CN113930082A - 一种环保型纸质餐具加工覆膜材料及其制备方法 - Google Patents
一种环保型纸质餐具加工覆膜材料及其制备方法 Download PDFInfo
- Publication number
- CN113930082A CN113930082A CN202111222707.3A CN202111222707A CN113930082A CN 113930082 A CN113930082 A CN 113930082A CN 202111222707 A CN202111222707 A CN 202111222707A CN 113930082 A CN113930082 A CN 113930082A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- water chestnut
- paper tableware
- sodium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种环保型纸质餐具加工覆膜材料及其制备方法，按重量组分配比包括有以下组分：荸荠皮30‑50份、纤维素酶1‑5份、柠檬酸5‑10份、柠檬酸钠8‑16份、羧甲基纤维素钠2‑10份、海藻酸钠10‑20份、甘油8‑16份、玉米淀粉20‑30份，本发明涉及环保型纸质餐具技术领域。本发明，解决了纸质餐具易吸水，不能长时间存放食物的问题。
Description
技术领域
本发明涉及环保型纸质餐具技术领域，特别是涉及一种环保型纸质餐具加工覆膜材料及其制备方法。
背景技术
现有技术中，纸质餐具易吸水，不能长时间存放食物，所以我们提出了一种环保型纸质餐具加工覆膜材料，覆在环保型纸质餐具表面，以达到隔水的目的。
发明内容
为了解决纸质餐具易吸水，不能长时间存放食物的问题，本发明的目的是提供一种环保型纸质餐具加工覆膜材料及其制备方法。
为了实现上述目的，本发明采用如下技术方案：一种环保型纸质餐具加工覆膜材料，按重量组分配比包括有以下组分：
荸荠皮30-50份、纤维素酶1-5份、柠檬酸5-10份、柠檬酸钠8-16份、羧甲基纤维素钠2-10份、海藻酸钠10-20份、甘油8-16份、玉米淀粉20-30份。
优选的，按重量组分配比包括有以下组分：
荸荠皮31份、纤维素酶1.5份、柠檬酸5.8份、柠檬酸钠9份、羧甲基纤维素钠3份、海藻酸钠11份、甘油9份、玉米淀粉21份。
优选的，按重量组分配比包括有以下组分：
荸荠皮40份、纤维素酶2.5份、柠檬酸7份、柠檬酸钠9份、羧甲基纤维素钠5份、海藻酸钠15份、甘油11份、玉米淀粉25份。
优选的，按重量组分配比包括有以下组分：
荸荠皮48份、纤维素酶4份、柠檬酸9份、柠檬酸钠15份、羧甲基纤维素钠9份、海藻酸钠18份、甘油15份、玉米淀粉28份。
一种环保型纸质餐具加工覆膜材料的制备方法，包括有以下步骤：
S1，准备原材料：荸荠皮、纤维素酶、柠檬酸、柠檬酸钠、羧甲基纤维素钠、海藻酸钠、甘油、玉米淀粉；
S2，制备干荸荠粉；
S3，制备多糖的提取液；
S4，制备覆膜液，并进行密封。
优选的，所述S2中，将取得的荸荠皮在50-66℃条件下进行烘干，3-5h后取出，用高速粉碎机粉碎，制得干荸荠粉。
优选的，所述S3中，干荸荠粉加入纤维素酶，pH为5，溶剂水和干荸荠粉的料液比为15∶1，在40-60℃条件下水浴酶解1-2.5h，然后水浴，温度80-95℃时间50-60min，在3000-4000r/min的条件下离心10-18min，取上层清液，为提取液。
