CN113279259A - 一种用于无纺布的100%再生水溶性聚酯硬挺剂的制备方法 - Google Patents
一种用于无纺布的100%再生水溶性聚酯硬挺剂的制备方法 Download PDFInfo
- Publication number
- CN113279259A CN113279259A CN202110685112.5A CN202110685112A CN113279259A CN 113279259 A CN113279259 A CN 113279259A CN 202110685112 A CN202110685112 A CN 202110685112A CN 113279259 A CN113279259 A CN 113279259A
- Authority
- CN
- China
- Prior art keywords
- stiffening agent
- soluble polyester
- water
- regenerated water
- woven fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种用于无纺布的100％再生水溶性聚酯硬挺剂的制备方法，包括以下制备步骤：S1、将再生水溶性聚酯切片与软水按照质量百分比20％:80％加入至加热搅拌罐中；S2、加热搅拌罐加热至100度，并保温3个小时；S3、加热搅拌罐冷却1个小时，过滤后运输至存储罐中得到用于无纺布的100％再生水溶性聚酯硬挺剂，待完全冷却后进行罐装存储。本发明能够制备可回收再利用的100％再生水溶性聚酯硬挺剂，环保性强。
Description
技术领域
本发明涉及胶黏剂技术领域，尤其涉及一种用于无纺布的100％再生水溶性聚酯硬挺剂的制备方法。
背景技术
全球为了实现绿色、环保的发展目标，积极发展资源循环再利用产业，开发资源循环再利用产品是未来的发展趋势。
无纺布通用的硬挺剂主要以水溶型聚乙烯醇和水基型丙烯酸脂类为主，聚乙烯醇简称PVA，是一种由聚乙酸乙烯酯经皂化而成的高分子有机化合物，通常采用石油裂解乙烯直接合成法，或天然气裂解乙烯直接合成法生产，不属于资源循环再利用产业的产品。而水基型丙烯酸聚酯是由甲基丙烯酸甲酯、苯乙烯、丙烯酸丁酯、丙烯酸等共聚合成的聚酯，不属于资源循环再利用产业的产品。因此目前的无纺布通用的硬挺剂存在以下缺点：
缺点1：水溶型聚乙烯醇与水基型丙烯酸聚酯都不是资源循环利用的产品，无法回收再循环利用，环保性较差。
缺点2：水溶型聚乙烯醇上浆退浆较困难，成品坯布PVA残留对人体有害，且不易生物降解，分解物含有毒物质，恶化生态环境，因此PVA已被一些国家列为“禁用浆料”或“不洁浆料”，西欧以立法形式禁止进口用PVA做浆料的坯布，也不允许本地区用PVA做浆料。
缺点3：水基型丙烯酸聚酯不能退浆，不利于无纺布回收再循环利用。
缺点4：水基型丙烯酸聚酯使用时有大量刺激性氨味，破坏生产环境。
缺点5：水基型丙烯酸聚酯生产过程会造成环境污染。
发明内容
(一)要解决的技术问题
为了解决现有技术的上述问题，本发明提供一种用于无纺布的100％再生水溶性聚酯硬挺剂的制备方法，能够制备可回收再利用的100％再生水溶性聚酯硬挺剂，环保性强。
(二)技术方案
为了达到上述目的，本发明采用的技术方案为：一种用于无纺布的100％再生水溶性聚酯硬挺剂的制备方法，包括以下制备步骤：
S1、将再生水溶性聚酯切片与软水按照质量百分比20％:80％加入至加热搅拌罐中；
S2、加热搅拌罐加热至100度，并保温3个小时；
S3、加热搅拌罐冷却1个小时，过滤后运输至存储罐中得到用于无纺布的100％再生水溶性聚酯硬挺剂，待完全冷却后进行罐装存储。
(三)有益效果
本发明的有益效果有：
1、首次将再生水溶性聚酯切片通过物理加工方法加工成无纺布专用聚酯硬挺剂。
2、本发明制备的硬挺剂的成分为再生水溶性聚酯，是采用与合成涤纶纤维相同或相近的芳香族二元羧酸、脂肪族二元羧酸等与二元醇通过酯化反应和缩聚反应合成的线型饱聚酯。在线型大分子中几乎每一个链节都含有两个脂基和适量的水溶性链节，因此，本发明制备的硬挺剂是一种水溶性良好，而又对疏水性涤纶纤维具有良好的粘着力的一种新型无纺布硬挺剂。
3、本发明制备的用于无纺布的100％再生水溶性聚酯硬挺剂在后续与无纺布结合进行烘干定型时，不存在需要成膜温度的特别要求，烘干定型机设定温度调整的范围可大可小，这一特点使产成品的质量比较好控制。
