CN113585574B - 一种楼地面保温隔声板及其加工方法 - Google Patents
一种楼地面保温隔声板及其加工方法 Download PDFInfo
- Publication number
- CN113585574B CN113585574B CN202111001575.1A CN202111001575A CN113585574B CN 113585574 B CN113585574 B CN 113585574B CN 202111001575 A CN202111001575 A CN 202111001575A CN 113585574 B CN113585574 B CN 113585574B
- Authority
- CN
- China
- Prior art keywords
- parts
- cement
- layer
- water
- sound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种UHPC饰面的楼地面保温隔声板,包括一组板体,板体从上至下依次包括UHPC饰面层、弹性缓冲层、增强型保温隔声层;本发明还公开了一种UHPC饰面的楼地面保温隔声板的加工方法。通过橡胶粉及高性能纳米铝镁质粉末隔声组份的应用,解决了无机材料隔声性能较差的问题;同时板体可以在工厂预制,可减少噪声、粉尘和建筑垃圾等污染,现场采用轻质胶泥进行找平和粘贴,装配式施工,省去饰面材料的铺贴,安装速度快,且可以最大限度保证产品质量和性能;本发明省去了传统40mm钢筋细石混凝土;本发明三层主材全部采用水泥基材料,三层结构协同作用,实现保温隔声装饰一体的功能,整个板体结实平整,同时实现绿色环保、防火性能好、整体性好的效果。
Description
技术领域
本发明涉及一种地面保温隔声板,特别是涉及一种建筑楼地面用保温隔声板及其加工方法,属于建材领域。
背景技术
随着装配式以及绿色建筑行业的快速发展,为突出高效、智能、绿色、环保、节能等现代建筑的优势,国家从政策角度提出高品质高质量的发展要求,不仅关注外墙和内隔墙的保温隔声,而随着生活质量的提高,人们对居住条件的要求也越来越高,人们关注的角度逐步转移到分户楼板的保温隔声性能上来。目前国内建筑楼地面保温隔声常见做法包括两种:一种是现场作业的方式,第一种结构是在混凝土楼板上铺设5mm隔音垫,然后在隔音垫上铺设10mm高分子保温层,再铺设40mm的钢筋细石混凝土,再做饰面层;第二种结构是在混凝土楼板上铺设10mm隔音垫,在隔音垫上直接铺设40mm钢筋细石混凝土,再做饰面层;另外一种是预制装配式板材现场干法作业的方式,具体包括增强型改性水泥基泡沫保温隔声板以及其他集成板材。但是无论哪一种方式最后都需要在现场做饰面层,饰面层大部分是人工现场湿作业铺贴瓷砖、天然石材、人造板材等各种块材面层,施工质量得不到保证,施工厚度大,空鼓、开裂现象严重,质量监管困难,业主投诉维权问题多,为后期维修、验收、交房带来了很多麻烦,且施工工序较多、周期长,现场污染严重。
因此本领域技术人员致力于开发一种不需要现场铺贴饰面层的绿色环保、安装方便的预制装配式建筑楼地面保温隔声装饰一体化板材。
发明内容
有鉴于现有技术的上述缺陷,本发明所要解决的技术问题是提供一种预制装配式建筑楼地面保温隔声装饰一体化板材,由无机材料制备的经过工厂批量预制和表面处理的集保温、隔声及装饰一体的新型功能地面板材,运至现场直接铺贴即可。
为实现上述目的,本发明提供了 一种楼地面保温隔声板,包括一组板体,所述板体从上至下依次包括饰面层、弹性缓冲层和保温隔声层。饰面层是起到装饰和保护作用,保持外观效果的逼真、永久光泽和耐久性,提高防滑耐磨性,同时增加硬度、密实度和抗污性,防止污渍影响外观效果。弹性缓冲层设置在保温隔声层上主要起到承重和缓冲的作用,同时为装饰层提供一个稳定坚实的底座,应具有较高的承载能力和抗弯能力的同时具备一定的缓冲和隔声作用,是起抗冲击、隔声增强作用的半刚性的结构层。
