KR102446596B1 - Eco-friendly functional inorganic paint compositions and air quality improvement construction method using the same - Google Patents

Eco-friendly functional inorganic paint compositions and air quality improvement construction method using the same Download PDF

Info

Publication number
KR102446596B1
KR102446596B1 KR1020220016368A KR20220016368A KR102446596B1 KR 102446596 B1 KR102446596 B1 KR 102446596B1 KR 1020220016368 A KR1020220016368 A KR 1020220016368A KR 20220016368 A KR20220016368 A KR 20220016368A KR 102446596 B1 KR102446596 B1 KR 102446596B1
Authority
KR
South Korea
Prior art keywords
inorganic paint
friendly functional
functional inorganic
eco
friendly
Prior art date
Application number
KR1020220016368A
Other languages
Korean (ko)
Inventor
윤여은
Original Assignee
다우산업(주)
윤여은
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 다우산업(주), 윤여은 filed Critical 다우산업(주)
Priority to KR1020220016368A priority Critical patent/KR102446596B1/en
Application granted granted Critical
Publication of KR102446596B1 publication Critical patent/KR102446596B1/en

Abstract

The present invention relates to an eco-friendly functional inorganic paint composition with enhanced adhesion strength, incombustibility, and finishing material function, and a construction method for improving indoor air quality using the same. The eco-friendly functional inorganic paint composition contains: a liquid inorganic mixture in which liquid sodium silicate is mixed with any one of shell powder or calcium carbonate; an adsorbent material in which at least one of activated carbon, charcoal, and zeolite is used; functional minerals using at least one of diatomaceous earth, bentonite, illite, and activated clay; a chlorine dioxide powder for the function of decomposing indoor pollutants.

Description

부착강도와 불연성능 및 마감재 기능을 강화한 친환경 기능성 무기질 도료 조성물 및 이를 이용한 실내 공기질 개선용 시공방법{ECO-FRIENDLY FUNCTIONAL INORGANIC PAINT COMPOSITIONS AND AIR QUALITY IMPROVEMENT CONSTRUCTION METHOD USING THE SAME}Eco-FRIENDLY FUNCTIONAL INORGANIC PAINT COMPOSITIONS AND AIR QUALITY IMPROVEMENT CONSTRUCTION METHOD USING THE SAME}

본 발명은 부착강도와 불연성능 및 마감재 기능을 강화한 친환경 기능성 무기질 도료 조성물 및 이를 이용한 실내 공기질 개선용 시공방법에 관한 것으로서, 더욱 상세하게는 흡착과 흡방습, 항균, 항곰팡이의 필수기능과 더불어 불연성능과 내마모성, 내오염성, 표면 부착강도 및 결로방지 등의 부가기능, 마감재로서 기능을 강화할 수 있도록 하며, 라돈 불검출 등 실내 공기질을 개선할 수 있도록 한 부착강도와 불연성능 및 마감재 기능을 강화한 친환경 기능성 무기질 도료 조성물 및 이를 이용한 실내 공기질 개선용 시공방법에 관한 것이다.The present invention relates to an eco-friendly functional inorganic paint composition with enhanced adhesion strength, non-combustible performance, and finishing material function, and a construction method for improving indoor air quality using the same, and more particularly, to a non-flammable composition with essential functions of adsorption, moisture absorption and desorption, antibacterial and antifungal. Additional functions such as performance, abrasion resistance, contamination resistance, surface adhesion strength and condensation prevention, and finishing materials can be strengthened. It relates to an inorganic paint composition and a construction method for improving indoor air quality using the same.

현대식 주택 건축에 있어서 실내 벽면의 마무리에는 합성 수지(emulsion) 도장 등의 방식이 많이 채용되어 오고 있지만, 최근에는 화학물질 과민증이나 새집증후군 등의 화학물질 또는 라돈 등의 악해가 문제시되게 되어, 친환경 마무리 소재에 대한 관심이 집중되고 있다.In modern housing construction, methods such as synthetic resin (emulsion) painting have been widely adopted for finishing interior walls in modern housing construction, but recently, chemical substances such as chemical hypersensitivity or sick house syndrome or harmful effects such as radon have become a problem, and eco-friendly finishing Attention is focused on the material.

특히, 환경부 “다중이용시설 등의 실내공기질 관리법”시행, 국토해양부의 주택등급표시제도 및 친환경 건축물인증제도 시행, 2014년부터 500세대 이상의 주택건설사업 시행, 및 500세대 이상의 리모델링 주택에 대해 「건강친화형주택 건설 기준」(국토교통부 고시 제2013-612호)이 적용되는 등 건축물의 환경 관련 기준은 날이 갈수록 강화되고 있는 추세이다.In particular, the Ministry of Environment’s “Indoor Air Quality Management Act for Multi-Use Facilities, etc.” enforcement, the Ministry of Land, Transport and Maritime Affairs’ implementation of the housing rating labeling system and eco-friendly building certification system, the implementation of housing construction projects for more than 500 households from 2014, and the “health Environment-related standards for buildings are being strengthened day by day, such as the application of the “Standards for Building Eco-Friendly Housing” (Ministry of Land, Infrastructure and Transport Notification No. 2013-612).

더욱이, 실내 공기 질에 대한 소비자의 까다로운 요구에 따라, 건축 자재 등에서 발생되는 휘발성 유기 화합물 및 암모니아 등의 유해 화학물질의 농도를 저감할 수 있는 기능성뿐 아니라, 동시에, 실내의 습도를 조절하고 결로현상을 방지하여 곰팡이 발생을 억제하는 등의 추가적인 공기 청정적 기능성도 요구되고 있다.Moreover, in response to consumer demand for indoor air quality, not only the ability to reduce the concentration of harmful chemicals such as volatile organic compounds and ammonia generated from building materials, but at the same time, it also controls indoor humidity and prevents condensation. An additional air-cleaning function is also required, such as suppressing the occurrence of mold by preventing

부연하여, 현대식 주택 건축은 벽체가 시멘트를 주성분으로 하는 콘크리트 벽체인 경우가 대부분인데, 주택 시공 직후 VOC, 폼알데히드, 톨루엔, 벤젠, 자일렌, 암모니아, 라돈 등의 유해성분이 방출되는 것으로 알려져 있으며, 이러한 유해성분에 의해 아토피, 천식, 두통, 소화불량 및 각종 기관지 질환을 유발함에 따라 이를 해결하기 위한 원인 규명과 대책 마련에 부심하고 있다.In addition, in most modern house construction, the walls are concrete walls with cement as the main component, and it is known that harmful components such as VOC, formaldehyde, toluene, benzene, xylene, ammonia, radon, etc. As these harmful ingredients cause atopy, asthma, headache, indigestion and various bronchial diseases, they are working hard to identify the cause and prepare countermeasures to solve them.

여기에서, VOC, 폼알데히드, 톨루엔, 벤젠, 자일렌, 암모니아 등은 새집증후군과 같은 환경 오염성 질환을 유발하고 있다.Here, VOC, formaldehyde, toluene, benzene, xylene, ammonia, etc. cause environmental pollution diseases such as sick house syndrome.

여기에서, 라돈은 암석이나 토양 건축자재 등에 존재하는 우라늄(U-238)과 토륨(Th-232)이 몇 차례 붕괴를 거치면서 생성되는 무색, 무취, 무미의 기체로 지구상에 존재하는 자연 방사능 물질이다. 실내에 존재하는 라돈은, 토양이나 지반의 암석에서 발생된 라돈기체가 건물 바닥이나 벽의 갈라진 틈을 통해 들어온 것이거나 대리석, 석고보드, 콘크리트, 벽돌, 시멘트, 모르타르, 타일 등의 건축 자재에 존재한 것이거나 토양 또는 지하수에 녹아있던 라돈이 유입된 것이며, 이렇게 유입된 라돈은 실내 등 밀폐된 공간에 고농도로 축적되어 인체에 치명적인 문제를 일으키고 대부분 호흡을 통해 인체에 흡입된 라돈(Radon)과 라돈자손(Radon progeny)은 붕괴를 일으키면서 알파선(α)을 방출하여 폐 조직을 파괴하고, 지속적으로 라돈에 노출되면 폐암을 유발하게 된다. 특히, 라돈자손(Radon progeny)은 기체가 아닌 미세한 입자로 호흡기 흡입 시 폐로 흡입되고, 폐세포나 기관지에 부착되어 알파선을 방출하기 때문에 더욱 치명적이라 할 수 있다.Here, radon is a colorless, odorless, tasteless gas that is produced by the decay of uranium (U-238) and thorium (Th-232), which are present in rocks and soil building materials, several times. to be. Radon existing indoors is radon gas generated from soil or rocks in the ground that enters through cracks in the floor or wall of a building, or exists in building materials such as marble, gypsum board, concrete, brick, cement, mortar, and tile. radon dissolved in soil or groundwater has been introduced, Radon progeny causes decay and emits alpha rays (α) to destroy lung tissue, and continuous exposure to radon causes lung cancer. In particular, Radon progeny is a fine particle, not a gas, which is inhaled into the lungs when inhaled by the respiratory system, and is more lethal because it attaches to lung cells or bronchi and emits alpha rays.

