CN113858737A - 一种多层复合笔记本电脑外壳材料 - Google Patents
一种多层复合笔记本电脑外壳材料 Download PDFInfo
- Publication number
- CN113858737A CN113858737A CN202111188198.7A CN202111188198A CN113858737A CN 113858737 A CN113858737 A CN 113858737A CN 202111188198 A CN202111188198 A CN 202111188198A CN 113858737 A CN113858737 A CN 113858737A
- Authority
- CN
- China
- Prior art keywords
- layer
- parts
- notebook computer
- multilayer composite
- graphene fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种多层复合笔记本电脑外壳材料,自上而下依次包括第一保护膜层、第一胶黏剂层、第一石墨烯纤维布层、第一过渡层、中间芯层、第二过渡层、第二石墨烯纤维布层、第二胶黏剂层、第二保护膜层;所述中间芯层由镁合金制成;所述第一过渡层和第二过渡层相互独立地分别由如下按重量份计的各原料制成:松香基超支化环氧树脂20‑30份、超支化聚硫醚多胺25‑35份、N‑(4‑氰基‑3‑三氟甲基苯基)甲基丙烯酰胺/乙烯基三甲氧基硅烷/1,3‑双(环氧乙烷基甲基)‑5‑(2‑丙烯基)‑1,3,5‑三嗪‑2,4,6(1H,3H,5H)‑三酮共聚物20‑30份、纳米铝粉3‑5份、石墨烯纤维3‑5份。本发明公开的多层复合笔记本电脑外壳材料各层之间粘结牢,机械强度和耐用性足,耐腐蚀性、耐磨损性、耐低温性和耐热性佳。
Description
技术领域
本发明涉及笔记本电脑外壳制备技术领域,尤其涉及一种多层复合笔记本电脑外壳材料。
背景技术
随着社会的发展,办公设备更加智能化,被人们广泛使用的笔记本电脑也逐步向中高端发展,其外壳追求更轻、更薄、更高强度和特殊外观效果。现有的笔记本电脑外壳用料有铝合金、钛合金、碳纤维、聚碳酸酯PC和ABS工程塑料。镁铝合金耐磨性较差,并且成本较高,成型困难。钛合金和碳纤维昂贵,碳纤维如果接地不好,会有轻微的漏电感。聚碳酸酯PC比较脆,一跌就破。ABS工程塑料质量较重,导热性能欠佳。
为了制成综合性能和性能稳定性更加优异的笔记本电脑外壳,业内研究者们作了许多工作。其中多层复合笔记本电脑外壳材料的研究最为热门,这类材料结合了多种材料的优点,散热和绝缘效果好,使用寿命长。然而,现有的多层复合笔记本电脑外壳材料还或多或少存在各层之间粘结不牢,机械强度和耐用性不足,耐腐蚀性、耐磨损性、耐低温性和耐热性不足的缺陷。
为了解决上述问题,发明专利CN107665015B公开了一种笔记本电脑外壳,该笔记本电脑外壳从外到内依次由第一碳纤维复合材料层、第一金镀层、铝合金层、第二金镀层以及第二碳纤维复合材料层组成。该笔记本电脑外壳的制备方法包括提供铝合金层、磁控溅射法,在铝合金层的表面镀覆第一金镀层和第二金镀层;制作第一碳纤维复合材料层与第二碳纤维复合材料层;热压成型。该发明笔记本电脑外壳的散热效果和力学性能优异,质量轻;然而,该材料绝缘性能有待进一步改善,制备成本和耗能高,制备效率低,各层之间结合力不强。
可见,开发一种各层之间粘结牢,机械强度和耐用性足,耐腐蚀性、耐磨损性、耐低温性和耐热性佳的多层复合笔记本电脑外壳材料符合市场需求,具有广泛的市场价值,对促进笔记本电脑制造领域的发展具有非常重要的意义。
