CN113943940A - 一种暖通空调水系统成套保运方法 - Google Patents
一种暖通空调水系统成套保运方法 Download PDFInfo
- Publication number
- CN113943940A CN113943940A CN202111201649.6A CN202111201649A CN113943940A CN 113943940 A CN113943940 A CN 113943940A CN 202111201649 A CN202111201649 A CN 202111201649A CN 113943940 A CN113943940 A CN 113943940A
- Authority
- CN
- China
- Prior art keywords
- water
- cleaning
- agent
- corrosion
- air conditioning
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种暖通空调水系统成套保运方法,包括以下步骤:步骤S1、清洗预膜;步骤S2、日常维护运行:采用无磷全有机产品作为缓蚀阻垢剂,不增加TDS,不增加磷含量,采用长效半衰期时间长的抑菌剂作为杀菌剂。本发明清洗预膜时采用全有机无磷预膜剂,结束预膜时不需要排污置换水质,直接可以运行;还在于日常维护运行时添加的缓蚀阻垢剂也是全有机无磷配方,可以实现敞开式循环水系统高倍率浓缩运行,真正意义上实现了暖通空调水处理的节能环保目标。
Description
技术领域
本发明涉及一种暖通空调水处理系统的防腐、阻垢、杀菌和水质稳定控制方法,尤其涉及一种暖通空调水系统成套保运方法,属于暖通空调水系统保运技术领域。
背景技术
当前社会,建筑正在朝着智能化的方向发展,人们为了更好的保障建筑室内的空气湿度和温度,维护良好的居住环境,暖通空调的安装成了现代建筑中的重要组成部分。中央空调水系统一般分为三个部分:循环水系统、冷冻水系统、采暖水系统。循环冷却水多为开式,冷冻及采暖水为封闭式。大多数高层建筑或集中供热、供冷建筑的冷冻水与采暖水多为同一系统,即在夏季走冷冻水,冬季走采暖水。
随着系统运行年限的延长,暖通空调水系统存在以下问题:结垢、腐蚀、微生物滋生以及由此而引起的水质二次污染、色度、浊度的提高,生物粘泥的积累。如不进行适当的处理,势必会引起系统出现一系列问题,如管道流通截面积的缩小甚至堵塞、腐蚀泄漏、传热效率降低,运行费用的提高、能源的浪费,都将影响供暖、空调系统的正常工作。
随时时代的不断发展进步,暖通空调系统未来的发展路径也将不断朝向节能、环保、可持续性方向过渡,所以,需要对暖通空调技术问题进行深入探索研究,这需要综合暖通、给排水、化学水处理、热工仪表自动化等多方技术,来形成一套完整的保运技术。
发明内容
为了解决上述技术所存在的不足之处,本发明提供了一种暖通空调水系统成套保运方法,其主要目的是提供一套完整的暖通空调冷却水保运方法,使其从新系统投运时,就开始布局控制,防止问题产生,同时针对旧系统,提供独特的保运方法。
为了解决以上技术问题,本发明采用的技术方案是:一种暖通空调水系统成套保运方法,包括以下步骤:
步骤S1、清洗预膜;
