CN114163459B - 具有双罗丹明结构的热致变色材料、显色组合物及其制备方法和应用 - Google Patents

具有双罗丹明结构的热致变色材料、显色组合物及其制备方法和应用 Download PDF

Info

Publication number
CN114163459B
CN114163459B CN202210131654.2A CN202210131654A CN114163459B CN 114163459 B CN114163459 B CN 114163459B CN 202210131654 A CN202210131654 A CN 202210131654A CN 114163459 B CN114163459 B CN 114163459B
Authority
CN
China
Prior art keywords
compound
thermochromic material
preparation
butyl
mol
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN202210131654.2A
Other languages
English (en)
Other versions
CN114163459A (zh
Inventor
孟鸿
牟震
李炜
贺耀武
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhixiang Technology Co ltd
Peking University Shenzhen Graduate School
Lenovo Wanxiang Shenzhen Technology Co Ltd
Beijing Gaode Pinchuang Technology Co Ltd
Original Assignee
Peking University Shenzhen Graduate School
Lenovo Image Tianjin Technology Co Ltd
Lenovo Wanxiang Shenzhen Technology Co Ltd
Beijing Gaode Pinchuang Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Peking University Shenzhen Graduate School, Lenovo Image Tianjin Technology Co Ltd, Lenovo Wanxiang Shenzhen Technology Co Ltd, Beijing Gaode Pinchuang Technology Co Ltd filed Critical Peking University Shenzhen Graduate School
Priority to CN202210131654.2A priority Critical patent/CN114163459B/zh
Publication of CN114163459A publication Critical patent/CN114163459A/zh
Application granted granted Critical
Publication of CN114163459B publication Critical patent/CN114163459B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及热致变色材料技术领域，具体涉及一种具有双罗丹明结构的热致变色材料、显色组合物及其制备方法和应用。本发明提供的热致变色材料，具有如式Ⅰ所示的结构：

Description

具有双罗丹明结构的热致变色材料、显色组合物及其制备方 法和应用
技术领域
本发明涉及热致变色材料技术领域，具体涉及一种具有双罗丹明结构的热致变色材料、显色组合物及其制备方法和应用。
背景技术
压、热敏染料是功能性染料的一个重要门类，主要用于压、热敏复写纸的加工。在九十年代以前，全世界压、热敏染料的产量达3000多吨/年，主要分布于美国、欧洲、日本等地，其中日本产量最大，占世界总量的30%，压、热敏纸的年产量达100多万吨。随着工业的发社会的信息化，对压、热敏染料的需求不断上升，到九十年代中期，压热敏纸的年需求量已达25000吨。
热致变色是指化合物或混合物在受热或冷却时所发生的颜色变化的现象。具有热致变色特性的物质称为热致变色化合物。罗丹明类材料是一种典型的热致变色材料，在低温时提供电子给电子受体双酚A，内酯环打开，其结构交替烯共轭系统延长，产生深色位移而显示颜色；高温时，罗丹明类材料形成内酯环而显示为无色，其变色机理如下所示：
Figure 100002_DEST_PATH_IMAGE001
。
现有罗丹明类热致变色材料与酚类显色剂混合后为室温显色，高温下呈无色。在使用过程中需要将罗丹明类热致变色材料与酚类显色剂分别制备成微胶囊，两个微胶囊在高温下熔化混合后呈无色，恢复至室温后显色。至今未见罗丹明类热致变色材料与酚类显色剂混合后在室温下呈无色，高温显色的报道。然而在某些应用领域，例如防伪领域等，其需要热致变色产品在室温下呈现无色，而在加热至高温后进行显色，因此，获得一种在室温下呈现无色，高温下显色的热致变色材料成为一大研究热点。
发明内容
针对现有技术的不足，本发明的目的在于克服现有罗丹明类热致变色材料与酚类显色剂混合后为室温显色，高温下呈无色，且在实际使用过程中需要将罗丹明类热致变色材料与酚类显色剂分别制备成微胶囊，工艺繁琐的缺陷，进而提供一种具有双罗丹明结构的红外热致变色材料、显色组合物及其制备方法和应用。
本发明所采用的方案如下：
一种具有双罗丹明结构的热致变色材料，具有如下所示的结构：
Figure DEST_PATH_IMAGE002
式Ⅰ
其中，R1、R2相同或不同，分别独立的选自取代或未取代C1-C36的烷基、取代或未取代C6-C30的芳基；
R3，R4，R5和R6相同或不同，分别独立的选自氢、卤素、硝基、氰基、取代或未取代C1-C36的烷基、取代或未取代C6-C30的芳基；
B选自如下结构的基团：
Figure 100002_DEST_PATH_IMAGE003
，
其中 n≥0，每一个R相同或不同，各自独立选自氢、取代或未取代C1-C36的烷基、取代或未取代C6-C30的芳基、取代或未取代C3-C30的杂环基。
上述CnH2n+1为烷基，包括但不限于甲基、乙基、正丙基、异丙基、正丁基、异丁基、仲丁基、叔丁基、戊基、己基、庚基、辛基、壬基、癸基、十一烷基、十二烷基；
优选的，R1、R2相同或不同，分别独立的选自取代或未取代C1-C36的烷基；
R3，R4，R5和R6分别独立的选自氢、取代或未取代C1-C36的烷基。
优选的，R1、R2相同或不同，分别独立的选自甲基、乙基、正丙基、异丙基、正丁基、异丁基、仲丁基、叔丁基；
R3，R4，R5和R6相同或不同，分别独立的选自氢、甲基、乙基、正丙基、异丙基、正丁基、异丁基、仲丁基、叔丁基。
优选的，n选自0-50，每一个R相同或不同，各自独立选自氢、取代或未取代C1-C36的烷基、取代或未取代C6-C30的芳基。
优选的，n选自1-20，每一个R相同或不同，各自独立选自氢、甲基、乙基、正丙基、异丙基、正丁基、异丁基、仲丁基、叔丁基、戊基、己基、庚基、辛基、壬基、癸基、十一烷基、十二烷基、苯甲基、对甲氧基苄基、对三氟甲氧基苄基。可选的，n选自1、2、3、4、5、6、7、8、9、10、11、12、13、14、15、16、17、18、19、20。
优选的，所述取代的C1-C36的烷基、取代的C6-C30的芳基任选被一个或多个取代基Ra取代；每一个Ra独立的选自氢、卤素、硝基、氰基、甲基、乙基、正丙基、异丙基、正丁基、异丁基、仲丁基、叔丁基、苯基、萘基、蒽基、苯并蒽基、菲基、苯并菲基、联苯基、偶苯基、对甲氧基苯基、对三氟甲氧基苯基。
优选的，所述卤素为氟、氯、溴和碘；所述C1-C36的烷基选自甲基、乙基、正丙基、异丙基、正丁基、异丁基、仲丁基、叔丁基；C6-C30的芳基选自苯基、萘基、蒽基、苯并蒽基、菲基、苯并菲基、联苯基、偶苯基。
优选的，所述热致变色材料具有如下所示的结构：
Figure DEST_PATH_IMAGE004
Figure 100002_DEST_PATH_IMAGE005
Figure DEST_PATH_IMAGE006
Figure 100002_DEST_PATH_IMAGE007
Figure DEST_PATH_IMAGE008
可以理解的是上述-C10H21为癸基、-C12H25为十二烷基。
本发明还提供一种上述所述的热致变色材料的制备方法，包括如下步骤：
1）将i所示化合物与ii所示化合物反应得到iii所示化合物；
2）将iv所示化合物与v所示化合物通过偶联反应得到vi所示化合物；
3）将iii所示化合物与vi所示化合物反应得到式Ⅰ所示化合物；
所述式Ⅰ所示化合物的制备路径如下所示：
Figure DEST_PATH_IMAGE009
其中X为卤素，优选的，X为溴或氯。
可选的，步骤2）中所述偶联反应为suzuki偶联反应。
本发明还提供一种显色组合物，包括热致变色材料和酚类化合物，所述热致变色材料为上述所述的热致变色材料或上述所述制备方法制备得到的热致变色材料。
优选的，所述热致变色材料和酚类化合物的摩尔比为（0.1-1）：（0.1-10）；所述酚类化合物为双酚A化合物。
本发明还提供一种上述所述的显色组合物的制备方法，包括如下步骤：将热致变色材料和酚类化合物混合均匀即得。
本发明还提供一种上述所述的热致变色材料或上述所述制备方法制备得到的热致变色材料在制备压敏染料、热敏染料中的用途。
本发明还提供一种上述所述的显色组合物或上述所述的制备方法制备得到的显色组合物在制备压敏染料、热敏染料中的用途。
本发明还提供一种上述所述的热致变色材料或上述所述制备方法制备得到的热致变色材料或上述所述的显色组合物或上述所述的制备方法制备得到的显色组合物在防伪领域中的应用。
本发明的有益效果：
1）本发明提供的具有双罗丹明结构的热致变色材料，具有式Ⅰ所示的结构，通过特定结构的B基团将双罗丹明结构进行键联，使材料室温下与酚类显色剂接触也不显色，加热后形成内酯环，吸收峰蓝移至可见区而显色，降温后又恢复至无色，同时获得了较高的变色温度。本发明提供的热致变色材料可应用于防伪领域，在实际使用过程中，无需按传统方法制备成胶囊，热致变色材料与酚类显色剂直接混合即可，工艺简单，制备方便。
