CN115003504A - 用于运输或储存氢气的多层结构体 - Google Patents

用于运输或储存氢气的多层结构体 Download PDF

Info

Publication number
CN115003504A
CN115003504A CN202180011517.9A CN202180011517A CN115003504A CN 115003504 A CN115003504 A CN 115003504A CN 202180011517 A CN202180011517 A CN 202180011517A CN 115003504 A CN115003504 A CN 115003504A
Authority
CN
China
Prior art keywords
polyamide
layer
multilayer structure
polymer
sealing layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN202180011517.9A
Other languages
English (en)
Other versions
CN115003504B (zh
Inventor
N.杜福尔
P.但格
A.古皮尔
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Arkema France SA
Original Assignee
Arkema France SA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Arkema France SA filed Critical Arkema France SA
Publication of CN115003504A publication Critical patent/CN115003504A/zh
Application granted granted Critical
Publication of CN115003504B publication Critical patent/CN115003504B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及用于运输、分配和储存氢气、特别地用于储存氢气的多层结构体，其从内到外包括至少一个密封层(1)和至少一个复合增强层(2)，所述最里面的复合增强层(2)被焊接到所述最外面的相邻密封层(1)，所述密封层(1)由组合物组成，所述组合物主要包括：至少一种半结晶聚酰胺热塑性聚合物P1i，i＝1至n，n为密封层的数量，排除酰胺聚醚嵌段(PEBA)；相对于组合物的总重量的最高达50重量％的抗冲改性剂、特别地最高达小于15重量％的抗冲改性剂、特别地最高达12重量％的抗冲改性剂；相对于组合物的总重量的最高达1.5重量％的增塑剂，其中各密封层的所述至少一种聚酰胺热塑性聚合物可相同或不同，并且所述复合增强层的至少一个由浸渍有组合物的连续纤维形式的纤维材料组成，所述组合物主要包括至少一种半结晶聚酰胺聚合物P2j，j＝1至m，m为增强层的数量，其中所述最外面的相邻密封层(1)的聚酰胺的每酰胺官能团的碳原子数与所述最里面的增强层(2)的聚酰胺的每酰胺官能团的碳原子数相差至多20％。

Description

用于运输或储存氢气的多层结构体
技术领域
本专利申请涉及运输(输送)、分配、或储存氢气(氢)、特别地用于分配或储存氢气的多层复合结构体、和用于制造其的方法。
背景技术
氢气罐当前正在引起来自众多制造商、尤其是汽车行业中的制造商的许多关注。寻求的目标之一是提出越来越少地引起污染的车辆。因而，包括电池的电动或混合动力车旨在逐步地代替内燃机车诸如汽油或柴油车。事实已证明，电池是相对复杂的车辆部件。取决于电池在车辆中的安置(位置)，保护它免受冲击以及免受可具有极端温度和可变湿度的外部环境可为必要的。避免任何火焰的风险也是必要的。
另外，如下是重要的：其运行温度不超过55℃以不破坏电池的单元电池和维护其寿命。相反，例如在冬天，提高电池温度以优化其运行可为必要的。
而且，电动车如今仍遭受几个问题，即电池续航里程、稀土金属在这些电池中的使用、用于其的资源不是无穷的、比填充罐花费的时间长度长得多的再充电时间、以及为了能够将电池再充电的在各个国家中的电力生产的问题。
因此氢气是电动电池的替代物，因为氢气可通过燃料电池被转换成电力且因而驱动电动车。
氢气罐经常由必须防止氢气渗透出去的金属衬里(或密封层)组成。展望的罐的类型之一，称作IV型，基于复合物缠绕在其周围的热塑性衬里。
它们的基本原理是将密封和机械强度这两种基本功能分开并且将它们彼此独立地管理。在该类型的罐中，由热塑性树脂制成的衬里(或密封护套)与也称作增强护套或层的由包裹在热塑性或热固性基体中的纤维(玻璃、芳族聚酰胺、碳)组成的增强结构组合，其使得可在高得多的压力下运行，同时减小重量和避免万一发生严重的外部攻击时的爆炸性破裂的风险。
衬里必须具有一些基本特性：
通过挤出吹塑、滚塑(旋转模塑)、注塑或挤出而变形(成型)的可能性；
低的对于氢气的渗透率，实际上，衬里的渗透率在限制从罐的氢气损失方面是关键因素；
在低温(-40至-70℃)下的良好的机械性质(疲劳)；
在120℃下的耐热性。
实际上，如下是必要的：提高氢气罐的填充速度，其应粗略地等于用于内燃机的燃料罐的填充速度(约3至5分钟)，但是该在速度方面的提高导致罐的更显著的加热，所述罐然后达到约100℃的温度。
第一代的IV型罐使用基于高密度聚乙烯(HDPE)的衬里。
然而，HDPE具有如下的缺点：具有太低的熔点和高的对于氢气的渗透率，其提出了在耐热性方面有新的要求的问题，并且未使得提高罐的填充速度是可能的。
基于聚酰胺PA6的衬里已经发展了许多年。
然而，PA6具有如下缺点：具有低的耐寒性。
WO18155491描述了具有三层结构的氢气运输组件，其内层为由如下组成的组合物：PA11、15至50％的抗冲改性剂和1至3％的增塑剂，或者没有(不含)增塑剂，其具有氢气阻挡性质、良好的柔性和在低温下的耐久性。然而，该结构适于用于运输氢气、但不用于存储氢气的管道。
