CN114224756B - 一种天然矿石的组合物及其应用 - Google Patents
一种天然矿石的组合物及其应用 Download PDFInfo
- Publication number
- CN114224756B CN114224756B CN202111595121.1A CN202111595121A CN114224756B CN 114224756 B CN114224756 B CN 114224756B CN 202111595121 A CN202111595121 A CN 202111595121A CN 114224756 B CN114224756 B CN 114224756B
- Authority
- CN
- China
- Prior art keywords
- powder
- nephrite
- nephrite powder
- natural ore
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及护肤品及化妆品领域,本申请提供了一种天然矿石的组合物及其应用,所述的组合物包括软玉粉A和软玉粉B,所述软玉粉A为10~20微米软玉玉石粉,所述软玉粉B为5~9微米软玉玉石粉。本发明实施例可利用锆材质的球磨机通过不同时间参数辗磨出不同粒径大小的软玉粉,并搭配不同粒径大小的软玉粉,具有良好的吸油值,肤感滑顺,应用于散粉与蜜粉饼等化妆制品中,达到滑顺肤感与最佳妆效,使玉石粉不仅仅停留于概念添加。
Description
技术领域
本申请涉及护肤品及化妆品技术领域,尤其涉及一种天然矿石的组合物及其应用。
背景技术
天然宝石粉有红宝石、绿宝石、碧玺等,绝大部分的宝石主要成分是硅酸盐类矿物,在护肤品及化妆品领域应用所起的功效主要来自于其中的微量元素。例如,在散粉等粉类化妆品中添加宝石粉末,期望达到滋养或活化细胞等功效。
然而,一般宝石粉末因硬度较高,造成粒径不均一,干感粗糙,其在化妆品中的应用仅限于概念添加,难以达到实质功效。
发明内容
有鉴于此,本发明要解决的问题在于提供一种天然矿石的组合物及其应用,本发明提供的矿石粉体组合物具有良好的吸油值,肤感滑顺,可应用于散粉或蜜粉饼等化妆制品中,达到控油的功效。
本发明提供一种天然矿石的组合物,包括软玉粉A和软玉粉B,所述软玉粉A为10~20微米软玉玉石粉,所述软玉粉B为5~9微米软玉玉石粉。
如通常所知的天然矿物中,玉石可被分成硬玉(即翡翠)和软玉两大类。硬玉属于辉石族,并且具有包括硅酸、氧化铝和碳酸钠的单斜晶系。它是一种紧密的物质,其硬度可与水晶的硬度相比。它是黑色、蓝绿色或绿色的透明或半透明体,人们通常习惯将硬玉称为“玉石”。
软玉玉石,是一种具有链硅酸盐单斜晶系的无机矿物材料。相较于硬玉等其他宝石,软玉玉石的莫氏硬度落在6~6.5,属于硬度较低的宝石。软玉玉石的品质是由其微结构决定的,纤维颗粒愈细小、通常质量就愈好。本发明可利用辗磨工艺控制辗磨时间、力道,能制备出不同粒径大小的软玉粉;组合的软玉粉具有良好的吸油值,有效起到控油功效,且肤感滑顺,可作为辅助原料应用于护肤品及化妆品,例如散粉或蜜粉饼中。
本发明所述天然矿石的组合物即两种不同粒径的软玉粉的组合搭配,其中,所述的软玉粉A是粒径为10~20微米的玉石粉,粒径大小进一步为10~15微米,而软玉粉B是粒径为5~9微米的玉石粉,可再分为5~7微米、7~9微米。在本发明中,所述的粉体粒径是片状粉末平均的片型大小。
