CN115109473A - 一种硅烷树脂胶防水涂料 - Google Patents
一种硅烷树脂胶防水涂料 Download PDFInfo
- Publication number
- CN115109473A CN115109473A CN202210984983.1A CN202210984983A CN115109473A CN 115109473 A CN115109473 A CN 115109473A CN 202210984983 A CN202210984983 A CN 202210984983A CN 115109473 A CN115109473 A CN 115109473A
- Authority
- CN
- China
- Prior art keywords
- waterproof coating
- resin adhesive
- adhesive waterproof
- silane resin
- coating material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本申请公开了一种硅烷树脂胶防水涂料，所述硅烷树脂胶防水涂料配方包括醋丙乳液、膨润土、重钙、轻钙、二辛脂、乳化剂、氯化石蜡18‑22公斤、胶联体、纯净水。通过采用重质碳酸钙、轻质碳酸钙、氯化石蜡等无毒、无味、无臭的原料，避免配比完成后，硅烷树脂胶防水涂料气味具有难闻的气味，且作为主要远离的醋丙乳液无甲醛，健康环保，解决了现有的硅烷树脂胶防水涂料气味较为难闻的问题，提高了防水涂料的实用性，避免防水涂料涂抹后的气味造成使用者的不适。
Description
技术领域
本申请涉及一种防水涂料，具体是一种硅烷树脂胶防水涂料。
背景技术
硅树脂，是一种具有高度交联结构的热固性聚硅氧烷聚合物，兼具有机树脂及无机材料的双重特性，具有独特的物理、化学性能，有很好的电绝缘性质，耐温及防水的效果，最突出的性能是耐高温，能在400℃高温下长期工作而不被破坏，还具有优良的耐腐蚀性、耐辐照性、电绝缘性和耐候性，用于金属、玻璃钢部件的胶接和密封，被广泛用作耐高低温绝缘漆、耐热涂料、耐候涂料、耐烧蚀涂料及耐高低温、电绝缘的模塑料等。
目前市场上的丙烯酸类水涂料在使用时，会带有一点难闻气味，需要很久才能消散，涂料涂在建筑墙体上后，会造成使用者，或居住者的不适，受热后更会发出刺鼻气味，大大降低了防水涂料的实用性。因此，针对上述问题提出一种硅烷树脂胶防水涂料。
发明内容
在本实施例中提供了一种硅烷树脂胶防水涂料用于解决现有技术中的硅烷树脂胶防水涂料气味较为难闻的问题
一种硅烷树脂胶防水涂料，所述硅烷树脂胶防水涂料配方包括醋丙乳液 480-520公斤、膨润土18-22公斤、重钙280-320公斤、轻钙75-85公斤、二辛脂32-37公斤、乳化剂38-42公斤、氯化石蜡18-22公斤、胶联体1.8-2 公斤、纯净水180-220公斤。
进一步地，所述醋丙乳液是以醋酸乙烯和丙烯酸丁酯为主要功能单体共聚而成的水性高分子树脂，所述醋丙乳液为五五固含量，即醋丙乳液中的固体和液体比例为1:1。
进一步地，所述膨润土是以蒙脱石为主要矿物成分的非金属矿产，蒙脱石结构是由两个硅氧四面体夹一层铝氧八面体组成的2：1型晶体结构，所述膨润土在加入时先用等比纯净水泡开，然后加入膨润土中搅拌20-25分钟。
进一步地，所述重钙为重质碳酸钙，是由天然碳酸盐矿物如方解石、大理石、石灰石磨碎而成，是常用的粉状无机填料，具有化学纯度高、惰性大、不易化学反应、热稳定性好、在400℃以下不会分解、白度高、吸油率低、折光率低、质软、干燥、不含结晶水、硬度低磨耗值小、无毒、无味、无臭、分散性好等优点。
进一步地，所述轻钙是轻质碳酸钙，是将石灰石等原料段烧生成石灰和二氧化碳，再加水消化石灰生成石灰乳，通入二氧化碳碳化石灰乳生成碳酸钙沉淀，经脱水、干燥和粉碎制得，所述重钙和轻钙加入后搅拌30-35分钟。
