CN114456695A - 高耐水聚合物水泥防水涂料及其制备工艺 - Google Patents
高耐水聚合物水泥防水涂料及其制备工艺 Download PDFInfo
- Publication number
- CN114456695A CN114456695A CN202210057633.0A CN202210057633A CN114456695A CN 114456695 A CN114456695 A CN 114456695A CN 202210057633 A CN202210057633 A CN 202210057633A CN 114456695 A CN114456695 A CN 114456695A
- Authority
- CN
- China
- Prior art keywords
- parts
- waterproof coating
- polymer cement
- cement waterproof
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了高耐水聚合物水泥防水涂料及其制备工艺，由以下重量份数的原料制成：水性聚氨酯树脂150‑220份、丙烯酸酯共聚物50‑150份、氯丁胶乳50‑80份、丁苯胶乳60‑75份、丙烯酸酯乳液25‑35份、浓氨水5‑10份、分散剂3‑8份、消泡剂4‑6份和防腐剂2‑6份，其具体重量份数如下：水性聚氨酯树脂200份、丙烯酸酯共聚物100份、氯丁胶乳60份、丁苯胶乳65份、丙烯酸酯乳液30份、浓氨水8份、分散剂5份、消泡剂4.5份和防腐剂4份。本发明通过在防水涂料的制备工艺中添加氯丁胶乳和丁苯胶乳可延长涂料的防水性能，同时抗变形和耐磨，气密性和抗水性好，总粘合力大，可用于饮水池施工使用，施工安全，简单，还能用于长期浸水的环境。
Description
技术领域
本发明涉及防水涂料制备技术领域，具体为高耐水聚合物水泥防水涂料及其制备工艺。
背景技术
聚合物水泥防水涂料是以聚丙烯酸酯乳液、乙烯-醋酸乙烯酯共聚乳液等聚合物乳液与各种添加剂组成的有机液料，和水泥、石英砂、轻重质碳酸钙等无机填料及各种添加剂所组成的无机粉料通过合理配比、复合制成的一种双组份、水性建筑防水涂料，但是目前的水泥防水涂料长期使用时耐水性较差，在墙面使用时会产生变形，且不耐磨，气密性和抗水性差，无法长期用于浸水的环境，性能指标达不到使用标准。
发明内容
本发明的目的在于提供高耐水聚合物水泥防水涂料及其制备工艺，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：高耐水聚合物水泥防水涂料，由以下重量份数的原料制成：水性聚氨酯树脂150-220份、丙烯酸酯共聚物50-150份、氯丁胶乳50-80份、丁苯胶乳60-75份、丙烯酸酯乳液25-35份、浓氨水5-10份、分散剂3-8份、消泡剂4-6份和防腐剂2-6份。
优选的，所述其具体重量份数如下：水性聚氨酯树脂200份、丙烯酸酯共聚物100份、氯丁胶乳60份、丁苯胶乳65份、丙烯酸酯乳液30份、浓氨水8份、分散剂5份、消泡剂4.5份和防腐剂4份。
优选的，所述水性聚氨酯树脂具有多个—NCO基，有足够的官能度，可与含活性的氢原子基团的化合物或聚合物在常温下反应生成一定数量的胺酯键的聚合物。
优选的，所述水性聚氨酯树脂为聚氨酯水溶液、聚氨酯水分散体和聚氨酯乳液中的一种或多种。
优选的，所述消泡剂为聚氧乙烯聚氧丙烯季戊四醇醚、聚氧乙烯聚氧丙醇胺醚、聚氧丙烯甘油醚和聚氧丙烯聚氧乙烯甘油醚中的其中一种。
优选的，所述浓氨水的浓度为28%，所述浓氨水与水的配合比为1：0.9。
优选的，所述防腐剂为取代芳烃类、有机溴类、有机胺类、哌三嗪类中的一种或多种组合。
优选的，所述分散剂为有聚羧酸盐，聚（甲基）丙烯酸衍生物和顺丁烯二酸酐共聚物中的一种或多种。
优选的，所述丙烯酸酯乳液以异丙醇作反应溶剂，n（丙烯酸）：n（GTA）=1.1：1.0，催化剂用量为GTA质量的5%，反应时间6h，反应温度70℃，该条件下产物酯化率78%，产物收率86%。
优选的，高耐水聚合物水泥防水涂料制备工艺，其制备工艺如下：
A、将水性聚氨酯树脂200份、丙烯酸酯共聚物100份、氯丁胶乳60份、丁苯胶乳65份、丙烯酸酯乳液30份加入至搅拌釜中进行搅拌，搅拌完成之后，对搅拌釜进行升温加热，温度控制在50℃-80℃之间；
B、将上述混合得到的涂料倒入反应釜中，然后加入浓氨水8份、分散剂5份和消泡剂4.5份，并持续搅拌混合，时间为15min；
C、最后对反应釜进行降温处理，使反应釜内部的温度在20℃-30℃之间，再次加入防腐剂4份，并继续进行搅拌，十分钟后使搅拌釜保持恒温，即可完成防水涂料的制备。
与现有技术相比，本发明的有益效果如下：