2）本发明提供的具有双罗丹明结构的红外热致变色材料，进一步的，通过调控R1，R2， R3，R4，R5，R6和R基团，同双罗丹明结构和B基团相互作用，在实现使材料室温呈现为无色，加热后呈现出有色，降温后又恢复至无色的同时，还获得了较高的变色温度，使其更利于应用到特定变色温度需要的产品中。
具体实施方式
提供下述实施例是为了更好地进一步理解本发明，并不局限于所述最佳实施方式，不对本发明的内容和保护范围构成限制，任何人在本发明的启示下或是将本发明与其他现有技术的特征进行组合而得出的任何与本发明相同或相近似的产品，均落在本发明的保护范围之内。
实施例中未注明具体实验步骤或条件者，按照本领域内的文献所描述的常规实验步骤的操作或条件即可进行。所用试剂或仪器未注明生产厂商者，均为可以通过市购获得的常规试剂产品。
实施例1
本实施例提供一种热致变色材料II-1-1，化合物II-1-1的合成路径如下所示：
Figure DEST_PATH_IMAGE010
；
化合物II-1-1的制备方法具体包括以下步骤：
1）148 g(1.0 mol)邻苯二甲酸酐(A)和165 g (1.0 mol) 3-二乙基氨基苯酚(B)溶解在1500 mL甲苯中，氮气条件下加热回流4 h，再滴加 200 mL20 mol/L的氢氧化钠溶液之后，100℃下加热4 小时。反应结束后，反应混合物倒入冰水中，用盐酸中和，用氯仿萃取，合并有机相，用无水硫酸钠干燥，浓缩除去溶剂之后得到粗品，粗产品用二氯甲烷/石油醚重结晶得到286 g的化合物2-(4-二乙基氨基-2-羟基苯甲酰基)-苯甲酸(C)。
化合物C核磁数据：1H NMR (300 MHz, CDCl3) δ 8.45 (d, J = 14.5, 1H), 8.11(d, J = 14.5, 1H), 7.94 (t, J = 14.6 Hz, 1H), 7.81 (t, J = 14.6 Hz, 1H), 7.14(d, J = 14.6 Hz, 1H), 6.45 (d, J = 14.7 Hz, 1H), 6.31 (s, 1H), 3.38 (q, J =12.3 Hz, 4H), 1.08 (t, J = 12.3 Hz, 6H). 13C NMR (75 MHz, CDCl3) δ 198.28,169.20, 164.26, 156.76, 138.16, 132.93, 132.82, 131.36, 130.28, 129.87,127.31, 107.46, 103.74, 96.78, 46.42, 12.99。
2）147 g (0.5 mol)的4,7-二溴苯并噻二唑(i-1)与 206.9 g(1.5 mol)间羟基苯硼酸(D)溶解在1000 mL 甲苯中，加入600 mL 2 mol/L的碳酸钾水溶液，用氮气吹洗30min，加入20 mmolPd(PPh3)4，在氮气环境下加热回流搅拌，TLC监测反应完全，冷却，反应液用二氯甲烷萃取三次，合并有机相，干燥浓缩，进一步用二氯甲烷与石油醚为洗脱剂柱层析得到136 g的关键中间体化合物4,7-二(3′-羟基苯基) 苯并噻二唑(i-2)。
化合物i-2核磁数据：1H NMR (300 MHz, CDCl3) δ 7.74 (s, 2H), 7.31 (t, J =14.6 Hz, 2H), 7.19 (s, 2H), 7.05 (d, J = 14.7 Hz, 2H), 6.75 (d, J = 14.5,2H). 13C NMR (75 MHz, CDCl3) δ 160.45, 157.67, 134.44, 129.47, 126.21, 121.99,119.76, 119.34, 112.56。
3）78.3 g (0.25 mol) 2-(4-二乙基氨基-2-羟基苯甲酰基)-苯甲酸(C)和32 g(0.1 mol) 4,7-二(3′-羟基苯基) 苯并噻二唑(i-2)，再加入200 mL 85%的硫酸，在120℃温度下搅拌加热6小时，冷却至室温之后，倒入冰水中，用2 mol/L的氢氧化钠溶液中和，过滤，滤饼分散到300 mL甲苯和150 mL 2mol/L的氢氧化钠溶液中，120℃下搅拌3小时，分液，有机相用无水硫酸钠干燥，浓缩，得粗产品，粗产品用二氯甲烷和石油醚重结晶得56 g 目标化合物 (II-1-1) 。
化合物II-1-1核磁数据： 1H NMR (300 MHz, CDCl3) δ 7.94 (d, J = 14.4 Hz,1H), 7.75 (s, 1H), 7.45 (m, 6H), 7.08 (d, J = 14.6 Hz, 1H), 6.35 (d, J = 14.7Hz, 1H), 6.23 (s, 1H), 3.31 (q, J = 12.3 Hz, 4H), 1.18 (t, J = 12.3 Hz, 6H). 13C NMR (75 MHz, CDCl3) δ 171.05, 160.45, 154.86, 153.15, 152.97, 146.64,137.50, 133.54, 129.90, 128.13, 128.13, 127.39, 127.10, 126.21, 125.40,124.87, 123.39, 121.99, 117.66, 108.26, 106.73, 98.85, 86.94, 46.42, 12.99。
实施例2
本实施例提供一种热致变色材料II-2-1，化合物II-2-1的合成路径如下所示：
Figure DEST_PATH_IMAGE011
；
化合物II-2-1的制备方法具体包括以下步骤：
1）化合物C的制备同实施例1；
2）176 g (0.5 mol)的4,7-二溴苯并〔1,2-c:4,5-c'的]双（[1,2,5]噻二唑(ii-1)与206.9 g(1.5 mol)间羟基苯硼酸(D)溶解在1000 mL 甲苯中，加入600 mL 2 mol/L的碳酸钾水溶液，用氮气吹洗30 min，加入20 mmol Pd(PPh3)4，在氮气环境下加热回流搅拌，TLC监测反应完全，冷却，反应液用二氯甲烷萃取三次，合并有机相，干燥浓缩，进一步用二氯甲烷与石油醚为洗脱剂柱层析得到163 g的关键中间体化合物4,7-二(3′-羟基苯基) 苯并[1,2-c:4,5-c']双（[1,2,5]噻二唑(ii-2)。
3）78.3 g (0.25 mol) 2-(4-二乙基氨基-2-羟基苯甲酰基)-苯甲酸(C)和37.8 g(0.1 mol) 4,7-二(3′-羟基苯基)苯并〔1,2-c:4,5-c'的]双（[1,2,5]噻二唑(ii-2)，再加入200 mL 85%的硫酸，在120℃温度下搅拌加热6小时，冷却至室温之后，倒入冰水中，用2mol/L的氢氧化钠溶液中和，过滤，滤饼分散到300 mL甲苯和150 mL 2mol/L的氢氧化钠溶液中，120℃下搅拌3小时，分液，有机相用无水硫酸钠干燥，浓缩，得粗产品，粗产品用二氯甲烷和石油醚重结晶得69 g 目标化合物 (II-2-1) 。
化合物II-2-1核磁数据：1H NMR (300 MHz, CDCl3) δ 7.89 (d, J = 14.4 Hz,2H), 7.45 (m, 10H), 7.31 (d, J = 14.6 Hz, 2H), 7.11 (d, J = 14.6 Hz, 2H),6.41 (d, J = 14.7 Hz, 2H), 6.25 (s, 2H), 3.38 (q, J = 12.3 Hz, 8H), 1.18 (t,J = 12.3 Hz, 12H). 13C NMR (75 MHz, CDCl3) δ 171.06, 154.86, 154.25, 152.97,151.51, 149.91, 146.64, 133.53, 133.15, 129.89, 128.13, 127.10, 127.04,124.87, 122.69, 122.46, 114.28, 113.83, 108.26, 106.73, 98.85, 86.94, 46.42,12.99。
实施例3
本实施例提供一种热致变色材料II-3-1，化合物II-3-1的合成路径如下所示：
Figure DEST_PATH_IMAGE012
Figure 322014DEST_PATH_IMAGE013
；
化合物II-3-1的制备方法具体包括以下步骤：
1）化合物C的制备同实施例1；
2）208.6 g (0.5 mol)的4, 7-二溴-2-(辛基)-2H-苯并三氮唑(iii-1)与 206.9g(1.5 mol)间羟基苯硼酸(D)溶解在1000 mL 甲苯中，加入600 mL 2 mol/L的碳酸钾水溶液，用氮气吹洗30 min，加入20 mmolPd(PPh3)4，在氮气环境下加热回流搅拌，TLC监测反应完全，冷却，反应液用二氯甲烷萃取三次，合并有机相，干燥浓缩，进一步用二氯甲烷与石油醚为洗脱剂柱层析得到196 g的化合物4,7-二(3′-羟基苯基)-2-(辛基)-2H-苯并三氮唑(iii-2)。
化合物iii-2核磁数据：1H NMR (300 MHz, CDCl3) δ 7.88 (s, 2H), 7.31 (t, J= 14.6 Hz, 2H), 7.11 (s, 2H), 7.02 (d, J = 14.7 Hz, 2H), 6.77 (d, J = 14.5Hz, 2H), 4.12 (t, J = 11.2 Hz, 2H), 1.95 (m, 2H), 1.35 (m, 14H), 0.88 (m,3H). 13C NMR (75 MHz, CDCl3) δ 157.67, 147.62, 134.44, 129.47, 128.88, 119.76,119.34, 117.13, 112.56, 54.95, 31.73, 29.15, 29.04, 27.64, 26.02, 23.16,14.00。
3）78.3 g (0.25 mol) 2-(4-二乙基氨基-2-羟基苯甲酰基)-苯甲酸(C)和44.3g(0.1 mol) 4,7-二(3′-羟基苯基) -2-(辛基)-2H-苯并三氮唑(iii-2)，再加入200 mL 85%的硫酸，在120℃温度下搅拌加热6小时，冷却至室温之后，倒入冰水中，用2 mol/L的氢氧化钠溶液中和，过滤，滤饼分散到300 mL甲苯和150 mL 2mol/L的氢氧化钠溶液中，120℃下搅拌3小时，分液，有机相用无水硫酸钠干燥，浓缩，得粗产品，粗产品用二氯甲烷和石油醚重结晶得56 g 目标化合物 (II-3-1) 。
