CN113717479A - 一种防鼠pvc涂层工艺夹网材料及其生产制备方法 - Google Patents
一种防鼠pvc涂层工艺夹网材料及其生产制备方法 Download PDFInfo
- Publication number
- CN113717479A CN113717479A CN202111091214.0A CN202111091214A CN113717479A CN 113717479 A CN113717479 A CN 113717479A CN 202111091214 A CN202111091214 A CN 202111091214A CN 113717479 A CN113717479 A CN 113717479A
- Authority
- CN
- China
- Prior art keywords
- polyvinyl chloride
- coating
- ratproof
- parts
- polyester fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种防鼠PVC涂层工艺夹网材料及其生产制备方法，将辣椒素添加到聚氯乙烯基础糊剂中制得防鼠聚氯乙烯糊剂，所述辣椒素的添加量占防鼠聚氯乙烯糊剂总重量的0.5％‑1.5％；涂覆打底：配制好的防鼠聚氯乙烯糊剂通过涂层工艺涂覆在聚酯纤维网布上，将聚酯纤维网布间隙涂满，对聚酯纤维网布两面涂覆后进行预塑化；塑化：对步骤二得到的聚酯纤维网布其中一面再涂覆一层防鼠聚氯乙烯糊剂；最后对聚酯纤维网布另外一面涂覆防鼠聚氯乙烯糊剂，最终进行完全塑化；成型。本发明涉及PVC涂层夹网布材料技术领域，具体是提供了一种防鼠PVC涂层工艺夹网材料及其生产制备方法，利用辣椒素的强烈辛辣味刺激鼠类动物的口腔粘膜和味觉神经。
Description
技术领域
本发明涉及PVC涂层夹网布材料技术领域，具体是指一种防鼠PVC涂层工艺夹网材料及其生产制备方法。
背景技术
PVC涂层夹网布材料已经广泛应用于各个领域，其中在作为粮仓建筑材料、储气柜材料和液袋材料等领域通常会遇到老鼠啃咬情况，导致粮食被毁、储气柜漏气以及液袋泄漏，更换修补麻烦费时费力。这些材料市场需求越来越大，解决防鼠咬问题就可以更好开发相关市场，而且目前国内外市场都还没有防鼠咬PVC涂层材料，因此，开发一款防鼠PVC涂层工艺夹网布材料在市场上将有广阔的应用前景。
发明内容
针对上述情况，为克服现有技术的缺陷，本发明提供了一种防鼠PVC涂层工艺夹网材料及其生产制备方法，利用辣椒素的强烈辛辣味，能使鼠类动物的口腔粘膜和味觉神经受到强烈刺激而厌弃咀嚼，同时又能击杀白蚁。
本发明采取的技术方案如下：一种防鼠PVC涂层工艺夹网材料的制备方法，包括如下步骤：
步骤一，制备防鼠聚氯乙烯糊剂：将溶化制成液体的辣椒素添加到聚氯乙烯基础糊剂中制得防鼠聚氯乙烯糊剂，所述辣椒素的添加量占防鼠聚氯乙烯糊剂总重量的0.5％-1.5％；
步骤二，涂覆打底：配制好的防鼠聚氯乙烯糊剂通过涂层工艺涂覆在聚酯纤维网布上，将聚酯纤维网布间隙涂满，聚酯纤维网布两面涂覆后进行预塑化，两面的涂覆量为80-200gsm，预塑化温度为140-160℃，完成打底工作；
步骤三，塑化：对步骤二得到的聚酯纤维网布其中一面再涂覆一层防鼠聚氯乙烯糊剂，涂覆量为200-500gsm，再次进行预塑化，预塑化温度为160-175℃；最后对聚酯纤维网布另外一面涂覆防鼠聚氯乙烯糊剂，涂覆量为200-700gsm，最终进行完全塑化，塑化温度180-210℃；
步骤四，成型：最后完成压花、冷切成型、切边和收卷。
进一步地，所述聚氯乙烯基础糊剂包括如下重量份的组分：聚氯乙烯80-85份，掺混树脂15-20份，邻苯二甲酸二异壬酯65-75份，热稳定剂2.5-3.5份，大豆油1-2份，阻燃剂6-12份，重钙20-35份，氢氧化铝10-15份，防霉剂2-2.5份，紫外吸收剂0.8-1.5份，抗
