CN114196363B - 一种低模量防火阻燃装配式建筑外墙接缝胶及其制备方法 - Google Patents
一种低模量防火阻燃装配式建筑外墙接缝胶及其制备方法 Download PDFInfo
- Publication number
- CN114196363B CN114196363B CN202111666879.XA CN202111666879A CN114196363B CN 114196363 B CN114196363 B CN 114196363B CN 202111666879 A CN202111666879 A CN 202111666879A CN 114196363 B CN114196363 B CN 114196363B
- Authority
- CN
- China
- Prior art keywords
- parts
- modified
- feldspar powder
- kaolin
- wall joint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开一种低模量防火阻燃装配式建筑外墙接缝胶及其制备方法，所述低模量防火阻燃装配式建筑外墙接缝胶按其重量份包括以下成分：硅烷改性聚醚树脂50‑75份；改性长石粉0‑5份；改性高岭土0‑35份；除水剂0‑3份；触变剂0‑2份；偶联剂0.1‑3份；催化剂0.1‑2份；增塑剂40份；抗氧化剂1.5份；紫外线吸收剂1份；色料3份；填料20份。本发明所述的低模量防火阻燃装配式建筑外墙接缝胶，通过调整阻燃剂之间质量比来获得更低模量应用于装配式建筑外墙接缝，粘结性好、弹性好、同时具备优异的防火阻燃能力，UL94‑V0。
Description
技术领域
本发明属于装修建材领域，特别涉及一种低模量防火阻燃装配式建筑外墙接缝胶及其制备方法。
背景技术
装配式建筑外墙接缝用密封胶主要为改性聚醚密封胶、聚氨酯密封胶、硅酮密封胶等，标准按照国标JC/T 881-2017《混凝土接缝用密封胶》实施。其中改性聚醚密封胶具有更优异的综合性能。近年国家消防部要求，现代高层建筑防火要求用材料须具有防火阻燃等性能要求。
其中市面上绝大多数改性聚醚密封胶不具备防火能力，并且由于无机阻燃剂的大量添加会大幅度降低材料的力学性能，材料的拉伸强度、断裂伸长率、柔性等力学性能，均无法满足装配式建筑外墙接缝施工要求。
装配式建筑外墙接缝胶需要具有低模量，优异的粘结性、耐候性、抗污染性，表面可涂刷涂料，安全环保等优点，对混凝土、硅酸钙板、纤维水泥板、石材和陶瓷等多孔性材料粘结性突出，主要用于装配式建筑墙板防水接缝密封，也可用于其他建筑接缝密封。
现阶段市面上装配式建筑外墙接缝胶在满足力学性能JC/T 881-2017《混凝土接缝用密封胶》的基础上，不具备防火阻燃性能。
发明内容
本发明的目的是提供一种低模量防火阻燃装配式建筑外墙接缝胶，通过调整阻燃剂之间质量比来获得更低模量应用于装配式建筑外墙接缝，同时具备优异的防火阻燃能力，UL94-V0。
有必要地，还提供了上述低模量防火阻燃装配式建筑外墙接缝胶的制备方法。
一种低模量防火阻燃装配式建筑外墙接缝胶，按其重量份包括以下成分：
硅烷改性聚醚树脂50-75份；
改性长石粉0-5份；
改性高岭土0-35份；
除水剂0-3份；
触变剂0-2份；
偶联剂0.1-3份；
催化剂0.1-2份；
增塑剂40份；
抗氧化剂1.5份；
紫外线吸收剂1份；