즉, VOC, 폼알데히드, 톨루엔, 벤젠, 자일렌, 암모니아, 라돈 등의 유해성분은 실내 공기질을 오염 및 악화시키며, 인체를 병들게 한다.That is, harmful components such as VOC, formaldehyde, toluene, benzene, xylene, ammonia, and radon pollute and deteriorate indoor air quality and make the human body sick.

이에, 종래에는 다양한 기능성 도료 조성물 및 시공방식들이 제안 및 개시되어 활용되고 있다.Accordingly, in the prior art, various functional paint compositions and construction methods have been proposed, disclosed, and utilized.

하지만, 종래에 제안 및 개시된 기술들은 특히 문제가 되는 포름알데히드 및 라돈과 같은 유해성분의 흡착 제거에 미흡한 실정에 있으며, 제거효율이 떨어지는 문제점이 있다.However, the conventionally proposed and disclosed techniques are in a situation that is insufficient for adsorption and removal of harmful components such as formaldehyde and radon, which are particularly problematic, and there is a problem that the removal efficiency is lowered.

한편, 종래 선행기술문헌에 있어, 국내등록특허 제10-1502457호에서는 "소석회, 바인더 수지, 및 기능성 첨가제를 포함하고, 상기 바인더 수지는, 에틸렌 비닐아세테이트 공중합체 : 에틸렌 비닐 라우레이트 및 비닐 클로라이드의 삼원중합체 = 1 : 0.1 ~ 1 중량 비율로 포함하는 친환경 다기능성 도료 조성물"을 개시하고 있고, 국내등록특허 제10-1528548호에서는 "해조류 2 내지 40중량부; 아크릴코폴리머 15 내지 35중량부; 메틸메타아크릴레이트 수지 10 내지 30중량부; 결합제 5 내지 15중량부; 벤토나이트, 헥토라이트, 사포나이트 및 몬모릴로나이트로 이루어진 군중에서 선택된 층상실리케이트 점토 20 내지 40중량부; 실리카미립자 15 내지 30중량부; 용제 5 내지 15중량부; 및 경화제 2 내지 8중량부를 포함하는 친환경 도료 조성물 및 이를 이용한 도장방법"을 개시하고 있으며, 이를 참조할 수 있다.On the other hand, in the prior art literature, in Korean Patent Registration No. 10-1502457, "Slaked lime, a binder resin, and a functional additive are included, and the binder resin is an ethylene vinyl acetate copolymer: ethylene vinyl laurate and vinyl chloride. Terpolymer = 1: An eco-friendly multifunctional paint composition containing 0.1 to 1 weight ratio," and in Korean Patent No. 10-1528548, "2 to 40 parts by weight of seaweed; 15 to 35 parts by weight of acrylic copolymer; 10 to 30 parts by weight of methyl methacrylate resin; 5 to 15 parts by weight of binder; 20 to 40 parts by weight of layered silicate clay selected from the group consisting of bentonite, hectorite, saponite and montmorillonite; 15 to 30 parts by weight of silica particles; Solvent 5 to 15 parts by weight; and an eco-friendly paint composition comprising 2 to 8 parts by weight of a curing agent and a coating method using the same”, which may be referred to.

대한민국 등록특허공보 제10-1502457호Republic of Korea Patent Publication No. 10-1502457 대한민국 등록특허공보 제10-2332552호Republic of Korea Patent Publication No. 10-2332552

본 발명은 상술한 종래의 문제점을 해소 및 이를 감안하여 안출된 것으로서, 흡착과 흡방습, 항균, 항곰팡이의 필수기능과 더불어 불연성능과 내마모성, 내오염성, 표면 부착강도 및 결로방지 등의 부가기능, 마감재로서 기능을 강화할 수 있도록 하며, 실내 공기질을 개선할 수 있도록 한 부착강도와 불연성능 및 마감재 기능을 강화한 친환경 기능성 무기질 도료 조성물 및 이를 이용한 실내 공기질 개선용 시공방법을 제공하는데 그 목적이 있다.The present invention has been devised in consideration of and solving the above-mentioned problems of the prior art. In addition to essential functions of adsorption, moisture absorption and desorptiveness, antibacterial and antifungal, additional functions such as non-combustible performance, abrasion resistance, contamination resistance, surface adhesion strength and condensation prevention It aims to provide an eco-friendly functional inorganic paint composition with enhanced adhesion strength, non-combustible performance, and finishing material function to improve indoor air quality, and to provide a construction method for improving indoor air quality using the same.

본 발명은 실내오염물질의 흡수와 분해 작용을 동시 유도할 수 있도록 하고, 공기정화효율 및 새집증후군 개선효율을 향상시킬 수 있도록 하며, 아토피 예방과 에너지 절감, 탈취, 및 보온보냉 등 다기능성을 발휘할 수 있도록 한 부착강도와 불연성능 및 마감재 기능을 강화한 친환경 기능성 무기질 도료 조성물 및 이를 이용한 실내 공기질 개선용 시공방법을 제공하는데 그 목적이 있다.The present invention can induce absorption and decomposition of indoor pollutants at the same time, improve air purification efficiency and sick house syndrome improvement efficiency, and exhibit versatility such as atopy prevention, energy saving, deodorization, and thermal insulation. An object of the present invention is to provide an eco-friendly functional inorganic paint composition with enhanced adhesion strength, non-combustible performance, and finishing material function, and a construction method for improving indoor air quality using the same.

본 발명은 흡착 및 분해에 의해 라돈 불검출(방사능 농도지수 '1' 이하)을 구현할 수 있도록 하며, 인체에 무해한 특성을 발휘할 수 있도록 한 부착강도와 불연성능 및 마감재 기능을 강화한 친환경 기능성 무기질 도료 조성물 및 이를 이용한 실내 공기질 개선용 시공방법을 제공하는데 그 목적이 있다.The present invention enables non-detection of radon (radioactivity concentration index '1' or less) by adsorption and decomposition, and an eco-friendly functional inorganic paint composition with enhanced adhesion strength, non-combustible performance, and finishing material function to exhibit harmless properties to the human body; An object of the present invention is to provide a construction method for improving indoor air quality using the same.

상기의 목적을 달성하기 위한 본 발명에 따른 부착강도와 불연성능 및 마감재 기능을 강화한 친환경 기능성 무기질 도료 조성물은, 패각분말 또는 탄산칼슘 중의 어느 하나에 액상규산나트륨을 혼합한 액상의 무기혼합물; 활성탄, 숯, 제올라이트 중에서 적어도 하나 이상이 사용되는 흡착성 소재; 규조토, 벤토나이트, 일라이트, 활성백토 중에서 적어도 하나 이상이 사용되는 기능성 광물질; 실내오염물질을 분해시키는 기능을 증대시키기 위한 이산화염소분말;을 포함하는 것을 특징으로 한다.In order to achieve the above object, an eco-friendly functional inorganic paint composition with enhanced adhesion strength, non-combustible performance and finishing material function according to the present invention is a liquid inorganic mixture obtained by mixing liquid sodium silicate with either shell powder or calcium carbonate; an absorbent material in which at least one of activated carbon, charcoal, and zeolite is used; a functional mineral in which at least one of diatomaceous earth, bentonite, illite, and activated clay is used; Chlorine dioxide powder for increasing the function of decomposing indoor pollutants; characterized in that it contains.

여기에서, 상기 무기혼합물 100~150중량부를 기준으로 하여 흡착성 소재 30~100중량부, 기능성 광물질 10~50중량부, 이산화염소분말 10~100중량부가 배합되는 구성일 수 있다.Here, based on 100 to 150 parts by weight of the inorganic mixture, 30 to 100 parts by weight of an adsorbent material, 10 to 50 parts by weight of a functional mineral, and 10 to 100 parts by weight of chlorine dioxide powder may be blended.