发明内容
本发明目的是为了克服现有技术的不足而提供一种各层之间粘结牢,机械强度和耐用性足,耐腐蚀性、耐磨损性、耐低温性和耐热性佳的多层复合笔记本电脑外壳材料。
为达到上述目的,本发明采用的技术方案是:一种多层复合笔记本电脑外壳材料,其特征在于,自上而下依次包括第一保护膜层、第一石墨烯纤维布层、第一过渡层、中间芯层、第二过渡层、第二石墨烯纤维布层、第二保护膜层;所述第一保护膜层与第一石墨烯纤维布层之间设有第一胶黏剂层;所述第二保护膜层与第二石墨烯纤维布层之间设有第二胶黏剂层;所述中间芯层由镁合金制成;所述第一过渡层和第二过渡层相互独立地分别由如下按重量份计的各原料制成:松香基超支化环氧树脂20-30份、超支化聚硫醚多胺25-35份、N-(4-氰基-3-三氟甲基苯基)甲基丙烯酰胺/乙烯基三甲氧基硅烷/1,3-双(环氧乙烷基甲基)-5-(2-丙烯基)-1,3,5-三嗪-2,4,6(1H,3H,5H)-三酮共聚物20-30份、纳米铝粉3-5份、石墨烯纤维3-5份。
优选的,所述镁合金为AZ31B镁合金、AZ40M镁合金、AZ61M镁合金、AZ91D镁合金中的任意一种。
优选的,所述第一保护膜层、第二保护膜层相互独立地由聚四氟乙烯、聚对苯二甲酸乙二醇酯、PBT树脂中的任意一种制成。
优选的,所述第一胶黏剂层、第二胶黏剂层相互独立地由德国汉高丙烯酸压敏胶DURO-TAK 8604-2、KL-6600有机硅压敏胶粘剂、橡胶型压敏胶胶水HX6012中任意一种制成。
优选的,所述松香基超支化环氧树脂的来源无特殊要求,在本发明的一个实施例中,所述松香基超支化环氧树脂是按发明专利CN201610861045.7中实施例1的方法制成。
优选的,所述超支化聚硫醚多胺的来源无特殊要求,在本发明的一个实施例中,所述超支化聚硫醚多胺为按CN201610625403.4实施例一的方法制成。
优选的,所述N-(4-氰基-3-三氟甲基苯基)甲基丙烯酰胺/乙烯基三甲氧基硅烷/1,3-双(环氧乙烷基甲基)-5-(2-丙烯基)-1,3,5-三嗪-2,4,6(1H,3H,5H)-三酮共聚物的制备方法,包括如下步骤:将N-(4-氰基-3-三氟甲基苯基)甲基丙烯酰胺、乙烯基三甲氧基硅烷、1,3-双(环氧乙烷基甲基)-5-(2-丙烯基)-1,3,5-三嗪-2,4,6(1H,3H,5H)-三酮、引发剂加入到高沸点溶剂中,在惰性气体氛围,65-75℃下搅拌反应3-5小时,后在水中沉出,并用乙醇洗涤沉出的聚合物3-6次,最后置于真空干燥箱中85-95℃下干燥至恒重,得到N-(4-氰基-3-三氟甲基苯基)甲基丙烯酰胺/乙烯基三甲氧基硅烷/1,3-双(环氧乙烷基甲基)-5-(2-丙烯基)-1,3,5-三嗪-2,4,6(1H,3H,5H)-三酮共聚物。
优选的,所述N-(4-氰基-3-三氟甲基苯基)甲基丙烯酰胺、乙烯基三甲氧基硅烷、1,3-双(环氧乙烷基甲基)-5-(2-丙烯基)-1,3,5-三嗪-2,4,6(1H,3H,5H)-三酮、引发剂、高沸点溶剂的质量比为(3-5):1:(1-2):(0.05-0.08):(20-40)。
优选的,所述引发剂为偶氮二异丁腈、偶氮二异庚腈中的至少一种;所述高沸点溶剂为二甲亚砜、N,N-二甲基甲酰胺、N,N-二甲基乙酰胺、N-甲基吡咯烷酮中的至少一种;所述惰性气体为氮气、氦气、氖气、氩气中的任意一种。
优选的,所述纳米铝粉的粒径为300-500nm;所述石墨烯纤维的平均直径为3-9μm,长径比为(16-25)。
具体实施方式
下面将结合对本发明优选实施方案进行详细说明。
