CN113563780A - Bluestone art paint and preparation method thereof - Google Patents
Bluestone art paint and preparation method thereof Download PDFInfo
- Publication number
- CN113563780A CN113563780A CN202110886875.6A CN202110886875A CN113563780A CN 113563780 A CN113563780 A CN 113563780A CN 202110886875 A CN202110886875 A CN 202110886875A CN 113563780 A CN113563780 A CN 113563780A
- Authority
- CN
- China
- Prior art keywords
- parts
- bluestone
- paint
- raw material
- art paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a bluestone art paint and a preparation method thereof, wherein the bluestone art paint comprises the following raw materials in parts by weight: 8-12 parts of natural bluestone, 10-12 parts of silica powder, 0.2-0.3 part of a film forming additive, 1-3 parts of a thickening agent, 0.8-1.2 parts of a pH regulator, 4-7 parts of talcum powder, 4-7 parts of a pure acrylic emulsion, 0.5-1.5 parts of a bactericide, 25-36 parts of water and 4-6 parts of ink powder. According to the invention, the silicon micropowder and the ink powder are introduced into the art paint, so that the proper fineness and dosage of the silicon micropowder and the ink powder are adjusted through research, and the proper auxiliary components and dosage are selected and matched through research to be combined with the existing raw materials, so that the art paint has better stereoscopic impression. The makeup art paint is non-toxic, green and environment-friendly, does not contain harmful substances such as formaldehyde and the like, has various colors and bright composite color, and other properties completely meet the national standard.
Description
Technical Field
The invention relates to the technical field of building coatings, in particular to a bluestone art paint and a preparation process thereof.
Background
The art paint originates from Europe, the advanced process is spread from Europe, and after entering the domestic market, the art paint is popular and advocated by people with novel decorative style and unusual decorative effect. The artistic coating is also called wallpaper paint, is an environment-friendly coating integrating the advantages of wallpaper and emulsion paint, can create different visual effects according to the will of a decorator, overcomes the defects of single color and no layering of the emulsion paint, and also avoids the defects of easy color change, edge warping, interface existence and the like of the wallpaper.
However, the existing art paint contains volatile toxic components such as formaldehyde, and the formaldehyde can cause serious damage to the health of people after being volatilized. On the other hand, the existing art paint is not bright in overall color, has no stereoscopic impression and is not bright in color.
Disclosure of Invention
The invention aims to solve the problems that the existing art paint contains toxic components such as formaldehyde and the like, and the art paint is not bright in color and has no three-dimensional sense, and provides a bluestone art paint and a preparation process thereof.
A bluestone art paint comprises the following raw materials in parts by weight: 8-12 parts of natural bluestone, 10-12 parts of silica powder, 0.2-0.3 part of a film forming additive, 1-3 parts of a thickening agent, 0.8-1.2 parts of a pH regulator, 4-7 parts of talcum powder, 4-7 parts of a pure acrylic emulsion, 0.5-1.5 parts of a bactericide, 25-36 parts of water and 4-6 parts of ink powder.
The film-forming assistant is any one of dipropylene glycol butyl ether or dipropylene glycol ethyl ether.
The mesh number of the silicon micro powder is 1200-1300 meshes.
The thickening agent is a mixture of cellulose and alkali swelling olefine acid with the ratio of 1: 1.
The mesh number of the talcum powder is 1000-1300 meshes.
The bactericide is an RS bactericide.
The art paint also comprises an inorganic pigment, wherein the weight part of the inorganic pigment is 1-3 parts.
A preparation method of a bluestone art paint comprises the following steps:
s1, weighing the raw materials in parts by weight.
S2: pouring natural bluestone, silica micropowder, talcum powder and powdered ink in the raw materials into a mixer, and carrying out primary mixing to obtain a mixed raw material A;
s3: pouring the mixed raw material A into a stirrer, adding water and pure acrylic emulsion, and mixing and dispersing for 6 minutes at the speed of 450-600 rpm to obtain a mixed raw material B
S4: adding a bactericide, a film-forming aid and a thickening agent into the mixed raw material B, and mixing and dispersing at 1500 rpm for 10 minutes to obtain a mixed raw material C;
s5: and adding a pH regulator into the mixed raw material C, regulating the pH, uniformly stirring, and discharging after the detection is qualified to obtain the bluestone artistic paint.
The invention has the beneficial effects that:
1. according to the invention, the silicon micropowder and the ink powder are introduced into the art paint, so that the proper fineness and dosage of the silicon micropowder and the ink powder are adjusted through research, and the proper auxiliary components and dosage are selected and matched through research to be combined with the existing raw materials, so that the art paint has better stereoscopic impression.
