CN113414547A - 一种矿用环链的高强度焊接补偿工艺 - Google Patents
一种矿用环链的高强度焊接补偿工艺 Download PDFInfo
- Publication number
- CN113414547A CN113414547A CN202110649587.9A CN202110649587A CN113414547A CN 113414547 A CN113414547 A CN 113414547A CN 202110649587 A CN202110649587 A CN 202110649587A CN 113414547 A CN113414547 A CN 113414547A
- Authority
- CN
- China
- Prior art keywords
- clamping jaws
- welding
- compensation process
- temperature
- clamping
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种矿用环链的高强度焊接补偿工艺，包括以下步骤：①、将环链的两端进行弯折，并保证端口处的距离小于1mm；②、使用夹爪分别夹持住环链的两端，并对中间处进行加热；③、在加工至一定温度A后，两个夹爪向中心处运动，当检测到阻力呈线性快速增长时，夹爪停止运动；④、此时继续加热至一定温度B；⑤、两个夹爪继续运动，此时的运动量为第一次运动量的1/3；⑥、采用明火对焊缝处进行高温烧结，烧结完成后进行水淬；⑦、使用刮刀将焊缝处的凸出部分进行切除，并对焊缝处进行打磨。通过焊接补偿的方式，可以很好的避免在使用中，由于重型载荷造成的焊接点处断裂现象的发生。
Description
技术领域
本发明涉及一种矿用环链的高强度焊接补偿工艺。
背景技术
矿用链条生产行业的编链机在编链过程中，会采用一定的措施，使得环口的距离小于1mm，且要求两端面平行，不允许出现喇叭口。
当两端的距离小于1mm后，可以进入下一步的焊接工艺将两端进行焊接，在传统的焊接工艺中，采用直接加热，且无焊料的焊接工艺。在焊接完成后，焊缝处的直径会小于棒料的直径，且焊接强度不足以应对重型载荷的工况。
针对该问题，通过在焊接时采用合适的长度补偿，可以明显的改善焊接处的强度，但是现有的补偿方式为直接到位或是线性补偿，其补偿能力较差，且容易产生裂缝等焊接缺陷，从而又加重了焊接点处的危险程度。
发明内容
本发明的目的是为了解决以上现有技术的不足，提供一种矿用环链的高强度焊接补偿工艺。
一种矿用环链的高强度焊接补偿工艺，包括以下步骤：
①、将环链的两端进行弯折，并保证端口处的距离小于1mm；
②、使用夹爪分别夹持住环链的两端，并对中间处进行加热；
③、在加工至一定温度A后，两个夹爪向中心处运动，当检测到阻力呈线性快速增长时，夹爪停止运动；
④、此时继续加热至一定温度B；
⑤、两个夹爪继续运动，此时的运动量为第一次运动量的1/10-20；
⑥、采用明火对焊缝处进行高温烧结，烧结完成后进行水淬；
⑦、使用刮刀将焊缝处的凸出部分进行切除，并对焊缝处进行打磨。
优选的，所述的温度A为材料的相变点温度。
优选的，所述的温度B为相变点温度以上30-50摄氏度。
优选的，所述夹爪的驱动方式为液压驱动，夹爪上设有力传感器。
优选的，步骤③中，夹爪的前期进给方式为往复式进给。
有益效果：
采用两次焊接进给的方式，通过第二次的微小补偿量，以提升焊接强度，防止由于热胀冷缩造成的焊接点处直径突变等问题。
通过焊接补偿的方式，可以很好的避免在使用中，由于重型载荷造成的焊接点处断裂现象的发生。
附图说明
图1是原有的时间-位移图；
图2是具有补偿功能的时间-位移图。
具体实施方式
为了加深对本发明的理解，下面将结合实施例和附图对本发明作进一步详述，该实施例仅用于解释本发明，并不构成对本发明保护范围的限定。
一种矿用环链的高强度焊接补偿工艺，包括以下步骤：
①、将环链的两端进行弯折，并保证端口处的距离小于1mm；
②、使用夹爪分别夹持住环链的两端，并对中间处进行加热；
③、在加工至一定温度A后，两个夹爪向中心处运动，当检测到阻力呈线性快速增长时，夹爪停止运动；
如图2所示，夹爪的进给初期采用往复式进给方式，当稳定后采用直线向上的进给方式，当到达指定位置时，继续缓慢进给补偿，以满足使用。
④、此时继续加热至一定温度B；
⑤、两个夹爪继续运动，此时的运动量为第一次运动量的1/15；
⑥、采用明火对焊缝处进行高温烧结，烧结完成后进行水淬；
⑦、使用刮刀将焊缝处的凸出部分进行切除，并对焊缝处进行打磨。
以上所述仅为本发明的较佳实施例而已，并不用以限制本发明，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (5)
1.一种矿用环链的高强度焊接补偿工艺，其特征在于，包括以下步骤：
①、将环链的两端进行弯折，并保证端口处的距离小于1mm；
②、使用夹爪分别夹持住环链的两端，并对中间处进行加热；
③、在加工至一定温度A后，两个夹爪向中心处运动，当检测到阻力呈线性快速增长时，夹爪停止运动；
④、此时继续加热至一定温度B；
⑤、两个夹爪继续运动，此时的运动量为第一次运动量的1/15；
⑥、采用明火对焊缝处进行高温烧结，烧结完成后进行水淬；
⑦、使用刮刀将焊缝处的凸出部分进行切除，并对焊缝处进行打磨。
2.根据权利要求1所述的一种矿用环链的高强度焊接补偿工艺，其特征在于，所述的温度A为材料的相变点温度。
3.根据权利要求1所述的一种矿用环链的高强度焊接补偿工艺，其特征在于，所述的温度B为相变点温度以上30-50摄氏度。
4.根据权利要求1所述的一种矿用环链的高强度焊接补偿工艺，其特征在于，所述夹爪的驱动方式为液压驱动，夹爪上设有力传感器。
5.根据权利要求1所述的一种矿用环链的高强度焊接补偿工艺，其特征在于，步骤③中，夹爪的前期进给方式为往复式进给。