CN113861892B - 一种保温板密封用不干胶 - Google Patents
一种保温板密封用不干胶 Download PDFInfo
- Publication number
- CN113861892B CN113861892B CN202111218692.3A CN202111218692A CN113861892B CN 113861892 B CN113861892 B CN 113861892B CN 202111218692 A CN202111218692 A CN 202111218692A CN 113861892 B CN113861892 B CN 113861892B
- Authority
- CN
- China
- Prior art keywords
- parts
- weight
- adhesive
- self
- sealing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供了一种保温板密封用不干胶，其中，所述不干胶包括以下重量份的组分：聚异丁烯10‑50份；聚二甲基硅氧烷10‑50份；相容剂1‑10份；填充物20‑80份；助剂0.1‑2.5份。本发明的密封胶在使用时操作便捷，相对硅酮密封胶而言具有更长的可操作时间和填缝密封性，与聚氨酯密封胶相比，具有优异的耐候性和长使用寿命；与机械固定相比，更密实而且拆解和维修方便，省时省力，经济效益突出，完全满足功能需求。
Description
技术领域
本发明涉及一种不干胶，尤其涉及一种保温板密封用不干胶。
背景技术
随着冷链存储、环保建筑的发展，越来越多的墙体和屋面选择使用复合型板材。然而板材在拼接时大多使用机械固定加湿气固化型密封胶粘结，这难免会存在一些由于外力(沉降、热胀冷缩形变等)形成的缝隙，从而降低保温性能，并造成能源浪费。然而，目前市场上暂无不固化密封胶(不干胶型)，全部是机械固定加硅酮、聚氨酯等湿气固化型密封胶，如专利CN210947191U(采用卡口加硅胶密封)，CN110284609B记载了使用一种聚氨酯密封条结合尼龙螺栓固定的结构。并且传统密封胶固化后如果出现板材运动，加上内部低温，外部高温，可能会导致粘结界面破坏，出现缝隙，造成密封失效，且后期维修拆卸时费时费力；有些密封胶存在低温发脆、高温流淌等问题，对于冷库、建筑应用范围窄，且耐候、使用期限较差。且常规的密封胶触变性不好，打胶时容易拉丝造成基材污染，增加施工处理时间，降低效率及长期使用容易干燥开裂。
因此，迫切需要开发一种新颖的保温板密封用不干胶。
发明内容
本发明针对传统拼接固定方式不足的基础上，提供了一种用于冷库板拼接时缝隙填充的不干胶。
为了达到上述目的，本设计采用的技术方案如下。
本发明提供了一种保温板密封用不干胶，其中，所述不干胶包括以下重量份的组分：
聚异丁烯 10-50份；
聚二甲基硅氧烷 10-50份；
相容剂 1-10份；
填充物 20-80份；
助剂 0.1-2.5份。
优选地，其中，所述聚异丁烯的分子量为300-95000。
优选地，其中，所述聚二甲基硅氧烷的粘度为100cp-500000cp。
优选地，其中，所述相容剂为马来酸酐改性聚异丁烯，其数均分子量(Mn)为1000-2000Dalton。
优选地，其中，所述填充物为云母粉、碳酸钙、滑石粉、高岭土、硅微粉、膨润土、白炭黑或钛白粉中一者或多者。
更优选地，其中，所述碳酸钙为纳米活性碳酸钙
优选地，其中，所述助剂为紫外吸收剂、抗氧剂、光稳定剂中一者或多者。
本发明的保温板密封用不干胶较常规密封胶具有下列优势：
1.在较宽使用温度范围内(使用温度-60℃-80℃，满足从冷库至建筑保温板的宽温范围)可实现永不固化，对缝隙具有一定的追随行；
2.耐低温可至-60℃，常规密封胶只有-40℃，密封胶在低温下变脆，粘结力下降，受力容易破坏；
3.环保，低VOC，不含溶剂，不变质分层；
4.方便拆卸，由于不固化，无需过多人力或破坏基材即可拆开板材；
5.通过不固化特性解决由于位移等造成的固化型密封胶粘结失效风险，同时方便保温板的拆卸，重新组装；
6.使用耐候性材料满足较长使用寿命的需要，可与建筑同等寿命甚至更久。
本发明的密封胶在使用时操作便捷，相对硅酮密封胶而言具有更长的可操作时间和填缝密封性，与聚氨酯密封胶相比，具有优异的耐候性和长使用寿命；与机械固定相比，更密实而且拆解和维修方便，省时省力，经济效益突出，完全满足功能需求。
具体实施方式
本发明的保温板密封用不干胶使用聚异丁烯(分子量300-95000，Mv)、聚二甲基硅氧烷(100cp-500000cp)为高分子材料骨架，具有优异的耐候性、粘结性、气密性以及伸长率。本发明的保温板密封用不干胶使用相容剂马来酸酐改性聚异丁烯，聚二甲基硅氧烷和聚异丁烯并不完全相容，这种不相容性赋予最终组分具有不拉丝的特性。如果不相容程度很高，则可能出现宏观分相，即渗油；为了控制不相容程度，需要增加一种相容剂马来酸酐改性聚异丁烯。