进一步地，所述二辛脂为邻苯二甲酸二辛酯，是一种无色油状液体，比重0.9861(20/20)，不溶于水，溶于乙醇、乙醚、矿物油等大多数有机溶剂
进一步地，所述乳化剂是能使两种或两种以上互不相溶的组分的混合液体形成稳定的乳状液的一类物质，在乳化过程中，分散相以微滴(微米级) 的形式分散在连续相中，乳化剂降低了混合体系中各组分的界面张力，并在微滴表面形成较坚固的薄膜或由于乳化剂给出的电荷而在微滴表面形成双电层，阻止微滴彼此聚集，而保持均匀的乳状液，所述二辛脂和乳化剂加入后搅拌30-35分钟。
进一步地，所述氯化石蜡是一种有机物，石蜡烃的氯化衍生物，具有低挥发性、阻燃、电绝缘性良好、价廉等优点，可用作阻燃剂和聚氯乙烯辅助增塑剂，白色至淡黄色固体粉末，无臭无味，无毒，所述氯化石蜡加入后搅拌20-25分钟。
进一步地，所述是以粘料为主剂，配合各种固化剂、增塑剂、填料、溶剂、防腐剂、稳定剂和偶联剂等助剂配制而成，所述胶联体加入后再加入纯净水，所述纯净水加入后搅拌30-35分钟得到硅烷树脂胶防水涂料。
进一步地，所述硅烷树脂胶防水涂料搅拌时将配料加热至30-35℃，所述硅烷树脂胶防水涂料配比完成后，通过分装机进行分装，使用时，通过双成玻纤布反复刷涂4-5遍。
本申请的有益效果是：采用了重质碳酸钙、轻质碳酸钙、氯化石蜡等无毒、无味、无臭的原料，避免配比完成后，硅烷树脂胶防水涂料气味具有难闻的气味，且作为主要远离的醋丙乳液无甲醛，健康环保，解决了现有的硅烷树脂胶防水涂料气味较为难闻的问题，提高了防水涂料的实用性，避免防水涂料涂抹后的气味造成使用者的不适。
具体实施方式
为了使本技术领域的人员更好地理解本申请方案，下面将结合本申请实施例，对本申请实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本申请一部分的实施例，而不是全部的实施例。基于本申请中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都应当属于本申请保护的范围。
需要说明的是，本申请的说明书和权利要求书中的术语“第一”、“第二”等是用于区别类似的对象，而不必用于描述特定的顺序或先后次序。应该理解这样使用的数据在适当情况下可以互换，以便这里描述的本申请的实施例。此外，术语“包括”和“具有”以及他们的任何变形，意图在于覆盖不排他的包含，例如，包含了一系列步骤或单元的过程、方法、系统、产品或设备不必限于清楚地列出的那些步骤或单元，而是可包括没有清楚地列出的或对于这些过程、方法、产品或设备固有的其它步骤或单元。
在本申请中，术语“上”、“下”、“左”、“右”、“前”、“后”、“顶”、“底”、“内”、“外”、“中”、“竖直”、“水平”、“横向”、“纵向”等指示的方位或位置关系。这些术语主要是为了更好地描述本申请及其实施例，并非用于限定所指示的装置、元件或组成部分必须具有特定方位，或以特定方位进行构造和操作。
并且，上述部分术语除了可以用于表示方位或位置关系以外，还可能用于表示其他含义，例如术语“上”在某些情况下也可能用于表示某种依附关系或连接关系。对于本领域普通技术人员而言，可以根据具体情况理解这些术语在本申请中的具体含义。
此外，术语“安装”、“设置”、“设有”、“连接”、“相连”、“套接”应做广义理解。例如，可以是固定连接，可拆卸连接，或整体式构造；可以是机械连接，或电连接；可以是直接相连，或者是通过中间媒介间接相连，又或者是两个装置、元件或组成部分之间内部的连通。对于本领域普通技术人员而言，可以根据具体情况理解上述术语在本申请中的具体含义。
需要说明的是，在不冲突的情况下，本申请中的实施例及实施例中的特征可以相互组合。下面将结合实施例来详细说明本申请。
实施例一：
所述硅烷树脂胶防水涂料配方包括醋丙乳液500公斤、膨润土20公斤、重钙300公斤、轻钙80公斤、二辛脂35公斤、乳化剂40公斤、氯化石蜡20 公斤、胶联体2公斤、纯净水200公斤；