色料3份；
填料20份。
其中，所述改性长石粉的活化指数为0.8-1，吸油值25g/100g-28g/100g。
其中，活化指数是指的计算公式如下：
活化指数的一般测定方法是，称取一定量表面改性后的粉体样品，置于盛有一定容积纯净水的烧杯中，以一定转速搅拌1～2min；然后静置，等溶液澄清后，刮去水溶液表面的粉体物料，并将沉入烧杯底的粉体物料过滤、烘干、称重。然后根据下式计算活化指数
吸油值的测试方法是：GB T 3780.2-2017第二部分:吸油值的测定。
其中，所述改性长石粉是由长石粉经过200型硬脂酸改性制得，其制备步骤为：
将重量比为100:(1.15-1.35)的长石粉与200型硬脂酸混合均匀，加入清水，浆料浓度为12.8％，长石粉与硬脂酸的重量占混合物的比例为12.8％，搅拌2.5h,反应温度为45℃，抽滤、干燥后得到改性长石粉。
在上述长石粉的改性方法中，浆料浓度为12.8％时,改性效果达到最佳,长石粉活化指数由原来的0.0325上升到0.8-1,即为完全活化,粘度降为48mPa.s,吸油量由原来的36.5g/100g降为25-28g/100g。
所述的硬指酸，为十八烷酸，选自上海锋翰化工有限公司SA-1801、SA-1803、SA-1804、SA-1805中的一种或几种。
长石粉硬脂酸表面改性采用湿法改性，在反应釜中进行。将重量比为100:(1.15-1.35)的长石粉与200型硬脂酸混合均匀，加入适量清水，一直搅拌，时间为2.5h，反应温度为45℃，然后进行抽滤、干燥即可使用。
其中，所述改性高岭土的比表面积小于1000cm2/g，优选为比表面积为955cm2/g，吸油值为15g/100g-18g/100g。
其中，所述改性高岭土由以下步骤制得：
将高岭土进行烘干、粉磨预处理，粉磨后高岭土颗粒的比表面积为：6400cm2/g，然后将高岭土粉均匀撒在耐火匣钵中煅烧时，料层厚度为0.5cm，以50℃/min升温到850℃，并在电炉内保温2min，急速冷却，粉碎得到改性高岭土。
优选地，所述长石粉选自滁州格锐矿业SM-525、SM-510、SM-530中的至少一种或几种复配。
优选地，所述高岭土选自山西金诚高岭土公司JC-60、JC-50、JC-40中的至少一种或几种复配进行工艺改性。
其中，所述硅烷改性聚醚树脂选自端基可水解的硅烷封端聚醚，20℃下的粘度为3000-50000cps，粘度测试设备为博勒飞粘度计dv2t型。
优选地，所述硅烷封端聚醚树脂的结构式为：
其中，R2为R1或OR1，R1选自甲基或乙基。
其中，所述增塑剂选自邻苯二甲酸二异壬酯、邻苯二甲酸二异癸酯和磷酸二苯基异癸酯中的至少一种。
所述抗氧化剂选自四[β-(3，5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯(IRGANOX1010)、β-(3,5-二叔丁基-4-羟基苯基)丙酸异辛醇酯(IRGANOX1135)和乙烯双(氧乙烯基)双[3-(5-叔丁基-4-羟基-间甲苯基)丙酸酯](IRGANOX245)中的至少一种。
所述紫外线吸收剂选自巴斯夫TINUVIN326、TINUVIN328、TINUVIN329、TINUVIN571、TINUVIN123、TINUVIN622、TINUVIN765、TINUVIN770、TINUVIN292、TINUVIN791和TINUVIN944中的至少一种。
所述色料选自钛白粉、炭黑和铁红中的至少一种。
