CN114292626B - 一种有机无氯环保液态融雪剂 - Google Patents
一种有机无氯环保液态融雪剂 Download PDFInfo
- Publication number
- CN114292626B CN114292626B CN202210056371.6A CN202210056371A CN114292626B CN 114292626 B CN114292626 B CN 114292626B CN 202210056371 A CN202210056371 A CN 202210056371A CN 114292626 B CN114292626 B CN 114292626B
- Authority
- CN
- China
- Prior art keywords
- snow
- melting agent
- melting
- ammonium nitrate
- industrial molasses
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开一种有机无氯环保液态融雪剂，按重量百分比计，包括以下组分：甲酸钾40％‑45％、硝酸铵钙7％‑13％、工业糖蜜1％‑8％和水39％‑46％，所述融雪剂的pH为6‑10。本发明将甲酸钾与硝酸铵钙、工业糖蜜及水经过搅拌、混合、溶解可制备成具有发热量大，融雪速度快，对植物的毒性小、无异味、且不会污染水体的融雪剂，适合道路、桥梁、机场融雪。
Description
技术领域
本发明涉及融雪剂技术领域，尤其是涉及一种有机无氯环保液态融雪剂。
背景技术
随着社会经济的迅速发展和人们认识水平的不断提高，单靠人工和机械除雪已无法适应现代交通发展的要求，使用化学融雪剂融雪除雪已逐步被人们所接受。以氯化钠、氯化钙及其复配物为主的含氯盐化学融雪剂开始被人们所使用。然而，尽管这种化学融雪剂达到了除雪目的，但却给道路、绿地、桥梁，特别是给大江河流等水系带来了极大损害，对周围环境造成了严重污染。据有关专家分析，含氯粗盐(包括氯化钠和氯化钙)中的氯离子才是真正破坏环保的凶手：其一，所有含氯盐均对基础设施如钢筋混凝土结构、路桥、地下管网、金属结构等具有严重腐蚀作用；其二，氯化钠对植物和环境水资源的影响大于其他含氯盐。因此，选用氯化镁、氯化钙作为融雪剂，对环保影响略小于氯化钠，但并未改变其具有严重腐蚀性的根本缺陷。国外以含氯盐为基础添加适量阻锈剂、缓蚀剂的作法，是为减少氯离子对钢材(特别是混凝土中钢筋)的腐蚀作用，但其效能是很有限的，仅减少对钢材的腐蚀作用却不能缓解含氯盐类融雪剂对混凝土冻融破坏，特别是对环境植物的破坏，不但没有起到缓解作用，由于多种离子存在的原因，还增加了环境的污染。
中国专利CN02149204.2公开了一种用于道路、桥梁雪后融雪的融雪剂，该融雪剂包括以下组分，其重量百分含量为：氯化钙50-95.5％，尿素2-47.5％，重过磷酸钙1.5-5％，还可以包括重量百分含量为0.5-2％的硫脲及重量百分含量为0.5-2％的葡萄糖酸钠。该融雪剂的使用温度为-5℃至-40℃，融雪速度快，对道路、桥梁的腐蚀性低，对植物的毒性小。但是，其添加的尿素、硫脲分解为氨，易使水体富营养化。
中国专利CN110845991A公开了一种生态环保融雪剂，该融雪剂包括以下组分，其重量百分含量为：植物基腐殖酸与钙盐的用量比为30～40份：30～50份；植物基腐殖酸与钾盐的用量比为30～40份：10～20份；植物基腐殖酸与缓蚀剂的用量比为30～40份：5～10份。该融雪剂腐蚀性小，自降解，能促进植物生长，环境友好。但是腐殖酸本身具有的气味和颜色比较重不利于城市道路大规模使用。
因此，提供一种对植物的毒性小、无异味且环境友好的环保型融雪剂具有重要的意义。
发明内容
本发明旨在解决现有技术中融雪剂对植物的毒性大、有异味、污染水体等技术问题，提供一种新型的有机无氯环保液态融雪剂。