因而，仍然存在如下需要：一方面，优化复合物的基体以优化其在高温下的机械强度，且另一方面，优化构成密封护套的材料，以优化其工作(操作)温度。因而，构成将被实施的密封衬里的材料的组成的任选的修改必须不导致与当今所实践的相比该衬里的制造温度(挤出吹塑、注塑、滚塑等)的显著增加。
这些问题通过提供本发明的打算用于运输、分配或储存氢气的多层结构体来解决。
在整个说明书中，术语“衬里”和“密封护套”具有相同的含义。
因此，本发明涉及打算用于运输、分配和储存氢气、特别地用于储存氢气的多层结构体，其从内到外包括密封层(1)和至少一个复合增强层(2)，
所述最里面的复合增强层(2)被焊接到所述最外面的相邻密封层(1)，
所述密封层(1)由组合物组成，所述组合物主要包括：
至少一种半结晶聚酰胺热塑性聚合物P1i，i＝1至n，其中n为密封层的数量，排除聚醚嵌段酰胺(PEBA)，
相对于组合物的总重量的最高达50重量％的抗冲改性剂、尤其是最高达小于15重量％的抗冲改性剂、特别地最高达12重量％的抗冲改性剂，
相对于组合物的总重量的最高达1.5重量％的增塑剂，
各密封层中的所述至少一种聚酰胺热塑性聚合物可相同或不同，
并且所述复合增强层的至少一个由浸渍有组合物的连续纤维形式的纤维材料组成，所述组合物主要包括至少一种半结晶聚酰胺聚合物P2j，j＝1至m，m为增强层的数量，
所述最外面的相邻密封层(1)的聚酰胺的每酰胺官能团的碳原子数与所述最里面的增强层(2)的聚酰胺的每酰胺官能团的碳原子数相差至多20％。
因此，本发明人已出乎意料地发现，对于密封层使用包括有限比例的抗冲改性剂和增塑剂的半结晶聚酰胺热塑性聚合物P1i(特别地短链或长链的)和对于复合物的基体使用半结晶热塑性聚合物P2j(所述复合物被焊接到密封层)，并且密封层和相邻的复合增强层的两种聚合物P1i和P2j在它们的每酰胺官能团的碳原子数方面相差至多20％，使得可获得适合用于运输、分配或储存氢气、特别地用于储存氢气的结构体以及最大使用温度的提高，其可达到最高达120℃，从而使得可提高罐的填充速度。
“多层结构体”意指包括如下或由如下组成的罐：若干个(几个)层，即若干个密封层和若干个增强层，或者一个密封层和若干个增强层，或者若干个密封层和一个增强层，或者一个密封层和一个增强层。
多层结构体因此被理解为排除管道或管子。
聚醚嵌段酰胺(PEBA)是具有酰胺单元(Ba1)和聚醚单元(Ba2)的共聚物，所述酰胺单元(Ba1)对应于选自如下的脂族重复单元：由至少一种氨基酸获得的单元或由至少一种内酰胺获得的单元、或由如下的缩聚获得的单元X.Y：
-至少一种二胺，所述二胺优先选自直链或支化的脂族二胺或其混合物，和
-至少一种羧二酸，所述二酸优先选自：
直链或支化的脂族二酸、或其混合物，
所述二胺和所述二酸包括4至36个碳原子、有利地6至18个碳原子；
所述聚醚单元(Ba2)尤其得自至少一种聚亚烷基醚多元醇、尤其是聚亚烷基醚二醇。在一种实施方式中，所述密封层的构成组合物(成分)没有成核剂。
成核剂是本领域技术人员已知的且该术语指的是如下物质：当引入聚合物中时，其形成用于在熔融聚合物中生长晶体的核。
它们可例如从微滑石、炭黑、二氧化硅、二氧化钛和纳米粘土选择。
在另一实施方式中，所述密封层的构成组合物没有成核剂和增塑剂。
在一种实施方式中，所述结构体也没有最外面的层并且与由聚酰胺聚合物制成的最外面的复合增强层相邻。
在一种实施方式中，所述多层结构体仅由以下两个层组成：密封层和增强层。
一个或多个密封层为与作为最外面的层的复合增强层相比最里面的层。
罐可为在用于运输氢气的卡车上、在用于运输氢气且用于向燃料电池供应氢气的小汽车上、例如在用于供应氢气的火车上或在用于供应氢气的无人机上的用于氢气的可移动储存的罐，但是它也可为在用于将氢气分配至车辆(交通工具)的站中的用于氢气的静态储存的罐。
有利地，密封层(1)在23℃下不漏氢气，即，在23℃下在0％相对湿度(RH)下在23℃下对于氢气的渗透率小于500cc.mm/m2.24h.atm。
在一种实施方式中，所述一个或多个密封层由组合物组成，所述组合物主要包括：
至少一种半结晶的聚酰胺热塑性聚合物P1i，i＝1至n，n为密封层的数量，排除聚醚嵌段酰胺(PEBA)，且排除PA11。
复合增强层(一个或多个)通过例如经由丝缠绕沉积的浸渍有聚合物的纤维的带(或带材或粗纱)缠绕在密封层周围。
当存在若干个层时，聚合物可不同。
当增强层的聚合物相同时，可存在若干个层，但是有利地存在单个增强层，其于是具有在密封层周围的至少一个完整的缠绕。
即使存在单个层，在密封层周围的若干个相继的完整的缠绕也可被进行且构成所述单个层。
为本领域技术人员所公知的该完全自动化的过程使得可逐层选择缠绕角度，其将向最终结构体提供其耐受内部压力负载的能力。
当存在若干个密封层时，密封层中的仅最里面的与氢气直接接触。
当存在仅一个密封层和一个复合增强层，从而导致双层多层结构体时，则那两个层可焊接到彼此，即，它们彼此直接接触地彼此粘附。
当存在若干个密封层和/或若干个复合增强层时，则所述密封层的最外面的层和因而与同氢气接触的层相反的层焊接到所述复合增强层的最里面的层，且因而彼此直接接触地彼此粘附。
其它复合增强层也可彼此粘附。
其它密封层也可彼此粘附。
有利地，仅一个密封层和一个增强层存在且不焊接到彼此。
关于密封层和热塑性聚合物P1i
可存在一个或多个密封层。
所述层各自由组合物组成，所述组合物主要包括至少一种热塑性聚合物P1i，i对应于存在的层的数量。i为1至10、特别地1至5、尤其是1至3，优先地i＝1。
术语“主要”意指，相对于组合物的总重量，所述至少一种聚合物以超过50重量％存在。
有利地，相对于组合物的总重量，所述至少一种主要聚合物以超过60重量％、尤其是以超过70重量％、特别地以超过80重量％、更特别地大于或等于90重量％存在。
所述组合物还可包括相对于组合物的总重量的最高达50重量％的抗冲改性剂和/或增塑剂和/或添加剂。
添加剂可选自另一聚合物、抗氧化剂、热稳定剂、UV吸收剂、光稳定剂、润滑剂、无机填料、阻燃剂、染料、炭黑和碳质纳米填料；特别地，添加剂选自抗氧化剂、热稳定剂、UV吸收剂、光稳定剂、润滑剂、无机填料、阻燃剂、染料、炭黑和碳质纳米填料。
在一种实施方式中，从添加剂排除成核剂。
在另一实施方式中，从添加剂排除成核剂，且在此情况下，组合物也没有增塑剂。
