CN113429190A - 高强度防火防潮的托盘的制作工艺及其制作配方 - Google Patents
高强度防火防潮的托盘的制作工艺及其制作配方 Download PDFInfo
- Publication number
- CN113429190A CN113429190A CN202110883443.XA CN202110883443A CN113429190A CN 113429190 A CN113429190 A CN 113429190A CN 202110883443 A CN202110883443 A CN 202110883443A CN 113429190 A CN113429190 A CN 113429190A
- Authority
- CN
- China
- Prior art keywords
- parts
- tray
- ferric oxide
- magnesium
- moisture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高强度防火防潮的托盘的制作工艺及其制作配方，涉及托盘技术领域。本发明包括如下重量份数的组成：氧化镁25‑15份、氯化镁20‑10份、硫酸镁20‑10份、玻纤布10‑1份、锯末20‑10份、稻壳20‑10份、秸秆15‑5份、珍珠岩2‑1份、氧化铁色浆2‑1份、氧化铁色粉2‑1份。本发明通过在托盘的配方中加入氯化镁和氧化镁，能提高托盘的耐热性，从而使托盘达到防火的效果，通过在托盘的配方中加入玻纤布、氧化铁色浆、珍珠岩，一方面能提高托盘的耐水性，从而使托盘达到防潮的效果，另一方面能减少托盘表面微生物和细菌的滋生，从而减少托盘发霉的情况。
Description
技术领域
本发明属于托盘技术领域，特别是涉及一种高强度防火防潮的托盘的制作工艺及其制作配方。
背景技术
托盘是用于集装、堆放、搬运和运输的放置作为单元负荷的货物和制品的水平平台装置。托盘作为物流运作过程中重要的装卸、储存和运输设备，与叉车配套使用在现代物流中发挥着巨大的作用，现有技术中的托盘发部分均为木质托盘或塑料托盘，木质托盘和塑料托盘的耐火性较低、易燃、易变性，在承受较重物品时，容易开裂，木质托盘处于潮湿环境下时，容易受潮发霉。
发明内容
本发明的目的在于提供一种高强度防火防潮的托盘的制作工艺及其制作配方，解决现有技术中的托盘耐火性和防潮性较差的技术问题。
为达上述目的，本发明是通过以下技术方案实现的：
一种高强度防火防潮的托盘的制作配方，包括如下重量份数的组成：氧化镁25-15份、氯化镁20-10份、硫酸镁20-10份、玻纤布10-1份、锯末20-10份、稻壳20-10份、秸秆15-5份、珍珠岩2-1份、氧化铁色浆2-1份、氧化铁色粉2-1份。
可选的，包括如下重量份数的组成：氧化镁20份、氯化镁15份、硫酸镁15份、玻纤布5份、锯末15份、稻壳10份、秸秆10份、珍珠岩2份、氧化铁色浆1份、氧化铁色粉2份。
可选的，包括如下重量份数的组成：氧化镁25份、氯化镁20份、硫酸镁15份、玻纤布10份、锯末10份、稻壳10份、秸秆5份、珍珠岩2份、氧化铁色浆2份、氧化铁色粉1份。
可选的，包括如下重量份数的组成：氧化镁15份、氯化镁10份、硫酸镁15份、玻纤布10份、锯末20份、稻壳15份、秸秆10份、珍珠岩2份、氧化铁色浆2份、氧化铁色粉1份。
可选的，还包括耐高温填料5-2份。
可选的，耐高温添加剂为玻璃纤维、氧化铝、重质碳酸钙中的任意一种或多种。
可选的，还包括防潮防霉填料5-2份。
可选的，防潮防霉填料为干粉防霉剂、活性炭中的一种或多种。
一种高强度防火防潮的托盘的制作工艺，包括如下步骤：
步骤一：检验原料，并将原料按照配比填入搅拌机中，进行充分搅拌混合；
