CN113138508A - 电致变色玻璃及其制备方法 - Google Patents
电致变色玻璃及其制备方法 Download PDFInfo
- Publication number
- CN113138508A CN113138508A CN202010059393.9A CN202010059393A CN113138508A CN 113138508 A CN113138508 A CN 113138508A CN 202010059393 A CN202010059393 A CN 202010059393A CN 113138508 A CN113138508 A CN 113138508A
- Authority
- CN
- China
- Prior art keywords
- layer
- sub
- ion conductor
- color
- changing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明实施例公开的一种电致变色玻璃及其制备方法。所述电致变色玻璃包括玻璃基板和依次形成于所述玻璃基板同一侧的第一透明导电层、第一复合变色层、第一离子导体层、第二透明导电层、第二复合变色层、第二离子导体层、第三透明导电层、主变色层、第三离子导体层、辅变色层、第四透明导电层以及外保护层。本发明实施例公开的电致变色玻璃可以增大玻璃的颜色调控范围，实现更多颜色的调控。
Description
技术领域
本发明涉及一种玻璃技术领域，尤其是一种电致变色玻璃及其制备方法。
背景技术
由于其低碳、节能、颜色可调等特性，电致变色玻璃已逐渐应用在建筑等诸多行业。电致变色玻璃可在外加电场作用下，材料的光学性能发生连续可逆变化，使得玻璃的颜色和透明度发生可逆变化，可实现多个颜色的调控和变化。但是目前的电致变色玻璃的颜色调控范围较单一，颜色均匀性较差，难以满足行业发展的需求。
发明内容
针对上述问题，本发明实施例提供了一种电致变色玻璃及其制备方法，可增大玻璃的颜色调控范围，实现更多颜色的调控，提升颜色均匀性。
具体地，本发明实施例提供一种电致变色玻璃，包括玻璃基板和依次形成于所述玻璃基板同一侧的第一透明导电层、第一复合变色层、第一离子导体层、第二透明导电层、第二复合变色层、第二离子导体层、第三透明导电层、主变色层、第三离子导体层、辅变色层、第四透明导电层以及外保护层，所述第一复合变色层包括第一子变色层和第二子变色层，所述第一子变色层与所述第一透明导电层相邻，所述第二子变色层与所述第一离子导体层相邻；所述第一子变色层的材料选自于W、Mo、Nb、Ti、Ta中至少两种组合的氧化物；所述第二子变色层的材料选自于Ni、V、Co、Ir、Fe、Mn中至少两种元素组合的氧化物；所述第二复合层包括第三子变色层和第四子变色层，所述第三子变色层与所述第二透明导电层相邻，所述第四子变色层与所述第二离子导体层相邻；所述第三子变色层的材料选自于W、Mo、Nb、Ti、Ta中至少两种组合的氧化物；所述第四子变色层的材料选自于Ni、V、Co、Ir、Fe、Mn中至少两种元素组合的氧化物。
另一方面，本发明实施例提供的一种电致变色玻璃，包括玻璃基板和依次形成于所述玻璃基板同一侧的第一透明导电层、第一复合变色层、第一离子导体层、第二透明导电层、第二复合变色层、第二离子导体层、第三透明导电层、主变色层、第三离子导体层、辅变色层、第四透明导电层以及外保护层。