所述其他聚合物可为另一半结晶热塑性聚合物或者不同的聚合物且尤其是EVOH(乙烯乙烯醇)。
有利地，所述组合物主要包括所述热塑性聚合物P1i，0至50重量％的抗冲改性剂、尤其是0至小于15％的抗冲改性剂、特别地0至12％的抗冲改性剂，0至1.5％的增塑剂和0至5重量％的添加剂，组合物的成分之和等于100％。
有利地，所述组合物主要由如下组成：所述热塑性聚合物P1i，0至50重量％的抗冲改性剂、尤其是0至小于15％的抗冲改性剂、特别地0至12％的抗冲改性剂，0至1.5％的增塑剂和0至5重量％的添加剂，组合物的成分之和等于100％。
有利地，所述组合物主要包括所述热塑性聚合物P1i，0至50重量％的抗冲改性剂、尤其是0至小于15％的抗冲改性剂、特别地0至12％的抗冲改性剂，0至1.5％的增塑剂和0至5重量％的添加剂，组合物的成分之和等于100％。
有利地，所述组合物主要由如下组成：所述热塑性聚合物P1i，0至50重量％的抗冲改性剂、尤其是0至小于15％的抗冲改性剂、特别地0至12％的抗冲改性剂，0至1.5％的增塑剂和0至5重量％的添加剂，组合物的成分之和等于100％。
有利地，所述组合物主要包括所述热塑性聚合物P1i，0至50重量％的抗冲改性剂、尤其是0至小于15％的抗冲改性剂、特别地0至12％的抗冲改性剂，0至5％的增塑剂和0至5重量％的添加剂，组合物的成分之和等于100％。
有利地，所述组合物主要由如下组成：所述热塑性聚合物P1i，0至50重量％的抗冲改性剂、尤其是0至小于15％的抗冲改性剂、特别地0至12％的抗冲改性剂，0至5％的增塑剂和0至5重量％的添加剂，组合物的成分之和等于100％。
各层中的所述至少一种主要聚合物可相同或不同。
在一种实施方式中，单一主要聚合物在至少粘附至复合增强层的密封层中存在。
在一种实施方式中，所述组合物包括0.1至50重量％、尤其是0.1至小于15重量％的抗冲改性剂、特别地0.1至12重量％的抗冲改性剂，相对于组合物的总重量。
在一种实施方式中，所述组合物没有增塑剂。
在另一实施方式中，所述组合物包括0.1至50重量％、尤其是0.1至小于15重量％的抗冲改性剂、特别地0.1至12重量％的抗冲改性剂，且所述组合物没有增塑剂，相对于组合物的总重量。
在还另一实施方式中，所述组合物包括0.1至50重量％、尤其是0.1至小于15重量％的抗冲改性剂、和0.1至1.5重量％的增塑剂，相对于组合物的总重量。
半结晶聚酰胺热塑性聚合物P1i
“热塑性”或“半结晶聚酰胺热塑性聚合物”指的是如下材料：其在环境温度下通常为固体，且其在温度升高期间、特别地在超出其玻璃化转变温度(Tg)之后软化，并且在超过所谓的其熔点(Tm)时可呈现出精确的熔融，并且当温度降低到低于其结晶温度时其再次变成固体。
Tg、Tc和Tm分别根据标准11357-2:2013和11357-3:2013通过差示扫描量热法(DSC)测定。
所述半结晶聚酰胺热塑性聚合物的数均分子量Mn优选地在10,000至85,000、尤其是10,000至60,000、优先地10,000至50,000、甚至更优先地12,000至50,000的范围内。这些Mn值可对应于大于或等于0.8的特性粘度，如在间甲酚中根据标准ISO 307:2007但是通过改变溶剂(使用间甲酚代替硫酸且温度为20℃)而测定的。
用于定义聚酰胺的命名法描述于ISO standard 1874-1:2011“Plastiques–Matériaux polyamides(PA)pour moulage et extrusion–Partie 1:Désignation”中，尤其是第3页(表1和2)上并且是本领域技术人员所公知的。
聚酰胺可为均聚酰胺或共聚酰胺或其混合物。
在一种实施方式中，所述热塑性聚合物为：短链半结晶脂族聚酰胺，即具有最高达9的每氮原子的平均碳原子数的聚酰胺；或长链脂族聚酰胺，即，具有大于9、优选地大于10的每氮原子的平均碳原子数的聚酰胺。
特别地，短链脂族聚酰胺选自：PA6、PA610、PA612和PA6/聚烯烃混合物。
特别地，长链脂族聚酰胺选自：
聚酰胺11(PA11)、聚酰胺12(PA12)、聚酰胺1010(PA1010)、聚酰胺1012(PA1012)、聚酰胺1212(PA1012)、或者其混合物或其共聚酰胺，特别地PA11和PA12。
在一种实施方式中，长链脂族聚酰胺选自：
聚酰胺12(PA12)、聚酰胺1010(PA1010)、聚酰胺1012(PA1012)、聚酰胺1212(PA1012)、或者其混合物或其共聚酰胺，特别地PA12。
在另一实施方式中，所述半结晶聚酰胺热塑性聚合物为半结晶半芳族聚酰胺、特别地具有大于8、优选地大于9的每氮原子的平均碳原子数和在240℃至小于280℃之间的熔融温度的半结晶半芳族聚酰胺。
有利地，半结晶聚酰胺为半芳族聚酰胺、尤其是如EP1505099中所描述的式X/YAr的半芳族聚酰胺、特别地式A/XT的半芳族聚酰胺，其中A选自由氨基酸获得的单元、由内酰胺获得的单元和对应于式(Ca二胺).(Cb二酸)的单元，其中a表示二胺的碳原子的数量且b表示二酸的碳原子的数量，a和b各自在4和36之间、有利地在9和18之间，单元(Ca二胺)选自直链或支化的脂族二胺、脂环族二胺和烷基芳族二胺，且单元(Cb二酸)选自直链或支化的脂族二酸、脂环族二酸和芳族二酸；
X.T表示由Cx二胺和对苯二甲酸的缩聚获得的单元，其中x表示Cx二胺的碳原子的数量，x在5和36之间、有利地在9和18之间，尤其是具有式A/5T、A/6T、A/9T、A/10T、或A/11T的聚酰胺，A如以上所定义的，特别地从如下之中选择的聚酰胺：PA MPMDT/6T、PA11/10T、PA5T/10T、PA11/BACT、PA 11/6T/10T、PA MXDT/10T、PA MPMDT/10T、PA BACT/10T、PA BACT/6T、PA BACT/10T/6T、PA 11/BACT/6T、PA 11/MPMDT/6T、PA11/MPMDT/10T、PA 11/BACT/10T、PA 11/MXDT/10T、PA 11/5T/10T。
特别地，半芳族半结晶聚酰胺选自聚酰胺11/5T或11/6T或11/10T、MXDT/10T、MPMDT/10T和BACT/10T。
