CN113638074A - 含姜活性成分的涤纶大生物纤维及其制备方法 - Google Patents
含姜活性成分的涤纶大生物纤维及其制备方法 Download PDFInfo
- Publication number
- CN113638074A CN113638074A CN202110955243.0A CN202110955243A CN113638074A CN 113638074 A CN113638074 A CN 113638074A CN 202110955243 A CN202110955243 A CN 202110955243A CN 113638074 A CN113638074 A CN 113638074A
- Authority
- CN
- China
- Prior art keywords
- parts
- ginger
- active ingredients
- polyester
- fiber containing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种含姜活性成分的涤纶大生物纤维及其制备方法，涤纶大生物纤维包括以下原料：涤纶聚酯切片、介孔SiO2纳米粉体、焦磷酸钠、季戊四醇、消光粉、直链烷基苯磺酸钠、烷基烯酮二聚体、富勒烯、抗氧化剂、聚乙烯胺、聚氯乙烯、聚丙烯、聚酰胺、玉米预糊化淀粉、瓜尔胶、乙醇、姜活性成分、分散剂。本发明能够有效的提高涤纶大生物纤维的抗拉伸性能，降低其损坏的风险，且提高涤纶大生物纤维的抗菌性能，有利于使用。
Description
技术领域
本发明涉及涤纶大生物纤维领域，尤其涉及一种含姜活性成分的涤纶大生物纤维及其制备方法。
背景技术
涤纶，又称聚酯纤维，是由有机二元酸和二元醇缩聚而成的聚酯经纺丝所得的合成纤维，简称PET纤维，属于高分子化合物，大生物纤维，是指在纤维(棉、麻、毛、丝、粘、涤、腈、锦等)中加入生物活性分子进行改性，由此生产出的具有生物功能的活性纤维，因此，涤纶大生物纤维正是通过利用人参/灵芝/枸杞/藏红花/姜中的生物活性分子对涤纶纤维进行改性，赋予涤纶纤维相应的生物功能；
现有的含姜活性成分的涤纶纤维，其抗菌性能和抗拉伸效果较差，其在使用的过程中经常出现因拉扯力较大造成拉坏的现象，且有害物质容易被吸收进入到纤维内，对使用人员的身体存在较大的危害，不能满足使用需求，综合上述情况加以改进，因此我们提出了含姜活性成分的涤纶大生物纤维及其制备方法。
发明内容
基于背景技术存在的技术问题，本发明提出了含姜活性成分的涤纶大生物纤维及其制备方法。
本发明提出的含姜活性成分的涤纶大生物纤维，包括以下重量份的原料：涤纶聚酯切片100-300份、介孔SiO2纳米粉体10-20份、焦磷酸钠0.5-2份、季戊四醇0.3-1份、消光粉1-3份、直链烷基苯磺酸钠1-2份、烷基烯酮二聚体0.2-0.8份、富勒烯0.5-0.8份、抗氧化剂0.1-0.3份、聚乙烯胺0.2-0.5份、聚氯乙烯1-2份、聚丙烯1-3份、聚酰胺1-2份、玉米预糊化淀粉0.7-1份、瓜尔胶0.2-0.5份、乙醇8-16份、姜活性成分1-3份、分散剂1-3份。
优选的，包括以下重量份的原料：涤纶聚酯切片100份、介孔SiO2纳米粉体10份、焦磷酸钠0.5份、季戊四醇0.3份、消光粉1份、直链烷基苯磺酸钠1份、烷基烯酮二聚体0.2份、富勒烯0.5份、抗氧化剂0.1份、聚乙烯胺0.2份、聚氯乙烯1份、聚丙烯1份、聚酰胺1份、玉米预糊化淀粉0.7份、瓜尔胶0.2份、乙醇8份、姜活性成分1份、分散剂1份。