在本发明的一个实施例中，所述第一复合变色层包括第一子变色层和第二子变色层，所述第一子变色层与所述第一透明导电层相邻，所述第二子变色层与所述第一离子导体层相邻；所述第一子变色层的材料选自于W、Mo、Nb、Ti、Ta中至少两种组合的氧化物；所述第二子变色层的材料选自于Ni、V、Co、Ir、Fe、Mn中至少两种元素组合的氧化物。
在本发明的一个实施例中，所述第二复合层包括第三子变色层和第四子变色层，所述第三子变色层与所述第二透明导电层相邻，所述第四子变色层与所述第二离子导体层相邻；所述第三子变色层的材料选自于W、Mo、Nb、Ti、Ta中至少两种组合的氧化物；所述第四子变色层的材料选自于Ni、V、Co、Ir、Fe、Mn中至少两种元素组合的氧化物。
在本发明的一个实施例中，所述第一子变色层的厚度范围为30nm-500nm；所述第二子变色层的厚度范围为20nm-500nm；所述第三子变色层的厚度范围为30nm-500nm；所述第四子变色层的厚度范围为20nm-500nm。
在本发明的一个实施例中，所述第一子变色层与所述第三子变色层的厚度相等；所述第二子变色层与所述第四子变色层的厚度相等。
在本发明的一个实施例中，所述主变色层的材料选自于W、Mo、Nb、Ti、Ta中至少两种组合的氧化物；所述辅变色层的材料选自于Ni、V、Co、Ir、Fe、Mn中至少两种元素组合的氧化物。
在本发明的一个实施例中，所述第一透明导电层、所述第二透明导电层、所述第三透明导电层、所述第四透明导电层的材料分别选自于FTO、ITO、IGZO、AZO、GZO、Ag中的一种或至少两种的组合；所述第一透明导电层、所述第二透明导电层、所述第三透明导电层的厚度范围分别为1-1100nm；所述第四透明导电层的厚度范围为10-1000nm。
在本发明的一个实施例中，所述第一离子导体层、所述第二离子导体层、所述第三离子导体层的材料分别选自于H、Li、Na、K、Mg中的一种或至少两种的组合；所述第一离子导体层、所述第二离子导体层、所述第三离子导体层的厚度范围分别为10nm-100nm。
又一方面，本发明实施例提供的一种电致变色玻璃制备方法，包括：提供玻璃基板；在所述玻璃基板上形成第一透明导电层；在所述第一透明导电层上形成第一复合变色层；在所述第一复合变色层上形成第一离子导体层；在所述第一离子导体层上形成第二透明导电层；在所述第二透明导电层上形成第二复合变色层；在所述第二复合变色层上形成第二离子导体层；在所述第二离子导体层上形成第三透明导电层；在所述第三透明导电层上形成主色层；在所述主变色层上形成第三离子导体层；在所述第三离子导体层上形成辅变色层；在所述辅变色层上形成第四透明导电层；以及在所述第四透明导电层上形成外保护层。
上述一个或多个技术方案可以具有如下优点或有益效果：分别独立调控的三个变色功能膜层，即两个复合变色层、一个主变色层与辅变色层间隔设置相结合的特定膜层结构，增大了电致变色玻璃的颜色调控范围，实现更多颜色的调控，电致变色玻璃的颜色坐标范围更广泛。另外，本发明实施例提供的电致变色玻璃制备方法采用磁控反应溅射沉积法形成各膜层，避免了生产过程中多次进出镀膜设备，简化了生产工艺，提高生产效率
附图说明
为了更清楚地说明本发明实施例的技术方案，下面将对实施例描述中所需要使用的附图作简单地介绍，显而易见地，下面描述中的附图仅仅是本发明的一些实施例，对于本领域普通技术人员来讲，在不付出创造性劳动的前提下，还可以根据这些附图获得其他的附图。
图1为本发明实施例提供的一种电致变色玻璃的结构示意图。
图2为本发明实施例提供的一种电致变色玻璃制备方法的流程示意图。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例，都属于本发明护的范围。