2. The makeup art paint is non-toxic, green and environment-friendly, does not contain harmful substances such as formaldehyde and the like, has various colors and bright composite color, and other properties completely meet the national standard.
Detailed Description
The embodiments of the present invention are described below with reference to specific embodiments, and other advantages and effects of the present invention will be easily understood by those skilled in the art from the disclosure of the present specification. The invention is capable of other and different embodiments and of being practiced or of being carried out in various ways, and its several details are capable of modification in various respects, all without departing from the spirit and scope of the present invention. It is to be noted that the features in the following embodiments and examples may be combined with each other without conflict.
It should be noted that the following embodiments are provided only for illustrating the basic concept of the present invention, and only show the components related to the present invention rather than the number, shape and size of the components in practical implementation, and the type, number and ratio of the components in practical implementation can be changed arbitrarily, and the layout of the components may be more complicated.
Example 1:
a bluestone art paint comprises the following raw materials in parts by weight: 8 parts of natural bluestone, 10 parts of silicon micropowder, 0.2 part of a film-forming additive, 1 part of a thickening agent, 0.8 part of a pH regulator, 4 parts of talcum powder, 4 parts of pure acrylic emulsion, 0.5 part of a bactericide, 25 parts of water and 4 parts of ink powder.
The film-forming aid is dipropylene glycol butyl ether.
The mesh number of the silicon micro powder is 1200 meshes.
The thickening agent is a mixture of cellulose and alkali swelling olefine acid with the ratio of 1: 1.
The mesh number of the talcum powder is 1000 meshes.
The bactericide is an RS bactericide.
The art paint also comprises an inorganic pigment, wherein the weight part of the inorganic pigment is 1 part.
A preparation method of a bluestone art paint comprises the following steps:
s1, weighing the raw materials in parts by weight.
S2: pouring natural bluestone, silica micropowder, talcum powder and powdered ink in the raw materials into a mixer, and carrying out primary mixing to obtain a mixed raw material A;
s3: pouring the mixed raw material A into a stirrer, adding water and pure acrylic emulsion, and mixing and dispersing for 6 minutes at the speed of 450 revolutions per minute to obtain a mixed raw material B
S4: adding a bactericide, a film-forming aid and a thickening agent into the mixed raw material B, and mixing and dispersing at 1500 rpm for 10 minutes to obtain a mixed raw material C;
s5: and adding a pH regulator into the mixed raw material C, regulating the pH, uniformly stirring, and discharging after the detection is qualified to obtain the bluestone artistic paint.
As shown in the table above, the silicon micropowder and the ink powder are introduced into the art paint, so that the fineness and the using amount of the silicon micropowder and the ink powder are adjusted through research, and the silicon micropowder, the ink powder and the auxiliary components are selected and matched through research and are combined with the existing raw materials, so that the silicon micropowder and the ink powder have better stereoscopic impression. The makeup art paint is non-toxic, green and environment-friendly, does not contain harmful substances such as formaldehyde and the like, has various colors and bright composite color, and other properties completely meet the national standard.
Example 2
A bluestone art paint comprises the following raw materials in parts by weight: 10 parts of natural bluestone, 10 parts of silicon micropowder, 0.2 part of film-forming additive, 3 parts of thickening agent, 1.2 parts of pH regulator, 4 parts of talcum powder, 4 parts of pure acrylic emulsion, 1.5 parts of bactericide, 36 parts of water and 4 parts of powdered ink.
The film-forming aid is dipropylene glycol butyl ether.
The mesh number of the silicon micro powder is 1200 meshes.
The thickening agent is a mixture of cellulose and alkali swelling olefine acid with the ratio of 1: 1.
The mesh number of the talcum powder is 1000 meshes.
The bactericide is an RS bactericide.
The art paint also comprises an inorganic pigment, wherein the weight part of the inorganic pigment is 3 parts.
A preparation method of a bluestone art paint comprises the following steps:
s1, weighing the raw materials in parts by weight.
S2: pouring natural bluestone, silica micropowder, talcum powder and powdered ink in the raw materials into a mixer, and carrying out primary mixing to obtain a mixed raw material A;
s3: pouring the mixed raw material A into a stirrer, adding water and pure acrylic emulsion, and mixing and dispersing at the speed of 500 revolutions per minute for 6 minutes to obtain a mixed raw material B
S4: adding a bactericide, a film-forming aid and a thickening agent into the mixed raw material B, and mixing and dispersing at 1500 rpm for 10 minutes to obtain a mixed raw material C;
s5: and adding a pH regulator into the mixed raw material C, regulating the pH, uniformly stirring, and discharging after the detection is qualified to obtain the bluestone artistic paint.