T对应于对苯二甲酸，MXD对应于间苯二甲胺，MPMD对应于甲基五亚甲基二胺且BAC对应于双(氨基甲基)环己烷。以上定义的半芳族聚酰胺尤其具有大于或等于80℃的Tg。
有利地，各密封层由包括相同类型的聚酰胺的组合物组成。
包括所述聚合物P1i的所述组合物在颜色上可为黑色的并且能够吸收适合用于焊接的辐射，然后在将复合增强层缠绕在密封层周围之后实施所述焊接。
假若焊接是必要的，则存在多种使得可焊接由聚酰胺热塑性聚合物制成的元件的方法。因而，可使用接触或无接触加热叶片、超声、红外、感应、振动、将待焊接的一个元件抵着另一个旋转或者甚至激光焊接。
聚酰胺热塑性聚合物元件的焊接、特别地通过激光焊接的焊接可要求待焊接的两个元件对于辐射、特别地激光辐射具有不同的性质：元件之一对于辐射、特别地激光辐射必须是透明的，且另一个必须吸收辐射、特别地激光辐射。辐射、特别地激光辐射通过透明的部分，然后到达吸收元件，在该处它被转换成热量。这容许在两个元件之间的接触区域融化且从而焊接发生。
在碳纤维的情况中，优选的情况是在除去时界面的熔融。
为了使它们是吸收性的，已知添加多种添加剂，包括例如炭黑，其赋予聚合物黑颜色且容许它吸收适合用于焊接的辐射。
在一种实施方式中，通过选自如下的系统进行焊接：激光、红外(IR)加热、LED加热、感应或微波加热、或高频(HF)加热。
在其中通过激光焊接实施焊接的情况中，则组合物P1i包括碳质填料。
在其中通过感应实施焊接的情况中，则组合物P1i包括金属颗粒。
有利地，通过激光系统进行焊接。
关于抗冲改性剂
抗冲改性剂可为任何抗冲改性剂，只要它是具有比所述树脂的模量低的模量、具有良好的对基体的粘附以耗散开裂能的聚合物。
抗冲改性剂有利地由具有根据标准ISO 178测量的低于100MPa的挠曲模量和低于0℃的Tg(根据标准11357-2在DSC温谱图的拐点处测量)的聚合物、特别地聚烯烃组成。
在一种实施方式中，从抗冲改性剂的定义排除PEBA。
抗冲改性剂的聚烯烃可为官能化的或非官能化的或者为至少一种官能化聚烯烃和/或至少一种非官能化聚烯烃的混合物。为了简化，聚烯烃用(B)表示且下面描述官能化聚烯烃(B1)和非官能化聚烯烃(B2)。
非官能化聚烯烃(B2)经典地为α-烯烃或二烯烃诸如例如乙烯、丙烯、1-丁烯、1-辛烯、丁二烯的均聚物或共聚物。作为实例，可提及：
-聚乙烯的均聚物和共聚物，特别地LDPE、HDPE、LLDPE(线性低密度聚乙烯)、VLDPE(极低密度聚乙烯)和茂金属聚乙烯。
-丙烯的均聚物或共聚物。
-乙烯/α-烯烃共聚物诸如乙烯/丙烯、EPR(对于乙烯-丙烯橡胶的缩写)和乙烯/丙烯/二烯(三元乙丙橡胶)(EPDM)。
-苯乙烯/乙烯-丁烯/苯乙烯(SEBS)、苯乙烯/丁二烯/苯乙烯(SBS)、苯乙烯/异戊二烯/苯乙烯(SIS)、苯乙烯/乙烯-丙烯/苯乙烯(SEPS)嵌段共聚物。
-乙烯与选自如下的至少一种产品的共聚物：不饱和羧酸的盐或酯诸如(甲基)丙烯酸烷基酯(例如丙烯酸甲酯)，或饱和羧酸的乙烯基酯诸如乙酸乙烯酯(EVA)，其中共聚单体的比例可达到40重量％。
官能化聚烯烃(B1)可为具有反应性单元(官能团)的α-烯烃的聚合物；这样的反应性单元为酸、酐、或环氧官能团。作为实例，可提及通过不饱和环氧化物诸如(甲基)丙烯酸缩水甘油酯、或通过羧酸或相应的盐或酯诸如(甲基)丙烯酸(其可被金属诸如Zn等完全地或部分地中和)或甚至通过羧酸酐诸如马来酸酐接枝或共聚或三元共聚的前面的聚烯烃(B2)。官能化聚烯烃为例如PE/EPR混合物，其重量计的比率可宽范围地改变，例如在40/60和90/10之间，所述混合物用酐、尤其是马来酸酐根据例如0.01至5重量％的接枝率共接枝。
官能化聚烯烃(B1)可选自以下的、马来酸酐或甲基丙烯酸缩水甘油酯接枝的(共)聚合物，其中接枝率为例如0.01至5重量％：
-PE，PP，含有例如35至80重量％的乙烯的乙烯与丙烯、丁烯、己烯、或辛烯的共聚物；
-乙烯/α-烯烃共聚物诸如乙烯/丙烯、EPR(对于乙烯-丙烯橡胶的缩写)和乙烯/丙烯/二烯(EPDM)。
-苯乙烯/乙烯-丁烯/苯乙烯(SEBS)、苯乙烯/丁二烯/苯乙烯(SBS)、苯乙烯/异戊二烯/苯乙烯(SIS)、苯乙烯/乙烯-丙烯/苯乙烯(SEPS)嵌段共聚物。
-含有最高达40重量％的乙酸乙烯酯的乙烯和乙酸乙烯酯的共聚物(EVA)；
-含有最高达40重量％的(甲基)丙烯酸烷基酯的乙烯和(甲基)丙烯酸烷基酯共聚物；
-含有最高达40重量％的共聚单体的乙烯与乙酸乙烯酯(EVA)和(甲基)丙烯酸烷基酯的共聚物。
官能化聚烯烃(B1)还可选自乙烯/丙烯共聚物，其中主要被马来酸酐接枝的丙烯与单胺聚酰胺(或聚酰胺低聚物)缩合(EP-A-0,342,066中描述的产品)。
官能化聚烯烃(B1)还可为至少以下单元的共聚物或三元共聚物：(1)乙烯、(2)(甲基)丙烯酸烷基酯或饱和羧酸的乙烯基酯、和(3)酐诸如马来酸酐或(甲基)丙烯酸或环氧诸如(甲基)丙烯酸缩水甘油酯。
作为后一类型的官能化聚烯烃的实例，可提及以下共聚物：其中乙烯优选地占共聚物的至少60重量％且其中三元共聚单体(官能团)占例如共聚物的0.1至10重量％：
-乙烯/(甲基)丙烯酸烷基酯/(甲基)丙烯酸或马来酸酐或甲基丙烯酸缩水甘油酯共聚物；
-乙烯/乙酸乙烯酯/马来酸酐或甲基丙烯酸缩水甘油酯共聚物；
-乙烯/乙酸乙烯酯或(甲基)丙烯酸烷基酯/(甲基)丙烯酸或马来酸酐或甲基丙烯酸缩水甘油酯共聚物。
在前面的共聚物中，可用Zn或Li使(甲基)丙烯酸成盐。
(B1)或(B2)中的术语“(甲基)丙烯酸烷基酯”表示甲基丙烯酸C1至C8烷基酯和丙烯酸C1至C8烷基酯，并且可选自丙烯酸甲酯、丙烯酸乙酯、丙烯酸正丁酯、丙烯酸异丁酯、丙烯酸2-乙基己酯、丙烯酸环己酯、甲基丙烯酸甲酯和甲基丙烯酸乙酯。
而且，之前提及的聚烯烃(B1)也可通过任何适当的方法或试剂(二环氧、二酸、过氧化物等)交联；术语官能化聚烯烃还包括之前提及的聚烯烃与可与这些反应的双官能试剂诸如二酸、二酐、二环氧等的混合物或者可在一起反应的至少两种官能化聚烯烃的混合物。
以上提及的共聚物(B1)和(B2)可以统计或顺序化的方式共聚并且具有直链或支化结构。
这些聚烯烃的分子量、指数MFI、密度也可宽范围地改变，本领域技术人员将知晓其。MFI，对于熔体流动指数的缩写，是在熔融状态下的流动性的度量。它是根据标准ASTM1238测量的。
