CN114717864A - 一种释放负离子和发射远红外线印点的制作工艺 - Google Patents
一种释放负离子和发射远红外线印点的制作工艺 Download PDFInfo
- Publication number
- CN114717864A CN114717864A CN202210314095.9A CN202210314095A CN114717864A CN 114717864 A CN114717864 A CN 114717864A CN 202210314095 A CN202210314095 A CN 202210314095A CN 114717864 A CN114717864 A CN 114717864A
- Authority
- CN
- China
- Prior art keywords
- far infrared
- manufacturing
- releasing
- fabric
- drying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种释放负离子和发射远红外线印点的制作工艺，所述制作材料包括油性硅胶、凝固剂、电气石粉，所述油性硅胶比例为35％‑80％，所述凝固剂比例为5％‑20％，电气石粉5％‑60％本发明本发明通过印点的制作，任何人体穿着物或者医疗设备上植入释放负离子和发射远红外线印点后的功效：促进血液循环，改善微循环，调节新陈代谢，活血化瘀、舒展筋骨、消炎、止痛、止痒、去异味，提高机体免疫力与自愈力。
Description
技术领域
本发明涉及技术领域，具体为一种释放负离子和发射远红外线印点的制作工艺。
背景技术
负离子对人体的7大作用在众多权威书籍《现代物理治疗学》、《空气负离子在医疗保健及环保中的应用》等及大量临床实验中记录了负离子对人体机能的作用，总结出来主要有7大方面。
1、活化细胞，提高免疫力
负离子进入人体后可以为细胞内供氧，激活细胞，增强细胞膜的通透性，提高新陈代谢及排毒能力，使单核吞噬细胞的功能加强，增加血液中抗体的含量，从而提高机体的免疫力和抗病能力，使人感到精神振奋，充满活力。
2、降低血液黏稠度、扩张血管、促进血液正常
负离子能有效修复细胞膜电位，增大血红细胞负电量，使得每个血红细胞有足够的负电位使各个细胞间产生同极斥力，可有效降低血液粘度，使冠状动脉得到扩张，增加冠状动脉血流量，恢复红细胞的变形能力，增强血浆蛋白的胶体稳定性，促进血液循环，保持微循环系统血液正常。
3、改善呼吸系统
负离子可以促进鼻腔粘膜柱状上皮细胞形成，使支气管粘膜的纤毛运动加速，增强呼吸酶活性，改善肺泡的分泌功能，提高肺泡的通气和换气功能，起到镇咳、缓解支气管痉挛、增加肺活量等功效，对改善哮喘、气管炎等呼吸系统疾病有良好效果。
4、改善神经系统
负离子可以穿透人体血液屏障进入脑脊液，调节大脑皮层功能，使兴奋和抑制机制得以平衡，起到消除疲劳、振奋精神、提高工作效率的作用，同时负离子还能消除影响睡眠的脑电波，起到助眠作用，对改善睡眠、神经衰弱有良好效果。
5、改善内分泌系统
负离子能通过血液循环，改善内分泌的分泌功能，提高性腺功能和甲状腺功能，促进血液的吸收和排出，使新陈代谢加快，能有效改善内分泌障碍。
6、改善消化功能
吸入大量的负离子还可增强胃液的分泌，调节肠胃蠕动，改善胃肠道功能，促进胃部的消化和吸收，增加食欲，对结肠炎、痢疾及便秘等有良好的缓解效果。
7、促进伤口愈合
负离子作用于人体皮肤后，可以使皮肤血管短暂收缩，继而扩张，可改善微循环和组织营养，加快皮肤上皮再生，可以促进伤口的愈合。有研究表明：负离子可使伤口愈合速度加快20％。
现有的印点制作方法存在的缺陷是：
1、专利文件CN106094247A公开了负离子陶瓷材料、负离子陶瓷鼻托及其制作方法，“其中，负离子陶瓷材料包括以下组分：钇稳定氧化锆、负离子粉，其中，负离子粉为纳米级高纯粉末，负离子粉占总原料的5％－15％重量比。负离子陶瓷鼻托，其制作原料包括：钇稳定氧化锆、负离子粉，其中，负离子粉为纳米级高纯粉末，负离子粉占总原料的5％－15％重量比。负离子陶瓷鼻托制造方法，包括如下步骤：准备原料、制备原料、原料干燥、添加成型剂、注塑成型、去除成型剂、窑炉烧成。采用上述方法及原料制成的陶瓷鼻托，具有质地坚硬、耐高温、防腐蚀、抗氧化、耐磨损、表面具有宝石般光泽、健康、能辅助缓解使用者眼部疲劳等优点”；
