CN114108322B - 一种肉感滑弹织物整理剂及其制备方法与应用 - Google Patents
一种肉感滑弹织物整理剂及其制备方法与应用 Download PDFInfo
- Publication number
- CN114108322B CN114108322B CN202111451156.8A CN202111451156A CN114108322B CN 114108322 B CN114108322 B CN 114108322B CN 202111451156 A CN202111451156 A CN 202111451156A CN 114108322 B CN114108322 B CN 114108322B
- Authority
- CN
- China
- Prior art keywords
- meat
- silicone rubber
- finishing agent
- elastic fabric
- smooth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供了一种肉感滑弹织物整理剂及其制备方法与应用，其中，制备方法包括步骤：将硅橡胶和非离子乳化剂混合并在搅拌条件下加水乳化，得到硅橡胶乳液；在搅拌条件下将水性涂料加入到所述硅橡胶乳液中，得到混合液；在搅拌条件下将增重剂和白胶浆加入到所述混合液中，得到肉感滑弹织物整理剂。本发明通过研究不同物质作用于棉织物的手感风格，使得所述肉感滑弹织物整理剂能同时满足挺括、滑爽、弹性、厚实、肉感等手感风格，极大地提升了棉织物的附加值。
Description
技术领域
本发明涉及纺织物技术领域，尤其涉及一种肉感滑弹织物整理剂及其制备方法与应用。
技术背景
随着民众消费水平的提高，人们对服饰手感的要求也也来越高。以前的时长对服装面料手感的要求还是以软、滑为主，近些年市场对于服饰的亲肤手感要求越来越多，比如肉感手感、弹性手感、厚实手感、爽挺滑手感以及亲水手感等，并且要求以上多种手感要同时满足。
因此，市场对于服饰新型复合手感的需求对印染助剂的开发提出了更高的要求。
因此，现有技术还有待于改进和发展。
发明内容
鉴于上述现有技术的不足，本发明的目的在于提供一种肉感滑弹织物整理剂及其制备方法与应用，旨在解决现有印染助剂无法满足织物多种亲肤手感要求的问题。
本发明的技术方案如下：
一种肉感滑弹织物整理剂的制备方法，其中，包括步骤：
将硅橡胶和非离子乳化剂混合并在搅拌条件下加水乳化，得到硅橡胶乳液；
在搅拌条件下将水性涂料加入到所述硅橡胶乳液中，得到混合液；
在搅拌条件下将增重剂和白胶浆加入到所述混合液中，得到肉感滑弹织物整理剂。
所述肉感滑弹织物整理剂的制备方法，其中，所述硅橡胶为甲基乙烯基硅橡胶、甲基苯基硅橡胶、甲基硅橡胶和室温硫化胶中的一种或者两者的混合物。
所述肉感滑弹织物整理剂的制备方法，其中，所述非离子乳化剂为脂肪醇聚氧乙烯醚和异构醇聚氧乙烯醚中的一种或者两者的混合物。
所述肉感滑弹织物整理剂的制备方法，其中，所述水性涂料为聚乙烯醇、水溶醇酸树脂、水溶环氧树脂和无机高分子水性树脂中的一种或多种。
所述肉感滑弹织物整理剂的制备方法，其中，所述增重剂为甘油、尿素、乙二醇和山梨醇中的一种或两者的混合物。
所述肉感滑弹织物整理剂的制备方法，其中，所述白胶浆为醋酸乙烯酯类共聚物的一种或两者的混合物。
所述肉感滑弹织物整理剂的制备方法，其中，将硅橡胶和非离子乳化剂混合并在搅拌条件下加水乳化的步骤中，搅拌速度为100-3000转/分钟。