여기에서, 부착성과 접착성 증대 및 조절을 위한 증점제를 포함하되, 상기 증점제는, 카르복시메틸셀룰로오스, 구아검, 아크릴공중합체수지와 에틸렌비닐아세테이트공중합체수지를 혼합한 아크릴계 수지 중에서 선택된 어느 1종일 수 있다.Here, including a thickener for increasing and controlling adhesion and adhesion, the thickener may be any one selected from carboxymethyl cellulose, guar gum, acrylic resin mixed with acrylic copolymer resin and ethylene vinyl acetate copolymer resin have.

여기에서, 상기 흡착성 소재와 기능성 광물질 및 아산화염소분말을 볼밀에 투입하여 200~300rpm의 속도로 20~30분 동안 1차 혼합하되, 상기 흡착성 소재와 기능성 광물질 및 아산화염소분말이 갖는 총 중량 대비 볼밀에 투입하는 볼 중량을 1:5~10의 중량비로 하여 1차 혼합하며, 상기 1차 혼합물과 액상의 무기혼합물을 교반기에 투입하여 교반 혼합하되, 25~40℃의 온도 및 1000~1500rpm의 속도로 30~60분 동안 교반 혼합하여 제조할 수 있다.Here, the adsorbent material, the functional mineral and the chlorine dioxide powder are put into the ball mill and first mixed for 20 to 30 minutes at a speed of 200 to 300 rpm. The weight of the balls to be put into the bowl is first mixed with a weight ratio of 1:5-10, and the first mixture and the liquid inorganic mixture are put into a stirrer and stirred and mixed, but at a temperature of 25-40°C and a speed of 1000-1500rpm It can be prepared by stirring and mixing for 30 to 60 minutes.

여기에서, 실내오염물질의 분해율을 높이기 위한 기능성 촉매제를 포함하되, 상기 기능성 촉매제는, 인산티타늄 화합물 또는 백금티타늄 화합물일 수 있다.Here, including a functional catalyst for increasing the decomposition rate of indoor pollutants, the functional catalyst may be a titanium phosphate compound or a platinum titanium compound.

여기에서, 상기 증점제를 포함하는 친환경 도료는, 점도 3000~10000cps인 것일 수 있다.Here, the eco-friendly paint including the thickener may have a viscosity of 3000 to 10000 cps.

여기에서, 실내오염물질의 흡수 및 공기정화 기능의 강화를 위한 천연식물류를 포함하되, 분말이나 추출물로 사용되며, 상기 천연식물류는, 석창포, 고추냉이, 노루발, 일당귀, 유칼립투스, 솔잎, 대나무, 녹차잎 중에서 적어도 하나 이상일 수 있다.Here, including natural plants for absorption of indoor pollutants and reinforcement of air purification functions, which are used as powders or extracts, and the natural plants include sagebrush, wasabi, presser's foot, mongoose, eucalyptus, pine needles, bamboo, green tea It may be at least one or more of the leaves.

또한, 상기의 목적을 달성하기 위한 본 발명에 따른 실내 공기질 개선용 시공방법은, (A) 건강친화형 기능성 무기질 도료를 준비하는 단계; (B) 대상물의 표면을 깨끗하게 청소 및 정리하는 단계; (C) 건강친화형 기능성 무기질 도료를 대상물의 표면에 도포하는 단계; (D) 도포된 건강친화형 기능성 무기질 도료를 건조시키는 단계;를 포함하며, 상기 건강친화형 기능성 무기질 도료는, 상술한 기술 구성을 갖는 부착강도와 불연성능 및 마감재 기능을 강화한 친환경 기능성 무기질 도료 조성물로 이루어진 것을 특징으로 한다.In addition, the construction method for improving indoor air quality according to the present invention for achieving the above object comprises the steps of: (A) preparing a health-friendly functional inorganic paint; (B) cleaning and arranging the surface of the object; (C) applying a health-friendly functional inorganic paint to the surface of the object; (D) drying the applied health-friendly functional inorganic paint; includes, wherein the health-friendly functional inorganic paint is an eco-friendly functional inorganic paint composition that has the above-described technical configuration, with enhanced adhesion strength, non-combustible performance, and finishing material function characterized in that it consists of

또한, 상기의 목적을 달성하기 위한 본 발명에 따른 실내 공기질 개선용 시공방법은, (A) 건강친화형 기능성 무기질 도료를 준비하는 단계; (B) 대상물의 표면을 깨끗하게 청소 및 정리하는 단계; (C) 대상물의 표면에 벽지 또는 마감재를 시공하는 단계; (D) 벽지 또는 마감재 위에 건강친화형 기능성 무기질 도료를 도포하는 단계; (E) 도포된 건강친화형 기능성 무기질 도료를 건조시키는 단계;를 포함하며, 상기 건강친화형 기능성 무기질 도료는, 상술한 기술 구성을 갖는 부착강도와 불연성능 및 마감재 기능을 강화한 친환경 기능성 무기질 도료 조성물로 이루어진 것을 특징으로 한다.In addition, the construction method for improving indoor air quality according to the present invention for achieving the above object comprises the steps of: (A) preparing a health-friendly functional inorganic paint; (B) cleaning and arranging the surface of the object; (C) applying a wallpaper or finishing material to the surface of the object; (D) applying a health-friendly functional inorganic paint on the wallpaper or finishing material; (E) drying the applied health-friendly functional inorganic paint; includes, wherein the health-friendly functional inorganic paint is an eco-friendly functional inorganic paint composition that has the above-described technical configuration, with enhanced adhesion strength, non-combustible performance, and finishing material function characterized in that it consists of

본 발명에 따르면, 흡착과 흡방습, 항균, 항곰팡이의 필수기능과 더불어 불연성능과 내마모성, 내오염성, 표면 부착강도 및 결로방지 등의 부가기능뿐만 아니라 마감재로서 기능 또한 강화할 수 있으며, 실내 공기질을 개선할 수 있는 부착강도와 불연성능 및 마감재 기능을 강화한 친환경 기능성 무기질 도료 조성물 및 이를 이용한 실내 공기질 개선용 시공방법을 제공할 수 있다.According to the present invention, in addition to the essential functions of adsorption, moisture absorption and desorptiveness, antibacterial and antifungal, additional functions such as non-combustible performance, abrasion resistance, stain resistance, surface adhesion strength and condensation prevention as well as additional functions as a finishing material can also be strengthened, and indoor air quality can be improved. It is possible to provide an eco-friendly functional inorganic paint composition with improved adhesion strength, non-combustible performance and finishing material function, and a construction method for improving indoor air quality using the same.

본 발명에 따르면, 부착강도가 우수하여 콘크리트 및 시멘트류의 천정이나 벽체면 뿐만 아니라 일반 벽지, 필름시트, 건축 마감재 위에 도장이 가능하며 무기질 및 천연광물에 의한 불연성능은 물론 원적외선 및 음이온 방출효과를 발휘할 수 있는 부착강도와 불연성능 및 마감재 기능을 강화한 친환경 기능성 무기질 도료 조성물 및 이를 이용한 실내 공기질 개선용 시공방법을 제공할 수 있다.According to the present invention, it has excellent adhesion strength, so it can be painted not only on the ceiling or wall surface of concrete and cement, but also on general wallpaper, film sheet, and building finishing materials. It is possible to provide an eco-friendly functional inorganic paint composition with enhanced adhesion strength, non-combustible performance and finishing material function, and a construction method for improving indoor air quality using the same.

본 발명에 따르면, 실내오염물질의 흡수와 분해 작용을 동시 유도할 수 있고, 공기정화효율 및 새집증후군 개선효율을 향상시킬 수 있으며, 아토피 예방과 에너지 절감, 탈취, 및 보온보냉 등 다기능성을 발휘할 수 있는 부착강도와 불연성능 및 마감재 기능을 강화한 친환경 기능성 무기질 도료 조성물 및 이를 이용한 실내 공기질 개선용 시공방법을 제공할 수 있다.According to the present invention, absorption and decomposition of indoor pollutants can be simultaneously induced, air purification efficiency and sick house syndrome improvement efficiency can be improved, and multifunctionality such as atopy prevention, energy saving, deodorization, and thermal insulation can be exhibited. It is possible to provide an eco-friendly functional inorganic paint composition with enhanced adhesion strength, non-combustible performance and finishing material function, and a construction method for improving indoor air quality using the same.

