CN114892913A - 一种变色水晶元素镶嵌地板及其制备方法 - Google Patents
一种变色水晶元素镶嵌地板及其制备方法 Download PDFInfo
- Publication number
- CN114892913A CN114892913A CN202210395553.6A CN202210395553A CN114892913A CN 114892913 A CN114892913 A CN 114892913A CN 202210395553 A CN202210395553 A CN 202210395553A CN 114892913 A CN114892913 A CN 114892913A
- Authority
- CN
- China
- Prior art keywords
- color
- changing
- parts
- base material
- crystal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种变色水晶元素镶嵌地板及其制备方法，所述的一种变色水晶元素镶嵌地板的制备方法，包括步骤1)将原料进行分段、开片、抛光处理，形成待加工基材；2)采用吸空泵吸住基材，水平固定在打孔机上；3)根据图纸，在基材表面打孔，打孔机转速控制在1900至2100转每分；4)采用手工打磨机清理基材表面因打孔机打孔而产生的毛刺；5)打磨完毛刺后，采用点胶器将胶水加入到孔中；6)根据水晶镶嵌图纸的要求，采用点钻笔吸住水晶，将水晶镶嵌在孔中；7)对镶嵌好水晶的基材进行树脂封胶处理，从而获得水晶地板，其中，所述树脂为耐高温变色树脂。
Description
技术领域
本发明涉及地板领域，特别是涉及一种变色水晶元素镶嵌地板及其制备方法。
背景技术
随着家居装修行业的兴起，人们对室内装潢设计的样式越来越重视，地板装饰作为装潢中主要的一部分，也需要迎合消费者需求。而现阶段地板种类虽然很多，但都比较单一，无法体现个性化差异，无法满足部分人们追求时尚，彰显自我的需求。急需在生产地板的方法上进行改进、创新，生产出一种满足人们个性化需求的地板。因此，如何解决上述现有技术存在的缺陷成为了该领域技术人员努力的方向。
CN201711035595.4公开一种水晶元素地板颗粒镶嵌铺装方法，但其封胶树脂颜色单一，本发明在前期研究的基础上进一步研究颜色更为丰富的水晶元素镶嵌地板，满足个性化需求。
发明内容
鉴于此，本发明的目的在于提供一种变色水晶元素镶嵌地板及其制备方法。本发明的目的是通过以下技术方案来实现的：
本发明提供一种变色水晶元素镶嵌地板的制备方法，包括以下步骤：
1)将原料进行分段、开片、抛光处理，形成待加工基材；
2)采用吸空泵吸住基材，水平固定在打孔机上；
3)根据图纸，在基材表面打孔，打孔机转速控制在1900至2100转每分；
4)采用手工打磨机清理基材表面因打孔机打孔而产生的毛刺；
5)打磨完毛刺后，采用点胶器将胶水加入到孔中；
6)根据水晶镶嵌图纸的要求，采用点钻笔吸住水晶，将水晶镶嵌在孔中；
7)对镶嵌好水晶的基材进行树脂封胶处理，从而获得水晶地板，其中，所述树脂为耐高温变色树脂。
步骤7)中，所述耐高温变色树脂按质量份数计，包括：
所述的含氟聚合物树脂包括四氟乙烯-全氟烷氧基乙烯基醚共聚物、聚四氟乙烯树酯或全氟乙烯丙烯共聚物、全氟烷氧基乙烯基醚共聚物中的一种。
所述的稳定剂包括甘油和或羟乙基纤维素。
所述的云母基含硼聚亚酰胺粘结剂制备方法为：
S1、将二氨基二苯醚20-50质量份、均苯四甲酸二酐30-50质量份、二甲基乙酰胺200-500质量份、80-150℃搅拌0.5-2h,再加入全氟烷基甲硅烷基云母1-5质量份、甲基丙烯磺酸甜菜碱0.5-2质量份、2-环己基乙烯硼酸0.5-3质量份、蓖麻油2质量份、混合均匀制备成混合物；
S2、将混合物于220-300℃搅拌1-5h，过滤，烘干，然后进行辐照，辐照能量为1-5Mev，辐照剂量为200-800KGy，得到云母基含硼聚亚酰胺粘结剂。
