CN112592146A - 自流平修补地坪材料 - Google Patents
自流平修补地坪材料 Download PDFInfo
- Publication number
- CN112592146A CN112592146A CN202110037358.1A CN202110037358A CN112592146A CN 112592146 A CN112592146 A CN 112592146A CN 202110037358 A CN202110037358 A CN 202110037358A CN 112592146 A CN112592146 A CN 112592146A
- Authority
- CN
- China
- Prior art keywords
- parts
- self
- leveling
- cement
- repairing material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种地坪材料，尤其是自流平修补地坪材料，由以下材料按照质量份数制成：半水石膏55～65份；骨料38～42份；水泥8～12份；重钙粉1～3份；减水剂0.1～0.3份；缓凝剂0.1～0.2份；保水剂0.1～0.2份；乳胶粉1～2份；消泡剂0.1～0.2份。本发明提供的自流平修补地坪材料使用时只需添加适量水搅拌，便可成为靠重力作用自发流平，无须人工抹平，强度高、塑性好、施工简便、耐磨损、稳定性佳、风格质朴简约，适用于混凝土地面的修补和精找平，质量均匀稳定，施工现场干净整洁，施工速度较传统人工抹面提高5～10倍，大幅缩短工期，降低人工费用。
Description
技术领域
本发明涉及一种地坪材料，尤其是自流平修补地坪材料。
背景技术
传统的地面修补和找平施工方法是将拌制好的普通水泥砂浆摊铺、刮平、抹面，在砂浆终凝前，还必须完成三遍压光等工序。这种多层作业法效率低，材料浪费严重，硬化后的地面平整度差，易磨损，常出现起砂起皮、空鼓开裂等质量问题，严重影响住宅的观感和使用效果。
发明内容
为解决上述问题，本发明提供一种施工简单、耐磨损、用料少、稳定性高、不易起皮、开裂的自流平修补地坪材料，具体技术方案为：
自流平修补地坪材料，由以下材料按照质量份数制成：
半水石膏55～65份；
骨料38～42份；
水泥8～12份；
重钙粉1～3份；
减水剂0.1～0.3份；
缓凝剂0.1～0.2份；
保水剂0.1～0.2份；
乳胶粉1～2份；
消泡剂0.1～0.2份。
优选的，所述水泥为硅酸盐水泥与铝酸盐水泥的混合物，所述硅酸盐水泥：铝酸盐水泥为5:1。
优选的，所述骨料为河砂，且为60～80目。
优选的，所述减水剂为萘系减水剂、聚羟酸减水剂或三聚氰胺减水剂中的一种。
优选的，所述保水剂为甲基纤维素醚，粘度为400mPa·s。
优选的，所述缓凝剂为碱性磷酸、柠檬酸或酒石酸中的一种。
优选的，所述消泡剂为有机硅油。
与现有技术相比本发明具有以下有益效果：
本发明提供的自流平修补地坪材料使用时只需添加适量水搅拌，便可成为靠重力作用自发流平，无须人工抹平，强度高、塑性好、施工简便、耐磨损、稳定性佳、风格质朴简约，适用于混凝土地面的修补和精找平，质量均匀稳定，施工现场干净整洁，施工速度较传统人工抹面提高5～10倍，大幅缩短工期，降低人工费用。
具体实施方式
现结合实施例对本发明作进一步说明。
自流平修补地坪材料，由以下材料按照质量份数制成：
