CN105655000A - 一种双芯电力导线 - Google Patents

一种双芯电力导线 Download PDF

Info

Publication number
CN105655000A
CN105655000A CN201610026154.7A CN201610026154A CN105655000A CN 105655000 A CN105655000 A CN 105655000A CN 201610026154 A CN201610026154 A CN 201610026154A CN 105655000 A CN105655000 A CN 105655000A
Authority
CN
China
Prior art keywords
parts
core
electrical lead
flame
surplus
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610026154.7A
Other languages
English (en)
Inventor
熊小辉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610026154.7A priority Critical patent/CN105655000A/zh
Publication of CN105655000A publication Critical patent/CN105655000A/zh
Pending legal-status Critical Current

Abstract

一种双芯电力导线，包括铝基合金芯材和铁基合金芯材，两个芯材外各包覆防腐层后形成两个独立导电芯坯，两个芯坯被阻燃填充料所包裹成整体，阻燃填充料外包覆铜合金金属丝屏蔽网，铜合金金属丝屏蔽网外为导线外套，双芯电力导线中的铝基合金芯材和铁基合金芯材保证了芯材的强度要求和导电性要求；独立设施保证多产品多功能使用防腐层可以提高产品的防腐蚀性能保证材料的使用寿命。

Description

一种双芯电力导线
技术领域
本发明涉一种双芯电力导线，属于导线技术领域。
背景技术
随着海洋能源的开发利用，作为海底电能传输载流设备的海底导线使用越来越多，技术要求也越来越高，尤其要求导线机械物理性能和电气性能优异，具有更大的载流量、优异的防渗水、耐海水腐蚀、耐外部水压、耐电压热冲击和耐张力弯曲性能，使用寿命长，可靠性高。
发明内容
一种双芯电力导线，包括铝基合金芯材和铁基合金芯材，两个芯材外各包覆防腐层后形成两个独立导电芯坯，两个芯坯被阻燃填充料所包裹成整体，阻燃填充料外包覆铜合金金属丝屏蔽网，铜合金金属丝屏蔽网外为导线外套，
铝基合金芯材各元素组分含量为：Co0.7-0.8﹪，Mn0.5-0.6﹪，Ni0.5-0.6﹪，Ca0.4-0.5﹪，W0.2-0.3﹪，In0.2-0.3﹪，Bi0.07-0.08﹪，Ba0.06-0.07﹪，Sc0.05-0.06﹪，Ga0.04-0.05﹪，Ta0.03-0.04﹪，余量为Al，
铁基合金芯材各元素组分含量为：C0.02-0.03﹪，Ti0.7-0.8﹪，Si0.5-0.6﹪，Zr0.4-0.5﹪，Nb0.2-0.3﹪，Co0.1-0.2﹪，Cu0.08-0.09﹪，Ag0.07-0.08﹪，Ta0.05-0.06﹪，Ga0.04-0.05﹪，In0.01-0.02﹪，余量为Fe，