化合物II-3-1核磁数据：1H NMR (300 MHz, CDCl3) δ 7.89 (s, 2H), 7.81 (d,J = 14.4 Hz, 2H), 7.46 (m, 10H), 7.31 (d, J = 14.7 Hz, 2H), 7.12 (d, J = 14.7Hz, 2H), 6.41 (d, J = 14.7 Hz, 2H), 6.24 (s, 2H), 4.13 (t, J = 14.9 Hz, 2H),3.35 (q, J = 12.3 Hz, 8H), 1.94 (m, 2H), 1.31 (m, 14H), 1.12 (m, 12H), 0.88(m, 3H). 13C NMR (75 MHz, CDCl3) δ 171.05, 154.86, 153.15, 152.97, 147.62,146.64, 137.50, 133.54, 129.90, 128.88, 128.13, 128.13, 127.39, 127.10,125.40, 124.87, 123.39, 117.66, 117.13, 108.26, 106.73, 98.85, 86.94, 54.95,46.42, 31.73, 29.15, 29.04, 27.64, 26.02, 23.16, 14.00, 12.99。
实施例4
本实施例提供一种热致变色材料II-4-1，化合物II-4-1的合成路径如下所示：
Figure DEST_PATH_IMAGE014
Figure DEST_PATH_IMAGE015
Figure DEST_PATH_IMAGE016
；
化合物II-4-1的制备方法具体包括以下步骤：
1）化合物C的制备同实施例1；
2）329g (0.5 mol)的1,3-二溴-5,7-双(辛基)苯并[1,2-C:4,5-C']二噻吩-4,8-二酮(iv-1)与 206.9 g(1.5 mol)间羟基苯硼酸(D)溶解在1000 mL 甲苯中，加入600 mL 2mol/L的碳酸钾水溶液，用氮气吹洗30 min，加入20 mmolPd(PPh3)4，在氮气环境下加热回流搅拌，TLC监测反应完全，冷却，反应液用二氯甲烷萃取三次，合并有机相，干燥浓缩，进一步用二氯甲烷与石油醚为洗脱剂柱层析得到196 g的化合物1,3-二(3′-羟基苯基)- 5,7-双(辛基)苯并[1,2-C:4,5-C']二噻吩-4,8-二酮(iv-2)。
化合物iv-2核磁数据：1H NMR (300 MHz, CDCl3) δ 7.41 (d, J = 14.5 Hz,2H), 7.19 (t, J = 14.5 Hz, 2H), 7.05 (s, 2H), 6.77 (d, J = 14.3 Hz, 2H), 2.74(t, J = 15.3 Hz, 4H), 1.71 (m, 4H), 1.31 (m, 30H), 0.89 (m, 6H). 13C NMR (75MHz, CDCl3) δ 172.36, 157.14, 153.16, 139.56, 137.94, 132.95, 128.45, 125.79,121.00, 119.69, 114.20, 31.73, 29.15, 29.04, 29.02, 28.35, 27.69, 23.16,14.00。
3）78.3 g (0.25 mol) 2-(4-二乙基氨基-2-羟基苯甲酰基)-苯甲酸(C)和68.4g(0.1 mol) 1,3-二(3′-羟基苯基)- 5,7-双(辛基)苯并[1,2-C:4,5-C']二噻吩-4,8-二酮(iv-2)，再加入200 mL 85%的硫酸，在120℃温度下搅拌加热6小时，冷却至室温之后，倒入冰水中，用2 mol/L的氢氧化钠溶液中和，过滤，滤饼分散到300 mL甲苯和150 mL 2mol/L的氢氧化钠溶液中，120℃下搅拌3小时，分液，有机相用无水硫酸钠干燥，浓缩，得粗产品，粗产品用二氯甲烷和石油醚重结晶得72 g 目标化合物 (II-4-1) 。
化合物II-4-1核磁数据：1H NMR (300 MHz, CDCl3) δ 7.85 (d, J = 14.4 Hz,2H), 7.42 (m, 12H), 7.08 (d, J = 14.7 Hz, 2H), 6.41 (d, J = 14.7 Hz, 2H),6.25 (s, 2H), 3.31 (q, J = 12.3 Hz, 8H), 2.69 (m, 4H), 1.73 (m, 4H), 1.24 (m,29H), 1.14 (t, J = 12.3 Hz, 12H), 0.87 (m, 6H). 13C NMR (75 MHz, CDCl3) δ172.36, 171.05, 154.86, 153.16, 152.97, 150.12, 146.64, 139.56, 133.54,132.95, 132.88, 129.90, 128.13, 128.13, 127.10, 126.86, 125.79, 125.11,124.99, 124.87, 113.14, 108.26, 106.73, 98.85, 86.94, 46.42, 31.73, 29.15,29.04, 29.02, 28.35, 27.69, 23.16, 14.00, 12.99。
实施例5
本实施例提供一种热致变色材料II-5-1，化合物II-5-1的合成路径如下所示：
Figure DEST_PATH_IMAGE017
；
化合物II-5-1的制备方法具体包括以下步骤：
1）化合物C的制备同实施例1；
2）198.5 g (0.5 mol)的3,6-二溴邻苯二甲辛基酰亚胺(v-1)与206.9g (1.5mol)间羟基苯硼酸(D)溶解在1000 mL 甲苯中，加入600 mL 2 mol/L的碳酸钾水溶液，用氮气吹洗30 min，加入20 mmol Pd(PPh3)4，在氮气环境下加热回流搅拌，TLC监测反应完全，冷却，反应液用二氯甲烷萃取三次，合并有机相，干燥浓缩，进一步用二氯甲烷与石油醚为洗脱剂柱层析得到251 g的化合物3,6-(3′-羟基苯基)邻苯二甲苄基酰亚胺(v-2) 。
化合物v-2核磁数据：1H NMR (300 MHz, CDCl3) δ 8.43 (s, 2H), 7.35 (m,7H), 7.11 (s, 2H), 7.02 (d, J = 14.7 Hz, 2H), 6.77 (d, J = 14.5 Hz, 2H), 4.75(s, 2H). 13C NMR (75 MHz, CDCl3) δ 173.94, 156.32, 143.88, 140.65, 136.93,136.16, 133.43, 128.94, 128.53, 128.41, 128.04, 118.25, 116.46, 114.03,44.51。
3）78.3 g (0.25 mol) 2-(4-二乙基氨基-2-羟基苯甲酰基)-苯甲酸(C)和42.1 g(0.1 mol) 3,6-(3′-羟基苯基)邻苯二甲苄基酰亚胺(v-2)，再加入200 mL 85%的硫酸，在120℃温度下搅拌加热6小时，冷却至室温之后，倒入冰水中，用2 mol/L的氢氧化钠溶液中和，过滤，滤饼分散到300 mL甲苯和150 mL 2mol/L的氢氧化钠溶液中，120℃下搅拌3小时，分液，有机相用无水硫酸钠干燥，浓缩，得粗产品，粗产品用二氯甲烷和石油醚重结晶得81g目标化合物 (II-5-1) 。
化合物II-5-1核磁数据：1H NMR (300 MHz, CDCl3) δ 8.41 (s, 2H), 7.89 (d,J = 14.4 Hz, 2H), 7.37 (m, 17H), 7.10 (d, J = 14.6 Hz, 2H), 6.45 (d, J = 14.7Hz, 2H), 6.23 (s, 2H), 4.79 (s, 2H), 3.35 (q, J = 12.3 Hz, 8H), 1.15 (t, J =12.3 Hz, 12H). 13C NMR (75 MHz, CDCl3)δ 173.94, 171.05, 154.86, 152.97,151.60, 146.64, 143.88, 140.35, 136.93, 136.16, 133.54, 133.43, 129.90,128.53, 128.41, 128.13, 128.13, 128.04, 127.38, 127.10, 124.87, 124.76,124.25, 114.20, 108.26, 106.73, 98.85, 86.94, 46.42, 44.51, 12.99。
实施例6
本实施例提供一种热致变色材料II-6-1，化合物II-6-1的合成路径如下所示：
Figure DEST_PATH_IMAGE018
Figure DEST_PATH_IMAGE019
；
化合物II-6-1的制备方法具体包括以下步骤：
1）化合物C的制备同实施例1；
2）319.7g (0.5 mol)的苯并噻二唑三唑-噻吩-双溴(vi-1)与 206.9 g(1.5 mol)间羟基苯硼酸(D)溶解在1000 mL 甲苯中，加入600 mL 2 mol/L的碳酸钾水溶液，用氮气吹洗30 min，加入20 mmolPd(PPh3)4，在氮气环境下加热回流搅拌，TLC监测反应完全，冷却，反应液用二氯甲烷萃取三次，合并有机相，干燥浓缩，进一步用二氯甲烷与石油醚为洗脱剂柱层析得到294 g的化合物 二(3′-羟基苯基噻吩) 苯并噻二唑三唑(vi-2)。
3）78.3 g (0.25 mol) 2-(4-二乙基氨基-2-羟基苯甲酰基)-苯甲酸(C)和66.5 g(0.1 mol) 二(3′-羟基苯基噻吩) 苯并噻二唑三唑(vi-2)，再加入200 mL 85%的硫酸，在120℃温度下搅拌加热6小时，冷却至室温之后，倒入冰水中，用2 mol/L的氢氧化钠溶液中和，过滤，滤饼分散到300 mL甲苯和150 mL 2mol/L的氢氧化钠溶液中，120℃下搅拌3小时，分液，有机相用无水硫酸钠干燥，浓缩，得粗产品，粗产品用二氯甲烷和石油醚重结晶得81g 目标化合物 (II-6-1) 。
