CN115071244A - 一种防火保温板 - Google Patents
一种防火保温板 Download PDFInfo
- Publication number
- CN115071244A CN115071244A CN202210608888.1A CN202210608888A CN115071244A CN 115071244 A CN115071244 A CN 115071244A CN 202210608888 A CN202210608888 A CN 202210608888A CN 115071244 A CN115071244 A CN 115071244A
- Authority
- CN
- China
- Prior art keywords
- insulation board
- paper
- adhesive film
- film paper
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及防火板技术领域,尤其是一种防火保温板;包括保温板本体和位于保温板本体表面的浸胶纸层,所述保温板本体为聚苯乙烯泡沫保温板,所述浸胶纸为三聚氰胺浸胶纸,其包括表层胶膜纸、装饰层胶膜纸和底层胶膜纸,所述表层胶膜纸的纸张定量为32‑60g/m2,其挥发物含量为4.8‑5%,装饰胶膜纸的纸张定量为75‑85g/m2,其挥发物含量为3.5‑4.5%,所述底层胶膜纸的纸张定量为100‑115g/m2,其挥发物含量为5‑5.5%;本发明中制备的防火保温板具有较好的防火性能、较低的收缩率和吸水率,具有加大的应用价值和应用前景,且由于采用了挥发物较低的浸胶纸,制备的防火保温板的板面没有湿花。
Description
技术领域
本发明涉及防火板技术领域,尤其是一种防火保温板。
背景技术
防火板是表面装饰用耐火建材,防火板是原纸(钛粉纸、牛皮纸)经过三聚氰胺与酚醛树脂的浸渍工艺,经过高温高压环境制成。且防火保温板的保温和隔热效果优异,是玻璃和混凝土不可比拟的,板材的质量如同金属一样强硬,但是重量仅仅和木材相仿,在搬运和安装过程中可以节省工时,所以防火保温板应用广泛。
目前使用比较多的是酚醛树脂防火板,其主要是以酚醛树脂作为主体原料,在添加剂、改性剂、催化剂作用下,充分混合,在规定温度下固化得到所需的防火板。然而,现有的酚醛树脂防火板主要存在以下不足,板面有湿花(水汽),边缘较为严重,其产生的主要原因有以下几点:
1.浸胶纸干燥后挥发物含量太高;
2.印刷木纹的油墨或染料所用的溶剂不合适;
3.浸胶干燥后的胶膜纸吸湿(回潮)。
发明内容
本发明的目的是:克服现有技术中的不足,提供一种板面没有湿花的防火保温板。
本发明中采用的技术方案如下:
一种防火保温板,包括保温板本体和位于保温板本体表面的浸胶纸层,所述保温板本体为聚苯乙烯泡沫保温板,其质量份组成如下:硫酸铝650-720份、氧化铝120-180份、缓凝剂1.2-4.8份、石墨聚苯乙烯泡沫颗粒100份、有机硅6-8份、石墨12-18份、减水剂2-5份、玻璃微珠0.1-2.4份;
所述浸胶纸为三聚氰胺浸胶纸,其包括表层胶膜纸、装饰层胶膜纸和底层胶膜纸,所述表层胶膜纸的纸张定量为32-60g/m2,其挥发物含量为4.8-5%,装饰胶膜纸的纸张定量为75-85g/m2,其挥发物含量为3.5-4.5%,所述底层胶膜纸的纸张定量为100-115g/m2,其挥发物含量为5-5.5%。
进一步的,所述表层胶膜纸的浸胶量为220-250%,装饰胶膜纸的浸胶量为90-100%,底层胶膜纸的浸胶量为100-120%。
进一步的,所述表层胶膜纸的流展为24-28%、装饰层胶膜纸的流展为1.5-2.5%、底层胶膜纸的流展为2.5-4.5。
进一步的,所述有机硅选自丙烯基三乙氧基硅烷、三维网状结构的二氧化硅气凝胶中的一种。
进一步的,所述三维网状的二氧化硅气凝胶的孔径率为90-99.8%,其比表面积为850-1000m2/g,热导率TC为12mW/m。