2、专利文件CN105751641B公开了一种消除有害气体且释放负离子的车内装饰材料制作方法，“包括以下步骤：将以下重量分数的原料放入容器内：电气石30-40份，砭石10-20份,锗石10-30份,稀土10-20份、硅藻土10-15份，阻燃剂1-10份,水1-10份，充分混合并加热到130摄氏度；混合加热后的物料通过搅拌机搅拌均匀，再加入抗静电粉剂及碳酸钙、石英粉，加热升温到160摄氏度；继续添加5％的稳定剂与PVC管材进行微空发泡成型，通过覆膜设备与优质透气的PU底面贴合；降温到140℃，与天然优质橡胶贴合形成防滑层，后经裁剪加工制作而成。本发明，制作成的车内装饰材料能够释放高浓度负离子，快速分解甲醛、苯、TVOC等有害气体，起到净化空气的作用，有利于人体健康”；
3、专利文件CN110549453A公开了一种用于负离子生态装饰板的复合气凝胶保温材料的制作方法，“包括以下步骤：将小麦秸秆洗净后烘干粉碎，球磨4h，加入到H2O2-NaOH溶液复合体系中，45℃超声震荡处理，过滤，洗涤至中性，烘干；加入到NaOH-尿素-硫脲溶液复合体系中，5℃搅拌20-25h后，过滤，向滤液滴加稀盐酸，直至纤维素完全析出后过滤，40-50℃烘干；将烘干后的纤维素加入到N,N-二甲基乙酰胺中，加入无水氯化锂，自然冷却至室温，再用去离子水浸泡纤维素醇凝胶15-20h；将正硅酸乙酯加入到乙醇中，再加入氨水搅拌均匀后，放入高压釜中，干燥5h，即可得到所述有机-无机复合气凝胶保温材料，本发明制备方法简单，易于操作，条件温和，适合大规模推广应用”，综上所述负离子的用于医疗或者穿戴设备上时，会增加人体免疫能力等等一系列功效。
发明内容
本发明的目的在于提供一种释放负离子和发射远红外线印点的制作工艺，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：一种释放负离子和发射远红外线印点的制作工艺，所述制作材料包括油性硅胶、凝固剂、负离子粉和电气石粉；
所述油性硅胶比例为35％-80％，所述凝固剂比例为5％-20％。
优选的，所述电气石粉比例为5％-60％。
优选的，所述油性硅胶与凝固剂搅拌时间2-30分钟，形成液态混合物，液态效果。
优选的，所述将电气石粉与所述液态混合物搅拌2-30分钟，形成综合液态混合物，液态效果。
优选的，所述综合液态混合物用1公斤以上压力通过丝网印植在面料上，印植时间1-20分钟，液态效果。
优选的，所述印植后将丝网垂直抬起移开，依据油性硅胶与凝固剂及电气石粉配比率，决定置留1-10分钟，凝固但不干燥的状态下或面料下有承载物时，移动印植面料。
优选的，所述把可移动的印植面料进行加热干燥或自然干燥。
优选的，所述进行加热干燥时，将可移动的印植面料平整放在烘干机的内部，根据面料的厚度与材质，选择加热干燥时间5分钟-2小时。
优选的，所述自然干燥时，将可移动的印植面料平展悬挂在距地面0.5-2.5米处，自然干燥时间2小时-2周。
优选的，所述印植面料干燥后取走使用。
与现有技术相比，本发明的有益效果是：
本发明通过印点的制作，任何人体穿着物或者医疗设备上植入释放负离子和发射远红外线印点后的功效：促进血液循环，改善微循环，调节新陈代谢，活血化瘀、舒展筋骨、消炎、止痛、止痒、去异味，提高机体免疫力与自愈力。
附图说明
图1是本发明的工艺流程图。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
在本发明的描述中，需要说明的是，术语“上”、“下”、“内”、“外”“前端”、“后端”、“两端”、“一端”、“另一端”等指示的方位或位置关系为基于附图所示的方位或位置关系，仅是为了便于描述本发明和简化描述，而不是指示或暗示所指的装置或元件必须具有特定的方位、以特定的方位构造和操作，因此不能理解为对本发明的限制。此外，术语“第一”、“第二”仅用于描述目的，而不能理解为指示或暗示相对重要性。