所述填料选自纳米碳酸钙、轻质碳酸钙、重质碳酸钙和氢氧化铝中的至少一种。
所述触变剂选自聚酰胺蜡和/或氢化蓖麻油。
所述除水剂包括乙烯基三甲氧基硅烷。
所述偶联剂选自γ-氨丙基三甲氧基硅烷、N-β-(氨乙基)-γ-氨丙基三甲氧基硅烷、N-β-(氨乙基)-γ-氨丙基甲基二甲氧基硅烷、γ-缩水甘油醚氧丙基三甲氧基硅烷和-甲基丙烯酰氧基丙基三甲氧基硅烷中的至少一种。
所述催化剂选自辛酸亚锡、二月桂酸二丁基锡和二正丁基双(乙酰丙酮基)锡中的至少一种。
一种如上所述的低模量防火阻燃装配式建筑外墙接缝胶的制备方法：
按比例将硅烷改性聚醚树脂、改性长石粉、改性高岭土、除水剂、触变剂、偶联剂、催化剂、增塑剂、抗氧化剂、紫外线吸收剂、色注和填料混合，加热至105-115℃，恒温2-3h脱水，脱水过程分散盘高速500-1500r/min搅拌，同时真空度保持-0.09--0.1Mpa，即可得到接缝胶。
优选地，所述脱水过程中进行高速搅拌，所述高速搅拌的速度为，优选1000r/min。
相较于现有技术，本发明低模量防火阻燃装配式建筑外墙接缝胶是由改性长石粉、改性高岭土以及特定粘度的硅烷改性聚醚树脂在除水剂、触变剂、偶联剂、催化剂、增塑剂、抗氧化剂、紫外线吸收剂、色注和填料的共同作用下制得。
普通未经改性长石粉是钾、钠、钙、钡等碱金属或碱土金属的铝硅酸盐矿物，晶体结构属架状结构。其主要成份为SiO2、Al2O3、K2O、Na2O、CaO、片状云母等。片状云母耐火阻燃能力强(耐火800℃以上)，所以长石粉兼具密封胶补强剂与阻燃剂。
长石粉经过改性的，长石粉表面由原来的亲水变为疏水，分散性及与相容性均得到明显改善。
高岭土，化学成分为：Al2O3＞43％，SiO2＝50-54％，具有硅氧四面体层微观结构，结构致密稳定，耐受温度高，高温下不会发生坍塌等特点。常规型高岭土煅烧温度在750℃，此时吸油值高达80.272g/100g,直接添加的话，成品密封胶强度大，力学性能差，无法满足装配式建筑外墙接缝胶性能要求。
改性后的高岭土的吸油性能高，比表面积小，用于接缝胶中制得的产品力学性能好，胶体柔软，伸长率高，长时间定伸不容易出现裂痕。
经过改性的长石粉和高岭土与特定粘度的硅烷改性聚醚树脂分子间作用力更强，制得的接缝胶粘结性能好、弹性好，同时具备优异的防火阻燃能力。
具体实施方式
为了使本技术领域的人员更好地理解本发明方案，下面结合具体实施方式对本发明作进一步的详细说明。
本发明所用物质来源如下：
长石粉：滁州格锐矿业SM-525，活化指数1、粘度48mPa.s、吸油值25.1g/100g
高岭土：山西金诚高岭土公司JC-60，比表面积900cm2/g，吸油值为16.2g/100g。
除水剂：乙烯基三甲氧基硅烷，市售。
触变剂：核心化学触变剂，聚酰胺蜡和/或氢化蓖麻油。
偶联剂：γ-氨丙基三甲氧基硅烷，市售。
催化剂：辛酸亚锡，市售。
增塑剂：邻苯二甲酸二异壬酯，市售。
抗氧化剂：四[β-(3，5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯(IRGANOX1010)，市售。
紫外线吸收剂：巴斯夫TINUVIN326、TINUVIN328、TINUVIN329、TINUVIN571、TINUVIN123、TINUVIN622、TINUVIN765、TINUVIN770、TINUVIN292、TINUVIN791和TINUVIN944中的至少一种。
色料：铁红，市售。