所述肉感滑弹织物整理剂的制备方法，其中，按重量百分比计，所述肉感滑弹织物整理剂中，所述硅橡胶乳液占比30-80％，所述水性涂料占比5-30％，所述增重剂占比5-30％，所述白胶浆占比1-20％。
一种肉感滑弹织物整理剂，其中，采用本发明所述肉感滑弹织物整理剂的制备方法制得。
一种肉感滑弹织物整理剂的应用，其中，将本发明所述的肉感滑弹织物整理剂用于制备织物。
有益效果：本发明提供了一种肉感滑弹织物整理剂的制备方法，通过将硅橡胶和非离子乳化剂混合并在搅拌条件下加水乳化，得到硅橡胶乳液，并在所述硅橡胶乳液中加入水性涂料、增重剂和白胶浆，搅拌混合制得所述肉感滑弹织物整理剂。本发明通过研究不同物质作用于棉织物的手感风格，使得所述肉感滑弹织物整理剂能同时满足挺括、滑爽、弹性、厚实、肉感等手感风格，极大地提升了棉织物的附加值。
附图说明
图1为本发明一种肉感滑弹织物整理剂的制备方法流程图。
具体实施方式
本发明提供了一种肉感滑弹织物整理剂及其制备方法与应用，为使本发明的目的、技术方案及效果更加清楚、明确，以下对本发明进一步详细说明。应当理解，此处所描述的具体实施例仅用以解释本发明，并不用于限定本发明。
请参阅图1，图1为本发明提供的一种肉感滑弹织物整理剂的制备方法流程图，如图所示，其包括步骤：
S10、将硅橡胶和非离子乳化剂混合并在搅拌条件下加水乳化，得到硅橡胶乳液；
S20、在搅拌条件下将水性涂料加入到所述硅橡胶乳液中，得到混合液；
S30、在搅拌条件下将增重剂和白胶浆加入到所述混合液中，得到肉感滑弹织物整理剂。
本发明制备的肉感滑弹织物整理剂作用于棉织物时，可使得所述棉织物同时满足挺括、滑爽、弹性、厚实、肉感等手感风格，极大地提升了棉织物的附加值。具体来讲，所述硅橡胶乳液提供平滑、回弹、光泽；所述水性涂料提供弹性；增重剂提供肉感、细腻手感；白胶浆提供厚实、挺括手感。
在一些实施方式中，所述硅橡胶为甲基乙烯基硅橡胶、甲基苯基硅橡胶、甲基硅橡胶和室温硫化胶中的一种或者两者的混合物，但不限于此。
在一些实施方式中，所述非离子乳化剂为脂肪醇聚氧乙烯醚和异构醇聚氧乙烯醚中的一种或者两者的混合物，但不限于此。
在一些实施方式中，所述水性涂料为聚乙烯醇、水溶醇酸树脂、水溶环氧树脂和无机高分子水性树脂中的一种或多种，但不限于此。
在一些实施方式中，所述增重剂为甘油、尿素、乙二醇和山梨醇中的一种或两者的混合物，但不限于此。
在一些实施方式中，所述白胶浆为醋酸乙烯酯类共聚物的一种或两者的混合物，但不限于此。
在一些实施方式中，将硅橡胶和非离子乳化剂混合并在搅拌条件下加水乳化的步骤中，搅拌速度为100-3000转/分钟。
在一些实施方式中，按重量百分比计，所述肉感滑弹织物整理剂中，所述硅橡胶乳液占比30-80％，所述水性涂料占比5-30％，所述增重剂占比5-30％，所述白胶浆占比1-20％。
在一些实施方式中，还提供一种肉感滑弹织物整理剂，其采用本发明所述肉感滑弹织物整理剂的制备方法制得。
在一些实施方式中，还提供一种肉感滑弹织物整理剂的应用，其中，将本发明所述的肉感滑弹织物整理剂用于制备织物。
下面通过具体实施例对本发明做进一步的解释说明：
实施例1
步骤一：将16克分子量为200万的室温硫化硅橡胶、4.8克的异构十三醇聚氧乙烯醚混合，在200转/分钟的转速下搅拌1小时，然后慢慢加入59.2克的水；
步骤二：将5克的环氧水性树脂加入到步骤一中的乳液中；
步骤三：将10克乙二醇和5克聚醋酸乙烯酯乳液加入到步骤二的乳液中。加完物料后慢速搅拌30分钟，转速30转/分钟，消泡后过滤出料。
实施例2
步骤一：将12克分子量为2万的室温硫化硅橡胶、3.6克的异构十三醇聚氧乙烯醚混合，在1000转/分钟的转速下搅拌1小时，然后慢慢加入44.4克的水；