4、再生水溶性聚酯切片是由回收垃圾(可乐瓶、矿泉水瓶等)为原料生产的，属于资源循环再利用产品，通过物理方法制成无纺布专用聚酯硬挺剂，生产过程环保，属于一种资源再利用的用于无纺布的聚酯硬挺剂。
5、由于水溶性聚酯在退浆时无残留，拥有优良的生物降解特性，对环境影响极小，因此，本发明制备的硬挺剂属于绿色环保型硬挺剂。
6、用于无纺布的100％再生水溶性聚酯硬挺剂生产的无纺布产品由于容易退浆处理便于无纺布产品的回收再循环使用。
附图说明
图1为本发明的一种用于无纺布的100％再生水溶性聚酯硬挺剂的制备方法的流程图；
图2为为本发明的一种用于无纺布的100％再生水溶性聚酯硬挺剂的制备方法的设备工艺图；
【附图标记说明】
1、加热搅拌罐；2、存储罐；3、蒸汽输送管。
具体实施方式
为了更好的解释本发明，以便于理解，下面结合附图，通过具体实施方式，对本发明作详细描述。
实施例一
请参照图1和图2所示，一种用于无纺布的100％再生水溶性聚酯硬挺剂的制备方法，包括以下制备步骤：
S1、将再生水溶性聚酯切片与软水按照质量百分比20％:80％加入至加热搅拌罐中；
S2、加热搅拌罐加热至100度，并保温3个小时；
S3、加热搅拌罐冷却1个小时，过滤后运输至存储罐中得到用于无纺布的100％再生水溶性聚酯硬挺剂，待完全冷却后进行罐装存储。
由于无纺布材料特性是比较蓬松柔软的，主要用于制鞋、包袋、装饰材料等领域，对材料的软硬度、强度、延伸都有要求，所以根据不同领域的要求需用100％水溶性聚酯硬挺剂对材料的软硬度、强度、延伸进行测试。以下将本发明制备的100％再生水溶性聚酯硬挺剂用于无纺中底布与水基型丙烯酸聚酯用于无纺中底布的检测报告如下：
上述各项测试的测试内容分别为：定长5mm、定长10mm为材料宽度2.54cm拉长5mm、10mm时所产生的力(N)，该数值越大说明材料强度越好；断裂延伸率为材料宽度2.54cm夹具10cm拉断后的伸长比例(％)；定强延伸率为材料宽度2.54cm夹具10cm产生100N拉力时的伸长比例(％)，断裂延伸率与定强延伸率越小也说明材料强度好，变形系数小，制鞋过程中套楦时帮面饱满。
上述两个测试报告可以看出：使用100％再生水溶性聚酯硬挺剂的材料定长拉力强度大，断裂延伸率与定强延伸率比较小，说明使用100％再生水溶性聚酯硬挺剂的材料比使用水基型丙烯酸聚酯的材料更适用于制鞋。
综上所述，本发明提供的一种用于无纺布的100％再生水溶性聚酯硬挺剂的制备方法，存在以下优点：
1、首次将再生水溶性聚酯切片通过物理加工方法加工成无纺布专用聚酯硬挺剂。
2、本发明制备的硬挺剂的成分为再生水溶性聚酯，是采用与合成涤纶纤维相同或相近的芳香族二元羧酸、脂肪族二元羧酸等与二元醇通过酯化反应和缩聚反应合成的线型饱聚酯。在线型大分子中几乎每一个链节都含有两个脂基和适量的水溶性链节，因此，本发明制备的硬挺剂是一种水溶性良好，而又对疏水性涤纶纤维具有良好的粘着力的一种新型无纺布硬挺剂。
3、本发明制备的用于无纺布的100％再生水溶性聚酯硬挺剂在后续与无纺布结合进行烘干定型时，不存在需要成膜温度的特别要求，烘干定型机设定温度调整的范围可大可小，这一特点使产成品的质量比较好控制。
4、再生水溶性聚酯切片是由回收垃圾(可乐瓶、矿泉水瓶等)为原料生产的，属于资源循环再利用产品，通过物理方法制成无纺布专用聚酯硬挺剂，生产过程环保，属于一种资源再利用的新型无纺布专用聚酯硬挺剂。
5、由于水溶性聚酯在退浆时无残留，拥有优良的生物降解特性，对环境影响极小，因此，本发明制备的硬挺剂属于绿色环保型硬挺剂。
6、用于无纺布的100％再生水溶性聚酯硬挺剂生产的无纺布产品由于容易退浆处理便于无纺布产品的回收再循环使用。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书及附图内容所作的等同变换，或直接或间接运用在相关的技术领域，均同理包括在本发明的专利保护范围内。
Claims (1)
1.一种用于无纺布的100％再生水溶性聚酯硬挺剂的制备方法，其特征在于，包括以下制备步骤：
S1、将再生水溶性聚酯切片与软水按照质量百分比20％:80％加入至加热搅拌罐中；
S2、加热搅拌罐加热至100度，并保温3个小时；
S3、加热搅拌罐冷却1个小时，过滤后运输至存储罐中得到用于无纺布的100％再生水溶性聚酯硬挺剂，待完全冷却后进行罐装存储。