有利地，非官能化聚烯烃(B2)选自聚丙烯的均聚物或共聚物以及任何乙烯均聚物或者乙烯与更高级α-烯烃共聚单体诸如丁烯、己烯、辛烯或4-甲基-1-戊烯的共聚物。可提及例如PP、高密度PE、中密度PE、线性低密度PE、低密度PE、极低密度PE。这些聚乙烯被本领域技术人员知晓为是根据“自由基”方法、根据“齐格勒”催化方法、或更近期地“茂金属”催化制造的。
有利地，官能化聚烯烃(B1)选自包括α烯烃单元和带有极性反应性官能团如环氧、羧酸或羧酸酐官能团的单元的任何聚合物。作为这样的聚合物的实例，可提及乙烯、丙烯酸烷基酯和马来酸酐或甲基丙烯酸缩水甘油酯的三元共聚物例如来自申请人的
Figure BDA0003769586490000111
或通过马来酸酐接枝的聚烯烃例如来自申请人的
Figure BDA0003769586490000112
以及乙烯、丙烯酸烷基酯和(甲基)丙烯酸的三元共聚物。还可提及聚丙烯的均聚物或者通过羧酸酐接枝、然后与聚酰胺或单胺聚酰胺低聚物缩合的聚丙烯的共聚物。
有利地，构成所述密封层(一个或多个)的所述组合物没有聚醚嵌段酰胺(PEBA)。在该实施方式中，因此从抗冲改性剂排除PEBA。
有利地，所述透明组合物没有芯-壳颗粒或芯-壳聚合物。
芯-壳颗粒必须被理解为如下颗粒：其第一层形成芯并且第二或所有接着的层形成相应的壳。
芯-壳颗粒可通过包括至少两个步骤的具有若干个步骤的方法获得。这样的方法描述于例如文献US2009/0149600或EP0,722,961中。
关于增塑剂:
增塑剂可为通常用在基于聚酰胺(一种或多种)的组合物中的增塑剂。
有利地，使用如下增塑剂：其具有良好的热稳定性，使得其在将不同的聚合物混合并且使所获得的组合物变形的步骤中不形成烟雾。
特别地，该增塑剂可选自：
苯磺酰胺衍生物，诸如n-丁基苯磺酰胺(BBSA)、乙基甲苯磺酰胺(ETSA)的邻位和对位异构体、N-环己基甲苯磺酰胺和N-(2-羟丙基)苯磺酰胺(HP-BSA)，
羟基苯甲酸的酯，诸如对-羟基苯甲酸2-乙基己酯(EHPB)和对-羟基苯甲酸2-癸基己酯(HDPB)，
四氢糠醇的酯或醚，诸如低聚亚乙基氧基四氢糠醇，和
柠檬酸或羟基丙二酸的酯，诸如低聚亚乙基氧基丙二酸酯。
优选的增塑剂为n-丁基苯磺酰胺(BBSA)。
另一更特别地优选的增塑剂为N-(2-羟丙基)苯磺酰胺(HP-BSA)。实际上，后者具有如下优势：在通过挤出的变形步骤期间防止在挤出螺杆和/或口模处的沉积物(“口模流涎”)的形成。
当然，可使用增塑剂的混合物。
关于复合增强层和聚合物P2j
聚合物P2j为半结晶聚酰胺热塑性聚合物，所述半结晶聚酰胺热塑性聚合物具有与以上相同的定义。
可存在一个或多个复合增强层。
所述层各自由浸渍有组合物的连续纤维形式的纤维材料组成，所述组合物主要包括至少一种热塑性聚合物P2j，j对应于存在的层的数量。
j包括1至10、特别地1至5、尤其是1至3，优先地j＝1。
术语“主要”意指相对于组合物和复合物的基体的总重量，所述至少一种聚合物以超过50重量％存在。
有利地，相对于组合物的总重量，所述至少一种主要聚合物以超过60重量％、尤其是以超过70重量％、特别地以超过80重量％、更特别地大于或等于90重量％存在。
所述组合物可进一步包括抗冲改性剂和/或添加剂。
添加剂可选自抗氧化剂、热稳定剂、UV吸收剂、光稳定剂、润滑剂、无机填料、阻燃剂、增塑剂和染料。
在一种实施方式中，添加剂排除成核剂。
有利地，所述组合物主要由如下组成：所述聚酰胺热塑性聚合物P2j，0至15重量％的抗冲改性剂、特别地0至12重量％的抗冲改性剂，0至5重量％的添加剂，组合物的成分之和等于100重量％。
有利地，所述组合物主要由如下组成：所述聚酰胺热塑性聚合物P2j，0至15重量％的抗冲改性剂、特别地0至12重量％的抗冲改性剂，0至5重量％的添加剂，组合物的成分之和等于100重量％。
有利地，所述组合物主要由如下组成：所述聚酰胺热塑性聚合物P2j，0至15重量％的抗冲改性剂、特别地0至12重量％的抗冲改性剂，0至5重量％的添加剂，组合物的成分之和等于100重量％。
有利地，所述组合物主要由如下组成：所述聚酰胺热塑性聚合物P2j，0至15重量％的抗冲改性剂、特别地0至12重量％的抗冲改性剂，0至5重量％的添加剂，组合物的成分之和等于100重量％。
各层中的所述至少一种主要聚合物可相同或不同。
在一种实施方式中，各增强层包括相同类型的聚酰胺。
聚合物P2j
聚酰胺热塑性聚合物P2j
“热塑性”或“半结晶聚酰胺热塑性聚合物”指的是如下材料：其在环境温度下通常为固体，且其在温度升高期间、特别地在超出其玻璃化转变温度(Tg)之后软化，并且在超过所谓的其熔点(Tm)时可呈现出精确的熔融，并且当温度降低到低于其结晶温度时其再次变成固体。
Tg、Tc和Tm分别根据标准11357-2:2013和11357-3:2013通过差示扫描量热法(DSC)测定。
所述聚酰胺热塑性聚合物P2j的数均分子量Mn优选地在10,000至40,000、优选地10,000至30,000的范围内。这些Mn值可对应于大于或等于0.8的特性粘度，如在间甲酚中根据标准ISO 307:2007但是通过改变溶剂(使用间甲酚代替硫酸且温度为20℃)而测定的。
用于定义聚酰胺的命名法描述于ISO standard 1874-1:2011“Plastiques–Matériaux polyamides(PA)pour moulage et extrusion–Partie 1:Désignation”中，尤其是第3页(表1和2)上并且是本领域技术人员所公知的。
聚酰胺可为均聚酰胺或共聚酰胺或其混合物。
在一种实施方式中，所述热塑性聚合物为短链半结晶脂族聚酰胺，即，具有最高达9的每氮原子的平均碳原子数的聚酰胺；或长链脂族聚酰胺，即，具有大于9、优选地大于10的每氮原子的平均碳原子数的聚酰胺。
特别地，短链脂族聚酰胺选自：PA6、PA610、PA612和PA6/聚烯烃混合物。
特别地，长链脂族聚酰胺选自：
聚酰胺11(PA11)、聚酰胺12(PA12)、聚酰胺1010(PA1010)、聚酰胺1012(PA1012)、聚酰胺1212(PA1012)，或者其混合物或其共聚酰胺，特别地PA11和PA12.