优选的，包括以下重量份的原料：涤纶聚酯切片200份、介孔SiO2纳米粉体25份、焦磷酸钠1份、季戊四醇0.8份、消光粉2份、直链烷基苯磺酸钠1.5份、烷基烯酮二聚体0.6份、富勒烯0.6份、抗氧化剂0.2份、聚乙烯胺0.3份、聚氯乙烯1.5份、聚丙烯2份、聚酰胺1.5份、玉米预糊化淀粉0.9份、瓜尔胶0.3份、乙醇12份、姜活性成分2份、分散剂2份。
优选的，包括以下重量份的原料：涤纶聚酯切片300份、介孔SiO2纳米粉体20份、焦磷酸钠2份、季戊四醇1份、消光粉3份、直链烷基苯磺酸钠2份、烷基烯酮二聚体0.8份、富勒烯0.8份、抗氧化剂0.3份、聚乙烯胺0.5份、聚氯乙烯2份、聚丙烯3份、聚酰胺2份、玉米预糊化淀粉1份、瓜尔胶0.5份、乙醇16份、姜活性成分3份、分散剂3份。
优选的，所述消光粉的型号为OK52。
优选的，所述姜活性成分包括姜精油、姜辣素、生姜蛋白酶和二苯基庚烷类物质，其中姜辣素包含姜烯酚类、姜二醇类、姜酚类、姜二酮类、姜醇类、姜酮类和副姜油酮类。
优选的，所述聚乙烯胺为硅烷偶联剂。
本发明还提出了含姜活性成分的涤纶大生物纤维的制备方法，包括以下步骤：
S1：取焦磷酸钠0.5-2份、季戊四醇0.3-1份、消光粉1-3份、直链烷基苯磺酸钠1-2份、烷基烯酮二聚体0.2-0.8份和富勒烯0.5-0.8份放置到搅拌箱内，进行搅拌混合，搅拌混合均匀后，取出放置在研磨机内进行研磨，研磨出粒径为6-8μm的粒子，得到混制颗粒；
S2：取聚乙烯胺0.2-0.5份、聚氯乙烯1-2份、聚丙烯1-3份、聚酰胺1-2份、玉米预糊化淀粉0.7-1份和瓜尔胶0.2-0.5份放置在搅拌箱内，同时加入适量的水，进行搅拌混合均匀，取出混合均匀的原料放入到加热罐中进行加热处理，加热至70-80℃，制得抗拉伸溶液，然后再浓缩操作，得到抗拉伸晶体，研磨粉碎、备用；
S3：将姜活性成分1-3份、介孔SiO2纳米粉体10-20份和分散剂1-3份依次加入到500mL去离子水中，并使用磁力搅拌器进行剪切分散，磁力搅拌器的转速设置为100-300r/min；得到含活性成分的纳米复合分散液，将分散液进行溶剂挥发，得到含小黄姜活性成分的介孔SiO2分子巢，研磨粉碎、备用；
S4：将S1中的混制颗粒、S2中的抗拉伸晶体、S3中的含小黄姜活性成分的介孔SiO2分子巢、抗氧化剂0.1-0.3份和涤纶聚酯切片100-300份使用熔融纺丝方法进行纺丝、拉伸卷绕，制得含姜活性成分的涤纶大生物纤维；
S5：将S4中制得的含姜活性成分的涤纶大生物纤维放入到8-16份的乙醇溶液中进行浸泡，浸泡30-50min，取出自然晾干，制得消毒处理后的含姜活性成分的涤纶大生物纤维。
与现有的技术相比，本发明的有益效果是：
本发明能够有效的提高涤纶大生物纤维的抗拉伸性能，降低其损坏的风险，且提高涤纶大生物纤维的抗菌性能，有利于使用。
具体实施方式
下面结合具体实施例对本发明作进一步解说。
实施例一
本实施例提出了含姜活性成分的涤纶大生物纤维，包括以下重量份的原料：涤纶聚酯切片100份、介孔SiO2纳米粉体10份、焦磷酸钠0.5份、季戊四醇0.3份、消光粉1份、直链烷基苯磺酸钠1份、烷基烯酮二聚体0.2份、富勒烯0.5份、抗氧化剂0.1份、聚乙烯胺0.2份、聚氯乙烯1份、聚丙烯1份、聚酰胺1份、玉米预糊化淀粉0.7份、瓜尔胶0.2份、乙醇8份、姜活性成分1份、分散剂1份，其中消光粉的型号为OK52，姜活性成分包括姜精油、姜辣素、生姜蛋白酶和二苯基庚烷类物质，其中姜辣素包含姜烯酚类、姜二醇类、姜酚类、姜二酮类、姜醇类、姜酮类和副姜油酮类，聚乙烯胺为硅烷偶联剂。
