CN113274558A - 一种用于洗肾的血液透析医用导管及其制备方法 - Google Patents

一种用于洗肾的血液透析医用导管及其制备方法 Download PDF

Info

Publication number
CN113274558A
CN113274558A CN202110555628.8A CN202110555628A CN113274558A CN 113274558 A CN113274558 A CN 113274558A CN 202110555628 A CN202110555628 A CN 202110555628A CN 113274558 A CN113274558 A CN 113274558A
Authority
CN
China
Prior art keywords
medical catheter
prepared
temperature
catheter
antibacterial
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202110555628.8A
Other languages
English (en)
Inventor
胡智凱
蔡忠霖
唐嘉豪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Songde Biotechnology Co ltd
Original Assignee
Jiangsu Songde Biotechnology Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Songde Biotechnology Co ltd filed Critical Jiangsu Songde Biotechnology Co ltd
Priority to CN202110555628.8A priority Critical patent/CN113274558A/zh
Publication of CN113274558A publication Critical patent/CN113274558A/zh
Pending legal-status Critical Current

Abstract

本发明涉及医用导管技术领域，尤其为一种用于洗肾的血液透析医用导管及其制备方法，医用导管包括管体以及涂覆于管体表面的抗菌涂层，管体由聚氯乙烯塑料、改性滤渣、碳酸镁、二氧化硅、乙二胺制备而成；抗菌涂层由铜粉和抗感染药物制备而成。本发明以桑白皮为原料，经过丙醇溶液处理，并配合碳酸镁、二氧化硅、乙二胺，使医用导管的抑菌性能得到提高；本发明通过以抗感染药物原料制备抗菌涂层，并将其喷涂至医用导管的表面，可进一步提高医用导管的抑菌性能。

