CN113598185A - 一种植物伤口涂补剂及其制备方法 - Google Patents
一种植物伤口涂补剂及其制备方法 Download PDFInfo
- Publication number
- CN113598185A CN113598185A CN202110693855.7A CN202110693855A CN113598185A CN 113598185 A CN113598185 A CN 113598185A CN 202110693855 A CN202110693855 A CN 202110693855A CN 113598185 A CN113598185 A CN 113598185A
- Authority
- CN
- China
- Prior art keywords
- coating agent
- stock solution
- deionized water
- guaiacol
- hydroxyquinoline
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种植物伤口涂补剂及其制备方法，原料组分包括：双(8‑羟基喹啉)锌、愈创木酚、丙烯酸树脂、表面活性剂、稳定剂、去离子水。制备步骤：S1、将去离子水加热至60‑100℃，将(8‑羟基喹啉)锌、愈创木酚、稳定剂加入至去离子水中并混合搅拌至各组分完全溶解制得涂补剂的原液；S2、将丙烯酸树脂徐徐加入S1步骤制备的原液中，并在55‑60℃温度范围内搅拌30‑40分钟；S3、加热S2步骤制备的原液至65‑70℃，向其中依次加入表面活性剂和胶悬粉；S4、停止加热并以60转/分钟继续搅拌至液体冷却后灌装。涂补剂中的防病促长促愈合的生物活性物质以分子状态迅速被植物伤口所吸收，迅速在植物伤口形成一层防风雨防病菌入侵的生物膜，促使植物伤口无腐无病迅速愈合。
Description
技术领域
本发明涉及农业化学技术领域，特别是一种植物伤口涂补剂及其制备方法。
背景技术
随着国内园林绿化面积不断地增大，树木移栽和园林养护过程中对植物伤口涂补剂的需求量越来越 大。但是大部分地区仍然是果农或者园林绿化养护工人按照传统的办法采用石硫合剂和波尔多液加上动植 物油和杀虫杀菌剂农药自己制作涂摸剂，这一类涂补剂产品技术落后，没有标准规范，制作麻烦；且其中 多含有：胂、硫、铜以及杀虫杀菌剂农药，使用起来效果既不稳定又有污染环境之隐患，树木伤口容易出 现腐烂死棵的问题。市场亟需一种标准规范、绿色环保、效果稳定、经济适用的植物伤口涂补剂。
发明内容
本发明的目的在于克服现有技术的缺点，提供一种园林专用植物伤口涂补剂及其制备方法，解决现有 的涂补剂效果既不稳定又有污染环境，树木伤口容易出现腐烂死棵的问题。
本发明的目的通过以下技术方案来实现：
一种植物伤口涂补剂，原料组分包括：双(8-羟基喹啉)锌、愈创木酚、丙烯酸树脂、表面活性剂、稳 定剂、去离子水。
涂补剂作用在植物伤口愈合处的反应原理如下：
其中H2O保护环境自然水分和植物生命活动所分泌的水；在植物伤口的涂补剂薄膜表层会自然形成 有机酸性水溶液环境，这种环境中会离解析出8-羟基喹啉+Zn++愈创木酚，8-羟基喹啉+Zn+具有防腐、 抗植物病菌侵染功能，Zn++愈创木酚等会被植物伤口处的皮层切口所吸收，这些物质会促使新的植物愈 伤组织的生成，进而促进植物愈伤组织形成，加速植物伤口的愈合速度。