本实施例还提出了含姜活性成分的涤纶大生物纤维的制备方法，包括以下步骤：
S1：取焦磷酸钠0.5份、季戊四醇0.3份、消光粉1份、直链烷基苯磺酸钠1份、烷基烯酮二聚体0.2份和富勒烯0.5份放置到搅拌箱内，进行搅拌混合，搅拌混合均匀后，取出放置在研磨机内进行研磨，研磨出粒径为6-8μm的粒子，得到混制颗粒；
S2：取聚乙烯胺0.2份、聚氯乙烯1份、聚丙烯1份、聚酰胺1份、玉米预糊化淀粉0.7份和瓜尔胶0.2份放置在搅拌箱内，同时加入适量的水，进行搅拌混合均匀，取出混合均匀的原料放入到加热罐中进行加热处理，加热至70-80℃，制得抗拉伸溶液，然后再浓缩操作，得到抗拉伸晶体，研磨粉碎、备用；
S3：将姜活性成分1份、介孔SiO2纳米粉体10份和分散剂1份依次加入到500mL去离子水中，并使用磁力搅拌器进行剪切分散，磁力搅拌器的转速设置为100-300r/min；得到含活性成分的纳米复合分散液，将分散液进行溶剂挥发，得到含小黄姜活性成分的介孔SiO2分子巢，研磨粉碎、备用；
S4：将S1中的混制颗粒、S2中的抗拉伸晶体、S3中的含小黄姜活性成分的介孔SiO2分子巢、抗氧化剂0.1份和涤纶聚酯切片100份使用熔融纺丝方法进行纺丝、拉伸卷绕，制得含姜活性成分的涤纶大生物纤维；
S5：将S4中制得的含姜活性成分的涤纶大生物纤维放入到8份的乙醇溶液中进行浸泡，浸泡30-50min，取出自然晾干，制得消毒处理后的含姜活性成分的涤纶大生物纤维。
实施例二
本实施例提出了含姜活性成分的涤纶大生物纤维，包括以下重量份的原料：涤纶聚酯切片200份、介孔SiO2纳米粉体25份、焦磷酸钠1份、季戊四醇0.8份、消光粉2份、直链烷基苯磺酸钠1.5份、烷基烯酮二聚体0.6份、富勒烯0.6份、抗氧化剂0.2份、聚乙烯胺0.3份、聚氯乙烯1.5份、聚丙烯2份、聚酰胺1.5份、玉米预糊化淀粉0.9份、瓜尔胶0.3份、乙醇12份、姜活性成分2份、分散剂2份，其中消光粉的型号为OK52，姜活性成分包括姜精油、姜辣素、生姜蛋白酶和二苯基庚烷类物质，其中姜辣素包含姜烯酚类、姜二醇类、姜酚类、姜二酮类、姜醇类、姜酮类和副姜油酮类，聚乙烯胺为硅烷偶联剂。
本实施例还提出了含姜活性成分的涤纶大生物纤维的制备方法，包括以下步骤：
S1：取焦磷酸钠1份、季戊四醇0.8份、消光粉2份、直链烷基苯磺酸钠1.5份、烷基烯酮二聚体0.6份和富勒烯0.6份放置到搅拌箱内，进行搅拌混合，搅拌混合均匀后，取出放置在研磨机内进行研磨，研磨出粒径为6-8μm的粒子，得到混制颗粒；
S2：取聚乙烯胺0.3份、聚氯乙烯1.5份、聚丙烯2份、聚酰胺1.5份、玉米预糊化淀粉0.9份和瓜尔胶0.3份放置在搅拌箱内，同时加入适量的水，进行搅拌混合均匀，取出混合均匀的原料放入到加热罐中进行加热处理，加热至70-80℃，制得抗拉伸溶液，然后再浓缩操作，得到抗拉伸晶体，研磨粉碎、备用；
S3：将姜活性成分2份、介孔SiO2纳米粉体25份和分散剂2份依次加入到500mL去离子水中，并使用磁力搅拌器进行剪切分散，磁力搅拌器的转速设置为100-300r/min；得到含活性成分的纳米复合分散液，将分散液进行溶剂挥发，得到含小黄姜活性成分的介孔SiO2分子巢，研磨粉碎、备用；
