CN112959775A - 一种耐寒易撕型包装膜及其制备方法 - Google Patents
一种耐寒易撕型包装膜及其制备方法 Download PDFInfo
- Publication number
- CN112959775A CN112959775A CN202110331988.XA CN202110331988A CN112959775A CN 112959775 A CN112959775 A CN 112959775A CN 202110331988 A CN202110331988 A CN 202110331988A CN 112959775 A CN112959775 A CN 112959775A
- Authority
- CN
- China
- Prior art keywords
- layer
- polyethylene
- density polyethylene
- raw materials
- composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐寒易撕型包装膜,包括聚脂薄膜层、铝箔层和聚乙烯膜层,所述聚乙烯膜层通过复合层、中间层和热封层组成,所述复合层包括以下原料:低密度聚乙烯、线性低密度聚乙烯、改性聚乙烯、爽滑剂和加工助剂,所述中间层包括以下原料:低密度聚乙烯、线性低密度聚乙烯、改性聚乙烯和加工助剂,所述热封层包括以下原料:低密度聚乙烯、茂金属线性低密度聚乙烯、改性聚乙烯、开口剂、爽滑剂和加工助剂。本发明生产的包装薄膜具有良好的横向、纵向、双向易撕性,极寒耐破性好等特点;横向、纵向、双向直线撕裂强度低,可提升消费者的使用体验。
Description
技术领域
本发明涉及包装膜技术领域,具体为一种耐寒易撕型包装膜及其制备方法。
背景技术
在食品行业中小包装产品因为使用方便、易于储存和运输,越来越成为人们生活中不可或缺的产品,像小包饼干、薯条、各种小零食、方便面调味包、酱包、酒店一次性洗漱用品等。然而一般的包装袋在打开时不容易撕开,有的是一个方向容易撕开,而另一个方向不易撕开,对生活质量要求越来越高的现代人带来了不便。而且食品包装分类方法很多。如按技法分为:防潮包装、防水包装、防霉包装、保鲜包装、速冻包装、透气包装、微波杀菌包装、无菌包装、充气包装、真空包装、脱氧包装、泡罩包装、贴体包装、拉伸包装、蒸煮袋包装等。上述各种包装皆是由不同复合材料制成的,其包装特性是对应不同食品的要求,能有效地保护食品品质。
现有的食品包装袋不仅不易撕开,而且耐寒性能不足,容易在低温下开裂,不能满足人们的使用需求。
发明内容
本发明的目的在于提供一种耐寒易撕型包装膜及其制备方法,以解决上述背景技术中提出的问题。
为了解决上述技术问题,本发明提供如下技术方案:一种耐寒易撕型包装膜,所述耐寒易撕型包装膜包括有聚脂薄膜层、铝箔层和聚乙烯膜层,所述聚乙烯膜层通过复合层、中间层和热封层组成,所述复合层包括以下百分比的原料:低密度聚乙烯15-25%、线性低密度聚乙烯30-50%、改性聚乙烯30-50%、爽滑剂0.2-0.8%和加工助剂0.2-0.8%,所述中间层包括以下百分比的原料:低密度聚乙烯15-25%、线性低密度聚乙烯30-50%、改性聚乙烯30-50%和加工助剂0.2-0.5%,所述热封层包括以下百分比的原料:低密度聚乙烯20-30%、茂金属线性低密度聚乙烯40-50%、改性聚乙烯30-40%、开口剂1-1.5%、爽滑剂0.2-0.8%和加工助剂0.2-0.8%。