涂补剂具有良好的附着力，不受雨水与日光损伤，同时由于表面活性剂在与双(8-羟基喹啉)锌、愈 创木酚、丙烯酸树脂反应的同时还与基体反应，形成胶体化结合，其所含双(8-羟基喹啉)锌、愈创木酚、 丙烯酸树脂胶体物在涂层中形成了无数的微笑网络区域，减少了涂层与基体之间的热膨胀系数之差，降低 了涂层硬化时的收缩率和涂层内部的应力，抑制了涂层的龟裂、脱落，提高了涂层的黏结力和抗介质渗透 能力，补充植物伤口愈合所是需要的愈创木酚和锌、丙烯酸树脂元素，从而提高了涂层的防病、防腐、促 伤口愈合性能。
表面活性剂包括有脂肪醇聚氧乙烯醚、餐厨再生油、菜籽油、烷基苯磺酸钙、有机硅渗透剂、花生油、 烷基醚羧酸盐、有机硅油、椰子油、烷醇酰胺聚氧乙烯醚、脂肪酸酯聚氧乙烯醚中的一种或多种。
进一步的技术方案是：所述原料还包括有胶悬粉。
进一步的技术方案是：按质量百分数计，所述原料包括双(8-羟基喹啉)锌0.15-6％、愈创木酚0.15-6％、 丙烯酸树脂0.5-20％、表面活性剂2-15％、稳定剂0.3-2％、胶悬粉0.5-3％、余量为去离子水。
进一步的技术方案是：所述稳定剂包括黄原胶粉、苯甲酸钠。
进一步的技术方案是：所述胶悬粉为低温型有机硅树脂胶黏剂。
一种植物伤口涂补剂的制备方法，其特征在于：包括以下步骤：
S1、制备涂补剂原液：将去离子水加热至60-100℃，将(8-羟基喹啉)锌、愈创木酚、稳定剂加入至去离子 水中并混合搅拌至各组分完全溶解，并保持60℃恒温静置2-3小时制得涂补剂的原液；
S2、将丙烯酸树脂徐徐加入S1步骤制备的原液中，并以100转/分钟的速度进行加热搅拌，并在55-60℃ 温度范围内搅拌30-40分钟，调整pH8-10，使原液呈胶黏状，pH值的调整可通过加入食碱进行调整，可 以理解的是还可以加入其它碱性物质进行调整，以保证胶悬状的稳定；
S3、加热S2步骤制备的原液至65-70℃，并向其中依次加入表面活性剂和胶悬粉，加料完成后以60转/分 钟的速度继续搅拌2-3小时；
S4、停止加热并以60转/分钟继续搅拌至液体冷却后灌装。
进一步的技术方案是：按质量百分数计，所述原料包括：双(8-羟基喹啉)锌0.15-6％、愈创木酚0.15-6％、 丙烯酸树脂0.5-20％、表面活性剂2-15％、稳定剂0.3-2％、胶悬粉0.5-3％、余量为去离子水。
进一步的技术方案是：所述S3步骤中，在表面活性剂和胶悬粉加入过程中，控制转速为200转/分钟。
本发明具有以下优点：
使防病促长促愈合的生物活性物质以分子状态迅速被植物伤口所吸收，成膜物质迅速在植物伤口形成 一层防风雨防病菌入侵的生物膜，达到促使植物伤口无腐无病迅速愈合。该涂补剂绿色环保，操作安全， 处理简单，节省成本。
具体实施方式
为使本发明实施方式的目的、技术方案和优点更加清楚，下面将结合本发明实施方式，对本发明实 施方式中的技术方案进行清楚、完整地描述，显然，所描述的实施方式是本发明一部分实施方式，而不 是全部的实施方式。
因此，以下对本发明的实施方式的详细描述并非旨在限制要求保护的本发明的范围，而是仅仅表示本 发明的选定实施方式。基于本发明中的实施方式，本领域普通技术人员在没有作出创造性劳动前提下所获 得的所有其他实施方式，都属于本发明保护的范围。
需要说明的是，在不冲突的情况下，本发明中的实施方式及实施方式中的特征可以相互组合。
实施例1
一种植物伤口涂补剂，原料组分包括：双(8-羟基喹啉)锌、愈创木酚、丙烯酸树脂、表面活性剂、稳 定剂、去离子水、胶悬粉，所述稳定剂为黄原胶粉、苯甲酸钠，所述胶悬粉为低温型有机硅树脂胶黏剂。 按质量百分数计，所述原料包括双(8-羟基喹啉)锌0.15％、愈创木酚0.15％、丙烯酸树脂0.5％、脂肪醇聚 氧乙烯醚2％、黄原胶粉0.2％、苯甲酸钠0.1％、胶悬粉3％、余量为去离子水。