进一步的,所述三维网状结构的二氧化硅气凝胶采用超临界干燥。超临界干燥通过压力和温度的控制,使溶剂在干燥过程中达到其本身的临界点,完成液相至气相的超临界的转变,整个过程中无明显的表面张力,在维持骨架结构的前提下完成湿凝胶向气凝胶的转变。
进一步的,所述减水剂选自三乙醇胺、甲酸钙、乙酸钙、尿素、草酸中的一种。
进一步的,所述石墨聚苯乙烯泡沫颗粒的粒径大小为0.8-1.2微米,所述石墨聚苯乙烯泡沫颗粒的导热系数<0.032。
进一步的,所述缓凝剂选自葡萄糖酸钠与六偏磷酸钠复配物或柠檬酸钠和三聚磷酸钠的复配物。
进一步的,葡萄糖酸钠与六偏磷酸钠的摩尔比为1:1,柠檬酸钠和三聚磷酸钠的摩尔比为1:1。
采用本发明中的技术方案的有益效果是:
本发明中制备的防火保温板具有较好的防火性能、较低的收缩率和吸水率,具有加大的应用价值和应用前景,且由于采用了挥发物较低的浸胶纸,制备的防火保温板的板面没有湿花。
具体实施方式
下面通过实施例的方式进一步说明本发明,但并不因此将本发明限制在所述的实施例范围之中。下列实施例中未注明具体条件的实验方法,按照常规方法和条件,或按照商品说明书选择。如没有特别强调温度,通常指在室温下进行反应,本发明中的室温是指10~30℃。
下述实施例中所使用的实验方法如无特殊说明,均为常规方法。
下述实施例中所使用的材料及试剂等,如无特殊说明,均可从商业途径买到。
实施例1
一种防火保温板,包括保温板本体和位于保温板本体表面的浸胶纸层,保温板本体为聚苯乙烯泡沫保温板,其质量份组成如下:硫酸铝650份、氧化铝120份、缓凝剂1.2份、石墨聚苯乙烯泡沫颗粒100份、有机硅6份、石墨12份、减水剂2份、玻璃微珠0.1份;
浸胶纸为三聚氰胺浸胶纸,其包括表层胶膜纸、装饰层胶膜纸和底层胶膜纸,所述表层胶膜纸的纸张定量为32g/m2,其挥发物含量为4.8%,装饰胶膜纸的纸张定量为75g/m2,其挥发物含量为3.5%,底层胶膜纸的纸张定量为100g/m2,其挥发物含量为5%;
表层胶膜纸的浸胶量为220%,装饰胶膜纸的浸胶量为90%,底层胶膜纸的浸胶量为100%,表层胶膜纸的流展为24%、装饰层胶膜纸的流展为1.5%、底层胶膜纸的流展为2.5。
其中,有机硅选用丙烯基三乙氧基硅烷。
其中,减水剂选用三乙醇胺种。
其中,石墨聚苯乙烯泡沫颗粒的粒径大小为0.8-1.2微米,所述石墨聚苯乙烯泡沫颗粒的导热系数<0.032。
其中,缓凝剂选自葡萄糖酸钠与六偏磷酸钠复配物,葡萄糖酸钠与六偏磷酸钠的摩尔比为1:1。
实施例2
一种防火保温板,包括保温板本体和位于保温板本体表面的浸胶纸层,保温板本体为聚苯乙烯泡沫保温板,其质量份组成如下:硫酸铝680份、氧化铝130份、缓凝剂1.8份、石墨聚苯乙烯泡沫颗粒100份、有机硅6.2份、石墨12份、减水剂2.5份、玻璃微珠0.5份;
浸胶纸为三聚氰胺浸胶纸,其包括表层胶膜纸、装饰层胶膜纸和底层胶膜纸,所述表层胶膜纸的纸张定量为38g/m2,其挥发物含量为4.8%,装饰胶膜纸的纸张定量为75g/m2,其挥发物含量为3.5%,底层胶膜纸的纸张定量为100g/m2,其挥发物含量为5%;
表层胶膜纸的浸胶量为230%,装饰胶膜纸的浸胶量为92%,底层胶膜纸的浸胶量为105%,表层胶膜纸的流展为24%、装饰层胶膜纸的流展为1.5%、底层胶膜纸的流展为2.5。
其中,有机硅选用三维网状结构的二氧化硅气凝胶中的,三维网状的二氧化硅气凝胶的孔径率为95%,其比表面积为850m2/g,热导率TC为12mW/m,三维网状结构的二氧化硅气凝胶采用超临界干燥。超临界干燥通过压力和温度的控制,使溶剂在干燥过程中达到其本身的临界点,完成液相至气相的超临界的转变,整个过程中无明显的表面张力,在维持骨架结构的前提下完成湿凝胶向气凝胶的转变。
其中,减水剂选用甲酸钙。
其中,石墨聚苯乙烯泡沫颗粒的粒径大小为0.8微米,所述石墨聚苯乙烯泡沫颗粒的导热系数<0.032。
其中,缓凝剂选自葡萄糖酸钠与六偏磷酸钠复配物葡萄糖酸钠与六偏磷酸钠的摩尔比为1:1。
实施例3