在一种实施方式中，长链脂族聚酰胺选自：
聚酰胺12(PA12)、聚酰胺1010(PA1010)、聚酰胺1012(PA1012)、聚酰胺1212(PA1012)、或者其混合物或其共聚酰胺，特别地PA12。
在另一实施方式中，所述半结晶聚酰胺热塑性聚合物为半结晶半芳族聚酰胺、特别地具有大于8、优选地大于9的每氮原子的平均碳原子数和在240℃至小于280℃之间的熔融温度的半结晶半芳族聚酰胺。
有利地，半结晶聚酰胺为半芳族聚酰胺、尤其是如EP1505099中所描述的式X/YAr的半芳族聚酰胺、特别地式A/XT的半芳族聚酰胺，其中A选自由氨基酸获得的单元、由内酰胺获得的单元和对应于式(Ca二胺).(Cb二酸)的单元，其中a表示二胺的碳原子的数量且b表示二酸的碳原子的数量，a和b各自在4和36之间、有利地在9和18之间，单元(Ca二胺)选自直链或支化的脂族二胺、脂环族二胺和烷基芳族二胺，且单元(Cb二酸)选自直链或支化的脂族二酸、脂环族二酸和芳族二酸；
X.T表示由Cx二胺和对苯二甲酸的缩聚获得的单元，其中x表示Cx二胺的碳原子的数量，x在5和36之间、有利地在9和18之间，尤其是具有式A/5T、A/6T、A/9T、A/10T、或A/11T的聚酰胺，A如以上所定义的，特别地从如下之中选择的聚酰胺：PA MPMDT/6T、PA11/10T、PA5T/10T、PA11/BACT、PA 11/6T/10T、PA MXDT/10T、PA MPMDT/10T、PA BACT/10T、PA BACT/6T、PA BACT/10T/6T、PA 11/BACT/6T、PA 11/MPMDT/6T、PA11/MPMDT/10T、PA11/BACT/10T、PA 11/MXDT/10T、PA 11/5T/10T。
特别地，半芳族半结晶聚酰胺选自聚酰胺11/5T或11/6T或11/10T、MXDT/10T、MPMDT/10T和BACT/10T。
T对应于对苯二甲酸，MXD对应于间苯二甲胺，MPMD对应于甲基五亚甲基二胺且BAC对应于双(氨基甲基)环己烷。以上定义的所述半芳族聚酰胺尤其是具有大于或等于80℃的Tg。
关于结构体
所述多层结构体因此包括至少一个密封层和至少一个复合增强层，最里面的增强层被焊接到最外面的密封层且因此彼此粘附。
存在的所有密封层彼此粘附且存在的所有增强层彼此粘附。
在一种实施方式中，所述最外面的相邻密封层(1)的聚酰胺的如根据ISO11357-3:2013测量的Tm与所述最里面的增强层(2)的聚酰胺的如根据ISO11357-3:2013测量的Tm相差至多30℃。
在另一实施方式中，所述最外面的相邻密封层(1)的聚酰胺的如根据ISO11357-2:2013测量的Tg与所述最里面的增强层(2)的聚酰胺的如根据ISO11357-2:2013测量的Tg相差至多30℃。
有利地，所述最外面的相邻密封层(1)的聚酰胺的Tm和Tg与所述最里面的增强层(2)的聚酰胺的Tm和Tg相差至多30℃。
在一种实施方式中，各密封层包括相同类型的聚酰胺且各增强层包括相同类型的聚酰胺。
所述多层结构体可包括不同性质的最高达10个复合增强层和最高达10个密封层。
显然所述多层结构体不必是对称的且其可因此包括比复合层多的密封层或者反过来，但是可不存在交替的层和增强层。
有利地，所述多层结构体包括一个、两个、三个、四个、五个、六个、七个、八个、九个或十个密封层和一个、两个、三个、四个、五个、六个、七个、八个、九个或十个复合增强层。
有利地，所述多层结构体包括一个、两个、三个、四个或五个密封层和一个、两个、三个、四个或五个复合增强层。
有利地，所述多层结构体包括一个、两个或三个密封层和一个、两个或三个复合增强层。
在一种实施方式中，所述多层结构体包括单个密封层和若干个增强层，与密封层相邻的所述增强层被焊接到所述密封层且另外的增强层被缠绕在直接相邻的增强层周围。
在另一实施方式中，所述多层结构体包括单个增强层和若干个密封层，所述增强层被焊接到所述相邻密封层。
在一种有利实施方式中，所述多层结构体包括单个密封层和单个复合增强层，所述增强层被焊接到所述密封层。
有利地，在所述多层结构体中，各密封层由包括相同类型的聚酰胺聚合物P1i的组合物组成。
有利地，对于所有密封层，聚酰胺P1i是相同的。
有利地，所述聚合物P1i为：短链脂族聚酰胺，其特别地选自PA6、PA610、PA612和PA6/聚烯烃混合物；或长链脂族聚酰胺，其特别地选自PA1010、PA1012、PA1212、PA11和PA12，特别地PA11和PA12；或半芳族聚酰胺，其特别地选自聚酰胺11/5T、11/6T、11/10T、MXDT/10T、MPMDT/10T和BACT/10T。
有利地，在所述多层结构体中，各增强层由包括相同类型的聚酰胺聚合物P2j的组合物组成。
有利地，对于所有增强层，聚酰胺P2j是相同的。
有利地，所述聚合物P2j为：短链脂族聚酰胺，其特别地选自PA6、PA610、PA612；或长链脂族聚酰胺，其特别地选自PA1010、PA1012、PA1212、PA11和PA12，特别地PA11和PA12；或半芳族聚酰胺，其特别地选自聚酰胺11/5T、11/6T、11/10T、MXDT/10T、MPMDT/10T和BACT/10T。
有利地，在所述多层结构体中，各密封层由包括相同类型的聚酰胺聚合物P1i的组合物组成，且各增强层由包括相同类型的聚酰胺聚合物P2j的组合物组成。
有利地，所述聚合物P1i为：短链脂族聚酰胺，其特别地选自PA6、PA610、PA612和aPA6/聚烯烃混合物；或长链脂族聚酰胺，其特别地选自PA1010、PA1012、PA1212、PA11和PA12，特别地PA11和PA12；或半芳族聚酰胺，其特别地选自聚酰胺11/5T、11/6T、11/10T、MXDT/10T、MPMDT/10T和BACT/10T，并且所述聚合物P2j为：短链脂族聚酰胺，其特别地选自PA6、PA610、PA612；或长链脂族聚酰胺，其特别地选自PA1010、PA1012、PA1212、PA11和PA12，特别地PA11和PA12；或半聚酰胺芳族，其特别地选自聚酰胺11/5T、11/6T、11/10T、MXDT/10T、MPMDT/10T和BACT/10T。
