CN113929166A - 一种可凝固废液的抑菌除臭剂及其制备方法和应用 - Google Patents
一种可凝固废液的抑菌除臭剂及其制备方法和应用 Download PDFInfo
- Publication number
- CN113929166A CN113929166A CN202111050824.6A CN202111050824A CN113929166A CN 113929166 A CN113929166 A CN 113929166A CN 202111050824 A CN202111050824 A CN 202111050824A CN 113929166 A CN113929166 A CN 113929166A
- Authority
- CN
- China
- Prior art keywords
- water
- bacteriostatic
- deodorant
- absorbent resin
- waste liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于垃圾处理技术领域,公开了一种可凝固废液的抑菌除臭剂及其制备方法和应用。该抑菌除臭剂,包括以下组分:吸水树脂、纳米银、铝盐和三氯乙酸甲基苯甲酯。该抑菌除臭剂,通过吸水树脂、纳米银、铝盐和三氯乙酸甲基苯甲酯的配合使用,使其具有良好的凝固废水的能力,通过吸附和包覆垃圾中的废液,方便含水分垃圾的处理;同时不仅能够起到抑菌,减少细菌滋生的作用,还能够清除异味,净化空气。该制备方法简单,原料易得。
Description
技术领域
本发明属于垃圾处理技术领域,具体涉及一种可凝固废液的抑菌除臭剂及其制备方法和应用。
背景技术
茶水、咖啡、饮料、蔬菜、果皮等厨余垃圾,以及宠物粪便等含有大量水分,将其扔入垃圾桶内,在垃圾桶内会积累一些废液。废液的异味重,影响空气质量;长时间不清理还会滋生病菌,如很多家庭喜欢将垃圾存放在垃圾桶,通常都是第二天甚至第三天积攒满袋后,再进行处理,这种生活习惯更加重了细菌的滋生和异味的产生。当有骨刺残渣等尖锐物刺破塑料垃圾袋时,废液还会泄漏到垃圾桶内或地面上,给垃圾的清理带来了极大的不便,甚至会带来二次污染。因此,对于含有水分或废液的垃圾的处理极其麻烦,给人们的生活带来了很大的困扰。
目前,针对含水分的易腐垃圾,市面上出现了很多除臭剂、芳香剂等,但是这些产品只能在一定时间内释放一些芳香物质,或是吸附一些臭味物质,减少臭味带来的不适感,并不能起到抑菌作用,或者对垃圾的处理带来便捷性。
因此,亟需提供一种抑菌除臭剂,能够减少细菌滋生,清除异味,方便含水分垃圾的处理。
发明内容
本发明旨在至少解决上述现有技术中存在的技术问题之一。为此,本发明提出一种可凝固废液的抑菌除臭剂,不仅能够减少细菌滋生,清除异味,还能够形成水凝胶,吸附和包覆垃圾中的废液,方便含水分垃圾的处理。
本发明第一方面提供了一种可凝固废液的抑菌除臭剂。
具体的,一种可凝固废液的抑菌除臭剂,包括以下组分:吸水树脂、纳米银、铝盐和三氯乙酸甲基苯甲酯。
在所述抑菌除臭剂中,吸水树脂、铝盐和三氯乙酸甲基苯甲酯三者配合使用,在遇水或水油混合物时,吸水树脂能大量吸收水分并膨胀形成凝胶,铝盐有利于凝胶的形成,增强吸水、包覆油分子的能力;而三氯乙酸甲基苯甲酯能够增强凝胶的稳定性,使已吸收的水分或已包覆的油分子不外流,达到锁水、固油的功效。同时,在形成凝胶的过程中,吸水树脂、铝盐和三氯乙酸甲基苯甲酯三者相互作用能够使纳米银得到良好的包覆,为纳米银创造良好的灭菌环境,纳米银在凝胶中部分溶解释放出银离子,纳米银和银离子共同作用于废液中的微生物,能够提高杀灭能力。此外,吸水树脂、铝盐和三氯乙酸甲基苯甲酯三者相互作用能够减缓香精中香味成分的挥发速度,使其缓慢均匀挥发,增加香气的持久性。