如图1所示，本发明一实施例提供了一种电致变色玻璃300。电致变色玻璃300例如包括玻璃基板5和依次形成于玻璃基板5同一侧的第一透明导电层11、第一复合变色层10、第一离子导体层14、第二透明导电层21、第二复合变色层20、第二离子导体层24、第三透明导电层31、主变色层32、第三离子导体层33、辅变色层34、第四透明导电层50以及外保护层60。
本发明实施例提供的电致变色玻璃采用分别独立调控的三个变色功能膜层，即两个复合变色层、一个主变色层与辅变色层间隔设置相结合的特定膜层结构，增大了电致变色玻璃的颜色调控范围，实现更多颜色的调控，其颜色坐标范围更广泛。
具体地，玻璃基板5可例如为超白玻璃、铝玻璃材等。玻璃基板5的厚度范围可例如为0.05-20mm。
第一透明导电层11、第二透明导电层21、第三透明导电层31和第四透明导电层50的材料分别为无机变色材料。无机变色材料选自于FTO(氟硅氧化物)、ITO(铟锡氧化物)、IGZO(铟镓锌氧化物)、AZO(铝锌氧化物)、GZO(镓锌氧化物)、Ag中的一种或至少两种的组合。此处的至少两种的组合可例如为两者组合比如AZO和GZO，或其中三个组合比如FTO、ITO、GZO，甚至更多种的组合等。优选地，第一透明导电层11、第二透明导电层21、第三透明导电层31、第四透明导电层50中至少两种的材料相同。第一透明导电层11、第二透明导电层21、第三透明导电层31的厚度范围分别为1-1100nm。第四透明导电层50的厚度范围为10-1000nm。优选地，第一透明导电层11、第二透明导电层21、第三透明导电层31、第四透明导电层50的厚度范围分别为10-300nm。进一步优选地，第一透明导电层11、第二透明导电层21、第三透明导电层31、第四透明导电层50中的至少两者的厚度相等。
第一复合变色层10包括第一子变色层12、第二子变色层13，第一子变色层12与第一透明导电层11相邻，第二子变色层13与第一离子导体层14相邻。第二复合变色层20包括第三子变色层22、第四子变色层23，第三子变色层22与第二透明导电层21相邻，第四子变色层23与第二离子导体层24相邻。
第一子变色层12、第三子变色层22、主变色层32为太阳能光谱主调节功能层。第一子变色层12、第三子变色层22、主变色层32的材料分别为无机变色材料。无机变色材料可例如选自于W、Mo、Nb、Ti、Ta中至少两种元素组合的氧化物，例如W、Mo、Nb、Ti、Ta中任意两者组合的氧化物比如WMoOx、WNbOx，或者三者组合的氧化物WMoTiOx、WNbTaOx，甚至更多种的组合的氧化物。优选地，第一子变色层12、第三子变色层22、主变色层32的材料相同。第一子变色层12、第三子变色层22、主变色层32的厚度范围分别为30-500nm。优选地，第一子变色层12、第三子变色层22、主变色层32的厚度相等。
第二子变色层13、第四子变色层23、辅变色层34为太阳能光谱辅助调节功能层。第二子变色层13、第四子变色层23、辅变色层34的材料分别选自于Ni、V、Co、Ir、Fe、Mn中至少两种组合的氧化物。具体地，第二子变色层13、第四子变色层23、辅变色层34的材料分别可例如为Ni、V、Co、Ir、Fe、Mn中两种的组合的氧化物比如NiVOx、NiCoOx、NiIrOx、NiFeOx，或者三种的组合的氧化物，甚至更多种的组合的氧化物。优选地，第二子变色层13、第四子变色层23、辅变色层34的材料相同。第二子变色层13、第四子变色层23、辅变色层34的厚度范围分别为20nm-500nm。优选地，第二子变色层13、第四子变色层23、辅变色层34的厚度相等。