一种多层复合笔记本电脑外壳材料,其特征在于,自上而下依次包括第一保护膜层、第一石墨烯纤维布层、第一过渡层、中间芯层、第二过渡层、第二石墨烯纤维布层、第二保护膜层;所述第一保护膜层与第一石墨烯纤维布层之间设有第一胶黏剂层;所述第二保护膜层与第二石墨烯纤维布层之间设有第二胶黏剂层;所述中间芯层由镁合金制成;所述第一过渡层和第二过渡层相互独立地分别由如下按重量份计的各原料制成:松香基超支化环氧树脂20-30份、超支化聚硫醚多胺25-35份、N-(4-氰基-3-三氟甲基苯基)甲基丙烯酰胺/乙烯基三甲氧基硅烷/1,3-双(环氧乙烷基甲基)-5-(2-丙烯基)-1,3,5-三嗪-2,4,6(1H,3H,5H)-三酮共聚物20-30份、纳米铝粉3-5份、石墨烯纤维3-5份。
优选的,所述镁合金为AZ31B镁合金、AZ40M镁合金、AZ61M镁合金、AZ91D镁合金中的任意一种。
优选的,所述第一保护膜层、第二保护膜层相互独立地由聚四氟乙烯、聚对苯二甲酸乙二醇酯、PBT树脂中的任意一种制成。
优选的,所述第一胶黏剂层、第二胶黏剂层相互独立地由德国汉高丙烯酸压敏胶DURO-TAK 8604-2、KL-6600有机硅压敏胶粘剂、橡胶型压敏胶胶水HX6012中任意一种制成。
优选的,所述松香基超支化环氧树脂的来源无特殊要求,在本发明的一个实施例中,所述松香基超支化环氧树脂是按发明专利CN201610861045.7中实施例1的方法制成。
优选的,所述超支化聚硫醚多胺的来源无特殊要求,在本发明的一个实施例中,所述超支化聚硫醚多胺为按CN201610625403.4实施例一的方法制成。
优选的,所述N-(4-氰基-3-三氟甲基苯基)甲基丙烯酰胺/乙烯基三甲氧基硅烷/1,3-双(环氧乙烷基甲基)-5-(2-丙烯基)-1,3,5-三嗪-2,4,6(1H,3H,5H)-三酮共聚物的制备方法,包括如下步骤:将N-(4-氰基-3-三氟甲基苯基)甲基丙烯酰胺、乙烯基三甲氧基硅烷、1,3-双(环氧乙烷基甲基)-5-(2-丙烯基)-1,3,5-三嗪-2,4,6(1H,3H,5H)-三酮、引发剂加入到高沸点溶剂中,在惰性气体氛围,65-75℃下搅拌反应3-5小时,后在水中沉出,并用乙醇洗涤沉出的聚合物3-6次,最后置于真空干燥箱中85-95℃下干燥至恒重,得到N-(4-氰基-3-三氟甲基苯基)甲基丙烯酰胺/乙烯基三甲氧基硅烷/1,3-双(环氧乙烷基甲基)-5-(2-丙烯基)-1,3,5-三嗪-2,4,6(1H,3H,5H)-三酮共聚物。
优选的,所述N-(4-氰基-3-三氟甲基苯基)甲基丙烯酰胺、乙烯基三甲氧基硅烷、1,3-双(环氧乙烷基甲基)-5-(2-丙烯基)-1,3,5-三嗪-2,4,6(1H,3H,5H)-三酮、引发剂、高沸点溶剂的质量比为(3-5):1:(1-2):(0.05-0.08):(20-40)。
优选的,所述引发剂为偶氮二异丁腈、偶氮二异庚腈中的至少一种;所述高沸点溶剂为二甲亚砜、N,N-二甲基甲酰胺、N,N-二甲基乙酰胺、N-甲基吡咯烷酮中的至少一种;所述惰性气体为氮气、氦气、氖气、氩气中的任意一种。
优选的,所述纳米铝粉的粒径为300-500nm;所述石墨烯纤维的平均直径为3-9μm,长径比为(16-25)。
由于上述技术方案运用,本发明与现有技术相比具有下列优点:
(1)本发明提供的一种多层复合笔记本电脑外壳材料,采用多层复合结构,使得材料能同时结合各层材料的优点,使得制成的外壳材料机械强度和耐用性足,耐腐蚀性、耐磨损性、耐低温性和耐热性佳。
