CN114749617A - Production method for reducing mountain scale at edge of hot-rolled 200-series stainless steel coil - Google Patents
Production method for reducing mountain scale at edge of hot-rolled 200-series stainless steel coil Download PDFInfo
- Publication number
- CN114749617A CN114749617A CN202210239210.0A CN202210239210A CN114749617A CN 114749617 A CN114749617 A CN 114749617A CN 202210239210 A CN202210239210 A CN 202210239210A CN 114749617 A CN114749617 A CN 114749617A
- Authority
- CN
- China
- Prior art keywords
- heating
- temperature
- section
- stainless steel
- furnace
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention disclosesA production method for reducing mountain scales on a hot-rolled edge part of 200 series stainless steel comprises the following steps: 1) smelting; 2) continuous casting: the casting speed of the continuous casting machine is 1.08 m/min; water quantity of continuous casting machine crystallizer 155m3H; the thickness of the liquid slag layer of the crystallizer covering slag for 200 series stainless steel in the crystallizer is 10mm during casting; 3) hot rolling: immediately sending the casting blank to a hot rolling heating furnace for heat preservation after the casting blank is cast, formed and cut off, and putting the casting blank into the heating furnace at the temperature of 435 ℃; the temperature of a preheating section is 910 ℃, the temperature of a first heating section is 1102 ℃, the temperature of a second heating section is 1250 ℃, and the temperature of a soaking section is 1260 ℃; the total time of the first heating stage and the second heating stage is controlled to be 83 minutes, and the total heating time in the furnace is 190 minutes. The steps are in ring buckling, and the defects are all not enough, so that the edge mountain scale defects of the high-carbon-nitrogen 200-series stainless steel are reduced from 20-30% to 1.55%.
Description
Technical Field
The invention relates to a stainless steel smelting process, in particular to a production method for reducing mountain scales on a hot-rolled edge part of 200-series stainless steel.
Background
The 200 series austenitic stainless steel is developed by adding manganese and nitrogen into the steel to replace noble metal nickel element on the basis of chromium-nickel series austenitic stainless steel, the austenitic element of the 200 series austenitic stainless steel contains nitrogen besides manganese and proper amount of nickel (4-6 percent) generally, the strength of the austenitic stainless steel is improved, and the 200 series austenitic stainless steel is suitable for equipment and parts which bear heavier load and have low requirements on corrosion resistance.
The high carbon nitrogen 200 series stainless steel is a cheap 200 series stainless steel which is newly developed in China in recent years and is mainly used for civil products such as pipe making, decoration and the like. The standard range (wt.%) of the components of the high carbon nitrogen 200 stainless steel is as follows: c: 0.10 to 0.15, Mn: 9-12, Si: 0.3 to 0.7, P: 0.060, S: less than or equal to 0.030, Cr: 13-14.5, Ni: 0-2, N: 0.17 to 0.2, Cu: 0.0-0.5, and the balance of residual iron and trace impurities. The stainless steel has the internal structure stability inferior to that of the original 200 series stainless steel due to the increase of the content of carbon and nitrogen, and the mountain scale (peeling) defect is easy to appear in the steel coil within 100mm from the edge part after the hot-rolled coil is pickled.
At present, the mainstream method for controlling the defects of mountain scale, scale folding or peeling and the like at the edge of stainless steel in China mainly comprises the steps of grinding the surface of a plate blank by a grinding machine or descaling by hot rolling descaling equipment. The measures are different according to different steel types, but the problem that the high carbon nitrogen 200 series stainless steel is easy to generate mountain scale defects within 100mm of the edge of the steel coil cannot be solved well by adopting the method.
Disclosure of Invention
The invention aims to provide a production method for reducing mountain scales on a hot-rolled edge part of 200 series stainless steel.
The technical scheme for realizing the purpose of the invention is as follows: a production method for reducing mountain scales on a hot-rolled edge part of 200 series stainless steel comprises the following steps:
1) Smelting: smelting high-carbon nitrogen 200 series stainless steel molten steel with smelting components controlled within a standard range in a refining furnace, and carrying out temperature control treatment, wherein the casting superheat degree is 28 ℃;
2) continuous casting: wherein the casting speed of the continuous casting machine is 1.08 m/min; the water quantity of the crystallizer of the continuous casting machine is controlled at 155m3H; 200 systems of crystallizer covering slag for stainless steel are uniformly added into a crystallizer during casting, and the thickness of a liquid slag layer of the covering slag in the crystallizer is 10 mm;
3) hot rolling: wherein, the casting blank is sent to a hot rolling heating furnace or a heat preservation furnace for heat preservation immediately after being cast, formed and cut off, and the temperature of the plate blank entering the heating furnace is 435 ℃; the heating process of the heating furnace is slowly heated up through a preheating section, a first heating section, a second heating section and a soaking section, wherein the temperature of the preheating section is 910 ℃, the temperature of the first heating section is 1102 ℃, the temperature of the second heating section is 1250 ℃, and the temperature of the soaking section is 1260 ℃; the total time of the first heating stage and the second heating stage is controlled to be 83 minutes, and the total heating time in the furnace is 190 minutes.