一种植物伤口涂补剂的制备方法，其特征在于：包括以下步骤：
S1、制备涂补剂原液：将去离子水加热至60℃，将(8-羟基喹啉)锌0.15％、愈创木酚0.15％、黄原胶粉0.2％、 苯甲酸钠0.1％，加入至去离子水中并混合搅拌至各组分完全溶解，并保持60℃恒温静置2小时制得涂补 剂的原液；
S2、将丙烯酸树脂0.5％徐徐加入S1步骤制备的原液中，并以100转/分钟的速度进行加热搅拌，并在55℃ 温度条件下搅拌35分钟，控制pH值为8，使原液呈胶黏状；
S3、加热S2步骤制备的原液至65℃，并向其中依次加入脂肪醇聚氧乙烯醚2％和胶悬粉3％，加料完成后 以60转/分钟的速度继续搅拌2.5小时；
S4、停止加热并以60转/分钟继续搅拌至液体冷却后灌装。
所述S3步骤中，在脂肪醇聚氧乙烯醚和胶悬粉加入过程中，控制转速为200转/分钟，所述双(8-羟基 喹啉)锌与愈创木酚以1:1的比例添加。
实施例2
一种植物伤口涂补剂，原料组分包括：双(8-羟基喹啉)锌、愈创木酚、丙烯酸树脂、表面活性剂、稳 定剂、去离子水、胶悬粉，所述稳定剂为黄原胶粉、苯甲酸钠，所述胶悬粉为低温型有机硅树脂胶黏剂。 按质量百分数计，所述原料包括双(8-羟基喹啉)锌1.5％、愈创木酚1.5％、丙烯酸树脂5％、脂肪醇聚氧乙 烯醚6％、餐厨再生油4％、黄原胶粉1％、苯甲酸钠0.3％、胶悬粉2.5％、余量为去离子水。
一种植物伤口涂补剂的制备方法，其特征在于：包括以下步骤：
S1、制备涂补剂原液：将去离子水加热至70℃，将(8-羟基喹啉)锌1.5％、愈创木酚1.5％、黄原胶粉1％、 苯甲酸钠0.3％，加入至去离子水中并混合搅拌至各组分完全溶解，并保持60℃恒温静置2.5小时制得涂补 剂的原液；
S2、将丙烯酸树脂5％徐徐加入S1步骤制备的原液中，并以100转/分钟的速度进行加热搅拌，并在58℃ 温度条件下搅拌30分钟，控制pH值为10，使原液呈胶黏状；
S3、加热S2步骤制备的原液至70℃，并向其中依次加入脂肪醇聚氧乙烯醚6％、餐厨再生油4％和胶悬粉 2.5％，加料完成后以60转/分钟的速度继续搅拌2小时；
S4、停止加热并以60转/分钟继续搅拌至液体冷却后灌装。
所述S3步骤中，在脂肪醇聚氧乙烯醚、餐厨再生油和胶悬粉加入过程中，控制转速为200转/分钟， 所述双(8-羟基喹啉)锌与愈创木酚以1:1的比例添加。
实施例3
一种植物伤口涂补剂，原料组分包括：双(8-羟基喹啉)锌、愈创木酚、丙烯酸树脂、表面活性剂、稳 定剂、去离子水、胶悬粉，所述稳定剂为黄原胶粉、苯甲酸钠，所述胶悬粉为低温型有机硅树脂胶黏剂。 按质量百分数计，所述原料包括双(8-羟基喹啉)锌3％、愈创木酚3％、丙烯酸树脂10％、脂肪醇聚氧乙烯 醚4％、菜籽油5％、烷基苯磺酸钙4％、黄原胶粉2％、苯甲酸钠0.5％、胶悬粉2％、余量为去离子水。
一种植物伤口涂补剂的制备方法，其特征在于：包括以下步骤：
S1、制备涂补剂原液：将去离子水加热至90℃，将(8-羟基喹啉)锌3％、愈创木酚3％、黄原胶粉2％、苯 甲酸钠0.5％，加入至去离子水中并混合搅拌至各组分完全溶解，并保持60℃恒温静置2.5小时制得涂补剂 的原液；
S2、将丙烯酸树脂10％徐徐加入S1步骤制备的原液中，并以100转/分钟的速度进行加热搅拌，并在60℃ 温度条件下搅拌30分钟，控制pH值为10，使原液呈胶黏状；
S3、加热S2步骤制备的原液至70℃，并向其中依次加入脂肪醇聚氧乙烯醚4％、菜籽油5％、烷基苯磺酸 钙4％和胶悬粉2％，加料完成后以60转/分钟的速度继续搅拌2小时；