优选的,所述吸水树脂包括第一吸水树脂和第二吸水树脂,所述第一吸水树脂的粒径范围为10-50目,所述第二吸水树脂的粒径范围为60-120目。进一步优选的,所述第一吸水树脂的粒径范围为20-50目,所述第二吸水树脂的粒径范围为80-120目。更优选的,所述第一吸水树脂的粒径为40目,所述第二吸水树脂的粒径为100目。通过控制吸水树脂的粒径,两种不同粒径树脂的搭配使用,有利于凝胶的形成,使纳米银得到更好的包覆。同时,较小的粒径具有更强的吸水能力,其吸水速度更快,但是只采用粒径范围为60-120目的吸水树脂,会在喷洒过程中引起扬尘的风险。通过加入粒径范围为10-50目的吸水树脂复配使用,增加重力,在单独使用除臭剂进行喷洒时,能够有效缓解此情况。此外,在将所述可凝固废液的抑菌除臭剂加入垃圾桶中特定装置时,与垃圾桶配合使用,也能避免抑菌除臭剂出现飞尘。优选的,所述吸水树脂的主要成分为聚丙烯酸钠。
优选的,所述第一吸水树脂和所述第二吸水树脂的质量比为1:(1-5);进一步优选的,所述第一吸水树脂和所述第二吸水树脂的质量比为1:(2-4)。
优选的,所述铝盐选自氯化铝(AlCl3)、硫酸铝(Al2(SO4)3)、硝酸铝(Al(NO3)3)或硅酸铝(Al3(SiO3)3)中的至少一种。
优选的,按重量份计,所述抑菌除臭剂,包括以下组分:
进一步优选的,按重量份计,所述抑菌除臭剂,包括以下组分:
更优选的,按重量份计,所述抑菌除臭剂,包括以下组分:
优选的,所述抑菌除臭剂还包括二乙二醇单甲醚。所用二乙二醇单甲醚与三氯乙酸甲基苯甲酯,能够增强二乙二醇单甲醚的作用,进一步提高所形成的凝胶的稳定性。
优选的,所述二乙二醇单甲醚与所述三氯乙酸甲基苯甲酯的质量比为1:(0.5-2);进一步优选的,所述二乙二醇单甲醚与所述三氯乙酸甲基苯甲酯的质量比为1:(1-2)。
优选的,所述抑菌除臭剂还包括香精。所述香精包括但不限于秘鲁香脂、吐鲁香脂、安息香、檀香、岩兰草、广藿香、龙涎香、海狸香、麝香或灵猫香或柠檬香精。
优选的,按重量份计,所述香精为0.001-3份。
本发明第二方面提供了一种可凝固废液的抑菌除臭剂的制备方法。
具体的,一种可凝固废液的抑菌除臭剂的制备方法,包括以下步骤:
称取各组分,混合,即制得所述抑菌除臭剂。
优选的,当含有香精和二乙二醇单甲醚时,所述抑菌除臭剂的制备方法,包括以下步骤:
向所述三氯乙酸甲基苯甲酯和二乙二醇单甲醚中加入香精,混合,然后再加入其他组分,混合,即制得所述抑菌除臭剂。
本发明第三方面提供了一种可凝固废液的抑菌除臭剂的应用。
具体的,所述可凝固废液的抑菌除臭剂在处理废液或垃圾中的应用。
一种垃圾桶,包含所述可凝固废液的抑菌除臭剂。具体的,如在垃圾桶的腔体内、底部或侧面加入所述抑菌除臭剂,协助处理垃圾。
相对于现有技术,本发明的有益效果如下:
(1)本发明提供的抑菌除臭剂,通过吸水树脂、纳米银、铝盐和三氯乙酸甲基苯甲酯的配合使用,使其具有良好的凝固废水的能力,通过吸附和包覆垃圾中的废液,方便含水分垃圾的处理;同时不仅能够起到抑菌,减少细菌滋生的作用,还能够清除异味,净化空气。
(2)本发明提供的抑菌除臭剂,其制备方法简单,原料易得,使用方便。
附图说明
图1为在厨余垃圾中加入实施例1制备的抑菌除臭剂后的状态图;
图2为在宠物尿液中加入实施例1制备的抑菌除臭剂后的状态图。
具体实施方式
为了让本领域技术人员更加清楚明白本发明所述技术方案,现列举以下实施例进行说明。需要指出的是,以下实施例对本发明要求的保护范围不构成限制作用。