硅烷封端聚醚树脂A：瓦克化学，XM-25型号，20℃下的粘度为3000cps，粘度测试方法为:博勒飞粘度计dv2t型
硅烷封端聚醚树脂B：瑞洋安泰，3623T型号，20℃下的粘度为50000cps，粘度测试方法为:博勒飞粘度计dv2t型
硅烷封端聚醚树脂C：钟渊化学厂商，SAX750型号，20℃下的粘度为1000cps，粘度测试方法为:博勒飞粘度计dv2t型
硅烷封端聚醚树脂D：瑞洋安泰厂商，3000T型号，20℃下的粘度为80000cps，粘度测试方法为:博勒飞粘度计dv2t型
填料：纳米碳酸钙，市售。
实施例1
1)、改性长石粉的制备：将重量比为100:1.35的长石粉与硬脂酸混合均匀，加入清水，使得浆料浓度为12.8％(即长石粉与硬脂酸的占混合物的重量百分比为12.8％)，搅拌时间为2.5h,反应温度为45℃；抽滤、干燥后得到改性长石粉；长石粉活化指数由原来的0.0325上升到0.8,粘度降为60mPa.s,吸油量由原来的36.5g/100g降为28g/100g。
2)、改性高岭土的制备：
将高岭土进行烘干、粉磨预处理，粉磨后高岭土颗粒的比表面积为：6400cm2/g，然后将高岭土粉均匀撒在耐火匣钵中煅烧时，料层厚度为0.5cm，升温速度采用急剧升温到850℃，并在电炉内保温2min，急速冷却，粉碎得到改性高岭土，改性高岭土的比表面积为955cm2/g，吸油值16.2g/100g。
3)、按表1所示的重量份配料，然后按以下步骤制备接缝胶：
按表1所示的重量份将硅烷改性聚醚树脂(瓦克化学，XM-25型号)、改性长石粉、改性高岭土、除水剂、触变剂、偶联剂、催化剂、增塑剂、抗氧化剂、紫外线吸收剂、色注和填料混合，加热至110℃，恒温2h脱水，脱水过程分散盘高速1000r/min搅拌，同时真空度保持-0.09--0.1Mpa，即可得到接缝胶。
实施例2
1)、改性长石粉的制备：将重量比为100:1.15的长石粉与硬脂酸混合均匀，加入清水，使得浆料浓度为12.8％(即长石粉与硬脂酸的占混合物的重量百分比为12.8％)，搅拌时间为2.5h,反应温度为45℃；抽滤、干燥后得到改性长石粉；长石粉活化指数由原来的0.0325上升到0.88,粘度降为55mPa.s,吸油量由原来的36.5g/100g降为26.5g/100g。
2)、改性高岭土的制备：
将高岭土进行烘干、粉磨预处理，粉磨后高岭土颗粒的比表面积为：6400cm2/g，然后将高岭土粉均匀撒在耐火匣钵中煅烧时，料层厚度为0.5cm，升温速度采用急剧升温到850℃，并在电炉内保温2min，急速冷却，粉碎得到改性高岭土，改性高岭土的比表面积为955cm2/g，吸油值16.2g/100g。
3)、按表1所示的重量份配料，然后按以下步骤制备接缝胶：
按表1所示的重量份将硅烷改性聚醚树脂(瑞洋安泰，3623T型号)、改性长石粉、改性高岭土、除水剂、触变剂、偶联剂、催化剂、增塑剂、抗氧化剂、紫外线吸收剂、色注和填料混合，加热至105℃，恒温3h脱水，脱水过程分散盘高速500r/min搅拌，同时真空度保持-0.09--0.1Mpa，即可得到接缝胶。
实施例3
1)、改性长石粉的制备：将重量比为100:1.25的长石粉与硬脂酸混合均匀，加入清水，使得浆料浓度为12.8％(即长石粉与硬脂酸的占混合物的重量百分比为12.8％)，搅拌时间为2.5h,反应温度为45℃；抽滤、干燥后得到改性长石粉；长石粉活化指数由原来的0.0325上升到1,即为完全活化,粘度降为48mPa.s,吸油量由原来的36.5g/100g降为25g/100g。