化合物II-6-1核磁数据：1H NMR (300 MHz, CDCl3) δ 7.94 (d, J = 14.4 Hz,2H), 7.45 (m, 10H), 7.31 (d, J = 14.6 Hz, 2H), 7.11 (d, J = 14.6 Hz, 2H),6.39 (d, J = 14.7 Hz, 2H), 6.25 (s, 2H), 4.11 (t, J = 15.3 Hz, 2H), 3.38 (q,J = 12.3 Hz, 8H), 1.91 (m, 2H), 1.29 (m, 13H), 1.14 (t, J = 12.3 Hz, 12H),0.87 (m, 3H). 13C NMR (75 MHz, CDCl3) δ 171.05, 154.86, 152.97, 151.51,146.64, 142.82, 140.80, 133.54, 133.15, 129.90, 128.13, 128.13, 127.10,127.04, 124.87, 122.69, 122.46, 114.29, 109.21, 108.26, 106.73, 98.85, 86.94,54.95, 46.42, 31.73, 29.15, 29.04, 27.64, 26.02, 23.16, 14.00, 12.99。
实施例7
本实施例提供一种热致变色材料II-7-1，化合物II-7-1的合成路径如下所示：
Figure DEST_PATH_IMAGE020
；
化合物II-7-1的制备方法具体包括以下步骤：
1）化合物C的制备同实施例1；
2）200.5 g (0.5 mol)的2,5-二溴-N-苄基-3,4-噻吩二甲酰亚胺(vii-1)与206.9 g(1.5 mol)间羟基苯硼酸(D)溶解在1000 mL 甲苯中，加入600 mL 2 mol/L的碳酸钾水溶液，用氮气吹洗30 min，加入20 mmolPd(PPh3)4，在氮气环境下加热回流搅拌，TLC监测反应完全，冷却，反应液用二氯甲烷萃取三次，合并有机相，干燥浓缩，进一步用二氯甲烷与石油醚为洗脱剂柱层析得到275 g的关键中间体化合物2,5-(3′-羟基苯基)-N-苄基-3,4-噻吩二甲酰亚胺(vii-2)。
化合物vii-2核磁数据：1H NMR (300 MHz, CDCl3) δ 7.35 (m, 6H), 6.89 (d, J= 14.3 Hz, 1H), 4.61 (s, 1H). 13C NMR (75 MHz, CDCl3) δ 164.34, 157.74,137.19, 136.93, 136.58, 129.57, 128.53, 128.41, 128.04, 125.84, 121.61,118.38, 114.60, 44.20。
3）78.3 g (0.25 mol) 2-(4-二乙基氨基-2-羟基苯甲酰基)-苯甲酸(C)和42.7g(0.1 mol) 2,5-(3′-羟基苯基)-N-苄基-3,4-噻吩二甲酰亚胺(vii-2)，再加入200 mL 85%的硫酸，在120℃温度下搅拌加热6小时，冷却至室温之后，倒入冰水中，用2 mol/L的氢氧化钠溶液中和，过滤，滤饼分散到300 mL甲苯和150 mL 2mol/L的氢氧化钠溶液中，120℃下搅拌3小时，分液，有机相用无水硫酸钠干燥，浓缩，得粗产品，粗产品用二氯甲烷和石油醚重结晶得46g 目标化合物 (II-7-1) 。
化合物II-7-1核磁数据：1H NMR (300 MHz, CDCl3) δ 7.92 (d, J = 14.4 Hz,2H), 7.41 (m, 17H), 7.08 (d, J = 14.6 Hz, 2H), 6.39 (d, J = 14.7 Hz, 2H),6.21 (s, 2H), 4.62 (s, 2H), 3.37 (q, J = 12.3 Hz, 8H), 1.15 (t, J = 12.3 Hz,12H). 13C NMR (75 MHz, CDCl3) δ 171.05, 164.34, 154.86, 152.97, 152.56,146.64, 136.93, 136.58, 135.66, 133.54, 129.90, 128.53, 128.41, 128.13,128.13, 128.04, 127.10, 126.09, 125.84, 125.81, 124.87, 123.35, 110.21,108.26, 106.73, 98.85, 86.94, 46.42, 44.20, 12.99。
实施例8
本实施例提供一种热致变色材料II-8-1，化合物II-8-1的合成路径如下所示：
Figure DEST_PATH_IMAGE021
Figure DEST_PATH_IMAGE022
；
化合物II-8-1的制备方法具体包括以下步骤：
1）化合物C的制备同实施例1；
2）387 g (0.5 mol)的2,5-对三氟甲氧基苄基-3,6-二(5-溴呋喃基-2-)-吡咯并吡咯二酮与 206.9 g(1.5 mol)间羟基苯硼酸(D)溶解在1000 mL 甲苯中，加入600 mL 2mol/L的碳酸钾水溶液，用氮气吹洗30 min，加入20 mmolPd(PPh3)4，在氮气环境下加热回流搅拌，TLC监测反应完全，冷却，反应液用二氯甲烷萃取三次，合并有机相，干燥浓缩，进一步用二氯甲烷与石油醚为洗脱剂柱层析得到382 g的中间体化合物2,5-对三氟甲氧基苄基-3,6-二(5-(3′-羟基苯基)呋喃基-2-)-吡咯并吡咯二酮(viii-2)。
化合物viii-2核磁数据：1H NMR (300 MHz, CDCl3) δ 7.65 (d, J = 14.7 Hz,1H), 7.37 (d, J = 14.7 Hz, 1H), 7.31 (m, 2H), 7.08 (m, 3H), 6.89 (m, 2H),6.78 (d, J = 14.5, Hz, 1H), 4.27 (s, 2H). 13C NMR (75 MHz, CDCl3) δ 161.05,157.04, 151.99, 150.70, 145.65, 141.15, 132.49, 132.09, 130.34, 129.54,121.36, 120.22, 120.06, 119.55, 118.68, 112.57, 108.98, 100.19, 48.38。
3）78.3 g (0.25 mol) 2-(4-二乙基氨基-2-羟基苯甲酰基)-苯甲酸(C)和80 g(0.1 mol) 2,5-对三氟甲氧基苄基-3,6-二(5-(3′-羟基苯基)呋喃基-2-)-吡咯并吡咯二酮(viii-2)，再加入200 mL 85%的硫酸，在120℃温度下搅拌加热6小时，冷却至室温之后，倒入冰水中，用2 mol/L的氢氧化钠溶液中和，过滤，滤饼分散到300 mL甲苯和150 mL2mol/L的氢氧化钠溶液中，120℃下搅拌3小时，分液，有机相用无水硫酸钠干燥，浓缩，得粗产品，粗产品用二氯甲烷和石油醚重结晶得105 g 目标化合物 (II-8-1) 。
化合物II-8-1核磁数据：1H NMR (300 MHz, CDCl3) δ 7.84 (d, J = 14.3 Hz,2H), 7.41 (m, 14H), 7.19 (d, J = 14.7 Hz, 2H), 6.82 (m, 4H), 6.37 (d, J =14.6 Hz, 2H), 6.25 (s, 2H), 4.26 (s, 4H), 3.38 (q, J = 12.3 Hz, 8H), 1.15 (t,J = 12.3 Hz, 12H). 13C NMR (75 MHz, CDCl3) δ 171.05, 161.05, 154.86, 152.97,152.80, 151.99, 150.70, 146.64, 145.65, 141.15, 135.88, 133.54, 132.09,129.90, 129.54, 128.13, 128.13, 127.10, 126.65, 124.87, 123.94, 122.91,121.36, 120.22, 119.55, 109.90, 108.98, 108.26, 106.73, 100.19, 98.85, 86.94,48.38, 46.42, 12.99。
实施例9
本实施例提供一种热致变色材料II-9-1，化合物II-9-1的合成路径如下所示：
Figure DEST_PATH_IMAGE023
Figure DEST_PATH_IMAGE024
；
化合物II-9-1的制备方法具体包括以下步骤：
1）化合物C的制备同实施例1；
2）369 g (0.5 mol)的3,6-双(5-溴-2-噻吩基)-2,5-二氢-2,5-二癸基吡咯并[3,4-C]吡咯-1,4-二酮与 206.9 g(1.5 mol)间羟基苯硼酸(D)溶解在1000 mL 甲苯中，加入600 mL 2 mol/L的碳酸钾水溶液，用氮气吹洗30 min，加入20 mmolPd(PPh3)4，在氮气环境下加热回流搅拌，TLC监测反应完全，冷却，反应液用二氯甲烷萃取三次，合并有机相，干燥浓缩，进一步用二氯甲烷与石油醚为洗脱剂柱层析得到296 g的中间体化合物3,6-双(5-(3′-羟基苯基)-2-噻吩基)-2,5-二氢-2,5-二癸基吡咯并[3,4-C]吡咯-1,4-二酮(ix-2)。
化合物ix-2核磁数据：1H NMR (300 MHz, CDCl3) δ 8.17 (d, J = 14.7 Hz,2H), 7.83 (d, J = 14.7 Hz, 2H), 7.31 (m, 6H), 6.85 (d, J = 14.3 Hz, 2H), 3.42(t, J = 14.5 Hz, 4H), 1.65 (m, 4H), 1.31 (m, 29H), 87 (m, 6H). 13C NMR (75MHz, CDCl3) δ 160.90, 157.28, 143.49, 142.62, 137.84, 133.72, 129.97, 123.11,120.78, 119.38, 118.53, 113.58, 108.77, 44.91, 31.73, 29.15, 29.04, 28.85,27.64, 23.16, 14.00。