所述醋丙乳液是以醋酸乙烯和丙烯酸丁酯为主要功能单体共聚而成的水性高分子树脂，所述醋丙乳液为五五固含量，即醋丙乳液中的固体和液体比例为1:1；
所述膨润土是以蒙脱石为主要矿物成分的非金属矿产，蒙脱石结构是由两个硅氧四面体夹一层铝氧八面体组成的2：1型晶体结构，所述膨润土在加入时先用等比纯净水泡开，然后加入膨润土中搅拌20分钟；
所述重钙为重质碳酸钙，是由天然碳酸盐矿物如方解石、大理石、石灰石磨碎而成，是常用的粉状无机填料，具有化学纯度高、惰性大、不易化学反应、热稳定性好、在400℃以下不会分解、白度高、吸油率低、折光率低、质软、干燥、不含结晶水、硬度低磨耗值小、无毒、无味、无臭、分散性好等优点；
所述轻钙是轻质碳酸钙，是将石灰石等原料段烧生成石灰和二氧化碳，再加水消化石灰生成石灰乳，通入二氧化碳碳化石灰乳生成碳酸钙沉淀，经脱水、干燥和粉碎制得，所述重钙和轻钙加入后搅拌30分钟；
所述二辛脂为邻苯二甲酸二辛酯，是一种无色油状液体，比重 0.9861(20/20)，不溶于水，溶于乙醇、乙醚、矿物油等大多数有机溶剂；
所述乳化剂是能使两种或两种以上互不相溶的组分的混合液体形成稳定的乳状液的一类物质，在乳化过程中，分散相以微滴(微米级)的形式分散在连续相中，乳化剂降低了混合体系中各组分的界面张力，并在微滴表面形成较坚固的薄膜或由于乳化剂给出的电荷而在微滴表面形成双电层，阻止微滴彼此聚集，而保持均匀的乳状液，所述二辛脂和乳化剂加入后搅拌30-35 分钟
所述氯化石蜡是一种有机物，石蜡烃的氯化衍生物，具有低挥发性、阻燃、电绝缘性良好、价廉等优点，可用作阻燃剂和聚氯乙烯辅助增塑剂，白色至淡黄色固体粉末，无臭无味，无毒，所述氯化石蜡加入后搅拌20-25分钟；
所述是以粘料为主剂，配合各种固化剂、增塑剂、填料、溶剂、防腐剂、稳定剂和偶联剂等助剂配制而成，所述胶联体加入后再加入纯净水，所述纯净水加入后搅拌30分钟得到硅烷树脂胶防水涂料；
所述硅烷树脂胶防水涂料搅拌时将配料加热至30℃，所述硅烷树脂胶防水涂料配比完成后，通过分装机进行分装，使用时，通过双成玻纤布反复刷涂4遍。
实施例二：
所述硅烷树脂胶防水涂料配方包括醋丙乳液520公斤、膨润土122公斤、重钙320公斤、轻钙85公斤、二辛脂37公斤、乳化剂42公斤、氯化石蜡22 公斤、胶联体2公斤、纯净水220公斤；
所述醋丙乳液是以醋酸乙烯和丙烯酸丁酯为主要功能单体共聚而成的水性高分子树脂，所述醋丙乳液为五五固含量，即醋丙乳液中的固体和液体比例为1:1；
所述膨润土是以蒙脱石为主要矿物成分的非金属矿产，蒙脱石结构是由两个硅氧四面体夹一层铝氧八面体组成的2：1型晶体结构，所述膨润土在加入时先用等比纯净水泡开，然后加入膨润土中搅拌25分钟；
所述重钙为重质碳酸钙，是由天然碳酸盐矿物如方解石、大理石、石灰石磨碎而成，是常用的粉状无机填料，具有化学纯度高、惰性大、不易化学反应、热稳定性好、在400℃以下不会分解、白度高、吸油率低、折光率低、质软、干燥、不含结晶水、硬度低磨耗值小、无毒、无味、无臭、分散性好等优点；
所述轻钙是轻质碳酸钙，是将石灰石等原料段烧生成石灰和二氧化碳，再加水消化石灰生成石灰乳，通入二氧化碳碳化石灰乳生成碳酸钙沉淀，经脱水、干燥和粉碎制得，所述重钙和轻钙加入后搅拌35分钟；
所述二辛脂为邻苯二甲酸二辛酯，是一种无色油状液体，比重 0.9861(20/20)，不溶于水，溶于乙醇、乙醚、矿物油等大多数有机溶剂；
所述乳化剂是能使两种或两种以上互不相溶的组分的混合液体形成稳定的乳状液的一类物质，在乳化过程中，分散相以微滴(微米级)的形式分散在连续相中，乳化剂降低了混合体系中各组分的界面张力，并在微滴表面形成较坚固的薄膜或由于乳化剂给出的电荷而在微滴表面形成双电层，阻止微滴彼此聚集，而保持均匀的乳状液，所述二辛脂和乳化剂加入后搅拌30-35 分钟；
所述氯化石蜡是一种有机物，石蜡烃的氯化衍生物，具有低挥发性、阻燃、电绝缘性良好、价廉等优点，可用作阻燃剂和聚氯乙烯辅助增塑剂，白色至淡黄色固体粉末，无臭无味，无毒，所述氯化石蜡加入后搅拌25分钟；