As shown in the table above, the silicon micropowder and the ink powder are introduced into the art paint, so that the fineness and the using amount of the silicon micropowder and the ink powder are adjusted through research, and the silicon micropowder, the ink powder and the auxiliary components are selected and matched through research and are combined with the existing raw materials, so that the silicon micropowder and the ink powder have better stereoscopic impression. The makeup art paint is non-toxic, green and environment-friendly, does not contain harmful substances such as formaldehyde and the like, has various colors and bright composite color, and other properties completely meet the national standard.
Example 3
A bluestone art paint comprises the following raw materials in parts by weight: 12 parts of natural bluestone, 12 parts of silicon micropowder, 0.2 part of a film-forming additive, 2 parts of a thickening agent, 1 part of a pH regulator, 7 parts of talcum powder, 7 parts of a pure acrylic emulsion, 1.5 parts of a bactericide, 36 parts of water and 6 parts of ink powder.
The film-forming aid is dipropylene glycol ethyl ether.
The mesh number of the silicon micro powder is 1300 meshes.
The thickening agent is a mixture of cellulose and alkali swelling olefine acid with the ratio of 1: 1.
The mesh number of the talcum powder is 1250 meshes.
The bactericide is an RS bactericide.
The art paint also comprises an inorganic pigment, wherein the weight part of the inorganic pigment is 3 parts.
A preparation method of a bluestone art paint comprises the following steps:
s1, weighing the raw materials in parts by weight.
S2: pouring natural bluestone, silica micropowder, talcum powder and powdered ink in the raw materials into a mixer, and carrying out primary mixing to obtain a mixed raw material A;
s3: pouring the mixed raw material A into a stirrer, adding water and pure acrylic emulsion, and mixing and dispersing for 6 minutes at the speed of 600 revolutions per minute to obtain a mixed raw material B
S4: adding a bactericide, a film-forming aid and a thickening agent into the mixed raw material B, and mixing and dispersing at 1500 rpm for 10 minutes to obtain a mixed raw material C;
s5: and adding a pH regulator into the mixed raw material C, regulating the pH, uniformly stirring, and discharging after the detection is qualified to obtain the bluestone artistic paint.
As shown in the table above, the silicon micropowder and the ink powder are introduced into the art paint, so that the fineness and the using amount of the silicon micropowder and the ink powder are adjusted through research, and the silicon micropowder, the ink powder and the auxiliary components are selected and matched through research and are combined with the existing raw materials, so that the silicon micropowder and the ink powder have better stereoscopic impression. The makeup art paint is non-toxic, green and environment-friendly, does not contain harmful substances such as formaldehyde and the like, has various colors and bright composite color, and other properties completely meet the national standard.
Example 4
A bluestone art paint comprises the following raw materials in parts by weight: 12 parts of natural bluestone, 12 parts of silicon micropowder, 0.3 part of film-forming additive, 3 parts of thickening agent, 1.2 parts of pH regulator, 7 parts of talcum powder, 7 parts of pure acrylic emulsion, 1.5 parts of bactericide, 36 parts of water and 6 parts of powdered ink.
The film-forming aid is dipropylene glycol ethyl ether.
The mesh number of the silicon micro powder is 1300 meshes.
The thickening agent is a mixture of cellulose and alkali swelling olefine acid with the ratio of 1: 1.
The mesh number of the talcum powder is 1300 meshes.
The bactericide is an RS bactericide.
The art paint also comprises an inorganic pigment, wherein the weight part of the inorganic pigment is 3 parts.
A preparation method of a bluestone art paint comprises the following steps:
s1, weighing the raw materials in parts by weight.
S2: pouring natural bluestone, silica micropowder, talcum powder and powdered ink in the raw materials into a mixer, and carrying out primary mixing to obtain a mixed raw material A;
s3: pouring the mixed raw material A into a stirrer, adding water and pure acrylic emulsion, and mixing and dispersing for 6 minutes at the speed of 600 revolutions per minute to obtain a mixed raw material B
S4: adding a bactericide, a film-forming aid and a thickening agent into the mixed raw material B, and mixing and dispersing at 1500 rpm for 10 minutes to obtain a mixed raw material C;
s5: and adding a pH regulator into the mixed raw material C, regulating the pH, uniformly stirring, and discharging after the detection is qualified to obtain the bluestone artistic paint.
As shown in the table above, the silicon micropowder and the ink powder are introduced into the art paint, so that the fineness and the using amount of the silicon micropowder and the ink powder are adjusted through research, and the silicon micropowder, the ink powder and the auxiliary components are selected and matched through research and are combined with the existing raw materials, so that the silicon micropowder and the ink powder have better stereoscopic impression. The makeup art paint is non-toxic, green and environment-friendly, does not contain harmful substances such as formaldehyde and the like, has various colors and bright composite color, and other properties completely meet the national standard.