防腐层是称取包括：氯磺化聚乙烯橡胶200-250份，聚碳酸酯70-80份，正硅酸丁酯30-40份，新戊二醇10份，偏苯三酸三辛酯15份，高岭土100份，重晶石粉30份，马来酸二丁酯2份的原料混合固化而成的，
阻燃填充料由长石20-30份，白云石10-20份，滑石粉10-20份，氢氧化铝5份，氧化镁20份，硫酸铝10份，硫酸铜40份，水30份，混合均匀形成糊状浆料填充后固化得到，
铜合金金属丝屏蔽网各组分元素为：W0.1-0.2﹪，Bi0.1-0.2﹪，In0.06-0.07﹪，Sr0.03-0.04﹪，Y0.02-0.03﹪，Ag0.01-0.02﹪，余量为Cu。
所述的一种双芯电力导线，防腐层是称取包括：氯磺化聚乙烯橡胶200份，聚碳酸酯70份，正硅酸丁酯30份，新戊二醇10份，偏苯三酸三辛酯15份，高岭土100份，重晶石粉30份，马来酸二丁酯2份的原料混合固化而成的。
所述的一种双芯电力导线，防腐层是称取包括：氯磺化聚乙烯橡胶250份，聚碳酸酯80份，正硅酸丁酯40份，新戊二醇10份，偏苯三酸三辛酯15份，高岭土100份，重晶石粉30份，马来酸二丁酯2份的原料混合固化而成的。
所述的一种双芯电力导线，防腐层是称取包括：氯磺化聚乙烯橡胶230份，聚碳酸酯75份，正硅酸丁酯35份，新戊二醇10份，偏苯三酸三辛酯15份，高岭土100份，重晶石粉30份，马来酸二丁酯2份的原料混合固化而成的。
所述的一种双芯电力导线，铜合金金属丝屏蔽网各组分元素为：W0.15﹪，Bi0.15﹪，In0.065﹪，Sr0.035﹪，Y0.025﹪，Ag0.015﹪，余量为Cu。
所述的一种双芯电力导线，铜合金金属丝屏蔽网各组分元素为：W0.1﹪，Bi0.1﹪，In0.06﹪，Sr0.03﹪，Y0.02﹪，Ag0.01﹪，余量为Cu。
所述的一种双芯电力导线，铜合金金属丝屏蔽网各组分元素为：W0.2﹪，Bi0.2﹪，In0.07﹪，Sr0.04﹪，Y0.03﹪，Ag0.02﹪，余量为Cu。
所述的一种双芯电力导线，阻燃填充料由长石20份，白云石10份，滑石粉10份，氢氧化铝5份，氧化镁20份，硫酸铝10份，硫酸铜40份，水30份，混合均匀形成糊状浆料填充后固化得到。
所述的一种双芯电力导线，阻燃填充料由长石30份，白云石20份，滑石粉20份，氢氧化铝5份，氧化镁20份，硫酸铝10份，硫酸铜40份，水30份，混合均匀形成糊状浆料填充后固化得到。
所述的一种双芯电力导线，阻燃填充料由长石25份，白云石15份，滑石粉15份，氢氧化铝5份，氧化镁20份，硫酸铝10份，硫酸铜40份，水30份，混合均匀形成糊状浆料填充后固化得到。
上述发明内容相对于现有技术的有益效果在于：1）本发明双芯电力导线中的铝基合金芯材和铁基合金芯材保证了芯材的强度要求和导电性要求；独立设施保证多产品多功能使用2）防腐层可以提高产品的防腐蚀性能保证材料的使用寿命；3）阻燃填充料可以保证其在工作过程中防火耐高温性能，又能降低产品成本；4）外套有效起到保护作用并且原料简单易获得，5）铜合金金属丝屏蔽网起到屏蔽作用。
附图说明
图1为双芯电力导线截面图。
具体实施方式
为了对本发明的技术特征、目的和效果有更加清楚的理解，现详细说明本发明的具体实施方式。
