CN114605909A - 一种大灯翻新修复剂 - Google Patents
一种大灯翻新修复剂 Download PDFInfo
- Publication number
- CN114605909A CN114605909A CN202210405369.5A CN202210405369A CN114605909A CN 114605909 A CN114605909 A CN 114605909A CN 202210405369 A CN202210405369 A CN 202210405369A CN 114605909 A CN114605909 A CN 114605909A
- Authority
- CN
- China
- Prior art keywords
- component
- resin
- headlamp
- percentage
- following components
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于树脂领域，公开了一种大灯翻新修复剂，其如下重量百分比组分组成：A组分55‑65％；1005TF树脂19‑20％；B组分8‑12％；有机溶剂余量。该修复剂的优势在于：透光率好、硬度高、附着力强、耐高温。
Description
技术领域
本发明涉及新材料领域，具体为一种大灯翻新修复剂。
背景技术
CN201210338794.3公开了一种制备汽车大灯翻新专用液的新方法。该专用液除具有去污打蜡效果外，还具有防静电、抑菌等多种功能，其由如下组分组成：纳米氧化钛1-5％，香精1-5％、硅油1-5％，液体石蜡1-5％，单氟磷酸钠0.1％-1％，水79-95.9％；
CN202110948014.6公开了.一种汽车大灯镀膜剂，其包含如下组分：高官能度脂肪族聚氨酯丙烯酸酯、有机-无机杂化聚氨酯丙烯酸酯、聚合单体、光引发剂，聚合单体包括季戊四醇四丙烯酸酯、乙氧化季戊四醇四丙烯酸酯、二-三羟甲基丙烷四丙烯酸酯、丙氧化季戊四醇四丙烯酸酯、二季戊四醇六丙烯酸酯中的一种或两种以上的混合物，聚合单体扮演交联剂的作用。
CN201110020806.3公开了一种汽车大灯修复镀膜工艺，它的修复工艺流程为:若为灯面划痕损伤:拆卸→划痕打磨→清理→镀膜喷涂→装灯→交车；若为发黄、龟裂灯损伤:拆卸→清洗→表面打磨→清理→镀膜喷涂→抛光→二次镀膜喷涂→装灯→交车。它主要用于修复亚克力、PBT、PA、PC和塑料、有机玻璃汽车大灯、尾灯、仪表盘、警灯等灯具上的划痕、发黄、龟裂、表面模糊不清等，修复镀膜后能快速、有效地恢复表面的原有透明度与清晰度,施工后硬度能达到4个H,抗拒油性好,耐达高温可达150℃以上。
大灯翻新、镀膜的配方在本领域中属于较为小众的产品，但是其产品的要求为修复后的大灯的透光率、膜层硬度、耐高温、附着性都有着较为苛刻的要求。
基于此，本案解决的技术问题是：如何开发出一款具有高透光率、膜层硬度高、耐高温、附着性优的双组分配方。
发明内容
本发明的目的在于提供一种大灯翻新修复剂，该修复剂的优势在于：透光率好、硬度高、附着力强、耐高温。
为实现上述目的，本发明提供如下技术方案：一种大灯翻新修复剂，其如下重量百分比组分组成：
A组分55-65％；
1005TF树脂19-20％；
B组分8-12％；
有机溶剂余量；
其中，所述A组分由如下重量百分比组分组成：
丙二醇甲醚7-9％；
甲苯5-7％；
乙酸乙酯32-36％；
SU1690树脂18-22％；
SU1750树脂30-34％；
所述B组分由如下重量百分比组成：
184引发剂34-38％；
TPO引发剂2-2.8％；
流平剂2.2-2.6％；
消泡剂1-1.4％；
醋酸正丁酯56-60％。
其中，1005TF树脂为東莞市云美新材料有限公司提供；其结构式如式1所示：
SU1690树脂为東莞市云美新材料有限公司提供；SU1690是一种6官脂肪族聚氨酯丙烯酸酯，其物理性质为：
SU1750树脂为東莞市云美新材料有限公司提供；SU1750是一种2官能团脂肪族聚氨酯丙烯酸酯，其物理性质为：
本方案采用了复合引发剂，特性光引发剂184是一种高效的自由基I型非泛黄光引发剂，UV体系最常用的光引发剂。化学名称1-羟基环己基苯基甲酮CAS号947-19-3；光引发剂TPO是一种高效的自由基(1)型、在长波长范围内都有吸收的高效光引发剂。由于具有很宽的吸收范围，其有效吸收峰值为350～400nm，一直吸收致420nm左右，它的吸收峰较常规引发剂偏长，经光照后可生成苯甲酰和磷酰基两个自由基，都能引发聚合，因此光固化速度快，它还具有光漂白作用，适合于厚膜深层固化和涂层不变黄的特性。
两者结合，作用于本发明的复合树脂体系，具有不变黄、漂白的作用，其有助于树脂形成轻交联三维网络，涂层的强度和附着力都有改善。
在上述的大灯翻新修复剂中，其如下重量百分比组分组成：
A组分60％；
1005TF树脂19.2％；
B组分10.8％；
有机溶剂余量；
其中，所述A组分由如下重量百分比组分组成：
丙二醇甲醚8％；
甲苯6％；
乙酸乙酯34％；
SU1690树脂20％；
SU1750树脂32％；
所述B组分由如下重量百分比组成：
184引发剂36％；
TPO引发剂2.4％；
流平剂2.4％；
消泡剂1.2％；
醋酸正丁酯58％。
在上述的大灯翻新修复剂中，所述流平剂有如下重量百分比组分组成：
