
负离子粉3-23份，
电气石1-17份，
中空玻璃微珠3-8份，
去离子水18-40份。
2.如权利要求1所述的免打磨的腻子膏，其特征在于，由以下重量份的组份组成：
矿物填料30-60份，
水性丙烯酸乳液20-40份，
钛白粉3-8份，
羧甲基纤维素8-15份，
膨润土3-5份，
木质纤维3-8份，
消泡剂1-3份，
增稠剂12-23份，
成膜助剂1-3份，
负离子粉3-5份，
电气石1-3份，
中空玻璃微珠3-8份，
去离子水20-30份。
3.如权利要求2所述的免打磨的腻子膏，其特征在于：所述矿物填料为目数180目且打磨去棱角后的圆形砂粒，白度不小于60。
4.如权利要求1所述的免打磨的腻子膏，其特征在于，由以下重量份的组份组成：
石英砂25-50份，
水性丙烯酸弹性乳液18-35份，
钛白粉5-7份，
羧甲基纤维素7-12份，
膨润土3-5份，
木质纤维15-25份，
消泡剂0.5-1.5份，
增稠剂5-8份，
成膜助剂0.2-2份，
负离子粉8-12份，
电气石5-8份，
中空玻璃微珠3-8份，
去离子水18-28份。
5.如权利要求4所述的免打磨的腻子膏，其特征在于：所述石英砂为目数100目且打磨去棱角后的圆形砂粒，白度不小于60。
6.如权利要求1所述的免打磨的腻子膏，其特征在于，由以下重量份的组份组成：
重质碳酸钙40-65份，
水性丙烯酸乳液30-45份，
钛白粉2-3份，
羧甲基纤维素5-10份，
膨润土2-4份，
木质纤维2-5份，
消泡剂0.5-2份，
增稠剂1-3份，
成膜助剂2-5份，
负离子粉15-23份，
电气石12-17份，
中空玻璃微珠3-8份，
去离子水30-40份。
7.如权利要求6所述的免打磨的腻子膏，其特征在于：所述重质碳酸钙为目数60目且打磨去棱角后的圆形砂粒，白度不小于60。
8.如权利要求7所述的免打磨的腻子膏，其特征在于：所述重质碳酸钙为白云石。