在本发明的描述中，需要说明的是，除非另有明确的规定和限定，术语“安装”、“设置有”、“连接”等，应做广义理解，例如“连接”，可以是固定连接，也可以是可拆卸连接，或一体的连接；可以是机械连接，也可以是电连接；可以是直接相连，也可以通过中间媒介间接相连，可以是两个元件内部的连通。对于本领域的普通技术人员而言，可以具体情况理解上述术语在本发明中的具体含义。
实施例1：请参阅图1，本发明提供的一种实施例：一种释放负离子和发射远红外线印点的制作工艺，所述制作材料包括油性硅胶、凝固剂、电气石粉，所述油性硅胶比例为53％，所述凝固剂比例为18％，所述电气石粉比例为29％，所述油性硅胶与凝固剂搅拌时间2-30分钟，形成液态混合物，液态效果，所述将液态混合物和电气石粉搅拌2-30分钟后，形成综合液态混合物，液态效果，将综合液态混合物用1公斤以上压力通过丝网印植在面料上，所述印植时间1-20分钟，将丝网垂直抬起移开，依据油性硅胶与凝固剂和电气石粉配比率，决定置留1-10分钟，凝固但不干燥的状态下或面料下有承载物时，移动印植的面料，把己经印植的面料进行加热干燥或自然干燥，所述加热干燥时，将可移动的印植面料平整放在烘干机的内部，根据面料的厚度与材质，选择烘干时间5分钟-2小时，所述自然干燥时，将可移动的印植面料平展悬挂在距地面0.5-2.5米处，自然干燥时间2小时-2周，所述印植面料干燥后取走使用。
实施例2：请参阅图1，本发明提供的一种实施例：一种释放负离子和发射远红外线印点的制作工艺，所述制作材料包括油性硅胶、凝固剂、电气石粉，所述油性硅胶比例为47％，所述凝固剂比例为10％，所述电气石粉比例为43％，所述油性硅胶与凝固剂搅拌时间2-30分钟，形成液态混合物，液态效果，所述将液态混合物和电气石粉搅拌2-30分钟后，形成综合液态混合物，液态效果，将综合液态混合物用1公斤以上压力通过丝网印植在面料上，所述印植时间1-20分钟，将丝网垂直抬起移开，依据油性硅胶与凝固剂和电气石粉配比率，决定置留1-10分钟，凝固但不干燥的状态下或面料下有承载物时，移动印植的面料，把己经印植的面料进行加热干燥或自然干燥，所述加热干燥时，将可移动的印植面料平整放在烘干机的内部，根据面料的厚度与材质，选择烘干时间5分钟-2小时，所述自然干燥时，将可移动的印植面料平展悬挂在距地面0.5-2.5米处，自然干燥时间2小时-2周，所述印植面料干燥后取走使用。
实施例3：请参阅图1，本发明提供的一种实施例：一种释放负离子和发射远红外线印点的制作工艺，所述制作材料包括油性硅胶、凝固剂、电气石粉，所述油性硅胶比例为55％，所述凝固剂比例为7％，所述电气石粉比例为38％，所述油性硅胶与凝固剂搅拌时间2-30分钟，形成液态混合物，液态效果，所述将液态混合物和电气石粉搅拌2-30分钟后，形成综合液态混合物，液态效果，将综合液态混合物用1公斤以上压力通过丝网印植在面料上，所述印植时间1-20分钟，将丝网垂直抬起移开，依据油性硅胶与凝固剂和电气石粉配比率，决定置留1-10分钟，凝固但不干燥的状态下或面料下有承载物时，移动印植的面料，把己经印植的面料进行加热干燥或自然干燥，所述加热干燥时，将可移动的印植面料平整放在烘干机的内部，根据面料的厚度与材质，选择烘干时间5分钟-2小时，所述自然干燥时，将可移动的印植面料平展悬挂在距地面0.5-2.5米处，自然干燥时间2小时-2周，所述印植面料干燥后取走使用。
实施例4：请参阅图1，本发明提供的一种实施例：一种释放负离子和发射远红外线印点的制作工艺，所述制作材料包括油性硅胶、凝固剂、电气石粉，所述油性硅胶比例为69％，所述凝固剂比例为12％，所述电气石粉比例为19％，所述油性硅胶与凝固剂搅拌时间2-30分钟，形成液态混合物，液态效果，所述将液态混合物和电气石粉搅拌2-30分钟后，形成综合液态混合物，液态效果，将综合液态混合物用1公斤以上压力通过丝网印植在面料上，所述印植时间1-20分钟，将丝网垂直抬起移开，依据油性硅胶与凝固剂和电气石粉配比率，决定置留1-10分钟，凝固但不干燥的状态下或面料下有承载物时，移动印植的面料，把己经印植的面料进行加热干燥或自然干燥，所述加热干燥时，将可移动的印植面料平整放在烘干机的内部，根据面料的厚度与材质，选择烘干时间5分钟-2小时，所述自然干燥时，将可移动的印植面料平展悬挂在距地面0.5-2.5米处，自然干燥时间2小时-2周，所述印植面料干燥后取走使用。