在一种实施方式中，所述多层结构体由单个增强层和单个密封层组成，其中所述聚合物P1i为：短链脂族聚酰胺，其特别地选自PA6、PA610、PA612和PA6/聚烯烃；或长链混合物，其特别地选自PA1010、PA1012、PA1212、PA11和PA12，特别地PA 11和PA12；或半芳族聚酰胺，其特别地选自聚酰胺11/5T、11/6T、11/10T、MXDT/10T、MPMDT/10T和BACT/10T，并且所述聚合物P2j为：短链脂族聚酰胺，其特别地选自PA6、PA610、PA612；或长链脂族聚酰胺，其特别地选自PA1010、PA1012、PA1212、PA11和PA12，特别地PA11和PA12；或半芳族聚酰胺，其特别地选自聚酰胺11/5T、11/6T、11/10T、MXDT/10T、MPMDT/10T和BACT/10T。
在一种实施方式中，所述多层结构体由单个增强层和单个密封层组成，其中所述聚合物P1i为短链脂族聚酰胺，其特别地选自PA6、PA610、PA612和PA6/聚烯烃混合物，并且所述聚合物P2j为短链脂族聚酰胺，其特别地选自PA6、PA610、PA612。
在一种实施方式中，所述多层结构体由单个增强层和单个密封层组成，其中所述聚合物P1i为短链脂族聚酰胺，其特别地选自PA6、PA610、PA612和PA6/聚烯烃混合物，并且所述聚合物P2j为长链脂族聚酰胺，其特别地选自PA1010、PA1012、PA1212、PA11和PA12，特别地PA11和PA12。
在一种实施方式中，所述多层结构体由单个增强层和单个密封层组成，其中所述聚合物P1i为短链脂族聚酰胺，其特别地选自PA6、PA610、PA612和PA6/聚烯烃混合物，并且所述聚合物P2j为半芳族聚酰胺，其特别地选自聚酰胺11/5T、11/6T、11/10T、MXDT/10T、MPMDT/10T和BACT/10T。
在一种实施方式中，所述多层结构体由单个增强层和单个密封层组成，其中所述聚合物P1i为长链脂族聚酰胺，其特别地选自PA1010、PA1012、PA1212、PA11和PA12，特别地PA11和PA12，并且所述聚合物P2j为短链脂族聚酰胺，其特别地选自PA6、PA610、PA612。
在一种实施方式中，所述多层结构体由单个增强层和单个密封层组成，其中所述聚合物P1i为长链脂族聚酰胺，其特别地选自PA1010、PA1012、PA1212、PA11和PA12，特别地PA11和PA12，并且所述聚合物P2j为长链脂族聚酰胺，其特别地选自PA1010、PA1012、PA1212、PA11和PA12，特别地PA11和PA12。
在一种实施方式中，所述多层结构体由单个增强层和单个密封层组成，其中所述聚合物P1i为长链脂族聚酰胺，其特别地选自PA1010、PA1012、PA1212、PA11和PA12，特别地PA11和PA12，并且所述聚合物P2j为半芳族聚酰胺，其特别地选自聚酰胺11/5T、11/6T、11/10T、MXDT/10T、MPMDT/10T和BACT/10T。
在一种实施方式中，所述多层结构体由单个增强层和单个密封层组成，其中所述聚合物P1i为半芳族聚酰胺，其特别地选自聚酰胺11/5T、11/6T、11/10T、MXDT/10T、MPMDT/10T和BACT/10T，并且所述聚合物P2j为短链脂族聚酰胺，其特别地选自PA6、PA610、PA612。
在一种实施方式中，所述多层结构体由单个增强层和单个密封层组成，其中所述聚合物P1i为半芳族聚酰胺，其特别地选自聚酰胺11/5T、11/6T、11/10T、MXDT/10T、MPMDT/10T和BACT/10T，并且所述聚合物P2j为长链脂族聚酰胺，其特别地选自PA1010、PA1012、PA1212、PA11和PA12，特别地PA11和PA12。
一种实施方式中，所述多层结构体由单个增强层和单个密封层组成，其中所述聚合物P1i为半芳族聚酰胺，其特别地选自聚酰胺11/5T、11/6T、11/10T、MXDT/10T、MPMDT/10T和BACT/10T，并且所述聚合物P2j为半芳族聚酰胺，其特别地选自聚酰胺11/5T、11/6T、11/10T、MXDT/10T、MPMDT/10T和BACT/10T。
有利地，所述多层结构体进一步包括至少一个由浸渍有透明无定形聚合物的由连续玻璃纤维制成的纤维材料组成的外层，所述层为所述多层结构体的最外面的层。
所述外层为第二增强层，但是为透明的，这使得可能够在结构体上设置文本(text)。
关于纤维材料
关于构成所述纤维材料的纤维，它们特别地为矿物、有机或植物纤维。
有利地，所述纤维材料可为上浆的或未上浆的。
所述纤维材料可因此包括最高达3.5重量％的有机材料(热固性或热塑性树脂型的)，称作上浆。
矿物纤维包括例如碳纤维、玻璃纤维、玄武岩或玄武岩基纤维、二氧化硅纤维、或碳化硅纤维。有机纤维包括例如热塑性或热固性聚合物基纤维，诸如半芳族聚酰胺纤维、芳族聚酰胺纤维或聚烯烃纤维。优选地，它们是基于无定形热塑性聚合物的并且当构成预浸渍基体的聚合物或热塑性聚合物混合物是无定形的时具有比后者的Tg高的玻璃化转变温度Tg、或者当构成预浸渍基体的聚合物或热塑性聚合物混合物是半结晶的时具有比后者的Tm高的玻璃化转变温度Tg。有利地，它们是基于半结晶热塑性聚合物的并且当构成预浸渍基体的聚合物或热塑性聚合物混合物是无定形的时具有比后者的Tg高的熔融温度Tm、或者当构成预浸渍基体的聚合物或热塑性聚合物混合物是半结晶的时具有比后者的Tm高的熔融温度Tm。因而，构成纤维材料的有机纤维在通过最终复合物的热塑性基体的浸渍期间不存在熔化风险。植物纤维包括天然的亚麻，汉麻(hemp)，木质素，竹子，丝、特别地蜘蛛丝，剑麻和其它纤维素纤维、特别地粘胶。这些植物纤维可纯地使用、被处理过或者涂覆有涂层，以促进热塑性聚合物基体的粘附和浸渍。
纤维材料也可为用纤维编织或纺织的织物。
它也可对应于具有支持线的纤维。
这些构成纤维可单独地或以混合物使用。因而，有机纤维可与矿物纤维混合以用热塑性聚合物粉末预浸渍和以形成预浸渍的纤维材料。
有机纤维束(股)可具有若干克重。它们可进一步具有若干几何形状。纤维材料的构成纤维可进一步采取具有不同几何形状的这些增强纤维的混合物的形式。纤维为连续纤维。
优选地，纤维材料选自玻璃纤维、碳纤维、玄武岩纤维或玄武岩基纤维、或其混合物，特别地碳纤维。
它以一根粗纱或若干粗纱的形式使用。
根据另一方面，本发明涉及制造如上定义的多层结构体的方法，特征在于，其包括将以上定义的增强层丝缠绕在如上定义的密封层周围的步骤。
