CN1142473A - 一种复合型轻质混凝土制品 - Google Patents

一种复合型轻质混凝土制品 Download PDF

Info

Publication number
CN1142473A
CN1142473A CN 95111715 CN95111715A CN1142473A CN 1142473 A CN1142473 A CN 1142473A CN 95111715 CN95111715 CN 95111715 CN 95111715 A CN95111715 A CN 95111715A CN 1142473 A CN1142473 A CN 1142473A
Authority
CN
China
Prior art keywords
concrete
water
agent
auxiliary agent
gypsum
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 95111715
Other languages
English (en)
Inventor
陈尧成
张筱薇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Institute of Ceramics of CAS
Original Assignee
Shanghai Institute of Ceramics of CAS
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Institute of Ceramics of CAS filed Critical Shanghai Institute of Ceramics of CAS
Priority to CN 95111715 priority Critical patent/CN1142473A/zh
Publication of CN1142473A publication Critical patent/CN1142473A/zh
Pending legal-status Critical Current

Abstract

一种复合型轻质混凝土制品，它是由无机胶凝材料和泡沫塑料颗粒及混凝土外加剂或助剂组成。属于复合型建筑材料领域。其无机胶凝材料可为硅酸盐水泥、石膏及活性氯化镁—氧化镁。本发明特点是，利用废弃泡沫塑料颗粒，产品为阻燃型防火材料，工艺简单而容重小于0.5g/cm3，而强度可满足使用要求。本发明提供的复合型超轻质混凝土制品主要使用于框架结构建筑物的非承重墙体材料。

