CN114705585A - 硅碳合金、脱氧剂、孕化剂、硅碳合剂中硅的测定方法 - Google Patents
硅碳合金、脱氧剂、孕化剂、硅碳合剂中硅的测定方法 Download PDFInfo
- Publication number
- CN114705585A CN114705585A CN202210340533.9A CN202210340533A CN114705585A CN 114705585 A CN114705585 A CN 114705585A CN 202210340533 A CN202210340533 A CN 202210340533A CN 114705585 A CN114705585 A CN 114705585A
- Authority
- CN
- China
- Prior art keywords
- silicon
- sample
- crucible
- deoxidizer
- alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于化学分析技术领域，涉及一种硅碳合金、脱氧剂、孕化剂、硅碳合剂中硅的测定方法，包括以下步骤：(1)试样碱熔分解；(2)制取沙状试样；(3)凝聚、过滤、洗涤、灼烧。本发明的测定方法操作简便，过程耗时短，硅含量检测值准确，适用于对硅碳合金、脱氧剂、孕化剂及硅碳合剂等不同物质中硅含量的测定，且能满足同时对大批量硅碳合金、脱氧剂、孕化剂及硅碳合剂中硅含量的检测。
Description
技术领域
本发明属于化学分析技术领域，尤其涉及一种硅碳合金、脱氧剂、孕化剂、硅碳合剂中硅的测定方法。
背景技术
转炉炼钢过程中，钢液中氧的存在是不可避免的，如果钢液中的氧气没有经过有效的处理，氧含量非常高的钢液在凝固的过程中就会和已有的钢液发生反应、结晶、并且出现氧化亚铁，这种氧化亚铁物质在钢液中存在，铸坯被破坏，对钢产品的质量会产生直接性的影响，严重还会出现变形的现象，有热脆产生，还可能会让钢铁出现进一步的氧化现象。钢液当中出现非常多的氧含量会让硫的危害被加重，进而相继的发生化学反应，生成各种氧化杂质，在夹杂钢体当中，这些现象的出现都会对钢产品的力学性能产生危害。
因此，在炼钢过程中需对钢液进行脱氧，脱氧过程一般需加入硅碳合金、脱氧剂、孕化剂和硅碳合剂等，其中硅含量的确定对炼钢质量至关重要，由于硅碳合金、脱氧剂、孕化剂及硅碳合剂中的成分不同，目前还没有一种通用的方法能都适用于上述各种物质中硅的检测。
发明内容
本发明的目的是为了解决现有技术中存在的问题，而提出的一种硅碳合金、脱氧剂、孕化剂、硅碳合剂中硅的测定方法。
为了实现上述目的，本发明采用了如下技术方案：
硅碳合金、脱氧剂、孕化剂、硅碳合剂中硅的测定方法，包括以下步骤：
(1)称取0.2g样品于镍坩埚中，加氢氧化钠4g于所述镍坩埚中拌匀，加热熔至清亮后，加3.5g过氧化钠于所述镍坩埚中，加热溶解后，转入750度的高温炉中溶解10分钟，取出，得样液；
(2)将所述样液转到盛有75ml盐酸水溶液的烧杯中脱埚，脱埚后在所述镍坩锅中再加20ml浓盐酸，洗锅沸煮，取埚，用盐酸水溶液冲洗所述镍坩埚，冲洗液转入所述烧杯中，将所述烧杯中的样液和冲洗液的混合液蒸干至沙状，得沙状试样；
(3)将所述沙状试样加入氯化铵盐酸饱和液20ml和1％wt动物胶20ml，保温10分钟，过滤，过滤时所述烧杯中加沸水至100ml，过滤后的废液用pH试纸测至无酸性，后将滤渣转入已恒重的瓷坩埚中进行灰化，灰化好后，转入900度的高温炉中烧30分钟，取出，冷却恒重。
检测方法原理：试样经碱熔分解后，用盐酸酸化，并蒸干至沙状，在浓盐酸溶液中，加动物明胶使硅酸凝聚、过滤、洗涤、灼烧，测得Si含量。
动物胶是一种富含氨基酸的蛋白质，在水中形成亲水性胶体，由于其中氨基酸的氨基和羧基并存，在不同酸度条件下，它们既可接受质子，又可放出质子，从而显示为两性电解质。在硅酸介质中，由于硅酸胶粒带负电荷，动物胶质点带正电荷，可以发生相互吸引和电性中和，使硅酸胶体凝聚，另外，由于动物胶是亲水性很强的胶体，它能从硅酸质点上夺取水分，以破坏其水化外壳，促使硅酸凝聚。