在本发明中,所述软玉粉A的粒径相对较大,利于好的肤感、妆感;10微米的软玉粉妆感最透。并且,本发明搭配粒径在5~9微米的软玉粉B,应用时才能达到贴肤度最佳(人体毛孔与沟槽孔隙大约在7微米左右),控油度优秀。在本发明的实施例中,经过球磨机研磨后可制备粒径较小且均匀的玉石粉体;因其特殊的结构,微观形状为片状的,更能达到贴肤、易铺展的效果。
在本发明的实施例中,所述软玉粉A和软玉粉B的莫氏硬度分别在6~6.5;均可利用锆材质球磨机,通过不同时间碾磨制得。本发明实施例控制了球磨机工艺参数,制备了两种不同粒径大小的软玉玉石粉,并搭配不同比例,获得最佳肤感与高控油度的玉石组方,进一步可得到贴肤度最佳、控油度最好的最佳复配比例。
在本发明的一些实施例中,所述软玉粉A和软玉粉B的质量比为1~5:9~5,优选为1~3:9~7,更优选为1:9、2:8或3:7。
本发明实施例将此玉石组方运用于散粉与蜜粉饼配方中,其控油度与妆效均能比一般云母粉配方达到更高的消费者喜爱度。
本发明实施例可利用锆材质的球磨机通过不同时间参数辗磨出不同粒径大小的软玉粉,并搭配不同粒径大小的软玉粉,应用于散粉与蜜粉饼中,达到滑顺肤感与最佳妆效,使软玉粉不仅仅停留于概念添加。
本发明实施例可提供所述的玉石粉组合物的制备方法:原料为块状软玉玉石,将该玉石利用对辊破碎机磨成20目粉末,将所述粉末与水(固含量40%-60%,使用蒸馏水)混合,具体的球磨机设备为锆材质行星球磨机,包括不锈钢研磨配件,并采用大小球搭配方式,蒸馏水为一次蒸馏水。
作为优选,球料质量比为2-4:1。示例地,研磨120转/分,8小时后得到浆状物,加入5倍重量的纯水,加入0.1%六偏磷酸钠,搅拌1小时,得到玉石粉半成品。
在本发明的具体实施例中,得到的玉石粉半成品静置沉淀20分钟,沉淀物即为10~20微米的软玉玉石粉;持续沉淀6小时得到沉淀物,即为7~9微米的玉石粉;持续沉淀16小时得到沉淀物,即为5~7微米的软玉粉。
本发明实施例将不同粒径的软玉粉混合,即得玉石组方产品(天然矿石的组合物)。
本发明提供如前文所述的天然矿石的组合物在制备护肤品及化妆品中的应用,可以为乳化制品或固体粉末制品。
按照生产工艺可分为膏霜和乳液、带粉体的膏霜和乳液、固体粉末制品等,本发明实施例可将所述天然矿石的组合物制备粉类化妆品;粉类化妆品主要是以粉类为主要原料配制而成、外观呈粉状或块状的一类制品。
本发明某些实施例提供一种散粉,由基质原料和辅助原料组成,所述辅助原料包括前文所述的天然矿石的组合物。
在本发明中,所述散粉的配方主要由硅石组成;所述天然矿石的组合物在散粉中的质量占比不超过6%,优选为0.1-6%,更优选为0.5-5%。
本发明实施例所述散粉配方主要原料为硅石;硅石为球型粉体,球型粉末提供良好肤感,也有很好的吸油值。硅石(quartz stone)是脉石英、石英岩、石英砂岩的总称,有鲜明的化合物和硅酸盐成分。纯硅石可作石英玻璃或提炼单晶硅,结晶硅石外观一般呈乳白色、灰白色、淡黄色以及红褐色。
本发明所述天然矿石的组合物在散粉等化妆品中,可起到控油、去角质,抗结块及填充等作用。
此外,所述散粉的配方还可添加增稠剂、柔软剂、润滑剂、防腐剂等化妆品用的辅助原料。其中,通过常规的加脂可获得蜜粉,所用的油脂添加量可为1~5%,种类没有特殊限制。
在本发明的一些实施例中,按质量份数,所述散粉配方具体包括:硅石38-56份、硅油类增稠剂15-20份、合成氟金云母13-23份、月桂酰赖氨酸2-4份、所述天然矿石的组合物1-6份、鲸蜡基聚二甲基硅氧烷1-5份、氮化硼1-3份、防腐剂0.1-2份。另一些实施例中,散粉配方中的填充剂还可以采用滑石粉;也可以加入丙烯酸树脂等成膜剂。