步骤S2、日常维护运行:采用无磷全有机产品作为缓蚀阻垢剂,不增加TDS,不增加磷含量,采用长效半衰期时间长的抑菌剂作为杀菌剂。
优选的,步骤S1中,对于新系统,投运前要进行油污、焊渣清洗,并在金属材质表面预膜;对于长期运行的旧系统,要进行杀菌、粘泥剥离清洗,还要进行除锈酸洗,使干净的金属表面暴露于水中后,再进行预膜;
步骤S1的具体实施方法为:
S11、系统进行降低水量操作:首先应将冷却塔水位降低至最低运转水位,密闭系统则无需此操作;
S12、杀菌剥离/油污清洗;
S13、铁锈清洗;
S14、预膜处理。
优选的,步骤S12包括以下过程:
A、旧系统杀菌粘泥剥离清洗:
采用次氯酸钠作为杀菌灭藻剂,加药量为900-1100ppm,按照系统保有水量添加,期间维持余氯0.5ppm以上,运行16-24h;
然后将系统中水质进行排污置换,置换至浊度低于20NTU;所用粘泥剥离剂为异噻唑啉酮、季铵盐、布罗波尔杀菌剂中的一种或两种,加药量为200-400ppm,按照系统保有水量进行投加,剥离运行23-25h;
B、新系统油污清洗:
所用油污清洗剂为阴离子表面活性剂,按照保有水量添加400-600ppm,根据泡沫情况,选择性添加有机硅类消泡剂。
优选的,步骤S13中,铁锈清洗时,所用酸洗清洗剂为柠檬酸、氨基磺酸的一种或两种,按照保有水量添加300-500ppm,同时用硫酸调整pH值为2-3之间,期间添加酸洗缓蚀剂以防止系统腐蚀;酸洗至酸洗液中铁离子含量维持平衡,然后进行排污置换至浊度小于20NTU。
优选的,步骤S14中,使用的预膜剂为有机胺复配产品,有机胺复配产品为N,N-二仲丁基对苯二胺、N,N-二甲基乙醇胺、妥尔油基脂肪酸铵按照质量比为0.8-1.2:2.8-3.2:1.8-3.2配置成浓度为900-1100ppm的溶液;
按照保有水量添加上述配制好的预膜剂,同时挂入监控挂片,然后运转46-50h,取出挂片监测预膜效果。
优选的,步骤S2的具体实施过程如下:
S21、了解系统参数,根据系统参数计算缓蚀阻垢剂和杀菌剂的加药量;
S22、检测补水水质,根据系统参数确定浓缩倍数,密闭系统无需确定;
S23、按照加药量将缓蚀阻垢剂添加到系统中,同时挂入挂片监控;
S24、每半个月补加一次药剂;
S25、每月检测一次水质,重点检测PH、TDS、硬度、氯离子、硫酸根、碱度、全铁、浊度;
S26、根据水质监测结果调整加药量。
优选的,缓蚀阻垢剂为无磷全有机产品即聚环氧琥珀酸,杀菌剂为异噻唑啉酮、布罗波尔中的一种。
本发明主要涵盖新系统投运前、旧系统定期清理的清洗预膜方法,以及系统在夏冬季节介质为热水和冷水运行时的保运方法。其主要目标是,保证暖通空调水系统防腐、阻垢、杀菌及稳定水质,创新点是所使用的主要化学品为无磷有机产品,不会造成水体富营养化,同时不增加水系统的TDS(总溶解固体)。特别是全有机无磷预膜剂和无磷缓蚀阻垢剂,预膜结束后,无需像传统方法一样排污置换水质,可直接补加运行药剂运行。可以使水系统水质高倍率浓缩,降低水的消耗量,真正意义上实现节能环保保运。
本发明与传统暖通空调水处理方法相比,主要在于清洗预膜时采用全有机无磷预膜剂,结束预膜时不需要排污置换水质,直接可以运行;还在于日常维护运行时添加的缓蚀阻垢剂也是全有机无磷配方,可以实现敞开式循环水系统高倍率浓缩运行,真正意义上实现了暖通空调水处理的节能环保目标。
具体实施方式
下面结合具体实施方式对本发明作进一步详细的说明。
