CN115353358B - Negative oxygen ion health mud for purifying air, preventing condensation and inhibiting bacteria and preparation method thereof - Google Patents

Negative oxygen ion health mud for purifying air, preventing condensation and inhibiting bacteria and preparation method thereof Download PDF

Info

Publication number
CN115353358B
CN115353358B CN202211062452.3A CN202211062452A CN115353358B CN 115353358 B CN115353358 B CN 115353358B CN 202211062452 A CN202211062452 A CN 202211062452A CN 115353358 B CN115353358 B CN 115353358B
Authority
CN
China
Prior art keywords
powder
negative
negative ion
hydrophobic
aerogel particles
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN202211062452.3A
Other languages
Chinese (zh)
Other versions
CN115353358A (en
Inventor
王武成
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mulin Health Negative Oxygen Ion Medical Building Materials Shenzhen Group Co ltd
Original Assignee
Mulin Health Negative Oxygen Ion Medical Building Materials Shenzhen Group Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mulin Health Negative Oxygen Ion Medical Building Materials Shenzhen Group Co ltd filed Critical Mulin Health Negative Oxygen Ion Medical Building Materials Shenzhen Group Co ltd
Priority to CN202211062452.3A priority Critical patent/CN115353358B/en
Publication of CN115353358A publication Critical patent/CN115353358A/en
Application granted granted Critical
Publication of CN115353358B publication Critical patent/CN115353358B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses an air-purifying anti-condensation bacteriostatic negative oxygen ion healthy mud and a preparation method thereof, wherein the air-purifying anti-condensation bacteriostatic negative oxygen ion healthy mud comprises the following components in parts by weight: 15 to 50 portions of white cement, 15 to 50 portions of sierozem powder, 20 to 60 portions of coarse whiting powder and 6 to 20 portions of negative ion source. When the negative oxygen ion healthy mud for purifying air, preventing condensation and inhibiting bacteria is used, only a proper amount of water needs to be added for blending to form aqueous slurry, the hydrophobic adhesive covers the aerogel particles, so that the surface of the negative ion source forms a hydrophobic layer, the negative ion source has power moving towards the surface in the aqueous slurry in the drying process of the aqueous slurry, and after the aqueous slurry is dried to form a coating, the content of the negative ion source on the surface of the coating is larger than that in the coating.

Description

Negative oxygen ion health mud for purifying air, preventing condensation and inhibiting bacteria and preparation method thereof
Technical Field
The invention relates to the field of coatings, in particular to negative oxygen ion health mud for purifying air, preventing condensation and inhibiting bacteria.
Background
With the acceleration of industrialization and urbanization processes, the problem of human living environment pollution is increasingly prominent, and especially with the common application of industrial decoration materials, a large amount of chemical decoration materials and chemical building materials enter the room, the use of household appliances, the tight closing of doors and windows and other problems cause rare negative ions in the indoor air, increase of harmful organic pollutants such as formaldehyde and the like, and great influence is generated on human health.
The air negative oxygen ions can effectively inhibit the growth of bacteria and degrade organic pollutants, the concentration of the air negative ions is listed as an important index for measuring the quality of air in environmental evaluation, and the content of the air negative ions is closely related to the cleanliness of the air. In addition, the research of medical scientists shows that the health care effect and the auxiliary curative effect of the air negative ions on human bodies are related to the concentration of the air negative ions. When the concentration of negative ions is more than or equal to that of positive ions, people can feel comfortable, and the concentration of negative ions in the air reaches 700/cm 3 The above-mentioned raw materials are good for human health, and when the concentration is up to 1 ten thousand/cm 3 The above-mentioned diseases can be cured, and has auxiliary therapeutic action for several diseases, so that it is known as "air vitamin" and "longevity element in atmosphere".
Anion materials such as monazite, hexacyclic stone, tourmaline, vermiculite and artificial anion powder have the function of releasing negative oxygen ions, and the anion mud containing the materials can continuously release the negative oxygen ions and decompose formaldehyde, can purify air for a long time, and is increasingly sought in recent years.
In the coating formed after the negative ion coating is coated, negative oxygen ions released by the negative ion material in the coating are difficult to release into the air, and generally only the negative ion material on the surface of the coating can effectively release the released negative oxygen ions into the air, so that the negative ion material in the coating is wasted.
Disclosure of Invention
Based on the above, it is necessary to provide negative oxygen ion health mud for purifying air, preventing condensation and inhibiting bacteria.
In addition, a preparation method of the negative oxygen ion health mud for purifying air, preventing condensation and inhibiting bacteria is also necessarily provided.