Description

一种复合型轻质混凝土制品
本发明涉及一种复合型轻质混凝土制品，特别是有关无机胶凝材料和泡沫塑料颗粒复合型轻质混凝土制品，属于复合型建筑材料领域。
众所周知，随着建筑业的发展，用于墙体的轻质建材愈来愈受到重视。现有轻质墙体材料品种甚多，主要有空心砖、空心水泥混凝土砌块；加气混凝土砌块；抽空石膏条板(或砌块)；泰柏板(一种钢丝网泡沫塑料墙板)；轻质夹热隔心板(两面镀锌薄钢板中夹泡沫塑料)等，它们的容重和抗压强度列于表1。
      表1不同种类轻质墙体材料的性能
品名性能 空心砖  空心混凝土 砌 块 加气混凝土 砌 块  抽空石膏条    板 泰 柏 板*  轻质隔热夹 心 板
容重(g/cm3) 1.1-1.4  0.8-1.4 0.5～0.7 0.58～0.68      0.88  0.3～0.4
抗压强度(MPa) 4.5-20  2.8～15 2.2～4.7 1300M** 轴向78～88Pa横向1220～19850Pa  0.18～0.23
*钢丝网泡沫塑料板两面沫水泥砂浆
**集中破坏载荷
表1数据引自李书田著《新型建材围炉材料与施工》一书，(中国建材工业出版社，1990)。从表1可见，用于墙体轻质水泥制品的容重大多在0.7g/cm3以上，只有500级加气混凝土砌块容重低于0.7g/cm3，但其制作难度大，破损率高。抽空石膏条板的容重在0.6～0.7g/cm3之间。
而近几年来新开发两面用薄钢板中间夹泡沫的轻质夹心板，容重虽能降到0.3～0.4g/cm3，但其价格高达150～250元/米2，防火性能也差，缺乏竞争力。
本发明的目的在于寻找一种由无机胶凝材料和泡沫塑料及混凝土外加剂或助剂组成的复合型超轻混凝土制品，其容重低于0.5g/cm3而强度又与一般轻质墙面材料相当。
本发明的目的是通过利用白色垃圾(聚苯乙烯或聚氨脂泡沫塑料的废弃物，例如大量的泡沫塑料包装材料和目前市场已限制使用的一次性泡塑饭盒和器皿)经机械粉碎后分别与水泥，石膏和镁质胶凝材料复合制成混凝土制品来实施的。它们不仅比现有同类产品的工艺简单，可使容重大大降低而强度还能满足应用要求。例如与水泥复合型的混凝土实心块的容重与普通水泥混凝土相比可降低30～50％，抗压强度在4～10MPa之间，而抽空水泥混凝土砌块容重可下降至0.4～0.7g/cm3，比同类产品低得多；又如与QA增强石膏复合的实心砌块其容重可下降至0.5～0.7g/cm3，抗压强度维持在2-6MPa，导热系数只有0.2-0.3W/m·k，制成抽空砌块后容重可降至0.3～0.4cm3。
本发明具体实施中使用的无机胶凝材料为水泥、石膏和活性氧化镁-氯化镁，依它们不同的凝结特性，有三类不同的配比(重量份数)
(1)硅酸盐水泥  粉煤灰    砂    泡沫塑料颗粒    水   混凝土外加剂
     100       0～150 0～50     0.2-10     40-100     0～8
(2)石膏   泡沫塑料   水      QA增强剂   助 剂
   100     0.2-10  40-100    0-20      0-20
(3)活性氧化镁   石 粉   木 屑   泡沫塑料   水    氯化镁  助加剂
100    0～50    0-10   0.1～10  30-100  35～60  0～10
具体实施方法是将无机胶凝材料和添加物、水、助剂混和，然而与经机械粉碎的泡沫塑料颗粒混和并搅拌均匀浇注，脱模，养护干燥，质量检验等工艺制备的。
混凝土外加剂包括各类常用减水剂、引气剂、调凝剂(速凝剂、早强剂、缓凝剂)、膨胀剂、防水剂、泡沫剂等；石膏为无机胶凝材料时的助剂包括聚乙烯醇，各类改性聚乙烯醇溶液、聚醋酸乙烯、乳胶、尿醛树脂水溶液酚醛树脂、苯丙乳液、石腊、松香等。
以氧化镁-氯化镁为无机胶凝材料时，助剂为尿醛树脂、苯丙乳液、氯乙烯-偏氯乙烯共聚乳液、水溶性酚醛树脂、磷酸三丁脂、硫酸和各类消泡剂；石粉包括粉煤灰、滑石粉、碳酸钙粉、长石粉和黄砂或石英砂。
如泡沫塑料表面较脏，则需先进行洗涤，干燥后再机械粉碎成0.5～7mm左右的颗粒。
本发明提供的复合型超轻质混凝土制品主要使用于框架结构建筑物的非承重墙体材料；少数容重在0.6g/cm3左右的水泥混凝土制品；亦能作低层建筑的承重墙体。其主要优点是：
(1)制作工艺简单，投资少，收益高；
(2)利用废弃泡沫塑料，不仅对消除白色污染具有较好的社会效益，而且原料成本低廉，还能产生较大的经济效益；
(3)容重明显低于现有同类墙体材料，这可大大降低高层建筑的造价；
(4)产品为阻燃型防火材料，其导热系数低，保温性能好并具有较好的机械可加工性——可锯、易钻孔，可旋木螺钉等。
现举各种类型的实施例五个，作为对本发明内容的进一步说明。实施例1
用水泥、泡沫塑料制成空心混凝土标准砌块。砌块尺寸为19公分×19公分×19公分，抽孔率为47％左右，具体制备方法是将水泥、粉煤灰和泡沫塑料颗粒混合均匀，再加入水和调凝剂其用量分别为：水泥2公斤；粉煤灰1.4公斤；经粉碎成1mm颗粒直径的泡沫塑料51克；水1.33公斤；三乙醇胺复合早强剂2克；甲醛、尿素改性聚乙烯醇7克，搅拌均匀后浇入模具内经抽模芯、脱模工序后湿养护三天，再自然养护25天，制得产品的容重为0.554克/厘米3。市场上现有水泥混凝土空心砌块的容重一般为0.8-1.4克/厘米3，本产品容重比现有产品容重低得多。实施例2
用硅酸盐水泥、泡沫塑料复合制标准块，尺寸为4×4×16公分，称水泥280克，粉煤灰250克，黄砂30克，泡塑颗粒12克，水230毫升，木质素减水剂1.1克，甲醛、尿素改性聚乙烯醇0.8克，制作工艺同实施例1。制得标准块的容重为0.95克/厘米3，抗压强度5.5MPa。实施例3
用石膏、泡沫塑料复合制成空心石膏砌块，砌块尺寸为19cm×9。5cm×50cm，抽双孔，抽孔率为50％左右，具体制备方法是水和QA增强剂混合均匀，加入经粉碎后的泡沫塑料颗粒，搅拌均匀后再加入石膏粉搅拌，浇入模具，经抽芯，脱模后自然干燥或烘房干燥(50℃)。其加入量分别为水2400ml，QA增强剂300克，泡塑颗粒36克，石膏粉3公斤。产品容重为0.35克/厘米3，市场现有石膏抽孔条板的容重为0.6-0.7g/cm3，本制品容重比同类产品低30-50％。实施例4
用石膏、泡塑颗粒复合制成标准块，尺寸为4×4×16公分，量水450毫升，聚乙烯醇0.5克，聚醋酸乙烯1克，泡塑颗粒4.6克，石膏粉460克，制作工艺同实施例3，制得标准块容重0.60克/厘米3，抗压强度3MPa。实施例5
用活性氧化镁与泡塑颗粒复合制成空心砌块，砌块尺寸为19公分×19公分×19公分，抽孔率为47％左右，具体制备方法是：将氧化镁，木屑，粉煤灰和泡塑颗粒混合均匀加氯化镁水溶液和添加剂，其用量分别为氧化镁1.8公斤，木屑54克，粉煤灰360克，泡塑颗粒40克，氯化镁890克，水1000毫升，添加剂12克(其中磷酸0.5克，尿醛树脂10克，磷酸三丁脂0.5克，氯化镁1克)，搅拌均匀后，浇入模具内，经抽模芯，脱膜工序后，自然养护28天，制得产品容重为0.48克/厘米3