一种暖通空调水系统成套保运方法,包括以下步骤:
步骤S1、清洗预膜:对于新系统,投运前要进行油污、焊渣清洗,并在金属材质表面预膜;对于长期运行的旧系统,要进行杀菌、粘泥剥离清洗,还要进行除锈酸洗,使干净的金属表面暴露于水中后,再进行预膜;
具体实施方法为:
S11、系统进行降低水量操作:首先应将冷却塔水位降低至最低运转水位,密闭系统则无需此操作;
S12、杀菌剥离/油污清洗;具体包括以下过程:
A、旧系统杀菌粘泥剥离清洗:(向管道中加药清洗即可)
采用次氯酸钠作为杀菌灭藻剂,加药量为900-1100ppm,按照系统保有水量添加,期间维持余氯0.5ppm以上,运行16-24h;
然后将系统中水质进行排污置换,置换至浊度低于20NTU;所用粘泥剥离剂为异噻唑啉酮、季铵盐、布罗波尔杀菌剂中的一种或两种,加药量为200-400ppm,按照系统保有水量进行投加,剥离运行23-25h;
B、新系统油污清洗:
所用油污清洗剂为阴离子表面活性剂(采用磺酸盐类阴离子表面活性剂:十二烷基苯磺酸钠、烷基苯磺酸钠中的一种),按照保有水量添加400-600ppm,根据泡沫情况,选择性添加有机硅类消泡剂。根据是否影响现场的生产情况决定是否要添加消泡剂。
S13、铁锈清洗;铁锈清洗时,所用酸洗清洗剂为柠檬酸、氨基磺酸的一种或两种,按照保有水量添加300-500ppm,同时用硫酸调整pH值为2-3之间,期间添加酸洗缓蚀剂以防止系统腐蚀;酸洗至酸洗液中铁离子含量维持平衡(多次检测后,铁离子的浓度保持不变时为平衡),然后进行排污置换至浊度小于20NTU。
S14、预膜处理:使用的预膜剂为有机胺复配产品,有机胺复配产品为N,N-二仲丁基对苯二胺、N,N-二甲基乙醇胺、妥尔油基脂肪酸铵按照质量比为0.8-1.2:2.8-3.2:1.8-3.2配置成浓度为900-1100ppm的溶液;
按照保有水量添加上述配制好的预膜剂,同时挂入监控挂片,然后运转46-50h,取出挂片监测预膜效果。
预膜处理:使用的预膜剂为有机胺复配产品,而非传统意义的磷锌预膜剂,采用无磷全有机预膜剂,不会增加磷含量,也不会增加水质TDS。最重要的一点是清洗预膜结束后,不需要像传统预膜方法一样将混浊水质排污置换,该预膜剂水质一直比较清澈,不影响系统运行。
有机胺复合预膜剂能在金属表面形成一层致密的吸附膜,像保护伞一样防止氯离子等腐蚀离子接触,防止电化学反应的发生;而且该预膜剂,不需要像传统预膜剂一样,对水质有要求,且预膜过程中,也无需检测磷含量,大大降低了检测成本。
致密吸附膜的形成机理:
以N,N-二仲丁基对苯二胺作为主要膜胺,分子中含亲水基团-NH和亲油基烷基,投加到水中后,氨基(亲水基)吸附在金属表面,烷基(亲油基)朝外腐蚀环境。吸附在金属表面后形成一层吸附膜,吸附膜中的烷基发挥遮蔽作用,阻止水、氯离子和氧等腐蚀性物质和金属接触,起到防止金属腐蚀的作用,同时能够透过金属表面上已存在的腐蚀产物或污垢面而逐渐在金属表面形成保护膜。
N,N-二甲基乙醇胺能够改变金属腐蚀的阳极电化学过程:分子中含有氨基和羟基等官能团,其上的N、O等杂原子具有孤对电子,可以和金属原子发生配位作用,在金属表面阳极区与金属离子作用,生成氧化物或氢氧化物氧化膜,吸附在金属表面形成保护膜,抑制金属向水中溶解。同时分子中的烷基(亲油基)形成疏水保护层,阻止水、氯离子和氧等腐蚀性物质和金属接触,起到防止金属腐蚀的作用。