The negative oxygen ion health mud for purifying air, preventing condensation and inhibiting bacteria comprises the following components in parts by mass: 15 to 50 parts of white cement, 15 to 50 parts of ash calcium powder, 20 to 60 parts of heavy calcium powder and 6 to 20 parts of negative ion source;
the negative ion source comprises aerogel particles, a negative ion powder and a hydrophobic adhesive, wherein the negative ion powder is filled in pores of the aerogel particles, the hydrophobic adhesive is used for gluing the negative ion powder and the hydrophobic adhesive, and the hydrophobic adhesive covers the outside of the aerogel particles.
In one embodiment, the particle size of the negative ion source is 10-200 μm, and the particle size of the negative ion powder is 1-10 μm.
In one embodiment, the mass ratio of the aerogel particles to the negative ion powder is 1:5 to 20.
In one embodiment, the aerogel particles are aerogel particles with a porosity of 80% to 95%, the anion powder is at least one of monazite powder, hexacyclic ring stone powder, tourmaline powder, vermiculite powder and artificial anion powder, and the hydrophobic binder is soluble in a volatile organic solvent.
In one embodiment, the negative ion source is prepared by:
dissolving the hydrophobic adhesive in the volatile organic solvent to obtain hydrophobic glue;
uniformly mixing the aerogel particles and the negative ion powder to enable the negative ion powder to be filled in pores of the aerogel particles to obtain a mixture, wherein the particle size of the aerogel particles is 10-200 microns, and the particle size of the negative ion powder is 1-10 microns;
adding the hydrophobic glue into the mixture, fully mixing, drying and carrying out heat treatment to obtain a semi-finished product;
and crushing the semi-finished product to obtain the negative ion source.
In one embodiment, in the hydrophobic glue, the mass ratio of the hydrophobic adhesive to the volatile organic solvent is 0.8-2: 1, the hydrophobic adhesive is phenolic resin, and the volatile organic solvent is at least one selected from ethanol, propanol, acetone and butanol.
In one embodiment, said adding of said hydrophobic glue to said mixture is: under the stirring state, the hydrophobic glue is sprayed on the mixture for multiple times, and the ratio of the mixture to the hydrophobic glue is 100g:1mL to 3mL.
In one embodiment, the temperature of the heat treatment is 140-180 ℃, and the time of the heat treatment is 5-15 min.
In one embodiment, the white cement has a particle size of 10 to 100 μm, the sierozem powder has a particle size of 10 to 100 μm, and the coarse whiting powder has a particle size of 2 to 20 μm.
The preparation method of the negative oxygen ion health mud for purifying air, preventing condensation and inhibiting bacteria comprises the following steps:
according to the mass ratio, 15 to 50 parts of white cement, 15 to 50 parts of ash calcium powder and 20 to 60 parts of heavy calcium powder are uniformly mixed, 6 to 20 parts of negative ion source is added and uniformly mixed again, and the negative oxygen ion healthy mud with the functions of air purification, moisture condensation prevention and bacteriostasis is obtained.
When the negative oxygen ion healthy mud for purifying air, preventing condensation and inhibiting bacteria is used, only a proper amount of water needs to be added for blending to form aqueous slurry, the hydrophobic adhesive covers the outside of aerogel particles, so that a hydrophobic layer is formed on the surface of the negative ion source, the negative ion source has power moving towards the surface in the aqueous slurry in the drying process of the aqueous slurry, and meanwhile, the negative ion powder is filled in pores of the aerogel particles.
Compared with the traditional negative ion coating, the negative oxygen ion healthy mud for purifying air, preventing condensation and inhibiting bacteria forms relatively fewer negative ion sources wasted in the coating.
The negative ion source of the negative oxygen ion healthy mud for purifying air, preventing condensation and inhibiting bacteria can release negative oxygen ions, decompose toxic and harmful substances such as formaldehyde, VOC and the like in air, settle PM2.5, remove peculiar smell and achieve the aim of purifying air.
In addition, negative oxygen ions also have certain bacteriostatic action, and when indoor humidity was too high, the moisture that the aerogel granule can also absorb in the air was stored in the hole simultaneously, and when humidity was crossed lowly, the moisture of storing in the hole before can releasing again, thereby played the effect of antisweat.
Drawings
In order to more clearly illustrate the embodiments of the present invention or the technical solutions in the prior art, the drawings used in the embodiments or the prior art descriptions will be briefly described below, it is obvious that the drawings in the following description are only some embodiments of the present invention, and other drawings can be obtained by those skilled in the art without creative efforts.