2)、改性高岭土的制备：
将高岭土进行烘干、粉磨预处理，粉磨后高岭土颗粒的比表面积为：6400cm2/g，然后将高岭土粉均匀撒在耐火匣钵中煅烧时，料层厚度为0.5cm，升温速度采用急剧升温到850℃，并在电炉内保温2min，急速冷却，粉碎得到改性高岭土，改性高岭土的比表面积为955cm2/g，吸油值16.2g/100g。
3)、按表1所示的重量份配料，然后按以下步骤制备接缝胶：
按表1所示的重量份将硅烷改性聚醚树脂(瓦克化学，XM-25型号)、改性长石粉、改性高岭土、除水剂、触变剂、偶联剂、催化剂、增塑剂、抗氧化剂、紫外线吸收剂、色注和填料混合，加热至115℃，恒温2h脱水，脱水过程分散盘高速1500r/min搅拌，同时真空度保持-0.09--0.1Mpa，即可得到接缝胶。
对比例1
1)、改性高岭土的制备：
将高岭土进行烘干、粉磨预处理，粉磨后高岭土颗粒的比表面积为：6400cm2/g，然后将高岭土粉均匀撒在耐火匣钵中煅烧时，料层厚度为0.5cm，升温速度采用急剧升温到850℃，并在电炉内保温2min，急速冷却，粉碎得到改性高岭土，改性高岭土的比表面积为955cm2/g，吸油值16.2g/100g。
3)、按表1所示的重量份配料，然后按以下步骤制备接缝胶：
按表1所示的重量份将硅烷改性聚醚树脂(瓦克化学，XM-25型号)、长石粉、改性高岭土、除水剂、触变剂、偶联剂、催化剂、增塑剂、抗氧化剂、紫外线吸收剂、色注和填料混合，加热至110℃，恒温2h脱水，脱水过程分散盘高速1000r/min搅拌，同时真空度保持-0.09--0.1Mpa，即可得到接缝胶。
对比例2
1)、改性长石粉的制备：将重量比为100:1.35的长石粉与硬脂酸混合均匀，加入清水，使得浆料浓度为12.8％(即长石粉与硬脂酸的占混合物的重量百分比为12.8％)，搅拌时间为2.5h,反应温度为45℃；抽滤、干燥后得到改性长石粉；长石粉活化指数由原来的0.0325上升到0.8,即为完全活化,粘度降为60mPa.s,吸油量由原来的36.5g/100g降为28g/100g。
2)、按表1所示的重量份配料，然后按以下步骤制备接缝胶：
按表1所示的重量份将硅烷改性聚醚树脂(瓦克化学，XM-25型号)、改性长石粉、高岭土、除水剂、触变剂、偶联剂、催化剂、增塑剂、抗氧化剂、紫外线吸收剂、色注和填料混合，加热至110℃，恒温2h脱水，脱水过程分散盘高速1000r/min搅拌，同时真空度保持-0.09--0.1Mpa，即可得到接缝胶。
对比例3
1)、改性高岭土的制备：
将高岭土进行烘干、粉磨预处理，粉磨后高岭土颗粒的比表面积为：6400cm2/g，然后将高岭土粉均匀撒在耐火匣钵中煅烧时，料层厚度为0.5cm，升温速度采用急剧升温到850℃，并在电炉内保温2min，急速冷却，粉碎得到改性高岭土，改性高岭土比表面积为955cm2/g，吸油值16.2g/100g。
2)、按表1所示的重量份配料，然后按以下步骤制备接缝胶：
按表1所示的重量份将硅烷改性聚醚树脂(瓦克化学，XM-25型号)、改性高岭土、除水剂、触变剂、偶联剂、催化剂、增塑剂、抗氧化剂、紫外线吸收剂、色注和填料混合，加热至110℃，恒温2h脱水，脱水过程分散盘高速1000r/min搅拌，同时真空度保持-0.09--0.1Mpa，即可得到接缝胶。
对比例4
