CN101696117A - Preparation method for bamboo charcoal health-care ceramic tiles - Google Patents
Preparation method for bamboo charcoal health-care ceramic tiles Download PDFInfo
- Publication number
- CN101696117A CN101696117A CN200910153653A CN200910153653A CN101696117A CN 101696117 A CN101696117 A CN 101696117A CN 200910153653 A CN200910153653 A CN 200910153653A CN 200910153653 A CN200910153653 A CN 200910153653A CN 101696117 A CN101696117 A CN 101696117A
- Authority
- CN
- China
- Prior art keywords
- ceramic tile
- bamboo
- ceramic
- preparation
- charcoal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a preparation method for ceramic tiles, in particular to a preparation method for the ceramic tiles with a health-care function, and discloses a preparation method for bamboo charcoal health-care ceramic tiles. The preparation method comprises the following steps of: 1, uniformly mixing and stirring 1 volume part of bamboo charcoal which has a grain size of 5 to 10 Mum and 1 to 3 volume parts of ceramic clay; 2, pressing the uniformly stirred material to make ceramic tile blanks; 3, drying the ceramic tile blanks in the shade for 12 to 48h; 4, putting the dried ceramic tile blanks in a liquefied gas kiln to heat the dried ceramic tile blanks to 700-1,250 DEG C with naked flame; 5, glazing part of the surface of each ceramic tile product taken out from the kiln, namely the surface of the ceramic tile without being glazed is left; and 6, putting the ceramic tile products with part of the surface thereof glazed into the liquefied gas kiln to heat the ceramic tile products to 700-1,250 DEG C with naked flame until the tile is sintered, and thus forming the bamboo charcoal health-care ceramic tiles. The bamboo charcoal health-care ceramic tiles can guarantee the strength of the ceramic tile and also can fully exert the properties of the bamboo charcoal.
Description
Technical field
The present invention relates to the preparation method of ceramic tile, relate in particular to the preparation method of ceramic tile with nourishing function.
Background technology
Health is the problem that people are concerned about most, yet along with the electrification of working and living, electromagnetic radiation has become the important factor of harm health of people.In addition, the various objectionable impuritiess that discharge in the building and ornament materials also are the important factors of harm health of people.How to make indoor environment more healthy, people more favor the bamboo charcoal product at present.Contain multiple beneficial elements such as charcoal, hydrogen, oxygen mainly due to bamboo charcoal, quality is hard, and fine and closely woven porous can radioprotective, produces negative ion, and various free objectionable impuritiess are decomposed in absorption, and humidity in the surge chamber automatically can also produce the far infrared rays of suitable human body.
With regard to radioprotective, bamboo charcoal can not only be blocked the erosion of the harm ray of various electrical equipment generations, more can absorb this ray, makes human body thoroughly exempt the harm of this harm ray.
With regard to it can produce negative ion, the 4410/m of negative ion that bamboo charcoal produced
3, have stronger penetrance, energy relax human somatic nerves, Ginseng Extract.Bump against at indoor this negative ion and airborne grain diameter thing, make it charged, these charged particle particle diameter things can reach the effect that purifies air easily attached to body surfaces such as wall minute surface, floors, stay wherein just as rippling in the forest of the Nature.
With regard to its absorption capacity of decomposition with regard to, the densification of bamboo charcoal density, than great, hole is many, content of mineral substances is abundant, the every gram of its surface-area is at 500m
2More than, so it has powerful adsorptive power and capacity of decomposition, its adsorptive power ml/g＜iodine number〉88.
5Because it has countless holes, the pore of this carbonaceous can absorb airborne various suspended solid effectively, harmful chemicals such as sulfide, hydride, methyl alcohol, phenol is played absorb the special role of decomposing.In addition, its adsorptive power is more than 10 times of consubstantiality building blocks charcoal, and contained mineral substance is more than 5 times of consubstantiality building blocks charcoal.