第一离子导体层14、第二离子导体层24、第三离子导体层33的材料分别选自于：H、Li、Na、K、Mg中的一种或者至少两种的组合，例如包括其中的两者组合比如Li、Na，三者组合比如Na、K、Mg，甚至更多的组合等。优选地，第一离子导体层14、第二离子导体层24、第三离子导体层33的材料相同。第一离子导体层14、第二离子导体层24、第三离子导体层33的厚度范围分别为10nm-100nm。优选地，第一离子导体层14、第二离子导体层24、第三离子导体层33的厚度相等。
外保护层60的材料选自于Si、Ti、Zn、Sn、Nb、Ta中之一的氧化物或氮化物或氮氧化物。外保护层的厚度为0.2-100nm。例如外保护层60的材料为Si3N4，其为一种高温陶瓷材料，硬度大、熔点高、化学性质稳定，可以很好的起到保护作用。
此外，本发明实施例还提供了一种电致变色玻璃制备方法，例如用于制备前述的电致变色玻璃300。电致变色玻璃制备方法例如包括步骤：
S11：提供玻璃基板。将玻璃基板清洁、干燥。
S12：在玻璃基板上形成第一透明导电层。具体地，将玻璃基板升温至预设温度，所述预设温度的范围例如280-300℃，以FTO、ITO、IGZO、AZO、GZO、Ag中的一种或至少两种的组合为靶材材料，在预设真空溅射气压下沉积得到第一透明导电层。预设真空溅射气压例如为1.0E-3～9.0E-3mbar。优选的，第一透明导电层也可以是预先制备好的导电膜层。这样可以达到膜层间更好的折射率匹配。
S13：在第一透明导电层上形成第一复合变色层。具体地，首先以W、Mo、Nb、Ti、Ta中至少两种组合的氧化物为靶材材料，将靶材材料置于预设真空溅射气压下沉积，得到第一子变色层；接着以Ni、V、Co、Ir、Fe、Mn中至少两种组合的氧化物为靶材材料，将靶材材料置于预设真空溅射气压条件下沉积得到第二子变色层。优选地，第一子变色层和/或也可以同时采用多个靶位形成，如此可以获得膜层间更好的结合力。
S14：在第一复合变色层上形成第一离子导体层。以H、Li、Na、K、Mg元素的一种或者至少两种的组合为靶材材料，并将靶材材料置于预设真空溅射气压条件下沉积得到第一离子导体层。优选地，第一离子导体层也可以同时采用多个靶位形成，以获得膜层间更好的结合力。
S15：在第一离子导体层上形成第二透明导电层。具体地，以FTO、ITO、IGZO、AZO、GZO、Ag中的一种或至少两种的组合为靶材材料，将靶材材料置于预设真空溅射气压条件下沉积得到第二透明导电层。优选的，第二透明导电层也可以是预先制备好的导电膜层。这样可以达到膜层间更好的折射率匹配。
S16：在第二透明导电层上形成第二复合变色层。具体地，首先以W、Mo、Nb、Ti、Ta中至少两种组合的氧化物为靶材材料，将靶材材料置于预设真空溅射气压下沉积，得到第三子变色层；接着以Ni、V、Co、Ir、Fe、Mn中至少两种组合的氧化物为靶材材料，将靶材材料置于预设真空溅射气压条件下沉积得到第四子变色层。优选地，第三子变色层和/或第四子变色层也可以同时采用多个靶位形成，如此可以获得膜层间更好的结合力。
S17：在第二复合变色层上形成第二离子导体层。以H、Li、Na、K、Mg元素的一种或者至少两种的组合为靶材材料，并将靶材材料置于预设真空溅射气压条件下沉积得到第二离子导体层。优选地，第二离子导体层也可以同时采用多个靶位形成，以获得膜层间更好的结合力。
S18：在第二离子导体层上形成第三透明导电层。以FTO、ITO、IGZO、AZO、GZO、Ag中的一种或至少两种的组合为靶材材料，将靶材材料置于预设真空溅射气压下沉积得到第三透明导电层。优选的，第三透明导电层也可以是预先制备好的导电膜层。这样可以达到膜层间更好的折射率匹配。