1)、改性长石粉的制备：将重量比为100:1.35的长石粉与硬脂酸混合均匀，加入清水，使得浆料浓度为12.8％(即长石粉与硬脂酸的占混合物的重量百分比为12.8％)，搅拌时间为2.5h,反应温度为45℃；抽滤、干燥后得到改性长石粉；长石粉活化指数由原来的0.0325上升到0.8,即为完全活化,粘度降为60mPa.s,吸油量由原来的36.5g/100g降为28g/100g。
2)、按表1所示的重量份配料，然后按以下步骤制备接缝胶：
按表1所示的重量份将硅烷改性聚醚树脂(瓦克化学，XM-25型号)、改性长石粉、除水剂、触变剂、偶联剂、催化剂、增塑剂、抗氧化剂、紫外线吸收剂、色注和填料混合，加热至110℃，恒温2h脱水，脱水过程分散盘高速1000r/min搅拌，同时真空度保持-0.09--0.1Mpa，即可得到接缝胶。
对比例5
1)、改性长石粉的制备：将重量比为100:1.35的长石粉与硬脂酸混合均匀，加入清水，使得浆料浓度为12.8％(即长石粉与硬脂酸的占混合物的重量百分比为12.8％)，搅拌时间为2.5h,反应温度为45℃；抽滤、干燥后得到改性长石粉；长石粉活化指数由原来的0.0325上升到0.8,即为完全活化,粘度降为60mPa.s,吸油量由原来的36.5g/100g降为28g/100g。
2)、改性高岭土的制备：
将高岭土进行烘干、粉磨预处理，粉磨后高岭土颗粒的比表面积为：6400cm2/g，然后将高岭土粉均匀撒在耐火匣钵中煅烧时，料层厚度为0.5cm，升温速度采用急剧升温到850℃，并在电炉内保温2min，急速冷却，粉碎得到改性高岭土，改性高岭土的比表面积为955cm2/g，吸油值16.2g/100g。
3)、按表1所示的重量份配料，然后按以下步骤制备接缝胶：
按表1所示的重量份将硅烷改性聚醚树脂(钟渊化学厂商，SAX750型号)、改性长石粉、改性高岭土、除水剂、触变剂、偶联剂、催化剂、增塑剂、抗氧化剂、紫外线吸收剂、色注和填料混合，加热至110℃，恒温2h脱水，脱水过程分散盘高速1000r/min搅拌，同时真空度保持-0.09--0.1Mpa，即可得到接缝胶。
对比例6
1)、改性长石粉的制备：将重量比为100:1.35的长石粉与硬脂酸混合均匀，加入清水，使得浆料浓度为12.8％(即长石粉与硬脂酸的占混合物的重量百分比为12.8％)，搅拌时间为2.5h,反应温度为45℃；抽滤、干燥后得到改性长石粉；长石粉活化指数由原来的0.0325上升到0.8,即为完全活化,粘度降为60mPa.s,吸油量由原来的36.5g/100g降为28g/100g。
2)、改性高岭土的制备：
将高岭土进行烘干、粉磨预处理，粉磨后高岭土颗粒的比表面积为：6400cm2/g，然后将高岭土粉均匀撒在耐火匣钵中煅烧时，料层厚度为0.5cm，升温速度采用急剧升温到850℃，并在电炉内保温2min，急速冷却，粉碎得到改性高岭土，改性高岭土的比表面积为955cm2/g，吸油值16.2g/100g。
3)、按表1所示的重量份配料，然后按以下步骤制备接缝胶：
按表1所示的重量份将硅烷改性聚醚树脂(瑞洋安泰厂商，3000T型号)、改性长石粉、改性高岭土、除水剂、触变剂、偶联剂、催化剂、增塑剂、抗氧化剂、紫外线吸收剂、色注和填料混合，加热至110℃，恒温2h脱水，脱水过程分散盘高速1000r/min搅拌，同时真空度保持-0.09--0.1Mpa，即可得到接缝胶。
对比例7