优选的，所述S4中，提取液、柠檬酸、柠檬酸钠、羧甲基纤维素钠、海藻酸钠、玉米淀粉、甘油混合，于50-65℃水浴锅中搅拌至完全溶解，冷却后再加入甘油，在-0.9～-0.95MPa下用真空脱气装罐密封。
与现有技术相比，本发明实现的有益效果：本发明，制得的覆膜材料覆在环保型纸质餐具表面，以达到隔水的目的；本发明，制得的覆膜材料为食品级覆膜材料，保证了食客的人体健康；本发明，在制备覆膜材料过程中环保无污染。
附图说明
以下结合附图和具体实施方式来进一步详细说明本发明：
图1为本发明的制备方法流程的示意图。
具体实施方式
以下由特定的具体实施例说明本发明的实施方式，熟悉此技术的人士可由本说明书所揭露的内容轻易地了解本发明的其他优点及功效。
请参阅图1。须知，本说明书所附图式所绘示的结构、比例、大小等，均仅用以配合说明书所揭示的内容，以供熟悉此技术的人士了解与阅读，并非用以限定本发明可实施的限定条件，故不具技术上的实质意义，任何结构的修饰、比例关系的改变或大小的调整，在不影响本发明所能产生的功效及所能达成的目的下，均应仍落在本发明所揭示的技术内容得能涵盖的范围内。同时，本说明书中所引用的如“上”、“下”、“左”、“右”、“中间”及“一”等的用语，亦仅为便于叙述的明了，而非用以限定本发明可实施的范围，其相对关系的改变或调整，在无实质变更技术内容下，当亦视为本发明可实施的范畴。
实施例1：一种环保型纸质餐具加工覆膜材料，按重量组分配比包括有以下组分：
荸荠皮31份、纤维素酶1.5份、柠檬酸5.8份、柠檬酸钠9份、羧甲基纤维素钠3份、海藻酸钠11份、甘油9份、玉米淀粉21份。
实施例2：一种环保型纸质餐具加工覆膜材料，按重量组分配比包括有以下组分：
荸荠皮40份、纤维素酶2.5份、柠檬酸7份、柠檬酸钠9份、羧甲基纤维素钠5份、海藻酸钠15份、甘油11份、玉米淀粉25份。
实施例3：一种环保型纸质餐具加工覆膜材料，按重量组分配比包括有以下组分：
荸荠皮48份、纤维素酶4份、柠檬酸9份、柠檬酸钠15份、羧甲基纤维素钠9份、海藻酸钠18份、甘油15份、玉米淀粉28份。
实施例4：一种环保型纸质餐具加工覆膜材料的制备方法，包括有以下步骤：
S1，准备原材料：荸荠皮、纤维素酶、柠檬酸、柠檬酸钠、羧甲基纤维素钠、海藻酸钠、甘油、玉米淀粉；
S2，制备干荸荠粉；
S3，制备多糖的提取液；
S4，制备覆膜液，并进行密封。
所述S2中，将取得的荸荠皮在50℃条件下进行烘干，3h后取出，用高速粉碎机粉碎，制得干荸荠粉。
所述S3中，干荸荠粉加入纤维素酶，pH为5，溶剂水和干荸荠粉的料液比为15∶1，在40℃条件下水浴酶解1h，然后水浴，温度80℃时间50min，在3000r/min的条件下离心10min，取上层清液，为提取液。
所述S4中，提取液、柠檬酸、柠檬酸钠、羧甲基纤维素钠、海藻酸钠、玉米淀粉、甘油混合，于50℃水浴锅中搅拌至完全溶解，冷却后再加入甘油，在-0.9MPa下用真空脱气装罐密封。
实施例5：一种环保型纸质餐具加工覆膜材料的制备方法，包括有以下步骤：
S1，准备原材料：荸荠皮、纤维素酶、柠檬酸、柠檬酸钠、羧甲基纤维素钠、海藻酸钠、甘油、玉米淀粉；
S2，制备干荸荠粉；
S3，制备多糖的提取液；
S4，制备覆膜液，并进行密封。
所述S2中，将取得的荸荠皮在55℃条件下进行烘干，4h后取出，用高速粉碎机粉碎，制得干荸荠粉。
所述S3中，干荸荠粉加入纤维素酶，pH为5，溶剂水和干荸荠粉的料液比为15∶1，在55℃条件下水浴酶解1.5h，然后水浴，温度85℃时间55min，在3500r/min的条件下离心15min，取上层清液，为提取液。