S19：在第三透明导电层上形成主变色层。具体地，以W、Mo、Nb、Ti、Ta中至少两种组合的氧化物为靶材材料，将靶材材料置于预设真空溅射气压下沉积，得到主变色层。优选地，主变色层也可以同时采用多个靶位形成，如此可以获得膜层间更好的结合力。
S20：在主变色层上形成第三离子导体层。以H、Li、Na、K、Mg元素的一种或者至少两种的组合为靶材材料，并将靶材材料置于预设真空溅射气压条件下沉积得到第三离子导体层。优选地，第三离子导体层也可以同时采用多个靶位形成，以获得膜层间更好的结合力。
S21：在第三离子导体层上形成辅变色层。具体地，以Ni、V、Co、Ir、Fe、Mn中至少两种组合的氧化物为靶材材料，将靶材材料置于预设真空溅射气压条件下沉积得到辅变色层。优选地，辅变色层也可以同时采用多个靶位形成，如此可以获得膜层间更好的结合力。
S22：在辅变色层上形成第四透明导电层。以FTO、ITO、IGZO、AZO、GZO、Ag中的一种或至少两种的组合为靶材材料，将靶材材料置于预设真空溅射气压下沉积得到第四透明导电层。优选的，第四透明导电层也可以是预先制备好的导电膜层。这样可以达到膜层间更好的折射率匹配。
S23：在第四透明导电层上形成外保护层。以Si、Ti、Zn、Sn、Nb、Ta之一的氧化物或氮化物或氮氧化物为靶材材料，并将靶材材料置于预设真空溅射气压下沉积得到外保护层。优选地，外保护层也可以同时采用多个靶位形成，以获得膜层间更好的结合力。
此外，本发明实施例提供的电致变色玻璃制备方法还可以包括热处理步骤。具体地，进行真空热处理及退火工艺，热处理温度例如为300-300℃，热处理时间例如为5-120min。
进步一地，本发明实施例提供的电致变色玻璃制备方法还可以包括预真空过渡并接电极，完成电致变色玻璃的制备。其可采用现有技术中的方法完成预真空过渡并接电极，此处不再赘述。
综上所述，本发明实施例提供的电致变色玻璃采用分别独立调控的三个变色功能膜层，即两个复合变色层、一个主变色层与辅变色层间隔设置相结合的特定膜层结构，增大了电致变色玻璃的颜色调控范围，实现更多颜色的调控，电致变色玻璃的颜色坐标范围更广泛，而且颜色更为稳定，大面积颜色均匀性更好，一次激励调色后颜色保持的时间更长，其可广泛应用于各种场合。另外，本发明实施例提供的电致变色玻璃制备方法采用磁控反应溅射沉积法形成各膜层，避免了生产过程中多次进出镀膜设备，简化了生产工艺，提高生产效率。
此外，可以理解的是，前述各个实施例仅为本发明的示例性说明，在技术特征不冲突、结构不矛盾、不违背本发明的发明目的前提下，各个实施例的技术方案可以任意组合、搭配使用。
最后应说明的是：以上实施例仅用以说明本发明的技术方案，而非对其限制；尽管参照前述实施例对本发明进行了详细的说明，本领域的普通技术人员应当理解：其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换；而这些修改或者替换，并不使相应技术方案的本质脱离本发明各实施例技术方案的精神和范围。
Claims (10)
1.一种电致变色玻璃，其特征在于，包括玻璃基板和依次形成于所述玻璃基板同一侧的第一透明导电层、第一复合变色层、第一离子导体层、第二透明导电层、第二复合变色层、第二离子导体层、第三透明导电层、主变色层、第三离子导体层、辅变色层、第四透明导电层以及外保护层，所述第一复合变色层包括第一子变色层和第二子变色层，所述第一子变色层与所述第一透明导电层相邻，所述第二子变色层与所述第一离子导体层相邻；所述第一子变色层的材料选自于W、Mo、Nb、Ti、Ta中至少两种组合的氧化物；所述第二子变色层的材料选自于Ni、V、Co、Ir、Fe、Mn中至少两种元素组合的氧化物；所述第二复合层包括第三子变色层和第四子变色层，所述第三子变色层与所述第二透明导电层相邻，所述第四子变色层与所述第二离子导体层相邻；所述第三子变色层的材料选自于W、Mo、Nb、Ti、Ta中至少两种组合的氧化物；所述第四子变色层的材料选自于Ni、V、Co、Ir、Fe、Mn中至少两种元素组合的氧化物。