1)、改性长石粉的制备：将重量比为100:1.35的长石粉与硬脂酸混合均匀，加入清水，使得浆料浓度为12.8％(即长石粉与硬脂酸的占混合物的重量百分比为12.8％)，搅拌时间为2.5h,反应温度为45℃；抽滤、干燥后得到改性长石粉；长石粉活化指数由原来的0.0325上升到0.8,即为完全活化,粘度降为60mPa.s,吸油量由原来的36.5g/100g降为28g/100g。
2)、改性高岭土的制备：
将高岭土进行烘干、粉磨预处理，粉磨后高岭土颗粒的比表面积为：6400cm2/g，然后将高岭土粉均匀撒在耐火匣钵中煅烧时，料层厚度为0.5cm，升温速度采用急剧升温到850℃，并在电炉内保温2min，急速冷却，粉碎得到改性高岭土，改性高岭土的比表面积为955cm2/g，吸油值16.2g/100g。
3)、按表1所示的重量份配料，然后按以下步骤制备接缝胶：
按表1所示的重量份将硅烷改性聚醚树脂(瓦克化学，XM-25型号)、改性长石粉、改性高岭土、除水剂、触变剂、偶联剂、催化剂、增塑剂、抗氧化剂、紫外线吸收剂、色注和填料混合，加热至110℃，恒温2h脱水，脱水过程分散盘高速1000r/min搅拌，同时真空度保持-0.09--0.1Mpa，即可得到接缝胶。
表1实施例和对比例的原料表(单位：重量份)
将实施例与对比例制备的接缝胶按以下方法进行测试，并将结果列于表2中。
弹性恢复率：检测标准JCT 881-2017《混凝土接缝用密封胶》，(弹恢＞80％合格，且样件定伸无破坏)
拉伸模量：检测标准JCT 881-2017《混凝土接缝用密封胶》(模量＜0.4合格＝
定伸粘结性：检测标准JCT 881-2017《混凝土接缝用密封胶》
浸水后定伸粘结性：将接缝胶进行在23℃浸水4天，然后用定伸片进行100％定伸1天，即样件胶厚度12mm，拉伸到胶厚24mm,保持一天，然后按检测标准JCT 881-2017《混凝土接缝用密封胶》检测，观察样件是否破坏；
冷拉—热压后的粘结性：将接缝胶进行冷拉-热压处理后，然后按检测标准JCT881-2017《混凝土接缝用密封胶》检测,观察样件是否破坏。
其中冷拉-热压的处理步骤为：
具体步骤
①样件标况23℃放置28天
第一周：
①天，试件放入-20℃低温箱，3h后将样件从12mm拉伸至15mm,在-20℃下保持拉伸状态21h。
②天解除拉伸，试件放入70℃干燥箱，3h后将样件从12mm压缩至9mm,在70℃下保持拉伸状态21h。
③天，解除压缩，重复第①天步骤。
④天：同第②天步骤。
⑤-⑦天，解除压缩，试样标况23℃放置。
第二周：重复第一周步骤。
阻燃性能测试：ANSI/UL-94-1985。
表2实施例与对比例制备的接缝胶的性能测试结果
注：/表示待测件出现破坏，则弹恢无数据。
上述结果表明，本发明所述的接缝胶中，经过改性的长石粉和高岭土与特定粘度的硅烷改性聚醚树脂分子间作用力更强，制得的接缝胶粘结性能、弹性显著好于对比例，同时具备优异的防火阻燃能力。
对所公开的实施例的上述说明，使本领域专业技术人员能够实现或使用本发明。对这些实施例的多种修改对本领域的专业技术人员来说将是显而易见的，本文中所定义的一般原理可以在不脱离本发明的精神或范围的情况下，在其它实施例中实现。因此，本发明将不会被限制于本文所示的这些实施例，而是要符合与本文所公开的原理和新颖特点相一致的最宽的范围。
Claims (8)
1.一种低模量防火阻燃装配式建筑外墙接缝胶，其特征在于按其重量份包括以下成分：
硅烷改性聚醚树脂50-75份；
改性长石粉0-5份；
改性高岭土0-35份；
除水剂0-3份；
触变剂0-2份；
偶联剂0.1-3份；
催化剂0.1-2份；
增塑剂40份；