本发明构思如下：甲酸钾结晶物或水合物甲酸钾冰点低至-55℃，发明人偶然发现，将甲酸钾与硝酸铵钙、工业糖蜜及水经过搅拌、混合、溶解可制备成具有发热量大，融雪速度快，对植物的毒性小、无异味、且不会污染水体的融雪剂，适合道路、桥梁、机场融雪。
为了实现本发明目的，第一方面，本发明提供的有机无氯环保液态融雪剂，按重量百分比计，包括以下组分：甲酸钾40％-45％、硝酸铵钙7％-13％、工业糖蜜1％-8％和水39％-46％。所述融雪剂的pH为6-10。
本发明中，所述工业糖蜜来自制糖工业中将甘蔗加工成白砂糖后产生的副产物母液。在本发明的一些具体实施方式中，工业糖蜜的具体组成为：糖份25-28g/L、腐殖酸47-52g/L、氮18-25g/L、P2O5 1-5g/L、K2O 60-65g/L、游离氨基酸18-22g/L，pH值4-6。
本发明中，发明人经过试验发现硝酸铵钙与工业糖蜜的比例对于降低植物种子相对受害率发挥重要的作用。硝酸铵钙与工业糖蜜的质量比为1:(0.14-1)时，植物种子相对受害率更低，进一步优选为1:(0.2-0.3)，更优选为1:(0.2-0.21)。
本发明中，上述融雪剂中还包括柠檬酸钾。本发明通过加入柠檬酸钾，可提高植物种子相对受害率的稳定性。柠檬酸钾可直接加入本发明的融雪剂配方中，也可采用来自柠檬酸生产过程中产生的母液。在本发明的一些具体实施方式中，采用含有20％-25％柠檬酸钾的母液。进一步地，含柠檬酸钾的母液的加入量为融雪剂的0.1％-2％，优选为1％-1.2％。
本发明中，上述融雪剂中还包括缓蚀剂。本发明通过加入缓蚀剂可提高融雪剂对碳钢的缓蚀性能。需要说明的是，加入缓蚀剂后，为控制融雪剂的pH为6～10，优选pH为6.4～7.2，还可根据需要加入pH调节剂。进一步地，缓蚀剂可选自2-羟基膦酰基乙酸(HPAA)、羟基乙叉二膦酸四钠(HEDPNA4)、2-磷酸基-1,2,4-三羧酸丁烷(PBTCA)等中的至少一种。在本发明的一些优选实施方式中，缓蚀剂为2-羟基膦酰基乙酸、羟基乙叉二膦酸四钠、2-磷酸基-1,2,4-三羧酸丁烷按照1:(0.8-1):(0.8-1)质量比复配而成的混合物，且缓蚀剂的加入量为融雪剂重量百分数的0.01％-1％，进一步优选为0.2％-0.7％，更优选为0.6％-0.7％。
本发明还提供上述有机无氯环保液态融雪剂的制备方法，包括以下步骤：将各组分原料按比例混合，并搅拌使其充分溶解，混合均匀，经过过滤，得到有机无氯液态融雪剂。
本发明的融雪剂使用时，可使用专用融雪除冰喷洒车散布于积雪或结冰路面，也可适用于道路专用固定喷洒设备，连续喷洒于易积雪或结冰路段。
借由上述技术方案，本发明至少具有下列优点及有益效果：
(一)本发明将甲酸钾与硝酸铵钙、工业糖蜜及水经过搅拌、混合、溶解可制备成具有发热量大，融雪速度快，对植物的毒性小、无异味的融雪剂，适合道路、桥梁、机场融雪。
(二)本发明的融雪剂在融雪时缓慢放热，既能加快融雪速度，又能防止路面急剧收缩引起的损害；
(三)本发明的融雪剂的原料可选用工业废料、环境处理副产物，能够减轻环保压力，方便生活；
(四)本发明的融雪剂对道路、桥梁的腐蚀性极低，且不会引起水质污染。
具体实施方式
以下实施例用于说明本发明，但不用来限制本发明的范围。若未特别指明，实施例中所用的技术手段为本领域技术人员所熟知的常规手段，所用原料均为市售商品。
以下实施例中使用的工业糖蜜(糖蜜液)购自山东中阳生物科技有限公司，主要指标如下：糖份26.52g/L、密度1.29g/mL、锤度60g/L、腐殖酸49.1g/L、氮21.6g/L、磷(P2O5)3.3g/L、钾(K2O)62.9g/L、游离氨基酸20.11g/L，pH值4.98；使用含20％的柠檬酸钾的母液向体系中加入柠檬酸钾。
实施例1
本实施例的融雪剂组成如下：甲酸钾45kg、硝酸铵钙7kg、工业糖蜜1kg、含柠檬酸钾的母液1.1kg、HPAA 0.25kg、HEDPNA4 0.20kg、PBTCA 0.2kg、水45.25kg。
本实施例融雪剂的制备方法：将各组分原料按比例混合，并搅拌使其充分溶解，混合均匀，过滤，得到有机无氯液态融雪剂。
实施例2-3和对比例1-6相比，区别仅在于各组分含量不同，具体见表1，单位kg。
