CN114031359A - 一种水泥基自流平及其制备方法 - Google Patents
一种水泥基自流平及其制备方法 Download PDFInfo
- Publication number
- CN114031359A CN114031359A CN202111578403.0A CN202111578403A CN114031359A CN 114031359 A CN114031359 A CN 114031359A CN 202111578403 A CN202111578403 A CN 202111578403A CN 114031359 A CN114031359 A CN 114031359A
- Authority
- CN
- China
- Prior art keywords
- cement
- powder
- based self
- leveling
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种水泥基自流平，包括以下质量份的各物质：普硅水泥：25‑45、硫铝酸盐水泥：10‑20、无水石膏：3‑7、填料：5‑10、石英砂：35‑45、胶粉：1‑2、减水剂：0.2‑0.3、消泡剂：0.1‑0.2、纤维素醚：0.05‑0.1、碳酸锂：0.05‑0.2、水：23‑27；本发明还公开了一种水泥基自流平的制备方法，包括以下步骤：S1，粉体部分制备：将普硅水泥、硫铝酸盐水泥、无水石膏、石英砂、填料、胶粉、减水剂、消泡剂、纤维素醚和碳酸锂按配方量加入粉料搅拌机中搅拌均匀。本发明的水泥基自流平的流动性好、粘接强度高，抗折强度，抗压强度大大高于市场同类产品，本发明水泥基自流平的制备方法简单易行，具有很大的应用前景。
Description
技术领域
本发明涉及建筑材料技术领域，尤其涉及一种水泥基自流平及其制备方法。
背景技术
自流平砂浆是一种由无机或有机胶凝材料、细骨料、填料及外加剂等组成，加水搅拌后具有流动性或稍加辅助性铺摊就能流动找平的地面用材料它具有流动度大、施工快速、表面光滑平整等优点，是大型超市、商场、停车场、工厂车间、仓库等地面铺筑的理想材料，是现在建筑地面施工的一个发展方向，市场潜力很大。
近年来，随着我国施工技术的不断发展，人们对建筑材料研究愈发的重视，对工程品质及质量要求越来越高。而目前地面铺筑中，常用的水泥砂浆存在找平施工困难、上强度时间长、容易开裂的问题，且水泥砂浆一般为工人现场混料搅拌，物料配比多为工人凭经验手工配比，不够精确。
为了能有效的杜绝这类问题的产生，需提供一种提前在工厂严格按照配方预混好、操作简洁、上强度快且不易开裂的地面铺筑材料。
发明内容
本发明的目的是为了解决现有技术中存在的缺点，而提出的一种水泥基自流平及其制备方法，其施工性及填充找平性能均良好、粘接强度大、抗开裂性能强，可降低施工难度，改善工程建设质量，节约工程建设成本。
为了实现上述目的，本发明采用了如下技术方案：
一种水泥基自流平，包括以下质量份的各物质：普硅水泥：25-45、硫铝酸盐水泥：10-20、无水石膏：3-7、填料：5-10、石英砂：35-45、胶粉：1-2、减水剂：0.2-0.3、消泡剂：0.1-0.2、纤维素醚：0.05-0.1、碳酸锂：0.05-0.2、水：23-27。
优选地，所述普硅水泥强度等级为42.5R。
优选地，所述填料为重质碳酸钙、粉煤灰或石英粉中的一种或一种以上，所述重质碳酸钙为200-300目过筛处理。
优选地，所述石英砂为规格40-70目、70-140目中的一种。
优选地，所述胶粉为可再分散乳胶粉。
优选地，所述减水剂为聚羧酸类减水剂。
优选地，所述消泡剂为聚醚类消泡剂。
优选地，所述纤维素醚为粘度为400左右的羟丙基甲基纤维素醚。
本发明还公开了一种水泥基自流平的制备方法，包括以下步骤：
S1，粉体部分制备：将普硅水泥、硫铝酸盐水泥、无水石膏、石英砂、填料、胶粉、减水剂、消泡剂、纤维素醚和碳酸锂按配方量加入粉料搅拌机中搅拌均匀；
S2，在步骤S1所制得的混合粉料中按配方量加入水(水与上述混合的粉料混合液为灰水)，搅拌均匀，即得本发明的水泥基自流平。
本发明的有益效果为：