1、本发明通过在防水涂料的制备工艺中添加氯丁胶乳和丁苯胶乳可延长涂料的防水性能，同时抗变形和耐磨，气密性和抗水性好，总粘合力大，可用于饮水池施工使用，施工安全，简单，还能用于长期浸水的环境，同时具备优异的性能指标、耐候性和耐水性。
具体实施方式
下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
为实现上述目的，本发明提供如下技术方案：高耐水聚合物水泥防水涂料，由以下重量份数的原料制成：水性聚氨酯树脂150-220份、丙烯酸酯共聚物50-150份、氯丁胶乳50-80份、丁苯胶乳60-75份、丙烯酸酯乳液25-35份、浓氨水5-10份、分散剂3-8份、消泡剂4-6份和防腐剂2-6份。
实施例一：
高耐水聚合物水泥防水涂料制备工艺，其制备工艺如下：
A、将水性聚氨酯树脂200份、丙烯酸酯共聚物100份、氯丁胶乳60份、丁苯胶乳65份、丙烯酸酯乳液30份加入至搅拌釜中进行搅拌，搅拌完成之后，对搅拌釜进行升温加热，温度控制在50℃-80℃之间；
B、将上述混合得到的涂料倒入反应釜中，然后加入浓氨水8份、分散剂5份和消泡剂4.5份，并持续搅拌混合，时间为15min；
C、最后对反应釜进行降温处理，使反应釜内部的温度在20℃-30℃之间，再次加入防腐剂4份，并继续进行搅拌，十分钟后使搅拌釜保持恒温，即可完成防水涂料的制备。
实施例二：
高耐水聚合物水泥防水涂料制备工艺，其制备工艺如下：
A、将水性聚氨酯树脂180份、丙烯酸酯共聚物80份、氯丁胶乳55份、丁苯胶乳60份、丙烯酸酯乳液25份加入至搅拌釜中进行搅拌，搅拌完成之后，对搅拌釜进行升温加热，温度控制在50℃-80℃之间；
B、将上述混合得到的涂料倒入反应釜中，然后加入浓氨水6份、分散剂4份和消泡剂4份，并持续搅拌混合，时间为15min；
C、最后对反应釜进行降温处理，使反应釜内部的温度在20℃-30℃之间，再次加入防腐剂3份，并继续进行搅拌，十分钟后使搅拌釜保持恒温，即可完成防水涂料的制备。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (10)
1.高耐水聚合物水泥防水涂料，其特征在于：由以下重量份数的原料制成：水性聚氨酯树脂150-220份、丙烯酸酯共聚物50-150份、氯丁胶乳50-80份、丁苯胶乳60-75份、丙烯酸酯乳液25-35份、浓氨水5-10份、分散剂3-8份、消泡剂4-6份和防腐剂2-6份。
2.根据权利要求1所述的高耐水聚合物水泥防水涂料，其特征在于：所述其具体重量份数如下：水性聚氨酯树脂200份、丙烯酸酯共聚物100份、氯丁胶乳60份、丁苯胶乳65份、丙烯酸酯乳液30份、浓氨水8份、分散剂5份、消泡剂4.5份和防腐剂4份。
3.根据权利要求1所述的高耐水聚合物水泥防水涂料，其特征在于：所述水性聚氨酯树脂具有多个—NCO基，有足够的官能度，可与含活性的氢原子基团的化合物或聚合物在常温下反应生成一定数量的胺酯键的聚合物。
4.根据权利要求1所述的高耐水聚合物水泥防水涂料，其特征在于：所述水性聚氨酯树脂为聚氨酯水溶液、聚氨酯水分散体和聚氨酯乳液中的一种或多种。
5.根据权利要求1所述的高耐水聚合物水泥防水涂料，其特征在于：所述消泡剂为聚氧乙烯聚氧丙烯季戊四醇醚、聚氧乙烯聚氧丙醇胺醚、聚氧丙烯甘油醚和聚氧丙烯聚氧乙烯甘油醚中的其中一种。
6.根据权利要求1所述的高耐水聚合物水泥防水涂料，其特征在于：所述浓氨水的浓度为28%，所述浓氨水与水的配合比为1：0.9。
7.根据权利要求1所述的高耐水聚合物水泥防水涂料，其特征在于：所述防腐剂为取代芳烃类、有机溴类、有机胺类、哌三嗪类中的一种或多种组合。
8.根据权利要求1所述的高耐水聚合物水泥防水涂料，其特征在于：所述分散剂为有聚羧酸盐，聚（甲基）丙烯酸衍生物和顺丁烯二酸酐共聚物中的一种或多种。
9.根据权利要求1所述的高耐水聚合物水泥防水涂料，其特征在于：所述丙烯酸酯乳液以异丙醇作反应溶剂，n（丙烯酸）：n（GTA）=1.1：1.0，催化剂用量为GTA质量的5%，反应时间6h，反应温度70℃，该条件下产物酯化率78%，产物收率86%。
10.高耐水聚合物水泥防水涂料制备工艺，其特征在于：其制备工艺如下：
A、将水性聚氨酯树脂200份、丙烯酸酯共聚物100份、氯丁胶乳60份、丁苯胶乳65份、丙烯酸酯乳液30份加入至搅拌釜中进行搅拌，搅拌完成之后，对搅拌釜进行升温加热，温度控制在50℃-80℃之间；
B、将上述混合得到的涂料倒入反应釜中，然后加入浓氨水8份、分散剂5份和消泡剂4.5份，并持续搅拌混合，时间为15min；
C、最后对反应釜进行降温处理，使反应釜内部的温度在20℃-30℃之间，再次加入防腐剂4份，并继续进行搅拌，十分钟后使搅拌釜保持恒温，即可完成防水涂料的制备。