3）78.3 g (0.25 mol) 2-(4-二乙基氨基-2-羟基苯甲酰基)-苯甲酸(C)和76.5 g(0.1 mol) 3,6-双(5-(3′-羟基苯基)-2-噻吩基)-2,5-二氢-2,5-二癸基吡咯并[3,4-C]吡咯-1,4-二酮(ix-2)，再加入200 mL 85%的硫酸，在120℃温度下搅拌加热6小时，冷却至室温之后，倒入冰水中，用2 mol/L的氢氧化钠溶液中和，过滤，滤饼分散到300 mL甲苯和150mL 2mol/L的氢氧化钠溶液中，120℃下搅拌3小时，分液，有机相用无水硫酸钠干燥，浓缩，得粗产品，粗产品用二氯甲烷和石油醚重结晶得96 g 目标化合物 (II-9-1) 。
化合物II-9-1核磁数据：1H NMR (300 MHz, CDCl3) δ 8.23 (d, J = 7.2 Hz,2H), 7.85 (m, 4H), 7.37 (m, 12H), 7.13 (d, J = 7.2 Hz, 2H), 6.41 (d, J = 7.2Hz, 2H), 6.25 (s, 2H), 3.45 (t, J = 7.0 Hz, 4H), 3.38 (q, J = 5.9 Hz, 8H),1.61 (m, 4H), 1.25 (m, 31H), 1.15 (t, J = 6.0 Hz, 12H), 0.87 (m, 6H). 13C NMR(75 MHz, CDCl3) δ 171.05, 160.90, 154.86, 152.97, 152.42, 146.64, 143.49,142.62, 139.86, 133.72, 133.54, 129.90, 128.13, 128.13, 127.10, 126.81,124.87, 123.58, 123.11, 122.11, 119.38, 110.31, 108.77, 108.26, 106.73,98.85, 86.94, 46.42, 44.91, 31.73, 29.15, 29.04, 28.85, 27.64, 23.16, 14.00,12.99。
实施例10
本实施例提供一种热致变色材料II-10-1，化合物II-10-1的合成路径如下所示：
Figure DEST_PATH_IMAGE025
Figure DEST_PATH_IMAGE026
Figure DEST_PATH_IMAGE027
；
化合物II-10-1的制备方法具体包括以下步骤：
1）化合物C的制备同实施例1；
2）391 g (0.5 mol)的3,6-双对溴苯基-2,5-二氢-2,5-双十二烷基吡咯并[3,4-C]吡咯-1,4-二酮与 206.9 g(1.5 mol)间羟基苯硼酸(D)溶解在1000 mL 甲苯中，加入600mL 2 mol/L的碳酸钾水溶液，用氮气吹洗30 min，加入20 mmolPd(PPh3)4，在氮气环境下加热回流搅拌，TLC监测反应完全，冷却，反应液用二氯甲烷萃取三次，合并有机相，干燥浓缩，进一步用二氯甲烷与石油醚为洗脱剂柱层析得到329 g的中间体化合物3,6-双对(3′-羟基苯基)苯基-2,5-二氢-2,5-双十二烷基吡咯并[3,4-C]吡咯-1,4-二酮(x-2)。
化合物x-2核磁数据：1H NMR (300 MHz, CDCl3) δ 7.81 (m, 8H), 7.15 (m,6H), 6.75 (d, J = 14.5 Hz, 2H), 3.43 (t, J = 14.2 Hz, 4H), 1.63 (m, 4H), 1.35(m, 36H), 0.88 (m, 6H). 13C NMR (75 MHz, CDCl3) δ 160.86, 156.58, 151.90,141.94, 138.47, 132.70, 129.99, 126.69, 126.17, 119.79, 118.25, 116.12,113.84, 44.45, 31.73, 29.15, 29.04, 28.85, 27.64, 23.16, 14.00。
3）78.3 g (0.25 mol) 2-(4-二乙基氨基-2-羟基苯甲酰基)-苯甲酸(C)和80.9 g(0.1 mol) 3,6-双对(3′-羟基苯基)苯基-2,5-二氢-2,5-双十二烷基吡咯并[3,4-C]吡咯-1,4-二酮(x-2)，再加入200 mL 85%的硫酸，在120℃温度下搅拌加热6小时，冷却至室温之后，倒入冰水中，用2 mol/L的氢氧化钠溶液中和，过滤，滤饼分散到300 mL甲苯和150 mL2mol/L的氢氧化钠溶液中，120℃下搅拌3小时，分液，有机相用无水硫酸钠干燥，浓缩，得粗产品，粗产品用二氯甲烷和石油醚重结晶得125 g 目标化合物 (II-10-1) 。
化合物II-10-1核磁数据： 1H NMR (300 MHz, CDCl3) δ 7.75 (m, 10H), 7.36(m, 12H), 7.03 (d, J = 14.5 Hz, 2H), 6.37 (d, J = 14.6 Hz, 2H), 6.21 (s, 2H),3.43 (t, J = 14.8 Hz, 4H), 3.32 (q, J = 12.2Hz, 8H), 1.64 (m, 4H), 1.25 (m,34H), 1.13 (t, J = 12.3 Hz, 12H), 0.89 (m, 6H). 13C NMR (75 MHz, CDCl3) δ171.05, 160.86, 154.86, 152.97, 151.90, 151.44, 146.64, 142.69, 138.47,133.54, 132.70, 129.90, 128.13, 128.13, 127.10, 126.69, 126.17, 125.30,124.87, 124.51, 124.24, 119.79, 113.49, 108.26, 106.73, 98.85, 86.94, 46.42,44.45, 31.73, 29.15, 29.04, 28.85, 27.64, 23.16, 14.00, 12.99。
实施例11
本实施例提供一种热致变色材料II-11-1，化合物II-11-1的合成路径如下所示：
Figure DEST_PATH_IMAGE028
Figure DEST_PATH_IMAGE029
Figure DEST_PATH_IMAGE030
；
化合物II-11-1的制备方法具体包括以下步骤：
1）化合物C的制备同实施例1；
2）378 g (0.5 mol)的6,6’-二溴-N,N’-(2-十二烷基)异靛与 206.9 g(1.5 mol)间羟基苯硼酸(D)溶解在1000 mL 甲苯中，加入600 mL 2 mol/L的碳酸钾水溶液，用氮气吹洗30 min，加入20 mmolPd(PPh3)4，在氮气环境下加热回流搅拌，TLC监测反应完全，冷却，反应液用二氯甲烷萃取三次，合并有机相，干燥浓缩，进一步用二氯甲烷与石油醚为洗脱剂柱层析得到421 g的中间体化合物6,6’-二-(3′-羟基苯基)-N,N’-(2-十二烷基)异靛(xi-2)。
化合物xi-2核磁数据：1H NMR (300 MHz, CDCl3) δ 7.69 (s, 2H), 7.61 (d, J= 14.7 Hz, 2H), 7.45 (d, J = 14.7 Hz, 2H), 7.31 (t, J = 14.6 Hz, 2H), 7.11(s, 2H), 7.02 (d, J = 14.5 Hz, 2H), 6.83 (d, J = 14.5 Hz, 2H), 4.37 (t, J =14.9 Hz, 4H), 1.67 (m, 4H), 1.29 (m, 36H), 0.85 (m, 6H). 13C NMR (75 MHz,CDCl3) δ 173.00, 156.87, 142.43, 141.52, 139.43, 129.70, 127.54, 125.50,119.75, 118.10, 117.14, 116.45, 113.79, 110.99, 43.77, 31.73, 29.15, 29.04,28.40, 27.64, 23.16, 14.00。
3）78.3 g (0.25 mol) 2-(4-二乙基氨基-2-羟基苯甲酰基)-苯甲酸(C)和78.3 g(0.1 mol) 6,6’-二-(3′-羟基苯基)-N,N’-(2-十二烷基)异靛(xi-2)，再加入200 mL 85%的硫酸，在120℃温度下搅拌加热6小时，冷却至室温之后，倒入冰水中，用2 mol/L的氢氧化钠溶液中和，过滤，滤饼分散到300 mL甲苯和150 mL 2mol/L的氢氧化钠溶液中，120℃下搅拌3小时，分液，有机相用无水硫酸钠干燥，浓缩，得粗产品，粗产品用二氯甲烷和石油醚重结晶得94 g 目标化合物 (II-11-1) 。
化合物II-11-1核磁数据： 1H NMR (300 MHz, CDCl3) δ 7.85 (d, J = 14.5 Hz,2H), 7.75 (s, 2H), 7.64 (d, J = 14.6 Hz, 2H), 7.41 (m, 14H), 7.15 (d, J =14.5 Hz, 2H), 6.42 (d, J = 14.7 Hz, 2H), 6.29 (s, 2H), 4.35 (m, 4H), 3.38 (q,J = 12.3 Hz, 8H), 1.63 (m, 4H), 1.27 (m, 36H), 1.15 (t, J = 12.3 Hz, 12H),0.86 (m, 6H). 13C NMR (75 MHz, CDCl3) δ 173.00, 171.05, 154.86, 152.97,151.58, 146.64, 142.47, 142.43, 139.43, 133.54, 129.90, 128.13, 128.13,127.54, 127.10, 125.60, 125.50, 125.24, 124.87, 123.97, 119.75, 117.14,113.87, 110.99, 108.26, 106.73, 98.85, 86.94, 46.42, 43.77, 31.73, 29.15,29.04, 28.40, 27.64, 23.16, 14.00, 12.99。
实施例12
本实施例提供一种热致变色材料II-12-1，化合物II-12-1的合成路径如下所示：
Figure DEST_PATH_IMAGE031