所述耐高温变色颜料为一种石墨烯负载三氧化钨/三氧化二铁纳米材料，制备方法包如下步骤：
按照质量份数，将0.1-0.8份的硝酸亚铁和0.7-1.8份的钨酸亚铁分散于20-40份的0.5-1.0M的草酸水溶液中，加入2-8份的石墨烯纳米粉末，然后控温50-70℃搅拌分散30-60min；然后降温到室温，将0.05-0.25份的三异硬酯酸钛酸异丙酯和0.04-0.15份的乙酰丙酮胺混合均匀后加入到反应釜中，升温到60-80℃，搅拌反应20-30min，完成反应后转移到水热釜中，控温120-150℃，反应5-10h，完成反应后过滤，干燥后于空气的氛围下于600-800℃下煅烧3-8h，最后粉碎至纳米级，制备得到所述耐高温变色颜料。
所述步骤2)中打孔机采用数控打孔机。
所述步骤3)中打孔机在打孔的过程中，同时采用吸尘器吸木屑。
所述步骤5)中胶水为环氧树脂AB胶。点胶器将胶水加到孔深度的三分之一即可。
树脂封胶处理在无尘室中进行。
与现有技术相比，本发明的有益效果在于：
1、本发明将水晶镶嵌在基材上，其方法简单，操作方便，个性化强，水晶可组成不同的图案，客户可单独定制，满足不同客户需求；
2、封胶树脂采用耐高温变色树脂，结合水晶的光芒，制备出颜色多样，富有美感的水晶地板；
3、耐高温变色颜料采用石墨烯代替二氧化硅，制备的耐高温变色颜料不易褪色；
4、云母基含硼聚亚酰胺粘结剂通过添加蓖麻油，蓖麻油中含有天然的多羟基化合物，蓖麻油的高羟值和高官能度，可以提高耐热性能。
具体实施方式
下面结合实施例对本发明进行详细说明。以下实施例将有助于本领域的技术人员进一步理解本发明，但不以任何形式限制本发明。应当指出的是，对本领域的普通技术人员来说，在不脱离本发明构思的前提下，还可以做出若干调整和改进。这些都属于本发明的保护范围。
一、制备例
1、耐高温变色颜料的制备
制备例1
将0.3份的硝酸亚铁和1.5份的钨酸亚铁分散于30份的1.0M的草酸水溶液中，加入5份的石墨烯纳米粉末，然后控温70℃搅拌分散60min；然后降温到室温，将0.25份的三异硬酯酸钛酸异丙酯和0.1份的乙酰丙酮胺混合均匀后加入到反应釜中，升温到80℃，搅拌反应30min，完成反应后转移到水热釜中，控温120-150℃，反应10h，完成反应后过滤，干燥后于空气的氛围下800℃下煅烧3-8h，最后粉碎至纳米级，制备得到耐高温变色颜料。
对比制备例1
与制备例1的区别在于将石墨烯替换为二氧化硅。
2、云母基含硼聚亚酰胺粘结剂的制备
制备例2
将二氨基二苯醚26质量份、均苯四甲酸二酐33质量份、二甲基乙酰胺300质量份、90℃搅拌0.5-2h,再加入全氟烷基甲硅烷基云母3质量份、甲基丙烯磺酸甜菜碱1质量份、2-环己基乙烯硼酸1质量份、蓖麻油2质量份混合均匀，270℃搅拌3h，过滤，烘干，然后进行辐照，辐照能量为3Mev，辐照剂量为600KGy，得到云母基含硼聚亚酰胺粘结剂。
对比制备例2
与制备例1的区别在于不添加蓖麻油。
3、耐高温变色树脂制备
制备例3-5
按表1的组分及用量备料，并混合均匀，制备得到耐高温变色树脂
表1耐高温变色树脂的组分及用量(单位：质量份数)
对比制备例3
与制备例3的区别在于云母基含硼聚亚酰胺粘结剂替换为对比制备例2所制备的物质。
对比制备例4
与制备例3的区别在于耐高温变色颜料替换为对比制备例1所制备的颜料。
对比制备例5
与制备例3的区别在于不添加稳定剂。
二、实施例
一种水晶元素地板颗粒镶嵌铺装方法，包括以下步骤：
1)将原料进行分段、开片、抛光处理，形成待加工基材；
2)采用吸空泵吸住基材，水平固定在打孔机上，打孔机采用数控打孔机，工作效率更高；
3)根据图纸要求，在基材表面打孔，打孔机转速控制在1900-2000转每分，在打孔机打孔的同时，采用吸尘器吸木屑；
4)打好孔后，取下基材，采用手工打磨机清理基材表面因打孔机打孔而产生的毛刺；
5)打磨完毛刺后，采用点胶器将胶水加入到孔深度三分之一处即可，所用胶水为水晶胶；
6)根据水晶镶嵌图纸的要求，采用点钻笔吸住水晶，将水晶镶嵌在孔中，等待胶水固化，将水晶粘住；其中胶水为环氧树脂AB胶；