妥尔油基脂肪酸铵为18碳的不饱和脂肪酸铵混合物,镀膜作用与上述N,N-二甲基乙醇胺类似,但其中含有铵根离子,在碱性条件下受热分解出一水合氨,在协同金属镀膜的过程中起到调节PH及分散剂的作用。协同作用下最终在金属表面形成一层致密、持续和疏水性的保护膜,提高金属防腐蚀能力。
步骤S2、日常维护运行:暖通空调水系统清洗预膜固然关键,但是日常维护运行更加关键。采用无磷全有机产品(聚环氧琥珀酸)作为缓蚀阻垢剂,不增加TDS,不增加磷含量,采用长效半衰期时间长的抑菌剂(异噻唑啉酮、布罗波尔)作为杀菌剂,可以使密闭系统长时间运行不加药剂,也可以使开放式系统高倍率运行,降低水的消耗量,真正实现节能环保。
其具体实施过程如下:
S21、了解系统参数(参数包括保有水量、循环水量、换热温差、系统材质、补水水源、循环水水质),根据系统参数计算缓蚀阻垢剂和杀菌剂的加药量;根据计算软件计算的加药量,每个公司有自己的计算系统,根据输入的参数进行计算。
S22、检测补水水质,根据系统参数确定浓缩倍数,密闭系统无需确定;
S23、按照加药量将缓蚀阻垢剂添加到系统中,同时挂入挂片监控;
S24、每半个月补加一次药剂;
S25、每月检测一次水质,重点检测PH、TDS、硬度、氯离子、硫酸根、碱度、全铁、浊度;
S26、根据水质监测结果调整加药量。
缓蚀阻垢剂为无磷全有机产品即聚环氧琥珀酸,杀菌剂为异噻唑啉酮、布罗波尔中的一种。
下面通过实施例对本申请作进一步的说明。
实施例一
一种暖通空调水系统成套保运方法,包括以下步骤:
步骤S1、清洗预膜:对于新系统,投运前要进行油污、焊渣清洗,并在金属材质表面预膜;对于长期运行的旧系统,要进行杀菌、粘泥剥离清洗,还要进行除锈酸洗,使干净的金属表面暴露于水中后,再进行预膜;
具体实施方法为:
S11、系统进行降低水量操作:首先应将冷却塔水位降低至最低运转水位,密闭系统则无需此操作;
S12、杀菌剥离/油污清洗;具体包括以下过程:
A、旧系统杀菌粘泥剥离清洗:(向管道中加药清洗即可)
采用次氯酸钠作为杀菌灭藻剂,加药量为900ppm,按照系统保有水量添加,期间维持余氯0.5ppm以上,运行16h;
然后将系统中水质进行排污置换,置换至浊度低于20NTU;所用粘泥剥离剂为异噻唑啉酮、季铵盐、布罗波尔杀菌剂中的一种或两种,加药量为200ppm,按照系统保有水量进行投加,剥离运行23h;
B、新系统油污清洗:
所用油污清洗剂为阴离子表面活性剂(采用磺酸盐类阴离子表面活性剂:十二烷基苯磺酸钠、烷基苯磺酸钠中的一种),按照保有水量添加400ppm,根据泡沫情况,选择性添加有机硅类消泡剂。根据是否影响现场的生产情况决定是否要添加消泡剂。
S13、铁锈清洗;铁锈清洗时,所用酸洗清洗剂为柠檬酸、氨基磺酸的一种或两种,按照保有水量添加300ppm,同时用硫酸调整pH值为2,期间添加酸洗缓蚀剂以防止系统腐蚀;酸洗至酸洗液中铁离子含量维持平衡(多次检测后,铁离子的浓度保持不变时为平衡),然后进行排污置换至浊度小于20NTU。
S14、预膜处理:使用的预膜剂为有机胺复配产品,有机胺复配产品为N,N-二仲丁基对苯二胺、N,N-二甲基乙醇胺、妥尔油基脂肪酸铵按照质量比为0.8:2.8:1.8配置成浓度为900ppm的溶液;
按照保有水量添加上述配制好的预膜剂,同时挂入监控挂片,然后运转46h,取出挂片监测预膜效果。