With regard to the ability of humidity in its automatic surge chamber, the fine and closely woven porous of bamboo charcoal, specific surface area is big, automatically humidity in the surge chamber.If when ambient humidity was big, it can absorb moisture; If the surrounding environment drying then can discharge moisture.Because its water-intake rate can reach more than 1424%, so it is that humidity prevents the special product that material goes mouldy in the surge chamber.
With regard to its far infrared rays wavelength that can produce the most suitable absorption of human body, the far infrared rays wavelength of suitable absorption of human body of its generation, can make object produce low-grade fever, its far infrared rays emittance is 92%, can promote the activation of human senility cell, strengthen blood circulation. improve the human internal environment, thereby reach practical health-care effect.
At present, people's multiselect is placed in indoor with bamboo charcoal bag or bamboo charcoal artwork, to reach the effect that purifies air.It is indoor that but these products all can only oddly intersperse among, and can't large-arealy use, and therefore the effect that purifies air also is limited.
Ceramic tile is the interior architecture finishing material of using always, and big area is layed in metope or ground.At present people select for use main because its cleaning easily of ceramic tile, maintenance simple, advantage such as be difficult for hiding that dirt, no air pollutant, long service life, fire prevention, waterproof, preservative property are good, environmental protection, moulding are enriched.If bamboo charcoal can be applied to ceramic tile, give full play to the advantage of the two, will be subjected to people's favor.
Name is called " a kind of ceramic tile and manufacture craft thereof ", application artificial " Tang Jianhua ", the applying date is " on 05 27th, 2005 ", application number is " 200510049855.4 ", and the Chinese invention patent application for " on December 21st, 2005 " in open day also discloses a kind of ceramic tile that contains bamboo charcoal and preparation method thereof.It comprises that following raw materials by weight percent fires: golden bank potter's clay 50-70%, Hushan argil 10-25%, bamboo charcoal powder 15-35%.Its manufacture craft comprises that (1) select materials; (2) washing; (3) pugging; (4) moulding; (5) drying; (6) soak glaze; (7) fire, sintering temperature is 1030-1180 ℃.But its preparation method can not be prepared and can give full play to the bamboo charcoal radioprotective, produces negative ion, and various free objectionable impuritiess are decomposed in absorption, and humidity in the surge chamber automatically produces the ceramic tile of the function of the far infrared rays of suitable human body.
Summary of the invention
The present invention is directed to can not preparing of existing in the prior art and give full play to the bamboo charcoal radioprotective, produce negative ion, various free objectionable impuritiess are decomposed in absorption, humidity in the automatic surge chamber, produce the deficiency of the functional bamboo-carbon health-care ceramic tile of the far infrared rays of suitable human body, provide a kind of preparing to give full play to the bamboo charcoal radioprotective, produce negative ion, various free objectionable impuritiess are decomposed in absorption, automatically humidity in the surge chamber produces the preparation method of the bamboo-charcoal health-care ceramic tile of the functional bamboo-carbon health-care ceramic tile of the far infrared rays of suitable human body.
In order to solve the problems of the technologies described above, the present invention is solved by following technical proposals:
The preparation method of bamboo-charcoal health-care ceramic tile, it may further comprise the steps:
The first step in volume parts, is that bamboo charcoal and the 1-3 part ceramic clay of 5-10 μ m mixes stirring with 1 part of grain diameter;
In second step, the material after stirring is pressed into the ceramic tile base substrate;
In the 3rd step, the ceramic tile base substrate was dried in the shade 12-48 hour;
In the 4th step, the ceramic tile base substrate after will drying in the shade is put into liquefied gas kiln naked light and is heated to 700-1250 ℃;
In the 5th step, the ceramic tile goods part surface glazing to behind the kiln discharge promptly leaves not glazed ceramic brick surface;
The 6th step, the glazed ceramic tile goods of part surface are put into liquefied gas kiln naked light be heated to 700-1250 ℃ of sintering, promptly make bamboo-charcoal health-care ceramic tile.