100#硅油1％；
二甲苯99％。
在上述的大灯翻新修复剂中，所述A组分的配置方法为：
将SU1690树脂、SU1750树脂缓慢加入到溶剂中，直至完全溶解。
在上述的大灯翻新修复剂中，制备方法为：
在使用之前，将A组分、1005TF树脂加入到溶剂中，搅拌分散均匀，再加入B组分，即可用于加工。
与现有技术相比，本发明的有益效果是：
采用本发明的修复剂修复大灯后能够有效改善车灯的透光率、光泽度，在耐高温、附着力、硬度方面达到了较好的效果。
附图说明
图1和图2为采用本发明的实施例1的修复剂修复前后的效果图。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
一种大灯翻新修复剂，本修复剂适用于亚克力、PBT、PA、PC和塑料、有机玻璃汽车大灯等，在喷涂前参考CN201110020806.3所述的针对龟裂、发黄的大灯进行前处理，本案的修复剂只需喷涂一次即可。
本实施例的修复剂的制备方法如下：
在使用之前，将A组分、1005TF树脂加入到溶剂中，搅拌分散均匀，再加入B组分，即可用于施工。
配方参考表1。
表1配方表
实施例2
大体同实施例1，不同的地方在于，配方表如下表2。
表2配方表
实施例3
大体同实施例1，不同的地方在于，配方表如下表3。
表3配方表
实施例4
大体同实施例1，不同的地方在于，配方表如下表4。
表4配方表
实施例5
大体同实施例1，不同的地方在于，配方表如下表5。
表5配方表
对比例1
大体同实施例1，不同的地方在于，配方表如下表6。
表6配方表
对比例2
大体同实施例1，不同的地方在于，配方表如下表7。
表7配方表
对比例3
大体同实施例1，不同的地方在于，配方表如下表8。
表8配方表
性能测试
本发明涉及的测试项目包括：耐温性、膜层透光率、硬度、附着力、光泽度。
1、附着力：按照ASTM D 3359-2002《胶带法测定附着力》进行测定；
2、硬度：按照GB/T 6739-2006《色漆和清漆铅笔法测定漆膜硬度》进行测试；
3、150℃漆膜耐高温测试：GB/T 1735-89《漆膜耐热性测定法》。
4、透光率：GB/T2566-2010《低煤阶煤的透光率测试方法》
5、光泽度：GB/T450-2008《纸及纸板试样的采取及试样纵横、正反面的测定》或光泽度测试仪。
测试结果可参考表8。
表9
| 附着力 | 硬度 | 耐高温测试(h) | 透光率(％) | 光泽度(60℃) | |
| 实施例1 | 5B | 2H | 500 | 90％ | 105 |
| 实施例3 | 5B | 3H | 500 | 89％ | 103 |
| 实施例5 | 5B | 2H | 500 | 90％ | 103 |
| 对比例1 | 5B | 2H | 400 | 85％ | 100 |
| 对比例2 | 5B | 2H | 400 | 80％ | 99 |
| 对比例3 | 5B | 2H | 450 | 85％ | 97 |
通过上述测试可以得到如下结论：
(1).1005TF树脂、SU1690树脂、SU1750树脂缺一不可，高低官能度的脂肪族聚氨酯丙烯酸酯在交联剂的作用下可以保持较优的硬度、附着力、透光率、光泽度。
(2).1005TF树脂的用量应该控制在19-20％；过于低于该用量，在透光率和光泽度方面将表现出劣化趋势。
(3).采用复合光引发剂对于透光率、光泽度、耐高温性能有积极作用，其能够配合1005TF树脂改善相关性能。
图1和图2为采用本发明的实施例1的修复剂修复前后的效果图。
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。不应将权利要求中的任何附图标记视为限制所涉及的权利要求。
Claims (5)
1.一种大灯翻新修复剂，其特征在于，其如下重量百分比组分组成：
A组分55-65％；
1005TF树脂19-20％；
B组分8-12％；
有机溶剂余量；
其中，所述A组分由如下重量百分比组分组成：
丙二醇甲醚7-9％；
甲苯5-7％；
乙酸乙酯32-36％；
SU1690树脂18-22％；
SU1750树脂30-34％；
所述B组分由如下重量百分比组成：
184引发剂34-38％；
TPO引发剂2-2.8％；
流平剂2.2-2.6％；
消泡剂1-1.4％；
醋酸正丁酯56-60％。
2.根据权利要求1所述的大灯翻新修复剂，其特征在于，其如下重量百分比组分组成：
A组分60％；
1005TF树脂19.2％；
B组分10.8％；
有机溶剂余量；
其中，所述A组分由如下重量百分比组分组成：
丙二醇甲醚8％；
甲苯6％；
乙酸乙酯34％；
SU1690树脂20％；
SU1750树脂32％；
所述B组分由如下重量百分比组成：
184引发剂36％；
TPO引发剂2.4％；
流平剂2.4％；
消泡剂1.2％；
醋酸正丁酯58％。
3.根据权利要求1或2所述的大灯翻新修复剂，其特征在于，所述流平剂有如下重量百分比组分组成：
100#硅油1％；
二甲苯99％。
4.根据根据权利要求1或2所述的大灯翻新修复剂，其特征在于，所述A组分的配置方法为：
将SU1690树脂、SU1750树脂缓慢加入到溶剂中，直至完全溶解。
5.根据根据根据权利要求1或2所述的大灯翻新修复剂，其特征在于，制备方法为：
在使用之前，将A组分、1005TF树脂加入到溶剂中，搅拌分散均匀，再加入B组分，即可用于加工。