步骤二：将30克的环氧水性树脂加入到步骤一中的乳液中；
步骤三：将5克山梨醇和5克聚醋酸乙烯酯乳液加入到步骤二的乳液中。加完物料后慢速搅拌30分钟，转速30转/分钟，消泡后过滤出料。
实施例3
步骤一：将12克分子量为30万的甲基乙烯基硅橡胶、3.6克的脂肪醇醇聚氧乙烯醚混合，在200转/分钟的转速下搅拌1小时，然后慢慢加入44.4克的水；
步骤二：将5克的醇酸水性树脂加入到步骤一中的乳液中；
步骤三：将5克尿素和30克聚醋酸乙烯酯乳液加入到步骤二的乳液中。加完物料后慢速搅拌30分钟，转速30转/分钟，消泡后过滤出料。
实施例4
步骤一：将12克分子量为200万的甲基硅橡胶、3.6克的异构十三醇聚氧乙烯醚混合，在200转/分钟的转速下搅拌1小时，然后慢慢加入44.4克的水；
步骤二：将5克的聚乙烯醇水性树脂加入到步骤一中的乳液中；
步骤三：将30克甘油和5克聚醋酸乙烯酯乳液加入到步骤二的乳液中。加完物料后慢速搅拌30分钟，转速30转/分钟，消泡后过滤出料。
对上述实施例1-实施例4制备的乳液进行手感性能测试，结果如下所示：实施例1中的乳液有更好的爽滑度，兼具一定的肉感弹性厚实感；实施例2中的乳液有更好的弹性，兼具一定的肉感爽滑厚实感；实施例3中的乳液有更好的厚实感和挺括度，兼具一定的肉感弹性爽滑感；实施例4中的乳液有更好的肉感，兼具一定的爽滑弹性厚实感。
综上所述，本发明提供了一种肉感滑弹织物整理剂的制备方法，通过将硅橡胶和非离子乳化剂混合并在搅拌条件下加水乳化，得到硅橡胶乳液，并在所述硅橡胶乳液中加入水性涂料、增重剂和白胶浆，搅拌混合制得所述肉感滑弹织物整理剂。本发明通过研究不同物质作用于棉织物的手感风格，使得所述肉感滑弹织物整理剂能同时满足挺括、滑爽、弹性、厚实、肉感等手感风格，极大地提升了棉织物的附加值。
应当理解的是，本发明的应用不限于上述的举例，对本领域普通技术人员来说，可以根据上述说明加以改进或变换，所有这些改进和变换都应属于本发明所附权利要求的保护范围。
Claims (6)
1.一种肉感滑弹织物整理剂的制备方法，其特征在于，包括步骤：
将硅橡胶和非离子乳化剂混合并在搅拌条件下加水乳化，得到硅橡胶乳液；
在搅拌条件下将水性涂料加入到所述硅橡胶乳液中，得到混合液；
在搅拌条件下将增重剂和白胶浆加入到所述混合液中，得到肉感滑弹织物整理剂；
所述增重剂为甘油、尿素、乙二醇和山梨醇中的一种或两种的混合物；
所述白胶浆为醋酸乙烯酯类共聚物的一种或两种的混合物；
将硅橡胶和非离子乳化剂混合并在搅拌条件下加水乳化的步骤中，搅拌速度为100-3000转/分钟；
所述水性涂料为聚乙烯醇、水溶醇酸树脂、水溶环氧树脂和无机高分子水性树脂中的一种或多种。
2.根据权利要求1所述肉感滑弹织物整理剂的制备方法，其特征在于，所述硅橡胶为甲基乙烯基硅橡胶、甲基苯基硅橡胶、甲基硅橡胶和室温硫化胶中的一种或者两种的混合物。
3.根据权利要求1所述肉感滑弹织物整理剂的制备方法，其特征在于，所述非离子乳化剂为脂肪醇聚氧乙烯醚和异构醇聚氧乙烯醚中的一种或者两种的混合物。
4.根据权利要求1所述肉感滑弹织物整理剂的制备方法，其特征在于，按重量百分比计，所述肉感滑弹织物整理剂中，所述硅橡胶乳液占比30-80％，所述水性涂料占比5-30％，所述增重剂占比5-30％，所述白胶浆占比1-20％。
5.一种肉感滑弹织物整理剂，其特征在于，采用权利要求1-4任一所述肉感滑弹织物整理剂的制备方法制得。
6.一种肉感滑弹织物整理剂的应用，其特征在于，将权利要求5所述的肉感滑弹织物整理剂用于制备织物。