较佳的,饰面层为超高性能混凝土UHPC(Ultra-High Performance Concrete),所述饰面层的材料组分按质量百分百比计,包括水泥24%-32%、硅灰3%-6%、石粉8%-15%、石屑40%-45%、无机颜料0-1%、水5%-10%、外加剂0.2%-0.8%。饰面层采用紧密堆积原理,加入无机颜料,加入包括硅灰和偏高岭土的活性微粉,增加装饰层的耐磨性和装饰性。饰面层的厚度宜为3~5mm。
较佳的,所述外加剂包括消泡剂、增稠剂、流平剂的一种或几种。
较佳的,所述弹性缓冲层按重量份数计,包括水泥580-630份、粉煤灰120-150份、石英砂750-800份、引气剂0.15-0.2份、废橡胶10-15份、减水剂3-5份以及水180-240份。弹性缓冲层的厚度宜为10或20mm,不做地暖采用10mm厚,做地暖则采用20mm以便预留水暖管。
为解决材料兼容性和半刚性的技术问题,所述弹性缓冲层按重量份数计,还包括木屑20-30份、改性丙烯酸酯弹性乳液22-27份和高性能纳米铝镁质纤维5-10份。
较佳的,所述保温隔声层由上纤维增强层、水泥基泡沫芯材层和下纤维增强层组成,作为保温隔声板的核心层,起到保温隔声的作用。保温隔声层厚度为23mm较佳。
较佳的,所述上纤维增强材料层和下纤维增强材料层按重量份数计,包括水泥300-350份、重钙粉100-150份、石英砂500-550份、胶粉15-20份,保水组份2-5份以及水180-220份。
所述水泥基泡沫芯材按重量份数计,包括水泥150-200份、、粉煤灰10-15份、双氧水18-23份、硬脂酸钙1.5-2份、憎水组分1-2份、保水组分0.2-0.4份、聚丙烯纤维1-2份以及80-120份水。
进一步提高材料的隔声性能和保温性能,所述水泥为硅酸盐水泥;所述水泥基泡沫芯材按重量份数计,还包括橡胶粉5-10份、高性能纳米铝镁质粉末5-10份、二氧化硅气凝胶组分1-2份、硅微粉10-15份。
本发明还提供了一种楼地面保温隔声板的加工方法,包括以下步骤:
A、增强型保温隔声层制备:首先将水泥、硅微粉、粉煤灰、憎水组分、保水组分、橡胶粉、高性能纳米铝镁质粉末、二氧化硅气凝胶组分、聚丙烯纤维以及水拌和得到混合浆料A;再将双氧水、硬脂酸钙加入到浆料A中拌和得到混合浆料B,将混合浆料B快速倒入模具中发泡成型,硬化养护后得到水泥基泡沫芯材,切割成板材备用;然后在水泥基泡沫芯材上下表面铺贴一层纤维增强层;
B、饰面层制备:将水泥、硅灰、石粉、石屑、外加剂、颜料以及水拌和得到混合浆料,倒入模具中成型;
C、弹性缓冲层制备:将水泥、粉煤灰、石英砂、木屑、改性丙烯酸酯弹性乳液、引气剂、废橡胶、高性能纳米铝镁质纤维、减水剂以及水拌和得到混合浆料,浇筑于饰面层上,再将制备好的增强型保温隔声层压入弹性缓冲层浆料中。
较佳的,在步骤A中,在水泥基泡沫芯材上下表面铺贴纤维增强层的具体步骤为:在水泥基泡沫芯材上下表面先铺贴一层耐碱玻璃纤维网格布,再将水泥、重钙粉、石英砂、胶粉,保水组份以及水拌和并浇于铺贴好耐碱玻璃纤维网格布的水泥基泡沫芯材上并收面。
本发明的有益效果是:
1、本发明UHPC饰面的楼地面保温隔声板是在工厂预制,环保性强,可减少噪声、粉尘和建筑垃圾等污染,现场采用轻质胶泥进行找平和粘贴,装配式施工,省去饰面材料的铺贴,可大幅缩短建设周期,安装速度快,且可以最大限度保证产品质量和性能。
2、本发明通过橡胶粉及高性能纳米铝镁质粉末隔声组份的应用技术,能够解决无机材料隔声性能较差的技术问题。
3、本发明省去了传统中的40mm钢筋细石混凝土,相当于增加了精装房的净高,也大大节省了成本。
4、本发明符合国家倡导精装修交付及装配式建筑构件要求。
5、本发明避免了由于采用隔声垫、保温板时受力出现向下移动导致的保护层开裂现象,整个板体结实平整。
