CN114456662A - 一种纳米改性橡胶防水涂料及其生产工艺 - Google Patents
一种纳米改性橡胶防水涂料及其生产工艺 Download PDFInfo
- Publication number
- CN114456662A CN114456662A CN202210180312.XA CN202210180312A CN114456662A CN 114456662 A CN114456662 A CN 114456662A CN 202210180312 A CN202210180312 A CN 202210180312A CN 114456662 A CN114456662 A CN 114456662A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- rubber waterproof
- mesh
- nano
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种纳米改性橡胶防水涂料，以质量份数计，包括增强剂10‑15份、改性丙烯酸乳液300‑500份、有机硅50‑70份、阻聚剂0.5‑1.5份、消泡剂5‑10份、分散剂2‑5份、湿润剂0.5‑1.5份、PH值调节剂1‑2份、400目重钙200‑300份、800目重钙100‑200份、1250目重钙100‑200份、防腐剂0.5‑1.5份、乳化沥青250‑350份、增稠剂0.5‑1.5份和去离子水2‑7份。该防水涂料具有优异的防水性能和附着性能，能够用于粘结防水卷材的搭接部分，充分保证防水卷材的防水性能。
Description
技术领域
本发明涉及了一种防水涂料，具体的说，涉及了一种纳米改性橡胶防水涂料及其生产工艺。
背景技术
防水卷材通常包括无纺布基材和设置于无纺布基材下侧面的柔性防水涂层，为了保证建筑的防水性能，通常需要铺设防水卷材，但是，传统的防水卷材施工对基层的要求较高，对于外形复杂的基层通常需要多块防水卷材进行搭接，而防水卷材之间相互搭接处单纯依靠自带的柔性防水涂层，很难进行完全密封，容易存在漏水隐患，但是，目前国内尚少与防水卷材相匹配的长效粘结剂，普通的粘结剂由于受到粘结环境和粘结材料自身等因素的限制往往容易失去粘结功能，无法充分粘结防水卷材。
为了解决以上存在的问题，人们一直在寻求一种理想的技术解决方案。
发明内容
本发明的目的是针对现有技术的不足，从而提供一种纳米改性橡胶防水涂料及其生产工艺。
为了实现上述目的，本发明所采用的技术方案是：
一种纳米改性橡胶防水涂料，以质量份数计，包括增强剂10-15份、改性丙烯酸乳液300-500份、有机硅50-70份、阻聚剂0.5-1.5份、消泡剂5-10份、分散剂2-5份、湿润剂0.5-1.5份、PH值调节剂1-2份、400目重钙200-300份、800目重钙100-200份、1250目重钙100-200份、防腐剂0.5-1.5份、乳化沥青250-350份、增稠剂0.5-1.5份和去离子水2-7份。
基于上述，以质量份数计，包括增强剂12份、改性丙烯酸乳液400份、有机硅60份、阻聚剂1份、消泡剂8份、分散剂3份、湿润剂1份、PH值调节剂1.1份、400目重钙250份、800目重钙150份、1250目重钙150份、防腐剂1份、乳化沥青300份、增稠剂1份和去离子水5份。
基于上述，所述增强剂包括质量比为1:2:1:1的滑石粉、云母粉、硅藻土和高岭土，所述增强剂的粒径为100-150nm。
基于上述，以质量份数计，所述改性丙烯酸乳液主要包括去离子水50-60份、聚丙烯酸酯聚合物25-35份和固化剂1-3份；其中，所述聚丙烯酸酯聚合物为具备碳氧双键的聚丙烯酸酯，所述固化剂可以为己二酸二酰肼。
