CN113215681A - 一种耐磨耐老化渔网线 - Google Patents
一种耐磨耐老化渔网线 Download PDFInfo
- Publication number
- CN113215681A CN113215681A CN202110472268.5A CN202110472268A CN113215681A CN 113215681 A CN113215681 A CN 113215681A CN 202110472268 A CN202110472268 A CN 202110472268A CN 113215681 A CN113215681 A CN 113215681A
- Authority
- CN
- China
- Prior art keywords
- parts
- mixture
- resistant
- calcium carbonate
- talcum powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种耐磨耐老化渔网线，包括以下成分组成：聚乙烯25‑40份、尼龙30‑40份、聚异戊二烯橡胶5‑9份、二甲基硅油2‑5份、聚异二烯1‑4份，五氯硝基苯2‑3份、复合助剂5‑7份、三元羧基氯醋树脂8‑12份、硅氧烷接枝改性丙烯酸树脂12‑16份、碳化硼纤维2‑6份、聚对苯二甲酸丁二酯2‑4份、碳酸钙与滑石粉混合物1‑3份、乙酸4‑6份、防老剂RD2‑4份，氧化锌1‑3份。
Description
技术领域
本发明涉及渔具技术领域，尤其涉及一种耐磨耐老化渔网线。
背景技术
渔网是捕鱼用的网，古代人使用粗布加上麻作为原料，通过捆卷的方法制成渔网。虽然这种渔网易腐烂，坚韧度差，但是其捕鱼效率已经大大提高。随着渔业的发展，渔猎的对象不只是鱼，捕捞的工具也与时俱进。古代人使用粗布加上麻作为原料，通过捆卷的方法制成渔网。
虽然这种渔网易腐烂，坚韧度差，但是其捕鱼效率已经大大提高。随着渔业的发展，渔猎的对象不只是鱼，捕捞的工具也与时俱进。现代渔网主要采用聚乙烯，尼龙等原料进行加工，有较长的使用周期，和更高的捕捞效率，但是聚乙烯本身的力学性能一般，拉伸强度较低，抗蠕变性不好，就导致传统渔网的强度、耐磨性能、韧性不适宜于复杂海底和大风大浪环境捕捞作业，降低了渔具的使用寿命，不仅浪费资源，还直接影响渔获量。
发明内容
针对现有技术中的上述不足，本发明提供了一种耐磨耐老化渔网线，其制备简单，易加工，更加的耐磨耐老化。
为了达到上述发明目的，本发明采用的具体方案为：
一种耐磨耐老化渔网线，包括以下成分组成：聚乙烯25-40份、尼龙30-40份、聚异戊二烯橡胶5-9份、二甲基硅油2-5份、聚异二烯1-4份，五氯硝基苯2-3份、复合助剂5-7份、三元羧基氯醋树脂8-12份、硅氧烷接枝改性丙烯酸树脂12-16份、碳化硼纤维2-6份、聚对苯二甲酸丁二酯2-4份、碳酸钙与滑石粉混合物1-3份、乙酸4-6份、防老剂RD2-4份，氧化锌1-3份。
优选地，所述碳酸钙与滑石粉混合物中碳酸钙与滑石粉按3:2质量比例混合；所述碳酸钙与滑石粉混合物的制备方法为：将碳酸钙与滑石粉先混合进行研磨，研磨助剂为丙三醇，研磨30分钟后，过滤，干燥，然后添加到气流粉碎机中粉碎30分钟，然后，将经过气流粉碎机处理后的碳酸钙与滑石粉混合物采用质量浓度为1.25％的氢氧化钠溶液浸泡30分钟后，过滤，干燥，即可。
优选地，所述复合助剂为酚醛树脂、柠檬酸钠、香叶、苯基对苯二胺和纳米二氧化钛中的一种或几种组成。
一种耐磨耐老化渔网线的制备方法，将聚乙烯、尼龙、聚异戊二烯橡胶、二甲基硅油、聚异二烯、三元羧基氯醋树脂、硅氧烷接枝改性丙烯酸树脂放入温152-154℃的容器中混合40分钟，将容器内部温度调节到70-72℃时向容器中依次加入相应重量份的聚对苯二甲酸丁二酯、碳酸钙与滑石粉混合物、氧化锌、碳化硼纤维、五氯硝基苯进行搅拌，搅拌15分钟后再添加复合助剂和防老剂搅拌30分钟，最后添加到挤出机进行造粒，然后使用注塑机注塑，然后使用喷丝机喷丝，得到渔网线。
本发明的有益效果为：本发明制作的渔网线加工工艺简单，有效解决了渔网老化的问题，提供强度高、耐磨性好的渔网线，利用抗老化材料和并且加入防老剂，显著增加了渔网的抗老化性，增加渔网的使用寿命，从而达到节约使用成本的目的。