以下实施例中所用的原料、试剂或装置如无特殊说明,均可从常规商业途径得到,或者可以通过现有已知方法得到。
实施例1
一种可凝固废液的抑菌除臭剂,由以下组分组成:
其中吸水树脂包括40目的30份,100目的90份。
一种可凝固废液的抑菌除臭剂的制备方法,包括以下步骤:
将三氯乙酸甲基苯甲酯和二乙二醇单甲醚混合,然后加入香精,混合均匀后,再加入其他组分,混合,即制得抑菌除臭剂。
实施例2
一种可凝固废液的抑菌除臭剂,由以下组分组成:
其中吸水树脂包括40目的50份,100目的100份。
一种可凝固废液的抑菌除臭剂的制备方法,包括以下步骤:
将三氯乙酸甲基苯甲酯和二乙二醇单甲醚混合,然后加入香精,混合均匀后,再加入其他组分,混合,即制得抑菌除臭剂。
实施例3
一种可凝固废液的抑菌除臭剂,由以下组分组成:
其中吸水树脂包括40目的90份,100目的30份。
一种可凝固废液的抑菌除臭剂的制备方法,包括以下步骤:
将三氯乙酸甲基苯甲酯和二乙二醇单甲醚混合,然后加入香精,混合均匀后,再加入其他组分,混合,即制得抑菌除臭剂。
实施例4
一种可凝固废液的抑菌除臭剂,由以下组分组成:
一种可凝固废液的抑菌除臭剂的制备方法,包括以下步骤:
将三氯乙酸甲基苯甲酯和二乙二醇单甲醚混合,然后加入香精,混合均匀后,再加入其他组分,混合,即制得抑菌除臭剂。
实施例5
一种可凝固废液的抑菌除臭剂,由以下组分组成:
其中吸水树脂包括40目的30份,100目的90份。
一种可凝固废液的抑菌除臭剂的制备方法,包括以下步骤:
将三氯乙酸甲基苯甲酯混合,然后加入香精,混合均匀后,再加入其他组分,混合,即制得抑菌除臭剂。
实施例6
一种防洒漏去异味的垃圾桶,包括:桶身、桶盖和加料机构,桶身内部设置有垃圾腔;桶盖安装于桶身上;加料机构安装于桶身侧面,从加料机构加入本发明实施例1提供的可凝固废液的抑菌除臭剂。
对比例1
对比例1与实施例1的区别在于,将纳米银替换为等量次氯酸钠,其余组分和制备方法同实施例1。
对比例2
对比例3与实施例1的区别在于,将8份硫酸铝替换为等量吸水树脂,其余组分和制备方法同实施例1。
对比例3
对比例3与实施例1的区别在于,将8份三氯乙酸甲基苯甲酯替换为等量吸水树脂,其余组分和制备方法同实施例1。
产品效果测试
1.抑菌效果测试
(1)以酵母菌为受试菌,考察实施例1-5以及对比例1-3所制得的抑菌除臭剂的抑菌效果。测试方法如下:吸取100mL悬菌液(106CFU/mL),分别加入1mg实施例1-5以及对比例1-5所制得的抑菌除臭剂,待抑菌除臭剂吸水完毕后,静置2小时,然后将受测样品稀释数倍,无菌条件下充分混匀,得处理液。再取处理液20μL涂平板,于28℃下培养48小时,测定菌落数。计算抑菌率,抑菌率=1-(换算后原始菌落总数/处理2小时后菌落总数)。
测试结果如表1所示:
表1
由表1可知,实施例1-5制得的抑菌除臭剂对酵母菌的抑菌率达到99.5%-99.92%。其效果明显优于对比例1-3制得的抑菌除臭剂。
(2)以枯草芽孢杆菌为受试菌,考察实施例1-5以及对比例1-3所制得的抑菌除臭剂的抑菌效果。测试方法如下:吸取100mL悬菌液(106CFU/mL),分别加入1mg实施例1-5以及对比例1-5所制得的抑菌除臭剂,待抑菌除臭剂吸水完毕后,静置2小时,然后将受测样品稀释数倍,无菌条件下充分混匀,得处理液。再取处理液20μL涂平板,于32℃下培养48小时,测定菌落数。
测试结果如表2所示:
表2
换算后原始菌落总数 | 处理2小时后菌落总数 | 抑菌率% | |
实施例1 | 5×10<sup>5</sup>CFU/mL | 2.5×10<sup>2</sup>CFU/mL | 99.95 |
实施例2 | 5×10<sup>5</sup>CFU/mL | 5×10<sup>2</sup>CFU/mL | 99.90 |