在一种优选的实施方式中,所述复合层包括以下百分比的原料:低密度聚乙烯18-22%、线性低密度聚乙烯35-45%、改性聚乙烯35-45%、爽滑剂0.4-0.6%和加工助剂0.4-0.6%,所述中间层包括以下百分比的原料:低密度聚乙烯18-22%、线性低密度聚乙烯35-45%、改性聚乙烯35-45%和加工助剂0.3-0.4%,所述热封层包括以下百分比的原料:低密度聚乙烯24-26%、茂金属线性低密度聚乙烯43-47%、改性聚乙烯33-37%、开口剂1.2-1.3%、爽滑剂0.4-0.6%和加工助剂0.4-0.6%。
在一种优选的实施方式中,所述复合层包括以下百分比的原料:低密度聚乙烯20%、线性低密度聚乙烯40%、改性聚乙烯40%、爽滑剂0.5%和加工助剂0.5%,所述中间层包括以下百分比的原料:低密度聚乙烯20%、线性低密度聚乙烯40%、改性聚乙烯40%和加工助剂0.25%,所述热封层包括以下百分比的原料:低密度聚乙烯25%、茂金属线性低密度聚乙烯40%、改性聚乙烯35%、开口剂1.2%、爽滑剂0.5%和加工助剂0.5%。
在一种优选的实施方式中,所述复合层、中间层和热封层的厚度比为1:3:1、1:2:1或3:4:3中的一种,所述开口剂为AB-20LD开口剂,所述加工助剂为聚烯烃加工助剂。
在一种优选的实施方式中,所述聚脂薄膜层的厚度为12-20um,所述铝箔层的厚度为6-12um,所述聚乙烯膜层的厚度为40-100um。
本发明还提供一种耐寒易撕型包装膜的制备方法,包括以下步骤:
a)吹膜,按照上述百分比分别称取复合层、中间层和热封层的原料,将称取的原料分别放入到混合罐中混合均匀,对混合均匀的物料进行加热熔融,熔融后分别导入到双螺杆挤出机中进行挤出造粒,将得到的粒子进行烘干,然后在160-180℃下进行吹膜分别得到复合层、中间层和热封层;
b)聚乙烯膜层的制备,根据聚乙烯膜层中复合层、中间层和热封层的层厚比例选取相应后的复合层、中间层和热封层,复合层、中间层和热封层在压辊的作用下涂上胶黏剂,然后在压辊的作用使复合层、中间层和热封层形成聚乙烯膜层;
c)将聚脂薄膜层预处理后进行印刷,印刷完成后与铝箔层进行干式复合或无溶剂复合形成复合结构A,将复合结构A与步骤b)中得到的聚乙烯膜层进行干式复合或无溶剂复合得到复合结构B;
d)对步骤c)中得到的复合结构B进行熟化处理,熟化处理后进行分切,将分切后的复合结构B进行制袋得到耐寒易撕型包装膜袋。
在一种优选的实施方式中,所述步骤a)中物料加热熔融的温度为150-170℃,所述复合层、中间层和热封层挤出造粒后粒子直径为50-100nm,且挤出造粒时双螺杆挤出机的螺杆转速为100-140r/min,所述粒子烘干时温度为65-75℃。
在一种优选的实施方式中,所述步骤a)中复合层、中间层和热封层的原料中改性聚乙烯的制备方法为:称取适量的聚乙烯树脂和丁二烯单体放入到密闭反应釜中进行加热搅拌,使得聚乙烯树脂和丁二烯单体进行裂解,裂解温度为500-600℃,裂解时间为2-4h,裂解后冷却到100℃,然后加入抗氧化剂进行搅拌出料,进行破碎筛选得到改性聚乙烯。
在一种优选的实施方式中,所述步骤c)中干式复合时压辊温度为70℃,复合压力为5.5kgf/cm2,上胶干量为2.8g/cm2。
在一种优选的实施方式中,所述步骤d)中熟化处理的温度为40-50℃,熟化时间为36-48h,所述步骤d)中分切处理是将复合结构B的工艺边打掉收卷整齐,按一定尺寸分条后备用制袋。
与现有技术相比,本发明所达到的有益效果是:
1、本发明生产的包装膜采用聚脂薄膜层、铝箔层和聚乙烯膜层组成,铝箔层具有良好的阻隔性能够有效保证食品的保质期,聚脂薄膜层具有较好的印刷适应性和尺寸稳定性,聚乙烯膜层由复合层、中间层和热封层组成,复合层和中间层中均包括有低密度聚乙烯、线性低密度聚乙烯和改性聚乙烯,而且线性低密度聚乙烯含量较高,线性低密度聚乙烯具有较高的刚性、韧性以及较好的耐热和耐寒性能,而热封层中包括有低密度聚乙烯、茂金属线性低密度聚乙烯、改性聚乙烯,复合层、中间层和热封层组成中均含有改性聚乙烯,改性聚乙烯通过聚乙烯与丁二烯单体裂解接枝共聚生产,可以提高包装膜的耐热、耐寒和耐应力开裂性能,从而使得包装膜具有较好的耐寒耐破性能,可提升消费者的使用体验;