步骤二：将充分搅拌混合后的原料注入模具中，进行定型；
步骤三：将定型后的托盘进行修整，去除毛边、毛刺，并在周侧托盘周侧安装防护垫；
步骤四：将成品的托盘机型检验，并包装入库。
可选的，在步骤四中，对检验不合格的成品托盘进行粉碎，粉碎后的废料作为原料进行循环使用。
本发明的实施例具有以下有益效果：
本发明的一个实施例通过在托盘的配方中加入氯化镁和氧化镁，能提高托盘的耐热性，从而使托盘达到防火的效果，通过在托盘的配方中加入玻纤布、氧化铁色浆、珍珠岩，一方面能提高托盘的耐水性，从而使托盘达到防潮的效果，另一方面能减少托盘表面微生物和细菌的滋生，从而减少托盘发霉的情况。
当然，实施本发明的任一产品并不一定需要同时达到以上所述的所有优点。
附图说明
构成本申请的一部分的说明书附图用来提供对本发明的进一步理解，本发明的示意性实施例及其说明用于解释本发明，并不构成对本发明的不当限定。在附图中：
图1为本发明一实施例的托盘制作工艺流程图。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅是本发明一部分实施例，而不是全部的实施例。以下对至少一个示例性实施例的描述实际上仅仅是说明性的，决不作为对本发明及其应用或使用的任何限制。
为了保持本发明实施例的以下说明清楚且简明，本发明省略了已知功能和已知部件的详细说明。
请参阅图1所示，在本实施例中提供了一种高强度防火防潮的托盘的制作配方，包括如下重量份数的组成：氧化镁25-15份、氯化镁20-10份、硫酸镁20-10份、玻纤布10-1份、锯末20-10份、稻壳20-10份、秸秆15-5份、珍珠岩2-1份、氧化铁色浆2-1份、氧化铁色粉2-1份。
本实施例一个方面的应用为：需要制作托盘时，先检验原料，并将原料按照配比填入搅拌机中，进行充分搅拌混合，再将充分搅拌混合后的原料注入模具中，进行定型，将定型后的托盘进行修整，去除毛边、毛刺，并在周侧托盘周侧安装防护垫，将成品的托盘机型检验，并包装入库。需要注意的是，本申请中所涉及的所有用电设备均可通过蓄电池供电或外接电源。
通过在托盘的配方中加入氯化镁和氧化镁，能提高托盘的耐热性，从而使托盘达到防火的效果，通过在托盘的配方中加入玻纤布、氧化铁色浆、珍珠岩，一方面能提高托盘的耐水性，从而使托盘达到防潮的效果，另一方面能减少托盘表面微生物和细菌的滋生，从而减少托盘发霉的情况。
本实施例的包括如下重量份数的组成：氧化镁20份、氯化镁15份、硫酸镁15份、玻纤布5份、锯末15份、稻壳10份、秸秆10份、珍珠岩2份、氧化铁色浆1份、氧化铁色粉2份。通过在托盘的配方中加入氧化铁色浆、珍珠岩，能提高托盘的耐水性，从而使托盘达到防潮的效果。
本实施例的包括如下重量份数的组成：氧化镁25份、氯化镁20份、硫酸镁15份、玻纤布10份、锯末10份、稻壳10份、秸秆5份、珍珠岩2份、氧化铁色浆2份、氧化铁色粉1份。通过在托盘的配方中加入氯化镁和氧化镁，能提高托盘的耐热性，从而使托盘达到防火的效果。
本实施例的包括如下重量份数的组成：氧化镁15份、氯化镁10份、硫酸镁15份、玻纤布10份、锯末20份、稻壳15份、秸秆10份、珍珠岩2份、氧化铁色浆2份、氧化铁色粉1份。通过在托盘的配方中加入玻纤布，能减少托盘表面微生物和细菌的滋生，从而减少托盘发霉的情况。
为了提高托盘的防火性或防潮性，提出以下两种实施例：
实施例1：本实施例的还包括耐高温填料5-2份；耐高温添加剂为玻璃纤维、氧化铝、重质碳酸钙中的任意一种或多种。玻璃纤维具有良好的耐热性和抗拉强度，从而提高托盘的耐热性与韧性；氧化铝一种高硬度的化合物，熔点高，从而提高托盘的耐热性与耐磨性；重质碳酸钙强度高、隔热性能好。