具体实施方式
以下通过具体实施例进一步描述本发明，但本发明不仅仅限于以下实施例。在本发明的范围内或者在不脱离本发明的内容、精神和范围内，对本发明进行的变更、组合或替换，对于本领域的技术人员来说是显而易见的，且包含在本发明的范围之内。
实施例1：一种耐磨耐老化渔网线，包括以下成分组成：聚乙烯25份、尼龙30份、聚异戊二烯橡胶5份、二甲基硅油2份、聚异二烯1份，五氯硝基苯2份、复合助剂5份、三元羧基氯醋树脂8份、硅氧烷接枝改性丙烯酸树脂12份、碳化硼纤维2份、聚对苯二甲酸丁二酯2份、碳酸钙与滑石粉混合物1份、乙酸4份、防老剂RD2份，氧化锌1份。
实施例2：一种耐磨耐老化渔网线，其包括以下成分组成：聚乙烯30份、尼龙35份、聚异戊二烯橡胶7份、二甲基硅油3份、聚异二烯2份，五氯硝基苯2.5份、复合助剂6份、三元羧基氯醋树脂9份、硅氧烷接枝改性丙烯酸树脂13份、碳化硼纤维4份、聚对苯二甲酸丁二酯3份、碳酸钙与滑石粉混合物2份、乙酸5份、防老剂RD3份，氧化锌2份。
实施例3：一种耐磨耐老化渔网线，包括以下成分组成：聚乙烯40份、尼龙40份、聚异戊二烯橡胶9份、二甲基硅油5份、聚异二烯4份，五氯硝基苯3份、复合助剂7份、三元羧基氯醋树脂11份、硅氧烷接枝改性丙烯酸树脂15份、碳化硼纤维5份、聚对苯二甲酸丁二酯4份、碳酸钙与滑石粉混合物3份、乙酸6份、防老剂RD4份，氧化锌3份。
所述碳酸钙与滑石粉混合物中碳酸钙与滑石粉按3:2质量比例混合；所述碳酸钙与滑石粉混合物的制备方法为：将碳酸钙与滑石粉先混合进行研磨，研磨助剂为丙三醇，研磨30分钟后，过滤，干燥，然后添加到气流粉碎机中粉碎30分钟，然后，将经过气流粉碎机处理后的碳酸钙与滑石粉混合物采用质量浓度为1.25％的氢氧化钠溶液浸泡30分钟后，过滤，干燥，即可。
所述复合助剂为酚醛树脂、柠檬酸钠、香叶、苯基对苯二胺和纳米二氧化钛中的一种或几种组成。
一种耐磨耐老化渔网线的制备方法，将聚乙烯、尼龙、聚异戊二烯橡胶、二甲基硅油、聚异二烯、三元羧基氯醋树脂、硅氧烷接枝改性丙烯酸树脂放入温152-154℃的容器中混合40分钟，将容器内部温度调节到70-72℃时向容器中依次加入相应重量份的聚对苯二甲酸丁二酯、碳酸钙与滑石粉混合物、氧化锌、碳化硼纤维、五氯硝基苯进行搅拌，搅拌15分钟后再添加复合助剂和防老剂搅拌30分钟，最后添加到挤出机进行造粒，然后使用注塑机注塑，然后使用喷丝机喷丝，得到渔网线。
以上所述仅为本发明专利的较佳实施例而已，并不用以限制本发明专利，凡在本发明专利的精神和原则之内所作的任何修改、等同替换和改进等，均应包含在本发明专利的保护范围之内。
Claims (4)
1.一种耐磨耐老化渔网线，其特征在于：包括以下成分组成：聚乙烯25-40份、尼龙30-40份、聚异戊二烯橡胶5-9份、二甲基硅油2-5份、聚异二烯1-4份，五氯硝基苯2-3份、复合助剂5-7份、三元羧基氯醋树脂8-12份、硅氧烷接枝改性丙烯酸树脂12-16份、碳化硼纤维2-6份、聚对苯二甲酸丁二酯2-4份、碳酸钙与滑石粉混合物1-3份、乙酸4-6份、防老剂RD2-4份，氧化锌1-3份。
2.根据权利要求1所述的一种耐磨耐老化渔网线，其特征在于：所述碳酸钙与滑石粉混合物中碳酸钙与滑石粉按3:2质量比例混合；所述碳酸钙与滑石粉混合物的制备方法为：将碳酸钙与滑石粉先混合进行研磨，研磨助剂为丙三醇，研磨30分钟后，过滤，干燥，然后添加到气流粉碎机中粉碎30分钟，然后，将经过气流粉碎机处理后的碳酸钙与滑石粉混合物采用质量浓度为1.25％的氢氧化钠溶液浸泡30分钟后，过滤，干燥，即可。
3.根据权利要求1所述的一种耐磨耐老化渔网线，其特征在于：所述复合助剂为酚醛树脂、柠檬酸钠、香叶、苯基对苯二胺和纳米二氧化钛中的一种或几种组成。
4.根据权利要求1所述的一种耐磨耐老化渔网线的制备方法，其特征在于：将聚乙烯、尼龙、聚异戊二烯橡胶、二甲基硅油、聚异二烯、三元羧基氯醋树脂、硅氧烷接枝改性丙烯酸树脂放入温152-154℃的容器中混合40分钟，将容器内部温度调节到70-72℃时向容器中依次加入相应重量份的聚对苯二甲酸丁二酯、碳酸钙与滑石粉混合物、氧化锌、碳化硼纤维、五氯硝基苯进行搅拌，搅拌15分钟后再添加复合助剂和防老剂搅拌30分钟，最后添加到挤出机进行造粒，然后使用注塑机注塑，然后使用喷丝机喷丝，得到渔网线。