抗氧化剂1.5份；
紫外线吸收剂1份；
色料3份；
填料20份；
其中，所述改性长石粉、改性高岭土的用量均不为0；
所述改性长石粉是由长石粉经过200型硬脂酸改性制得，其制备步骤为：
将重量比为100:(1.15-1.35)的长石粉与200型硬脂酸混合均匀，加入清水，浆料浓度为12.8％，长石粉与硬脂酸的重量占混合物的比例为12.8％，搅拌2.5h,反应温度为45℃，抽滤、干燥后得到改性长石粉；
所述改性长石粉的活化指数为0.8-1，吸油值25g/100g-28g/100g。
2.如权利要求1所述的低模量防火阻燃装配式建筑外墙接缝胶，其特征在于所述改性高岭土的比表面积小于1000cm2/g，吸油值为15g/100g-18g/100g。
3.如权利要求1所述的低模量防火阻燃装配式建筑外墙接缝胶，其特征在于所述改性高岭土由以下步骤制得：
将高岭土进行烘干、粉磨预处理，然后将高岭土粉均匀撒在耐火匣钵中煅烧时，料层厚度为0.5cm，以50℃/min升温到850℃，并在电炉内保温2min，急速冷却，粉碎得到改性高岭土。
4.如权利要求1所述的低模量防火阻燃装配式建筑外墙接缝胶，其特征在于
所述硅烷改性聚醚树脂选自端基可水解的硅烷封端聚醚，20℃下的粘度为3000-50000cps；
所述硅烷封端聚醚树脂的结构式为：
其中，R2为R1或OR1，R1选自甲基或乙基。
5.如权利要求1所述的低模量防火阻燃装配式建筑外墙接缝胶，其特征在于：
所述增塑剂选自邻苯二甲酸二异壬酯、邻苯二甲酸二异癸酯和磷酸二苯基异癸酯中的至少一种；
所述抗氧化剂选自四[β-(3，5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯(IRGANOX1010)、β-(3,5-二叔丁基-4-羟基苯基)丙酸异辛醇酯(IRGANOX1135)和乙烯双(氧乙烯基)双[3-(5-叔丁基-4-羟基-间甲苯基)丙酸酯](IRGANOX245)中的至少一种；
所述紫外线吸收剂选自TINUVIN326、TINUVIN328、TINUVIN329、TINUVIN571、TINUVIN123、TINUVIN622、TINUVIN765、TINUVIN770、TINUVIN292、TINUVIN791和TINUVIN944中的至少一种。
6.如权利要求1所述的低模量防火阻燃装配式建筑外墙接缝胶，其特征在于：
所述填料选自纳米碳酸钙、轻质碳酸钙、重质碳酸钙和氢氧化铝中的至少一种。
7.如权利要求1所述的低模量防火阻燃装配式建筑外墙接缝胶，其特征在于：
所述色料选自钛白粉、炭黑和铁红中的至少一种；
所述触变剂选自聚酰胺蜡和/或氢化蓖麻油；
所述除水剂包括乙烯基三甲氧基硅烷；
所述偶联剂选自γ-氨丙基三甲氧基硅烷、N-β-(氨乙基)-γ-氨丙基三甲氧基硅烷、N-β-(氨乙基)-γ-氨丙基甲基二甲氧基硅烷、γ-缩水甘油醚氧丙基三甲氧基硅烷和甲基丙烯酰氧基丙基三甲氧基硅烷中的至少一种；
所述催化剂选自辛酸亚锡、二月桂酸二丁基锡和二正丁基双(乙酰丙酮基)锡中的至少一种。
8.一种如权利要求1-7任一项所述的低模量防火阻燃装配式建筑外墙接缝胶的制备方法：
按比例将硅烷改性聚醚树脂、改性长石粉、改性高岭土、除水剂、触变剂、偶联剂、催化剂、增塑剂、抗氧化剂、紫外线吸收剂、色料和填料混合，加热至105-115℃，恒温2-3h脱水，脱水过程分散盘高速500-1500r/min搅拌，同时真空度保持-0.09--0.1Mpa，即可得到接缝胶。