Description

一种用于洗肾的血液透析医用导管及其制备方法
技术领域
本发明涉及医用导管技术领域，具体为一种用于洗肾的血液透析医用导管及其制备方法。
背景技术
医用导管是连通人体内外的管腔制品总称，在排液、灌流、投药、采血、传输血液、通过感应元件检测生物体状况、辅助导入其它医疗器具等方面作为通路被广泛应用。常用的医用导管有血液透析导管、中心静脉导管、透析导管、留置针外周导管、动脉导管鞘、快速交换PTCA球囊扩张导管、带囊气管导管、管腔内支架、单、多腔引流及电极导管等。医用导管已成为临床医学中不可缺少的工具，目前，常用的医用导管的原材料主要为聚氯乙烯、聚氯乙烯糊树脂，但这种普通材料抗菌性较差，容易造成交叉感染。鉴于此，我们提出一种用于洗肾的血液透析医用导管及其制备方法。
发明内容
本发明的目的在于提供一种用于洗肾的血液透析医用导管及其制备方法，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：
一种用于洗肾的血液透析医用导管，包括管体以及涂覆于管体表面的抗菌涂层，管体由聚氯乙烯塑料、改性滤渣、碳酸镁、二氧化硅、乙二胺制备而成；抗菌涂层由铜粉和抗感染药物制备而成。
作为本发明优选的技术方案，改性滤渣由桑白皮、丙醇溶液、蒸馏水制备而成。
作为本发明优选的技术方案，改性滤渣的制备过程为：将桑白皮置于烘箱中进行干燥处理，干燥后投入行星球磨机中进行研磨处理，然后过100目筛得到研磨产物；将研磨产物与丙醇溶液以及蒸馏水进行搅拌混合，搅拌后过滤得到滤渣，将滤渣烘干后研磨成粉末状。
作为本发明优选的技术方案，烘箱的温度为60～70℃，干燥时间为3～4h，行星球磨机的转速为200～240r/min，研磨时间为60～80min，搅拌装置的转速为300～400r/min，搅拌时间为20～30min。
作为本发明优选的技术方案，抗感染药物采用单季铵盐类杀菌剂、聚合季铵盐类杀菌剂、聚六亚甲基双胍、酚类有机抗菌剂、银离子无机抗菌剂、锌离子无机抗菌剂、聚丙乙烯、磷酸酯、硬脂酸、乙炔二醇中的一种或多种。
一种用于洗肾的血液透析医用导管的制备方法，包括如下步骤：
S1：将聚氯乙烯塑料、改性滤渣、碳酸镁、二氧化硅和乙二胺经过混料机进行充分混合后投入高温密炼炉中进行高温融化合成制得待反应物，将待反应物投入双螺杆挤出机中挤出即得医用导管；
S2：将铜粉和抗感染药物充分混合后，再加入蒸馏水搅拌制成可涂覆溶液；
S3：将由铜粉和抗感染药物制得的可涂覆溶液采用高压喷涂的方式均匀喷涂至S1制得的医用导管表面，并在医用导管表面形成致密的抗菌涂层；
S4：将经过S3制得的含有抗菌涂层的医用导管放在室温环境下自然风干，至抗菌涂层完全凝固，最终制得抗菌型医用导管。
作为本发明优选的技术方案，高温密炼炉中的温度为140～160℃，高温密炼炉的转速为400～500r/min，混合反应时间为30～40min，双螺杆挤出机的转速为220～240r/min，双螺杆挤出机中的温度为210～230℃。
与现有技术相比，本发明的有益效果是：
本发明以桑白皮为原料，经过丙醇溶液处理，并配合碳酸镁、二氧化硅、乙二胺，使医用导管的抑菌性能得到提高；
本发明通过以抗感染药物原料制备抗菌涂层，并将其喷涂至医用导管的表面，可进一步提高医用导管的抑菌性能。
具体实施方式
下面将结合本发明实施例对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
本发明提供的技术方案：
实施例1
一种用于洗肾的血液透析医用导管，包括管体以及涂覆于管体表面的抗菌涂层，管体由聚氯乙烯塑料、改性滤渣、碳酸镁、二氧化硅、乙二胺制备而成；抗菌涂层由铜粉和抗感染药物制备而成。
作为本实施例优选的技术方案，改性滤渣由桑白皮、丙醇溶液、蒸馏水制备而成。
作为本实施例优选的技术方案，改性滤渣的制备过程为：将桑白皮置于烘箱中进行干燥处理，干燥后投入行星球磨机中进行研磨处理，然后过100目筛得到研磨产物；将研磨产物与丙醇溶液以及蒸馏水进行搅拌混合，搅拌后过滤得到滤渣，将滤渣烘干后研磨成粉末状。
作为本实施例优选的技术方案，烘箱的温度为60～70℃，干燥时间为3～4h，行星球磨机的转速为200～240r/min，研磨时间为60～80min，搅拌装置的转速为300～400r/min，搅拌时间为20～30min。
本实施例中，烘箱的温度优选为60℃，干燥时间优选为3h，行星球磨机的转速优选为200r/min，研磨时间优选为60min，搅拌装置的转速优选为300r/min，搅拌时间优选为20min。
作为本实施例优选的技术方案，抗感染药物采用单季铵盐类杀菌剂、聚合季铵盐类杀菌剂、聚六亚甲基双胍、酚类有机抗菌剂、银离子无机抗菌剂、锌离子无机抗菌剂、聚丙乙烯、磷酸酯、硬脂酸、乙炔二醇中的一种或多种。
本实施例中，抗感染药物优选为单季铵盐类杀菌剂和聚合季铵盐类杀菌剂。
一种用于洗肾的血液透析医用导管的制备方法，包括如下步骤：
S1：将聚氯乙烯塑料、改性滤渣、碳酸镁、二氧化硅和乙二胺经过混料机进行充分混合后投入高温密炼炉中进行高温融化合成制得待反应物，将待反应物投入双螺杆挤出机中挤出即得医用导管；
S2：将铜粉和抗感染药物充分混合后，再加入蒸馏水搅拌制成可涂覆溶液；
S3：将由铜粉和抗感染药物制得的可涂覆溶液采用高压喷涂的方式均匀喷涂至S1制得的医用导管表面，并在医用导管表面形成致密的抗菌涂层；
S4：将经过S3制得的含有抗菌涂层的医用导管放在室温环境下自然风干，至抗菌涂层完全凝固，最终制得抗菌型医用导管。
作为本实施例优选的技术方案，高温密炼炉中的温度为140～160℃，高温密炼炉的转速为400～500r/min，混合反应时间为30～40min，双螺杆挤出机的转速为220～240r/min，双螺杆挤出机中的温度为210～230℃。
