CN113652605B - 一种高强韧汽车车轮用钢、薄壁汽车车轮及其制备方法 - Google Patents
一种高强韧汽车车轮用钢、薄壁汽车车轮及其制备方法 Download PDFInfo
- Publication number
- CN113652605B CN113652605B CN202110785499.1A CN202110785499A CN113652605B CN 113652605 B CN113652605 B CN 113652605B CN 202110785499 A CN202110785499 A CN 202110785499A CN 113652605 B CN113652605 B CN 113652605B
- Authority
- CN
- China
- Prior art keywords
- automobile wheel
- steel
- toughness
- cooling
- strength
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
元素 | C | Mn | Si | Al | P | S |
含量 | 0.20 | 1.8 | 1.0 | 0.036 | 0.014 | 0.002 |
元素 | C | Mn | Si | Cr | Mo | Ni | Cu | Ti | V | P | S |
含量 | 0.20 | 1.8 | 1.0 | 1.0 | 0.3 | 0.5 | 0.2 | 0.05 | 0.06 | 0.01 | 0.005 |
Claims (10)