步骤S2、日常维护运行:暖通空调水系统清洗预膜固然关键,但是日常维护运行更加关键。采用无磷全有机产品(聚环氧琥珀酸)作为缓蚀阻垢剂,不增加TDS,不增加磷含量,采用长效半衰期时间长的抑菌剂(异噻唑啉酮、布罗波尔)作为杀菌剂,可以使密闭系统长时间运行不加药剂,也可以使开放式系统高倍率运行,降低水的消耗量,真正实现节能环保。
其具体实施过程如下:
S21、了解系统参数(参数包括保有水量、循环水量、换热温差、系统材质、补水水源、循环水水质),根据系统参数计算缓蚀阻垢剂和杀菌剂的加药量;根据计算软件计算的加药量,每个公司有自己的计算系统,根据输入的参数进行计算。
S22、检测补水水质,根据系统参数确定浓缩倍数,密闭系统无需确定;
S23、按照加药量将缓蚀阻垢剂添加到系统中,同时挂入挂片监控;
S24、每半个月补加一次药剂;
S25、每月检测一次水质,重点检测PH、TDS、硬度、氯离子、硫酸根、碱度、全铁、浊度;
S26、根据水质监测结果调整加药量。
实施例二
一种暖通空调水系统成套保运方法,包括以下步骤:
步骤S1、清洗预膜:对于新系统,投运前要进行油污、焊渣清洗,并在金属材质表面预膜;对于长期运行的旧系统,要进行杀菌、粘泥剥离清洗,还要进行除锈酸洗,使干净的金属表面暴露于水中后,再进行预膜;
具体实施方法为:
S11、系统进行降低水量操作:首先应将冷却塔水位降低至最低运转水位,密闭系统则无需此操作;
S12、杀菌剥离/油污清洗;具体包括以下过程:
A、旧系统杀菌粘泥剥离清洗:(向管道中加药清洗即可)
采用次氯酸钠作为杀菌灭藻剂,加药量为1100ppm,按照系统保有水量添加,期间维持余氯0.5ppm以上,运行24h;
然后将系统中水质进行排污置换,置换至浊度低于20NTU;所用粘泥剥离剂为异噻唑啉酮、季铵盐、布罗波尔杀菌剂中的一种或两种,加药量为400ppm,按照系统保有水量进行投加,剥离运行25h;
B、新系统油污清洗:
所用油污清洗剂为阴离子表面活性剂(采用磺酸盐类阴离子表面活性剂:十二烷基苯磺酸钠、烷基苯磺酸钠中的一种),按照保有水量添加600ppm,根据泡沫情况,选择性添加有机硅类消泡剂。根据是否影响现场的生产情况决定是否要添加消泡剂。
S13、铁锈清洗;铁锈清洗时,所用酸洗清洗剂为柠檬酸、氨基磺酸的一种或两种,按照保有水量添加500ppm,同时用硫酸调整pH值为3,期间添加酸洗缓蚀剂以防止系统腐蚀;酸洗至酸洗液中铁离子含量维持平衡(多次检测后,铁离子的浓度保持不变时为平衡),然后进行排污置换至浊度小于20NTU。
S14、预膜处理:使用的预膜剂为有机胺复配产品,有机胺复配产品为N,N-二仲丁基对苯二胺、N,N-二甲基乙醇胺、妥尔油基脂肪酸铵按照质量比为1.2:3.2:3.2配置成浓度为1100ppm的溶液;
按照保有水量添加上述配制好的预膜剂,同时挂入监控挂片,然后运转50h,取出挂片监测预膜效果。
步骤S2、日常维护运行:暖通空调水系统清洗预膜固然关键,但是日常维护运行更加关键。采用无磷全有机产品(聚环氧琥珀酸)作为缓蚀阻垢剂,不增加TDS,不增加磷含量,采用长效半衰期时间长的抑菌剂(异噻唑啉酮、布罗波尔)作为杀菌剂,可以使密闭系统长时间运行不加药剂,也可以使开放式系统高倍率运行,降低水的消耗量,真正实现节能环保。
其具体实施过程如下:
S21、了解系统参数(参数包括保有水量、循环水量、换热温差、系统材质、补水水源、循环水水质),根据系统参数计算缓蚀阻垢剂和杀菌剂的加药量;根据计算软件计算的加药量,每个公司有自己的计算系统,根据输入的参数进行计算。
S22、检测补水水质,根据系统参数确定浓缩倍数,密闭系统无需确定;
S23、按照加药量将缓蚀阻垢剂添加到系统中,同时挂入挂片监控;
S24、每半个月补加一次药剂;
S25、每月检测一次水质,重点检测PH、TDS、硬度、氯离子、硫酸根、碱度、全铁、浊度;
S26、根据水质监测结果调整加药量。
实施例三
一种暖通空调水系统成套保运方法,包括以下步骤:
步骤S1、清洗预膜:对于新系统,投运前要进行油污、焊渣清洗,并在金属材质表面预膜;对于长期运行的旧系统,要进行杀菌、粘泥剥离清洗,还要进行除锈酸洗,使干净的金属表面暴露于水中后,再进行预膜;
具体实施方法为:
S11、系统进行降低水量操作:首先应将冷却塔水位降低至最低运转水位,密闭系统则无需此操作;
S12、杀菌剥离/油污清洗;具体包括以下过程:
A、旧系统杀菌粘泥剥离清洗:(向管道中加药清洗即可)
采用次氯酸钠作为杀菌灭藻剂,加药量为1000ppm,按照系统保有水量添加,期间维持余氯0.5ppm以上,运行20h;
然后将系统中水质进行排污置换,置换至浊度低于20NTU;所用粘泥剥离剂为异噻唑啉酮、季铵盐、布罗波尔杀菌剂中的一种或两种,加药量为300ppm,按照系统保有水量进行投加,剥离运行24h;
B、新系统油污清洗:
所用油污清洗剂为阴离子表面活性剂(采用磺酸盐类阴离子表面活性剂:十二烷基苯磺酸钠、烷基苯磺酸钠中的一种),按照保有水量添加500ppm,根据泡沫情况,选择性添加有机硅类消泡剂。根据是否影响现场的生产情况决定是否要添加消泡剂。
S13、铁锈清洗;铁锈清洗时,所用酸洗清洗剂为柠檬酸、氨基磺酸的一种或两种,按照保有水量添加400ppm,同时用硫酸调整pH值为2.5,期间添加酸洗缓蚀剂以防止系统腐蚀;酸洗至酸洗液中铁离子含量维持平衡(多次检测后,铁离子的浓度保持不变时为平衡),然后进行排污置换至浊度小于20NTU。
S14、预膜处理:使用的预膜剂为有机胺复配产品,有机胺复配产品为N,N-二仲丁基对苯二胺、N,N-二甲基乙醇胺、妥尔油基脂肪酸铵按照质量比为1:3:2配置成浓度为1000ppm的溶液;
按照保有水量添加上述配制好的预膜剂,同时挂入监控挂片,然后运转48h,取出挂片监测预膜效果。
步骤S2、日常维护运行:暖通空调水系统清洗预膜固然关键,但是日常维护运行更加关键。采用无磷全有机产品(聚环氧琥珀酸)作为缓蚀阻垢剂,不增加TDS,不增加磷含量,采用长效半衰期时间长的抑菌剂(异噻唑啉酮、布罗波尔)作为杀菌剂,可以使密闭系统长时间运行不加药剂,也可以使开放式系统高倍率运行,降低水的消耗量,真正实现节能环保。
其具体实施过程如下:
S21、了解系统参数(参数包括保有水量、循环水量、换热温差、系统材质、补水水源、循环水水质),根据系统参数计算缓蚀阻垢剂和杀菌剂的加药量;根据计算软件计算的加药量,每个公司有自己的计算系统,根据输入的参数进行计算。
S22、检测补水水质,根据系统参数确定浓缩倍数,密闭系统无需确定;
S23、按照加药量将缓蚀阻垢剂添加到系统中,同时挂入挂片监控;
S24、每半个月补加一次药剂;
S25、每月检测一次水质,重点检测PH、TDS、硬度、氯离子、硫酸根、碱度、全铁、浊度;
