CN1144786A - 铬渣镁橄榄石耐火材料及制备方法 - Google Patents

铬渣镁橄榄石耐火材料及制备方法 Download PDF

Info

Publication number
CN1144786A
CN1144786A CN 96115173 CN96115173A CN1144786A CN 1144786 A CN1144786 A CN 1144786A CN 96115173 CN96115173 CN 96115173 CN 96115173 A CN96115173 A CN 96115173A CN 1144786 A CN1144786 A CN 1144786A
Authority
CN
China
Prior art keywords
refractory
brick
temp
preparation
refractory material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 96115173
Other languages
English (en)
Inventor
秦凤久
于青
田青
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Northeastern University China
Original Assignee
Northeastern University China
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Northeastern University China filed Critical Northeastern University China
Priority to CN 96115173 priority Critical patent/CN1144786A/zh
Publication of CN1144786A publication Critical patent/CN1144786A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种用冶金炉渣制备的耐火材料及其制造方法。其化学组分含量为45％<Mg<50％，15％<Al2O3<20％，0.5％<Cr2O3<3％，25％<SiO2<30％，2％<CaO<6％。制备方法为：取高碳铬铁渣70-80％，加入高温结合剂——镁砂20-30％，按常规生产不烧耐火砖或其它耐火制品的工艺，生产不烧砖或其它耐火制品，在1450-1500℃的温度下焙烧，生产烧结的耐火砖或其它耐火制品。本发明的耐火材料具有高耐火度、荷重软化温度、抗热震性和抗含FeO等碱性渣的侵蚀能力，是适用于冶金、化工领域高温反应炉耐火砌体的良好耐火材料。

Description

铬渣镁橄榄石耐火材料及制备方法
本发明涉及一种用冶金炉渣制备的耐火材料及其制造方法。
目前，冶金炉渣——高碳铬铁渣在大多情况下被做为废渣弃掉，要花运输费和占地费，只有少数做水渣，以低廉的价格卖给水泥厂做为生产水泥的添加料，这虽然使高碳铬铁渣得到了利用，但需要消耗水资源。
本发明的目的在于提供一种利用高碳铬铁渣生产具有高耐火度、荷重软化温度、抗热震性和抗含FeO等碱性渣侵蚀能力的铬渣镁橄榄耐火材料及其生产方法。
本发明的耐火材料其化学组分含量为：45％＜Mg＜50％，15％＜Al2O3＜20％，0.5％＜Cr2O3＜3％，25％＜SiO2＜30％，2％＜CaO＜6％。
本发明的制备铬渣镁橄榄耐火材料通过如下方法制备：
取高碳铬铁渣70-80％，加入高温结合剂-镁砂20-30％，按常规生产不烧耐火砖或其它耐火制品的工艺，生产不烧砖或其它耐火制品；采用烧结砖的成形工艺，在1450-1500℃的温度下焙烧，生产烧结的耐火砖或其它耐火制品。
本发明的耐火材料具有高耐火度、荷重软化温度、抗热震性和抗含FeO等碱性渣的侵蚀能力，是适用于冶金、化工领域高温反应炉耐火砌体的良好耐火材料。本发明的制造耐火材料的方法使废弃的高碳铬铁炉渣得到了最大限度地利用，通过添加高温结合剂的方法，把高碳铬铁渣转化成高性能的，以镁橄榄石为主晶相的耐火材料，把炉渣的经济价值提高了几十倍。
下面对本发明的耐火材料的生产制备方法作进一步的描述：
实施例一：
取高碳铬铁渣70％加入高温反应结合-镁砂30％，按常规生产不烧耐火砖的方法，可得到不烧镁橄榄石耐火砖。
实施例二：采用烧结砖的成型工艺，其原料的组分含量及烧结温度如下表所示，生产烧结的镁橄榄石耐火砖。
实施例序号 高碳铬铁渣 镁砂 烧结温度℃
     1      70     30     1450
2 75 25 1450
     3      80     20     1450
     4      70     30     1470
     5      75     25     1470
     6      80     20     1470
     7      70     30     1500
     8      75     25     1500
     9      80     20     1500

Claims (2)

1、铬渣镁橄榄石耐火材料，其化学组分及含量为45％＜Mg＜50％，15％＜Al2O3＜20％，0.5％＜Cr2O3＜3％，25％＜SiO2＜30％，2％＜CaO＜6％。
2、如权利要求1所述的耐火材料的生产方法，取高碳铬铁渣70-80％，加入高温结合剂-镁砂20-30％，按常规生产不烧耐火砖或其它耐火制品的工艺，生产不烧砖或其它耐火制品；采用烧结砖的成形工艺，在1450-1500℃的温度下焙烧，生产烧结的耐火砖或其它耐火制品。
CN 96115173 1996-03-26 1996-03-26 铬渣镁橄榄石耐火材料及制备方法 Pending CN1144786A (zh)