2、本发明聚乙烯膜层中复合层、中间层和热封层均采用聚乙烯材料制作而成,在提高耐寒性能的同时能够有效降低包装膜的撕裂强度,使得包装膜具有良好的横向、纵向、双向易撕性,横向、纵向、双向直线撕裂强度低,能够满足人们的使用需求。
附图说明
附图用来提供对本发明的进一步理解,并且构成说明书的一部分,与本发明的实施例一起用于解释本发明,并不构成对本发明的限制。在附图中:
图1是本发明的整体截面结构示意图;
图中:1聚脂薄膜层;2铝箔层;3聚乙烯膜层;4复合层;5中间层;6热封层。
具体实施方式
下面将结合本发明实施例中的附图,对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
实施例1:
请参阅图1,本发明提供一种耐寒易撕型包装膜,所述耐寒易撕型包装膜包括有聚脂薄膜层1、铝箔层2和聚乙烯膜层3,所述聚乙烯膜层3通过复合层4、中间层5和热封层6组成,所述复合层4包括以下百分比的原料:低密度聚乙烯15%、线性低密度聚乙烯30%、改性聚乙烯30%、爽滑剂0.2%和加工助剂0.2%,所述中间层5包括以下百分比的原料:低密度聚乙烯15%、线性低密度聚乙烯30%、改性聚乙烯30%和加工助剂0.2%,所述热封层6包括以下百分比的原料:低密度聚乙烯20%、茂金属线性低密度聚乙烯40%、改性聚乙烯30%、开口剂1%、爽滑剂0.2%和加工助剂0.2%。
在一种优选的实施方式中,所述复合层4、中间层5和热封层6的厚度比为1:3:1,所述开口剂为AB-20LD开口剂,所述加工助剂为聚烯烃加工助剂。
在一种优选的实施方式中,所述聚脂薄膜层1的厚度为12um,所述铝箔层2的厚度为7um,所述聚乙烯膜层3的厚度为80um。
本发明还提供一种耐寒易撕型包装膜的制备方法,包括以下步骤:
a)吹膜,按照上述百分比分别称取复合层4、中间层5和热封层6的原料,将称取的原料分别放入到混合罐中混合均匀,对混合均匀的物料进行加热熔融,熔融后分别导入到双螺杆挤出机中进行挤出造粒,将得到的粒子进行烘干,然后在170℃下进行吹膜分别得到复合层4、中间层5和热封层6;
b)聚乙烯膜层3的制备,根据聚乙烯膜层3中复合层4、中间层5和热封层6的层厚比例选取相应后的复合层4、中间层5和热封层6,复合层4、中间层5和热封层6在压辊的作用下涂上胶黏剂,然后在压辊的作用使复合层4、中间层5和热封层6形成聚乙烯膜层3;
c)将聚脂薄膜层1预处理后进行印刷,印刷完成后与铝箔层2进行干式复合或无溶剂复合形成复合结构A,将复合结构A与步骤b)中得到的聚乙烯膜层(3)进行干式复合或无溶剂复合得到复合结构B;
d)对步骤c)中得到的复合结构B进行熟化处理,熟化处理后进行分切,将分切后的复合结构B进行制袋得到耐寒易撕型包装膜袋。
在一种优选的实施方式中,所述步骤a)中物料加热熔融的温度为160℃,所述复合层4、中间层5和热封层6挤出造粒后粒子直径为50-100nm,且挤出造粒时双螺杆挤出机的螺杆转速为120r/min,所述粒子烘干时温度为70℃。
在一种优选的实施方式中,所述步骤a)中复合层4、中间层5和热封层6的原料中改性聚乙烯的制备方法为:称取适量的聚乙烯树脂和丁二烯单体放入到密闭反应釜中进行加热搅拌,使得聚乙烯树脂和丁二烯单体进行裂解,裂解温度为550℃,裂解时间为3h,裂解后冷却到100℃,然后加入抗氧化剂进行搅拌出料,进行破碎筛选得到改性聚乙烯。
在一种优选的实施方式中,所述步骤c)中干式复合时压辊温度为70℃,复合压力为5.5kgf/cm2,上胶干量为2.8g/cm2。
在一种优选的实施方式中,所述步骤d)中熟化处理的温度为45℃,熟化时间为36h,所述步骤d)中分切处理是将复合结构B的工艺边打掉收卷整齐,按一定尺寸分条后备用制袋。
实施例2:
与实施例2不同的是,所述复合层4包括以下百分比的原料:低密度聚乙烯20%、线性低密度聚乙烯40%、改性聚乙烯40%、爽滑剂0.5%和加工助剂0.5%,所述中间层5包括以下百分比的原料:低密度聚乙烯20%、线性低密度聚乙烯40%、改性聚乙烯40%和加工助剂0.25%,所述热封层6包括以下百分比的原料:低密度聚乙烯25%、茂金属线性低密度聚乙烯40%、改性聚乙烯35%、开口剂1.2%、爽滑剂0.5%和加工助剂0.5%。
实施例3:
与实施例1-2不同的是,所述复合层包括以下百分比的原料:低密度聚乙烯25%、线性低密度聚乙烯50%、改性聚乙烯50%、爽滑剂0.8%和加工助剂0.2-0.8%,所述中间层包括以下百分比的原料:低密度聚乙烯25%、线性低密度聚乙烯50%、改性聚乙烯50%和加工助剂0.5%,所述热封层包括以下百分比的原料:低密度聚乙烯30%、茂金属线性低密度聚乙烯50%、改性聚乙烯40%、开口剂1.5%、爽滑剂0.8%和加工助剂0.8%。
实施例4:
本发明提供一种耐寒易撕型包装膜,所述耐寒易撕型包装膜包括有聚脂薄膜层1、铝箔层2和聚乙烯膜层3,所述聚乙烯膜层3通过复合层4、中间层5和热封层6组成,所述复合层4包括以下百分比的原料:低密度聚乙烯15%、线性低密度聚乙烯30%、改性聚乙烯30%、爽滑剂0.2%和加工助剂0.2%,所述中间层5包括以下百分比的原料:低密度聚乙烯15%、线性低密度聚乙烯30%、改性聚乙烯30%和加工助剂0.2%,所述热封层6包括以下百分比的原料:低密度聚乙烯20%、茂金属线性低密度聚乙烯40%、改性聚乙烯30%、开口剂1%、爽滑剂0.2%和加工助剂0.2%。
在一种优选的实施方式中,所述复合层4、中间层5和热封层6的厚度比为1:2:1,所述开口剂为AB-20LD开口剂,所述加工助剂为聚烯烃加工助剂。
在一种优选的实施方式中,所述聚脂薄膜层1的厚度为12um,所述铝箔层2的厚度为7um,所述聚乙烯膜层3的厚度为80um。
本发明还提供一种耐寒易撕型包装膜的制备方法,包括以下步骤:
a)吹膜,按照上述百分比分别称取复合层4、中间层5和热封层6的原料,将称取的原料分别放入到混合罐中混合均匀,对混合均匀的物料进行加热熔融,熔融后分别导入到双螺杆挤出机中进行挤出造粒,将得到的粒子进行烘干,然后在170℃下进行吹膜分别得到复合层4、中间层5和热封层6;
b)聚乙烯膜层3的制备,根据聚乙烯膜层3中复合层4、中间层5和热封层6的层厚比例选取相应后的复合层4、中间层5和热封层6,复合层4、中间层5和热封层6在压辊的作用下涂上胶黏剂,然后在压辊的作用使复合层4、中间层5和热封层6形成聚乙烯膜层3;
c)将聚脂薄膜层1预处理后进行印刷,印刷完成后与铝箔层2进行干式复合或无溶剂复合形成复合结构A,将复合结构A与步骤b)中得到的聚乙烯膜层(3)进行干式复合或无溶剂复合得到复合结构B;
d)对步骤c)中得到的复合结构B进行熟化处理,熟化处理后进行分切,将分切后的复合结构B进行制袋得到耐寒易撕型包装膜袋。
在一种优选的实施方式中,所述步骤a)中物料加热熔融的温度为160℃,所述复合层4、中间层5和热封层6挤出造粒后粒子直径为50-100nm,且挤出造粒时双螺杆挤出机的螺杆转速为120r/min,所述粒子烘干时温度为70℃。
在一种优选的实施方式中,所述步骤a)中复合层4、中间层5和热封层6的原料中改性聚乙烯的制备方法为:称取适量的聚乙烯树脂和丁二烯单体放入到密闭反应釜中进行加热搅拌,使得聚乙烯树脂和丁二烯单体进行裂解,裂解温度为550℃,裂解时间为3h,裂解后冷却到100℃,然后加入抗氧化剂进行搅拌出料,进行破碎筛选得到改性聚乙烯。
在一种优选的实施方式中,所述步骤c)中干式复合时压辊温度为70℃,复合压力为5.5kgf/cm2,上胶干量为2.8g/cm2。