氧剂0.4-0.6份。
进一步地，所述防鼠聚氯乙烯糊剂的制备方法为：将辣椒素与邻苯二甲酸二异壬酯先混合后放置在60-80℃烘箱中溶解，然后与聚氯乙烯、掺混树脂、热稳定剂、大豆油、阻燃剂、重钙、氢氧化铝、防霉剂、紫外吸收剂和抗氧剂混合。
进一步地，所述热稳定剂为钡锌稳定剂或钙锌稳定剂。
进一步地，所述大豆油为环氧大豆油。
进一步地，所述阻燃剂为氧化锑。
采用上述结构本发明取得的有益效果如下：
1、本方案具备配方、生产工艺完整性、可行性和操作性；
2、本方案开发一款新的防鼠PVC涂层工艺夹网布材料，防鼠咬保护率可以达到99％以上，并且具有永久性；
3、本方案产品符合环保要求，同时阻燃、防霉和抗老化等优良性能，也具体高强度的物理性能。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例；基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1，一种防鼠PVC涂层工艺夹网材料的制备方法，包括如下步骤：
步骤一，制备防鼠聚氯乙烯糊剂：将辣椒素与邻苯二甲酸二异壬酯先混合后放置在60-80℃烘箱中溶解，然后与聚氯乙烯、掺混树脂、热稳定剂、大豆油、阻燃剂、重钙、氢氧化铝、防霉剂、紫外吸收剂和抗氧剂混合，所述辣椒素的添加量占防鼠聚氯乙烯糊剂总重量的0.5％-1.5％；
所述聚氯乙烯基础糊剂包括如下重量份的组分：聚氯乙烯80份，掺混树脂15份，邻苯二甲酸二异壬酯65份，热稳定剂2.5份，大豆油1份，氧化锑6份，重钙20份，氢氧化铝10份，防霉剂2份，紫外吸收剂0.8份，抗氧剂0.4份；
步骤二，涂覆打底：配制好的防鼠聚氯乙烯糊剂通过涂层工艺涂覆在聚酯纤维网布上，将聚酯纤维网布间隙涂满，对聚酯纤维网布两面涂覆后进行预塑化，两面的涂覆量为80-200gsm，预塑化温度为140-160℃，完成打底工作；
步骤三，塑化：对步骤二得到的聚酯纤维网布其中一面再涂覆一层防鼠聚氯乙烯糊剂，涂覆量为200-500gsm，再次进行预塑化，预塑化温度为160-175℃；最后对聚酯纤维网布另外一面涂覆防鼠聚氯乙烯糊剂，涂覆量为200-700gsm，最终进行完全塑化，塑化温度180-210℃；
步骤四，成型：最后完成压花、冷切成型、切边和收卷。
所述热稳定剂为钡锌稳定剂或钙锌稳定剂。
所述大豆油为环氧大豆油。
实施例2，一种防鼠PVC涂层工艺夹网材料的制备方法，包括如下步骤：
步骤一，制备防鼠聚氯乙烯糊剂：将辣椒素与邻苯二甲酸二异壬酯先混合后放置在60-80℃烘箱中溶解，然后与聚氯乙烯、掺混树脂、热稳定剂、大豆油、阻燃剂、重钙、氢氧化铝、防霉剂、紫外吸收剂和抗氧剂混合，所述辣椒素的添加量占防鼠聚氯乙烯糊剂总重量的0.5％-1.5％；
所述聚氯乙烯基础糊剂包括如下重量份的组分：聚氯乙烯82.5份，掺混树脂17.5份，邻苯二甲酸二异壬酯70份，热稳定剂3份，大豆油1.5份，氧化锑9.5份，重钙27.5份，氢氧化铝12.5份，防霉剂2.25份，紫外吸收剂1.15份，抗氧剂0.5份；
步骤二，涂覆打底：配制好的防鼠聚氯乙烯糊剂通过涂层工艺涂覆在聚酯纤维网布上，将聚酯纤维网布间隙涂满，对聚酯纤维网布两面涂覆后进行预塑化，两面的涂覆量为80-200gsm，预塑化温度为140-160℃，完成打底工作；
步骤三，塑化：对步骤二得到的聚酯纤维网布其中一面再涂覆一层防鼠聚氯乙烯糊剂，涂覆量为200-500gsm，再次进行预塑化，预塑化温度为160-175℃；最后对聚酯纤维网布另外一面涂覆防鼠聚氯乙烯糊剂，涂覆量为200-700gsm，最终进行完全塑化，塑化温度180-210℃；
步骤四，成型：最后完成压花、冷切成型、切边和收卷。
所述热稳定剂为钡锌稳定剂或钙锌稳定剂。
所述大豆油为环氧大豆油。
实施例3，一种防鼠PVC涂层工艺夹网材料的制备方法，包括如下步骤：