；
化合物II-12-1的制备方法具体包括以下步骤：
1）化合物C的制备同实施例1；
2）201 g (0.5 mol)的5,10-二溴萘并[1,2-c:5,6-c]双[1,2,5]噻二唑(xii-1)与206.9 g(1.5 mol)间羟基苯硼酸(D)溶解在1000 mL 甲苯中，加入600 mL 2 mol/L的碳酸钾水溶液，用氮气吹洗30 min，加入20 mmolPd(PPh3)4，在氮气环境下加热回流搅拌，TLC监测反应完全，冷却，反应液用二氯甲烷萃取三次，合并有机相，干燥浓缩，进一步用二氯甲烷与石油醚为洗脱剂柱层析得到319 g的中间体化合物5,10-二(3-羟基苯基) 萘并[1,2-c:5,6-c]双[1,2,5]噻二唑(xii-2)。
化合物xii-2核磁数据：1H NMR (300 MHz, CDCl3) δ 8.05 (s, 2H), 7.32 (t, J= 14.6Hz, 2H), 7.15 (s, 2H), 7.03 (d, J = 14.7 Hz, 2H), 6.85 (d, J = 14.5 Hz,2H). 13C NMR (75 MHz, CDCl3) δ 157.69, 153.63, 153.35, 133.84, 132.24, 129.30,122.65, 122.50, 120.25, 119.68, 113.08。
3）78.3 g (0.25 mol) 2-(4-二乙基氨基-2-羟基苯甲酰基)-苯甲酸(C)和42.8 g(0.1 mol) 5,10-二(3-羟基苯基) 萘并[1,2-c:5,6-c]双[1,2,5]噻二唑(xii-2)，再加入200 mL 85%的硫酸，在120℃温度下搅拌加热6小时，冷却至室温之后，倒入冰水中，用2mol/L的氢氧化钠溶液中和，过滤，滤饼分散到300 mL甲苯和150 mL 2mol/L的氢氧化钠溶液中，120℃下搅拌3小时，分液，有机相用无水硫酸钠干燥，浓缩，得粗产品，粗产品用二氯甲烷和石油醚重结晶得79 g 目标化合物 (II-12-1) 。
化合物II-12-1核磁数据：1H NMR (300 MHz, CDCl3) δ 7.91 (m, 4H), 7.45 (m,12H), 7.08 (d, J = 14.6 Hz, 2H), 6.39 (d, J = 14.7 Hz, 2H), 6.25 (s, 2H),3.37 (q, J = 12.3 Hz, 8H), 1.15 (t, J = 12.3 Hz, 12H). 13C NMR (75 MHz, CDCl3)δ 171.05, 154.86, 153.63, 153.35, 153.04, 152.97, 146.64, 137.28, 133.54,132.24, 129.90, 128.13, 128.13, 127.90, 127.10, 125.06, 124.87, 123.45,122.65, 122.50, 117.54, 108.26, 106.73, 98.85, 86.94, 46.42, 12.99。
实施例13
本实施例提供一种热致变色材料II-13-1，化合物II-13-1的合成路径如下所示：
Figure DEST_PATH_IMAGE032
Figure DEST_PATH_IMAGE033
Figure DEST_PATH_IMAGE034
；
化合物II-13-1的制备方法具体包括以下步骤：
1）化合物C的制备同实施例1；
2）423 g (0.5 mol)的萘酚[1,2-c:5,6-c']双[1,2,5]噻二唑,5,10-双[5-溴-4-（2-癸基）-2-噻吩] (xiii-1)与 206.9 g(1.5 mol)间羟基苯硼酸(D)溶解在1000 mL 甲苯中，加入600 mL 2 mol/L的碳酸钾水溶液，用氮气吹洗30 min，加入20 mmolPd(PPh3)4，在氮气环境下加热回流搅拌，TLC监测反应完全，冷却，反应液用二氯甲烷萃取三次，合并有机相，干燥浓缩，进一步用二氯甲烷与石油醚为洗脱剂柱层析得到465 g的中间体化合物萘酚[1,2-c:5,6-c']双[1,2,5]噻二唑,5,10-二-[5-(3-羟基苯基)-4-（2-癸基）-2-噻吩] (xiii-2)。
化合物xiii-2核磁数据：1H NMR (300 MHz, CDCl3) δ 8.15 (s, 2H), 7.35 (m,8H), 6.81 (d, J = 14.5 Hz, 2H), 2.65 (m, 4H), 1.49 (m, 4H), 1.21 (m, 28H),0.83 (m, 6H). 13C NMR (75 MHz, CDCl3) δ 157.14, 157.08, 152.91, 142.57,142.37, 140.74, 138.48, 137.88, 133.13, 129.51, 127.34, 124.49, 119.82,119.01, 114.22, 31.73, 29.15, 29.04, 29.02, 28.76, 25.92, 23.16, 14.00。
3）78.3 g (0.25 mol) 2-(4-二乙基氨基-2-羟基苯甲酰基)-苯甲酸(C)和87.3 g(0.1 mol) 萘酚[1,2-c:5,6-c']双[1,2,5]噻二唑,5,10-二-[5-(3-羟基苯基)-4-（2-癸基）-2-噻吩] (xiii-2)，再加入200 mL 85%的硫酸，在120℃温度下搅拌加热6小时，冷却至室温之后，倒入冰水中，用2 mol/L的氢氧化钠溶液中和，过滤，滤饼分散到300 mL甲苯和150 mL 2mol/L的氢氧化钠溶液中，120℃下搅拌3小时，分液，有机相用无水硫酸钠干燥，浓缩，得粗产品，粗产品用二氯甲烷和石油醚重结晶得131 g 目标化合物 (II-13-1) 。
化合物II-13-1核磁数据：1H NMR (300 MHz, CDCl3) δ 7.95 (s, 2H), 7.83 (d,J = 14.3 Hz, 2H), 7.35 (m, 14H), 7.08 (d, J = 14.7 Hz, 2H), 6.43 (d, J = 14.6Hz, 2H), 6.28 (s, 2H), 3.37 (q, J = 12.3 Hz, 8H), 2.61 (t, J = 14.9 Hz, 4H),1.49 (m, 4H), 1.25 (m, 28H), 1.14 (t, J = 12.3 Hz, 12H), 0.88 (m, 6H). 13C NMR(75 MHz, CDCl3) δ 171.05, 157.08, 154.86, 152.97, 152.91, 152.06, 146.64,142.57, 142.37, 140.74, 137.88, 136.96, 133.54, 133.13, 129.90, 128.13,128.13, 127.34, 127.10, 126.14, 124.87, 124.79, 124.49, 123.04, 110.35,108.26, 106.73, 98.85, 86.94, 46.42, 31.73, 29.15, 29.04, 29.02, 28.76,25.92, 23.16, 14.00, 12.99，
实施例14
本实施例提供一种热致变色材料II-14-1，化合物II-14-1的合成路径如下所示：
Figure DEST_PATH_IMAGE035
Figure DEST_PATH_IMAGE036
Figure DEST_PATH_IMAGE037
；
化合物II-14-1的制备方法具体包括以下步骤：
1）化合物C的制备同实施例1；
2）525 g (0.5 mol)的化合物(xiv-1)与206.9 g(1.5 mol)间羟基苯硼酸(D)溶解在1000 mL 甲苯中，加入600 mL 2 mol/L的碳酸钾水溶液，用氮气吹洗30 min，加入20mmol Pd(PPh3)4，在氮气环境下加热回流搅拌，TLC监测反应完全，冷却，反应液用二氯甲烷萃取三次，合并有机相，干燥浓缩，进一步用二氯甲烷与石油醚为洗脱剂柱层析得到429 g的关键中间体化合物 (xiv-2)。
化合物xiv-2核磁数据：1H NMR (300 MHz, CDCl3) δ 8.89 (s, 2H), 7.42 (m,18H), 6.85 (d, J = 14.5 Hz, 2H), 4.37 (s, 4H), 2.64 (m, 4H), 1.55 (m, 4H),1.25 (m, 26H), 87 (m, 6H). 13C NMR (75 MHz, CDCl3) δ 161.43, 160.39, 157.14,143.24, 143.13, 142.57, 141.00, 140.74, 138.48, 136.93, 132.43, 129.51,128.53, 128.41, 128.04, 127.37, 126.22, 119.82, 119.01, 116.35, 114.22,45.99, 31.73, 29.15, 29.04, 29.02, 28.76, 25.92, 23.16, 14.00。
3）78.3 g (0.25 mol) 2-(4-二乙基氨基-2-羟基苯甲酰基)-苯甲酸(C)和107.5g (0.1 mol) (xiv-2)，再加入200 mL 85%的硫酸，在120℃温度下搅拌加热6小时，冷却至室温之后，倒入冰水中，用2 mol/L的氢氧化钠溶液中和，过滤，滤饼分散到300 mL甲苯和150 mL 2mol/L的氢氧化钠溶液中，120℃下搅拌3小时，分液，有机相用无水硫酸钠干燥，浓缩，得粗产品，粗产品用二氯甲烷和石油醚重结晶得115 g 目标化合物 (II-14-1) 。
化合物II-14-1核磁数据： 1H NMR (300 MHz, CDCl3) δ 8.81 (s, 2H), 8.37(s, 2H), 7.82 (d, J = 14.5 Hz, 2H), 7.41 (m, 22H), 7.08 (d, J = 14.5 Hz, 2H),6.38 (d, J = 14.6 Hz, 2H), 6.24 (s, 2H), 4.31 (s, 4H), 3.38 (q, J = 12.2 Hz,8H), 2.65 (t, J = 15.3 Hz, 4H), 1.49 (m, 4H), 1.26 (m, 28H), 1.15 (t, J =12.3 Hz, 12H), 0.81 (m, 6H)。