所述是以粘料为主剂，配合各种固化剂、增塑剂、填料、溶剂、防腐剂、稳定剂和偶联剂等助剂配制而成，所述胶联体加入后再加入纯净水，所述纯净水加入后搅拌35分钟得到硅烷树脂胶防水涂料；
所述硅烷树脂胶防水涂料搅拌时将配料加热至35℃，所述硅烷树脂胶防水涂料配比完成后，通过分装机进行分装，使用时，通过双成玻纤布反复刷涂5遍。
涉及到电路和电子元器件和模块均为现有技术，本领域技术人员完全可以实现，无需赘言，本申请保护的内容也不涉及对于软件和方法的改进。
以上所述仅为本申请的优选实施例而已，并不用于限制本申请，对于本领域的技术人员来说，本申请可以有各种更改和变化。凡在本申请的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本申请的保护范围之内。
Claims (10)
1.一种硅烷树脂胶防水涂料，其特征在于：所述硅烷树脂胶防水涂料配方包括醋丙乳液480-520公斤、膨润土18-22公斤、重钙280-320公斤、轻钙75-85公斤、二辛脂32-37公斤、乳化剂38-42公斤、氯化石蜡18-22公斤、胶联体1.8-2公斤、纯净水180-220公斤。
2.根据权利要求1所述的一种硅烷树脂胶防水涂料，其特征在于：所述醋丙乳液是以醋酸乙烯和丙烯酸丁酯为主要功能单体共聚而成的水性高分子树脂，所述醋丙乳液为五五固含量，即醋丙乳液中的固体和液体比例为1:1。
3.根据权利要求1所述的一种硅烷树脂胶防水涂料，其特征在于：所述膨润土是以蒙脱石为主要矿物成分的非金属矿产，蒙脱石结构是由两个硅氧四面体夹一层铝氧八面体组成的2：1型晶体结构，所述膨润土在加入时先用等比纯净水泡开，然后加入膨润土中搅拌20-25分钟。
4.根据权利要求1所述的一种硅烷树脂胶防水涂料，其特征在于：所述重钙为重质碳酸钙，是由天然碳酸盐矿物如方解石、大理石、石灰石磨碎而成，是常用的粉状无机填料，具有化学纯度高、惰性大、不易化学反应、热稳定性好、在400℃以下不会分解、白度高、吸油率低、折光率低、质软、干燥、不含结晶水、硬度低磨耗值小、无毒、无味、无臭、分散性好等优点。
5.根据权利要求1所述的一种硅烷树脂胶防水涂料，其特征在于：所述轻钙是轻质碳酸钙，是将石灰石等原料段烧生成石灰和二氧化碳，再加水消化石灰生成石灰乳，通入二氧化碳碳化石灰乳生成碳酸钙沉淀，经脱水、干燥和粉碎制得，所述重钙和轻钙加入后搅拌30-35分钟。
6.根据权利要求1所述的一种硅烷树脂胶防水涂料，其特征在于：所述二辛脂为邻苯二甲酸二辛酯，是一种无色油状液体，比重0.9861(20/20)，不溶于水，溶于乙醇、乙醚、矿物油等大多数有机溶剂。
7.根据权利要求1所述的一种硅烷树脂胶防水涂料，其特征在于：所述乳化剂是能使两种或两种以上互不相溶的组分的混合液体形成稳定的乳状液的一类物质，在乳化过程中，分散相以微滴(微米级)的形式分散在连续相中，乳化剂降低了混合体系中各组分的界面张力，并在微滴表面形成较坚固的薄膜或由于乳化剂给出的电荷而在微滴表面形成双电层，阻止微滴彼此聚集，而保持均匀的乳状液，所述二辛脂和乳化剂加入后搅拌30-35分钟。
8.根据权利要求1所述的一种硅烷树脂胶防水涂料，其特征在于：所述氯化石蜡是一种有机物，石蜡烃的氯化衍生物，具有低挥发性、阻燃、电绝缘性良好、价廉等优点，可用作阻燃剂和聚氯乙烯辅助增塑剂，白色至淡黄色固体粉末，无臭无味，无毒，所述氯化石蜡加入后搅拌20-25分钟。
9.根据权利要求1所述的一种硅烷树脂胶防水涂料，其特征在于：所述是以粘料为主剂，配合各种固化剂、增塑剂、填料、溶剂、防腐剂、稳定剂和偶联剂等助剂配制而成，所述胶联体加入后再加入纯净水，所述纯净水加入后搅拌30-35分钟得到硅烷树脂胶防水涂料。
10.根据权利要求1所述的一种硅烷树脂胶防水涂料，其特征在于：所述硅烷树脂胶防水涂料搅拌时将配料加热至30-35℃，所述硅烷树脂胶防水涂料配比完成后，通过分装机进行分装，使用时，通过双成玻纤布反复刷涂4-5遍。