CN115245748B - 复合膜制备方法 - Google Patents
复合膜制备方法 Download PDFInfo
- Publication number
- CN115245748B CN115245748B CN202110467463.9A CN202110467463A CN115245748B CN 115245748 B CN115245748 B CN 115245748B CN 202110467463 A CN202110467463 A CN 202110467463A CN 115245748 B CN115245748 B CN 115245748B
- Authority
- CN
- China
- Prior art keywords
- film
- solution
- core
- composite
- active monomer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明属于分离膜领域，具体涉及一种复合膜制备方法，包括下述步骤：1)铸膜液经由制膜机经喷丝头挤出，同时，芯液经芯液腔流出，铸膜液与芯液接触后，发生相分离成为预成型膜；所述的芯液为包含多元胺类活性单体的去离子水溶液；2)预成型膜浸入聚合浴中即可形成复合膜；所述的聚合浴为包含多元酰氯活性单体的乙醇溶液。本发明公开了一种复合膜制备方法，结合了涂覆法和界面聚合法的特点，减少工艺路线，获得薄层复合膜。
Description
技术领域
本发明属于分离膜领域，具体涉及一种复合膜制备方法。
背景技术
分离膜作为分离科学中重要的手段之一，兼有分离、浓缩、纯化和精制的功能，又有高效、节能、环保、分子级过滤及过滤过程简单、易于控制等特征，广泛应用于市政用水、工业净水、海水淡化及特种物料分离提纯等领域。
目前，复合膜常用技术有涂覆法和界面聚合法。涂覆法是把涂覆液浸涂于基膜上，然后成膜形成分离膜功能层；界面聚合法是在基膜表面上，用活性单体进行界面聚合形成分离膜功能层。
在分离膜复合制备过程中，涂覆法属于物理方法，涂覆形成的功能层相对较厚；而界面聚合法属于化学法，功能层较薄，需连续经过两种单体溶液，工艺线设计较长，占地面积大。
发明内容
本发明的目的在于克服现有技术中的缺点，提供一种复合膜制备方法。
为实现上述目的，本发明采用的技术方案为：
一种复合膜制备方法，包括下述步骤：
1)铸膜液经由制膜机经喷丝头挤出，同时，芯液经芯液腔流出，铸膜液与芯液接触后，发生相分离成为预成型膜；所述的芯液为包含多元胺类活性单体的去离子水溶液；
2)预成型膜浸入聚合浴中即可形成复合膜；所述的聚合浴为包含多元酰氯活性单体的乙醇溶液。
所述的铸膜液包括下述质量份组分：聚碳酸酯10-40份，复合溶剂60-90份；所述的复合溶剂为聚乙二醇与DMAC的混合物。
所述的多元胺类活性单体为哌嗪、间苯二胺、二乙烯三胺中的一种，所述的多元酰氯活性单体为均苯三甲酰氯。
多元酰氯活性单体的浓度为1-3wt％。
多元胺类活性单体的浓度为5-10wt％。
与现有技术相比，本发明的有益效果是：
本发明公开了一种复合膜制备方法，结合了涂覆法和界面聚合法的特点，减少工艺路线，获得薄层复合膜。将多元胺类活性单体与芯液、多元酰氯活性单体与聚合浴液分别糅合在一起，能够快速生产超薄功能层复合膜。简化了工艺流程，设备占地面积减小；与现有制膜机器搭配使用方便，无需高成本升级改造。
具体实施方式
为了使本技术领域的技术人员更好地理解本发明的技术方案，下面结合最佳实施例对本发明作进一步的详细说明。
实施例一：70℃，聚碳酸酯10wt％，聚乙二醇1000 10wt％分量多次加入DMAC80wt％中，不断搅拌直至溶解完全，静置脱泡形成聚碳酸酯铸膜液；5wt％四乙烯三胺溶于水中为芯液；3wt％均苯三甲酰氯溶于乙醇中为聚合浴液。
聚碳酸酯铸膜液经由制膜机经喷丝头挤出，同时，芯液经芯液腔流出，铸膜液与芯液接触后，发生相分离成型，多元胺类活性单体在相分离过程中以水载体逐渐由内腔向外扩散至膜外表层；成型膜浸入聚合浴中，聚合浴中的多元酰氯活性单体在膜外表层与扩散出的多元胺类活性单体发生界面聚合反应成致密功能层，膜最终成型。
实施例二：80℃，聚碳酸酯40wt％，聚乙二醇600 10wt％分量多次加入DMAC50wt％中，不断搅拌直至溶解完全，静置脱泡形成聚碳酸酯铸膜液；10wt％乙二胺溶于水中为芯液；1wt％均苯三甲酰氯溶于乙醇中为聚合浴液。
聚碳酸酯铸膜液经由制膜机经喷丝头挤出，同时，芯液经芯液腔流出，铸膜液与芯液接触后，发生相分离成型，多元胺类活性单体在相分离过程中以水载体逐渐由内腔向外扩散至膜外表层；成型膜浸入聚合浴中，聚合浴中的多元酰氯活性单体在膜外表层与扩散出的多元胺类活性单体发生界面聚合反应成致密功能层，膜最终成型。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。
Claims (3)
1.一种复合膜制备方法，其特征在于，包括下述步骤：
1）铸膜液经由制膜机经喷丝头挤出，同时，芯液经芯液腔流出，铸膜液与芯液接触后，发生相分离成为预成型膜；所述的芯液为包含多元胺类活性单体的去离子水溶液；
2）预成型膜浸入聚合浴中即可形成复合膜；所述的聚合浴为包含多元酰氯活性单体的乙醇溶液；
所述的铸膜液包括下述质量份组分：聚碳酸酯10-40份，复合溶剂60-90份；所述的复合溶剂为聚乙二醇与DMAC的混合物；
所述的多元胺类活性单体为哌嗪、间苯二胺、二乙烯三胺中的一种，所述的多元酰氯活性单体为均苯三甲酰氯。
2.根据权利要求1所述的复合膜制备方法，其特征在于，多元酰氯活性单体的浓度为1-3wt%。
3.根据权利要求1所述的复合膜制备方法，其特征在于，多元胺类活性单体的浓度为5-10wt%。