实施例2：本实施例的还包括防潮防霉填料5-2份；防潮防霉填料为干粉防霉剂、活性炭、石棉粉中的一种或多种。干粉防霉剂具有对霉菌杀死或抑制作用，从而减少托盘表面的霉变；活性炭吸附力强防水性好，从而提高了托盘的防水性；石棉粉是含有石棉纤维的粉状非金属材料，具有良好的防水性。
一种高强度防火防潮的托盘的制作工艺，包括如下步骤：
步骤一：检验原料，并将原料按照配比填入搅拌机中，进行充分搅拌混合；
步骤二：将充分搅拌混合后的原料注入模具中，进行定型；
步骤三：将定型后的托盘进行修整，去除毛边、毛刺，并在周侧托盘周侧安装防护垫；
步骤四：将成品的托盘机型检验，并包装入库。
本实施例的在步骤四中，对检验不合格的成品托盘进行粉碎，粉碎后的废料作为原料进行循环使用。
上述实施例可以相互结合。
需要说明的是，本申请的说明书和权利要求书及上述附图中的术语“第一”、“第二”等是用于区别类似的对象，而不必用于描述特定的顺序或先后次序。应该理解这样使用的数据在适当情况下可以互换，以便这里描述的本申请的实施方式能够以除了在这里图示或描述的那些以外的顺序实施。
在本发明的描述中，需要理解的是，方位词如“前、后、上、下、左、右”、“横向、竖向、垂直、水平”和“顶、底”等所指示的方位或位置关系通常是基于附图所示的方位或位置关系，仅是为了便于描述本发明和简化描述，在未作相反说明的情况下，这些方位词并不指示和暗示所指的装置或元件必须具有特定的方位或者以特定的方位构造和操作，因此不能理解为对本发明保护范围的限制；方位词“内、外”是指相对于各部件本身的轮廓的内外。
Claims (10)
1.一种高强度防火防潮的托盘的制作配方，其特征在于，包括如下重量份数的组成：氧化镁25-15份、氯化镁20-10份、硫酸镁20-10份、玻纤布10-1份、锯末20-10份、稻壳20-10份、秸秆15-5份、珍珠岩2-1份、氧化铁色浆2-1份、氧化铁色粉2-1份。
2.如权利要求1所述的一种高强度防火防潮的托盘的制作配方，其特征在于，包括如下重量份数的组成：氧化镁20份、氯化镁15份、硫酸镁15份、玻纤布5份、锯末15份、稻壳10份、秸秆10份、珍珠岩2份、氧化铁色浆1份、氧化铁色粉2份。
3.如权利要求1所述的一种高强度防火防潮的托盘的制作配方，其特征在于，包括如下重量份数的组成：氧化镁25份、氯化镁20份、硫酸镁15份、玻纤布10份、锯末10份、稻壳10份、秸秆5份、珍珠岩2份、氧化铁色浆2份、氧化铁色粉1份。
4.如权利要求1所述的一种高强度防火防潮的托盘的制作配方，其特征在于，包括如下重量份数的组成：氧化镁15份、氯化镁10份、硫酸镁15份、玻纤布10份、锯末20份、稻壳15份、秸秆10份、珍珠岩2份、氧化铁色浆2份、氧化铁色粉1份。
5.如权利要求1所述的一种高强度防火防潮的托盘的制作配方，其特征在于，还包括耐高温填料5-2份。
6.如权利要求5所述的一种高强度防火防潮的托盘的制作配方，其特征在于，耐高温填料为玻璃纤维、氧化铝、重质碳酸钙中的任意一种或多种。
7.如权利要求1所述的一种高强度防火防潮的托盘的制作配方，其特征在于，还包括防潮防霉填料5-2份。
8.如权利要求7所述的一种高强度防火防潮的托盘的制作配方，其特征在于，防潮防霉填料为干粉防霉剂、活性炭中的一种或多种。
9.一种高强度防火防潮的托盘的制作工艺，其特征在于，包括如下步骤：
步骤一：检验原料，并将原料按照配比填入搅拌机中，进行充分搅拌混合；
步骤二：将充分搅拌混合后的原料注入模具中，进行定型；
步骤三：将定型后的托盘进行修整，去除毛边、毛刺，并在周侧托盘周侧安装防护垫；
步骤四：将成品的托盘机型检验，并包装入库。
10.如权利要求9所述的一种高强度防火防潮的托盘的制作工艺，其特征在于，在步骤四中，对检验不合格的成品托盘进行粉碎，粉碎后的废料作为原料进行循环使用。