CN106497207A - A kind of inner wall putty powder - Google Patents
A kind of inner wall putty powder Download PDFInfo
- Publication number
- CN106497207A CN106497207A CN201611232132.2A CN201611232132A CN106497207A CN 106497207 A CN106497207 A CN 106497207A CN 201611232132 A CN201611232132 A CN 201611232132A CN 106497207 A CN106497207 A CN 106497207A
- Authority
- CN
- China
- Prior art keywords
- parts
- wall putty
- putty powder
- powder
- activated carbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of inner wall putty powder, is mainly made up of following raw material：White portland cement, heavy calcium carbonate, Pulvis Talci, activated carbon, nano-titanium oxide, polyanion cellulose PAC, NSJF 6A rubber powders, 1008 glue powders of GN, dispersant LBD 1, organic silicon solid defoaming agent, polypropylene anti-crack and anti-seepage chopped fiber, nanometer silver, arrow grass, european aspidium, lavender powder.The inner wall putty powder of the present invention, with highly versatile, resist sagging, viscosity is strong, the advantages of energy-conserving and environment-protective；Activated carbon, nano-titanium oxide and nanometer silver is with the addition of, the effects such as have formaldehyde adsorption, antibacterial, purify air；With the addition of medicinal herb componentses arrow grass, european aspidium and lavandula angustifolia simultaneously, also there are the effects such as bacteria mildew-proof, purify air, insect prevention sterilization；The inner wall putty powder of the present invention can distribute pure and fresh simple and elegant fragrance, and have health-care effect, be suitable for living.
Description
Technical field
The present invention relates to construction material, and in particular to a kind of inner wall putty powder.
Background technology
Before inner wall putty powder is paint class construction, a kind of surface packing material of pretreatment, main purpose is carried out to construction surface
It is the curve deviation of the hole and correction construction surface for filling construction surface, is to obtain uniform, smooth lacquer painting to lay a solid foundation.Our states
The standard of family, finished product putty is divided into：GENERAL TYPE putty (Y types) and water-resistant type putty (N-type).And existing inner wall putty powder is general
Property poor, not energy-conserving and environment-protective, and easily there is jaundice, the phenomenon such as mouldy.
Content of the invention
For existing inner wall putty powder versatility poor, easily there is jaundice, the phenomenon problem such as mouldy, the present invention proposes one
Plant highly versatile, the inner wall putty powder without mouldy yellowing phenomenon, energy-conserving and environment-protective.
For realizing object above, the technical scheme for adopting of the present invention for：A kind of inner wall putty powder, by following weight portion
Raw material is constituted：
White portland cement 15-20 parts, heavy calcium carbonate 35-40 parts, Pulvis Talci 20-30 parts, activated carbon 10-15
Part, nano-titanium oxide 5-10 parts, polyanion cellulose PAC 0.3-0.5 parts, NSJF-6A rubber powder 0.4-0.6 parts, GN-1008
Glue powder 0.8-1.2 parts, dispersant LBD-1 0.1-0.5 parts, organic silicon solid defoaming agent 0.4-0.8 parts, polypropylene cracking resistance are prevented
Ooze chopped fiber 1-2 part, nanometer silver powder 0.3-1 parts, arrow grass 0.3-0.7 parts, european aspidium 0.5-1 parts, lavandula angustifolia 0.5-1.0 parts.
The white portland cement, heavy calcium carbonate, talcous particle diameter are 10-15 microns.
The particle diameter of the activated carbon is 8-12 microns.
The arrow grass, european aspidium, the particle diameter of lavandula angustifolia are 4-8 microns.
The dispersant LBD-1 is acrylic polymer surfactant.
Beneficial effects of the present invention：The inner wall putty powder of the present invention, with highly versatile, resist sagging, viscosity is strong, energy-saving ring
The advantages of guarantor；Activated carbon, nano-titanium oxide and nanometer silver is with the addition of, has formaldehyde adsorption, antibacterial, deodorization to dispel taste, purify air, tune
The effects such as section indoor humidity；With the addition of medicinal herb componentses arrow grass, european aspidium and lavandula angustifolia simultaneously, also have bacteria mildew-proof, purification
The effects such as air, insect prevention sterilization；The inner wall putty powder of the present invention can distribute pure and fresh simple and elegant fragrance, and have health-care effect, fit
Close and live.
Specific embodiment
Hereinafter the specific embodiment of the present invention is described in detail.It should be appreciated that described herein concrete
Embodiment is merely to illustrate and explains the present invention, is not limited to the present invention.In embodiment, white portland cement, weight
Matter Paris white, Pulvis Talci, activated carbon, nano-titanium oxide, polyanion cellulose PAC, organic silicon solid defoaming agent, polypropylene
Anti-crack and anti-seepage chopped fiber, nanometer silver powder are Gaede chemical industry net commercially available product, and NSJF-6A rubber powders are that Nai Si chemistry painting industries company limited produces
Product, GN-1008 glue powders are the sensible great achievement waterproof material company limited product in Harbin, and dispersant LBD-1 is that Shijiazhuang is bright rich
Chemical technology company limited product.