本发明利用普硅水泥、硫铝酸盐水泥作为胶凝材料，利用普硅水泥、硫铝酸盐水泥提供地面铺筑工程所需的硬度和强度；石英砂为骨料，使产品具有良好的抗折、抗压性能；重钙为填料，使产品浆体稠度合适，防止出现泌水，且制备方法简单易行，得到的自流平施工性及抗折、抗压性能均良好，粘接强度大，抗开裂性能好，上强度速度快，具有很大的应用前景。
具体实施方式
下面将结合本发明中的实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。
实施例1
一种水泥基自流平，包括水泥基自流平，由以下质量份的各物质组成：普硅水泥：35、石英砂(40-70目)：20、石英砂(70-140目)：20、硫铝酸盐水泥：10、重质碳酸钙：8、无水石膏：5、可分散乳胶粉：1.5、减水剂：0.3、消泡剂：0.1、HPMC：0.05、碳酸锂：0.1、灰水质量比为1:0.26。
其中，所述普硅水泥强度等级为42.5R。
其中，所述填料为重质碳酸钙、粉煤灰或石英粉中的一种或一种以上，所述重质碳酸钙为200-300目过筛处理。
其中，所述石英砂为规格40-70目、70-140目中的一种。
其中，所述胶粉为可再分散乳胶粉。
其中，所述减水剂为聚羧酸类减水剂。
其中，所述纤维素醚为粘度为400左右的羟丙基甲基纤维素醚。
本发明还公开了一种水泥基自流平的制备方法，其特征在于，包括以下步骤：
S1，粉体部分制备：将普硅水泥、硫铝酸盐水泥、无水石膏、石英砂、填料、胶粉、减水剂、消泡剂、纤维素醚和碳酸锂按配方量加入粉料搅拌机中搅拌均匀；
S2，在步骤S1所制得的混合粉料中按配方量加入水(水与上述混合的粉料混合液为灰水)，搅拌均匀，即得本发明的水泥基自流平。
实施例2
水泥基自流平，由以下质量份的各物质组成：
普硅水泥：35、石英砂(40-70目)：15、石英砂(70-140目)：15、硫铝酸盐水泥：20、重质碳酸钙：8、无水石膏：5、可分散乳胶粉：1.5、减水剂：0.3、消泡剂：0.1、HPMC：0.05、碳酸锂：0.1、灰水质量比为1:0.25。
其中，所述普硅水泥强度等级为42.5R。
其中，所述填料为重质碳酸钙、粉煤灰或石英粉中的一种或一种以上，所述重质碳酸钙为200-300目过筛处理。
其中，所述石英砂为规格40-70目、70-140目中的一种。
其中，所述胶粉为可再分散乳胶粉。
其中，所述减水剂为聚羧酸类减水剂。
其中，所述纤维素醚为粘度为400左右的羟丙基甲基纤维素醚。
本发明还公开了一种水泥基自流平的制备方法，其特征在于，包括以下步骤：
S1，粉体部分制备：将普硅水泥、硫铝酸盐水泥、无水石膏、石英砂、填料、胶粉、减水剂、消泡剂、纤维素醚和碳酸锂按配方量加入粉料搅拌机中搅拌均匀；
S2，在步骤S1所制得的混合粉料中按配方量加入水(水与上述混合的粉料混合液为灰水)，搅拌均匀，即得本发明的水泥基自流平。
实施例3
水泥基自流平，由以下质量份的各物质组成：
普硅水泥：35、石英砂(40-70目)：20、石英砂(70-140目)：20、硫铝酸盐水泥：15、重质碳酸钙：5、无水石膏：3、可分散乳胶粉：1.5、减水剂：0.3、消泡剂：0.1、HPMC：0.05、碳酸锂：0.2、灰水质量比为1:0.26。
其中，所述普硅水泥强度等级为42.5R。
其中，所述填料为重质碳酸钙、粉煤灰或石英粉中的一种或一种以上，所述重质碳酸钙为200-300目过筛处理。
其中，所述石英砂为规格40-70目、70-140目中的一种。
其中，所述胶粉为可再分散乳胶粉。
其中，所述减水剂为聚羧酸类减水剂。
其中，所述纤维素醚为粘度为400左右的羟丙基甲基纤维素醚。
本发明还公开了一种水泥基自流平的制备方法，其特征在于，包括以下步骤：
S1，粉体部分制备：将普硅水泥、硫铝酸盐水泥、无水石膏、石英砂、填料、胶粉、减水剂、消泡剂、纤维素醚和碳酸锂按配方量加入粉料搅拌机中搅拌均匀；
S2，在步骤S1所制得的混合粉料中按配方量加入水(水与上述混合的粉料混合液为灰水)，搅拌均匀，即得本发明的水泥基自流平。
实施例4
水泥基自流平，由以下质量份的各物质组成：