Temperature is set to 700-1250 ℃ in the 4th step and the 6th step, be to prepare to give full play to the bamboo charcoal radioprotective, produce negative ion, various free objectionable impuritiess are decomposed in absorption, automatically humidity in the surge chamber produces the key of the functional bamboo-carbon health-care ceramic tile of the far infrared rays of suitable human body.Ceramic clay can not harden when temperature is lower than 700 ℃, and when temperature surpassed 1250 ℃, the bamboo charcoal molecule lost effect automatically and oxidizes away, and becomes the ceramic honeycomb piece, can not produce the nourishing function of negative ion.
As preferably, the Heating temperature in described the 4th step is 1050-1170 ℃, and the Heating temperature in described the 6th step is 1050-1170 ℃.
As preferably, the Heating temperature in described the 4th step is 1075 ℃, and the Heating temperature in described the 6th step is 1075 ℃.
As preferably, the Heating temperature in described the 4th step is 1100 ℃, and the Heating temperature in described the 6th step is 1100 ℃.
As preferably, the Heating temperature in described the 4th step is 1125 ℃, and the Heating temperature in described the 6th step is 1125 ℃.
As preferably, the Heating temperature in described the 4th step is 1175 ℃, and the Heating temperature in described the 6th step is 1175 ℃.
As preferably, the preparation method of described bamboo-charcoal health-care ceramic tile is characterized in that: the described the first step in volume parts, is that bamboo charcoal and 1.75 parts of ceramic clays of 5-10 μ m mix stirring with 1 part of grain diameter.
As preferably, the preparation method of described bamboo-charcoal health-care ceramic tile is characterized in that: the described the first step in volume parts, is that bamboo charcoal and 2 parts of ceramic clays of 5-10 μ m mix stirring with 1 part of grain diameter.
As preferably, the preparation method of described bamboo-charcoal health-care ceramic tile is characterized in that: the described the first step in volume parts, is that bamboo charcoal and 2.25 parts of ceramic clays of 5-10 μ m mix stirring with 1 part of grain diameter.
As preferably, the preparation method of described bamboo-charcoal health-care ceramic tile is characterized in that: the described the first step in volume parts, is that bamboo charcoal and 2.5 parts of ceramic clays of 5-10 μ m mix stirring with 1 part of grain diameter.
According to technical scheme of the present invention, can prepare and to give full play to the bamboo charcoal radioprotective, produce negative ion, various free objectionable impuritiess are decomposed in absorption, humidity in the automatic surge chamber, produce the functional bamboo-carbon health-care ceramic tile of the far infrared rays of suitable human body, the 700-1250 ℃ of intensity that can guarantee ceramic tile can not make bamboo charcoal oxidized and lose the character that it has again.
Embodiment
Below in conjunction with embodiment the present invention is described in further detail:
Embodiment 1
The preparation method of bamboo-charcoal health-care ceramic tile, it may further comprise the steps:
The first step in volume parts, is that bamboo charcoal and 2 parts of ceramic clays of 5-10 μ m mix stirring with 1 part of grain diameter;
In second step, the material after stirring is pressed into the ceramic tile base substrate;
In the 3rd step, the ceramic tile base substrate was dried in the shade 24 hours;
In the 4th step, the ceramic tile base substrate after will drying in the shade is put into liquefied gas kiln naked light and is heated to 700 ℃;
In the 5th step, the ceramic tile goods part surface glazing to behind the kiln discharge promptly leaves not glazed ceramic brick surface;
The 6th step, the glazed ceramic tile goods of part surface are put into liquefied gas kiln naked light be heated to 700 ℃ of sintering, promptly make bamboo-charcoal health-care ceramic tile.
Embodiment 2
On embodiment 1 basis, Heating temperature in the 4th step and the 6th step is changed into 750 ℃.