本实施例中，高温密炼炉中的温度优选为140℃，高温密炼炉的转速优选为400r/min，混合反应时间优选为30min，双螺杆挤出机的转速优选为220r/min，双螺杆挤出机中的温度优选为210℃。
实施例2
一种用于洗肾的血液透析医用导管，包括管体以及涂覆于管体表面的抗菌涂层，管体由聚氯乙烯塑料、改性滤渣、碳酸镁、二氧化硅、乙二胺制备而成；抗菌涂层由铜粉和抗感染药物制备而成。
作为本实施例优选的技术方案，改性滤渣由桑白皮、丙醇溶液、蒸馏水制备而成。
作为本实施例优选的技术方案，改性滤渣的制备过程为：将桑白皮置于烘箱中进行干燥处理，干燥后投入行星球磨机中进行研磨处理，然后过100目筛得到研磨产物；将研磨产物与丙醇溶液以及蒸馏水进行搅拌混合，搅拌后过滤得到滤渣，将滤渣烘干后研磨成粉末状。
作为本实施例优选的技术方案，烘箱的温度为60～70℃，干燥时间为3～4h，行星球磨机的转速为200～240r/min，研磨时间为60～80min，搅拌装置的转速为300～400r/min，搅拌时间为20～30min。
本实施例中，烘箱的温度优选为65℃，干燥时间优选为3.5h，行星球磨机的转速优选为220r/min，研磨时间优选为70min，搅拌装置的转速优选为350r/min，搅拌时间优选为25min。
作为本实施例优选的技术方案，抗感染药物采用单季铵盐类杀菌剂、聚合季铵盐类杀菌剂、聚六亚甲基双胍、酚类有机抗菌剂、银离子无机抗菌剂、锌离子无机抗菌剂、聚丙乙烯、磷酸酯、硬脂酸、乙炔二醇中的一种或多种。
本实施例中，抗感染药物优选为聚六亚甲基双胍和酚类有机抗菌剂。
一种用于洗肾的血液透析医用导管的制备方法，包括如下步骤：
S1：将聚氯乙烯塑料、改性滤渣、碳酸镁、二氧化硅和乙二胺经过混料机进行充分混合后投入高温密炼炉中进行高温融化合成制得待反应物，将待反应物投入双螺杆挤出机中挤出即得医用导管；
S2：将铜粉和抗感染药物充分混合后，再加入蒸馏水搅拌制成可涂覆溶液；
S3：将由铜粉和抗感染药物制得的可涂覆溶液采用高压喷涂的方式均匀喷涂至S1制得的医用导管表面，并在医用导管表面形成致密的抗菌涂层；
S4：将经过S3制得的含有抗菌涂层的医用导管放在室温环境下自然风干，至抗菌涂层完全凝固，最终制得抗菌型医用导管。
作为本实施例优选的技术方案，高温密炼炉中的温度为140～160℃，高温密炼炉的转速为400～500r/min，混合反应时间为30～40min，双螺杆挤出机的转速为220～240r/min，双螺杆挤出机中的温度为210～230℃。
本实施例中，高温密炼炉中的温度优选为150℃，高温密炼炉的转速优选为450r/min，混合反应时间优选为35min，双螺杆挤出机的转速优选为230r/min，双螺杆挤出机中的温度优选为220℃。
实施例3
一种用于洗肾的血液透析医用导管，包括管体以及涂覆于管体表面的抗菌涂层，管体由聚氯乙烯塑料、改性滤渣、碳酸镁、二氧化硅、乙二胺制备而成；抗菌涂层由铜粉和抗感染药物制备而成。
作为本实施例优选的技术方案，改性滤渣由桑白皮、丙醇溶液、蒸馏水制备而成。
作为本实施例优选的技术方案，改性滤渣的制备过程为：将桑白皮置于烘箱中进行干燥处理，干燥后投入行星球磨机中进行研磨处理，然后过100目筛得到研磨产物；将研磨产物与丙醇溶液以及蒸馏水进行搅拌混合，搅拌后过滤得到滤渣，将滤渣烘干后研磨成粉末状。
作为本实施例优选的技术方案，烘箱的温度为60～70℃，干燥时间为3～4h，行星球磨机的转速为200～240r/min，研磨时间为60～80min，搅拌装置的转速为300～400r/min，搅拌时间为20～30min。
本实施例中，烘箱的温度优选为70℃，干燥时间优选为4h，行星球磨机的转速优选为240r/min，研磨时间优选为80min，搅拌装置的转速优选为400r/min，搅拌时间优选为30min。
作为本实施例优选的技术方案，抗感染药物采用单季铵盐类杀菌剂、聚合季铵盐类杀菌剂、聚六亚甲基双胍、酚类有机抗菌剂、银离子无机抗菌剂、锌离子无机抗菌剂、聚丙乙烯、磷酸酯、硬脂酸、乙炔二醇中的一种或多种。
本实施例中，抗感染药物优选为锌离子无机抗菌剂和聚丙乙烯。
一种用于洗肾的血液透析医用导管的制备方法，包括如下步骤：
S1：将聚氯乙烯塑料、改性滤渣、碳酸镁、二氧化硅和乙二胺经过混料机进行充分混合后投入高温密炼炉中进行高温融化合成制得待反应物，将待反应物投入双螺杆挤出机中挤出即得医用导管；
S2：将铜粉和抗感染药物充分混合后，再加入蒸馏水搅拌制成可涂覆溶液；
S3：将由铜粉和抗感染药物制得的可涂覆溶液采用高压喷涂的方式均匀喷涂至S1制得的医用导管表面，并在医用导管表面形成致密的抗菌涂层；
S4：将经过S3制得的含有抗菌涂层的医用导管放在室温环境下自然风干，至抗菌涂层完全凝固，最终制得抗菌型医用导管。
作为本实施例优选的技术方案，高温密炼炉中的温度为140～160℃，高温密炼炉的转速为400～500r/min，混合反应时间为30～40min，双螺杆挤出机的转速为220～240r/min，双螺杆挤出机中的温度为210～230℃。
本实施例中，高温密炼炉中的温度优选为160℃，高温密炼炉的转速优选为500r/min，混合反应时间优选为40min，双螺杆挤出机的转速优选为240r/min，双螺杆挤出机中的温度优选为230℃。
以上显示和描述了本发明的基本原理、主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的仅为本发明的优选例，并不用来限制本发明，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (7)