Wherein:
fig. 1 is a schematic sectional structure view of a coating layer formed by negative oxygen ion health mud for air purification, anti-condensation and bacteriostasis according to an embodiment, wherein o in the figure is a negative ion source.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the drawings in the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
The invention discloses negative oxygen ion health mud for purifying air, preventing condensation and inhibiting bacteria, which comprises the following components in parts by weight: 15 to 50 portions of white cement, 15 to 50 portions of sierozem powder, 20 to 60 portions of coarse whiting powder and 6 to 20 portions of negative ion source.
The anion source comprises aerogel particles, anion powder and a hydrophobic adhesive, wherein the anion powder is filled in pores of the aerogel particles, the hydrophobic adhesive is used for gluing the anion powder and the hydrophobic adhesive, and the hydrophobic adhesive covers the outside of the aerogel particles.
When the negative oxygen ion healthy mud for purifying air, preventing condensation and inhibiting bacteria is used, only a proper amount of water needs to be added for blending to form water-based slurry, the hydrophobic adhesive covers the outside of the aerogel particles, so that the surface of the negative ion source forms a hydrophobic layer, the negative ion source has power moving towards the surface in the water-based slurry in the drying process, and meanwhile, the negative ion powder is filled in the pores of the aerogel particles. Referring to fig. 1, when the aqueous slurry is dried to form a coating, the content of the negative ion source on the surface of the coating is greater than that in the interior of the coating.
Compared with the traditional negative ion coating, the negative oxygen ion healthy mud for purifying air, preventing condensation and inhibiting bacteria forms relatively fewer negative ion sources wasted inside the coating.
The negative ion source of the negative oxygen ion healthy mud for purifying air, preventing condensation and inhibiting bacteria can release negative oxygen ions, decompose toxic and harmful substances such as formaldehyde, VOC and the like in air, settle PM2.5, remove peculiar smell and achieve the aim of purifying air.
In addition, negative oxygen ions also have certain bacteriostatic action, and when indoor humidity was too high, the moisture that the aerogel granule can also absorb in the air was stored in the hole simultaneously, and when humidity was crossed lowly, the moisture of storing in the hole before can releasing again, thereby played the effect of antisweat.
Preferably, in the present embodiment, the particle size of the negative ion source is 10 μm to 200 μm, and the particle size of the negative ion powder is 1 μm to 10 μm.
Preferably, in the present embodiment, the mass ratio of the aerogel particles to the negative ion powder is 1:5 to 20.
Preferably, in this embodiment, the aerogel particles are aerogel particles with a porosity of 80% to 95%, the anion powder is at least one of monazite powder, hexacyclic stone powder, tourmaline powder, vermiculite powder and artificial anion powder, and the hydrophobic binder is soluble in the volatile organic solvent.
Specifically, the aerogel particles can be silica aerogel particles.
Specifically, in the present embodiment, the negative ion source is prepared by:
dissolving a hydrophobic adhesive in a volatile organic solvent to obtain hydrophobic glue;
uniformly mixing the aerogel particles and the negative ion powder to enable the negative ion powder to be filled in pores of the aerogel particles to obtain a mixture;
adding hydrophobic glue into the mixture, fully mixing, drying and carrying out heat treatment to obtain a semi-finished product;
and crushing the semi-finished product to obtain the negative ion source.
Wherein the grain diameter of the aerogel particles is 10-200 μm, and the grain diameter of the anion powder is 1-10 μm.
The particle size of the anion powder is much smaller than that of the aerogel particles, so that the anion powder can be filled in the pores of the aerogel particles.
Preferably, in the hydrophobic glue, the mass ratio of the hydrophobic adhesive to the volatile organic solvent is 0.8-2: the hydrophobic adhesive is phenolic resin, and the volatile organic solvent is at least one of ethanol, propanol, acetone and butanol.
In other embodiments, other organic glues may be selected for the hydrophobic binder, as long as they are soluble in volatile organic solvents and hydrophobic.
In order to reduce the content of the hydrophobic binder in the negative ion source, it is preferable that the operation of adding the hydrophobic glue to the mixture in the present embodiment is: under the stirring state, spraying the hydrophobic glue on the mixture for multiple times (three to five times), wherein the ratio of the mixture to the hydrophobic glue is 100g:1mL to 3mL.
The purpose of drying is to fully volatilize the volatile organic solvent, and the heat treatment can further ensure that the volatile organic solvent is fully volatilized on one hand, and can also cure the phenolic resin on the other hand, and the cured phenolic resin has higher stability, and has better hydrophobicity and adhesiveness.