(2)本发明提供的一种多层复合笔记本电脑外壳材料,所述第一过渡层和第二过渡层相互独立地分别由如下按重量份计的各原料制成:松香基超支化环氧树脂20-30份、超支化聚硫醚多胺25-35份、N-(4-氰基-3-三氟甲基苯基)甲基丙烯酰胺/乙烯基三甲氧基硅烷/1,3-双(环氧乙烷基甲基)-5-(2-丙烯基)-1,3,5-三嗪-2,4,6(1H,3H,5H)-三酮共聚物20-30份、纳米铝粉3-5份、石墨烯纤维3-5份。其中同时加有铝粉和石墨烯纤维,它们与中间芯层和石墨烯纤维布层由于含有相类似的结构和组分,通过渗透能增强两层之间的结合力,进行提高材料的耐用性;其中选取的组分松香基超支化环氧树脂和N-(4-氰基-3-三氟甲基苯基)甲基丙烯酰胺/乙烯基三甲氧基硅烷/1,3-双(环氧乙烷基甲基)-5-(2-丙烯基)-1,3,5-三嗪-2,4,6(1H,3H,5H)-三酮共聚物上的环氧基能与超支化聚硫醚多胺上的氨基发生化学反应形成互穿网络结构,有效改善了粘结性能,其分子链上引入是三嗪酮、松香、氰基、三氟甲基苯基、酰胺基结构,在电子效应、位阻效应和共轭效应的多重作用下,使得材料性能稳定性好,使用寿命长,机械强度和耐用性足,耐腐蚀性、耐磨损性、耐低温性和耐热性佳。
(3)本发明提供的一种多层复合笔记本电脑外壳材料,在外壳最外层设置了保护膜层,能有效保护壳体,进而提高耐用性,改善耐候性、耐磨性和耐腐蚀性。石墨烯纤维布层的加入还能改善机械力学性能和导热性。
下面将结合具体实施例对本发明进行进一步描述,但本发明的保护范围并不仅限于此:
实施例1
一种多层复合笔记本电脑外壳材料,其特征在于,自上而下依次包括第一保护膜层、第一石墨烯纤维布层、第一过渡层、中间芯层、第二过渡层、第二石墨烯纤维布层、第二保护膜层;所述第一保护膜层与第一石墨烯纤维布层之间设有第一胶黏剂层;所述第二保护膜层与第二石墨烯纤维布层之间设有第二胶黏剂层;所述中间芯层由镁合金制成;所述第一过渡层和第二过渡层相互独立地分别由如下按重量份计的各原料制成:松香基超支化环氧树脂20份、超支化聚硫醚多胺25份、N-(4-氰基-3-三氟甲基苯基)甲基丙烯酰胺/乙烯基三甲氧基硅烷/1,3-双(环氧乙烷基甲基)-5-(2-丙烯基)-1,3,5-三嗪-2,4,6(1H,3H,5H)-三酮共聚物20份、纳米铝粉3份、石墨烯纤维3份。
所述镁合金为AZ31B镁合金;所述第一保护膜层、第二保护膜层相互独立地由聚四氟乙烯制成;所述第一胶黏剂层、第二胶黏剂层相互独立地由德国汉高丙烯酸压敏胶DURO-TAK 8604-2制成。
所述松香基超支化环氧树脂是按发明专利CN201610861045.7中实施例1的方法制成;所述超支化聚硫醚多胺为按CN201610625403.4实施例一的方法制成。
所述N-(4-氰基-3-三氟甲基苯基)甲基丙烯酰胺/乙烯基三甲氧基硅烷/1,3-双(环氧乙烷基甲基)-5-(2-丙烯基)-1,3,5-三嗪-2,4,6(1H,3H,5H)-三酮共聚物的制备方法,包括如下步骤:将N-(4-氰基-3-三氟甲基苯基)甲基丙烯酰胺、乙烯基三甲氧基硅烷、1,3-双(环氧乙烷基甲基)-5-(2-丙烯基)-1,3,5-三嗪-2,4,6(1H,3H,5H)-三酮、引发剂加入到高沸点溶剂中,在惰性气体氛围,65℃下搅拌反应3小时,后在水中沉出,并用乙醇洗涤沉出的聚合物3次,最后置于真空干燥箱中85℃下干燥至恒重,得到N-(4-氰基-3-三氟甲基苯基)甲基丙烯酰胺/乙烯基三甲氧基硅烷/1,3-双(环氧乙烷基甲基)-5-(2-丙烯基)-1,3,5-三嗪-2,4,6(1H,3H,5H)-三酮共聚物。
所述N-(4-氰基-3-三氟甲基苯基)甲基丙烯酰胺、乙烯基三甲氧基硅烷、1,3-双(环氧乙烷基甲基)-5-(2-丙烯基)-1,3,5-三嗪-2,4,6(1H,3H,5H)-三酮、引发剂、高沸点溶剂的质量比为3:1:1:0.05:20;所述引发剂为偶氮二异丁腈;所述高沸点溶剂为二甲亚砜;所述惰性气体为氮气。