半水石膏55～65份；
骨料38～42份；
水泥8～12份；
重钙粉1～3份；
减水剂0.1～0.3份；
缓凝剂0.1～0.2份；
保水剂0.1～0.2份；
乳胶粉1～2份；
消泡剂0.1～0.2份。
所述水泥为硅酸盐水泥与铝酸盐水泥的混合物，所述硅酸盐水泥：铝酸盐水泥为5:1。
所述骨料为河砂，且为60～80目。
所述减水剂为萘系减水剂、聚羟酸减水剂或三聚氰胺减水剂中的一种。
保水剂为甲基纤维素醚，粘度为400mPa·s。
所述缓凝剂为碱性磷酸、柠檬酸或酒石酸中的一种。
所述消泡剂为有机硅油。
减水剂通过分散磷建筑石膏颗粒，释放石膏颗粒遇水团聚所包裹的游离水，从而起到了提高浆体的流动性的效果。
以下实施例中，减水剂为聚羟酸，缓凝剂为柠檬酸。
实施例一
自流平修补地坪材料，由以下材料按照质量份数制成：
半水石膏55份；骨料38份；水泥8份；重钙粉1；减水剂0.1份；缓凝剂0.1份；保水剂0.1份；乳胶粉1份；消泡剂0.1份。
实施例二
自流平修补地坪材料，由以下材料按照质量份数制成：
半水石膏60份；骨料40份；水泥10份；重钙粉1份；减水剂0.1份；缓凝剂0.1份；保水剂0.1份；乳胶粉1份；消泡剂0.份。
实施例三
自流平修补地坪材料，由以下材料按照质量份数制成：
半水石膏65份；骨料42份；水泥12份；重钙粉1份；减水剂0.1份；缓凝剂0.1份；保水剂0.1份；乳胶粉1份；消泡剂0.1份。
实施例四
自流平修补地坪材料，由以下材料按照质量份数制成：
半水石膏60份；骨料40份；水泥10份；重钙粉2份；减水剂0.2份；缓凝剂0.1份；保水剂0.1份；乳胶粉1份；消泡剂0.1份。
实施例五
自流平修补地坪材料，由以下材料按照质量份数制成：
半水石膏60份；骨料40份；水泥10份；重钙粉2份；减水剂0.3份；缓凝剂0.1份；保水剂0.1份；乳胶粉1份；消泡剂0.1份。
实施例六
自流平修补地坪材料，由以下材料按照质量份数制成：
半水石膏60份；骨料40份；水泥10份；重钙粉2份；减水剂0.1份；缓凝剂0.1份；保水剂0.15份；乳胶粉1份；消泡剂0.1份。
实施例七
自流平修补地坪材料，由以下材料按照质量份数制成：
半水石膏60份；骨料40份；水泥10份；重钙粉2份；减水剂0.1份；缓凝剂0.1份；保水剂0.2份；乳胶粉1份；消泡剂0.1份。
实施例八
自流平修补地坪材料，由以下材料按照质量份数制成：
半水石膏60份；骨料40份；水泥10份；重钙粉2份；减水剂0.3份；缓凝剂0.1份；保水剂0.1份；乳胶粉1.5份；消泡剂0.1份。
实施例九
自流平修补地坪材料，由以下材料按照质量份数制成：
半水石膏60份；骨料40份；水泥10份；重钙粉2份；减水剂0.3份；缓凝剂0.1份；保水剂0.1份；乳胶粉2份；消泡剂0.1份。
砂浆流动度随纤维素醚掺量增加而降低。在没有添加纤维素醚时，砂浆中的水使得砂粒表面形成一层薄薄的水膜，这层水膜在砂浆体系中起到润滑作用，从而使自流平砂浆具有较好的流动性，当砂浆体系中添加了纤维素醚时，由于纤维素醚分子链中羟基和醚键与水之间形成了氢键，使得一部分水由自由水变成结合水，使得砂粒表面的水分减少，不能充分的形成水膜，从而增大了骨料之间的摩擦力，并且由于纤维素醚分子在砂浆中形成的立体网络结构，导致砂浆的流动度降低。