Embodiment 3
On embodiment 1 basis, Heating temperature in the 4th step and the 6th step is changed into 800 ℃.
Embodiment 4
On embodiment 1 basis, Heating temperature in the 4th step and the 6th step is changed into 850 ℃.
Embodiment 5
On embodiment 1 basis, Heating temperature in the 4th step and the 6th step is changed into 900 ℃.
Embodiment 6
On embodiment 1 basis, Heating temperature in the 4th step and the 6th step is changed into 950 ℃.
Embodiment 7
On embodiment 1 basis, Heating temperature in the 4th step and the 6th step is changed into 1000 ℃.
Embodiment 8
On embodiment 1 basis, Heating temperature in the 4th step and the 6th step is changed into 1050 ℃.
Embodiment 9
On embodiment 1 basis, Heating temperature in the 4th step and the 6th step is changed into 1075 ℃.
Embodiment 10
On embodiment 1 basis, Heating temperature in the 4th step and the 6th step is changed into 1100 ℃.
Embodiment 11
On embodiment 1 basis, Heating temperature in the 4th step and the 6th step is changed into 1125 ℃.
Embodiment 12
On embodiment 1 basis, Heating temperature in the 4th step and the 6th step is changed into 1150 ℃.
Embodiment 13
On embodiment 1 basis, Heating temperature in the 4th step and the 6th step is changed into 1175 ℃.
Embodiment 14
On embodiment 1 basis, Heating temperature in the 4th step and the 6th step is changed into 1200 ℃.
Embodiment 15
On embodiment 1 basis, Heating temperature in the 4th step and the 6th step is changed into 1225 ℃.
Embodiment 16
On embodiment 1 basis, Heating temperature in the 4th step and the 6th step is changed into 1250 ℃.
Air purification effect test about the bamboo-charcoal health-care ceramic tile made among the embodiment 1-15 is as follows:
1, front and back indoor concentration of formaldehyde and electromagnetic radiation are used in contrast, to characterize its adsorptive power.
In one 10 square metres vacant room, place following article:
1. make 10 on the clamping plate that furniture uses, the surface does not have packing;
2. paint 5 barrels, bung is opened;
3. televisor is 1, opened condition;
4. electric fan is 1, opened condition.
Before bamboo-charcoal health-care ceramic tile used, it was as follows to detect data:
| Concentration of formaldehyde | Benzene concentration | Electromagnetic radiation | Relative humidity |
| 2.8 milligram/cubic meter | 2.5 milligram/cubic meter | 36 milligauss | ??20％ |
The bamboo-charcoal health-care ceramic tile that each embodiment is made used after 48 hours, and it is as follows to detect data:
| Embodiment | Four, six the step in Heating temperature (℃) | Concentration of formaldehyde (mg/m 3) | Benzene concentration (mg/m 3) | Electromagnetic radiation (milligauss) | Relative humidity (%) |
| ??1 | ??700 | ??0.8 | ??0.6 | ??8 | ??39 |
| ??2 | ??750 | ??0.9 | ??0.6 | ??8 | ??39 |
| ??3 | ??800 | ??0.9 | ??0.5 | ??6 | ??41 |
| ??4 | ??850 | ??0.7 | ??0.4 | ??4 | ??42 |
| ??5 | ??900 | ??0.5 | ??0.5 | ??5 | ??42 |
| ??6 | ??950 | ??0.3 | ??0.4 | ??5 | ??43 |
| ??7 | ??1000 | ??0.3 | ??0.3 | ??3 | ??45 |
| ??8 | ??1050 | ??0.1 | ??0.2 | ??3 | ??49 |
| Embodiment | Four, six the step in Heating temperature (℃) | Concentration of formaldehyde (mg/m 3) | Benzene concentration (mg/m 3) | Electromagnetic radiation (milligauss) | Relative humidity (%) |
| ??9 | ??1075 | ??0.1 | ??0.1 | ??2 | ??47 |
| ??10 | ??1100 | ??0.1 | ??0.1 | ??3 | ??50 |
| ??11 | ??1125 | ??0.1 | ??0.2 | ??2 | ??48 |
| ??12 | ??1150 | ??0.1 | ??0.1 | ??3 | ??48 |
| ??13 | ??1175 | ??0.2 | ??0.2 | ??2 | ??45 |
| ??14 | ??1200 | ??0.3 | ??0.2 | ??3 | ??43 |
| ??15 | ??1225 | ??0.5 | ??0.4 | ??4 | ??45 |
| ??16 | ??1250 | ??0.7 | ??0.6 | ??6 | ??40 |
Above-mentioned detection data show that when sintering temperature was 700-1250 ℃, making bamboo-charcoal health-care ceramic tile had significant improvement to room air.