2.一种电致变色玻璃，其特征在于，包括玻璃基板和依次形成于所述玻璃基板同一侧的第一透明导电层、第一复合变色层、第一离子导体层、第二透明导电层、第二复合变色层、第二离子导体层、第三透明导电层、主变色层、第三离子导体层、辅变色层、第四透明导电层以及外保护层。
3.根据权利要求2所述的电致变色玻璃，其特征在于，所述第一复合变色层包括第一子变色层和第二子变色层，所述第一子变色层与所述第一透明导电层相邻，所述第二子变色层与所述第一离子导体层相邻；所述第一子变色层的材料选自于W、Mo、Nb、Ti、Ta中至少两种组合的氧化物；所述第二子变色层的材料选自于Ni、V、Co、Ir、Fe、Mn中至少两种元素组合的氧化物。
4.根据权利要求2所述的电致变色玻璃，其特征在于，所述第二复合层包括第三子变色层和第四子变色层，所述第三子变色层与所述第二透明导电层相邻，所述第四子变色层与所述第二离子导体层相邻；所述第三子变色层的材料选自于W、Mo、Nb、Ti、Ta中至少两种组合的氧化物；所述第四子变色层的材料选自于Ni、V、Co、Ir、Fe、Mn中至少两种元素组合的氧化物。
5.根据权利要求2所述的电致变色玻璃，其特征在于，所述第一子变色层的厚度范围为30nm-500nm；所述第二子变色层的厚度范围为20nm-500nm；所述第三子变色层的厚度范围为30nm-500nm；所述第四子变色层的厚度范围为20nm-500nm。
6.根据权利要求5所述的电致变色玻璃，其特征在于，所述第一子变色层与所述第三子变色层的厚度相等；所述第二子变色层与所述第四子变色层的厚度相等。
7.根据权利要求2所述的电致变色玻璃，其特征在于，所述主变色层的材料选自于W、Mo、Nb、Ti、Ta中至少两种组合的氧化物；所述辅变色层的材料选自于Ni、V、Co、Ir、Fe、Mn中至少两种元素组合的氧化物。
8.根据权利要求2所述的电致变色玻璃，其特征在于，所述第一透明导电层、所述第二透明导电层、所述第三透明导电层、所述第四透明导电层的材料分别选自于FTO、ITO、IGZO、AZO、GZO、Ag中的一种或至少两种的组合；所述第一透明导电层、所述第二透明导电层、所述第三透明导电层的厚度范围分别为1-1100nm；所述第四透明导电层的厚度范围为10-1000nm。
9.根据权利要求2所述的电致变色玻璃，其特征在于，所述第一离子导体层、所述第二离子导体层、所述第三离子导体层的材料分别选自于H、Li、Na、K、Mg中的一种或至少两种的组合；所述第一离子导体层、所述第二离子导体层、所述第三离子导体层的厚度范围分别为10nm-100nm。
10.一种电致变色玻璃制备方法，其特征在于，包括：
提供玻璃基板；
在所述玻璃基板上形成第一透明导电层；
在所述第一透明导电层上形成第一复合变色层；
在所述第一复合变色层上形成第一离子导体层；
在所述第一离子导体层上形成第二透明导电层；
在所述第二透明导电层上形成第二复合变色层；
在所述第二复合变色层上形成第二离子导体层；
在所述第二离子导体层上形成第三透明导电层；
在所述第三透明导电层上形成主色层；
在所述主变色层上形成第三离子导体层；
在所述第三离子导体层上形成辅变色层；
在所述辅变色层上形成第四透明导电层；以及
在所述第四透明导电层上形成外保护层。