一种防火保温板,包括保温板本体和位于保温板本体表面的浸胶纸层,保温板本体为聚苯乙烯泡沫保温板,其质量份组成如下:硫酸铝680份、氧化铝150份、缓凝剂2.4份、石墨聚苯乙烯泡沫颗粒100份、有机硅7份、石墨15份、减水剂3.5份、玻璃微珠1.8份;
浸胶纸为三聚氰胺浸胶纸,其包括表层胶膜纸、装饰层胶膜纸和底层胶膜纸,所述表层胶膜纸的纸张定量为45g/m2,其挥发物含量为5%,装饰胶膜纸的纸张定量为80g/m2,其挥发物含量为4%,底层胶膜纸的纸张定量为110g/m2,其挥发物含量为5%;
表层胶膜纸的浸胶量为230%,装饰胶膜纸的浸胶量为95%,底层胶膜纸的浸胶量为110%,表层胶膜纸的流展为26%、装饰层胶膜纸的流展为1.8%、底层胶膜纸的流展为3。
其中,有机硅选用三维网状结构的二氧化硅气凝胶中的一种,三维网状的二氧化硅气凝胶的孔径率为99.8%,其比表面积为900m2/g,热导率TC为12mW/m,三维网状结构的二氧化硅气凝胶采用超临界干燥。超临界干燥通过压力和温度的控制,使溶剂在干燥过程中达到其本身的临界点,完成液相至气相的超临界的转变,整个过程中无明显的表面张力,在维持骨架结构的前提下完成湿凝胶向气凝胶的转变。
其中,减水剂选用尿素。
其中,石墨聚苯乙烯泡沫颗粒的粒径大小为0.8-1.2微米,所述石墨聚苯乙烯泡沫颗粒的导热系数<0.032。
其中,缓凝剂选用柠檬酸钠和三聚磷酸钠的复配物,柠檬酸钠和三聚磷酸钠的摩尔比为1:1。
实施例4
一种防火保温板,包括保温板本体和位于保温板本体表面的浸胶纸层,保温板本体为聚苯乙烯泡沫保温板,其质量份组成如下:硫酸铝700份、氧化铝160份、缓凝剂4份、石墨聚苯乙烯泡沫颗粒100份、有机硅7.5份、石墨16份、减水剂4份、玻璃微珠2份;
浸胶纸为三聚氰胺浸胶纸,其包括表层胶膜纸、装饰层胶膜纸和底层胶膜纸,所述表层胶膜纸的纸张定量为50g/m2,其挥发物含量为5%,装饰胶膜纸的纸张定量为80g/m2,其挥发物含量为4%,底层胶膜纸的纸张定量为110g/m2,其挥发物含量为5.5%;
表层胶膜纸的浸胶量为240%,装饰胶膜纸的浸胶量为95%,底层胶膜纸的浸胶量为115%,表层胶膜纸的流展为26%、装饰层胶膜纸的流展为2.4%、底层胶膜纸的流展为4。
其中,有机硅选用三维网状结构的二氧化硅气凝胶中的一种,三维网状的二氧化硅气凝胶的孔径率为99.8%,其比表面积为1000m2/g,热导率TC为12mW/m,三维网状结构的二氧化硅气凝胶采用超临界干燥。超临界干燥通过压力和温度的控制,使溶剂在干燥过程中达到其本身的临界点,完成液相至气相的超临界的转变,整个过程中无明显的表面张力,在维持骨架结构的前提下完成湿凝胶向气凝胶的转变。
其中,减水剂选用草酸。
其中,石墨聚苯乙烯泡沫颗粒的粒径大小为0.8-1.2微米,所述石墨聚苯乙烯泡沫颗粒的导热系数<0.032。
其中,缓凝剂选用柠檬酸钠和三聚磷酸钠的复配物,柠檬酸钠和三聚磷酸钠的摩尔比为1:1。
实施例5
一种防火保温板,包括保温板本体和位于保温板本体表面的浸胶纸层,保温板本体为聚苯乙烯泡沫保温板,其质量份组成如下:硫酸铝720份、氧化铝180份、缓凝剂4.8份、石墨聚苯乙烯泡沫颗粒100份、有机硅8份、石墨18份、减水剂5份、玻璃微珠2.4份;
浸胶纸为三聚氰胺浸胶纸,其包括表层胶膜纸、装饰层胶膜纸和底层胶膜纸,所述表层胶膜纸的纸张定量为60g/m2,其挥发物含量为5%,装饰胶膜纸的纸张定量为85g/m2,其挥发物含量为4.5%,底层胶膜纸的纸张定量为115g/m2,其挥发物含量为5.5%;
表层胶膜纸的浸胶量为250%,装饰胶膜纸的浸胶量为100%,底层胶膜纸的浸胶量为120%,表层胶膜纸的流展为28%、装饰层胶膜纸的流展为2.5%、底层胶膜纸的流展为4.5。
其中,有机硅选用三维网状结构的二氧化硅气凝胶中的一种,三维网状的二氧化硅气凝胶的孔径率为90-99.8%,其比表面积为850-1000m2/g,热导率TC为12mW/m,三维网状结构的二氧化硅气凝胶采用超临界干燥。超临界干燥通过压力和温度的控制,使溶剂在干燥过程中达到其本身的临界点,完成液相至气相的超临界的转变,整个过程中无明显的表面张力,在维持骨架结构的前提下完成湿凝胶向气凝胶的转变。