在一种优选的实施方式中,所述步骤d)中熟化处理的温度为45℃,熟化时间为36h,所述步骤d)中分切处理是将复合结构B的工艺边打掉收卷整齐,按一定尺寸分条后备用制袋。
实施例5:
与实施例4不同的是,所述复合层4、中间层5和热封层6的厚度比为3:4:3。
分别选取实施例1、实施例2、实施例3、实施例4和实施例5生产的包装膜分别作为实验组1、实验组2、实验组3、实验组4和实验组5,选取传统的包装膜作为对照组,分别测量每组包装膜的拉伸强度、耐寒性和撕开的难易程度,测量结果如表一所示:
拉伸强度/MPa | 耐寒性/℃ | 横向撕开 | 纵向撕开 | |
实验组1 | 26 | -28 | 易 | 易 |
实验组2 | 30 | -33 | 易 | 易 |
实验组3 | 29 | -30 | 易 | 易 |
实验组4 | 30 | -32 | 易 | 易 |
实验组5 | 28 | -30 | 易 | 易 |
对照组 | 18 | -12 | 易 | 难 |
表一
经过多次实验可以得出,如表一所示实施例生产的包装膜具有较高的拉伸强度,而且耐寒性明显高于传统的包装膜,具有双向易撕性,实施例4和实施例5聚乙烯膜层中复合层、中间层和热封层的厚度不同,与实施例1相比,实施例4中复合层、中间层和热封层的厚度配比效果最佳,聚脂薄膜层具有较好的印刷适应性和尺寸稳定性,聚乙烯膜层由复合层、中间层和热封层组成,复合层和中间层中均包括有低密度聚乙烯、线性低密度聚乙烯和改性聚乙烯,而且线性低密度聚乙烯含量较高,线性低密度聚乙烯具有较高的刚性、韧性以及较好的耐热和耐寒性能,而热封层中包括有低密度聚乙烯、茂金属线性低密度聚乙烯、改性聚乙烯,复合层、中间层和热封层组成中均含有改性聚乙烯,改性聚乙烯通过聚乙烯与丁二烯单体裂解接枝共聚生产,可以提高包装膜的耐热、耐寒和耐应力开裂性能,从而使得包装膜具有较好的耐寒耐破性能,可提升消费者的使用体验。
需要说明的是,在本文中,诸如第一和第二等之类的关系术语仅仅用来将一个实体或者操作与另一个实体或操作区分开来,而不一定要求或者暗示这些实体或操作之间存在任何这种实际的关系或者顺序。而且,术语“包括”、“包含”或者其任何其他变体意在涵盖非排他性的包含,从而使得包括一系列要素的过程、方法、物品或者设备不仅包括那些要素,而且还包括没有明确列出的其他要素,或者是还包括为这种过程、方法、物品或者设备所固有的要素。
最后应说明的是:以上所述仅为本发明的优选实施例而已,并不用于限制本发明,尽管参照前述实施例对本发明进行了详细的说明,对于本领域的技术人员来说,其依然可以对前述各实施例所记载的技术方案进行修改,或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (10)
1.一种耐寒易撕型包装膜,其特征在于:所述耐寒易撕型包装膜包括有聚脂薄膜层(1)、铝箔层(2)和聚乙烯膜层(3),所述聚乙烯膜层(3)通过复合层(4)、中间层(5)和热封层(6)组成,所述复合层(4)包括以下百分比的原料:低密度聚乙烯15-25%、线性低密度聚乙烯30-50%、改性聚乙烯30-50%、爽滑剂0.2-0.8%和加工助剂0.2-0.8%,所述中间层(5)包括以下百分比的原料:低密度聚乙烯15-25%、线性低密度聚乙烯30-50%、改性聚乙烯30-50%和加工助剂0.2-0.5%,所述热封层(6)包括以下百分比的原料:低密度聚乙烯20-30%、茂金属线性低密度聚乙烯40-50%、改性聚乙烯30-40%、开口剂1-1.5%、爽滑剂0.2-0.8%和加工助剂0.2-0.8%。