本发明的保温板密封用不干胶使用的填充物包含云母粉、碳酸钙、滑石粉、高岭土、硅微粉、膨润土、白炭黑、钛白粉中的2种或3种，起到降低成本、方便施工、隔热保温以及耐候等作用。
本发明的保温板密封用不干胶使用的助剂包含紫外吸收剂、抗氧剂、光稳定剂中的1种或多种。
实施例
下列实施例中使用的商品1和商品2分别为购于上海新珂复合材料的Butyl 300和Butyl 200不干胶。
下列实施例中使用的马来酸酐改性聚异丁烯购自锦州圣大化学品有限公司，数均分子量为1000Dalton。
实施例1
一种保温板密封用不干胶，包括聚异丁烯(1300，Mv)20重量份；聚二甲基硅氧烷(100cp)15重量份；聚二甲基硅氧烷(500000cp)5重量份；马来酸酐改性聚异丁烯5重量份；光稳定剂(Tinuvin 770)0.5重量份；紫外吸收剂(TINUVIN B75)0.5重量份；抗氧剂(IRGANOX1010)0.5重量份；纳米活性碳酸钙25重量份；钛白粉(金红型)10重量份；气相二氧化硅3.5重量份；云母粉15重量份。
使用具有抽真空功能的高速分散机(1000L或1300L)进行胶料加工，首先投入聚异丁烯(1300，Mv)、1/2(一半)聚二甲基硅氧烷(500000cp)、马来酸酐改性聚异丁烯(Mn1000dalton)、抗氧剂(IRGANOX1010)、紫外吸收剂(TINUVIN B75)、光稳定剂(Tinuvin770)进行欲分散，常温搅拌10-20分钟；分批投入粉体(包括纳米活性碳酸钙、钛白粉(金红型)、气相二氧化硅及云母粉)、1/2(一半)聚二甲基硅氧烷(500000cp)以及聚二甲基硅氧烷(100cp)，升温至90-110℃搅拌30-45分钟；抽真空(-0.08MPa)保持至少15分钟，出胶后包装成300ml硬管或者600ml软包。
实施例2
一种保温板密封用不干胶，包括聚异丁烯(1300，Mv)20重量份；聚异丁烯(50000，Mv)5重量份；聚二甲基硅氧烷(500000cp)15重量份；马来酸酐改性聚异丁烯5重量份；光稳定剂(Tinuvin 770)0.5重量份；紫外吸收剂(TINUVIN B75)0.5重量份；抗氧剂(IRGANOX1010)0.5重量份；硅微粉25重量份；钛白粉(金红型)10重量份；气相二氧化硅3.5重量份；云母粉15重量份。
使用具有抽真空功能的高速分散机(1000L或1300L)进行胶料加工，首先投入聚异丁烯(1300，Mv)、1/2(一半)聚二甲基硅氧烷(500000cp)、马来酸酐改性聚异丁烯(Mn1000dalton)、抗氧剂(IRGANOX1010)、紫外吸收剂(TINUVIN B75)、光稳定剂(Tinuvin 770)进行欲分散，常温搅拌10-20分钟；分批投入粉体(包括硅微粉、钛白粉(金红型)、气相二氧化硅及云母粉)以及1/2(一半)聚二甲基硅氧烷(500000cp)以及聚二甲基硅氧烷(100cp)，升温至90-110℃搅拌30-45分钟；抽真空(-0.08MPa)保持至少15分钟，出胶后包装成300ml硬管或者600ml软包。
实施例3
一种保温板密封用不干胶，包括聚异丁烯(1300，Mv)20重量份；聚异丁烯(50000，Mv)5重量份；聚二甲基硅氧烷(100cp)10重量份；聚二甲基硅氧烷(500000cp)5重量份；马来酸酐改性聚异丁烯5重量份；光稳定剂(Tinuvin 770)0.5重量份；紫外吸收剂(TINUVINB75)0.5重量份；抗氧剂(IRGANOX1010)0.5重量份；纳米活性碳酸钙25重量份；钛白粉(金红型)10重量份；气相二氧化硅3.5重量份；高岭土15重量份。
使用具有抽真空功能的高速分散机(1000L或1300L)进行胶料加工，首先投入聚异丁烯(1300，Mv)、聚异丁烯(50000，Mv)、1/2(一半)聚二甲基硅氧烷(500000cp)、马来酸酐改性聚异丁烯(Mn 1000dalton)、抗氧剂(IRGANOX1010)、紫外吸收剂(TINUVIN B75)、光稳定剂(Tinuvin 770)进行欲分散，常温搅拌10-20分钟；分批投入粉体(包括纳米活性碳酸钙、钛白粉(金红型)、气相二氧化硅及高岭土)以及1/2(一半)聚二甲基硅氧烷(500000cp)以及聚二甲基硅氧烷(100cp)，升温至90-110℃搅拌30-45分钟；抽真空(-0.08MPa)保持至少15分钟，出胶后包装成300ml硬管或者600ml软包。
表1为本发明的保温板密封用不干胶的配方成分。
表1
表2为本发明的保温板密封用不干胶与市售商品的物性指标对比结果。
表2
Claims (1)
1.一种保温板密封用不干胶，其中，所述不干胶包括以下重量份的组分：粘均分子量1300的聚异丁烯20份；
粘均分子量50000的聚异丁烯5份；
粘度500000cp的聚二甲基硅氧烷15份；
马来酸酐改性聚异丁烯5份；
Tinuvin770光稳定剂0.5份；
TINUVINB75紫外吸收剂0.5份；
IRGANOX1010抗氧剂0.5份；
硅微粉25份；
金红型钛白粉10份；
气相二氧化硅3.5份；
云母粉15份。