The inventor does not find a second phase such as inclusion in a defect part and a matrix structure is normal through microscopic analysis of an electron scanning microscope of a large number of mountain scale defect samples within 100mm from the edge of a steel coil, and does not find defects such as cracks and air holes through sampling analysis from the surface of a slab before hot rolling corresponding to the defect position, so that the defects and the peeling defect caused by the original slab surface cracks can be judged to be completely different defects. Moreover, in practice, it is found that the slab has no cracks and cannot avoid the generation of edge mountain scales: the slab blank adopting the conventional process is comprehensively inspected, the slab blank with the crack defect invisible to naked eyes is selected, the surface of the slab blank is uniformly ground by a grinding wheel for 2-3 mm, the surface of the slab blank is ensured to have no crack defect, the slab blank is hot-rolled by adopting the conventional process, the defect rate of mountain scale at the edge is not obviously reduced after the slab blank is inspected by acid pickling, and the defect rate is equivalent to that of the slab blank which is not specially selected.
Further, according to the analysis of the internal structure of the slab, the columnar crystals of the casting blank of the high-carbon-nitrogen 200-series stainless steel are developed, a chilling layer is thin (only 1-2 mm), the bonding force between the columnar crystals is weak, the probability of cracking between the columnar crystals is increased by heating at an overhigh temperature of a hot rolling heating furnace, and the scale appears due to metal deformation in the hot rolling process to form macroscopic scale defects.
Based on the research on the scale (peeling) defect of the 200 series stainless steel hot rolled edge part, the invention adjusts the parameters in the preparation process, and controls the water quantity of the crystallizer to be 155m under the premise of certain superheat degree and casting speed3/h～165m3H, under the cooling intensity, the columnar crystal size of the casting blank is relatively uniform; then, the surface temperature of the plate blank entering the heating furnace is 350-650 ℃, and after the plate blank is cooled and then enters the heating furnace for heating, the temperature gradient is too large, and the micro-cracks are caused by the stress between columnar crystal grains; the thickness of the liquid slag layer of the protective slag in the crystallizer is 8-15 mm, which is beneficial to uniform cooling of the slab, improvement of the internal structure and reduction of the stress between casting blank structures; then, in the total heating time of 180-230 minutes, the heating process of the heating furnace adopts slow temperature rise, the temperature of a preheating section is 900-950 ℃, the temperature of a first heating section is 1100-1120 ℃, and the temperature of a second heating section is The temperature is 1240-1255 ℃, and the temperature of the soaking section is 1255-1265 ℃; the total time of the first heating section and the second heating section is controlled to be 80-100 minutes, the total heating time in the furnace is 180-230 minutes, the problem of overlarge temperature gradient in the heating process can be relieved through controlling the temperature of the preheating section, and expansion of microcracks on the edges, caused by stress increase between columnar crystals, is relieved.
In the process of the invention, each step is annularly buckled, and one of the steps is absent, so that when the casting speed of the continuous casting machine is 1.08 m/min; the water quantity of the crystallizer of the continuous casting machine is controlled at 155m3H; the thickness of the liquid slag layer of the covering slag in the crystallizer is 10 mm; the temperature of a plate blank of a heating furnace in the hot rolling step is 435 ℃; the temperature of the preheating section of the heating furnace is 910 ℃, the temperature of the first heating section is 1102 ℃, the temperature of the second heating section is 1250 ℃, and the temperature of the soaking section is 1260 ℃; the total time of the first heating section and the second heating section is controlled to be 83 minutes, and when the total heating time in the furnace is 190 minutes, the edge scale defects of the high-carbon nitrogen 200 stainless steel are finally reduced to 1.55% from 20% -30%, the defect rate is effectively controlled, and the product quality and the market competitiveness are improved.
Detailed Description
The following is a detailed description of the preferred embodiments of the invention.