普硅水泥：35、石英砂(40-70目)：15、石英砂(70-140目)：25、硫铝酸盐水泥：15、重质碳酸钙：5、无水石膏：3、可分散乳胶粉：1.5、减水剂：0.3、消泡剂：0.1、HPMC：0.05、碳酸锂：0.2、灰水质量比为1:0.26。
其中，所述普硅水泥强度等级为42.5R。
其中，所述填料为重质碳酸钙、粉煤灰或石英粉中的一种或一种以上，所述重质碳酸钙为200-300目过筛处理。
其中，所述石英砂为规格40-70目、70-140目中的一种。
其中，所述胶粉为可再分散乳胶粉。
其中，所述减水剂为聚羧酸类减水剂。
其中，所述纤维素醚为粘度为400左右的羟丙基甲基纤维素醚。
本发明还公开了一种水泥基自流平的制备方法，其特征在于，包括以下步骤：
S1，粉体部分制备：将普硅水泥、硫铝酸盐水泥、无水石膏、石英砂、填料、胶粉、减水剂、消泡剂、纤维素醚和碳酸锂按配方量加入粉料搅拌机中搅拌均匀；
S2，在步骤S1所制得的混合粉料中按配方量加入水(水与上述混合的粉料混合液为灰水)，搅拌均匀，即得本发明的水泥基自流平。
实施例5
水泥基自流平，由以下质量份的各物质组成：
普硅水泥：35、石英砂(40-70目)：25、石英砂(70-140目)：15、硫铝酸盐水泥：15、重质碳酸钙：5、无水石膏：3、可分散乳胶粉：1.5、减水剂：0.3、消泡剂：0.1、HPMC：0.05、碳酸锂：0.2、灰水质量比为1:0.26。
其中，所述普硅水泥强度等级为42.5R。
其中，所述填料为重质碳酸钙、粉煤灰或石英粉中的一种或一种以上，所述重质碳酸钙为200-300目过筛处理。
其中，所述石英砂为规格40-70目、70-140目中的一种。
其中，所述胶粉为可再分散乳胶粉。
其中，所述减水剂为聚羧酸类减水剂。
其中，所述纤维素醚为粘度为400左右的羟丙基甲基纤维素醚。
本发明还公开了一种水泥基自流平的制备方法，其特征在于，包括以下步骤：
S1，粉体部分制备：将普硅水泥、硫铝酸盐水泥、无水石膏、石英砂、填料、胶粉、减水剂、消泡剂、纤维素醚和碳酸锂按配方量加入粉料搅拌机中搅拌均匀；
S2，在步骤S1所制得的混合粉料中按配方量加入水(水与上述混合的粉料混合液为灰水)，搅拌均匀，即得本发明的水泥基自流平。
将实施例1-5按照上述的步骤制作产品和对比产品(市售水泥基自流平)做对比试验，检测其施工性、粘接强度、抗折强度和抗压强度等指标，结果如下：
通过以上检测结果可知，本发明的水泥基自流平的流动性好、粘接强度高，抗折强度，抗压强度大大高于市场同类产品，本发明水泥基自流平的制备方法简单易行，具有很大的应用前景。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。
Claims (9)
1.一种水泥基自流平，其特征在于，包括以下质量份的各物质：普硅水泥：25-45、硫铝酸盐水泥：10-20、无水石膏：3-7、填料：5-10、石英砂：35-45、胶粉：1-2、减水剂：0.2-0.3、消泡剂：0.1-0.2、纤维素醚：0.05-0.1、碳酸锂：0.05-0.2、水：23-27。
2.根据权利要求1所述的一种水泥基自流平，其特征在于，所述普硅水泥强度等级为42.5R。
3.根据权利要求1所述的一种水泥基自流平，其特征在于，所述填料为重质碳酸钙、粉煤灰或石英粉中的一种或一种以上，所述重质碳酸钙为200-300目过筛处理。
4.根据权利要求1所述的一种水泥基自流平，其特征在于，所述石英砂为规格40-70目、70-140目中的一种。
5.根据权利要求1所述的一种水泥基自流平，其特征在于，所述胶粉为可再分散乳胶粉。
6.根据权利要求1所述的一种水泥基自流平，其特征在于，所述减水剂为聚羧酸类减水剂。
7.根据权利要求1所述的一种水泥基自流平，其特征在于，所述消泡剂为聚醚类消泡剂。
8.根据权利要求1所述的一种水泥基自流平，其特征在于，所述纤维素醚为粘度为400左右的羟丙基甲基纤维素醚。
9.一种水泥基自流平的制备方法，其特征在于，包括以下步骤：
S1，粉体部分制备：将普硅水泥、硫铝酸盐水泥、无水石膏、石英砂、填料、胶粉、减水剂、消泡剂、纤维素醚和碳酸锂按配方量加入粉料搅拌机中搅拌均匀；
S2，在步骤S1所制得的混合粉料中按配方量加入水(水与上述混合的粉料混合液为灰水)，搅拌均匀，即得本发明的水泥基自流平。