以上详述的所有特性也适用于所述方法。
实施例
在所有实施例中，罐通过在适合于所使用的热塑性树脂的性质的温度下对密封层(衬里)进行滚塑而获得。
在复合增强物的情况中，使用之前浸渍有热塑性树脂(带材)的纤维材料。该带材使用具有1500W激光加热器的自动操作装置通过丝缠绕以12m/分钟的速度沉积并且不存在聚合步骤。
实施例1(反例)：
由环氧复合增强物(Tg 100℃)T700SC31E碳纤维(由Toray生产)和PA11密封层构成的IV型氢气储存罐。
实施例2：由T700SC31E碳纤维PA11复合增强物(由Toray生产)和PA11密封层构成的IV型氢气储存罐。
使由此获得的罐经历在10和800巴之间改变的循环压力测试。使用水施加所述压力。在10,000次循环之后停止测试。
在这之后，从所述罐切下约1cm宽的条。然后通过在界面处引起分离并且通过使用牵引机实施剥离试验而测量在衬里和复合物之间的粘附。剥离强度以N/cm的条宽度表示。在实施例1的情况中，对于3N/cm的值看见分离。在实施例2的情况中，达到大于30N/cm的力。

Claims (14)

1.打算用于运输、分配和储存氢气、特别地用于储存氢气的多层结构体，其从内到外包括密封层(1)和至少一个复合增强层(2)，
所述最里面的复合增强层(2)被焊接到所述最外面的相邻密封层(1)，
所述密封层(1)由组合物组成，所述组合物主要包括：
至少一种半结晶聚酰胺热塑性聚合物P1i，i＝1至n，其中n为密封层的数量，排除聚醚嵌段酰胺(PEBA)，
相对于组合物的总重量的最高达50重量％的抗冲改性剂、尤其是最高达小于15重量％的抗冲改性剂、特别地最高达12重量％的抗冲改性剂，
相对于组合物的总重量的最高达1.5重量％的增塑剂，
各密封层中的所述至少一种聚酰胺热塑性聚合物可相同或不同，
并且所述复合增强层的至少一个由浸渍有组合物的连续纤维形式的纤维材料组成，所述组合物主要包括至少一种半结晶聚酰胺聚合物P2j，j＝1至m，m为增强层的数量，
所述最外面的相邻密封层(1)的聚酰胺的每酰胺官能团的碳原子数与所述最里面的增强层(2)的聚酰胺的每酰胺官能团的碳原子数相差至多20％。
2.根据权利要求1的多层结构体，特征在于，所述最外面的相邻密封层(1)的聚酰胺的根据ISO 11357-3:2013测量的Tm与所述最里面的增强层(2)的聚酰胺的根据ISO 11357-3:2013测量的Tm相差至多30℃。
3.根据权利要求1的多层结构体，特征在于，所述最外面的相邻密封层(1)的聚酰胺的根据ISO 11357-2:2013测量的Tg与所述最里面的增强层(2)的聚酰胺的根据ISO 11357-2:2013测量的Tg相差至多30℃。
4.根据权利要求2或3的多层结构体，特征在于，所述最外面的相邻密封层(1)的聚酰胺的Tm和Tg与所述最里面的增强层(2)的聚酰胺的Tm和Tg相差至多30℃。
5.根据权利要求1或4之一的多层结构体，特征在于，各密封层包括相同类型的聚酰胺。
6.根据权利要求1或4之一的多层结构体，特征在于，各增强层包括相同类型的聚酰胺。
7.根据权利要求5或6之一的多层结构体，特征在于，各密封层包括相同类型的聚酰胺且各增强层包括相同类型的聚酰胺。
8.根据权利要求1至4之一的多层结构体，特征在于，其具有单个密封层和单个增强层。
9.根据权利要求1至8之一的多层结构体，特征在于，所述聚合物P1i为：具有最高达9的每氮原子的平均碳原子数的短链脂族聚酰胺，其特别地选自PA6、PA610、PA612和PA6/聚烯烃混合物；或具有大于9、优选地大于10的每氮原子的平均碳原子数的长链脂族聚酰胺，其特别地选自PA1010、PA1012、PA1212、PA11和PA12，特别地PA11和PA12；或半芳族聚酰胺，其特别地选自聚酰胺11/5T、11/6T、11/10T、MXDT/10T、MPMDT/10T和BACT/10T。
10.根据权利要求1至8之一的多层结构体，特征在于，所述聚合物P2j为：具有最高达9的每氮原子的平均碳原子数的短链脂族聚酰胺，其特别地选自PA6、PA610、PA612；或具有大于9、优选地大于10的每氮原子的平均碳原子数的长链脂族聚酰胺，其特别地选自PA1010、PA1012、PA1212、PA11和PA12，特别地PA11和PA12；或半芳族聚酰胺，其特别地选自聚酰胺11/5T、11/6T、11/10T、MXDT/10T、MPMDT/10T和BACT/10T。
11.根据权利要求9或10之一的多层结构体，特征在于，所述聚合物P1i为：具有最高达9的每氮原子的平均碳原子数的短链脂族聚酰胺，特别地PA6、PA610、PA612或PA6/聚烯烃混合物；或具有大于9、优选地大于10的每氮原子的平均碳原子数的长链脂族聚酰胺，特别地PA1010、PA1012、PA1212、PA11、PA12，特别地PA11或PA12；或半芳族聚酰胺，其特别地选自聚酰胺11/5T或11/6T或11/10T、MXDT/10T、MPMDT/10T和BACT/10T，并且所述聚合物P2j为：具有最高达9的每氮原子的平均碳原子数的短链脂族聚酰胺，其特别地选自PA6、PA610、PA612；或具有大于9、优选地大于10的每氮原子的平均碳原子数的长链脂族聚酰胺，其特别地选自PA1010、PA1012、PA1212、PA11和PA12，特别地PA11和PA12；或半芳族聚酰胺，其特别地选自聚酰胺11/5T、11/6T、11/10T、MXDT/10T、MPMDT/10T和BACT/10T。
12.根据权利要求1至11之一的多层结构体，特征在于，复合增强层的纤维材料选自玻璃纤维、碳纤维、玄武岩纤维或玄武岩基纤维、或其混合物，特别地碳纤维。
13.根据权利要求1至12之一的多层结构体，特征在于，所述结构体进一步包括至少一个由浸渍有透明无定形聚合物的由连续玻璃纤维制成的纤维材料组成的外层，所述层为所述多层结构体的最外面的层。
14.用于制造如权利要求1至13之一中所限定的多层结构体的方法，特征在于，其包括将如权利要求1中所限定的增强层焊接到如权利要求1中所限定的密封层上的步骤。
CN202180011517.9A 2020-01-28 2021-01-26 用于运输或储存氢气的多层结构体 Active CN115003504B (zh)