Example 1:
a production method for reducing mountain scales on a hot-rolled edge part of 200 series stainless steel comprises the following steps:
1) Smelting: smelting high-carbon nitrogen 200 series stainless steel molten steel with smelting components controlled within a standard range in a refining furnace, and carrying out temperature control treatment, wherein the casting superheat degree is 25 ℃;
2) continuous casting: wherein the casting speed of the continuous casting machine is 1.2 m/min; the water quantity of the crystallizer of the continuous casting machine is controlled at 155m3H; during casting, 200 systems of crystallizer covering slag for stainless steel is uniformly added into a crystallizer, and the thickness of the liquid slag layer of the covering slag in the crystallizer is 8 mm;
3) hot rolling: wherein, the casting blank is sent to a hot rolling heating furnace or a heat preservation furnace for heat preservation immediately after being cast, formed and cut off, and the temperature of the plate blank entering the heating furnace is 350 ℃; the heating process of the heating furnace is slowly heated up through a preheating section, a first heating section, a second heating section and a soaking section, wherein the temperature of the preheating section is 920 ℃, the temperature of the first heating section is 1110, the temperature of the second heating section is 1240 ℃, and the temperature of the soaking section is 1258 ℃; the total time of the first heating stage and the second heating stage is controlled to 92 minutes, and the total heating time in the furnace is 210 minutes.
Example 2:
a production method for reducing mountain scales on a hot-rolled edge part of 200 series stainless steel comprises the following steps:
1) smelting: smelting high-carbon nitrogen 200 series stainless steel molten steel with smelting components controlled within a standard range in a refining furnace, and controlling the temperature, wherein the casting superheat degree is 40 ℃;
2) Continuous casting: wherein the casting speed of the continuous casting machine is 1.0 m/min; water quantity control of 160m for continuous casting machine crystallizer3H; during casting, 200 systems of crystallizer covering slag for stainless steel is uniformly added into a crystallizer, and the thickness of the liquid slag layer of the covering slag in the crystallizer is 12 mm;
3) hot rolling: wherein, the casting blank is sent to a hot rolling heating furnace or a heat preservation furnace for heat preservation immediately after being cast, formed and cut off, and the temperature of the plate blank entering the heating furnace is 402 ℃; the heating process of the heating furnace is slowly heated up through a preheating section, a first heating section, a second heating section and a soaking section, wherein the temperature of the preheating section is 900 ℃, the temperature of the first heating section is 1100 ℃, the temperature of the second heating section is 1245 ℃, and the temperature of the soaking section is 1258 ℃; the total time of the first heating section and the second heating section is controlled to be 80 minutes, and the total heating time in the furnace is 180 minutes.
Example 3:
a production method for reducing mountain scales on a hot-rolled edge part of 200 series stainless steel comprises the following steps:
1) smelting: smelting high-carbon nitrogen 200 series stainless steel molten steel with smelting components controlled within a standard range in a refining furnace, and controlling the temperature, wherein the casting superheat degree is 30 ℃;
2) continuous casting: wherein the casting speed of the continuous casting machine is 1.1 m/min; the water quantity of the crystallizer of the continuous casting machine is controlled to be 165m 3H; 200 systems of crystallizer covering slag for stainless steel are uniformly added into a crystallizer during casting, and the thickness of a liquid slag layer of the covering slag in the crystallizer is 10 mm;
3) hot rolling: wherein, the casting blank is sent to a hot rolling heating furnace or a heat preservation furnace for heat preservation immediately after being cast, formed and cut off, and the temperature of the plate blank entering the heating furnace is 650 ℃; the heating process of the heating furnace is slowly heated up through a preheating section, a first heating section, a second heating section and a soaking section, wherein the temperature of the preheating section is 950 ℃, the temperature of the first heating section is 1120 ℃, the temperature of the second heating section is 1255 ℃, and the temperature of the soaking section is 1260 ℃; the total time of the first heating section and the second heating section is controlled to be 100 minutes, and the total heating time in the furnace is 230 minutes.
Example 4:
a production method for reducing mountain scales on a hot-rolled edge part of 200 series stainless steel comprises the following steps:
1) smelting: smelting high-carbon nitrogen 200 series stainless steel molten steel with smelting components controlled within a standard range in a refining furnace, and controlling the temperature, wherein the casting superheat degree is 33 ℃;
2) continuous casting: wherein the casting speed of the continuous casting machine is 1.06 m/min; the water quantity of the crystallizer of the continuous casting machine is controlled at 163m3H; 200 systems of crystallizer covering slag for stainless steel are uniformly added into a crystallizer during casting, and the thickness of a liquid slag layer of the covering slag in the crystallizer is 11 mm;
3) Hot rolling: wherein, the casting blank is sent to a hot rolling heating furnace or a heat preservation furnace for heat preservation immediately after being cast, formed and cut off, and the temperature of the plate blank entering the heating furnace is 455 ℃; the heating process of the heating furnace is slowly heated up through a preheating section, a first heating section, a second heating section and a soaking section, wherein the temperature of the preheating section is 920 ℃, the temperature of the first heating section is 1110 ℃, the temperature of the second heating section is 1245 ℃, and the temperature of the soaking section is 1265 ℃; the total time of the first heating stage and the second heating stage is controlled to be 95 minutes, and the total heating time in the furnace is 212 minutes.