实施例15
本实施例提供一种热致变色材料II-15-1，化合物II-15-1的合成路径如下所示：
Figure DEST_PATH_IMAGE038
Figure DEST_PATH_IMAGE039
Figure DEST_PATH_IMAGE040
，
化合物II-15-1的制备方法具体包括以下步骤：
1）化合物C的制备同实施例1；
2）586.5 g (0.5 mol)的 (xv-1)与206.9 g(1.5 mol)间羟基苯硼酸(D)溶解在1000 mL 甲苯中，加入600 mL 2 mol/L的碳酸钾水溶液，用氮气吹洗30 min，加入20mmolPd(PPh3)4，在氮气环境下加热回流搅拌，TLC监测反应完全，冷却，反应液用二氯甲烷萃取三次，合并有机相，干燥浓缩，进一步用二氯甲烷与石油醚为洗脱剂柱层析得到547 g的关键中间体化合物 (xv-2)。
化合物xv-2核磁数据：1H NMR (300 MHz, CDCl3) δ 9.42 (s, 2H), 8.81 (d, J= 14.7 Hz, 2H), 8.09(d, J = 14.7 Hz, 2H), 7.38 (m, 18H), 6.79 (d, J = 14.5Hz, 2H), 4.31 (s, 4H), 2.65 (t, J = 10.3 Hz, 4H), 1.48 (m, 4H), 1.22 (m,30H), 0.81 (m, 6H). 13C NMR (75 MHz, CDCl3) δ 160.97, 160.39, 157.14, 142.57,142.57, 140.74, 138.48, 138.09, 137.83, 136.93, 136.28, 134.93, 132.99,132.07, 130.53, 129.51, 128.53, 128.41, 128.04, 125.71, 123.11, 120.60,119.82, 119.23, 119.01, 114.22, 45.99, 31.73, 29.15, 29.04, 29.02, 28.76,25.92, 23.16, 14.00。
3）78.3 g (0.25 mol) 2-(4-二乙基氨基-2-羟基苯甲酰基)-苯甲酸(C)和120 g(0.1 mol) 化合物 (xv-2)，再加入200 mL 85%的硫酸，在120℃温度下搅拌加热6小时，冷却至室温之后，倒入冰水中，用2 mol/L的氢氧化钠溶液中和，过滤，滤饼分散到300 mL甲苯和150 mL 2mol/L的氢氧化钠溶液中，120℃下搅拌3小时，分液，有机相用无水硫酸钠干燥，浓缩，得粗产品，粗产品用二氯甲烷和石油醚重结晶得149 g 目标化合物 (II-15-1) 。
化合物II-15-1核磁数据： 1H NMR (300 MHz, CDCl3)δ 8.35(s, 2H), 8.11 (d,J = 14.7 Hz, 2H), 7.82 (d, J = 14.5 Hz, 2H), 7.38 (m, 22H), 7.11 (m, 2H),6.45(d, J = 14.7 Hz, 2H), 6.25 (s, 2H), 4.31 (s, 4H), 3.35 (q, J = 12.3 Hz,8H), 2.65 (t, J = 15.3 Hz, 4H), 1.47 (m, 4H), 1.26 (m, 32H), 1.15 (t, J =12.3 Hz, 12H), 0.88 (m, 6H)。
实施例16
本实施例提供一种热致变色材料II-16-1，化合物II-16-1的合成路径如下所示：
Figure DEST_PATH_IMAGE041
；
化合物II-16-1的制备方法具体包括以下步骤：
1）化合物C的制备同实施例1；
2）229 g (0.5 mol)的噻吩[3，4-b]吡嗪，5，7-双（5-溴-2-噻吩）(xvi-1)与 206.9g(1.5 mol)间羟基苯硼酸(D)溶解在1000 mL 甲苯中，加入600 mL 2 mol/L的碳酸钾水溶液，用氮气吹洗30 min，加入20 mmolPd(PPh3)4，在氮气环境下加热回流搅拌，TLC监测反应完全，冷却，反应液用二氯甲烷萃取三次，合并有机相，干燥浓缩，进一步用二氯甲烷与石油醚为洗脱剂柱层析得到465 g的中间体化合物噻吩[3，4-b]吡嗪，5，7-双（5-(3-羟基苯基)-2-噻吩）(xvi-2)。
化合物xvi-2核磁数据：1H NMR (300 MHz, CDCl3) δ 8.58 (s, 2H), 7.52 (d, J= 14.7 Hz, 2H), 7.45 (m, 6H), 7.11 (s, 2H), 6.82 (d, J = 14.3 Hz, 2H). 13C NMR(75 MHz, CDCl3)δ 157.28, 155.12, 148.46, 143.49, 141.94, 137.84, 132.97,129.97, 123.11, 120.78, 119.62, 118.53, 113.58。
3）78.3 g (0.25 mol) 2-(4-二乙基氨基-2-羟基苯甲酰基)-苯甲酸(C)和48.4 g(0.1 mol) 噻吩[3，4-b]吡嗪，5，7-双（5-(3-羟基苯基)-2-噻吩）(xvi-2)，再加入200 mL85%的硫酸，在120℃温度下搅拌加热6小时，冷却至室温之后，倒入冰水中，用2 mol/L的氢氧化钠溶液中和，过滤，滤饼分散到300 mL甲苯和150 mL 2mol/L的氢氧化钠溶液中，120℃下搅拌3小时，分液，有机相用无水硫酸钠干燥，浓缩，得粗产品，粗产品用二氯甲烷和石油醚重结晶得82 g 目标化合物 (II-16-1).
化合物II-16-1核磁数据：1H NMR ((75 MHz, CDCl3)) δ 8.59 (s, 2H), 7.88(d, J = 14.3 Hz, 2H), 7.47 (m, 16H), 7.11(d, J = 14.6 Hz, 2H), 6.39 (d, J =14.7 Hz, 2H), 6.25 (s Hz, 2H), 3.31 (q, J = 12.3 Hz, 8H), 1.15 (t, J = 12.3Hz, 12H). 13C NMR (75 MHz, CDCl3) δ 171.05, 155.12, 154.86, 152.97, 152.42,148.46, 146.64, 143.49, 141.94, 139.86, 133.54, 132.97, 129.90, 128.13,128.13, 127.10, 126.81, 124.87, 123.58, 123.11, 122.11, 119.62, 110.31,108.26, 106.73, 98.85, 86.94, 46.42, 12.99。
实施例17
本实施例提供一种热致变色材料II-17-1，化合物II-17-1的合成路径如下所示：
Figure DEST_PATH_IMAGE042
Figure DEST_PATH_IMAGE043
；
化合物II-17-1的制备方法具体包括以下步骤：
1）化合物C的制备同实施例1；
2）486.5 g (0.5 mol)的5，8-双（5-溴-2-噻吩基）-2，3-双[3-（十二烷氧基）苯基]喹噁啉(xvii-1)与206.9 g(1.5 mol)间羟基苯硼酸(D)溶解在1000 mL 甲苯中，加入600mL 2 mol/L的碳酸钾水溶液，用氮气吹洗30 min，加入20 mmolPd(PPh3)4，在氮气环境下加热回流搅拌，TLC监测反应完全，冷却，反应液用二氯甲烷萃取三次，合并有机相，干燥浓缩，进一步用二氯甲烷与石油醚为洗脱剂柱层析得到564 g的关键中间体化合物5，8-双（5-(3-羟基苯基)-2-噻吩基）-2，3-双[3-（十二烷氧基）苯基] 喹噁啉(xvii-2)。
化合物xvii-2核磁数据：1H NMR (300 MHz, CDCl3) δ 8.19 (m, 6H), 7.10 (m,16H), 4.08 (t, J = 14.6 Hz, 4H), 1.57 (m, 4H), 1.32 (m, 35H), 0.89 (m, 6H).13C NMR (75 MHz, CDCl3) δ 161.28, 157.28, 149.87, 149.42, 143.00, 141.91,137.84, 133.93, 130.13, 129.97, 128.59, 127.83, 123.56, 120.78, 120.61,118.53, 114.47, 113.58, 69.66, 31.73, 29.15, 29.04, 28.80, 26.58, 23.16,14.00。
3）78.3 g (0.25 mol) 2-(4-二乙基氨基-2-羟基苯甲酰基)-苯甲酸(C)和100 g(0.1 mol) 5，8-双（5-(3-羟基苯基)-2-噻吩基）-2，3-双[3-（十二烷氧基）苯基] 喹噁啉(xvii-2)，再加入200 mL 85%的硫酸，在120℃温度下搅拌加热6小时，冷却至室温之后，倒入冰水中，用2 mol/L的氢氧化钠溶液中和，过滤，滤饼分散到300 mL甲苯和150 mL 2mol/L的氢氧化钠溶液中，120℃下搅拌3小时，分液，有机相用无水硫酸钠干燥，浓缩，得粗产品，粗产品用二氯甲烷和石油醚重结晶得108 g 目标化合物 (II-17-1) 。
化合物II-17-1核磁数据： 1H NMR (300 MHz, CDCl3) δ 8.12 (m, 6H), 7.89(d, J = 14.4 Hz, 2H), 7.42 (m, 16H), 7.10 (m, 6H), 6.39 (d, J = 14.7 Hz, 2H),6.22 (s, 2H), 4.08 (m, 4H), 3.31 (q, J = 12.3 Hz, 8H), 1.78 (m, 4H), 1.27 (m,50H), 0.89 (m, 6H)。
实施例18
本实施例提供一种热致变色材料II-18-1，化合物II-18-1的合成路径如下所示：
Figure DEST_PATH_IMAGE044
Figure DEST_PATH_IMAGE045
Figure DEST_PATH_IMAGE046
；
化合物II-18-1的制备方法具体包括以下步骤：
1）化合物C的制备同实施例1；