S26、根据水质监测结果调整加药量。
上述实施方式并非是对本发明的限制,本发明也并不仅限于上述举例,本技术领域的技术人员在本发明的技术方案范围内所做出的变化、改型、添加或替换,也均属于本发明的保护范围。
Claims (7)
1.一种暖通空调水系统成套保运方法,其特征在于:所述方法包括以下步骤:
步骤S1、清洗预膜;
步骤S2、日常维护运行:采用无磷全有机产品作为缓蚀阻垢剂,不增加TDS,不增加磷含量,采用长效半衰期时间长的抑菌剂作为杀菌剂。
2.根据权利要求1所述的暖通空调水系统成套保运方法,其特征在于:所述步骤S1中,对于新系统,投运前要进行油污、焊渣清洗,并在金属材质表面预膜;对于长期运行的旧系统,要进行杀菌、粘泥剥离清洗,还要进行除锈酸洗,使干净的金属表面暴露于水中后,再进行预膜;
步骤S1的具体实施方法为:
S11、系统进行降低水量操作:首先应将冷却塔水位降低至最低运转水位,密闭系统则无需此操作;
S12、杀菌剥离/油污清洗;
S13、铁锈清洗;
S14、预膜处理。
3.根据权利要求2所述的暖通空调水系统成套保运方法,其特征在于:所述步骤S12包括以下过程:
A、旧系统杀菌粘泥剥离清洗:
采用次氯酸钠作为杀菌灭藻剂,加药量为900-1100ppm,按照系统保有水量添加,期间维持余氯0.5ppm以上,运行16-24h;
然后将系统中水质进行排污置换,置换至浊度低于20NTU;所用粘泥剥离剂为异噻唑啉酮、季铵盐、布罗波尔杀菌剂中的一种或两种,加药量为200-400ppm,按照系统保有水量进行投加,剥离运行23-25h;
B、新系统油污清洗:
所用油污清洗剂为阴离子表面活性剂,按照保有水量添加400-600ppm,根据泡沫情况,选择性添加有机硅类消泡剂。
4.根据权利要求2所述的暖通空调水系统成套保运方法,其特征在于:所述步骤S13中,铁锈清洗时,所用酸洗清洗剂为柠檬酸、氨基磺酸的一种或两种,按照保有水量添加300-500ppm,同时用硫酸调整pH值为2-3之间,期间添加酸洗缓蚀剂以防止系统腐蚀;酸洗至酸洗液中铁离子含量维持平衡,然后进行排污置换至浊度小于20NTU。
5.根据权利要求2所述的暖通空调水系统成套保运方法,其特征在于:所述步骤S14中,使用的预膜剂为有机胺复配产品,有机胺复配产品为N,N-二仲丁基对苯二胺、N,N-二甲基乙醇胺、妥尔油基脂肪酸铵按照质量比为0.8-1.2:2.8-3.2:1.8-3.2配置成浓度为900-1100ppm的溶液;
按照保有水量添加上述配制好的预膜剂,同时挂入监控挂片,然后运转46-50h,取出挂片监测预膜效果。
6.根据权利要求1所述的暖通空调水系统成套保运方法,其特征在于:所述步骤S2的具体实施过程如下:
S21、了解系统参数,根据系统参数计算缓蚀阻垢剂和杀菌剂的加药量;
S22、检测补水水质,根据系统参数确定浓缩倍数,密闭系统无需确定;
S23、按照加药量将缓蚀阻垢剂添加到系统中,同时挂入挂片监控;
S24、每半个月补加一次药剂;
S25、每月检测一次水质,重点检测PH、TDS、硬度、氯离子、硫酸根、碱度、全铁、浊度;
S26、根据水质监测结果调整加药量。
7.根据权利要求6所述的暖通空调水系统成套保运方法,其特征在于:所述步骤S2中,所述缓蚀阻垢剂为无磷全有机产品即聚环氧琥珀酸,所述杀菌剂为异噻唑啉酮、布罗波尔中的一种。