S4、停止加热并以60转/分钟继续搅拌至液体冷却后灌装。
所述S3步骤中，在脂肪醇聚氧乙烯醚、菜籽油、烷基苯磺酸钙和胶悬粉加入过程中，控制转速为200 转/分钟，所述双(8-羟基喹啉)锌与愈创木酚以1:1的比例添加。
实施例4
一种植物伤口涂补剂，原料组分包括：双(8-羟基喹啉)锌、愈创木酚、丙烯酸树脂、表面活性剂、稳 定剂、去离子水、胶悬粉，所述稳定剂为黄原胶粉、苯甲酸钠，所述胶悬粉为低温型有机硅树脂胶黏剂。 按质量百分数计，所述原料包括双(8-羟基喹啉)锌6％、愈创木酚6％、丙烯酸树脂20％、菜籽油3％、有机 硅油3％、烷基苯磺酸钙4％、黄原胶粉2％、苯甲酸钠0.3％、胶悬粉1.5％、余量为去离子水。
一种植物伤口涂补剂的制备方法，其特征在于：包括以下步骤：
S1、制备涂补剂原液：将去离子水加热至95℃，将(8-羟基喹啉)锌6％、愈创木酚6％、黄原胶粉2％、苯 甲酸钠0.3％，加入至去离子水中并混合搅拌至各组分完全溶解，并保持60℃恒温静置3小时制得涂补剂 的原液；
S2、将丙烯酸树脂20％徐徐加入S1步骤制备的原液中，并以100转/分钟的速度进行加热搅拌，并在58℃ 温度条件下搅拌40分钟，控制pH值为9，使原液呈胶黏状；
S3、加热S2步骤制备的原液至68℃，并向其中依次加入菜籽油3％、有机硅油3％、烷基苯磺酸钙4％和 胶悬粉1.5％，加料完成后以60转/分钟的速度继续搅拌3小时；
S4、停止加热并以60转/分钟继续搅拌至液体冷却后灌装。
所述S3步骤中，在菜籽油、有机硅油、烷基苯磺酸钙和胶悬粉加入过程中，控制转速为200转/分钟， 所述双(8-羟基喹啉)锌与愈创木酚以1:1的比例添加。
实施例5
一种植物伤口涂补剂，原料组分包括：双(8-羟基喹啉)锌、愈创木酚、丙烯酸树脂、表面活性剂、稳 定剂、去离子水、胶悬粉，所述稳定剂为黄原胶粉、苯甲酸钠，所述胶悬粉为低温型有机硅树脂胶黏剂。 按质量百分数计，所述原料包括双(8-羟基喹啉)锌0.15％、愈创木酚0.15％、丙烯酸树脂0.5％、花生油5％、 脂肪醇聚氧乙烯醚5％、烷基羧酸盐4％、黄原胶粉1％、苯甲酸钠0.3％、胶悬粉1.5％、余量为去离子水。
一种植物伤口涂补剂的制备方法，其特征在于：包括以下步骤：
S1、制备涂补剂原液：将去离子水加热至65℃，将(8-羟基喹啉)锌0.15％、愈创木酚0.15％、黄原胶粉1％、 苯甲酸钠0.3％，加入至去离子水中并混合搅拌至各组分完全溶解，并保持60℃恒温静置2小时制得涂补 剂的原液；
S2、将丙烯酸树脂0.5％徐徐加入S1步骤制备的原液中，并以100转/分钟的速度进行加热搅拌，并在56℃ 温度条件下搅拌30分钟，控制pH值为9，使原液呈胶黏状；
S3、加热S2步骤制备的原液至65℃，并向其中依次加入花生油5％、脂肪醇聚氧乙烯醚5％、烷基羧酸盐 4％和胶悬粉1.5％，加料完成后以60转/分钟的速度继续搅拌2小时；
S4、停止加热并以60转/分钟继续搅拌至液体冷却后灌装。
所述S3步骤中，在花生油、脂肪醇聚氧乙烯醚5烷基羧酸盐和胶悬粉加入过程中，控制转速为200 转/分钟，所述双(8-羟基喹啉)锌与愈创木酚以1:1的比例添加。
实施例6
一种植物伤口涂补剂，原料组分包括：双(8-羟基喹啉)锌、愈创木酚、丙烯酸树脂、表面活性剂、稳 定剂、去离子水、胶悬粉，所述稳定剂为黄原胶粉、苯甲酸钠，所述胶悬粉为低温型有机硅树脂胶黏剂。 按质量百分数计，所述原料包括双(8-羟基喹啉)锌1.5％、愈创木酚1.5％、丙烯酸树脂5％、有机硅油3％、 烷基苯磺酸钙4％、黄原胶粉1％、苯甲酸钠0.3％、胶悬粉0.5％、余量为去离子水。