2）433 g (0.5 mol)的4, 9- 二溴- 6, 7- 二[4-辛氧基] 苯基]噻二唑并喹喔啉(xviii-1)与206.9 g(1.5 mol)间羟基苯硼酸(D)溶解在1000 mL 甲苯中，加入600 mL 2mol/L的碳酸钾水溶液，用氮气吹洗30 min，加入20 mmolPd(PPh3)4，在氮气环境下加热回流搅拌，TLC监测反应完全，冷却，反应液用二氯甲烷萃取三次，合并有机相，干燥浓缩，进一步用二氯甲烷与石油醚为洗脱剂柱层析得到553 g的关键中间体化合物4, 9- 二(3-羟基苯基)- 6, 7- 二[4-十二烷氧基] 苯基]噻二唑并喹喔啉(xviii-2)。
化合物xviii-2核磁数据：1H NMR (300 MHz, CDCl3) δ 8.08 (m, 4H), 7.19 (m,12H), 4.07 (t, J = 14.6 Hz, 4H), 1.72 (m, 4H), 1.37 (m, 37H), 0.89 (m, 6H).13C NMR (75 MHz, CDCl3) δ 161.28, 155.51, 149.24, 148.02, 145.53, 138.76,130.13, 129.37, 128.20, 127.43, 122.06, 121.95, 116.66, 114.47, 69.66, 31.73,29.15, 29.04, 28.80, 26.58, 23.16, 14.00。
3）78.3 g (0.25 mol) 2-(4-二乙基氨基-2-羟基苯甲酰基)-苯甲酸(C)和89.3 g(0.1 mol) 4, 9- 二(3-羟基苯基)- 6, 7- 二[4-十二烷氧基] 苯基]噻二唑并喹喔啉(xviii-2)，再加入200 mL 85%的硫酸，在120℃温度下搅拌加热6小时，冷却至室温之后，倒入冰水中，用2 mol/L的氢氧化钠溶液中和，过滤，滤饼分散到300 mL甲苯和150 mL 2mol/L的氢氧化钠溶液中，120℃下搅拌3小时，分液，有机相用无水硫酸钠干燥，浓缩，得粗产品，粗产品用二氯甲烷和石油醚重结晶得56 g 目标化合物 (II-18-1) 。
化合物II-18-1核磁数据：1H NMR (300 MHz, CDCl3) δ 8.09(m, 4H), 7.85 (d,J = 14.4 Hz, 2H), 7.43 (m, 12H), 7.08 (m, 6H), 6.41 (d, J = 14.7 Hz, 2H),6.25 (s, 2H), 4.12 (t, J = 14.6 Hz, 4H), 3.35 (m, 6H), 2.75 (s, 3H), 1.73 (m,4H), 1.26 (m, 46H), 0.88 (m, 6H). 13C NMR (75 MHz, CDCl3) δ 171.05, 161.28,154.86, 154.05, 153.26, 152.97, 150.70, 149.24, 148.02, 146.64, 145.53,134.85, 133.54, 130.13, 129.90, 128.20, 128.13, 128.13, 128.12, 127.43,127.10, 125.40, 124.87, 123.97, 122.46, 118.53, 114.47, 108.26, 108.07,106.73, 106.30, 100.19, 98.85, 86.94, 69.66, 48.04, 46.42, 39.28, 31.73,29.15, 29.04, 28.80, 26.58, 23.16, 14.00, 12.99, 11.88。
实施例19
本实施例提供一种热致变色材料II-19-1，化合物II-19-1的合成路径如下所示：
Figure DEST_PATH_IMAGE047
；
化合物II-19-1的制备方法具体包括以下步骤：
1）化合物C的制备同实施例1；
2）150 g (0.5 mol)的二溴噻吩并噻二唑(xix-1)与206.9 g(1.5 mol)间羟基苯硼酸(D)溶解在1000 mL 甲苯中，加入600 mL 2 mol/L的碳酸钾水溶液，用氮气吹洗30min，加入20 mmolPd(PPh3)4，在氮气环境下加热回流搅拌，TLC监测反应完全，冷却，反应液用二氯甲烷萃取三次，合并有机相，干燥浓缩，进一步用二氯甲烷与石油醚为洗脱剂柱层析得到198 g的关键中间体化合物二（5-(3-羟基苯基)噻吩并噻二唑(xix-2)。
3）78.3 g (0.25 mol) 2-(4-二乙基氨基-2-羟基苯甲酰基)-苯甲酸(C)和32.6 g(0.1 mol) 二（5-(3-羟基苯基)噻吩并噻二唑(xix-2)，再加入200 mL 85%的硫酸，在120℃温度下搅拌加热6小时，冷却至室温之后，倒入冰水中，用2 mol/L的氢氧化钠溶液中和，过滤，滤饼分散到300 mL甲苯和150 mL 2mol/L的氢氧化钠溶液中，120℃下搅拌3小时，分液，有机相用无水硫酸钠干燥，浓缩，得粗产品，粗产品用二氯甲烷和石油醚重结晶得63 g 目标化合物 (II-19-1) 。
化合物II-19-1核磁数据：1H NMR(300 MHz, CDCl3) δ 7.89 (d, J = 14.4 Hz,2H), 7.42 (m, 12H), 7.08 (d, J = 14.6 Hz, 2H), 6.37 (d, J = 14.7 Hz, 2H),6.25 (s, 2H), 3.38 (q, J = 12.3 Hz, 8H), 1.14 (t, J = 12.3 Hz, 12H). 13C NMR(75 MHz, CDCl3) δ 171.05, 164.28, 156.25, 154.86, 152.97, 151.55, 146.64,137.79, 133.54, 129.90, 128.13, 128.13, 127.10, 127.01, 125.42, 124.87,124.53, 114.41, 108.26, 106.73, 98.85, 86.94, 46.42, 12.99。
对比例1
本对比例提供一种热致变色材料M，具体结构如下所示：
Figure DEST_PATH_IMAGE048
。
测试例1
对上述实施例1-19和对比例1制备得到的热致变色材料进行测试，测试方法包括如下步骤：分别将1mol上述实施例或对比例中的热致变色材料与1mol双酚A化合物混合均匀，然后将所得混合物从室温以1℃/分钟的升温速率连续升温至200℃，观察混合物颜色变化，并记录变色温度，最后将混合物从200℃以1℃/分钟的降温速率连续降温至15℃，在降温过程中混合物又由显色变为无色。其中在升温过程中混合物的颜色变化以及变色温度如表1所示。
表1热致变色材料和双酚A混合物升温测试结果
Figure DEST_PATH_IMAGE049
显然，上述实施例仅仅是为清楚地说明所作的举例，而并非对实施方式的限定。对于所属领域的普通技术人员来说，在上述说明的基础上还可以做出其它不同形式的变化或变动。这里无需也无法对所有的实施方式予以穷举。而由此所引伸出的显而易见的变化或变动仍处于本发明创造的保护范围之中。

Claims (10)

1.一种具有双罗丹明结构的热致变色材料，其特征在于，具有如下所示的结构：
Figure DEST_PATH_IMAGE001
式Ⅰ
其中，R1、R2相同或不同，分别独立的选自未取代C1-C36的烷基；
R3，R4，R5和R6相同或不同，分别独立的选自氢、未取代C1-C36的烷基；
B选自如下结构的基团：
Figure 671597DEST_PATH_IMAGE002
，
其中n选自1-20的整数，每一个R相同或不同，各自独立选自氢、甲基、乙基、正丙基、异丙基、正丁基、异丁基、仲丁基、叔丁基、戊基、己基、庚基、辛基、壬基、癸基、十一烷基、十二烷基、苯甲基、对甲氧基苄基、对三氟甲氧基苄基。
2.根据权利要求1所述的热致变色材料，其特征在于，R1、R2相同或不同，分别独立的选自甲基、乙基、正丙基、异丙基、正丁基、异丁基、仲丁基、叔丁基；
R3，R4，R5和R6相同或不同，分别独立的选自氢、甲基、乙基、正丙基、异丙基、正丁基、异丁基、仲丁基、叔丁基。
3.根据权利要求1-2任一项所述的热致变色材料，其特征在于，所述热致变色材料具有如下所示的结构：
Figure DEST_PATH_IMAGE003
Figure 214836DEST_PATH_IMAGE004
Figure DEST_PATH_IMAGE005
Figure 56890DEST_PATH_IMAGE006
。
4.权利要求1-3任一项所述的热致变色材料的制备方法，其特征在于，包括如下步骤：
1）将i所示化合物与ii所示化合物反应得到iii所示化合物；
2）将iv所示化合物与v所示化合物通过偶联反应得到vi所示化合物；
3）将iii所示化合物与vi所示化合物反应得到式Ⅰ所示化合物；
所述式Ⅰ所示化合物的制备路径如下所示：
Figure DEST_PATH_IMAGE007
；
其中X为卤素，其它变量与权利要求1-3任一项所述热致变色材料的相应位置取代基定义相同。
5.一种显色组合物，其特征在于，包括热致变色材料和酚类化合物，所述热致变色材料为权利要求1-3任一项所述的热致变色材料或权利要求4所述制备方法制备得到的热致变色材料。
6.根据权利要求5所述的显色组合物，其特征在于，所述热致变色材料和酚类化合物的摩尔比为（0.1-1）：（0.1-10）；所述酚类化合物为双酚A化合物。
7.权利要求5或6所述的显色组合物的制备方法，其特征在于，包括如下步骤：将热致变色材料和酚类化合物混合均匀即得。
8.权利要求1-3任一项所述的热致变色材料或权利要求4所述制备方法制备得到的热致变色材料在制备压敏染料、热敏染料中的用途。
9.权利要求5-6任一项所述的显色组合物或权利要求7所述的制备方法制备得到的显色组合物在制备压敏染料、热敏染料中的用途。
10.权利要求1-3任一项所述的热致变色材料或权利要求4所述制备方法制备得到的热致变色材料或权利要求5-6任一项所述的显色组合物或权利要求7所述的制备方法制备得到的显色组合物在防伪领域中的应用。
CN202210131654.2A 2022-02-14 2022-02-14 具有双罗丹明结构的热致变色材料、显色组合物及其制备方法和应用 Active CN114163459B (zh)