基于上述，所述有机硅为含氢硅油、含氢硅树脂或含氢硅橡胶。
基于上述，所述改性丙烯酸乳液为低温交联乳液。
基于上述，所述的纳米改性橡胶防水涂料为弱酸性涂料。
基于上述，一种所述纳米改性橡胶防水涂料的生产工艺，其包括以下步骤：将乳化沥青、400目重钙、800目重钙、1250目重钙混合均匀，依次加入包括增强剂、改性丙烯酸乳液、消泡剂、分散剂、湿润剂、防腐剂、增稠剂、去离子水混合均匀，然后加入PH值调节剂调节为弱酸性，最后加入阻聚剂和有机硅。
基于上述，先将阻聚剂和有机硅混合后再和其他成分混合。
本发明相对现有技术具有突出的实质性特点和显著进步，具体的说，本发明提供一种纳米改性橡胶防水涂料，该防水涂料具有优异的防水性能和附着性能，能够用于粘结防水卷材的搭接部分，充分保证防水卷材的防水性能。具体的，该防水涂料主要由乳化沥青、改性丙烯酸酯乳液、有机硅、重钙、增强剂和相关助剂构成，防水涂料整体呈弱酸性，避免发生脱氢反应，成膜过程中，有机硅和双键在紫外线作用下发生硅氢加成，改性丙烯酸酯乳液也进行交联反应，进而提高涂层的耐磨性、耐水性和附着力等涂层性能；另外，通过采用不同粒度的重钙和增强剂提高其对于基材的渗透性。同时，本发明还提供该防水涂料的制备方法，该方法简单、易操作，便于工业生产。
具体实施方式
下面通过具体实施方式，对本发明的技术方案做进一步的详细描述。
一种纳米改性橡胶防水涂料，以质量份数计，包括增强剂10-15份、改性丙烯酸乳液300-500份、有机硅50-70份、阻聚剂0.5-1.5份、消泡剂5-10份、分散剂2-5份、湿润剂0.5-1.5份、PH值调节剂1-2份、400目重钙200-300份、800目重钙100-200份、1250目重钙100-200份、防腐剂0.5-1.5份、乳化沥青250-350份、增稠剂0.5-1.5份和去离子水2-7份。
具体的，本实施例中，一种纳米改性橡胶防水涂料，pH值约为6.3，以质量份数计，包括增强剂12份、改性丙烯酸乳液400份、有机硅60份、阻聚剂1份、消泡剂8份、分散剂3份、湿润剂1份、PH值调节剂1.1份、400目重钙250份、800目重钙150份、1250目重钙150份、防腐剂1份、乳化沥青300份、催化剂、增稠剂1份和去离子水5份。
所述增强剂包括质量比为1:2:1:1的滑石粉、云母粉、硅藻土和高岭土，所述增强剂的粒径为100-150nm，平均粒径为137nm。以质量份数计，所述改性丙烯酸乳液主要包括去离子水50-60份、聚丙烯酸酯聚合物32份和固化剂2份；其中，所述聚丙烯酸酯聚合物为具备碳氧双键的聚丙烯酸酯，所述固化剂为己二酸二酰肼。具体的，所述改性丙烯酸乳液中聚丙烯酸酯聚合物的用量可以直接采用未添加固化剂的改性丙烯酸乳液，通过测量固含量进行调整，需要说明的是，该成分为主要成分，实际改性丙烯酸乳液可能含有微量的未反应单体；所述有机硅为含氢硅油、含氢硅树脂或含氢硅橡胶；催化剂的用量可以为有机硅的30-40ppm之间的任意值，本实施例为30ppm，催化剂可以采用Pt类催化剂，例如：speier催化剂、karstedt催化剂；各种增稠剂、防腐剂等助剂可以根据需求购买市售常规助剂。
一种所述纳米改性橡胶防水涂料的生产工艺，其包括以下步骤：将乳化沥青、400目重钙、800目重钙、1250目重钙混合均匀，依次加入包括增强剂、改性丙烯酸乳液、消泡剂、分散剂、湿润剂、防腐剂、增稠剂、去离子水混合均匀，然后加入PH值调节剂调节为弱酸性，最后加入阻聚剂和有机硅，混合均匀，得到成品。具体的，该防水涂料在使用过程中，可以采用喷涂的方式施工，干燥可以采用自然风干或是加热结合紫外线照射。
对本实施例得到防水涂料进行性能测试，其性能满足JC/T864-2008要求，部分测试结果参见表1.