본 발명에 따르면, 흡착 및 분해 작용에 의해 라돈 불검출(방사능 농도지수 '1' 이하)을 구현할 수 있으며, 인체에 무해한 특성을 발휘할 수 있는 부착강도와 불연성능 및 마감재 기능을 강화한 친환경 기능성 무기질 도료 조성물 및 이를 이용한 실내 공기질 개선용 시공방법을 제공할 수 있다.According to the present invention, it is possible to realize non-detection of radon (radioactive concentration index '1' or less) by adsorption and decomposition, and eco-friendly functional inorganic paint composition with enhanced adhesion strength and non-combustible performance and finishing material function that can exhibit harmless properties to the human body And it is possible to provide a construction method for improving indoor air quality using the same.

본 발명에 따르면, 콘크리트 및 시멘트류의 천정, 벽체면 뿐만 아니라 일반 벽지, 건축 마감재 등 다양하게 적용할 수 있다.According to the present invention, it can be variously applied not only to the ceiling and wall surfaces of concrete and cement, but also to general wallpaper and building finishing materials.

도 1은 본 발명의 일 실시예에 따른 부착강도와 불연성능 및 마감재 기능을 강화한 친환경 기능성 무기질 도료 조성물을 이용한 시공방법을 나타낸 개략적 공정도이다.
도 2는 본 발명의 다른 실시예에 따른 부착강도와 불연성능 및 마감재 기능을 강화한 친환경 기능성 무기질 도료 조성물을 이용한 시공방법을 나타낸 개략적 공정도이다.
1 is a schematic process diagram showing a construction method using an eco-friendly functional inorganic paint composition with enhanced adhesion strength, non-combustible performance and finishing material function according to an embodiment of the present invention.
2 is a schematic process diagram showing a construction method using an eco-friendly functional inorganic paint composition with enhanced adhesion strength, non-combustible performance and finishing material function according to another embodiment of the present invention.

본 발명에 대해 첨부한 도면을 참조하여 바람직한 실시예를 설명하면 다음과 같으며, 이와 같은 상세한 설명을 통해서 본 발명의 목적과 구성 및 그에 따른 특징들을 보다 잘 이해할 수 있게 될 것이다.Preferred embodiments of the present invention will be described with reference to the accompanying drawings, and the purpose and configuration of the present invention and its features will be better understood through such detailed description.

본 발명의 실시예에 따른 부착강도와 불연성능 및 마감재 기능을 강화한 친환경 기능성 무기질 도료 조성물은 패각분말 또는 탄산칼슘 중의 어느 하나에 액상규산나트륨을 혼합한 액상의 무기혼합물과; 활성탄, 숯, 제올라이트 중에서 적어도 하나 이상이 사용되는 흡착성 소재와; 규조토, 일라이트, 활성백토 중에서 적어도 하나 이상이 사용되는 기능성 광물질과; 실내오염물질을 분해시키는 기능을 증대시키기 위한 이산화염소분말;을 포함하는 구성으로 이루어진다.An eco-friendly functional inorganic paint composition with enhanced adhesion strength, non-combustibility performance and finishing material function according to an embodiment of the present invention comprises: a liquid inorganic mixture obtained by mixing liquid sodium silicate with either shell powder or calcium carbonate; an absorbent material in which at least one of activated carbon, charcoal, and zeolite is used; a functional mineral in which at least one of diatomaceous earth, illite, and activated clay is used; It consists of a configuration comprising; chlorine dioxide powder for increasing the function of decomposing indoor pollutants.

상기 액상의 무기혼합물 100~150중량부를 기준으로 하여 흡착성 소재 30~100중량부, 기능성 광물질 10~50중량부, 이산화염소분말 10~100중량부로 배합할 수 있다.Based on 100 to 150 parts by weight of the liquid inorganic mixture, 30 to 100 parts by weight of an adsorbent material, 10 to 50 parts by weight of a functional mineral, and 10 to 100 parts by weight of chlorine dioxide powder can be blended.

상기 액상의 무기혼합물은 본 발명의 친환경 기능성 무기질 도료에 대한 도막 형성을 가능하게 하면서 대상물의 표면으로 친환경 기능성 무기질 도료를 도포할 시 균일한 도막을 형성시켜주는 기능을 한다.The liquid inorganic mixture functions to form a uniform coating film when applying the eco-friendly functional inorganic paint to the surface of an object while enabling the formation of a coating film for the environmentally-friendly functional inorganic paint of the present invention.

상기 패각분말은 굴, 꼬막, 조개 등의 패각을 분쇄한 분말이며, 자원 재활용 차원과 더불어 탄산칼슘을 주성분으로 갖는 것이므로 천연의 탄산칼슘 성분을 활용하기 위함이다.The shell powder is a powder obtained by pulverizing shells such as oysters, cockles, and clams, and since it has a calcium carbonate as a main component in addition to a resource recycling dimension, it is intended to utilize a natural calcium carbonate component.

상기 패각은 천연 항균기능을 갖는 것으로서, 박테리아나 곰팡이 같은 미생물의 번식을 차단 및 유해균의 증식을 억제하고, 실내 습도조절, 포름알데히드나 톨루엔 등의 휘발성 유기화합물이 발생되지 않는 친환경 재료이면서 항균성을 통해 이를 제거할 수 있으며, 유기성 미세먼지 등을 저감할 수 있다.The shell has a natural antibacterial function, it blocks the growth of microorganisms such as bacteria and mold, suppresses the growth of harmful bacteria, controls indoor humidity, and is an eco-friendly material that does not generate volatile organic compounds such as formaldehyde or toluene. This can be removed, and organic fine dust can be reduced.

이때, 상기 패각분말은 패각을 구비하되 깨끗한 물로 세척한 후 염분을 제거하기 위해 증류수에 2~3일 동안 담궈두고, 세척한 패각은 100~120℃의 오븐에서 12~24시간 동안 건조시킨 후 전기로 등을 이용하여 1200~1800℃에서 4~6시간 동안 소성한 다음에, 소성 처리한 패각에 대해 200메쉬 이하의 미세 분말로 분쇄한 것일 수 있다.At this time, the shell powder is provided with shells, washed with clean water and then soaked in distilled water for 2-3 days to remove salt, and the washed shells are dried in an oven at 100-120° C. for 12-24 hours and then electric After calcining for 4 to 6 hours at 1200~1800°C using a furnace, the calcined shell may be pulverized into fine powder of 200 mesh or less.

상기 탄산칼슘은 건축재료의 충전재로 사용되고, 접착성을 부여할 수 있으며, 흡수재로 사용되기도 한다.The calcium carbonate is used as a filler for building materials, can provide adhesiveness, and is also used as an absorbent material.

상기 규산나트륨은 경화제로서 기능하고, 도막을 안정화시키는 작용을 하며, 접착성을 부여함과 더불어 충전재로 사용되기도 한다.The sodium silicate functions as a curing agent, serves to stabilize the coating film, and is also used as a filler while imparting adhesiveness.

상기 무기혼합물은 불연성능과 더불어 내마모성 및 내오염성 등의 기능을 강화할 수 있다.The inorganic mixture may enhance functions such as abrasion resistance and stain resistance as well as non-combustible performance.

상기 흡착성 소재는 포름알데히드를 비롯한 각종 휘발성 유기화합물과 라돈 등의 실내오염물질은 물론 습기를 흡착하는 기능을 위한 것으로서, 활성탄, 숯, 제올라이트 중에서 적어도 하나 이상을 사용함으로써 실내 공기를 정화 및 살균하는 작용을 한다.The absorbent material serves to absorb moisture as well as various volatile organic compounds including formaldehyde and indoor pollutants such as radon, and purifies and sterilizes indoor air by using at least one of activated carbon, charcoal, and zeolite. do

상기 흡착성 소재는 천연의 방부기능을 가지며, 실내오염물질을 방출하지 않는 재료이다.The absorbent material has a natural antiseptic function and is a material that does not emit indoor pollutants.

상기 기능성 광물질은 흡방습 기능은 물론 음이온과 원적외선 방사에 의한 항균 탈취 및 살균 기능을 위한 천연재료로서, 포름알데히드를 비롯한 각종 휘발성 유기화합물과 라돈 등의 실내오염물질을 흡착 및 분해하여 제거하기 위한 구성이다.The functional mineral is a natural material for antibacterial and deodorizing and sterilizing functions by anion and far-infrared radiation as well as moisture absorptive and desorptive functions. to be.