S4：将S1中的混制颗粒、S2中的抗拉伸晶体、S3中的含小黄姜活性成分的介孔SiO2分子巢、抗氧化剂0.2份和涤纶聚酯切片200份使用熔融纺丝方法进行纺丝、拉伸卷绕，制得含姜活性成分的涤纶大生物纤维；
S5：将S4中制得的含姜活性成分的涤纶大生物纤维放入到乙醇12份的乙醇溶液中进行浸泡，浸泡30-50min，取出自然晾干，制得消毒处理后的含姜活性成分的涤纶大生物纤维。
实施例三
本实施例提出了含姜活性成分的涤纶大生物纤维，包括以下重量份的原料：涤纶聚酯切片300份、介孔SiO2纳米粉体20份、焦磷酸钠2份、季戊四醇1份、消光粉3份、直链烷基苯磺酸钠2份、烷基烯酮二聚体0.8份、富勒烯0.8份、抗氧化剂0.3份、聚乙烯胺0.5份、聚氯乙烯2份、聚丙烯3份、聚酰胺2份、玉米预糊化淀粉1份、瓜尔胶0.5份、乙醇16份、姜活性成分3份、分散剂3份，其中消光粉的型号为OK52，姜活性成分包括姜精油、姜辣素、生姜蛋白酶和二苯基庚烷类物质，其中姜辣素包含姜烯酚类、姜二醇类、姜酚类、姜二酮类、姜醇类、姜酮类和副姜油酮类，聚乙烯胺为硅烷偶联剂。
本实施例还提出了含姜活性成分的涤纶大生物纤维的制备方法，包括以下步骤：
S1：取焦磷酸钠2份、季戊四醇1份、消光粉3份、直链烷基苯磺酸钠2份、烷基烯酮二聚体0.8份和富勒烯0.8份放置到搅拌箱内，进行搅拌混合，搅拌混合均匀后，取出放置在研磨机内进行研磨，研磨出粒径为6-8μm的粒子，得到混制颗粒；
S2：取聚乙烯胺0.5份、聚氯乙烯2份、聚丙烯3份、聚酰胺2份、玉米预糊化淀粉1份和瓜尔胶0.5份放置在搅拌箱内，同时加入适量的水，进行搅拌混合均匀，取出混合均匀的原料放入到加热罐中进行加热处理，加热至70-80℃，制得抗拉伸溶液，然后再浓缩操作，得到抗拉伸晶体，研磨粉碎、备用；
S3：将姜活性成分3份、介孔SiO2纳米粉体20份和分散剂3份依次加入到500mL去离子水中，并使用磁力搅拌器进行剪切分散，磁力搅拌器的转速设置为100-300r/min；得到含活性成分的纳米复合分散液，将分散液进行溶剂挥发，得到含小黄姜活性成分的介孔SiO2分子巢，研磨粉碎、备用；
S4：将S1中的混制颗粒、S2中的抗拉伸晶体、S3中的含小黄姜活性成分的介孔SiO2分子巢、抗氧化剂0.3份和涤纶聚酯切片300份使用熔融纺丝方法进行纺丝、拉伸卷绕，制得含姜活性成分的涤纶大生物纤维；
S5：将S4中制得的含姜活性成分的涤纶大生物纤维放入到乙醇16份的乙醇溶液中进行浸泡，浸泡30-50min，取出自然晾干，制得消毒处理后的含姜活性成分的涤纶大生物纤维。
对实施例一至三制得的含姜活性成分的涤纶大生物纤维，对比常规的含姜活性成分的涤纶大生物纤维，实验数据如下表所示：
由上述表格可知，本发明提出的含姜活性成分的涤纶大生物纤维具有明显提高，且实施二为最佳实施例。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。
Claims (8)
1.含姜活性成分的涤纶大生物纤维，其特征在于，包括以下重量份的原料：涤纶聚酯切片100-300份、介孔SiO2纳米粉体10-20份、焦磷酸钠0.5-2份、季戊四醇0.3-1份、消光粉1-3份、直链烷基苯磺酸钠1-2份、烷基烯酮二聚体0.2-0.8份、富勒烯0.5-0.8份、抗氧化剂0.1-0.3份、聚乙烯胺0.2-0.5份、聚氯乙烯1-2份、聚丙烯1-3份、聚酰胺1-2份、玉米预糊化淀粉0.7-1份、瓜尔胶0.2-0.5份、乙醇8-16份、姜活性成分1-3份、分散剂1-3份。