7)在无尘室中，将温度控制在10-25℃，采用环氧树脂和无影胶体积比3∶1混合，对镶嵌水晶的基材进行树脂封胶处理，同时对基材四周封边，不留缝隙，待其固化，从而得到水晶地板。
实施例1-3分别使用制备例3-5所制备的耐高温变色树脂进行封胶处理；
对比例1-3分别使用对比制备例3-5制备的树脂进行封胶处理。
三、效果验证例
对各实施例和对比例制备的地板进行测试，测试产品变色效果，结果如下表2所示：
| 感温变色温度区间(℃) | 褪色情况 | |
| 实施例1 | -10-50℃ | 不易褪色 |
| 实施例2 | -20-60℃ | 不易褪色 |
| 实施例3 | -20-65℃ | 不易褪色 |
| 对比例1 | 0-45℃ | 易褪色 |
| 对比例2 | 5-50℃ | 易褪色 |
| 对比例3 | 7-45℃ | 易褪色 |
以上对本发明的具体实施例进行了描述。需要理解的是，本发明并不局限于上述特定实施方式，本领域技术人员可以在权利要求的范围内做出各种变形或修改，这并不影响本发明的实质内容。
Claims (10)
1.一种变色水晶元素镶嵌地板的制备方法，其特征在于，包括以下步骤：
1)将原料进行分段、开片、抛光处理，形成待加工基材；
2)采用吸空泵吸住基材，水平固定在打孔机上；
3)根据图纸，在基材表面打孔，打孔机转速控制在1900至2100转每分；
4)采用手工打磨机清理基材表面因打孔机打孔而产生的毛刺；
5)打磨完毛刺后，采用点胶器将胶水加入到孔中；
6)根据水晶镶嵌图纸的要求，采用点钻笔吸住水晶，将水晶镶嵌在孔中；
7)对镶嵌好水晶的基材进行树脂封胶处理，从而获得水晶地板，其中，所述树脂为耐高温变色树脂。
2.根据权利要求1所述的变色水晶元素镶嵌地板的制备方法，其特征在于，步骤7)中，所述耐高温变色树脂按质量份数计，包括：
3.根据权利要求2所述的变色水晶元素镶嵌地板的制备方法，其特征在于，所述的含氟聚合物树脂包括四氟乙烯-全氟烷氧基乙烯基醚共聚物、聚四氟乙烯树酯或全氟乙烯丙烯共聚物、全氟烷氧基乙烯基醚共聚物中的一种。
4.根据权利要求2所述的变色水晶元素镶嵌地板的制备方法，其特征在于，所述的云母基含硼聚亚酰胺粘结剂制备方法为：
S1、将二氨基二苯醚20-50质量份、均苯四甲酸二酐30-50质量份、二甲基乙酰胺200-500质量份、80-150℃搅拌0.5-2h,再加入全氟烷基甲硅烷基云母1-5质量份、甲基丙烯磺酸甜菜碱0.5-2质量份、2-环己基乙烯硼酸0.5-3质量份、蓖麻油2质量份、混合均匀制备成混合物；
S2、将混合物于220-300℃搅拌1-5h，过滤，烘干，然后进行辐照，辐照能量为1-5Mev，辐照剂量为200-800KGy，得到云母基含硼聚亚酰胺粘结剂。
5.根据权利要求2所述的变色水晶元素镶嵌地板的制备方法，其特征在于，所述耐高温变色颜料为石墨烯负载三氧化钨/三氧化二铁纳米材料，制备方法包如下步骤：
按照质量份数，将0.1-0.8份的硝酸亚铁和0.7-1.8份的钨酸亚铁分散于20-40份的0.5-1.0M的草酸水溶液中，加入2-8份的石墨烯纳米粉末，然后控温50-70℃搅拌分散30-60min；然后降温到室温，将0.05-0.25份的三异硬酯酸钛酸异丙酯和0.04-0.15份的乙酰丙酮胺混合均匀后加入到反应釜中，升温到60-80℃，搅拌反应20-30min，完成反应后转移到水热釜中，控温120-150℃，反应5-10h，完成反应后过滤，干燥后于空气的氛围下于600-800℃下煅烧3-8h，最后粉碎至纳米级，制备得到所述耐高温变色颜料。
6.根据权利要求1所述的变色水晶元素镶嵌地板的制备方法，其特征在于，所述步骤2)中打孔机采用数控打孔机。
7.根据权利要求1所述的变色水晶元素镶嵌地板的制备方法，其特征在于，所述步骤3)中打孔机在打孔的过程中，同时采用吸尘器吸木屑。
8.根据权利要求1所述的变色水晶元素镶嵌地板的制备方法，其特征在于，所述步骤5)中胶水为环氧树脂AB胶。
9.根据权利要求1所述的变色水晶元素镶嵌地板的制备方法，其特征在于，所述步骤7)中树脂封胶处理在无尘室中进行。
10.如权利要求1-9中任一项所述的制备方法制备的地板。