상기 규조토는 공기 중으로부터 포름알데히드를 비롯한 휘발성 유기화합물(VOC)과 라돈 등을 흡착해 분해하는 성능이 있어 새집증후군 분해 성능은 물론 라돈 흡착 제거기능을 갖는 것으로서, 이와 더불어 항균, 항 곰팡이, 탈취, 단열, 습도조절, 결로 예방, 음이온, 원적외선 발생 효과를 제공할 수 있다.The diatomaceous earth has the ability to decompose by adsorbing and decomposing volatile organic compounds (VOC) including formaldehyde and radon from the air. It can provide heat insulation, humidity control, condensation prevention, negative ions, and far-infrared ray generation effects.

삭제delete

상기 일라이트는 항박테리아, 항바이러스, 항곰팡이, 방부, 원적외선 및 음이온을 방출하는 효과를 제공할 수 있다.The illite may provide an effect of emitting antibacterial, antiviral, antifungal, antiseptic, far-infrared rays and negative ions.

상기 일라이트는 벤젠, 톨루엔, 폼알데하이드, 암모니아 등 유해물질을 흡착 및 탈취하는 효과가 있고, 대장균, 녹농균, 황색포도상구균, 살모넬라균, 폐렴균 등을 살균하는 항균 효과가 있으며, 유해물질 저감 효과를 제공할 수 있다.The illite has an effect of adsorbing and deodorizing harmful substances such as benzene, toluene, formaldehyde, and ammonia, and has an antibacterial effect to sterilize E. can do.

상기 활성백토는 원적외선 및 음이온 방출에 의한 항균 및 살균 효과를 제공할 수 있다.The activated clay can provide antibacterial and sterilizing effects by emitting far-infrared rays and negative ions.

상기 기능성 광물질은 다공성 구조를 갖는 것들로서, 포름알데히드를 비롯한 각종 휘발성 유기화합물과 라돈 등의 실내오염물질을 흡착하는 기능 또한 발휘할 수 있으며, 200메쉬 이하가 사용될 수 있다.The functional minerals are those having a porous structure, and can also exhibit a function of adsorbing various volatile organic compounds including formaldehyde and indoor pollutants such as radon, and 200 mesh or less can be used.

여기에서, 상기 규조토는 밀도 1.9~2.1g/㎤이며, Si 43.1%, Fe 55.3%, Al 0.92%, P 0.31%의 성분 및 조성을 갖는 것일 수 있다.Here, the diatomaceous earth has a density of 1.9 to 2.1 g/cm 3 , and may have components and compositions of 43.1% Si, 55.3% Fe, 0.92% Al, and 0.31% P.

삭제delete

여기에서, 상기 일라이트는 밀도 2.25~2.35g/㎤인 것일 수 있다.Here, the illite may have a density of 2.25 to 2.35 g/cm 3 .

또한, 상기 기능성 광물질을 통해서도 불연성능과 더불어 내마모성 및 내오염성 등의 기능을 강화할 수 있다.In addition, functions such as abrasion resistance and contamination resistance as well as non-combustible performance can be strengthened through the functional mineral.

상기 이산화염소분말은 표백, 탈취, 살균 및 소독 작용을 하는 이산화염소 성분을 갖는 것으로서, 공기중에서 포름알데히드, 암모니아, 사이롤(-SH), 설파이드(R-S-R'), 페놀 등을 산화시켜 다른 물질로 전환시키며, 하기의 표 1에 나타낸 바와 같이, 알데히드계를 비롯한 각종 휘발성 유기화합물을 분해시키는 작용을 한다.The chlorine dioxide powder has chlorine dioxide components for bleaching, deodorizing, sterilizing and disinfecting, and oxidizing formaldehyde, ammonia, cyrol (-SH), sulfide (R-S-R'), phenol, etc. in air It is converted into a substance, and as shown in Table 1 below, it acts to decompose various volatile organic compounds including aldehydes.

Figure 112022014116067-pat00001
Figure 112022014116067-pat00001

또한, 본 발명에서는 실내오염물질의 분해율을 높이기 위한 기능성 촉매제를 첨가하여 더 포함할 수 있는데, 상기 액상의 무기혼합물 100~150중량부에 대하여 10~50중량부를 첨가할 수 있다.In addition, the present invention may further include a functional catalyst for increasing the decomposition rate of indoor pollutants, and 10 to 50 parts by weight may be added based on 100 to 150 parts by weight of the liquid inorganic mixture.

상기 기능성 촉매제는 인산티타늄 화합물 또는 백금티타늄 화합물일 수 있으며, 상기 인산티타늄 화합물은 산화티탄을 인산과 반응시킨 화합물이고, 백금티타늄 화합물은 산화티탄에 백금을 분산시킨 혼합물이다.The functional catalyst may be a titanium phosphate compound or a platinum titanium compound, the titanium phosphate compound is a compound obtained by reacting titanium oxide with phosphoric acid, and the platinum titanium compound is a mixture obtained by dispersing platinum in titanium oxide.

여기에서, 상기 기능성 촉매제는 항균과 소취 및 방오 기능을 하며, 실내오염물질의 분해 작용을 통해 포름알데히드(HCHO)를 유용하게 제거하는 등 새집증후군 개선효과와 더불어 라돈 등을 제거하는 역할을 한다.Here, the functional catalyst functions as an antibacterial, deodorizing and antifouling agent, and serves to effectively remove formaldehyde (HCHO) through the decomposition of indoor pollutants, thereby improving sick house syndrome and removing radon, etc.

여기에서, 상기 인산티타늄 화합물은 밀도 1.49~1.53g/㎤, pH 6~7을 만족하는 것일 수 있다.Here, the titanium phosphate compound may have a density of 1.49 to 1.53 g/cm 3 and a pH of 6 to 7.

또한, 본 발명에서는 실내오염물질의 흡수 및 공기정화 기능의 강화를 위해 천연식물류를 첨가하여 더 포함할 수 있는데, 상기 액상의 무기혼합물 100~150중량부에 대하여 1~30중량부를 첨가할 수 있다.In addition, in the present invention, natural plants may be added to enhance the absorption of indoor pollutants and air purification functions, and 1 to 30 parts by weight may be added based on 100 to 150 parts by weight of the liquid inorganic mixture. .

상기 천연식물류는 분말이나 추출물(액상)의 형태로 사용될 수 있다.The natural plants may be used in the form of powder or extract (liquid).

상기 천연식물류는 석창포, 고추냉이, 노루발, 일당귀, 유칼립투스, 솔잎, 녹차잎 중에서 적어도 하나 이상이 사용될 수 있다.The natural plants may be used at least one or more of seokchangpo, horseradish, presser foot, perch, eucalyptus, pine needles, and green tea leaves.

또한, 본 발명에서는 친환경 기능성 무기질 도료의 부착성과 접착성 증대 및 조절을 위한 증점제를 더 포함하는 구성일 수 있는데, 상기 액상의 무기혼합물 100~150중량부에 대하여 1~10중량부를 첨가할 수 있다.In addition, in the present invention, the composition may further include a thickener for increasing and controlling the adhesion and adhesion of the eco-friendly functional inorganic paint, and 1 to 10 parts by weight may be added based on 100 to 150 parts by weight of the liquid inorganic mixture. .

상기 증점제는 카르복시메틸셀룰로오스, 구아검, 아크릴공중합체수지와 에틸렌비닐아세테이트공중합체수지를 혼합한 아크릴계 수지 중에서 선택된 어느 1종일 수 있다.The thickener may be any one selected from carboxymethyl cellulose, guar gum, and an acrylic resin in which an acrylic copolymer resin and an ethylene vinyl acetate copolymer resin are mixed.

상기와 같은 성분 및 조성을 갖는 본 발명에 따른 부착강도와 불연성능 및 마감재 기능을 강화한 친환경 기능성 무기질 도료는 하기에서와 같은 제조방식으로 제조할 수 있다.The eco-friendly functional inorganic paint with enhanced adhesion strength, non-combustible performance and finishing material function according to the present invention having the above components and compositions can be manufactured by the following manufacturing method.

먼저, 흡착성 소재와 기능성 광물질 및 아산화염소분말을 볼밀에 투입하여 200~300rpm의 속도로 20~30분 동안 1차 혼합한다.First, an adsorbent material, a functional mineral, and chlorine dioxide powder are put into a ball mill and first mixed for 20 to 30 minutes at a speed of 200 to 300 rpm.

이때, 흡착성 소재와 기능성 광물질 및 아산화염소분말이 갖는 총 중량 대비 볼밀에 투입하는 볼 중량을 1:5~10의 중량비로 하여 1차 혼합함으로써 친환경 도료를 시공시 균일하면서도 평평한 도막을 형성시킬 수 있도록 한다.At this time, the weight of the balls put into the ball mill is 1:5-10 based on the total weight of the absorbent material, the functional minerals, and the chlorine dioxide powder, and the first mixing is performed to form a uniform and flat coating film when constructing an eco-friendly paint. do.