实施例5：请参阅图1，本发明提供的一种实施例：一种释放负离子和发射远红外线印点的制作工艺，所述制作材料包括油性硅胶、凝固剂、电气石粉，所述油性硅胶比例为80％，所述凝固剂比例为15％，所述电气石粉比例为5％，所述油性硅胶与凝固剂搅拌时间2-30分钟，形成液态混合物，液态效果，所述将液态混合物和电气石粉搅拌2-30分钟后，形成综合液态混合物，液态效果，将综合液态混合物用1公斤以上压力通过丝网印植在面料上，所述印植时间1-20分钟，将丝网垂直抬起移开，依据油性硅胶与凝固剂和电气石粉配比率，决定置留1-10分钟，凝固但不干燥的状态下或面料下有承载物时，移动印植的面料，把己经印植的面料进行加热干燥或自然干燥，所述加热干燥时，将可移动的印植面料平整放在烘干机的内部，根据面料的厚度与材质，选择烘干时间5分钟-2小时，所述自然干燥时，将可移动的印植面料平展悬挂在距地面0.5-2.5米处，自然干燥时间2小时-2周，所述印植面料干燥后取走使用。
实施例6：请参阅图1，本发明提供的一种实施例：一种释放负离子和发射远红外线印点的制作工艺，所述制作材料包括油性硅胶、凝固剂、电气石粉，所述油性硅胶比例为40％，所述凝固剂比例为7％，所述电气石粉比例为53％，所述油性硅胶与凝固剂搅拌时间2-30分钟，形成液态混合物，液态效果，所述将液态混合物和电气石粉搅拌2-30分钟后，形成综合液态混合物，液态效果，将综合液态混合物用1公斤以上压力通过丝网印植在面料上，所述印植时间1-20分钟，将丝网垂直抬起移开，依据油性硅胶与凝固剂和电气石粉配比率，决定置留1-10分钟，凝固但不干燥的状态下或面料下有承载物时，移动印植的面料，把己经印植的面料进行加热干燥或自然干燥，所述加热干燥时，将可移动的印植面料平整放在烘干机的内部，根据面料的厚度与材质，选择烘干时间5分钟-2小时，所述自然干燥时，将可移动的印植面料平展悬挂在距地面0.5-2.5米处，自然干燥时间2小时-2周，所述印植面料干燥后取走使用。
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。不应将权利要求中的任何附图标记视为限制所涉及的权利要求。
Claims (10)
1.一种释放负离子和发射远红外线印点的制作工艺，其特征在于：所述制作材料包括油性硅胶、凝固剂、电气石粉；
所述油性硅胶比例为35％-80％，所述凝固剂比例为5％-20％。
2.根据权利要求1所述的一种释放负离子和发射远红外线印点的制作工艺，其特征在于：所述电气石粉比例为5％-60％。
3.根据权利要求1所述的一种释放负离子和发射远红外线印点的制作工艺，其特征在于：所述要求1油性硅胶与凝固剂搅拌2-30分钟，形成液态混合物，液态效果。
4.根据权利要求1所述的一种释放负离子和发射远红外线印点的制作工艺，其特征在于：所述要求2电气石粉与所述3液态混合物搅拌2-30分钟，形成综合液态混合物，液态效果。
5.根据权利要求1所述的一种释放负离子和发射远红外线印点的制作工艺，其特征在于：所述将4的综合液态混合物用1公斤以上压力通过丝网印植在面料上，印植时间为1-20分钟，液态效果。
6.根据权利要求1所述的一种释放负离子和发射远红外线印点的制作工艺，其特征在于：所述5印植后将丝网垂直抬起移开，依据油性硅胶与凝固剂及电气石粉配比率，决定置留1-10分钟，凝固但不干燥的状态下或面料下有承载物时，移动印植的面料。
7.根据权利要求1所述的一种释放负离子和发射远红外线印点的制作工艺，其特征在于：所述6进行加热干燥或自然干燥。
8.根据权利要求1所述的一种释放负离子和发射远红外线印点的制作工艺，其特征在于：所述6加热干燥时，将可移动的印植面料要平整放在烘干机的内部，根据面料的厚度与材质，选择烘干时间5分钟-2小时。
9.根据权利要求1所述的一种释放负离子和发射远红外线印点的制作工艺，其特征在于：所述6自然干燥，将可移动的印植面料平展悬挂在距地面0.5-2.5米处，自然干燥时间2小时-2周。
10.根据权利要求1所述的一种释放负离子和发射远红外线印点的制作工艺，其特征在于：所述印植面料干燥后取走使用。