如图1所示一种双芯电力导线，包括铝基合金芯材1和铁基合金芯材2，两个芯材外各包覆防腐层3后形成两个独立导电芯坯，两个芯坯被阻燃填充料4所包裹成整体，阻燃填充料外包覆铜合金金属丝屏蔽网5，铜合金金属丝屏蔽网外为导线外套6。
实施例1
一种双芯电力导线，包括铝基合金芯材和铁基合金芯材，两个芯材外各包覆防腐层后形成两个独立导电芯坯，两个芯坯被阻燃填充料所包裹成整体，阻燃填充料外包覆铜合金金属丝屏蔽网，铜合金金属丝屏蔽网外为导线外套，
铝基合金芯材各元素组分含量为：Co0.7﹪，Mn0.5﹪，Ni0.5﹪，Ca0.4﹪，W0.2﹪，In0.2﹪，Bi0.07﹪，Ba0.06﹪，Sc0.05﹪，Ga0.04﹪，Ta0.03﹪，余量为Al，
铁基合金芯材各元素组分含量为：C0.02﹪，Ti0.7﹪，Si0.5﹪，Zr0.4﹪，Nb0.2﹪，Co0.1﹪，Cu0.08﹪，Ag0.07﹪，Ta0.05﹪，Ga0.04﹪，In0.01﹪，余量为Fe，
防腐层是称取包括：氯磺化聚乙烯橡胶200份，聚碳酸酯70份，正硅酸丁酯30份，新戊二醇10份，偏苯三酸三辛酯15份，高岭土100份，重晶石粉30份，马来酸二丁酯2份的原料混合固化而成的，
阻燃填充料由长石20份，白云石10份，滑石粉10份，氢氧化铝5份，氧化镁20份，硫酸铝10份，硫酸铜40份，水30份，混合均匀形成糊状浆料填充后固化得到
铜合金金属丝屏蔽网各组分元素为：W0.1﹪，Bi0.1﹪，In0.06﹪，Sr0.03﹪，Y0.02﹪，Ag0.01﹪，余量为Cu
实施例2
一种双芯电力导线，包括铝基合金芯材和铁基合金芯材，两个芯材外各包覆防腐层后形成两个独立导电芯坯，两个芯坯被阻燃填充料所包裹成整体，阻燃填充料外包覆铜合金金属丝屏蔽网，铜合金金属丝屏蔽网外为导线外套，
铝基合金芯材各元素组分含量为：Co0.8﹪，Mn0.6﹪，Ni0.6﹪，Ca0.5﹪，W0.3﹪，In0.3﹪，Bi0.08﹪，Ba0.07﹪，Sc0.06﹪，Ga0.05﹪，Ta0.04﹪，余量为Al，
铁基合金芯材各元素组分含量为：C0.03﹪，Ti0.8﹪，Si0.6﹪，Zr0.5﹪，Nb0.3﹪，Co0.2﹪，Cu0.09﹪，Ag0.08﹪，Ta0.06﹪，Ga0.05﹪，In0.02﹪，余量为Fe，
防腐层是称取包括：氯磺化聚乙烯橡胶250份，聚碳酸酯80份，正硅酸丁酯40份，新戊二醇10份，偏苯三酸三辛酯15份，高岭土100份，重晶石粉30份，马来酸二丁酯2份的原料混合固化而成的，
阻燃填充料由长石30份，白云石20份，滑石粉20份，氢氧化铝5份，氧化镁20份，硫酸铝10份，硫酸铜40份，水30份，混合均匀形成糊状浆料填充后固化得到
铜合金金属丝屏蔽网各组分元素为：W0.2﹪，Bi0.2﹪，In0.07﹪，Sr0.04﹪，Y0.03﹪，Ag0.02﹪，余量为Cu
实施例3
一种双芯电力导线，包括铝基合金芯材和铁基合金芯材，两个芯材外各包覆防腐层后形成两个独立导电芯坯，两个芯坯被阻燃填充料所包裹成整体，阻燃填充料外包覆铜合金金属丝屏蔽网，铜合金金属丝屏蔽网外为导线外套，
铝基合金芯材各元素组分含量为：Co0.75﹪，Mn0.55﹪，Ni0.55﹪，Ca0.45﹪，W0.25﹪，In0.25﹪，Bi0.075﹪，Ba0.065﹪，Sc0.055﹪，Ga0.045﹪，Ta0.035﹪，余量为Al，
铁基合金芯材各元素组分含量为：C0.025﹪，Ti0.75﹪，Si0.55﹪，Zr0.45﹪，Nb0.25﹪，Co0.15﹪，Cu0.085﹪，Ag0.075﹪，Ta0.055﹪，Ga0.045﹪，In0.015﹪，余量为Fe，