2, Yong Ren sense of smell goes to experience the improvement of the use front and back of bamboo-charcoal health-care ceramic tile to peculiar smell in the air, also characterizes its adsorptive power.
Invite 10 unwitting visitors to enter the meeting room of a residual dense cigarette flavor, point out its sensation to the cigarette taste, but do not inform its purpose, after treating that the visitor leaves, on conference table, place 10 bamboo-charcoal health-care ceramic tiles, invite this 10 people to return to this meeting room after 2 hours again, do not changing under the environment of any air-conditioning, reresent its sensation to the cigarette taste, and require front and back are felt for twice to compare, all the cigarette taste before the expression is obviously eliminated.
Each embodiment has all done above-mentioned similar test, and dense cigarette taste had had tangible elimination before all visitors all represented.
Embodiment 17
On the basis of embodiment 9, the first step is changed into:, be that bamboo charcoal and 1 part of ceramic clay of 5-10 μ m mixes stirring again with 1 part of grain diameter in volume parts.
Embodiment 18
On the basis of embodiment 9, the first step is changed into:, be that bamboo charcoal and 1.5 parts of ceramic clays of 5-10 μ m mix stirring again with 1 part of grain diameter in volume parts.
Embodiment 19
On the basis of embodiment 9, the first step is changed into:, be that bamboo charcoal and 1.75 parts of ceramic clays of 5-10 μ m mix stirring again with 1 part of grain diameter in volume parts.
Embodiment 20
On the basis of embodiment 9, the first step is changed into:, be that bamboo charcoal and 2.25 parts of ceramic clays of 5-10 μ m mix stirring again with 1 part of grain diameter in volume parts.
Embodiment 21
On the basis of embodiment 9, the first step is changed into:, be that bamboo charcoal and 2.5 parts of ceramic clays of 5-10 μ m mix stirring again with 1 part of grain diameter in volume parts.
Embodiment 22
On the basis of embodiment 9, the first step is changed into:, be that bamboo charcoal and 3 parts of ceramic clays of 5-10 μ m mix stirring again with 1 part of grain diameter in volume parts.
The bamboo-charcoal health-care ceramic tile of making among the embodiment 17-22 has also carried out the detection with embodiment 1-16 the same terms, and it is as follows to detect data:
1, front and back indoor concentration of formaldehyde and electromagnetic radiation are used in contrast, and it is as follows to detect data:
| Embodiment | Bamboo charcoal and ceramic clay proportioning in second step | Concentration of formaldehyde (mg/m 2) | Benzene concentration (mg/m 2) | Electromagnetic radiation (milligauss) | Relative humidity (%) |
| ??17 | ??1∶1 | ??0.2 | ??0.3 | ??4 | ??42 |
| ??18 | ??1∶1.5 | ??0.2 | ??0.2 | ??4 | ??45 |
| ??19 | ??1∶1.75 | ??0.1 | ??0.2 | ??3 | ??47 |
| ??20 | ??1∶2.25 | ??0.1 | ??0.1 | ??2 | ??45 |
| ??21 | ??1∶2.5 | ??0.2 | ??0.2 | ??3 | ??43 |
| ??22 | ??1∶3 | ??0.3 | ??0.3 | ??5 | ??43 |
Above-mentioned detection data show that bamboo charcoal and ceramic clay proportioning are 1: 1-1: 3 o'clock, make bamboo-charcoal health-care ceramic tile room air is still had remarkable improvement.