Claims (5)

1.一种复合型轻质混凝土制品，其特征在于它是由无机胶凝材料和泡沫塑料颗粒及混凝土外加剂或助剂组成。
2.按权利要求1所述的复合轻质混凝土制品，其特征在于所述的无机胶凝材料可以是硅酸盐水泥、石膏或活性氧化镁-氯化镁。
3.按权利要求1或2所述的复合轻质混凝土制品，其特征在于具体组成(重量份数)为硅酸盐水泥100，粉煤灰0-150，砂0-50，泡沫塑料颗粒0.2-10，水40-100，混凝土外加剂0-8组成，混凝土外加剂包括各类减水剂，引气剂，调凝剂(速凝剂，早强剂，缓凝剂)，膨胀剂，防水剂，泡沫剂。
4.按权利要求1或2所述复合轻质混凝土制品，其特征在于具体组份(重量份数)为石膏100，泡沫塑料0.2-10，水40-100，QA增强剂0-20，助剂0-20，助剂包括聚乙烯醇，各类改性聚乙烯醇溶液，聚醋酸乙烯，乳酸，尿醛树脂，水溶性酚醛树脂，苯丙乳液，石腊，松香。
5.按权利要求1或2所述复合轻质混凝土制品，其特征在于具体组份(重量份数)为：活性氧化镁100，木屑0-10，泡沫塑料0.1-10，石粉0-50，水30-100，氧化镁35-60，助剂0-10，助剂包括尿醛树脂，苯丙乳液，氯乙烯-偏氯乙烯共聚乳液，水溶性酚醛树脂，磷酸三丁脂，硫酸和各类消泡剂等，石粉包括粉煤灰，滑石粉，碳酸钙粉，长石粉和黄砂或石英砂。
CN 95111715 1995-08-04 1995-08-04 一种复合型轻质混凝土制品 Pending CN1142473A (zh)