实施例3 | 5×10<sup>5</sup>CFU/mL | 1×10<sup>3</sup>CFU/mL | 99.80 |
实施例4 | 5×10<sup>5</sup>CFU/mL | 2×10<sup>3</sup>CFU/mL | 99.60 |
实施例5 | 5×10<sup>5</sup>CFU/mL | 2.25×10<sup>3</sup>CFU/mL | 99.55 |
对比例1 | 5×10<sup>3</sup>CFU/mL | 2.5×10<sup>2</sup>CFU/mL | 95.0 |
对比例2 | 5×10<sup>4</sup>CFU/mL | 5×10<sup>2</sup>CFU/mL | 99.0 |
对比例3 | 5×10<sup>4</sup>CFU/mL | 1.25×10<sup>3</sup>CFU/mL | 97.5 |
由表2可知,实施例1-5制得的抑菌除臭剂对枯草芽孢杆菌的抑菌率达到99.55%-99.95%。其效果明显优于对比例1-3制得的抑菌除臭剂。
2.吸水、吸油,除臭效果测试
(1)取100mL咖啡,向其中加入1mg实施例1-5以及对比例1-3所制得的抑菌除臭剂。
(2)取100mL植物油混合物(水油体积比为1:1),向其中加入1mg实施例1-5以及对比例1-3所制得的抑菌除臭剂。
(3)取100mL厨余垃圾(由剩余饭菜、汤汁组成),向其中加入1mg实施例1-5以及对比例1-3所制得的抑菌除臭剂。图1为在厨余垃圾中加入实施例1制备的抑菌除臭剂后的状态图,由图1可知,加入抑菌除臭剂后,厨余垃圾中的水与油均被吸附,形成凝胶状,无废液渗出。
(4)取100mL宠物尿液(狗),向其中加入1mg实施例1-5以及对比例1-3所制得的抑菌除臭剂。图2为在宠物尿液中加入实施例1制备的抑菌除臭剂后的状态图,由图2可知,加入抑菌除臭剂后,宠物尿液被吸附形成凝胶状,无废液渗出。
在试验中,记录完全形成凝胶或固体状,无液体渗出的时间,记录在处理后一定时间内气味变化情况。测试结果见表3、表4。
表3 厨余垃圾处理后放置0天、3天、7天的味道变化
由表3可知,本发明实施例提供的抑菌除臭剂对厨余垃圾进行处理后,能够改善臭味,其效果明显优于对比例。
表4 宠物尿液处理后放置0天、3天、7天的味道变化
由表4可知,本发明实施例提供的抑菌除臭剂对宠物尿液进行处理后,能够改善臭味,其效果明显优于对比例。
Claims (10)
1.一种可凝固废液的抑菌除臭剂,其特征在于,包括以下组分:吸水树脂、纳米银、铝盐和三氯乙酸甲基苯甲酯。
2.根据权利要求1所述的抑菌除臭剂,其特征在于,所述吸水树脂包括第一吸水树脂和第二吸水树脂,所述第一吸水树脂的粒径范围为10-50目,所述第二吸水树脂的粒径范围为60-120目。
3.根据权利要求1所述的抑菌除臭剂,其特征在于,所述第一吸水树脂和所述第二吸水树脂的质量比为1:(1-5)。
4.根据权利要求1所述的抑菌除臭剂,其特征在于,所述铝盐选自氯化铝、硫酸铝、硝酸铝或硅酸铝中的至少一种。
6.根据权利要求1所述的抑菌除臭剂,其特征在于,所述抑菌除臭剂还包括香精和二乙二醇单甲醚。
7.根据权利要求6所述的抑菌除臭剂,其特征在于,所述二乙二醇单甲醚与所述三氯乙酸甲基苯甲酯的质量比为1:(0.5-2)。
8.权利要求1-7中任一项所述的抑菌除臭剂的制备方法,其特征在于,包括以下步骤:
称取各组分,混合,即制得所述抑菌除臭剂。
9.权利要求1-7中任一项所述的抑菌除臭剂在处理废液或垃圾中的应用。
10.一种垃圾桶,其特征在于,包含权利要求1-7中任一项所述的抑菌除臭剂。