6、本发明三层主材全部采用水泥基材料,三层结构协同作用,实现保温隔声装饰一体的功能,同时实现绿色环保、防火性能好、整体性好的效果。
附图说明
图1是本发明UHPC饰面的楼地面保温隔声板一种具体实施方式的结构示意图;
图2是本发明UHPC饰面的楼地面保温隔声板一种具体实施方式的剖视结构示意图。
实施方式
下面结合附图和实施例对本发明作进一步说明:
如图1和图2所示,一种UHPC饰面的楼地面保温隔声板,包括一组板体,所述板体从上至下依次包括UHPC饰面层10,与UHPC饰面层10相连的弹性缓冲层20,与弹性缓冲层20相连的增强型保温隔声层30。所述增强型保温隔声层30,以废橡胶及高性能纳米铝镁质粉末作为隔声组份,以硅灰为活性粉末掺合料,以气凝胶粉末为保温隔热材料,和水泥作为胶凝剂混合经过化学发泡而制成的水泥基泡沫芯材,在水泥基泡沫芯材上下表面进行耐碱玻璃纤维增强处理进而制成增强型保温隔声层。所述UHPC饰面层10为超高性能混凝土或活性粉末混凝土,经过彩色粗细骨料以及无机颜料的加入并经过表面处理实现装饰效果。所述弹性缓冲层20,以木屑、橡胶颗粒以及高性能纳米铝镁质纤维为隔声材料,以聚氨酯改性丙烯酸酯弹性乳液为弹性改性材料,和水泥作为胶凝剂混合而制成的弹性缓冲层。所述UHPC饰面层10厚度为3~5mm。所述弹性缓冲层20为10mm或20mm。所述增强型保温隔声层30厚度23mm,其中水泥基泡沫芯材20mm,上下纤维增强层各1.5mm。所述板体侧面与墙体接触时,与墙体的接触侧面也可设有一竖向弹性缓冲层。所述板体侧面与墙角接触时,与墙角的接触的两个侧面也可设有一竖向弹性缓冲层。
UHPC饰面层材料组分如下:
类别 | 水泥 | 硅灰 | 石粉 | 石屑 | 无机颜料 | 水 | 外加剂 |
质量占比% | 30 | 5 | 10 | 45 | 0.6 | 10 | 0.5 |
规格 | PO525 | 硅含量90%以上 | 40-120目 | 5-20目 | 氧化铁类 | / | 以减水剂为主,包含有消泡剂、增稠剂、流平剂等 |
弹性缓冲层按重量份数计,水泥620份、粉煤灰130份、石英砂760份、木屑30份、改性丙烯酸酯弹性乳液24份、引气剂0.15份、废橡胶13份、高性能纳米铝镁质纤维6份、减水剂4份以及水185份。
上下纤维增强材料按重量份数计,水泥320份、重钙粉110份、石英砂550份、胶粉20份,保水组份4.5份以及水202份。
水泥基泡沫芯材按重量份数计,水泥195份、硅微粉15份、粉煤灰15份、双氧水20份、硬脂酸钙2份、憎水组分1.2份、保水组分0.3份、橡胶粉7份、高性能纳米铝镁质粉末8份、二氧化硅气凝胶组分1.6份、聚丙烯纤维1.8份以及114份水。
本发明所述UHPC饰面的楼地面保温隔声板优选的制备工艺如下:
A、增强型保温隔声层制备:首先将水泥、硅微粉、粉煤灰、憎水组分、保水组分、橡胶粉、高性能纳米铝镁质粉末、二氧化硅气凝胶组分、聚丙烯纤维以及水在转速不低于300r/min转速下均匀拌和5min以上得到混合浆料A,再将双氧水、硬脂酸钙加入到浆料A中,在转速不低于2000r/min转速下均匀拌和得到混合浆料B,将制备出的混合浆料B在快速倒入模具中发泡成型,待浆料发泡成型硬化养护后得到水泥基泡沫芯材,按照尺寸要求进行切割成板材备用。然后在水泥基泡沫芯材上下表面铺贴一层耐碱玻璃纤维网格布,将水泥、重钙粉、石英砂、胶粉,保水组份以及水在转速不低于1200r/min转速下均匀拌和得到混合浆料,再将混合浆料浇于铺贴好耐碱玻璃纤维网格布的水泥基泡沫芯材上并收面。
B、UHPC饰面层制备:为满足批量生产,按尺寸要求定制塑料模具,在模具内涂刷脱模剂放置在振动模台上,将水泥、硅灰、石粉、石屑、外加剂、颜料以及水在转速不低于300r/min转速下均匀拌和5min以上得到混合浆料,倒入模具中。