表1部分测试结果
| 不透水性(0.3Mpa，30min) | 不透水 |
| 低温柔性，绕Φ10mm棒弯180° | -10℃无裂纹 |
| 断裂伸长率，％≥ | 300 |
| 拉伸强度，Mpa≥ | 1 |
在其他的实施例中，一种纳米改性橡胶防水涂料，以质量份数计，包括增强剂10份、改性丙烯酸乳液300份、有机硅50份、阻聚剂0.5份、消泡剂5份、分散剂2份、湿润剂0.5份、PH值调节剂1份、400目重钙200份、800目重钙100份、1250目重钙100份、防腐剂0.5份、乳化沥青250份、增稠剂0.5份和去离子水2份；改性丙烯酸乳液可以采用其他的室温自交联固化体系；所述有机硅可以采用含氢硅树脂；或是一种纳米改性橡胶防水涂料，以质量份数计，包括增强剂15份、改性丙烯酸乳液500份、有机硅70份、阻聚剂1.5份、消泡剂10份、分散剂5份、湿润剂1.5份、PH值调节剂2份、400目重钙300份、800目重钙200份、1250目重钙200份、防腐剂1.5份、乳化沥青350份、增稠剂1.5份和去离子水7份；所述有机硅可以采用氢硅橡胶。
最后应当说明的是：以上实施例仅用以说明本发明的技术方案而非对其限制；尽管参照较佳实施例对本发明进行了详细的说明，所属领域的普通技术人员应当理解：依然可以对本发明的具体实施方式进行修改或者对部分技术特征进行等同替换；而不脱离本发明技术方案的精神，其均应涵盖在本发明请求保护的技术方案范围当中。
Claims (9)
1.一种纳米改性橡胶防水涂料，其特征在于：以质量份数计，包括增强剂10-15份、改性丙烯酸乳液300-500份、有机硅50-70份、阻聚剂0.5-1.5份、消泡剂5-10份、分散剂2-5份、湿润剂0.5-1.5份、PH值调节剂1-2份、400目重钙200-300份、800目重钙100-200份、1250目重钙100-200份、防腐剂0.5-1.5份、乳化沥青250-350份、增稠剂0.5-1.5份和去离子水2-7份。
2.根据权利要求1所述的纳米改性橡胶防水涂料，其特征在于：以质量份数计，包括增强剂12份、改性丙烯酸乳液400份、有机硅60份、阻聚剂1份、消泡剂8份、分散剂3份、湿润剂1份、PH值调节剂1.1份、400目重钙250份、800目重钙150份、1250目重钙150份、防腐剂1份、乳化沥青300份、增稠剂1份和去离子水5份。
3.根据权利要求1或2所述的纳米改性橡胶防水涂料，其特征在于：所述增强剂包括质量比为1:2:1:1的滑石粉、云母粉、硅藻土和高岭土，所述增强剂的粒径为100-150nm。
4.根据权利要求3所述的纳米改性橡胶防水涂料，其特征在于：以质量份数计，所述改性丙烯酸乳液主要包括去离子水50-60份、聚丙烯酸酯聚合物25-35份和固化剂1-3份；其中，所述聚丙烯酸酯聚合物为具备碳氧双键的聚丙烯酸酯。
5.根据权利要求1或2所述的纳米改性橡胶防水涂料，其特征在于：所述有机硅为含氢硅油、含氢硅树脂或含氢硅橡胶。
6.根据权利要求1或2所述的纳米改性橡胶防水涂料，其特征在于：所述改性丙烯酸乳液为低温交联乳液。
7.根据权利要求1或2所述的纳米改性橡胶防水涂料，其特征在于：为弱酸性涂料。
8.一种权利要求1—7任一项所述纳米改性橡胶防水涂料的生产工艺，其包括以下步骤：将乳化沥青、400目重钙、800目重钙、1250目重钙混合均匀，依次加入包括增强剂、改性丙烯酸乳液、消泡剂、分散剂、湿润剂、防腐剂、增稠剂、去离子水混合均匀，然后加入PH值调节剂调节为弱酸性，最后加入阻聚剂和有机硅。
9.根据权利要求8所述的生产工艺，其特征在于：先将阻聚剂和有机硅混合后再和其他成分混合。