所述S4中，提取液、柠檬酸、柠檬酸钠、羧甲基纤维素钠、海藻酸钠、玉米淀粉、甘油混合，于56℃水浴锅中搅拌至完全溶解，冷却后再加入甘油，在-0.92MPa下用真空脱气装罐密封。
实施例6：一种环保型纸质餐具加工覆膜材料的制备方法，包括有以下步骤：
S1，准备原材料：荸荠皮、纤维素酶、柠檬酸、柠檬酸钠、羧甲基纤维素钠、海藻酸钠、甘油、玉米淀粉；
S2，制备干荸荠粉；
S3，制备多糖的提取液；
S4，制备覆膜液，并进行密封。
所述S2中，将取得的荸荠皮在66℃条件下进行烘干，5h后取出，用高速粉碎机粉碎，制得干荸荠粉。
所述S3中，干荸荠粉加入纤维素酶，pH为5，溶剂水和干荸荠粉的料液比为15∶1，在60℃条件下水浴酶解2.5h，然后水浴，温度95℃时间60min，在4000r/min的条件下离心18min，取上层清液，为提取液。
所述S4中，提取液、柠檬酸、柠檬酸钠、羧甲基纤维素钠、海藻酸钠、玉米淀粉、甘油混合，于65℃水浴锅中搅拌至完全溶解，冷却后再加入甘油，在-0.95MPa下用真空脱气装罐密封。
上述实施例仅例示性说明本发明的原理及其功效，而非用于限制本发明。任何熟悉此技术的人士皆可在不违背本发明的精神及范畴下，对上述实施例进行修饰或改变。因此，举凡所属技术领域中具有通常知识者在未脱离本发明所揭示的精神与技术思想下所完成的一切等效修饰或改变，仍应由本发明的权利要求所涵盖。
Claims (8)
1.一种环保型纸质餐具加工覆膜材料，其特征在于，按重量组分配比包括有以下组分：
荸荠皮30-50份、纤维素酶1-5份、柠檬酸5-10份、柠檬酸钠8-16份、羧甲基纤维素钠2-10份、海藻酸钠10-20份、甘油8-16份、玉米淀粉20-30份。
2.根据权利要求1所述的一种环保型纸质餐具加工覆膜材料，其特征在于，按重量组分配比包括有以下组分：
荸荠皮31份、纤维素酶1.5份、柠檬酸5.8份、柠檬酸钠9份、羧甲基纤维素钠3份、海藻酸钠11份、甘油9份、玉米淀粉21份。
3.根据权利要求1所述的一种环保型纸质餐具加工覆膜材料，其特征在于，按重量组分配比包括有以下组分：
荸荠皮40份、纤维素酶2.5份、柠檬酸7份、柠檬酸钠9份、羧甲基纤维素钠5份、海藻酸钠15份、甘油11份、玉米淀粉25份。
4.根据权利要求1所述的一种环保型纸质餐具加工覆膜材料，其特征在于，按重量组分配比包括有以下组分：
荸荠皮48份、纤维素酶4份、柠檬酸9份、柠檬酸钠15份、羧甲基纤维素钠9份、海藻酸钠18份、甘油15份、玉米淀粉28份。
5.一种环保型纸质餐具加工覆膜材料的制备方法，其特征在于，包括有以下步骤：
S1，准备原材料：荸荠皮、纤维素酶、柠檬酸、柠檬酸钠、羧甲基纤维素钠、海藻酸钠、甘油、玉米淀粉；
S2，制备干荸荠粉；
S3，制备多糖的提取液；
S4，制备覆膜液，并进行密封。
6.根据权利要求5所述的一种环保型纸质餐具加工覆膜材料的制备方法，其特征在于：所述S2中，将取得的荸荠皮在50-66℃条件下进行烘干，3-5h后取出，用高速粉碎机粉碎，制得干荸荠粉。
7.根据权利要求5所述的一种环保型纸质餐具加工覆膜材料的制备方法，其特征在于：所述S3中，干荸荠粉加入纤维素酶，pH为5，溶剂水和干荸荠粉的料液比为15∶1，在40-60℃条件下水浴酶解1-2.5h，然后水浴，温度80-95℃时间50-60min，在3000-4000r/min的条件下离心10-18min，取上层清液，为提取液。
8.根据权利要求5所述的一种环保型纸质餐具加工覆膜材料的制备方法，其特征在于：所述S4中，提取液、柠檬酸、柠檬酸钠、羧甲基纤维素钠、海藻酸钠、玉米淀粉、甘油混合，于50-65℃水浴锅中搅拌至完全溶解，冷却后再加入甘油，在-0.9～-0.95MPa下用真空脱气装罐密封。