그리고, 상기의 1차 혼합물과 액상의 무기혼합물을 교반기에 투입하여 2차로 교반 혼합한다.Then, the first mixture and the liquid inorganic mixture are put into a stirrer and mixed with a second stirring.

이때에는 25~40℃의 온도 및 1000~1500rpm의 속도를 갖는 교반기 조건하에서 30~60분 동안 교반 혼합함으로써 양질의 친환경 기능성 무기질 도료를 제조할 수 있다.In this case, by stirring and mixing for 30 to 60 minutes under a stirrer condition having a temperature of 25 to 40° C. and a speed of 1000 to 1500 rpm, a good quality eco-friendly functional inorganic paint can be manufactured.

여기에서, 상기 첨가제 재료 중에서 기능성 촉매제는 1차 혼합시 첨가할 수 있다.Here, the functional catalyst among the additive materials may be added during the first mixing.

여기에서, 상기 첨가제 재료 중에서 천연식물류는 분말 형태인 경우 1차 혼합시에 첨가하고, 추출물(액상)의 형태인 경우 2차 혼합시에 첨가할 수 있다.Here, among the additive materials, natural plants may be added at the time of primary mixing in the case of powder form, and may be added at the time of secondary mixing in the case of extract (liquid).

여기에서, 상기 첨가제 재료 중에서 증점제는 2차 혼합시에 첨가할 수 있다.Here, in the additive material, a thickener may be added at the time of secondary mixing.

이에 따라, 본 발명에 있어 친환경 기능성 무기질 도료 조성물은 증점제를 첨가하여 최종적으로 점도를 조절하되, 점도 3000~10000cps인 조건을 만족시킴이 바람직하다.Accordingly, in the present invention, the eco-friendly functional inorganic paint composition finally adjusts the viscosity by adding a thickener, but preferably satisfies the condition of the viscosity of 3000 to 10000 cps.

한편, 상술한 성분 및 조성을 갖는 본 발명에 따른 부착강도와 불연성능 및 마감재 기능을 강화한 친환경 기능성 무기질 도료 조성물에 대한 구체적인 실시예 및 실내오염물질 제거효율을 테스트하였다.On the other hand, specific examples and indoor pollutant removal efficiency of the eco-friendly functional inorganic paint composition having the above-described components and compositions enhanced adhesion strength, non-combustible performance and finishing material function according to the present invention were tested.

하기 표 2에 구체적인 실시예를 갖는 성분과 조성(중량부)에 의한 친환경 기능성 무기질 도료 조성물을 나타내었다.Table 2 below shows the eco-friendly functional inorganic paint composition according to the components and compositions (parts by weight) having specific examples.

구분division 무기혼합물inorganic mixture 흡착성 소재absorbent material 기능성 광물질functional minerals 이산화염소chlorine dioxide 증점제thickener 기능성 촉매제functional catalyst 천연식물류natural plants 실시예 1Example 1 100100 9090 5050 100100 55 실시예 2Example 2 100100 100100 6060 100100 55 실시예 3Example 3 100100 9090 3030 8080 33 2020 실시예 4Example 4 100100 9090 3030 8080 33 55

상기 표 1에서, 실시예 1, 2에 있어서는 무기혼합물로 굴패각분말을 혼합 사용하였고, 실시예 3, 4에 있어서는 무기혼합물로 탄산칼슘을 혼합 사용하였다.In Table 1, in Examples 1 and 2, oyster shell powder was mixed and used as an inorganic mixture, and in Examples 3 and 4, calcium carbonate was mixed and used as an inorganic mixture.

실시예 1, 2에서는 흡착성 소재로 활성탄을 사용하였고, 실시예 3, 4에서는 흡착성 소재로 제올라이트를 사용하였다.In Examples 1 and 2, activated carbon was used as an adsorbent material, and in Examples 3 and 4, zeolite was used as an adsorbent material.

실시예 1, 2에서는 기능성 광물질로 규조토를 사용하였고, 실시예 3, 4에서는 일라이트를 사용하였다.In Examples 1 and 2, diatomaceous earth was used as a functional mineral, and in Examples 3 and 4, illite was used.

실시예 1 내지 4에서는 증점제로 카르복시메틸셀룰로오스를 사용하였다.In Examples 1 to 4, carboxymethyl cellulose was used as a thickener.

실시예 3에서는 기능성 촉매제로 인산티타늄 화합물을 첨가하였다.In Example 3, a titanium phosphate compound was added as a functional catalyst.

실시예 4에서는 천연식물류로 석창포 추출물을 첨가하였다.In Example 4, a seokchangpo extract was added as a natural plant.

이와 같은 성분 및 조성을 갖는 실시예 1 내지 4의 친환경 도료를 각각 포름알데히드(HCHO) 및 휘발성 유기화합물(VOCs)이 많이 방출되는 MDF합판에 도포하여 방출량(ppm) 및 차폐율(%)을 측정하였으며, 이러한 결과를 표 3에 나타내었다.The eco-friendly paints of Examples 1 to 4 having such components and compositions were applied to MDF plywood that emits a lot of formaldehyde (HCHO) and volatile organic compounds (VOCs), respectively, and the emission amount (ppm) and shielding rate (%) were measured. , these results are shown in Table 3.

비교예 1로서, 기재로 사용되는 MDF합판 자체에서의 포름알데히드(HCHO) 및 휘발성 유기화합물(VOCs)에 대해서도 방출량(ppm)을 측정하였다.As Comparative Example 1, the emission amount (ppm) of formaldehyde (HCHO) and volatile organic compounds (VOCs) from MDF plywood itself used as a substrate was also measured.

구분division 포름알데히드formaldehyde 차폐율shielding rate 휘발성유기화합물volatile organic compounds 차폐율shielding rate 비교예 1Comparative Example 1 0.280.28 1.411.41 실시예 1Example 1 0.080.08 71.471.4 0.360.36 74.574.5 실시예 2Example 2 0.060.06 78.678.6 0.310.31 78.078.0 실시예 3Example 3 0.030.03 89.389.3 0.140.14 90.190.1 실시예 4Example 4 0.050.05 82.182.1 0.210.21 85.185.1

표 3에서 보여주는 바와 같이, 본 발명에 따른 친환경 기능성 무기질 도료 조성물을 통해서는 포름알데히드 및 휘발성 유기화합물에 대한 차폐성능이 비교적 높게 나타냄을 확인할 수 있고, 새집증후군 개선 및 라돈 등을 흡착 제거하는데 활용성이 있음을 단적으로 보여주고 있으며, 시간 경과시 유해성분에 대한 차폐율을 더욱 높일 수 있다 할 것이다.As shown in Table 3, it can be confirmed that the shielding performance against formaldehyde and volatile organic compounds is relatively high through the eco-friendly functional inorganic paint composition according to the present invention, and it is useful for improving sick house syndrome and adsorbing and removing radon, etc. It clearly shows that there is this, and it will be possible to further increase the shielding rate against harmful components over time.

한편, 하기에서는 상술한 바와 같은 구성 및 작용성을 갖는 본 발명에 따른 부착강도와 불연성능 및 마감재 기능을 강화한 친환경 기능성 무기질 도료 조성물을 이용한 실내 공기질 개선용 시공방법에 대해 도 1 및 도 2를 참조하여 설명하기로 한다.Meanwhile, in the following, referring to FIGS. 1 and 2 for a construction method for improving indoor air quality using an eco-friendly functional inorganic paint composition with enhanced adhesion strength, non-combustible performance and finishing material function according to the present invention having the configuration and functionality as described above. to be explained.

본 발명에 따른 부착강도와 불연성능 및 마감재 기능을 강화한 친환경 기능성 무기질 도료 조성물을 이용한 실내 공기질 개선용 시공방법은 도 1에 나타낸 바와 같이, 건강친화형 기능성 무기질 도료 준비단계(S10), 대상물 표면 정리단계(S20), 건강친화형 기능성 무기질 도료 도포단계(S30), 및 건조단계(S40)를 포함하여 이루어진다.As shown in FIG. 1, the construction method for improving indoor air quality using an eco-friendly functional inorganic paint composition with enhanced adhesion strength, non-combustible performance and finishing material function according to the present invention is a health-friendly functional inorganic paint preparation step (S10), surface cleaning of the object A step (S20), a health-friendly functional inorganic paint application step (S30), and a drying step (S40) are included.