防腐层是称取包括：氯磺化聚乙烯橡胶230份，聚碳酸酯75份，正硅酸丁酯35份，新戊二醇10份，偏苯三酸三辛酯15份，高岭土100份，重晶石粉30份，马来酸二丁酯2份的原料混合固化而成的，
阻燃填充料由长石25份，白云石15份，滑石粉15份，氢氧化铝5份，氧化镁20份，硫酸铝10份，硫酸铜40份，水30份，混合均匀形成糊状浆料填充后固化得到
铜合金金属丝屏蔽网各组分元素为：W0.15﹪，Bi0.15﹪，In0.065﹪，Sr0.035﹪，Y0.025﹪，Ag0.015﹪，余量为Cu
实施例4
一种双芯电力导线，包括铝基合金芯材和铁基合金芯材，两个芯材外各包覆防腐层后形成两个独立导电芯坯，两个芯坯被阻燃填充料所包裹成整体，阻燃填充料外包覆铜合金金属丝屏蔽网，铜合金金属丝屏蔽网外为导线外套，
铝基合金芯材各元素组分含量为：Co0.72﹪，Mn0.51﹪，Ni0.52﹪，Ca0.42﹪，W0.23﹪，In0.24﹪，Bi0.074﹪，Ba0.061﹪，Sc0.051﹪，Ga0.043﹪，Ta0.033﹪，余量为Al，
铁基合金芯材各元素组分含量为：C0.021﹪，Ti0.73﹪，Si0.53﹪，Zr0.42﹪，Nb0.22﹪，Co0.14﹪，Cu0.084﹪，Ag0.072﹪，Ta0.053﹪，Ga0.041﹪，In0.013﹪，余量为Fe，
防腐层是称取包括：氯磺化聚乙烯橡胶210份，聚碳酸酯74份，正硅酸丁酯32份，新戊二醇10份，偏苯三酸三辛酯15份，高岭土100份，重晶石粉30份，马来酸二丁酯2份的原料混合固化而成的，
阻燃填充料由长石21份，白云石13份，滑石粉14份，氢氧化铝5份，氧化镁20份，硫酸铝10份，硫酸铜40份，水30份，混合均匀形成糊状浆料填充后固化得到
铜合金金属丝屏蔽网各组分元素为：W0.12﹪，Bi0.13﹪，In0.061﹪，Sr0.034﹪，Y0.023﹪，Ag0.014﹪，余量为Cu
实施例5
一种双芯电力导线，包括铝基合金芯材和铁基合金芯材，两个芯材外各包覆防腐层后形成两个独立导电芯坯，两个芯坯被阻燃填充料所包裹成整体，阻燃填充料外包覆铜合金金属丝屏蔽网，铜合金金属丝屏蔽网外为导线外套，
铝基合金芯材各元素组分含量为：Co0.79﹪，Mn0.58﹪，Ni0.56﹪，Ca0.47﹪，W0.29﹪，In0.26﹪，Bi0.077﹪，Ba0.068﹪，Sc0.059﹪，Ga0.049﹪，Ta0.037﹪，余量为Al，
铁基合金芯材各元素组分含量为：C0.026﹪，Ti0.79﹪，Si0.57﹪，Zr0.46﹪，Nb0.26﹪，Co0.17﹪，Cu0.089﹪，Ag0.077﹪，Ta0.057﹪，Ga0.048﹪，In0.018﹪，余量为Fe，
防腐层是称取包括：氯磺化聚乙烯橡胶240份，聚碳酸酯79份，正硅酸丁酯36份，新戊二醇10份，偏苯三酸三辛酯15份，高岭土100份，重晶石粉30份，马来酸二丁酯2份的原料混合固化而成的，
阻燃填充料由长石28份，白云石19份，滑石粉17份，氢氧化铝5份，氧化镁20份，硫酸铝10份，硫酸铜40份，水30份，混合均匀形成糊状浆料填充后固化得到
铜合金金属丝屏蔽网各组分元素为：W0.17﹪，Bi0.16﹪，In0.068﹪，Sr0.039﹪，Y0.029﹪，Ag0.017﹪，余量为Cu。