Example 5:
a production method for reducing mountain scale on a hot-rolled edge part of 200-series stainless steel comprises the following steps:
1) smelting: smelting high-carbon nitrogen 200 series stainless steel molten steel with smelting components controlled within a standard range in a refining furnace, and carrying out temperature control treatment, wherein the casting superheat degree is 28 ℃;
2) continuous casting: wherein the casting speed of the continuous casting machine is 1.08 m/min; the water quantity of the crystallizer of the continuous casting machine is controlled to be 155m3H; 200 series stainless steel knots are evenly added into the crystallizer during castingThe thickness of a liquid slag layer of the crystallizer casting powder in the crystallizer is 10 mm;
3) hot rolling: wherein, the casting blank is sent to a hot rolling heating furnace or a heat preservation furnace for heat preservation immediately after being cast, formed and cut off, and the temperature of the plate blank entering the heating furnace is 435 ℃; the heating process of the heating furnace is slowly heated up through a preheating section, a first heating section, a second heating section and a soaking section, wherein the temperature of the preheating section is 910 ℃, the temperature of the first heating section is 1102 ℃, the temperature of the second heating section is 1250 ℃, and the temperature of the soaking section is 1260 ℃; the total time of the first heating stage and the second heating stage is controlled to be 83 minutes, and the total heating time in the furnace is 190 minutes.
The crystallizer casting powder for 200 series stainless steel in this embodiment is a commercially available product, and is not described herein again.
The above-mentioned embodiment was referred to as a 452 coil of 200-series stainless steel strip, and after pickling, the quality inspector visually determined that the degraded coil with the mountain scale defect at the edge was 7 coils and the defect rate was 1.55%. From the practical situation of mass production, the defect rate is effectively controlled.
The casting superheat degree is limited to 25-40 ℃, the casting speed of a continuous casting machine is limited to 1.0-1.2 m/min, and the purposes of forming a good internal structure in the casting blank cooling and forming process, reducing internal stress and reducing cracking in the subsequent hot rolling and heating rolling process to cause scale folding defects are achieved; in the heating process of the hot rolling heating furnace, the heating speed of the plate blank is controlled as much as possible, the temperature gradient in the plate blank is reduced, the internal stress is reduced, and cracking is prevented. After a large number of experiments on the heating process of the heating furnace, the inventor finds that the edge crack defect of the hot-rolled steel coil can be caused by too slow heating and too low temperature control, and the edge mountain scale defect rate is obviously increased by too fast heating speed and too high temperature. Therefore, the temperature of the preheating section is 900-950 ℃, the temperature of the first heating section is 1100-1120 ℃, the temperature of the second heating section is 1240-1255 ℃, and the temperature of the soaking section is 1255-1265 ℃. In order to further reduce the defect rate of side mountain scale, the mechanism of reducing the internal thermal stress of the slab is combined, the cast slab is cast, formed and cut, and then is immediately sent to a hot rolling heating furnace or is insulated by a heat-insulating furnace (cover), the temperature of the slab entering the heating furnace is controlled to be 350-650 ℃, so that the core of the slab has a certain initial temperature when the slab enters the heating furnace, and the temperature gradient inside and outside the slab is further reduced under the heating of high-temperature flame.
The above description is only an embodiment of the present invention, and not intended to limit the scope of the present invention, and all equivalent flow transformations made by the present specification, or directly or indirectly applied to other related technical fields, are included in the scope of the present invention.
Claims (1)
1. A production method for reducing mountain scales on a 200-series stainless steel hot-rolled edge part is characterized by comprising the following steps of: which comprises the following steps:
1) smelting: smelting high-carbon nitrogen 200 series stainless steel molten steel with smelting components controlled within a standard range in a refining furnace, and controlling the temperature, wherein the casting superheat degree is 28 ℃;
2) continuous casting: wherein the casting speed of the continuous casting machine is 1.08 m/min; the water quantity of the crystallizer of the continuous casting machine is controlled to be 155m3H; 200 systems of crystallizer covering slag for stainless steel are uniformly added into a crystallizer during casting, and the thickness of a liquid slag layer of the covering slag in the crystallizer is 10 mm;
3) hot rolling: wherein, the casting blank is sent to a hot rolling heating furnace or a heat preservation furnace for heat preservation immediately after being cast, formed and cut off, and the temperature of the plate blank entering the heating furnace is 435 ℃; the heating process of the heating furnace is slowly heated up through a preheating section, a first heating section, a second heating section and a soaking section, wherein the temperature of the preheating section is 910 ℃, the temperature of the first heating section is 1102 ℃, the temperature of the second heating section is 1250 ℃, and the temperature of the soaking section is 1260 ℃; the total time of the first heating stage and the second heating stage is controlled to be 83 minutes, and the total heating time in the furnace is 190 minutes.