纤维素醚的保水性使得砂浆可以在长时间内使得砂浆内部保持水分促使水泥水化，同时纤维素醚在砂浆体系中形成的立体网络结构也会产生一定积极作用；当纤维素醚掺量过多时，纤维素醚使得过多的水分留在砂浆内部，当水分蒸发掉后留下气孔，砂浆内空隙增多，在受力时产生应力集中，加剧微裂纹的发展，同时纤维素醚吸附在水泥水化表面，抑制水泥水化，从而强度会有一定的下降。
聚羧酸减水剂对砂浆的流动性有较好的改善，当聚羧酸减水剂掺入到水泥浆体中时，减水剂分子中的憎水基与水泥颗粒表面吸附在一起，亲水基端朝向水溶液，水泥颗粒被减水剂分子所包围，而且分子定向吸附，导致水泥颗粒表面带有同种电荷，使水泥颗粒相互排斥。由于减水剂分子的存在，使水泥与水分离开来，将其束缚的游离水释放出来，大大提高了砂浆的流动性。当减水剂掺量在一定范围时，随着聚羧酸减水剂掺量的提高，水泥砂浆流动性也随之改善。随着减水剂掺量的增加，水泥对减水剂的吸附趋于饱和，流动度改善不再大幅度提升。继续增加减水剂加掺量，将不能使砂浆流动度继续大幅度增加。
乳胶粉在亲水性保护胶体的作用下，一部分水被保护胶体吸附，使之成为结合水，流动度减小。当乳胶粉超过一定量时，这是因为乳胶粉在亲水性保护胶体和搅拌时的机械剪切力下，乳胶粉颗粒迅速分散到砂浆体系中，并很快形成一层薄膜，在这过程中，会使得砂浆气体含量增加，从而起到引气的效果，起到类似于引气型减水剂的作用，又会使流动度增加。此时引气效果对流动度的影响大于吸附水对流动度的影响。
自流平修补地坪材料与国标要求对比表：
自流平砂浆的流动度、收缩性能等试验均按照标准JC/T 985—2017《地面用水泥基自流平砂浆》规定进行；凝结时间测试参照 GB/J 1346—2011《水泥标准稠度用水量、凝结时间、安定性检验方法》；砂浆强度测试参照 GB/J 17671—1999《水泥胶砂强度检验方法》。
采用自流平修补地坪材料制作的地坪尺寸准确、平整度高、舒适有弹性、保温隔声，干密度仅1600 kg/m3，比传统混凝土轻 30%，可有效降低建筑载荷，提高抗震等级。 石膏本身具有微膨胀性和良好热稳定性，相应的石膏砂浆体积稳定性佳、不易空鼓，也不易产生收缩裂缝。硬化时间短，4～6 h可上人行走，24 h强度可达设计强度90% 以上，1～2d可进行饰面层施工。施工厚度为3～80mm ，可根据地面高差及设计强度自由选择，机械化泵送，自动化浇筑，单机施工面积可达2000m2/d。回填找平一次完成，无需后期养护，尤其适用于地面采暖系统，一次施工即可达成地暖管覆盖和地面找平，与需二次找平的水泥基砂浆相比优点突出。
Claims (7)
1.自流平修补地坪材料，其特征在于，由以下材料按照质量份数制成：
半水石膏55～65份；
骨料38～42份；
水泥8～12份；
重钙粉1～3份；
减水剂0.1～0.3份；
缓凝剂0.1～0.2份；
保水剂0.1～0.2份；
乳胶粉1～2份；
消泡剂0.1～0.2份。
2.根据权利要求1所述的自流平修补地坪材料，其特征在于，
所述水泥为硅酸盐水泥与铝酸盐水泥的混合物，所述硅酸盐水泥：铝酸盐水泥为5:1。
3.根据权利要求1所述的自流平修补地坪材料，其特征在于，
所述骨料为河砂，且为60～80目。
4.根据权利要求1所述的自流平修补地坪材料，其特征在于，
所述减水剂为萘系减水剂、聚羟酸减水剂或三聚氰胺减水剂中的一种。
5.根据权利要求1所述的自流平修补地坪材料，其特征在于，
所述保水剂为甲基纤维素醚，粘度为400mPa·s。
6.根据权利要求1所述的自流平修补地坪材料，其特征在于，
所述缓凝剂为碱性磷酸、柠檬酸或酒石酸中的一种。
7.根据权利要求1所述的自流平修补地坪材料，其特征在于，
所述消泡剂为有机硅油。