步骤一，制备防鼠聚氯乙烯糊剂：将辣椒素与邻苯二甲酸二异壬酯先混合后放置在60-80℃烘箱中溶解，然后与聚氯乙烯、掺混树脂、热稳定剂、大豆油、阻燃剂、重钙、氢氧化铝、防霉剂、紫外吸收剂和抗氧剂混合，所述辣椒素的添加量占防鼠聚氯乙烯糊剂总重量的0.5％-1.5％；
所述聚氯乙烯基础糊剂包括如下重量份的组分：聚氯乙烯85份，掺混树脂20份，邻苯二甲酸二异壬酯75份，热稳定剂3.5份，大豆油2份，氧化锑12份，重钙35份，氢氧化铝15份，防霉剂2.5份，紫外吸收剂1.5份，抗氧剂0.6份；
步骤二，涂覆打底：配制好的防鼠聚氯乙烯糊剂通过涂层工艺涂覆在聚酯纤维网布上，将聚酯纤维网布间隙涂满，对聚酯纤维网布两面涂覆后进行预塑化，两面的涂覆量为80-200gsm，预塑化温度为140-160℃，完成打底工作；
步骤三，塑化：对步骤二得到的聚酯纤维网布其中一面再涂覆一层防鼠聚氯乙烯糊剂，涂覆量为200-500gsm，再次进行预塑化，预塑化温度为160-175℃；最后对聚酯纤维网布另外一面涂覆防鼠聚氯乙烯糊剂，涂覆量为200-700gsm，最终进行完全塑化，塑化温度180-210℃；
步骤四，成型：最后完成压花、冷切成型、切边和收卷。
所述热稳定剂为钡锌稳定剂或钙锌稳定剂。
所述大豆油为环氧大豆油。
需要说明的是，在本文中，术语“包括”、“包含”或者其任何其他变体意在涵盖非排他性的包含，从而使得包括一系列要素的过程、方法、物品或者设备不仅包括那些要素，而且还包括没有明确列出的其他要素，或者是还包括为这种过程、方法、物品或者设备所固有的要素。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (7)
1.一种防鼠PVC涂层工艺夹网材料的制备方法，其特征在于，包括如下步骤：
步骤一，制备防鼠聚氯乙烯糊剂：将溶化制成液体的辣椒素添加到聚氯乙烯基础糊剂中制得防鼠聚氯乙烯糊剂，所述辣椒素的添加量占防鼠聚氯乙烯糊剂总重量的0.5％-1.5％；
步骤二，涂覆打底：配制好的防鼠聚氯乙烯糊剂通过涂层工艺涂覆在聚酯纤维网布上，将聚酯纤维网布间隙涂满，对聚酯纤维网布两面涂覆后进行预塑化，两面的涂覆量为80-200gsm，预塑化温度为140-160℃，完成打底工作；
步骤三，塑化：对步骤二得到的聚酯纤维网布其中一面再涂覆一层防鼠聚氯乙烯糊剂，涂覆量为200-500gsm，再次进行预塑化，预塑化温度为160-175℃；最后对聚酯纤维网布另外一面涂覆防鼠聚氯乙烯糊剂，涂覆量为200-700gsm，最终进行完全塑化，塑化温度180-210℃；
步骤四，成型：最后完成压花、冷切成型、切边和收卷。
2.根据权利要求1所述的一种防鼠PVC涂层工艺夹网材料的制备方法，其特征在于，所述聚氯乙烯基础糊剂包括如下重量份的组分：聚氯乙烯80-85份，掺混树脂15-20份，邻苯二甲酸二异壬酯65-75份，热稳定剂2.5-3.5份，大豆油1-2份，阻燃剂6-12份，重钙20-35份，氢氧化铝10-15份，防霉剂2-2.5份，紫外吸收剂0.8-1.5份，抗氧剂0.4-0.6份。
3.根据权利要求1所述的一种防鼠PVC涂层工艺夹网材料的制备方法，其特征在于，所述防鼠聚氯乙烯糊剂的制备方法为：将辣椒素与邻苯二甲酸二异壬酯先混合后放置在60-80℃烘箱中溶解，然后与聚氯乙烯、掺混树脂、热稳定剂、大豆油、阻燃剂、重钙、氢氧化铝、防霉剂、紫外吸收剂和抗氧剂混合。
4.根据权利要求1所述的一种防鼠PVC涂层工艺夹网材料的制备方法，其特征在于，所述热稳定剂为钡锌稳定剂或钙锌稳定剂。
5.根据权利要求1所述的一种防鼠PVC涂层工艺夹网材料的制备方法，其特征在于，所述大豆油为环氧大豆油。
6.根据权利要求1所述的一种防鼠PVC涂层工艺夹网材料的制备方法，其特征在于，所述阻燃剂为氧化锑。
7.一种防鼠PVC涂层工艺夹网材料，其特征在于，所述防鼠PVC涂层工艺夹网材料根据权利要求1～6任一项所述的制备方法制得。