상기 건강친화형 기능성 무기질 도료 준비단계(S10)는 건강친화형 기능성 무기질 도료를 준비하는 단계로서, 앞서 상술한 성분 및 조성을 갖는 부착강도와 불연성능 및 마감재 기능을 강화한 친환경 기능성 무기질 도료 조성물로 제조하여 구비하는 단계이다.The health-friendly functional inorganic paint preparation step (S10) is a step of preparing a health-friendly functional inorganic paint. It is prepared with an eco-friendly functional inorganic paint composition that has the above-described ingredients and composition, enhanced adhesion strength, non-combustible performance, and finishing material function. This is the stage of preparation.

앞서 상술한 성분 및 조성을 갖는 부착강도와 불연성능 및 마감재 기능을 강화한 친환경 기능성 무기질 도료 조성물의 기술내용을 준용하기로 한다.The technical contents of the eco-friendly functional inorganic paint composition with the above-described components and compositions, which have enhanced adhesion strength, non-combustibility, and finishing material function, will be applied mutatis mutandis.

상기 대상물 표면 정리단계(S20)는 대상물의 표면을 깨끗하게 청소 및 정리함으로써 이물질을 제거하는 단계이다.The object surface cleaning step (S20) is a step of removing foreign substances by cleaning and arranging the surface of the object cleanly.

이때, 상기 대상물은 벽체나 마감재일 수 있다.In this case, the object may be a wall or a finishing material.

상기 건강친화형 기능성 무기질 도료 도포단계(S30)는 건강친화형 기능성 무기질 도료를 대상물의 표면에 도포함으로써 일정 두께로 도장 처리하는 단계이다.The health-friendly functional inorganic paint application step (S30) is a step of coating the health-friendly functional inorganic paint to a predetermined thickness by applying the health-friendly functional inorganic paint to the surface of the object.

상기 건조단계(S40)는 대상물의 표면으로 도포된 건강친화형 기능성 무기질 도료를 건조시키는 단계이다.The drying step (S40) is a step of drying the health-friendly functional inorganic paint applied to the surface of the object.

상기 건조단계(S40)는 자연 건조, 송풍 건조, 열풍 건조 중에서 어느 하나의 방식으로 수행될 수 있다.The drying step (S40) may be performed by any one of natural drying, air drying, and hot air drying.

또한, 본 발명에 따른 부착강도와 불연성능 및 마감재 기능을 강화한 친환경 기능성 무기질 도료 조성물을 이용한 실내 공기질 개선용 시공방법은 도 2에 나타낸 바와 같이, 건강친화형 기능성 무기질 도료 준비단계(S110), 대상물 표면 정리단계(S120), 벽지 또는 마감재 시공단계(S130), 건강친화형 기능성 무기질 도료 도포단계(S140), 및 건조단계(S150)를 포함하여 이루어진다.In addition, as shown in FIG. 2, the construction method for improving indoor air quality using the eco-friendly functional inorganic paint composition with enhanced adhesion strength, non-combustibility performance and finishing material function according to the present invention is a health-friendly functional inorganic paint preparation step (S110), the object It consists of a surface cleaning step (S120), a wallpaper or finishing material construction step (S130), a health-friendly functional inorganic paint application step (S140), and a drying step (S150).

상기 건강친화형 기능성 무기질 도료 준비단계(S110)는 건강친화형 기능성 무기질 도료를 준비하는 단계로서, 앞서 상술한 성분 및 조성을 갖는 부착강도와 불연성능 및 마감재 기능을 강화한 친환경 기능성 무기질 도료 조성물로 제조하여 구비하는 단계이다.The health-friendly functional inorganic paint preparation step (S110) is a step of preparing a health-friendly functional inorganic paint. It is prepared with an eco-friendly functional inorganic paint composition having the above-described ingredients and composition, with enhanced adhesion strength, non-combustible performance, and finishing material function. This is the stage of preparation.

앞서 상술한 성분 및 조성을 갖는 부착강도와 불연성능 및 마감재 기능을 강화한 친환경 기능성 무기질 도료 조성물의 기술내용을 준용하기로 한다.The technical contents of the eco-friendly functional inorganic paint composition with the above-described components and compositions, which have enhanced adhesion strength, non-combustibility, and finishing material function, will be applied mutatis mutandis.

상기 대상물 표면 정리단계(S120)는 대상물의 표면을 깨끗하게 청소 및 정리함으로써 이물질을 제거하는 단계이다.The object surface cleaning step (S120) is a step of removing foreign substances by cleaning and arranging the surface of the object cleanly.

이때, 상기 대상물은 벽체일 수 있다.In this case, the object may be a wall.

상기 벽지 또는 마감재 시공단계(S130)는 대상물의 표면에 벽지 또는 마감재를 시공하는 단계이다.The wallpaper or finishing material construction step (S130) is a step of installing the wallpaper or finishing material on the surface of the object.

상기 건강친화형 기능성 무기질 도료 도포단계(S140)는 벽지 또는 마감재 위에 건강친화형 기능성 무기질 도료를 도포하는 단계이다.The health-friendly functional inorganic paint application step (S140) is a step of applying a health-friendly functional inorganic paint on the wallpaper or finishing material.

상기 건조단계(S150)는 도포된 건강친화형 기능성 무기질 도료를 건조시키는 단계로서, 자연 건조, 송풍 건조, 열풍 건조 중에서 어느 하나의 방식으로 수행될 수 있다.The drying step (S150) is a step of drying the applied health-friendly functional inorganic paint, and may be performed by any one of natural drying, air drying, and hot air drying.

부연하여, 본 발명을 적용하기 위한 대상물은 콘크리트 및 시멘트류의 천정, 벽체면 뿐만 아니라 일반 벽지, 건축 마감재 등일 수 있다.In addition, the object to which the present invention is applied may be not only the ceiling and wall surfaces of concrete and cement, but also general wallpaper, building finishing materials, and the like.

즉, 본 발명에 있어, 부착강도와 불연성능 및 마감재 기능을 강화한 친환경 기능성 무기질 도료 조성물은 청초롱-W(CCR-100) 제품의 건강친화형 기능성 무기질 도료이며, 이를 이용한 청초롱-W 공법으로 실내 공기질 개선을 위한 시공을 수행할 수 있다.That is, in the present invention, the eco-friendly functional inorganic paint composition with enhanced adhesion strength, non-combustible performance and finishing material function is a health-friendly functional inorganic paint for Cheongchoron-W (CCR-100) product, Construction can be carried out to improve indoor air quality.

이에 따라, 본 발명에 따른 부착강도와 불연성능 및 마감재 기능을 강화한 친환경 기능성 무기질 도료 조성물 및 이를 이용한 실내 공기질 개선용 시공방법을 통해서는 하기의 4대 필수기능을 구현할 수 있다.Accordingly, the following four essential functions can be realized through the eco-friendly functional inorganic paint composition and the method for improving indoor air quality using the inorganic paint composition with enhanced adhesion strength, non-combustibility performance and finishing material function according to the present invention.

① 흡방습 : 습도가 높을 때 흡습을 하여, 건조할 때 방습하는 기능으로 실내 습도를 적절하게 유지 시켜주는 기능① Moisture absorption/desorption: A function that absorbs moisture when the humidity is high, and prevents moisture when it is dry, and maintains the indoor humidity appropriately.

② 흡착성능 : 세계보건기구(WHO)에서 정한 1급 발암물질인 휘발성유기화합물과 포름알데하이드 및 라돈 등을 흡착하여 분해하는 기능② Adsorption performance: The function of adsorbing and decomposing volatile organic compounds, formaldehyde and radon, which are class 1 carcinogens specified by the World Health Organization (WHO).