所述纳米铝粉的粒径为300nm;所述石墨烯纤维的平均直径为3μm,长径比为16。
实施例2
一种多层复合笔记本电脑外壳材料,其与实施例1基本相同,不同的是,所述第一过渡层和第二过渡层相互独立地分别由如下按重量份计的各原料制成:松香基超支化环氧树脂23份、超支化聚硫醚多胺28份、N-(4-氰基-3-三氟甲基苯基)甲基丙烯酰胺/乙烯基三甲氧基硅烷/1,3-双(环氧乙烷基甲基)-5-(2-丙烯基)-1,3,5-三嗪-2,4,6(1H,3H,5H)-三酮共聚物23份、纳米铝粉3.5份、石墨烯纤维3.5份。
实施例3
一种多层复合笔记本电脑外壳材料,其与实施例1基本相同,不同的是,所述第一过渡层和第二过渡层相互独立地分别由如下按重量份计的各原料制成:松香基超支化环氧树脂25份、超支化聚硫醚多胺30份、N-(4-氰基-3-三氟甲基苯基)甲基丙烯酰胺/乙烯基三甲氧基硅烷/1,3-双(环氧乙烷基甲基)-5-(2-丙烯基)-1,3,5-三嗪-2,4,6(1H,3H,5H)-三酮共聚物25份、纳米铝粉4份、石墨烯纤维4份。
实施例4
一种多层复合笔记本电脑外壳材料,其与实施例1基本相同,不同的是,所述第一过渡层和第二过渡层相互独立地分别由如下按重量份计的各原料制成:松香基超支化环氧树脂28份、超支化聚硫醚多胺33份、N-(4-氰基-3-三氟甲基苯基)甲基丙烯酰胺/乙烯基三甲氧基硅烷/1,3-双(环氧乙烷基甲基)-5-(2-丙烯基)-1,3,5-三嗪-2,4,6(1H,3H,5H)-三酮共聚物28份、纳米铝粉4.5份、石墨烯纤维4.5份。
实施例5
一种多层复合笔记本电脑外壳材料,其与实施例1基本相同,不同的是,所述第一过渡层和第二过渡层相互独立地分别由如下按重量份计的各原料制成:松香基超支化环氧树脂30份、超支化聚硫醚多胺35份、N-(4-氰基-3-三氟甲基苯基)甲基丙烯酰胺/乙烯基三甲氧基硅烷/1,3-双(环氧乙烷基甲基)-5-(2-丙烯基)-1,3,5-三嗪-2,4,6(1H,3H,5H)-三酮共聚物30份、纳米铝粉5份、石墨烯纤维5份。
对比例
一种多层复合笔记本电脑外壳材料,其与实施例1基本相同,不同的是,用松香基超支化环氧树脂代替N-(4-氰基-3-三氟甲基苯基)甲基丙烯酰胺/乙烯基三甲氧基硅烷/1,3-双(环氧乙烷基甲基)-5-(2-丙烯基)-1,3,5-三嗪-2,4,6(1H,3H,5H)-三酮共聚物。
为了进一步说明各实施例所涉及的多层复合笔记本电脑外壳材料的有益技术效果,按照现有技术中常规制造方法,将第一过渡层各原料加入到挤出机中熔融,并经过衣架型T-模、镀铬的压延辊、干燥辊等制成第一过渡层;将第二过渡层各原料加入到挤出机中熔融,并经过衣架型T-模、镀铬的压延辊、干燥辊等制成第二过渡层;然后自上而下依次叠合第一保护膜层、第一胶黏剂层、第一石墨烯纤维布层、第一过渡层、中间芯层、第二过渡层、第二石墨烯纤维布层、第二胶黏剂层、第二保护膜层,压制成型后,制得各例中的多层复合笔记本电脑外壳材料,再对各例制成的多层复合笔记本电脑外壳材料进行相关性能测试,测试方法参见我国现行相应国标,测试结果见表1。
表1
测试项目 | 单位 | 实施例1 | 实施例2 | 实施例3 | 实施例4 | 实施例5 | 对比例 |
20℃粘结强度 | MPa | 6.76 | 6.82 | 6.85 | 6.89 | 6.73 | 6.53 |
80℃粘结强度 | MPa | 6.70 | 6.78 | 6.82 | 6.86 | 6.72 | 6.29 |
-50℃粘结强度 | MPa | 6.67 | 6.76 | 6.81 | 6.85 | 6.70 | 6.22 |