Example 5
A bluestone art paint comprises the following raw materials in parts by weight: 12 parts of natural bluestone, 11 parts of silicon micropowder, 0.3 part of film-forming additive, 2 parts of thickening agent, 1.2 parts of pH regulator, 4 parts of talcum powder, 4 parts of pure acrylic emulsion, 0.5 part of bactericide, 25 parts of water and 4 parts of ink powder.
The film-forming aid is dipropylene glycol butyl ether.
The mesh number of the silicon micro powder is 1200 meshes.
The thickening agent is a mixture of cellulose and alkali swelling olefine acid with the ratio of 1: 1.
The mesh number of the talcum powder is 1000 meshes.
The bactericide is an RS bactericide.
The art paint also comprises an inorganic pigment, wherein the weight part of the inorganic pigment is 2 parts.
A preparation method of a bluestone art paint comprises the following steps:
s1, weighing the raw materials in parts by weight.
S2: pouring natural bluestone, silica micropowder, talcum powder and powdered ink in the raw materials into a mixer, and carrying out primary mixing to obtain a mixed raw material A;
s3: pouring the mixed raw material A into a stirrer, adding water and pure acrylic emulsion, and mixing and dispersing for 6 minutes at the speed of 600 revolutions per minute to obtain a mixed raw material B
S4: adding a bactericide, a film-forming aid and a thickening agent into the mixed raw material B, and mixing and dispersing at 1500 rpm for 10 minutes to obtain a mixed raw material C;
s5: and adding a pH regulator into the mixed raw material C, regulating the pH, uniformly stirring, and discharging after the detection is qualified to obtain the bluestone artistic paint.
As shown in the table above, the silicon micropowder and the ink powder are introduced into the art paint, so that the fineness and the using amount of the silicon micropowder and the ink powder are adjusted through research, and the silicon micropowder, the ink powder and the auxiliary components are selected and matched through research and are combined with the existing raw materials, so that the silicon micropowder and the ink powder have better stereoscopic impression. The makeup art paint is non-toxic, green and environment-friendly, does not contain harmful substances such as formaldehyde and the like, has various colors and bright composite color, and other properties completely meet the national standard.
The above-mentioned embodiments only express the specific embodiments of the present invention, and the description thereof is more specific and detailed, but not construed as limiting the scope of the present invention. It should be noted that, for a person skilled in the art, several variations and modifications can be made without departing from the inventive concept, which falls within the scope of the present invention.
Claims (8)
1. A bluestone art paint is characterized in that: the feed comprises the following raw materials in parts by weight: 8-12 parts of natural bluestone, 10-12 parts of silica powder, 0.2-0.3 part of a film forming additive, 1-3 parts of a thickening agent, 0.8-1.2 parts of a pH regulator, 4-7 parts of talcum powder, 4-7 parts of a pure acrylic emulsion, 0.5-1.5 parts of a bactericide, 25-36 parts of water and 4-6 parts of ink powder.
2. A bluestone paint of claim 1, wherein: the film-forming assistant is any one of dipropylene glycol butyl ether or dipropylene glycol ethyl ether.
3. A bluestone paint of claim 1, wherein: the mesh number of the silicon micro powder is 1200-1300 meshes.
4. A bluestone paint of claim 1, wherein: the thickening agent is a mixture of cellulose and alkali swelling olefine acid with the ratio of 1: 1.
5. A bluestone paint of claim 1, wherein: the mesh number of the talcum powder is 1000-1300 meshes.
6. A bluestone paint of claim 1, wherein: the bactericide is an RS bactericide.
7. A bluestone paint of claim 1, wherein: the art paint also comprises an inorganic pigment, wherein the weight part of the inorganic pigment is 1-3 parts.
8. A method of producing a bluestone art paint according to any one of claims 1 to 7, comprising:
s1, weighing the raw materials in parts by weight.
S2: pouring natural bluestone, silica micropowder, talcum powder and powdered ink in the raw materials into a mixer, and carrying out primary mixing to obtain a mixed raw material A;
s3: pouring the mixed raw material A into a stirrer, adding water and pure acrylic emulsion, and mixing and dispersing for 6 minutes at the speed of 450-600 rpm to obtain a mixed raw material B
S4: adding a bactericide, a film-forming aid and a thickening agent into the mixed raw material B, and mixing and dispersing at 1500 rpm for 10 minutes to obtain a mixed raw material C;
s5: and adding a pH regulator into the mixed raw material C, regulating the pH, uniformly stirring, and discharging after the detection is qualified to obtain the bluestone artistic paint.