③ 항균과 항곰팡이 성능 : 대장균, 황색포도상구균 등의 곰팡이균 증식을 억제해 주는 기능③ Antibacterial and antifungal performance: Function to inhibit the growth of mold bacteria such as E. coli and Staphylococcus aureus

또한, 상술한 흡착과 흡방습, 항균, 항곰팡이의 필수기능과 더불어 불연성능과 내마모성, 내오염성, 표면 부착강도은 물론 흡방습 특성에 의해 실내 습도를 조절하여주므로 결로방지성능까지 향상시킬 수 있는 등 부가기능을 강화할 수 있고 마감재로서 기능토록 할 수 있으며, 이를 통해 실내 공기질을 아주 유용하게 개선할 수 있을 뿐만 아니라 새집증후군을 비롯한 아토피 예방과 에너지 절감, 탈취, 및 보온보냉, 라돈 불검출 등 다기능성을 발휘할 수 있는 장점을 제공할 수 있다.In addition, in addition to the essential functions of adsorption, moisture absorption and desorptiveness, antibacterial and antifungal, as well as non-combustible performance, abrasion resistance, stain resistance, surface adhesion strength, as well as moisture absorption and desorptive properties, it regulates indoor humidity. Additional functions can be strengthened and can be used as a finishing material. Through this, not only can the indoor air quality be improved very usefully, but also atopy prevention including sick house syndrome, energy saving, deodorization, and multifunctionality such as thermal insulation and radon non-detection It can provide you with an advantage that you can use.

이상에서 설명한 실시예는 본 발명의 바람직한 실시예를 설명한 것에 불과하고 이러한 실시예에 극히 한정되는 것은 아니며, 본 발명의 기술적 사상과 청구범위 내에서 이 기술분야의 당해업자에 의하여 다양한 수정과 변형 또는 단계의 치환 등이 이루어질 수 있다 할 것이며, 이는 본 발명의 기술적 권리범위 내에 속한다 할 것이다.The embodiments described above are merely illustrative of preferred embodiments of the present invention and are not limited to these embodiments, and various modifications and variations or modifications by those skilled in the art within the spirit and claims of the present invention It will be said that the substitution of steps may be made, and this will be said to be within the scope of the technical rights of the present invention.

Claims (9)

패각분말 또는 탄산칼슘 중의 어느 하나에 액상규산나트륨을 혼합한 액상의 무기혼합물 100~150중량부를 기준으로 하며;
활성탄, 숯, 제올라이트 중에서 적어도 하나 이상이 사용되는 흡착성 소재 30~100중량부;
규조토, 일라이트, 활성백토 중에서 적어도 하나 이상이 사용되는 기능성 광물질 10~50중량부;
실내오염물질을 분해시키는 기능을 증대시키기 위한 이산화염소분말 10~100중량부;
실내오염물질의 분해율을 높이기 위한 기능성 촉매제 10~50중량부;
부착성과 접착성 증대 및 조절을 위한 증점제 1~10중량부;
실내오염물질의 흡수 및 공기정화 기능의 강화를 위한 것으로서, 분말이나 추출물로 사용되는 천연식물류 1~30중량부; 를 포함하며,
상기 기능성 촉매제는 인산티타늄 화합물 또는 백금티타늄 화합물이고,
상기 증점제는 카르복시메틸셀룰로오스, 구아검, 아크릴공중합체수지와 에틸렌비닐아세테이트공중합체수지를 혼합한 아크릴계 수지 중에서 선택된 어느 1종이고,
상기 천연식물류는 석창포, 고추냉이, 노루발, 일당귀, 유칼립투스, 솔잎, 녹차잎 중에서 적어도 하나 이상인 것을 특징으로 하는 부착강도와 불연성능 및 마감재 기능을 강화한 친환경 기능성 무기질 도료 조성물.
Based on 100 to 150 parts by weight of a liquid inorganic mixture obtained by mixing liquid sodium silicate with either shell powder or calcium carbonate;
30-100 parts by weight of an absorbent material in which at least one of activated carbon, charcoal, and zeolite is used;
10 to 50 parts by weight of a functional mineral in which at least one of diatomaceous earth, illite, and activated clay is used;
10-100 parts by weight of chlorine dioxide powder to increase the function of decomposing indoor pollutants;
10-50 parts by weight of a functional catalyst for increasing the decomposition rate of indoor pollutants;
1 to 10 parts by weight of a thickener for increasing and controlling adhesion and adhesion;
1 to 30 parts by weight of natural plants used as powders or extracts for reinforcing indoor pollutant absorption and air purification functions; includes,
The functional catalyst is a titanium phosphate compound or a platinum titanium compound,
The thickener is any one selected from carboxymethyl cellulose, guar gum, an acrylic resin mixed with an acrylic copolymer resin and an ethylene vinyl acetate copolymer resin,
The natural plant is an eco-friendly functional inorganic paint composition with enhanced adhesion strength, non-combustible performance and finishing material function, characterized in that at least one or more of stone calamus, wasabi, presser foot, daisy, eucalyptus, pine needles, and green tea leaves.
삭제delete 삭제delete 제 1항에 있어서,
상기 흡착성 소재와 기능성 광물질 및 아산화염소분말을 볼밀에 투입하여 200~300rpm의 속도로 20~30분 동안 1차 혼합하되, 상기 흡착성 소재와 기능성 광물질 및 아산화염소분말이 갖는 총 중량 대비 볼밀에 투입하는 볼 중량을 1 : 5~10의 중량비로 하여 1차 혼합하며,
상기 1차 혼합물과 액상의 무기혼합물을 교반기에 투입하여 교반 혼합하되, 25~40℃의 온도 및 1000~1500rpm의 속도로 30~60분 동안 교반 혼합하여 제조하는 것을 특징으로 하는 부착강도와 불연성능 및 마감재 기능을 강화한 친환경 기능성 무기질 도료 조성물.
The method of claim 1,
The adsorbent material, functional mineral and chlorine dioxide powder are put into the ball mill and mixed first for 20 to 30 minutes at a speed of 200 to 300 rpm, but the total weight of the absorbent material, functional mineral and chlorine dioxide powder is added to the ball mill First mix with a weight ratio of 1: 5 to 10,
Adhesive strength and non-combustible performance, characterized in that the primary mixture and the liquid inorganic mixture are put into a stirrer and stirred and mixed, and stirred and mixed for 30-60 minutes at a temperature of 25-40 ° C and a speed of 1000-1500 rpm and an eco-friendly functional inorganic paint composition with enhanced finishing material function.
삭제delete 삭제delete 삭제delete (A) 건강친화형 기능성 무기질 도료를 준비하는 단계;
(B) 대상물의 표면을 깨끗하게 청소 및 정리하는 단계;
(C) 건강친화형 기능성 무기질 도료를 대상물의 표면에 도포하는 단계;
(D) 도포된 건강친화형 기능성 무기질 도료를 건조시키는 단계; 를 포함하며,
상기 건강친화형 기능성 무기질 도료는,
청구항 1, 청구항 4 중에서 어느 한 항에 의한 부착강도와 불연성능 및 마감재 기능을 강화한 친환경 기능성 무기질 도료 조성물로 이루어진 것을 특징으로 하는 실내 공기질 개선용 시공방법.
(A) preparing a health-friendly functional inorganic paint;
(B) cleaning and arranging the surface of the object;
(C) applying a health-friendly functional inorganic paint to the surface of the object;
(D) drying the applied health-friendly functional inorganic paint; includes,
The health-friendly functional inorganic paint,
A construction method for improving indoor air quality, characterized in that it consists of an eco-friendly functional inorganic paint composition with enhanced adhesion strength, non-combustibility performance and finishing material function according to any one of claims 1 and 4.
(A) 건강친화형 기능성 무기질 도료를 준비하는 단계;
(B) 대상물의 표면을 깨끗하게 청소 및 정리하는 단계;
(C) 대상물의 표면에 벽지 또는 마감재를 시공하는 단계;
(D) 벽지 또는 마감재 위에 건강친화형 기능성 무기질 도료를 도포하는 단계;
(E) 도포된 건강친화형 기능성 무기질 도료를 건조시키는 단계; 를 포함하며,
상기 건강친화형 기능성 무기질 도료는,
청구항 1, 청구항 4 중에서 어느 한 항에 의한 부착강도와 불연성능 및 마감재 기능을 강화한 친환경 기능성 무기질 도료 조성물로 이루어진 것을 특징으로 하는 실내 공기질 개선용 시공방법.
(A) preparing a health-friendly functional inorganic paint;
(B) cleaning and arranging the surface of the object;
(C) applying a wallpaper or finishing material to the surface of the object;
(D) applying a health-friendly functional inorganic paint on the wallpaper or finishing material;
(E) drying the applied health-friendly functional inorganic paint; includes,
The health-friendly functional inorganic paint,
A construction method for improving indoor air quality, characterized in that it consists of an eco-friendly functional inorganic paint composition with enhanced adhesion strength, non-combustibility performance and finishing material function according to any one of claims 1 and 4.
KR1020220016368A 2022-02-08 2022-02-08 Eco-friendly functional inorganic paint compositions and air quality improvement construction method using the same KR102446596B1 (en)