Preferably, in the present embodiment, the heat treatment temperature is 140 to 180 ℃ and the heat treatment time is 5 to 15min.
In this embodiment, the white cement has a particle size of 10 to 100 μm, the sierozem powder has a particle size of 10 to 100 μm, and the triple superphosphate powder has a particle size of 2 to 20 μm.
Preferably, in other embodiments, the negative oxygen ion health mud for purifying air, preventing condensation and inhibiting bacteria further comprises 5 to 20 parts by weight of kaolin.
The kaolin can generate a three-dimensional network space polymer with a basic structure of-Si-O-Al-O-, so that the negative oxygen ion healthy mud for purifying air, preventing condensation and inhibiting bacteria has better integrity.
The invention also discloses a preparation method of the negative oxygen ion health mud for purifying air, preventing condensation and inhibiting bacteria, which comprises the following steps:
according to the mass ratio, 15 to 50 parts of white cement, 15 to 50 parts of ash calcium powder and 20 to 60 parts of heavy calcium powder are uniformly mixed, 6 to 20 parts of negative ion source is added and uniformly mixed again, and the negative oxygen ion healthy mud with the functions of air purification, moisture condensation prevention and bacteriostasis is obtained.
The following are specific examples.
Materials: phenolic resin (purchased from zhongwei new materials science ltd, product number 12041), hexacyclic stone (purchased from the guo long mineral processing plant in lingshou county, product number sl-24), silica aerogel powder (purchased from the needleless science and technology group hebei ltd, product number 008, customized fineness 80 μm, porosity 90%), white cement (purchased from albobo cement, product number bsn001, fineness 80 μm), ash calcium powder (purchased from houzhong hou zhong new materials ltd, product number SSH, mesh number 300), and heavy calcium powder (purchased from guangdong sen new industry and trade ltd, product number ST-6180, mesh number 5000).
Equipment: AN-500 model air negative (oxygen) ion detector (purchased from Chongqing En environmental technology Co., ltd.).
Example 1
According to the mass ratio of 1:1, dissolving phenolic resin in ethanol to obtain the phenolic resin glue.
And crushing the hexacyclic ring stone, and then sieving the crushed hexacyclic ring stone with a 5000-mesh sieve to obtain hexacyclic ring stone powder.
According to the mass ratio of 1: and 11, uniformly mixing the silicon dioxide aerogel powder and the anion powder in a stirrer to ensure that the anion powder is filled in the pores of the aerogel particles to obtain a mixture.
Spraying the same amount of phenolic resin glue to the mixture for three times under stirring, fully mixing, drying, and performing heat treatment at 160 ℃ for 6min to obtain a semi-finished product. Wherein, the proportion of the mixture and the hydrophobic glue (total amount) is 100g:3mL.
And (4) crushing the semi-finished product, and sieving the crushed semi-finished product through a 800-mesh sieve to obtain the negative ion source.
Example 2
Mixing white cement 150g, sierozem powder 500g and coarse whiting powder 200g, then 200g of the negative ion source prepared in the example 1 is added and uniformly mixed again to obtain the negative oxygen ion health mud for purifying air, preventing condensation and inhibiting bacteria.
Example 3
500g of white cement, 150g of sierozem powder and 600g of coarse whiting powder are uniformly mixed, 60g of the negative ion source prepared in example 1 is added and uniformly mixed again, and the negative oxygen ion healthy mud for purifying air, preventing condensation and inhibiting bacteria is obtained.
Example 4
300g of white cement, 300g of sierozem powder and 400g of coarse whiting powder are uniformly mixed, and then 120g of the negative ion source prepared in example 1 is added and uniformly mixed again to obtain the negative oxygen ion healthy mud for purifying air, preventing condensation and inhibiting bacteria.
Comparative example 1
300g of white cement, 300g of sierozem powder and 400g of coarse whiting powder are mixed uniformly, and then 110g of the hexacyclic stone powder prepared in example 1 is added and mixed uniformly again to obtain the negative oxygen ion cement.
Test example
50g of the negative oxygen ion health mud prepared in the examples 2 to 4 and the negative oxygen ion mud prepared in the comparative example 1 are mixed into slurry according to the mud-water ratio of 1.2g/1mL, the slurry is uniformly coated on a cement board of 10cm multiplied by 10cm, the negative ion release amount per unit area is detected by AN AN-500 type air negative (oxygen) ion detector on the 3 rd day, the 10 th day and the 20 th day respectively, and the measurement results are shown in the following table 1.