从上表可以看出,本发明实施例公开的多层复合笔记本电脑外壳材料较对比例具有更优异的粘结强度,且耐高温、耐低温性能更好,这是各原料和含量相互配合共同作用的结果。
上述实施例只为说明本发明的技术构思及特点,其目的在于让熟悉此项技术的人士能够了解本发明的内容并据以实施,并不能以此限制本发明的保护范围,凡根据依据本发明精神实质所作的等效变化或修饰,都应涵盖在本发明的保护范围之内。
Claims (8)
1.一种多层复合笔记本电脑外壳材料,其特征在于,自上而下依次包括第一保护膜层、第一石墨烯纤维布层、第一过渡层、中间芯层、第二过渡层、第二石墨烯纤维布层、第二保护膜层;所述第一保护膜层与第一石墨烯纤维布层之间设有第一胶黏剂层;所述第二保护膜层与第二石墨烯纤维布层之间设有第二胶黏剂层;所述中间芯层由镁合金制成;所述第一过渡层和第二过渡层相互独立地分别由如下按重量份计的各原料制成:松香基超支化环氧树脂20-30份、超支化聚硫醚多胺25-35份、N-(4-氰基-3-三氟甲基苯基)甲基丙烯酰胺/乙烯基三甲氧基硅烷/1,3-双(环氧乙烷基甲基)-5-(2-丙烯基)-1,3,5-三嗪-2,4,6(1H,3H,5H)-三酮共聚物20-30份、纳米铝粉3-5份、石墨烯纤维3-5份。
2.根据权利要求1所述多层复合笔记本电脑外壳材料,其特征在于,所述镁合金为AZ31B镁合金、AZ40M镁合金、AZ61M镁合金、AZ91D镁合金中的任意一种。
3.根据权利要求1所述多层复合笔记本电脑外壳材料,其特征在于,所述第一保护膜层、第二保护膜层相互独立地由聚四氟乙烯、聚对苯二甲酸乙二醇酯、PBT树脂中的任意一种制成。
4.根据权利要求1所述多层复合笔记本电脑外壳材料,其特征在于,所述第一胶黏剂层、第二胶黏剂层相互独立地由德国汉高丙烯酸压敏胶DURO-TAK 8604-2、KL-6600有机硅压敏胶粘剂、橡胶型压敏胶胶水HX6012中任意一种制成。
5.根据权利要求1所述多层复合笔记本电脑外壳材料,其特征在于,所述N-(4-氰基-3-三氟甲基苯基)甲基丙烯酰胺/乙烯基三甲氧基硅烷/1,3-双(环氧乙烷基甲基)-5-(2-丙烯基)-1,3,5-三嗪-2,4,6(1H,3H,5H)-三酮共聚物的制备方法,包括如下步骤:将N-(4-氰基-3-三氟甲基苯基)甲基丙烯酰胺、乙烯基三甲氧基硅烷、1,3-双(环氧乙烷基甲基)-5-(2-丙烯基)-1,3,5-三嗪-2,4,6(1H,3H,5H)-三酮、引发剂加入到高沸点溶剂中,在惰性气体氛围,65-75℃下搅拌反应3-5小时,后在水中沉出,并用乙醇洗涤沉出的聚合物3-6次,最后置于真空干燥箱中85-95℃下干燥至恒重,得到N-(4-氰基-3-三氟甲基苯基)甲基丙烯酰胺/乙烯基三甲氧基硅烷/1,3-双(环氧乙烷基甲基)-5-(2-丙烯基)-1,3,5-三嗪-2,4,6(1H,3H,5H)-三酮共聚物。
6.根据权利要求5所述多层复合笔记本电脑外壳材料,其特征在于,所述N-(4-氰基-3-三氟甲基苯基)甲基丙烯酰胺、乙烯基三甲氧基硅烷、1,3-双(环氧乙烷基甲基)-5-(2-丙烯基)-1,3,5-三嗪-2,4,6(1H,3H,5H)-三酮、引发剂、高沸点溶剂的质量比为(3-5):1:(1-2):(0.05-0.08):(20-40)。
7.根据权利要求5所述多层复合笔记本电脑外壳材料,其特征在于,所述引发剂为偶氮二异丁腈、偶氮二异庚腈中的至少一种;所述高沸点溶剂为二甲亚砜、N,N-二甲基甲酰胺、N,N-二甲基乙酰胺、N-甲基吡咯烷酮中的至少一种;所述惰性气体为氮气、氦气、氖气、氩气中的任意一种。
8.根据权利要求1所述多层复合笔记本电脑外壳材料,其特征在于,所述纳米铝粉的粒径为300-500nm;所述石墨烯纤维的平均直径为3-9μm,长径比为(16-25)。