表1各实施例和对比例融雪剂组成
对比例7：中国专利CN108395878B说明书实施例1公开的融雪剂，测得该融雪剂的pH为8.3。
对比例8：中国专利CN108084965A公开的融雪剂，具体组成为：醋酸钾15％、甲酸钠10％、无水乙醇20％、水55％，测得该融雪剂的pH为7.6。
融雪剂性能试验1：
以氯化钠为对照，分别取实施例1-3对比例1-6的融雪剂，按照中国融雪剂检测方法GB/T23851-2017为检测标准，对各实施例融雪剂的腐蚀性、融雪速度等指标进行对比，检测结果如表2所示。
表2融雪剂各指标检测结果(以氯化钠为对比)
从表2可以看出，与对比例1-8相比，本发明实施例1-3所得融雪剂均具有很好的融雪性能，对碳钢、水泥腐蚀低，且对植物种子伤害小。
进一步将实施例3和对比例1-6的结果对比可知，随着硝酸铵钙含量的增加，冰点逐渐降低；并且硝酸铵钙与工业糖蜜的比例对于降低植物种子相对受害率发挥重要的作用，在实际使用过程中，为降低植物种子相对受害率，需严格控制二者的比例。
融雪剂性能试验2：
分别取实施例1-3和对比例1-6的融雪剂进行重金属含量检测，结果如表3所示。
表3不同融雪剂重金属含量测试结果
| 序号 | Pb(mg/kg)≤25 | Cd(mg/kg)≤5 | As(mg/kg)≤5 | Cr(mg/kg)≤15 | Hg(mg/kg)≤1 |
| 实施例1 | 11 | 0.01 | 0.02 | 2.64 | 0.01 |
| 实施例2 | 11 | 0.01 | 0.01 | 2.64 | 0.01 |
| 实施例3 | 9 | 0.01 | 0.01 | 2.65 | 0.01 |
| 对比例1 | 10 | 0.01 | 0.01 | 2.63 | 0.01 |
| 对比例2 | 9 | 0.01 | 0.01 | 2.64 | 0.01 |
| 对比例3 | 9 | 0.01 | 0.01 | 2.65 | 0.01 |
| 对比例4 | 9 | 0.01 | 0.01 | 2.64 | 0.01 |
| 对比例5 | 9 | 0.01 | 0.01 | 2.65 | 0.01 |
| 对比例6 | 9 | 0.01 | 0.02 | 2.64 | 0.01 |
从表3可以看出，本发明的融雪剂重金属含量符合标准要求，对植物的毒性小，不会引起水质污染。
虽然，上文中已经用一般性说明及具体实施方案对本发明作了详尽的描述，但在本发明基础上，可以对之做一些修改或改进，这对本领域技术人员而言是显而易见的。因此，在不偏离本发明精神的基础上所做的这些修改或改进，均属于本发明要求保护的范围。
Claims (5)
1.一种有机无氯环保液态融雪剂，其特征在于，按重量百分比计，包括以下组分：甲酸钾40％-45％、硝酸铵钙7％-13％、工业糖蜜1％-8％和水39％-46％；所述融雪剂的pH为6-10；
所述硝酸铵钙与工业糖蜜的质量比为1:(0.14-1)；
所述融雪剂还含有柠檬酸钾；采用含有20％-25％柠檬酸钾的母液向融雪剂中添加柠檬酸钾，且母液的加入量为融雪剂重量百分数的0.1％-2％；
所述融雪剂还含有缓蚀剂；
所述缓蚀剂为2-羟基膦酰基乙酸、羟基乙叉二膦酸四钠、2-磷酸基-1,2,4-三羧酸丁烷按照1:(0.8-1):(0.8-1)质量比复配而成的混合物，且缓蚀剂的加入量为融雪剂重量百分数的0.01％-1％。
2.根据权利要求1所述的融雪剂，其特征在于，所述工业糖蜜来自制糖工业中将甘蔗加工成白砂糖后产生的副产物母液。
3.根据权利要求2所述的融雪剂，其特征在于，所述工业糖蜜的具体组成为：糖份25-28g/L、腐殖酸47-52g/L、氮18-25g/L、P2O5 1-5g/L、K2O 60-65g/L、游离氨基酸18-22g/L，pH值4-6。
4.根据权利要求3所述的融雪剂，其特征在于，所述硝酸铵钙与工业糖蜜的质量比为1:(0.2-0.3)。
5.根据权利要求3所述的融雪剂，其特征在于，所述硝酸铵钙与工业糖蜜的质量比为1:(0.2-0.21)。