Table 1: unit area (cm) 2 ) Release amount of negative ion
Example 2 Example 3 Example 4 Comparative example 1
Day 3 28751 12235 19548 13751
Day 10 29675 12246 19346 12875
Day 20 29140 12420 19123 13247
In combination with table 1, it can be seen that the coatings formed by the negative oxygen ion healthy mud for air purification, dewing prevention and bacteriostasis prepared in examples 2 to 4 can efficiently and stably release negative ions with higher concentration.
Comparing example 4 with comparative example 1, it can be seen that, under the condition that the dosage of the hexacyclic rock powder is close, the negative ion release amount of the coating formed by the negative oxygen ion healthy mud for purifying air, preventing condensation and inhibiting bacteria is obviously higher than that of the coating formed by the negative oxygen ion healthy mud prepared in comparative example 1.
The above-mentioned embodiments only express several embodiments of the present invention, and the description thereof is more specific and detailed, but not construed as limiting the claims. It should be noted that, for a person skilled in the art, several variations and modifications can be made without departing from the inventive concept, which falls within the scope of the present invention. Therefore, the protection scope of the present patent shall be subject to the appended claims.

Claims (5)

1. The negative oxygen ion health mud is characterized by comprising the following components in parts by mass: 15 to 50 parts of white cement, 15 to 50 parts of ash calcium powder, 20 to 60 parts of heavy calcium powder and 6 to 20 parts of negative ion source;
the negative ion source comprises aerogel particles, a negative ion powder and a hydrophobic adhesive, wherein the negative ion powder is filled in pores of the aerogel particles, the hydrophobic adhesive is used for bonding the negative ion powder and the hydrophobic adhesive, and the hydrophobic adhesive covers the outside of the aerogel particles;
the particle size of the negative ion source is 10-200 mu m, and the particle size of the negative ion powder is 1-10 mu m;
the mass ratio of the aerogel particles to the negative ion powder is 1:5 to 20;
the aerogel particles are aerogel particles with the porosity of 80% -95%, the anion powder is at least one of monazite powder, hexacyclic stone powder, tourmaline powder, vermiculite powder and artificial anion powder, and the hydrophobic adhesive can be dissolved in a volatile organic solvent;
the negative ion source is prepared by the following operations:
dissolving the hydrophobic adhesive in the volatile organic solvent to obtain hydrophobic glue;
uniformly mixing the aerogel particles and the negative ion powder to enable the negative ion powder to be filled in pores of the aerogel particles to obtain a mixture, wherein the particle size of the aerogel particles is 10-200 microns, and the particle size of the negative ion powder is 1-10 microns;
adding the hydrophobic glue into the mixture, fully mixing, drying and carrying out heat treatment to obtain a semi-finished product;
crushing the semi-finished product to obtain the negative ion source;
in the hydrophobic glue, the mass ratio of the hydrophobic adhesive to the volatile organic solvent is (0.8-2): 1, the hydrophobic adhesive is phenolic resin, and the volatile organic solvent is at least one selected from ethanol, propanol, acetone and butanol.
2. The negative oxygen ion health mud for purifying air, preventing condensation and inhibiting bacteria as claimed in claim 1, wherein the operation of adding the hydrophobic glue to the mixture is as follows: under the stirring state, the hydrophobic glue is sprayed on the mixture for multiple times, and the ratio of the mixture to the hydrophobic glue is 100g:1mL to 3mL.
3. The negative oxygen ion health mud for purifying air, preventing condensation and inhibiting bacteria as claimed in claim 1, wherein the temperature of the heat treatment is 140-180 ℃, and the time of the heat treatment is 5-15 min.
4. The negative oxygen ion health mud for purifying air, preventing condensation and inhibiting bacteria as claimed in claim 1, wherein the particle size of the white cement is 10-100 μm, the particle size of the ash calcium powder is 10-100 μm, and the particle size of the heavy calcium powder is 2-20 μm.
5. A preparation method of the negative oxygen ion health mud for purifying air, preventing condensation and inhibiting bacteria is characterized by comprising the following steps of:
according to the mass ratio, 15 to 50 parts of white cement, 15 to 50 parts of ash calcium powder and 20 to 60 parts of heavy calcium powder are uniformly mixed, 6 to 20 parts of negative ion source is added and uniformly mixed again, and the negative oxygen ion healthy mud with the functions of air purification, moisture condensation prevention and bacteriostasis is obtained.
CN202211062452.3A 2022-08-31 2022-08-31 Negative oxygen ion health mud for purifying air, preventing condensation and inhibiting bacteria and preparation method thereof Active CN115353358B (en)