CN112961607A - 一种爱屋净味除甲醛包裹剂 - Google Patents
一种爱屋净味除甲醛包裹剂 Download PDFInfo
- Publication number
- CN112961607A CN112961607A CN202110161450.9A CN202110161450A CN112961607A CN 112961607 A CN112961607 A CN 112961607A CN 202110161450 A CN202110161450 A CN 202110161450A CN 112961607 A CN112961607 A CN 112961607A
- Authority
- CN
- China
- Prior art keywords
- agent
- wrapping
- odor
- moisture
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种爱屋净味除甲醛包裹剂，所述包裹剂的组合物重量配合比包括0.5‑0.7％防潮剂、0.45‑0.6％粘合剂、0.2‑0.25％增塑剂、0.03‑0.06％氧化剂、0.3‑0.6％成膜剂、0.04‑0.06％渗透剂、0.15‑0.3％润湿剂、0.02‑0.04％增稠剂、0.03‑0.05％杀菌剂以及余量的无菌去离子水，本发明的包裹剂能牢牢附着在基材的表面，覆盖扎根，从而形成了功能型的钢性环保隐形分子膜，同时本发明采用环保水性原料无刺激味、不染色外观、不损害饰面、干后耐磨擦、耐污渍，阻隔空气中潮湿吸收抑制霉菌生长，含甲醛胶有害物质的挥发源封堵包裹起来，将室内空气污染降至最低，达到爱屋净味目的。
Description
技术领域
本发明涉及一种包裹剂，特别涉及一种爱屋净味除甲醛包裹剂，属于除甲醛剂技术领域。
背景技术
甲醛是一种有机化学物质，化学式是HCHO或CH2O分子量30.03，又称蚁醛。是无色有刺激性气体，对人眼、鼻等有刺激作用。气体相对密度1.067(空气＝1)，液体密度0.815g/cm3(-20℃)。熔点-92℃，沸点-19.5℃。易溶于水和乙醇。水溶液的浓度最高可达55％，一般是35％-40％，通常为37％，称做甲醛水，俗称福尔马林(formalin)。具有还原性，尤其在碱性溶液中，还原能力更强。能燃烧，蒸气与空气形成爆炸性混合物，爆炸极限7％-73％(体积)，燃点约300℃。
在使用装修基材的多层胶合板祼面、家具和厨柜内的人造复合板裸面时，因在梅雨节潮湿大或经常不开窗，容易潮湿会生霉菌，尤其炎热天含甲醛胶的基材面所长的霉菌会挥发出有害物质与气味，室内空气被污染。
发明内容
本发明的目的在于提供一种爱屋净味除甲醛包裹剂，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：一种爱屋净味除甲醛包裹剂，所述包裹剂的组合物重量配合比包括0.5-0.7％防潮剂、0.45-0.6％粘合剂、0.2-0.25％增塑剂、0.03-0.06％氧化剂、0.3-0.6％成膜剂、0.04-0.06％渗透剂、0.15-0.3％润湿剂、0.02-0.04％增稠剂、0.03-0.05％杀菌剂以及余量的无菌去离子水。
作为本发明的一种优选技术方案，一种爱屋净味除甲醛包裹剂的使用方法，包括以下步骤：
S1：量取足量的无菌去离子水，再称量防潮剂、粘合剂、增塑剂、氧化剂、成膜剂、渗透剂、润湿剂、增稠剂和杀菌剂，一同加入到搅拌仪器中；
S2：通过电动搅拌仪器对步骤S1中的混合物进行搅拌，搅拌时间为20-30min,搅拌速率为800-1000r/min；
S3：将步骤S2中混合均匀的组合物液添加到雾化喷涂设备中，均匀喷涂在释放污染源头表面，组合物液进行渗透包裹分解，待喷涂在污染物表面上聚合物液的水份完全蒸发干燥，能牢牢附着在基材表面覆盖扎根，从而形成了功能型的钢性环保隐形分子膜，使得含甲醛胶有害物质的挥发源封堵包裹起来，将室内空气污染降至最低，达到爱屋净味的目的。
与现有技术相比，本发明的有益效果是：
1.本发明一种爱屋净味除甲醛包裹剂，本发明的包裹剂能牢牢附着在基材的表面，覆盖扎根，从而形成了功能型的钢性环保隐形分子膜，同时本发明采用环保水性原料无刺激味、不染色外观、不损害饰面、干后耐磨擦、耐污渍，阻隔空气中潮湿吸收抑制霉菌生长，含甲醛胶有害物质的挥发源封堵包裹起来，将室内空气污染降至最低，达到爱屋净味目的。
具体实施方式