作为优选,所述硅油类增稠剂为乙烯基聚二甲基硅氧烷/聚甲基硅氧烷硅倍半氧烷交联聚合物;所述防腐剂优选为苯氧乙醇/乙基己基甘油,复配效果较好。
其中,乙烯基聚二甲基硅氧烷/聚甲基硅氧烷硅倍半氧烷交联聚合物:是有机硅树脂披覆有机硅橡胶粉末的复合粉末,是一种硅油增稠剂,具有优异的平滑性、弹性的特性,可以达到增稠和哑光的效果;同时具有增加保湿的功效。
月桂酰赖氨酸是一种氨基酸衍生物,它不仅具有高润滑性、柔滑的肤感、低磨擦系数,而且具有抗静电、抗氧化性,主要用于彩妆、化妆品粉体处理,赋予粉体很好的贴肤感、柔滑感及疏水性。
氟金云母片也称合成氟金云母碎片,是用化工原料经高温熔融、冷却析晶而制得,其单晶片的分子式为KMg3(AlSi3O10)F2,属于单斜晶系,为典型的层状硅酸盐。是模拟天然云母成矿而制成的一种新型无机晶体材料。除具有天然云母的性能以外,合成氟金云母还同时具有纯净度高、白度高,性能都比天然云母有大幅度提升。该材料属硅酸盐类、片层状、六方结构的晶体材料。合成氟金云母一般具有光泽,也可制作成无光泽状。氟金云母片在化妆品中主要作为着色剂使用,并增加化妆品明亮度,使用后会增加皮肤质感与触感。氟金云母片不会被皮肤吸收,由于是矿物质对皮肤无伤害,主要是为了增强化妆品闪亮的视觉效果。
氮化硼是由氮原子和硼原子所构成的晶体,化学组成为43.6%的硼和56.4%的氮,具有四种不同的变体:六方氮化硼(HBN)、菱方氮化硼(RBN)、立方氮化硼(CBN)和纤锌矿氮化硼(WBN),一氮化硼在化妆品中做吸收剂使用,和滑石粉作用类似,有一定遮瑕力,能增加产品顺滑之感,在蜜粉、粉底等化妆品中使用较多。
鲸蜡基聚二甲基硅氧烷是一种烷基接枝的硅氧烷,与多种油脂混溶,易乳化,广泛用于护肤、彩妆、护发等产品,提供非常好的滋润、柔软、丝滑肤感,不油不粘,在护发类产品中可取代苯基硅油以提高头发的光泽度;在本发明配方体系中可作为油脂应用。
本发明实施例采用一些球形颗粒原料,与所述软玉粉、合成氟金云母等片状原料进行配伍组合,可以达到较好的肤感、妆效和控油等功效。
苯氧乙醇/乙基己基甘油:乙基己基甘油影响微生物细胞膜上的表面张力,从而提高苯氧乙醇的防腐能力;对细菌、酵母菌和霉菌都具有很好的抑制作用,是一种典型的抑菌防腐产物,同时也具有一定的杀菌能力。
本发明优选实施例中的散粉配方为:乙烯基聚二甲基硅氧烷/聚甲基硅氧烷硅倍半氧烷交联聚合物15-20份、硅石38-56份、月桂酰赖氨酸2-4份、合成氟金云母13-23份、组合的软玉粉1-6份、氮化硼1-3份、甲基烷基化硅石0.01-1份、苯氧乙醇/乙基己基甘油0.1-2份、鲸蜡基聚二甲基硅氧烷1-5份、活性物0.01-1份。
上述的散粉配方中,甲基烷基化硅石的主体成份是SiO2,具有亲水性;但是其表面经过羟基二甲基硅氧烷(或其他硅烷类如硅氮烷等)处理后,通过硅石表面的硅羟基和羟基二甲基硅氧烷等的硅羟基缩合,从而使二甲基硅烷化的硅石具有疏水性或亲油型。并且,所述的活性物主要是增加控油能力的植物活性物,利于起到长效控油功效。
本发明一些实施例还提供了一种长效持妆、控油蜜粉的制备方法,其包括如下步骤:
(1)按选定重量份称取所述片状填充粉料、球状粉料等,均匀混合,倒入打粉锅内进行高速搅拌混合,作为第一相;
(2)将混合均匀的第一相加入油脂、防腐剂,进行再次充分高速搅拌混合,混合均匀后即可出料。
具体的,本发明实施例所述的散粉理化指标均符合国家标准GB/T29991-2013;其中:
本发明某些实施例提供一种粉饼,由基质原料和辅助原料混合后的物料经过压制而成,所述辅助原料包括前文所述的天然矿石的组合物。
进一步地,所述辅助原料还可包括油脂和防腐剂,优选通过分步混合再出料,进而制成蜜粉饼。
本发明对所述散粉主要原料的来源并无特殊限制,均可采用化妆品领域可接受的市售原辅料。本发明对所述的散粉、蜜粉、普通粉饼粉底、蜜粉饼等制备的设备及工艺也没有特殊限制,可以达到行业常规要求。
功效试验显示,本发明实施例提供的软玉矿石粉体组合物具有良好的吸油值,肤感滑顺;其应用于散粉或蜜粉饼等化妆制品中,达到控油、贴肤等效果。
具体实施方式
下面对本申请实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本申请一部分实施例,而不是全部的实施例。基于本申请中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例,都属于本申请保护的范围。
为了进一步理解本申请,下面结合实施例对本申请提供的天然矿石的组合物及其应用进行具体地描述。
实施例1
玉石制备方法:
原料为块状软玉玉石,软玉玉石的莫氏硬度落在6~6.5。将软玉玉石原料利用对辊破碎机磨成20目粉末,将20目粉末与蒸馏水(固含量50%)混合,球磨机设备为锆材质行星球磨机,不锈钢研磨配件,并采用大小球搭配方式,蒸馏水为一次蒸馏水。
其中,球料质量比为3:1。120转/分,研磨时间8小时后,得到浆状物,加入5倍重量的纯水,加入0.1wt%六偏磷酸钠,搅拌1小时,得到玉石半成品。将所述玉石半成品进行以下操作:
静置沉淀20分钟得到沉淀物,用电子显微镜拍照检测粒径,得到10~20微米的软玉玉石粉(以下可简称玉石粉、软玉粉);
持续沉淀6小时得到沉淀物,检测粒径,得到7~9微米的玉石粉;
持续沉淀16小时得到沉淀物,检测粒径,得到5~7微米的玉石粉。
玉石组方如下:
组方1:玉石粉A:玉石粉B=1:9;
组方2:玉石粉A:玉石粉B=2:8;
组方3:玉石粉A:玉石粉B=3:7;
组方4:玉石粉A。
玉石粉A为10~20微米玉石粉,玉石粉B为7~9微米玉石粉。
对以上的软玉玉石粉组方进行控油测试、人群测试:
组方滑顺度测试方法:选取10名手臂皮肤细致的女性,将0.3g的玉石粉组方均匀涂抹于每位测试者手臂内侧(2cm*2cm),固定打20个圈,并针对滑顺度与贴肤度进行评分。
评分标准如下:
滑顺程度:1分:不滑顺,阻力非常大;2分:不是很滑顺,阻力大;3分:不是很滑顺,阻力一般;4分:滑顺,没有阻力;5分:非常滑顺,毫无阻力。
贴肤程度:1分:非常不贴肤;2分:不是很贴肤;3分:一般;4分:很贴肤;5分:非常贴肤。
测试者按照以上评分标准进行评分,最后统计全部评分计算平均值,具体评分结果如表1所示。
控油测试:将人工皮酯(油酸:角鲨烷:橄榄油=1:2:2质量比)滴入1g的玉石组方中,并搅拌使其成团,待其无法在吸取皮酯后停止滴入,并测试其总吸取的皮酯量,计算控油率,具体结果如表1所示。
从表1可见,本发明实施例提供的矿石粉体组合物具有良好的吸油值,肤感滑顺。
表1玉石组方的功效实验结果
实施例2-6
蜜粉的制备方法包括如下步骤:
(1)按照表2的散粉配方,称取所述片状填充粉料、球状填充粉料等均匀混合,倒入打粉锅内进行高速搅拌混合,分别作为第一相;
(2)将混合均匀的第一相加入油脂、防腐剂,进行再次充分高速搅拌混合,混合均匀后即可出料,分别得到对应的散粉产品。
此外,表2中还有对比例1-2的散粉配方,对比例制备步骤与实施例基本相同。
表2本发明实施例中的散粉配方(质量份)