C、弹性缓冲层制备:将水泥、粉煤灰、石英砂、木屑、聚氨酯改性丙烯酸酯弹性乳液、引气剂、废橡胶、高性能纳米铝镁质纤维、减水剂以及水在转速不低于300r/min转速下均匀拌和5min以上得到混合浆料,浇筑于UHPC饰面层上,再将制备好的纤维增强水泥基保温隔声板压入浆料中约2mm深。
D、将制备好的UHPC饰面的楼地面保温隔声板的UHPC饰面层可通过水磨、抛丸、喷砂或酸洗等工艺进行表面处理,实现设计所需的表观效果。
以上较佳实施例测试结果如下:
项目 | 单位 | 测试结果 |
抗弯承载力(试件尺寸600*300*48mm) | N | 2620 |
抗冲击性 | -- | 无破碎或脱落 |
计权标准化撞击声压级 | dB | 59 |
干摩擦系数 | -- | 0.75 |
湿摩擦系数 | -- | 0.69 |
耐磨性 | mm3 | 83 |
以上详细描述了本发明的较佳具体实施例。应当理解,本领域的普通技术人员无需创造性劳动就可以根据本发明的构思作出诸多修改和变化。这些改进包括板体三层材料中各组份掺量和比例,以及板体各层材料的厚度等,也应视为本发明的保护范围。因此,凡本技术领域中技术人员依本发明的构思在现有技术的基础上通过逻辑分析、推理或者有限的实验可以得到的技术方案,皆应在由权利要求书所确定的保护范围内。
Claims (4)
1.一种楼地面保温隔声板,其特征是:包括一组板体,所述板体从上至下依次包括饰面层(10)、弹性缓冲层(20)和保温隔声层(30);
所述保温隔声层(30)由上纤维增强层、水泥基泡沫芯材层和下纤维增强层组成;
所述水泥基泡沫芯材按重量份数计,包括水泥150-200份、粉煤灰10-15份、双氧水18-23份、硬脂酸钙1.5-2份、憎水组分1-2份、保水组分0.2-0.4份、聚丙烯纤维1-2份以及80-120份水;
所述水泥为硅酸盐水泥;所述水泥基泡沫芯材按重量份数计,还包括橡胶粉5-10份、高性能纳米铝镁质粉末5-10份、二氧化硅气凝胶组分1-2份、硅微粉10-15份;
所述饰面层(10)的材料组分按质量百分百比计,包括水泥24%-32%、硅灰3%-6%、石粉8%-15%、石屑40%-45%、无机颜料0-1%、水5%-10%、外加剂0.2%-0.8%;
所述弹性缓冲层(20)按重量份数计,包括水泥580-630份、粉煤灰120-150份、石英砂750-800份、引气剂0.15-0.2份、废橡胶10-15份、减水剂3-5份以及水180-240份;
所述弹性缓冲层(20)按重量份数计,还包括木屑20-30份、改性丙烯酸酯弹性乳液22-27份和高性能纳米铝镁质纤维5-10份。
2.根据权利要求1所述的楼地面保温隔声板,其特征是:所述外加剂包括消泡剂、增稠剂、流平剂的一种或几种。
3.根据权利要求1所述的楼地面保温隔声板,其特征是:所述上纤维增强层和下纤维增强层包括铺贴于水泥基泡沫芯材层上下表面的耐碱玻璃纤维网格布,所述耐碱玻璃纤维网格布上浇混合料,所述混合料按重量份数计,包括水泥300-350份、重钙粉100-150份、石英砂500-550份、胶粉15-20份,保水组份2-5份以及水180-220份。
4.一种如权利要求1至3任一所述的楼地面保温隔声板的加工方法,其特征是:包括以下步骤:
A、增强型保温隔声层制备:首先将水泥、硅微粉、粉煤灰、憎水组分、保水组分、橡胶粉、高性能纳米铝镁质粉末、二氧化硅气凝胶组分、聚丙烯纤维以及水拌和得到混合浆料A;再将双氧水、硬脂酸钙加入到浆料A中拌和得到混合浆料B,将混合浆料B快速倒入模具中发泡成型,硬化养护后得到水泥基泡沫芯材,切割成板材备用;然后在水泥基泡沫芯材上下表面铺贴一层纤维增强层;
B、饰面层制备:将水泥、硅灰、石粉、石屑、外加剂、颜料以及水拌和得到混合浆料,倒入模具中成型;
C、弹性缓冲层制备:将水泥、粉煤灰、石英砂、木屑、改性丙烯酸酯弹性乳液、引气剂、废橡胶、高性能纳米铝镁质纤维、减水剂以及水拌和得到混合浆料,浇筑于饰面层上,再将制备好的增强型保温隔声层压入弹性缓冲层浆料中。