其中,减水剂选用草酸。
其中,石墨聚苯乙烯泡沫颗粒的粒径大小为0.8-1.2微米,所述石墨聚苯乙烯泡沫颗粒的导热系数<0.032。
其中,缓凝剂选用柠檬酸钠和三聚磷酸钠的复配物,柠檬酸钠和三聚磷酸钠的摩尔比为1:1。
性能测试
对实施例1-5中制备的防火保温板进行吸水率、导热系数、收缩率以及固化效果实验,吸水率测试方法为GB/T8810-2005,导热系数测试方法为GB/T10801.1-2002,收缩率测试方法为GB/T15585-1995,具体参数见表1。
表1
吸水率/% | 导热系数(λ) | 收缩率% | 湿花 | |
实施例1 | 1.1 | 0.032W/m·K | 0.15 | 无 |
实施例2 | 0.6 | 0.027W/m·K | 0.14 | 无 |
实施例3 | 0.5 | 0.021W/m·K | 0.13 | 无 |
实施例4 | 0.8 | 0.032W/m·K | 0.14 | 无 |
实施例5 | 0.9 | 0.032W/m·K | 0.15 | 无 |
表1中的测试结果显示,本发明中制备的防火保温板具有较好的防火性能、较低的收缩率和吸水率,具有加大的应用价值和应用前景,且由于采用了挥发物较低的浸胶纸,制备的防火保温板的板面没有湿花。
以上所述实施例仅表达了本发明的几种实施方式,其描述较为具体和详细,但并不能因此而理解为对发明专利范围的限制。应当指出的是,对于本领域的普通技术人员来说,在不脱离本发明构思的前提下,还可以做出若干变形和改进,这些都属于本发明的保护范围。因此,本发明的保护范围应以所附权利要求为准。
Claims (10)
1.一种防火保温板,其特征在于:包括保温板本体和位于保温板本体表面的浸胶纸层,所述保温板本体为聚苯乙烯泡沫保温板,其质量份组成如下:硫酸铝650-720份、氧化铝120-180份、缓凝剂1.2-4.8份、石墨聚苯乙烯泡沫颗粒100份、有机硅6-8份、石墨12-18份、减水剂2-5份、玻璃微珠0.1-2.4份;
所述浸胶纸为三聚氰胺浸胶纸,其包括表层胶膜纸、装饰层胶膜纸和底层胶膜纸,所述表层胶膜纸的纸张定量为32-60g/m2,其挥发物含量为4.8-5%,装饰胶膜纸的纸张定量为75-85g/m2,其挥发物含量为3.5-4.5%,所述底层胶膜纸的纸张定量为100-115g/m2,其挥发物含量为5-5.5%。
2.根据权利要求1所述的一种防火保温板,其特征在于:所述表层胶膜纸的浸胶量为220-250%,装饰胶膜纸的浸胶量为90-100%,底层胶膜纸的浸胶量为100-120%。
3.根据权利要求1所述的一种防火保温板,其特征在于:所述表层胶膜纸的流展为24-28%、装饰层胶膜纸的流展为1.5-2.5%、底层胶膜纸的流展为2.5-4.5。
4.根据权利要求1所述的一种防火保温板,其特征在于:所述有机硅选自丙烯基三乙氧基硅烷、三维网状结构的二氧化硅气凝胶中的一种。
5.根据权利要求4所述的一种防火保温板,其特征在于:所述三维网状的二氧化硅气凝胶的孔径率为90-99.8%,其比表面积为850-1000m2/g,热导率TC为12mW/m。
6.根据权利要求4所述的一种防火保温板,其特征在于:所述三维网状结构的二氧化硅气凝胶采用超临界干燥。
7.根据权利要求1所述的一种防火保温板,其特征在于:所述减水剂选自三乙醇胺、甲酸钙、乙酸钙、尿素、草酸中的一种。
8.根据权利要求1所述的一种防火保温板,其特征在于:所述石墨聚苯乙烯泡沫颗粒的粒径大小为0.8-1.2微米,所述石墨聚苯乙烯泡沫颗粒的导热系数<0.032。
9.根据权利要求1所述的一种防火保温板,其特征在于:所述缓凝剂选自葡萄糖酸钠与六偏磷酸钠复配物或柠檬酸钠和三聚磷酸钠的复配物。
10.根据权利要求9所述的一种防火保温板,其特征在于:葡萄糖酸钠与六偏磷酸钠的摩尔比为1:1,柠檬酸钠和三聚磷酸钠的摩尔比为1:1。