CN106747173A - 一种自流平水泥基环保地坪砂浆 - Google Patents

一种自流平水泥基环保地坪砂浆 Download PDF

Info

Publication number
CN106747173A
CN106747173A CN201610989937.5A CN201610989937A CN106747173A CN 106747173 A CN106747173 A CN 106747173A CN 201610989937 A CN201610989937 A CN 201610989937A CN 106747173 A CN106747173 A CN 106747173A
Authority
CN
China
Prior art keywords
parts
self
basic ring
cement
mortar
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610989937.5A
Other languages
English (en)
Inventor
覃乃舟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangxi Bai Rui Tong Building Materials Technology Co Ltd
Original Assignee
Guangxi Bai Rui Tong Building Materials Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangxi Bai Rui Tong Building Materials Technology Co Ltd filed Critical Guangxi Bai Rui Tong Building Materials Technology Co Ltd
Priority to CN201610989937.5A priority Critical patent/CN106747173A/zh
Publication of CN106747173A publication Critical patent/CN106747173A/zh
Pending legal-status Critical Current

Abstract

一种自流平水泥基环保地坪砂浆，其组分为：普通硅酸盐水泥100‑400份，高铝水泥80‑200份，石膏60‑150份，矿粉20‑240份，石英砂350‑500份，聚羧酸类高效减水剂2‑4份，再分散乳胶粉10‑60份，复合保水稳定剂1‑4份，消泡剂0.5‑5份，早强及复合缓凝剂2‑5份。本发明通过优化成分配比制备出不同性能的自流平水泥砂浆，流动度大于150mm，找平效果好，自动愈合能力强，地坪收缩不开裂，实现一次找平永久使用；强度高于C30等级，具有优秀的耐磨性能；施工周期短，施工后表面平滑，整体统一；节省材料，降低成本，对人体无害、无辐射。