2.根据权利要求1所述的一种耐寒易撕型包装膜,其特征在于:所述复合层(4)包括以下百分比的原料:低密度聚乙烯18-22%、线性低密度聚乙烯35-45%、改性聚乙烯35-45%、爽滑剂0.4-0.6%和加工助剂0.4-0.6%,所述中间层(5)包括以下百分比的原料:低密度聚乙烯18-22%、线性低密度聚乙烯35-45%、改性聚乙烯35-45%和加工助剂0.3-0.4%,所述热封层(6)包括以下百分比的原料:低密度聚乙烯24-26%、茂金属线性低密度聚乙烯43-47%、改性聚乙烯33-37%、开口剂1.2-1.3%、爽滑剂0.4-0.6%和加工助剂0.4-0.6%。
3.根据权利要求1所述的一种耐寒易撕型包装膜,其特征在于:所述复合层(4)包括以下百分比的原料:低密度聚乙烯20%、线性低密度聚乙烯40%、改性聚乙烯40%、爽滑剂0.5%和加工助剂0.5%,所述中间层(5)包括以下百分比的原料:低密度聚乙烯20%、线性低密度聚乙烯40%、改性聚乙烯40%和加工助剂0.25%,所述热封层(6)包括以下百分比的原料:低密度聚乙烯25%、茂金属线性低密度聚乙烯40%、改性聚乙烯35%、开口剂1.2%、爽滑剂0.5%和加工助剂0.5%。
4.根据权利要求1所述的一种耐寒易撕型包装膜,其特征在于:所述复合层(4)、中间层(5)和热封层(6)的厚度比为1:3:1、1:2:1或3:4:3中的一种,所述开口剂为AB-20LD开口剂,所述加工助剂为聚烯烃加工助剂。
5.根据权利要求1所述的一种耐寒易撕型包装膜,其特征在于:所述聚脂薄膜层(1)的厚度为12-20um,所述铝箔层(2)的厚度为6-12um,所述聚乙烯膜层(3)的厚度为8-12um。
6.根据权利要求1-5任意一项所述的一种耐寒易撕型包装膜的制备方法,其特征在于:包括以下步骤:
a)吹膜,按照上述百分比分别称取复合层(4)、中间层(5)和热封层(6)的原料,将称取的原料分别放入到混合罐中混合均匀,对混合均匀的物料进行加热熔融,熔融后分别导入到双螺杆挤出机中进行挤出造粒,将得到的粒子进行烘干,然后在160-180℃下进行吹膜分别得到复合层(4)、中间层(5)和热封层(6);
b)聚乙烯膜层(3)的制备,根据聚乙烯膜层(3)中复合层(4)、中间层(5)和热封层(6)的层厚比例选取相应后的复合层(4)、中间层(5)和热封层(6),复合层(4)、中间层(5)和热封层(6)在压辊的作用下涂上胶黏剂,然后在压辊的作用使复合层(4)、中间层(5)和热封层(6)形成聚乙烯膜层(3);
c)将聚脂薄膜层(1)预处理后进行印刷,印刷完成后与铝箔层(2)进行干式复合或无溶剂复合形成复合结构A,将复合结构A与步骤b)中得到的聚乙烯膜层(3)进行干式复合或无溶剂复合得到复合结构B;
d)对步骤c)中得到的复合结构B进行熟化处理,熟化处理后进行分切,将分切后的复合结构B进行制袋得到耐寒易撕型包装膜袋。
7.根据权利要求6所述的一种耐寒易撕型包装膜的制备方法,其特征在于:所述步骤a)中物料加热熔融的温度为150-170℃,所述复合层(4)、中间层(5)和热封层(6)挤出造粒后粒子直径为50-100nm,且挤出造粒时双螺杆挤出机的螺杆转速为100-140r/min,所述粒子烘干时温度为65-75℃。
8.根据权利要求6所述的一种耐寒易撕型包装膜的制备方法,其特征在于:所述步骤a)中复合层(4)、中间层(5)和热封层(6)的原料中改性聚乙烯的制备方法为:称取适量的聚乙烯树脂和丁二烯单体放入到密闭反应釜中进行加热搅拌,使得聚乙烯树脂和丁二烯单体进行裂解,裂解温度为500-600℃,裂解时间为2-4h,裂解后冷却到100℃,然后加入抗氧化剂进行搅拌出料,进行破碎筛选得到改性聚乙烯。
9.根据权利要求6所述的一种耐寒易撕型包装膜的制备方法,其特征在于:所述步骤c)中干式复合时压辊温度为70℃,复合压力为5.5kgf/cm2,上胶干量为2.8g/cm2。
10.根据权利要求6所述的一种耐寒易撕型包装膜的制备方法,其特征在于:所述步骤d)中熟化处理的温度为40-50℃,熟化时间为36-48h,所述步骤d)中分切处理是将复合结构B的工艺边打掉收卷整齐,按一定尺寸分条后备用制袋。