下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
本发明提供了一种爱屋净味除甲醛包裹剂的技术方案：
一种爱屋净味除甲醛包裹剂，包裹剂的组合物重量配合比包括0.5-0.7％防潮剂、0.45-0.6％粘合剂、0.2-0.25％增塑剂、0.03-0.06％氧化剂、0.3-0.6％成膜剂、0.04-0.06％渗透剂、0.15-0.3％润湿剂、0.02-0.04％增稠剂、0.03-0.05％杀菌剂以及余量的无菌去离子水。
一种爱屋净味除甲醛包裹剂的使用方法，包括以下步骤：
S1：量取足量的无菌去离子水，再称量防潮剂、粘合剂、增塑剂、氧化剂、成膜剂、渗透剂、润湿剂、增稠剂和杀菌剂，一同加入到搅拌仪器中；
S2：通过电动搅拌仪器对步骤S1中的混合物进行搅拌，搅拌时间为20-30min,搅拌速率为800-1000r/min；
S3：将步骤S2中混合均匀的组合物液添加到雾化喷涂设备中，均匀喷涂在释放污染源头表面，组合物液进行渗透包裹分解，待喷涂在污染物表面上聚合物液的水份完全蒸发干燥，能牢牢附着在基材表面覆盖扎根，从而形成了功能型的钢性环保隐形分子膜，使得含甲醛胶有害物质的挥发源封堵包裹起来，将室内空气污染降至最低，达到爱屋净味的目的。
具体使用时，本发明一种爱屋净味除甲醛包裹剂，将发明的组合物液添加到雾化喷涂设备中，均匀喷涂在释放污染源头表面，组合物液进行渗透包裹分解，待喷涂在污染物表面上聚合物液的水份完全蒸发干燥，能牢牢附着在基材表面覆盖扎根，从而形成了功能型的钢性环保隐形分子膜，使得含甲醛胶有害物质的挥发源封堵包裹起来，将室内空气污染降至最低，综上所述，本发明采用环保水性原料无刺激味、不染色外观、不损害饰面、干后耐磨擦、耐污渍，阻隔空气中潮湿吸收抑制霉菌生长，含甲醛胶有害物质的挥发源封堵包裹起来，将室内空气污染降至最低。
实施例一：作为本发明的最优配比，
量取足量的无菌去离子水，称重0.7％防潮剂、0.6％粘合剂、0.25％增塑剂、0.06％氧化剂、0.6％成膜剂、0.06％渗透剂、0.3％润湿剂、0.04％增稠剂和0.05％杀菌剂一同加入到搅拌仪器中；通过电动搅拌仪器对步骤S1中的混合物进行搅拌，搅拌时间为20-30min,搅拌速率为800-1000r/min；得到混合均匀的组合物液，并添加到雾化喷涂设备中，均匀喷涂在释放污染源头表面，组合物液进行渗透包裹分解，待喷涂在污染物表面上聚合物液的水份完全蒸发干燥，能牢牢附着在基材表面覆盖扎根，从而形成了功能型的钢性环保隐形分子膜，使得含甲醛胶有害物质的挥发源封堵包裹起来，将室内空气污染降至最低。
在本发明的描述中，需要理解的是，指示的方位或位置关系为基于实施例所示的方位或位置关系，仅是为了便于描述本发明和简化描述，而不是指示或暗示所指的装置或元件必须具有特定的方位、以特定的方位构造和操作，因此不能理解为对本发明的限制。
在本发明中，除非另有明确的规定和限定，例如，可以是固定连接，也可以是可拆卸连接，或成一体；可以是机械连接，也可以是电连接；可以是直接相连，也可以通过中间媒介间接相连，可以是两个元件内部的连通或两个元件的相互作用关系，除非另有明确的限定，对于本领域的普通技术人员而言，可以根据具体情况理解上述术语在本发明中的具体含义。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (2)
1.一种爱屋净味除甲醛包裹剂，其特征在于，所述包裹剂的组合物重量配合比包括0.5-0.7％防潮剂、0.45-0.6％粘合剂、0.2-0.25％增塑剂、0.03-0.06％氧化剂、0.3-0.6％成膜剂、0.04-0.06％渗透剂、0.15-0.3％润湿剂、0.02-0.04％增稠剂、0.03-0.05％杀菌剂以及余量的无菌去离子水。
2.一种爱屋净味除甲醛包裹剂的使用方法，其特征在于：包括以下步骤：
S1：量取足量的无菌去离子水，再称量防潮剂、粘合剂、增塑剂、氧化剂、成膜剂、渗透剂、润湿剂、增稠剂和杀菌剂，一同加入到搅拌仪器中；
S2：通过电动搅拌仪器对步骤S1中的混合物进行搅拌，搅拌时间为20-30min,搅拌速率为800-1000r/min；
S3：将步骤S2中混合均匀的组合物液添加到雾化喷涂设备中，均匀喷涂在释放污染源头表面，组合物液进行渗透包裹分解，待喷涂在污染物表面上聚合物液的水份完全蒸发干燥，能牢牢附着在基材表面覆盖扎根，从而形成了功能型的钢性环保隐形分子膜，使得含甲醛胶有害物质的挥发源封堵包裹起来，将室内空气污染降至最低，达到爱屋净味的目的。