Description

一种自流平水泥基环保地坪砂浆
技术领域
本发明涉及建筑材料领域，具体涉及一种自流平水泥基环保地坪砂浆。
背景技术
砂浆地坪是环氧树脂砂浆地坪的一种简称，环氧树脂砂浆是一种高快凝固、高粘度的混有砂浆灌浆料。现有的地坪砂浆材料多为普通的水泥砂浆粉料，在施工时现拌现用，砂浆性能的优劣决定地坪施工的质量，因现场无法保证砂浆的质量，施工后往往造成地坪起砂、起粉、平整度差、致密度差等问题。同时，由于普通水泥砂浆配方不够合理，凝固时间长，一般需要24小时才能完成初凝。
自流平砂浆是以无机胶凝材料、骨料、填料，并加入可再分散乳胶粉和少量化学添加剂，通过一定的生产工艺均匀混合成的粉状产品。自流平砂浆因其施工方便，施工质量好，强度高、耐磨性急抗渗性好，能够自动找平等优点，得到越来越多的推广应用。然而，由于自流平砂浆由多种材料组成，只有综合原料的质量、规格、成分、材料复配等的优化，才能获得合格的自流平砂浆。目前市售自流平砂浆存在着流平性、强度、耐磨性、缓凝时间不足等问题，影响自流平砂浆的施工质量。
发明内容
本发明针对现有自流平砂浆流平性、强度、耐磨性、缓凝时间等不足的问题，提供一种水泥基自流平环保砂浆。
本发明采取以下技术方案实现上述目的：
一种自流平水泥基环保地坪砂浆，其特征在于，以重量份计，各组分为：硅酸盐水泥100-400份，高铝水泥80-200份，石膏60-150份，矿粉20-240份，石英砂350-500份，聚羧酸减水剂2-4份，再分散乳胶粉10-60份，保水稳定剂1-4份，消泡剂0.5-5份，早强及复合缓凝剂2-5份。通过对材料配比的优化设计，合理利用废料，提高自流平砂浆的流平性、稳定性、强度、耐磨性、硬度等性能，缩短凝时间。
进一步的，为提高砂浆早强、高强、耐腐蚀等性能，所述高铝水泥为铝酸盐水泥或硫铝酸盐水泥中的任意一种。
进一步的，为提高工业副产物的利用，所述矿粉为硅灰。
进一步的，为提高保水效果，所述保水稳定剂由纤维素与橡胶粉复配而成。
进一步的，为提高保水效果，所述保水稳定剂由淀粉与橡胶粉复配而成。
进一步的，为提高早强及复合缓凝效果，早强及复合缓凝剂由锂酸盐、硼酸盐及葡萄糖酸盐复配而成。
进一步的，为提高早强及复合缓凝效果，所述早强及复合缓凝剂由有机早强剂与硼砂复配而成。
进一步的，为提复合效果，所述石膏为半水石膏或无水石膏中的任意一种。
本发明的有益效果是：
通过合理的材料配比，合理利用工业废料，采用复合保水稳定剂和早强及复合缓凝剂提高自流平砂浆的稳定性、流平性、强度、耐磨性等。
具体实施方式
下面结合具体实施例对本发明进行详细说明。
自流平水泥基地坪砂浆检测采用JC/T 985-2005《地面用水泥基自流平砂浆》标准，检测项目主要包括流动度、拉伸粘结强度、耐磨性、尺寸变化率、抗冲击性、24h抗折强度、24h抗压强度、28d抗折强度、28d抗压强度等。在实施例中，施工时，砂浆干粉与清水的比例为1:0.21，采用搅拌机充分混合后，进行施工，然后进行各种性能的测试。
实施例1：自流平水泥基环保地坪砂浆，以重量份计，各组分为：硅酸盐水泥100份，硫铝酸盐水泥80份，石膏60份，硅灰20份，石英砂350份，聚羧酸减水剂2份，再分散乳胶粉10份，保水稳定剂1份，消泡剂0.5份，早强及复合缓凝剂2份。
经过检测，实施例1产品施工后性能如表1所示。
表1 实施例1产品检测结果
实施例2：自流平水泥基环保地坪砂浆，以重量份计，各组分为：硅酸盐水泥250份，硫铝酸盐水泥150份，石膏110份，硅灰100份，石英砂430份，聚羧酸减水剂3份，再分散乳胶粉35份，保水稳定剂2.5份，消泡剂3份，早强及复合缓凝剂3份。
经过检测，实施例1产品施工后性能如表1所示。
表2 实施例2产品检测结果
实施例3：自流平水泥基环保地坪砂浆，，以重量份计，各组分为：硅酸盐水泥400份，硫铝酸盐水泥200份，石膏150份，硅灰240份，石英砂500份，聚羧酸减水剂4份，再分散乳胶粉160份，保水稳定剂4份，消泡剂5份，早强及复合缓凝剂5份。
表3 实施例3产品检测结果
综上，本发明产品自流平水泥基环保地坪砂浆具有优良的稳定性、流平性、强度、耐磨性等，性能超过了JC/T 985-2005《地面用水泥基自流平砂浆》标准。

Claims (8)

1.自流平水泥基环保地坪砂浆，其特征在于，以重量份计，各组分为：硅酸盐水泥100-400份，高铝水泥80-200份，石膏60-150份，矿粉20-240份，石英砂350-500份，聚羧酸减水剂2-4份，再分散乳胶粉10-60份，保水稳定剂1-4份，消泡剂0.5-5份，早强及复合缓凝剂2-5份。
2.如权利要求1所述的自流平水泥基环保地坪砂浆，其特征在于，所述高铝水泥为铝酸盐水泥或硫铝酸盐水泥中的任意一种。
3.如权利要求1所述的自流平水泥基环保地坪砂浆，其特征在于，所述矿粉为硅灰。
4.如权利要求1所述的自流平水泥基环保地坪砂浆，其特征在于，所述保水稳定剂由纤维素与橡胶粉复配而成。
5.如权利要求1所述的自流平水泥基环保地坪砂浆，其特征在于，所述保水稳定剂由淀粉与橡胶粉复配而成。
6.如权利要求1所述的自流平水泥基环保地坪砂浆，其特征在于，所述早强及复合缓凝剂由锂酸盐、硼酸盐、葡萄糖酸盐复配而成。
7.如权利要求1所述的自流平水泥基环保地坪砂浆，其特征在于，所述早强及复合缓凝剂由有机早强剂与硼砂复配而成。
8.如权利要求1-7所述的自流平水泥基环保地坪砂浆，其特征在于，所述石膏为半水石膏或无水石膏中的任意一种。
CN201610989937.5A 2016-11-10 2016-11-10 一种自流平水泥基环保地坪砂浆 Pending CN106747173A (zh)