1.一种用于洗肾的血液透析医用导管，其特征在于：包括管体以及涂覆于管体表面的抗菌涂层，管体由聚氯乙烯塑料、改性滤渣、碳酸镁、二氧化硅、乙二胺制备而成；抗菌涂层由铜粉和抗感染药物制备而成。
2.根据权利要求1所述的用于洗肾的血液透析医用导管，其特征在于：改性滤渣由桑白皮、丙醇溶液、蒸馏水制备而成。
3.根据权利要求1所述的用于洗肾的血液透析医用导管，其特征在于：改性滤渣的制备过程为：将桑白皮置于烘箱中进行干燥处理，干燥后投入行星球磨机中进行研磨处理，然后过100目筛得到研磨产物；将研磨产物与丙醇溶液以及蒸馏水进行搅拌混合，搅拌后过滤得到滤渣，将滤渣烘干后研磨成粉末状。
4.根据权利要求3所述的用于洗肾的血液透析医用导管，其特征在于：烘箱的温度为60～70℃，干燥时间为3～4h，行星球磨机的转速为200～240r/min，研磨时间为60～80min，搅拌装置的转速为300～400r/min，搅拌时间为20～30min。
5.根据权利要求1所述的用于洗肾的血液透析医用导管，其特征在于：抗感染药物采用单季铵盐类杀菌剂、聚合季铵盐类杀菌剂、聚六亚甲基双胍、酚类有机抗菌剂、银离子无机抗菌剂、锌离子无机抗菌剂、聚丙乙烯、磷酸酯、硬脂酸、乙炔二醇中的一种或多种。
6.根据权利要求1-5任意一项所述的用于洗肾的血液透析医用导管的制备方法，其特征在于：包括如下步骤：
S1：将聚氯乙烯塑料、改性滤渣、碳酸镁、二氧化硅和乙二胺经过混料机进行充分混合后投入高温密炼炉中进行高温融化合成制得待反应物，将待反应物投入双螺杆挤出机中挤出即得医用导管；
S2：将铜粉和抗感染药物充分混合后，再加入蒸馏水搅拌制成可涂覆溶液；
S3：将由铜粉和抗感染药物制得的可涂覆溶液采用高压喷涂的方式均匀喷涂至S1制得的医用导管表面，并在医用导管表面形成致密的抗菌涂层；
S4：将经过S3制得的含有抗菌涂层的医用导管放在室温环境下自然风干，至抗菌涂层完全凝固，最终制得抗菌型医用导管。
7.根据权利要求6所述的用于洗肾的血液透析医用导管的制备方法，其特征在于：高温密炼炉中的温度为140～160℃，高温密炼炉的转速为400～500r/min，混合反应时间为30～40min，双螺杆挤出机的转速为220～240r/min，双螺杆挤出机中的温度为210～230℃。
CN202110555628.8A 2021-05-21 2021-05-21 一种用于洗肾的血液透析医用导管及其制备方法 Pending CN113274558A (zh)