2.根据权利要求1所述的含姜活性成分的涤纶大生物纤维，其特征在于，包括以下重量份的原料：涤纶聚酯切片100份、介孔SiO2纳米粉体10份、焦磷酸钠0.5份、季戊四醇0.3份、消光粉1份、直链烷基苯磺酸钠1份、烷基烯酮二聚体0.2份、富勒烯0.5份、抗氧化剂0.1份、聚乙烯胺0.2份、聚氯乙烯1份、聚丙烯1份、聚酰胺1份、玉米预糊化淀粉0.7份、瓜尔胶0.2份、乙醇8份、姜活性成分1份、分散剂1份。
3.根据权利要求1所述的含姜活性成分的涤纶大生物纤维，其特征在于，包括以下重量份的原料：涤纶聚酯切片200份、介孔SiO2纳米粉体25份、焦磷酸钠1份、季戊四醇0.8份、消光粉2份、直链烷基苯磺酸钠1.5份、烷基烯酮二聚体0.6份、富勒烯0.6份、抗氧化剂0.2份、聚乙烯胺0.3份、聚氯乙烯1.5份、聚丙烯2份、聚酰胺1.5份、玉米预糊化淀粉0.9份、瓜尔胶0.3份、乙醇12份、姜活性成分2份、分散剂2份。
4.根据权利要求1所述的含姜活性成分的涤纶大生物纤维，其特征在于，包括以下重量份的原料：涤纶聚酯切片300份、介孔SiO2纳米粉体20份、焦磷酸钠2份、季戊四醇1份、消光粉3份、直链烷基苯磺酸钠2份、烷基烯酮二聚体0.8份、富勒烯0.8份、抗氧化剂0.3份、聚乙烯胺0.5份、聚氯乙烯2份、聚丙烯3份、聚酰胺2份、玉米预糊化淀粉1份、瓜尔胶0.5份、乙醇16份、姜活性成分3份、分散剂3份。
5.根据权利要求1所述的含姜活性成分的涤纶大生物纤维，其特征在于，所述消光粉的型号为OK52。
6.根据权利要求1所述的含姜活性成分的涤纶大生物纤维，其特征在于，所述姜活性成分包括姜精油、姜辣素、生姜蛋白酶和二苯基庚烷类物质，其中姜辣素包含姜烯酚类、姜二醇类、姜酚类、姜二酮类、姜醇类、姜酮类和副姜油酮类。
7.根据权利要求1所述的含姜活性成分的涤纶大生物纤维，其特征在于，所述聚乙烯胺为硅烷偶联剂。
8.含姜活性成分的涤纶大生物纤维的制备方法，其特征在于，包括以下步骤：
S1：取焦磷酸钠0.5-2份、季戊四醇0.3-1份、消光粉1-3份、直链烷基苯磺酸钠1-2份、烷基烯酮二聚体0.2-0.8份和富勒烯0.5-0.8份放置到搅拌箱内，进行搅拌混合，搅拌混合均匀后，取出放置在研磨机内进行研磨，研磨出粒径为6-8μm的粒子，得到混制颗粒；
S2：取聚乙烯胺0.2-0.5份、聚氯乙烯1-2份、聚丙烯1-3份、聚酰胺1-2份、玉米预糊化淀粉0.7-1份和瓜尔胶0.2-0.5份放置在搅拌箱内，同时加入适量的水，进行搅拌混合均匀，取出混合均匀的原料放入到加热罐中进行加热处理，加热至70-80℃，制得抗拉伸溶液，然后再浓缩操作，得到抗拉伸晶体，研磨粉碎、备用；
S3：将姜活性成分1-3份、介孔SiO2纳米粉体10-20份和分散剂1-3份依次加入到500mL去离子水中，并使用磁力搅拌器进行剪切分散，磁力搅拌器的转速设置为100-300r/min；得到含活性成分的纳米复合分散液，将分散液进行溶剂挥发，得到含小黄姜活性成分的介孔SiO2分子巢，研磨粉碎、备用；
S4：将S1中的混制颗粒、S2中的抗拉伸晶体、S3中的含小黄姜活性成分的介孔SiO2分子巢、抗氧化剂0.1-0.3份和涤纶聚酯切片100-300份使用熔融纺丝方法进行纺丝、拉伸卷绕，制得含姜活性成分的涤纶大生物纤维；
S5：将S4中制得的含姜活性成分的涤纶大生物纤维放入到8-16份的乙醇溶液中进行浸泡，浸泡30-50min，取出自然晾干，制得消毒处理后的含姜活性成分的涤纶大生物纤维。