用动物胶凝聚硅酸时，其完全程度与凝聚时的酸度、温度及动物胶的用量有关，由于试液的酸度较高，胶团水化程度较小，它们凝聚能力越强，因此在加动物胶之前应先把试液蒸发至沙状，然后加浓盐酸，保温10min。
作为一种改进，步骤(2)中，所述盐酸水溶液体积浓度为5％。
作为一种改进，步骤(1)中，所述样品过280目筛后再加入所述镍坩埚中。
作为一种改进，步骤(3)中，所述滤纸中加有滤纸浆。
与现有技术相比，本发明的有益效果是：
本发明的测定方法操作简便，过程耗时短，硅含量检测值准确，适用于对硅碳合金、脱氧剂、孕化剂及硅碳合剂等不同物质中硅含量的测定，且能满足同时对大批量硅碳合金、脱氧剂、孕化剂及硅碳合剂中硅含量的检测。
具体实施方式
下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完整地描述。
硅碳合金、脱氧剂、孕化剂、硅碳合剂中硅的测定方法，包括以下步骤：
(1)样品过280目筛后，称取0.2g样品于镍坩埚中，加氢氧化钠4g于镍坩埚中搅拌均匀，在电炉上加热熔至清亮后，加3.5g过氧化钠于镍坩埚中，加热溶解后，转入750度的高温炉中溶解10分钟，取出，得样液；
(2)将样液转到盛有75ml盐酸水溶液(浓盐酸与水的体积比为5:95)的烧杯中脱埚，脱埚后在镍坩锅中再加20ml浓盐酸，洗锅沸煮，取埚，用盐酸水溶液(浓盐酸与水的体积比为5:95)冲洗镍坩埚，冲洗液转入烧杯中，将烧杯中的样液和冲洗液的混合液蒸干至沙状，得沙状试样；
(3)将沙状试样加入氯化铵盐酸饱和液20ml和1％wt动物胶(或明胶)20ml，保温10分钟，过滤，过滤的滤纸中加少许滤纸浆，过滤时烧杯中加沸水至100ml，过滤后的废液用pH试纸测至无酸性，后将滤渣转入已恒重的瓷坩埚中进行灰化，灰化好后，转入900度的高温炉中烧30分钟，取出，冷却恒重。
根据以下公式计算硅的总量：
Si单质＝(烧后重-空埚重)×0.4675/0.2×100
Si残渣＝(烧后重-空埚重)×0.7/0.2×100
Si总＝Si单质+Si残渣
按上述方法分别对硅碳合金、脱氧剂、孕化剂和硅碳合剂等样品进行测定，结果如表1、表2、表3和表4：
表1硅碳合金中硅的含量
表2脱氧剂中硅的含量
表3孕化剂中硅的含量
表4硅碳合剂中硅的含量
从表1-表4中可以看出，通过本方法检测出的硅含量基本跟标准值相符，因此，本方法的检测结果准确。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。
Claims (4)
1.硅碳合金、脱氧剂、孕化剂、硅碳合剂中硅的测定方法，其特征在于，包括以下步骤：
(1)称取0.2g样品于镍坩埚中，加氢氧化钠4g于所述镍坩埚中拌匀，加热熔至清亮后，加3.5g过氧化钠于所述镍坩埚中，加热溶解后，转入750度的高温炉中溶解10分钟，取出，得样液；
(2)将所述样液转到盛有75ml盐酸水溶液的烧杯中脱埚，脱埚后在所述镍坩锅中再加20ml浓盐酸，洗锅沸煮，取埚，用盐酸水溶液冲洗所述镍坩埚，冲洗液转入所述烧杯中，将所述烧杯中的样液和冲洗液的混合液蒸干至沙状，得沙状试样；
(3)将所述沙状试样加入氯化铵盐酸饱和液20ml和1％wt动物胶20ml，保温10分钟，过滤，过滤时所述烧杯中加沸水至100ml，过滤后的废液用pH试纸测至无酸性，后将滤渣转入已恒重的瓷坩埚中进行灰化，灰化好后，转入900度的高温炉中烧30分钟，取出，冷却恒重。
2.根据权利要求1所述的硅碳合金、脱氧剂、孕化剂、硅碳合剂中硅的测定方法，其特征在于，步骤(2)中，所述盐酸水溶液体积浓度为5％。
3.根据权利要求1所述的硅碳合金、脱氧剂、孕化剂、硅碳合剂中硅的测定方法，其特征在于，步骤(1)中，所述样品过280目筛后再加入所述镍坩埚中。
4.根据权利要求1所述的硅碳合金、脱氧剂、孕化剂、硅碳合剂中硅的测定方法，其特征在于，步骤(3)中，所述滤纸中加有滤纸浆。