其中,红宝石粉主要由氧化铝组成,具有活颜养肤功效,以及些微的控油力。片状原料主要做填充剂,用于肤感调节;活性物为三皮素,主要用于长效控油。
散粉功效测试方法:选取50例女性,平均年龄25±10岁,首先分别在左脸和右脸涂抹等同分量的本发明的实施例样品和对比例样品,测试者依据涂抹过程及涂抹后的效果进行评价比较。
测试评分标准如下:
贴肤程度:1分:不贴肤,严重卡粉;2分:不贴肤,卡粉较明显;3分:贴肤一般,卡粉一般;4分:贴肤较好,基本不卡粉;5分:非常贴肤,不卡粉。
隐匿毛孔度:1分:差;2分:较差;3分:一般;4分:较好;5分:好。
持久度:1分:差;2分:较差;3分:一般;4分:较好;5分:好。
控油程度:1分:差;2分:较差;3分:一般;4分:较好;5分:好。
粉质细腻度:1分:粗糙;2分:较粗糙;3分:细腻度一般;4分:细腻度较好;5分:非常细腻。
妆效喜爱度:1分:差;2分:较差;3分:一般;4分:较好;5分:好。
测试者按照以上评分标准进行评分,最后统计全部评分计算平均值,具体评分结果如下表所示:
表3本发明实施例中的散粉功效评分结果
由以上实施例可知,本发明实施例将不同粒径的软玉玉石组方运用于散粉与蜜粉饼配方中,优选配比玉石粉A:玉石粉B=1:9,其控油度与妆效均能比一般云母粉配方达到更高的消费者喜爱度。本发明实施例可利用锆材质的球磨机通过不同时间参数辗磨出不同粒径大小的软玉粉,并搭配不同粒径大小的软玉粉,应用于散粉与蜜粉饼中,达到滑顺肤感与最佳妆效,使软玉粉不仅仅停留于概念添加。
以上所述仅是本发明的优选实施方式,应当指出,对于使本技术领域的专业技术人员,在不脱离本发明技术原理的前提下,是能够实现对这些实施例的多种修改的,而这些修改也应视为本发明应该保护的范围。
Claims (8)
1.一种天然矿石的组合物的制备方法,其特征在于,所述的天然矿石的组合物由软玉粉A和软玉粉B组成,所述软玉粉A为10~20微米软玉玉石粉,所述软玉粉B为5~9微米软玉玉石粉;所述软玉粉A和软玉粉B的质量比为1~5:9~5;所述的制备方法包括如下步骤:利用锆材质球磨机通过不同时间碾磨分别制得软玉粉A和软玉粉B,将软玉粉A和软玉粉B混合即得。
2.根据权利要求1所述的天然矿石的组合物的制备方法,其特征在于,所述软玉粉A和软玉粉B的质量比为1~3:9~7。
3.根据权利要求2所述的天然矿石的组合物的制备方法,其特征在于,所述软玉粉A和软玉粉B的质量比为1:9、2:8或3:7。
4.根据权利要求1-3任一项所述的天然矿石的组合物的制备方法,其特征在于,所述软玉粉A和软玉粉B的莫氏硬度分别在6~6.5。
5.一种散粉,由基质原料和辅助原料组成,所述辅助原料包括权利要求1-4任一项所述制备方法得到的天然矿石的组合物;所述散粉的配方主要由硅石组成,所述天然矿石的组合物在散粉中的质量占比为0.1-6%。
6.根据权利要求5所述的散粉,其特征在于,所述散粉的配方按质量份数具体包括:
硅石38-56份、硅油类增稠剂15-20份、合成氟金云母13-23份、月桂酰赖氨酸2-4份、所述天然矿石的组合物1-6份、鲸蜡基聚二甲基硅氧烷1-5份、氮化硼1-3份、防腐剂0.1-2份。
7.一种粉饼,由基质原料和辅助原料混合后的物料经过压制而成,所述辅助原料包括权利要求1-4任一项所述制备方法得到的天然矿石的组合物;所述基质原料主要为硅石,所述天然矿石的组合物在混合后物料中的质量占比为0.1-6%。
8.根据权利要求7所述的粉饼,其特征在于,所述辅助原料还包括油脂和防腐剂,通过分步混合再出料,进而制成蜜粉饼。