一种植物伤口涂补剂的制备方法，其特征在于：包括以下步骤：
S1、制备涂补剂原液：将去离子水加热至75℃，将(8-羟基喹啉)锌1.5％、愈创木酚1.5％、黄原胶粉1％、 苯甲酸钠0.3％，加入至去离子水中并混合搅拌至各组分完全溶解，并保持60℃恒温静置2.5小时制得涂补 剂的原液；
S2、将丙烯酸树脂5％徐徐加入S1步骤制备的原液中，并以100转/分钟的速度进行加热搅拌，并在58℃ 温度条件下搅拌35分钟，控制pH值为10，使原液呈胶黏状；
S3、加热S2步骤制备的原液至66℃，并向其中依次加入有机硅油3％、烷基苯磺酸钙4％和胶悬粉0.5％， 加料完成后以60转/分钟的速度继续搅拌2小时；
S4、停止加热并以60转/分钟继续搅拌至液体冷却后灌装。
所述S3步骤中，在有机硅油、烷基苯磺酸钙和胶悬粉加入过程中，控制转速为200转/分钟，所述双 (8-羟基喹啉)锌与愈创木酚以1:1的比例添加。
实施例7
一种植物伤口涂补剂，原料组分包括：双(8-羟基喹啉)锌、愈创木酚、丙烯酸树脂、表面活性剂、稳 定剂、去离子水、胶悬粉，所述稳定剂为黄原胶粉、苯甲酸钠，所述胶悬粉为低温型有机硅树脂胶黏剂。 按质量百分数计，所述原料包括双(8-羟基喹啉)锌3％、愈创木酚3％、丙烯酸树脂10％、椰子油5％、烷醇 酰胺聚氧乙烯醚4％、烷基苯磺酸钙3％、黄原胶粉1％、苯甲酸钠0.3％、胶悬粉1.5％、余量为去离子水。
一种植物伤口涂补剂的制备方法，其特征在于：包括以下步骤：
S1、制备涂补剂原液：将去离子水加热至65℃，将(8-羟基喹啉)锌3％、愈创木酚3％、黄原胶粉1％、苯 甲酸钠0.3％，加入至去离子水中并混合搅拌至各组分完全溶解，并保持60℃恒温静置2.8制得涂补剂的原 液；
S2、将丙烯酸树脂10％徐徐加入S1步骤制备的原液中，并以100转/分钟的速度进行加热搅拌，并在55℃ 温度条件下搅拌38分钟，控制pH值为10，使原液呈胶黏状；
S3、加热S2步骤制备的原液至65℃，并向其中依次加入椰子油5％、烷醇酰胺聚氧乙烯醚4％、烷基苯磺 酸钙3％和胶悬粉1.5％，加料完成后以60转/分钟的速度继续搅拌2.5小时；
S4、停止加热并以60转/分钟继续搅拌至液体冷却后灌装。
所述S3步骤中，在椰子油、烷醇酰胺聚氧乙烯醚、烷基苯磺酸钙和胶悬粉加入过程中，控制转速为 200转/分钟，所述双(8-羟基喹啉)锌与愈创木酚以1:1的比例添加。
实施例8
一种植物伤口涂补剂，原料组分包括：双(8-羟基喹啉)锌、愈创木酚、丙烯酸树脂、表面活性剂、稳 定剂、去离子水、胶悬粉，所述稳定剂为黄原胶粉、苯甲酸钠，所述胶悬粉为低温型有机硅树脂胶黏剂。 按质量百分数计，所述原料包括双(8-羟基喹啉)锌6％、愈创木酚6％、丙烯酸树脂20％、花生油6％、表面 活性剂酯聚氧乙烯醚5％、烷基苯磺酸钙4％、黄原胶粉2％、苯甲酸钠0.3％、胶悬粉0.8％、余量为去离 子水。
一种植物伤口涂补剂的制备方法，其特征在于：包括以下步骤：
S1、制备涂补剂原液：将去离子水加热至80℃，将(8-羟基喹啉)锌6％、愈创木酚6％、黄原胶粉2％、苯 甲酸钠0.3％，加入至去离子水中并混合搅拌至各组分完全溶解，并保持60℃恒温静置3制得涂补剂的原 液；
S2、将丙烯酸树脂20％徐徐加入S1步骤制备的原液中，并以100转/分钟的速度进行加热搅拌，并在60℃ 温度条件下搅拌40分钟，控制pH值为9，使原液呈胶黏状；