Embodiment 1
A kind of inner wall putty powder, is made up of the raw material of following weight portion：
16 parts of white portland cement, 38 parts of heavy calcium carbonate, 20 parts of Pulvis Talci, 12 parts of activated carbon, nano-titanium oxide
7.3 parts, 0.3 part of polyanion cellulose PAC, 0.5 part of NSJF-6A rubber powders, 0.8 part of GN-1008 glue powders, dispersant LBD-1
0.4 part, 0.6 part of organic silicon solid defoaming agent, 1.5 parts of polypropylene anti-crack and anti-seepage chopped fiber, 0.5 part of nanometer silver powder, arrow grass 0.5
Part, 0.6 part of european aspidium, 1.0 parts of lavandula angustifolia.
Embodiment 2
A kind of inner wall putty powder, is made up of the raw material of following weight portion：
15 parts of white portland cement, 36 parts of heavy calcium carbonate, 22 parts of Pulvis Talci, 13 parts of activated carbon, nano-titanium oxide
7.2 parts, 0.4 part of polyanion cellulose PAC, 0.4 part of NSJF-6A rubber powders, 1.0 parts of GN-1008 glue powders, dispersant LBD-1
0.5 part, 0.6 part of organic silicon solid defoaming agent, 1.5 parts of polypropylene anti-crack and anti-seepage chopped fiber, 0.4 part of nanometer silver powder, arrow grass 0.6
Part, 0.8 part of european aspidium, 1.0 parts of lavandula angustifolia.
Detection example
The inner wall putty powder of embodiment 1,2, after testing, institute's inspection project meets《Architecture indoor putty》JG/T3049-
The requirement of 1998 standards, qualified.
Detection results such as following table：
| Detection project | Standard is required | 1 result of embodiment | 2 result of embodiment | Conclusion |
| Condition in container | Without caking, uniformly | Without caking, uniformly | Without caking, uniformly | Qualified |
| Application property | Blade coating is accessible | Blade coating is accessible | Blade coating is accessible | Qualified |
| Surface drying time (h) | <5 | 2-3 | 2-3 | Qualified |
| Alkali resistance (24h) | Without exception | Without exception | Without exception | Qualified |
| Resistance to water (48h) | Without exception | Without exception | Without exception | Qualified |
| Adhesive strength (Mpa) | >0.5 | 1.8 | 2.0 | Qualified |
The inner wall putty powder of the present invention, with highly versatile, resist sagging, viscosity is strong, the advantages of energy-conserving and environment-protective；With the addition of work
Property charcoal, nano-titanium oxide and nanometer silver, the effects such as have formaldehyde adsorption, antibacterial, purify air；Medicinal herb componentses arrow with the addition of simultaneously
Head grass, european aspidium and lavandula angustifolia, also have the effects such as bacteria mildew-proof, purify air, insect prevention sterilization；The inner wall putty powder symbol of the present invention
Prescription is closed, effect is preferable.
Claims (5)
1. a kind of inner wall putty powder, it is characterised in that be made up of the raw material of following weight portion：
White portland cement 15-20 parts, heavy calcium carbonate 35-40 parts, Pulvis Talci 20-30 parts, activated carbon 10-15 parts, receive
Rice titanium oxide 5-10 parts, polyanion cellulose PAC 0.3-0.5 parts, NSJF-6A rubber powder 0.4-0.6 parts, GN-1008 glue powders
0.8-1.2 parts, dispersant LBD-1 0.1-0.5 parts, organic silicon solid defoaming agent 0.4-0.8 parts, the short fibre of polypropylene anti-crack and anti-seepage
Dimension 1-2 parts, nanometer silver powder 0.3-1 parts, arrow grass 0.3-0.7 parts, european aspidium 0.5-1 parts, lavandula angustifolia 0.5-1.0 parts.
2. a kind of inner wall putty powder according to claim 1, it is characterised in that：The white portland cement, heavy carbon
Sour calcium powder, talcous particle diameter are 10-15 microns.
3. a kind of inner wall putty powder according to claim 1, it is characterised in that：The particle diameter of the activated carbon is that 8-12 is micro-
Rice.
4. a kind of inner wall putty powder according to claim 1, it is characterised in that：The arrow grass, european aspidium, lavandula angustifolia
Particle diameter is 4-8 microns.
5. a kind of inner wall putty powder according to claim 1, it is characterised in that：The dispersant LBD-1 is acrylic compounds
Polymeric surfactant.