2, dense cigarette taste had had tangible elimination before all visitors all represented.
In a word, the above only is preferred embodiment of the present invention, and all equalizations of being done according to the present patent application claim change and modify, and all should belong to the covering scope of patent of the present invention.
Claims (10)
1. the preparation method of bamboo-charcoal health-care ceramic tile, it is characterized in that: it may further comprise the steps:
The first step in volume parts, is that bamboo charcoal and the 1-3 part ceramic clay of 5-10 μ m mixes stirring with 1 part of grain diameter;
In second step, the material after stirring is pressed into the ceramic tile base substrate;
In the 3rd step, the ceramic tile base substrate was dried in the shade 12-48 hour;
In the 4th step, the ceramic tile base substrate after will drying in the shade is put into liquefied gas kiln naked light and is heated to 700-1250 ℃;
In the 5th step, the ceramic tile goods part surface glazing to behind the kiln discharge promptly leaves not glazed ceramic brick surface;
The 6th step, the glazed ceramic tile goods of part surface are put into liquefied gas kiln naked light be heated to 700-1250 ℃ of sintering, promptly make bamboo-charcoal health-care ceramic tile.
2. according to the preparation method of the described bamboo-charcoal health-care ceramic tile of claim 1, it is characterized in that: the Heating temperature in described the 4th step is 1050-1170 ℃, and the Heating temperature in described the 6th step is 1050-1170 ℃.
3. according to the preparation method of the described bamboo-charcoal health-care ceramic tile of claim 1, it is characterized in that: the Heating temperature in described the 4th step is 1075 ℃, and the Heating temperature in described the 6th step is 1075 ℃.
4. according to the preparation method of the described bamboo-charcoal health-care ceramic tile of claim 1, it is characterized in that: the Heating temperature in described the 4th step is 1100 ℃, and the Heating temperature in described the 6th step is 1100 ℃.
5. according to the preparation method of the described bamboo-charcoal health-care ceramic tile of claim 1, it is characterized in that: the Heating temperature in described the 4th step is 1125 ℃, and the Heating temperature in described the 6th step is 1125 ℃.
6. according to the preparation method of the described bamboo-charcoal health-care ceramic tile of claim 1, it is characterized in that: the Heating temperature in described the 4th step is 1175 ℃, and the Heating temperature in described the 6th step is 1175 ℃.
7. according to the preparation method of claim 1 or 2 or 3 or 4 or 5 described bamboo-charcoal health-care ceramic tiles, it is characterized in that: the described the first step in volume parts, is that bamboo charcoal and 1.75 parts of ceramic clays of 5-10 μ m mix stirring with 1 part of grain diameter.
8. according to the preparation method of claim 1 or 2 or 3 or 4 or 5 described bamboo-charcoal health-care ceramic tiles, it is characterized in that: the described the first step in volume parts, is that bamboo charcoal and 2 parts of ceramic clays of 5-10 μ m mix stirring with 1 part of grain diameter.
9. according to the preparation method of claim 1 or 2 or 3 or 4 or 5 described bamboo-charcoal health-care ceramic tiles, it is characterized in that: the described the first step in volume parts, is that bamboo charcoal and 2.25 parts of ceramic clays of 5-10 μ m mix stirring with 1 part of grain diameter.
10. according to the preparation method of claim 1 or 2 or 3 or 4 or 5 described bamboo-charcoal health-care ceramic tiles, it is characterized in that: the described the first step in volume parts, is that bamboo charcoal and 2.5 parts of ceramic clays of 5-10 μ m mix stirring with 1 part of grain diameter.