S3、加热S2步骤制备的原液至68℃，并向其中依次加入花生油6％、脂肪酸酯聚氧乙烯醚5％、烷基苯磺 酸钙4％和胶悬粉0.8％，加料完成后以60转/分钟的速度继续搅拌2.8小时；
S4、停止加热并以60转/分钟继续搅拌至液体冷却后灌装。
所述S3步骤中，在花生油、脂肪酸酯聚氧乙烯醚、烷基苯磺酸钙和胶悬粉加入过程中，控制转速为 200转/分钟，所述双(8-羟基喹啉)锌与愈创木酚以1:1的比例添加。
植物试验结果如下
植物伤口涂补剂对移栽大树新伤口防腐、防裂田间药效试验结果统计表
注：郑州悬铃木移栽树伤口防腐试验，2015年选择在河南农业大学龙子湖新校区；
高碑店国槐移栽树伤口防腐试验，2017年选择在高碑店市燕赵公园；
通许银杏树移栽树伤口防腐试验，2018年选择在神润生物科技有限公司生产试验基地；
张家口白蜡移栽树伤口防腐试验，2018年选择在张家口市绿化处办公小区。
通过上述试验可以看出本申请的涂补剂能能迅速被植物伤口所吸收，并有效促进新的植物愈伤组织的 形成，加速植物伤口的愈合速度，同时具有防腐防裂的功能，而且，本申请的涂补剂由于未添加强酸强碱 性物质，不会对植物伤口造成额外损伤，使用效果稳定又不对环境造成污染，安全环保。
尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各 实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换,凡在本发明的精神和原则之 内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (8)
1.一种植物伤口涂补剂，其特征在于：原料组分包括：双(8-羟基喹啉)锌、愈创木酚、丙烯酸树脂、表面活性剂、稳定剂、去离子水。
2.根据权利要求1所述的一种植物伤口涂补剂，其特征在于：所述原料还包括有胶悬粉。
3.根据权利要求2所述的一种植物伤口涂补剂，其特征在于：按质量百分数计，所述原料包括双(8-羟基喹啉)锌0.15-6％、愈创木酚0.15-6％、丙烯酸树脂0.5-20％、表面活性剂2-15％、稳定剂0.3-2％、胶悬粉0.5-3％、余量为去离子水。
4.根据权利要求1或2所述的一种植物伤口涂补剂，其特征在于：所述稳定剂包括黄原胶粉、苯甲酸钠。
5.根据权利要求2所述的一种植物伤口涂补剂，其特征在于：所述胶悬粉为低温型有机硅树脂胶黏剂。
6.一种植物伤口涂补剂的制备方法，其特征在于：包括以下步骤：
S1、制备涂补剂原液：将去离子水加热至60-100℃，将(8-羟基喹啉)锌、愈创木酚、稳定剂加入至去离子水中并混合搅拌至各组分完全溶解，并保持60℃恒温静置2-3小时制得涂补剂的原液；
S2、将丙烯酸树脂徐徐加入S1步骤制备的原液中，并以100转/分钟的速度进行加热搅拌，并在55-60℃温度范围内搅拌30-40分钟，调整pH8-10，使原液呈胶黏状；调整PH8-10
S3、加热S2步骤制备的原液至65-70℃，并向其中依次加入表面活性剂和胶悬粉，加料完成后以60转/分钟的速度继续搅拌2-3小时；
S4、停止加热并以60转/分钟继续搅拌至液体冷却后灌装。
7.根据权利要6所述的一种植物伤口涂补剂的制备方法，其特征在于：按质量百分数计，所述原料包括：双(8-羟基喹啉)锌0.15-6％、愈创木酚0.15-6％、丙烯酸树脂0.5-20％、表面活性剂2-15％、稳定剂0.3-2％、胶悬粉0.5-3％、余量为去离子水。
8.根据权利要求6所述的一种植物伤口涂补剂的制备方法，其特征在于：所述S3步骤中，在表面活性剂和胶悬粉加入过程中，控制转速为200转/分钟。