Claims (10)

1.一种双芯电力导线，包括铝基合金芯材和铁基合金芯材，两个芯材外各包覆防腐层后形成两个独立导电芯坯，两个芯坯被阻燃填充料所包裹成整体，阻燃填充料外包覆铜合金金属丝屏蔽网，铜合金金属丝屏蔽网外为导线外套，
铝基合金芯材各元素组分含量为：Co0.7-0.8﹪，Mn0.5-0.6﹪，Ni0.5-0.6﹪，Ca0.4-0.5﹪，W0.2-0.3﹪，In0.2-0.3﹪，Bi0.07-0.08﹪，Ba0.06-0.07﹪，Sc0.05-0.06﹪，Ga0.04-0.05﹪，Ta0.03-0.04﹪，余量为Al，
铁基合金芯材各元素组分含量为：C0.02-0.03﹪，Ti0.7-0.8﹪，Si0.5-0.6﹪，Zr0.4-0.5﹪，Nb0.2-0.3﹪，Co0.1-0.2﹪，Cu0.08-0.09﹪，Ag0.07-0.08﹪，Ta0.05-0.06﹪，Ga0.04-0.05﹪，In0.01-0.02﹪，余量为Fe，
防腐层是称取包括：氯磺化聚乙烯橡胶200-250份，聚碳酸酯70-80份，正硅酸丁酯30-40份，新戊二醇10份，偏苯三酸三辛酯15份，高岭土100份，重晶石粉30份，马来酸二丁酯2份的原料混合固化而成的，
阻燃填充料由长石20-30份，白云石10-20份，滑石粉10-20份，氢氧化铝5份，氧化镁20份，硫酸铝10份，硫酸铜40份，水30份，混合均匀形成糊状浆料填充后固化得到，
铜合金金属丝屏蔽网各组分元素为：W0.1-0.2﹪，Bi0.1-0.2﹪，In0.06-0.07﹪，Sr0.03-0.04﹪，Y0.02-0.03﹪，Ag0.01-0.02﹪，余量为Cu。
2.如权利要求1所述的一种双芯电力导线，防腐层是称取包括：氯磺化聚乙烯橡胶200份，聚碳酸酯70份，正硅酸丁酯30份，新戊二醇10份，偏苯三酸三辛酯15份，高岭土100份，重晶石粉30份，马来酸二丁酯2份的原料混合固化而成的。
3.如权利要求1所述的一种双芯电力导线，防腐层是称取包括：氯磺化聚乙烯橡胶250份，聚碳酸酯80份，正硅酸丁酯40份，新戊二醇10份，偏苯三酸三辛酯15份，高岭土100份，重晶石粉30份，马来酸二丁酯2份的原料混合固化而成的。
4.如权利要求1所述的一种双芯电力导线，防腐层是称取包括：氯磺化聚乙烯橡胶230份，聚碳酸酯75份，正硅酸丁酯35份，新戊二醇10份，偏苯三酸三辛酯15份，高岭土100份，重晶石粉30份，马来酸二丁酯2份的原料混合固化而成的。
5.如权利要求1所述的一种双芯电力导线，铜合金金属丝屏蔽网各组分元素为：W0.15﹪，Bi0.15﹪，In0.065﹪，Sr0.035﹪，Y0.025﹪，Ag0.015﹪，余量为Cu。
6.如权利要求1所述的一种双芯电力导线，铜合金金属丝屏蔽网各组分元素为：W0.1﹪，Bi0.1﹪，In0.06﹪，Sr0.03﹪，Y0.02﹪，Ag0.01﹪，余量为Cu。
7.如权利要求1所述的一种双芯电力导线，铜合金金属丝屏蔽网各组分元素为：W0.2﹪，Bi0.2﹪，In0.07﹪，Sr0.04﹪，Y0.03﹪，Ag0.02﹪，余量为Cu。
8.如权利要求1所述的一种双芯电力导线，阻燃填充料由长石20份，白云石10份，滑石粉10份，氢氧化铝5份，氧化镁20份，硫酸铝10份，硫酸铜40份，水30份，混合均匀形成糊状浆料填充后固化得到。
9.如权利要求9所述的一种双芯电力导线，阻燃填充料由长石30份，白云石20份，滑石粉20份，氢氧化铝5份，氧化镁20份，硫酸铝10份，硫酸铜40份，水30份，混合均匀形成糊状浆料填充后固化得到。
10.如权利要求1所述的一种双芯电力导线，阻燃填充料由长石25份，白云石15份，滑石粉15份，氢氧化铝5份，氧化镁20份，硫酸铝10份，硫酸铜40份，水30份，混合均匀形成糊状浆料填充后固化得到。
CN201610026154.7A 2016-01-15 2016-01-15 一种双芯电力导线 Pending CN105655000A (zh)